Abstract
The regeneration of biological tissues in medicine is challenging, and 3D bioprinting offers an innovative way to create functional multicellular tissues. One common way in bioprinting is bioink, which is one type of the cell-loaded hydrogel. For clinical application, however, the bioprinting still suffers from satisfactory performance, e.g., in vascularization, effective antibacterial, immunomodulation, and regulation of collagen deposition. Many studies incorporated different bioactive materials into the 3D-printed scaffolds to optimize the bioprinting. Here, we reviewed a variety of additives added to the 3D bioprinting hydrogel. The underlying mechanisms and methodology for biological regeneration are important and will provide a useful basis for future research.
Keywords: 3D bioprinting, hydrogel, bioink, tissue engineering, bionic scaffold
1. Introduction
Owing to the rapid development of current medical technology, a high success rate in organ transplantation and tissue repair was recently achieved. However, the limited number of organs available from donors constrain organ transplantation and tissue repair [1]. In recent years, researchers focused on tissue engineering and regenerative medicine to overcome donor shortage and immune rejection. Tissue engineering focuses on creating autologous tissues or organs for transplantation by using cells, biomaterials, and some additives such as cytokines. Additionally, regenerative medicine reproduces the healthy functions of cells, tissues, or organs through substitution or regeneration [2,3].
An emerging technology is 3D printing; it made significant advances in many fields, including aerospace, consumer products, the food industry, and manufacturing, and it combines cells and biological materials [4] to construct complex 3D structures, which can be used for scaffold-based or scaffold-free tissue and organ structures, micro-organisms, and single-chip organ model systems. For the medical field, 3D printing is also revolutionary in treating diseases [3,5,6,7]. The core of 3D printing lies in the printing conditions, printing technology, and suitable bioinks. Bioinks are generally a formula containing biomaterials and bioactive components that can be processed by automated manufacturing technology [8,9]. The types of bioinks include hydrogels, cell aggregates, acellular matrix, etc. [10,11]. The ideal hydrogel materials should have good physical, chemical, and biological characteristics, such as printability, biocompatibility, degradability, mechanical properties, stability, non-toxic, and non-immunogenic, as well as promotion of cell adhesion proliferation and differentiation [11,12,13]. However, possession of these properties does not necessarily permit the functional scaffolds to achieve optimal tissue repair, as the microenvironment and growth conditions at various implantation sites are different. Problems such as insufficient vascularization, causing ischemia and hypoxia, microbial contamination, inflammatory reactions, collagen metabolism disorders, etc., may occur after scaffold implantation into the target tissue. Scaffold implantation, tissue regeneration, wound healing, and scar formation will then fail. Therefore, it is necessary to design the specific scaffold to better enhance the regeneration-promoting ability [14,15]. In this review, we summarize different additives that were added to 3D bioprinting bioinks. As mentioned above, we divided the various additives into these four categories precisely because sufficient vascularization, lower inflammatory response and infection, and appropriate collagen deposition are key to better adaptation of the repair site to the implant and are among the indispensable factors to improve implant success. As shown in Table 1, we first describe, in general terms, the functions of the different additives and the mechanisms by which they work, followed by examples of the specific ways in which different researchers applied them to hydrogel scaffolds and the good results that were eventually achieved. We believe that the major difference and advantage of this review is that it has the potential to be a timely report for future researchers in selecting the right additives for bioinks. By understanding the functions of different additives and the mechanisms by which they function, as well as by referring to the methodologies of others, it will help researchers to find the additives they are looking for more efficiently and conveniently.
Table 1.
