Figure 2.

Figure 2

(a) Guiding map for MXene TCE fabrication. (b) Digital photograph of Ti3C2Tx films from large-sized flakes on glass (T = 83%). (c) Top-view SEM images of a blade-coated Ti3C2Tx film (T = 74%). (d) XRD patterns of various transparent films by blade coating. (e) XRD patterns of blade-coated and spin-coated Ti3C2Tx films (T = 60%) on glass. (f) GISAXS measurement of a Ti3C2Tx TCE (T = 60%). GISAXS detector image showing the (002) peak over qz. (g) Lorentzian fit of the azimuthal profile for the (002) peak used to determine the Herman’s degree of orientation. (h) Raman spectra of Ti3C2Tx films with different transparency. (i) XPS spectrum of a Ti3C2Tx film (T = 80%).