Function | Additive | Mechanism | Methodology | References | |
---|---|---|---|---|---|
Vascularization | Growth factors | VEGF |
|
Wang et al. made BMP-2 and VEGF adsorbed onto silk fiber (SF) microspheres (diameter of 1.5 ± 0.3 μm) that were prepared using a co-flow capillary device. These microspheres were subsequently doped into the SF/nHAp scaffolds to provide regulated and controlled release. | [16] |
FGF-2 | FGF-2 can stimulate VEGF expression, granulation tissue formation, and vascular maturation. | Xiong et al. used 3D printing to fabricate a gelatin-sulfonated silk composite scaffold (3DG-SF-SO3-FGF). The basic FGF-2 was incorporated in this scaffold by binding with a sulfonic acid group (SO3). | [17] | ||
PDGF | PDGF can recruit SMC/pericytes to immature vessels to stabilize and remodel them. | / | / | ||
Heparin and its derivatives | Heparin | Heparin can accelerate neovascularization by binding angiogenic factors, such as VEGF, and improve their stability. | An et al. coated poly-L-lysine (PLL) and heparin on the surface of 3D printed hydrogel scaffolds, which were made from cross-linking of GelMA and HAMA via electrostatic interactions between PLL and heparin. | [18] | |
Heparan sulfate | Heparan sulfate can not only protect growth factors from degradation by proteases, but it also promote the binding of growth factors to their receptors, thus promoting growth factor activity. | Jiang et al. fabricated a scaffold with collagen and heparan sulfate | [19] | ||
Other materials | Angiogenic peptides | Angiogenic peptides are functionally equivalent to VEGF and can bind to the same receptors to initiate angiogenesis. | Wang et al. made a dual-delivery bone tissue engineering scaffold by low-temperature 3D printing of β-tricalcium phosphate and—osteogenic peptide (OP) containing water/PLGA/DCM emulsion—and coating AP on the scaffold surface. | [20] | |
Desferrioxamine |
|
Yan et al. designed a bionic degradable polycaprolactone (PCL) scaffold using 3D printing technology. It can control the release of DFO by surface degradation and layer-by-layer assembly techniques. | [21] | ||
Catalase | Catalase can break down hydrogen peroxide and produce oxygen, which not only reduces the damage caused by H2O2, but the oxygen that it produces also helps to induce angiogenesis | Rija et al. intercalated catalase in hydrogels to form functional decellularized adipose tissue-alginate (DAT-A) hydrogels using 3D printing technology. | [22] | ||
Decellularized extracellular matrix |
|
Kim et al. used S-dECM bioink to print and fabricate 3D pre-vascularized skin patches for wound healing with infusion of adipose-derived stem cells (ASCs) and endothelial progenitor cells (EPCs). | [23,24] | ||
Bejleri et al. fabricated a 3D bioprinted patch containing cECM for the delivery of pediatric cardiac progenitor cells hCPCs which is printed with bioinks consisting of cECM, hCPCs, and GelMA. | |||||
Antibacterial | Photothermal materials | MXenes can kill microorganisms such as Gram-positive and negative bacteria by disrupting bacterial membranes directly through physical contact, especially when supplemented with NIR irradiation for higher antimicrobial efficiency | Nie et al. fabricated a personalized MXene composite hydrogel scaffold GelMA/β-TCP/sodium alginate (Sr2+)/MXene (Ti3C2) (GTAM) with both photothermal antibacterial and osteogenic capabilities using 3D printing technology. | [25] | |
Antibiotic | Vancomycin + Ceftazidime | Vancomycin can exert a strong bactericidal ability by inhibiting cell wall biosynthesis through specific binding to the dipeptide d-Ala-d-Ala (AA) at the end of bacterial cell wall precursors. Ceftazidime can inhibit bacterial peptidoglycan synthesis by inhibiting penicillin-binding proteins, leading to cell wall instability and inhibition of synthesis and cell death. |
Yu et al. fabricated a mesh-like PCL scaffold by using 3D printing technology and poly(lactic-co-glycolic-acid) (PLGA) nanofibers with a hybrid sheath core structure by using co-axial electrospinning technique. Subsequently, they fabricated this nanofiber membrane in two layers (electrospun PLGA/vancomycin/ceftazidime layer and a coaxially spun PLGA/BMP-2 layer). | [26] | |
Levofloxacin | Levofloxacin can inhibit bacterial helicase activity, which leads to the inability of DNA to replicate and synthesize properly, ultimately causing bacterial death. | Sadaba et al. produced poly (lactic acid) (PLA) scaffolds with 3D printing technology and subsequently added polydopamine-coated BaSO4 particles within the scaffolds and adsorbed levofloxacin in it. | [27] | ||
Minocycline | Minocycline can inhibit protein synthesis in bacteria. | Martin et al. utilized 3D printing technology to prepare a PLA scaffold and combined the scaffold with collagen, minocycline and bio-inspired citrate hydroxyapatite nanoparticles (cHA). | [28] | ||
NO | NO can play a bactericidal role by damaging DNA, proteins and lipids of microorganisms. | Kabirian et al. designed a 3D printed small-diameter vascular graft (SDVG) which was printed from polylactic acid and coated with blending of 10 wt% S-nitroso-N-acetyl-D-penicillamine mixed in a polymer matrix consisting of poly (ethylene glycol) and polycaprolactone to achieve controlled release of NO. | [29] | ||
Satureja cuneifolia | Satureja cuneifolia (SC) is a natural aromatic plant which is rich in phenolic compounds with antimicrobial activity, which are strongly oxidizing and can cause protein coagulation and destroy bacterial proteins thus exerting antimicrobial effects. | Ilhan et al. used 3D printing technique to make SA/PEG composite scaffold and loaded methanol extract of SC into it. | [30] | ||
Nanodiamonds | The active oxygen-containing groups on the surface of NDS promote their interaction with cellular components to quickly kill Gram-positive and negative bacteria and prevent bacterial adhesion. | Rifai et al. fabricated selective laser melting titanium (SLM-Ti) scaffolds by using 3D printing and selective laser melting (SLM), and applied nanodiamond (ND) coating on the scaffolds for functionalization modification. | [31] | ||
Chitosan |
|
Intini et al. used 3D printing technology to manufacture porous chitosan scaffolds with 200 μm inter-filament opening. | [32] | ||
Immunomodulation | Adrenocorticos-teroids | Dexamethasone |
|
Lee et al. designed a robust and biodegradable 3D tubular scaffold by the combination of electrostatic spinning technique (ELSP) and 3D printing technique, and subsequently loaded DEX onto this scaffold using a mild surface modification reaction of PDA, polyethyleneimine (PEI), and carboxymethyl β-cyclodextrin (βCD). | [33] |
Prednisolone |
|
Farto-Vaamonde et al. utilized two different ways to load prednisolone or dexamethasone into a 3D printed PLA scaffold. The first one is immersing the pre-printed 3D PLA scaffold in a prednisolone solution, which covers its surface with prednisolone and allows for rapid release to exert its antimicrobial properties. The second one is immersing the polylactic acid filament in dexamethasone solution to make the polylactic acid swells reversibly. | [34] | ||
Animal sources | Interleukin-4 |
|
Wang et al. used GelMA-Dextran (PGelDex) as bioink and incorporated both IL-4 loaded silver-coated gold nanorods (AgGNRs) and hMSCs. | [35] | |
Ac2-26 peptide | It can inhibit tumor necrosis factor-α (TNF-α) production in monocytes, inhibit NF-κB signaling of the proinflammatory pathway, and promote phagocytosis of neutrophils. | Xu et al. fabricated a polylactic acid/4-arm polyethylene glycol hydrogel (PCL@tetra-PEG) composite scaffold with the encapsulation of Ac2-26 peptide. | [36] | ||
Plant sources | Curcumin |
|
Chen et al. made mesoporous CS (MesoCS/curcumin) scaffolds with curcumin. MesoCS nanoparticles were first prepared using a template followed by dissolving turmeric as a stock solution in 0.5 M NaOH to various concentration and finally mixing the scaffolds at the same 0.4 mL/g liquid/powder ratio to make the scaffolds. | [37] | |
Isoflavones |
|
Sarkar et al. loaded three soy isoflavones (Genistein, Daidzein, and Glycitein) in a 5:4:1 ratio mimicking their original ratios in soy on 3D printed TCP scaffolds with pores. | [38] | ||
Quercetin |
|
Wang et al. fabricated layered micro/nano surfaces on the surface of Ti6Al4V implants using 3D printing technique, alkali heat treatment and hydrothermal treatment after deposition of titanium dioxide (TiO2) on this surface. Because of the excellent ability to chelate metal cations of quercetin, it can be adsorbed as a monomer on TiO2, effectively creating a quercetin coating on the surface of the 3D printed Ti6Al4V implant. | [39] | ||
Regulation of collagen deposition | Collagen | Different types and ratios of collagen deposition play different roles in different periods of wound repair. | Martin et al. utilized 3D printing technology to prepare a PLA scaffold and combined the scaffold with collagen, minocycline and bio-inspired citrate hydroxyapatite nanoparticles (cHA). | [28] | |
Extracellular Matrix | Extracellular matrix is mainly composed of various components such as collagen, non-collagen, and elastin, and collagen as the main component can not only give the extracellular matrix the function of directly regulating collagen deposition, but also avoid the degradation and shrinkage process caused by a single collagen. | Kim et al. used S-dECM bioink to print and fabricate 3D pre-vascularized skin patches for wound healing with infusion of ASCs and EPCs. | [23] | ||
Silk fiber | As one of the filamentous proteins, Antheraea assama SF can improve cell fate and promote ECM secretion owing to its Arg-Gly-Asp (RGD) content. | Bandyopadhyay et al. mixed a blend of SF from mulberry (Bombyx mori) and non-mulberry (Antheraea assama) silk with gelatin as inks for 3D bioprinting to simulate the extracellular microenvironment of the meniscus. Subsequently, EDC and NHS were chemically cross-linked to enhance their stability and mechanical strength. | [40] | ||
Curcumin | Curcumin has the function of inhibiting the NF-κβ signaling pathway, thus promoting osteoblast differentiation and the secretion of ECM. | Bose et al. fabricated a PCL-PEG+curcumin-coated TCP scaffold using 3D printing technology. | [41] | ||
Granulocyte colony-stimulating factor | As an anti-inflammatory protein, endometrial stem cell-derived G-CSF can reduce scar formation by reducing Gli2 protein expression levels to regulate collagen deposition and reduce endometrial fibrosis. | Wen et al. made G-CSF-loaded slow-release microsphere (G-CSF-SRM) hydrogel scaffolds with 3D printing technology. | [42] | ||
Polyvinylidene fluoride | Polyvinylidene fluoride (PVDF) has excellent piezoelectric properties, biocompatibility, thermal stability and resistance to chemical irritation. Electricity generated by piezoelectric materials can reverse the effects of the gradual weakening of bioelectric stimulation with wound healing which may cause disruption of gene regulation, leading to downregulation of the wound healing cascade and eventually disorganized deposition of collagen fibers and abnormal remodeling of the ECM. | Liang et al. fabricated a novel ZnO nanoparticle-modified PVDF/SA piezoelectric hydrogel 3D scaffold (ZPFSA). The incorporation of SA precisely reduces the hydrophobicity of PVDF and creates the possibility of preparing hydrogels from its 3D printing. | [43] |
2. Vascularization
Good vascularization and vascular recanalization is crucial for the repair sites because blood vessels are vital to tissue repair [44,45]. Blood vessels can provide sufficient oxygen and nutrients and carry away metabolic wastes [46,47,48,49]. Therefore, the purpose of 3D printed scaffolds is to encourage vascular regeneration, which leads to in-tissue repair and regeneration. The details to make scaffolds are given below.
2.1. Growth Factors
In recent years, growth factors are being widely noticed. Specific cell receptors respond differently after being stimulated by growth factors [50,51]. Adding growth factors to the 3D bioprinting process can stimulate cell proliferation and differentiation, thus increasing cell activity and increasing the success rate of 3D bioprinting [52]. The activity of endothelial cells is additionally crucial for successful vascularization. The process of endothelium-mediated angiogenesis is complex and is impacted by multiple growth factors. Understanding the function of various growth factors and their methods for promoting angiogenesis is crucial for tissue repair. The growth factors that used in 3D bioprinting for vascularization such as vascular endothelial growth factor (VEGF) are listed below.
2.1.1. VEGF
VEGF is a vascular endothelial cell-specific heparin-binding growth factor that can induce vascular neogenesis in vivo and is a highly conserved homodimeric glycoprotein with a high specificity for cell mitosis. In vivo, VEGF induces endothelial cell proliferation, promotes cell migration, and inhibits apoptosis. In contrast, VEGF-induced angiogenesis with increased vascular permeability plays a critical regulatory role in the generation of blood vessels [53,54]. Both the short half-life of VEGF and the lack of a suitable long-term sustained release device make it difficult to ensure effective angiogenesis as well as raise waste and safety issues [3]. Therefore, it is necessary to select a suitable controlled delivery system.
Encapsulation of growth factors into microspheres before incorporating into 3D printed scaffolds was shown to be one of the most effective ways to achieve controlled release [55,56]. Wang et al. [16] made bone morphogenetic protein-2 (BMP-2) and VEGF adsorbed onto silk fiber (SF) microspheres (diameter of 1.5 ± 0.3 μm) that were prepared using a co-flow capillary device. These microspheres were, subsequently, doped into the SF/nano-hydroxyapatite (nHAp) scaffolds to provide regulated release. As shown in Figure 1, BMP-2 and VEGF are incorporated into SF microspheres by chemical covalent bonding via EDC/NHS (1-ethyl-3-(3-(dimethylamino) propyl) carbodiimide (EDC) and N-hydroxysuccinimide (NHS)) chemistry and physisorption, respectively, which leads to the controlled and sustained release from the SF/nHAp scaffold. The initial rapid release of VEGF mimics its expression during the early bone healing phase and promotes angiogenesis. The comparatively gradual and continuous release of BMP-2 facilitated osteogenic differentiation both in vitro and in vivo.
After 12 weeks of inserting the printed scaffold into the rat cranial defect location, a CD31 staining experiment showed that blood vessels were identified as brown, round, or oval structures. Compared with control or BMP-2 scaffolds, scaffolds that were loaded with VEGF showed a much higher blood vessel density, and the VEGF group exhibited the strongest signal among all groups. These findings suggested that the scaffolds that contained VEGF help vascularization. Furthermore, compared with BMP-2 or VEGF alone, the combination of BMP-2 and VEGF produced a synergistic effect on bone formation in rat cranial defects with good scaffold angiogenic properties and better osteogenesis, since vascularization is crucial for bone regeneration [57,58].
2.1.2. FGF-2
Fibroblast growth factor-2 (FGF-2) is a multifunctional peptide that promotes the growth, migration, and differentiation of many cell types [59]. FGF-2 was also shown to stimulate VEGF expression, granulation tissue formation, and vascular maturation [60,61]. Xiong et al. [17] used 3D printing to fabricate a gelatin-sulfonated silk composite scaffold (3DG-SF-SO3-FGF). The basic FGF-2 was incorporated in this scaffold by binding with a sulfonic acid group (SO3). SF has good biocompatibility, mechanical properties, stability, and non-inflammatory response and can be used as a repair for skin, bone, blood vessels, and other tissues [62,63,64]. Modified SF with SO3 was used in this scaffold to increase its hydrophilicity and can promote the binding of FGF-2. The in vitro release profile of FGF-2 from 3DG-SF-SO3-FGF scaffold showed that a 32% burst release was detected during the first 24 h, followed by a sustained slow release profile. A total of 30% of the FGF-2 remained in the stent after 12 days. Then, 4 weeks after implantation, skin wounds of rats showed significantly enhanced regeneration of dermatomal tissue due to the addition of FGF-2. Further investigation showed that a more extensive distribution of vascular recanalization was observed in the scaffold group with FGF-2 binding. Additionally, immunohistochemistry showed a significant increase in the expression of vascular-associated proteins such as α-smooth muscle actin (α-SMA) and CD31. These results demonstrate the importance of FGF-2 in recruiting endogenous cells for epithelialization and angiogenesis at defective sites.
2.1.3. PDGF
Some other growth factors were found to promote angiogenesis, e.g., platelet-derived growth factor (PDGF), which can recruit smooth muscle cell (SMC)/pericytes to immature vessels to stabilize and remodel them [65]. The deficiency of this factor will lead to the maintenance of a proliferative endothelial cells (ECs) phenotype, which is detrimental to maturation and even causes vascular degeneration. Currently, there are few experiments in applying them alone to 3D printing technology for tissue regeneration and angiogenesis.
2.2. Heparin and Its Derivatives
Heparin is a negatively charged polysaccharide macromolecule that has good affinity for angiogenic factors. Nih et al. proved that it can accelerate neovascularization by binding angiogenic factors, such as VEGF, and improving their stability [66,67,68,69]. An et al. [18] coated poly-L-lysine (PLL) and heparin on the surface of 3D-printed hydrogel scaffolds, which were made from cross-linking of gelatin methacrylate (GelMA) and hyaluronic acid methacrylate (HAMA) via electrostatic interactions between PLL (positively charged) and heparin (negatively charged). Then, they were inoculated with hypoxia-inducible factor-1α (HIF-1α) mutated muscle-derived stem cells (MDSCs). At last, the scaffolds were implanted into the injured cavernous body of rabbits finally. After 4 months, the erectile and ejaculatory functions of rabbit’s penile corpus cavernosum were greatly improved. Additionally, compared with the non-heparin-coated group, the relative protein expression of angiogenic markers (VEGF, PDGF, and stroma cell-derived factor-1 (SDF-1)) was significantly increased in the heparin-coated group. Specifically, angiogenic factors produced by HIF-1αmutant MDSCs were accumulated on the scaffold surface by adsorption of heparin, which, subsequently, stimulated angiogenesis in vivo. The increase in neovascularization further promoted the recovery of erectile and ejaculatory function in the injured penile corpus cavernosum.
Heparan sulfate (HS), one of the heparin derivatives, is a linear polysaccharide of the glycosaminoglycan family, which can be synthesized by almost all animal cells [70]. It has good mechanical properties and thermal stability, and has a large number of binding sites for bioactive molecules. In addition, HS can not only protect growth factors from degradation by proteases [71,72], but it also promote the binding of growth factors to their receptors, thus promoting growth factor activity [73]. Jiang et al. [19] fabricated a scaffold with collagen and HS and implanted it at the site of traumatic brain injury in hounds. In situ hybridization (ISH) and immunofluorescence staining showed that HS-containing scaffold promoted vascular and nerve regeneration compared with the control group, and that micro-vessel formation may underlie tissue regeneration and nerve repair.
2.3. Ionic Composition
Many studies incorporated various ionic components with osteogenic, angiogenic, and other functions directly into scaffold materials to allow the controlled delivery, or to functionalize the scaffold surface, or to make scaffolds have specific biological functions [74,75,76]. In addition, most of these ions have some biological interactions with cells (e.g., promoting the expression of growth factors by endothelial cells, promoting cell migration differentiation and proliferation, etc.), and perform pro-vascularization functions via these interactions. Table 2 shows the role of the different ions in the hydrogel and briefly describes the mechanisms by which they function and how they are applied.
Table 2.
Ions | Function | Mechanism | Methodology | Reference |
---|---|---|---|---|
Silicon ion | Vascularization |
|
Use a novel calcium phosphate cement (CPC) as the basis for a scaffold that combined mesoporous silica (MS) with recombinant human bone morphogenetic protein-2 (rhBMP-2). | [77] |
Magnesium ion | Vascularization |
|
Fabricated Mg-doped β-TCP (Mg-TCP) scaffolds by 3D printing and sintering, in which MgO was mixed in different ratios. | [78] |
Make Ta-PDA-Mg scaffolds by doping Mg2+ on the surface of 3D printed tantalum scaffolds by using the surface adhesion ability of polydopamine. | [79] | |||
Immunomodulation |
|
Load magnesium ions in the form of Mg-MOF-74 into 3D bioprinted scaffolds to exert anti-inflammatory effects in combination with icariin. | [80] | |
Zinc ions | Antibacterial |
|
Made yttrium oxide-stabilized zirconium oxide (3Y-ZrO2) nanopowder into 3Y-ZrO2 ceramic by 3D printing, mold plasticity, and sintering. Then the ISO resin was uniformly coated onto the ceramic. Subsequently, ZnO nanosolution was dropped on this ceramic to finally produce ZnO-ISO bilayer modified ceramics. | [81] |
Copper ion | Vascularization |
|
Prepared a novel metal-organic framework, a β-tricalcium phosphate (Cu-TCPP-TCP) scaffold containing a copper coordinated tetrakis (4-carboxyphenyl) porphyrin (Cu-TCPP) nanosheet interfacial structure, by using 3D printing technology. | [82] |
Antibacterial |
|
Used 3D printing technology to prepare nanocomposites of medical grade polyamide 12 (PA12) with copper oxide (cuprous oxide) in different ratios. | [83] | |
Immunomodulation | Inhibit the activation of macrophages and suppress the synthesis and release of inflammatory factors. | Made Cu-BGC scaffolds by incorporating different concentrations of copper (0.781–25 mg/mL) into bioactive microcrystalline glass using 3D printing technology. | [84] | |
Regulation of collagen deposition | Upregulate hypoxia-inducible factor-1 (HIF-1) expression and stimulates the expression of SOX-9, which leads to increased levels of COL II and ACAN expression. | Fabricated Cu-BGC scaffolds by doping different concentrations of copper (0.781–25 mg/mL) into bioactive microcrystalline glass with 3D printing technology. | ||
Silver ion | Antibacterial |
|
Silver is mainly used in the form of metallic silver nanoparticles (AgNPs). Designed a superporous polyacrylamide (PAM)/Hydroxypropyl Methyl Cellulose (HPMC) hydrogel with antibacterial ability by using silver-ethylene interactions and 3D printing technology. |
[85] |
2.3.1. Silicon Ions
Silicon (Si) is one of the essential elements for the development of healthy bones and blood vessels [86,87,88]. It was demonstrated that the addition of Si ions may promote osteogenic differentiation of human bone marrow stromal cells (hBMSCs) [89], and play a significant role in enhancing angiogenesis of ECs [90,91]. Many researchers found that the expression of many factors related to angiogenesis (e.g., VEGF, kinase insert domain-containing receptor (KDR), and HIF-1α et al.) in vascular endothelial cells was significantly boosted under the stimulation of Si ions. In addition, in vitro migration, differentiation, and tubular formation of vascular endothelial cells were stimulated in the presence of Si ions. To better utilize the pro-vascularization and osteogenic functions of Si ions, Li et al. [77] used a novel calcium phosphate cement (CPC) as the basis for a scaffold that combined mesoporous silica (MS) with recombinant human bone morphogenetic protein-2 (rhBMP-2) to promote osteogenesis and angiogenesis. This bioactive mesoporous scaffold has well-interconnected macropores. Due to the inherent self-setting properties of calcium phosphate cements, the scaffolds can be printed at room temperature without sintering afterwards and have enhanced mechanical strength. This study showed that more newly formed vessels could be observed in the MS/CPC group compared to the CPC-only group. As seen in Figure 2, the micro-computerized tomography (μCT) results of the rabbit radius—4 weeks after stent implantation—showed that abundant blood vessels formed around the CPC-only stent, and no blood vessels were observed inside the stent. The MS/CPC and MS/CPC/rhBMP-2 stents not only had abundant blood vessels around the stent, but the blood vessels also grew along the interconnected macropores inside the stent. This suggests significant promotion of vascularization by Si ions. However, this study did not delve into the mechanism of Si ions on promoting neovascularization, and so, further studies are needed in this area.
2.3.2. Magnesium Ions
Magnesium (Mg) is one of the essential elements of the human body and is associated with many physiological activities [92,93]. Compared to other metallic or polymeric materials, Mg can promote vascular growth and improve local blood perfusion [94,95], they also play a direct and important role in maintaining vascular function [96], especially for vascular endothelial cells. It is well known that vascular endothelial cells play an irreplaceable role in angiogenesis and that capillary branching, germination, and proliferation are dependent on them. It was shown that magnesium ions stimulate the proliferation of HUVEC and increase their response to some motogenic factors. In addition, Mg ion can also upregulate integrin function, which is one of the reasons why it can promote endothelial cell migration [94,95]. In addition, Mg ions were also demonstrated to have the ability to promote new bone formation and bone growth [97,98].
Gu et al. [78] fabricated Mg-doped β-TCP (Mg-TCP) scaffolds by 3D printing and sintering, in which MgO was mixed in four groups at 0, 1, 2, and 4 wt% ratios. β-TCP, as one of the commonly used biomaterials for scaffold preparation, has excellent biocompatibility and biodegradability, and its composition is also similar to that of natural bone minerals [99]. Endothelium-derived nitric oxide (NO) was used as an index to evaluate the angiogenic capacity. In vitro experiments showed that the 1Mg-TCP group produced the most NO compared to the other groups of human umbilical vein endothelial cells (HUVECs) cultured in extracts. This indicated that Mg2+ had the strongest angiogenic capacity at this dose, but the specific correlation between the high and low angiogenic capacity and Mg2+ dose was not elucidated.
Due to the inherent properties of some scaffolds, Mg2+ can’t be immobilized on its inner and outer surfaces uniformly. Therefore, it should rely on other substances to assist in immobilization, such as polydopamine (PDA). Inspired by mussel adhesion, PDA is able to hold onto almost anything and was extensively studied in many surface-modification experiments [100,101]. Ma et al. [79] used the surface adhesion ability of PDA to make Ta-PDA-Mg scaffolds by doping Mg2+ on the surface of 3D printed tantalum scaffolds. Then, Mg(NO3)2 was added to the surface of the scaffolds at doses of 0, 10, 20, and 50 mg, and the four groups of scaffolds were named Ta-PDA, Ta-PDA-Mg1, Ta-PDA-Mg2, and Ta-PDA-Mg3, respectively. The results showed that the constructed Ta-PDA-Mg scaffold promoted osteogenic and angiogenic responses in vitro and in vivo compared with the control group. In particular, Ta-PDA-Mg2 is the most effective (not Ta-PDA-Mg3), and immunofluorescence showed more mature angiogenesis in this group.
There is no doubt that Mg2+ promotes blood vessel regeneration, but high concentrations of Mg2+ may have the opposite effect [78,79]. The decreased angiogenic capacity may be related to the decrease in cell viability caused by high concentrations of Mg2+, but most experiments did not involve further studies. In addition, there are few reports on the relationship between the expression of angiogenesis-related genes in endothelial cells and Mg2+ concentration.
2.3.3. Copper Ions
Copper (Cu) is one of the indispensable trace elements for human beings, and the appropriate amount of Cu2+ is very important for maintaining health [82]. In addition, Cu2+ can stimulate endothelial cell proliferation and differentiation. They promote angiogenesis by mimicking hypoxia, stabilizing the expression of HIF-1α, and promoting the expression of VEGF [102,103,104]. Tao et al. [82] fabricated a novel metal-organic framework, a β-tricalcium phosphate (Cu-TCPP-TCP) scaffold containing a Cu2+ coordinated tetrakis (4-carboxyphenyl) porphyrin (Cu-TCPP) nanosheet interfacial structure, by using 3D printing technology. Cu-TCPP belongs to the family of metal organic frameworks (MOFs). MOF-based materials can be used for tumor therapy by converting infrared light into thermal energy in the biomedical field [105,106]. It turned out that Cu-TCPP-TCP scaffold supported the attachment of hBMSCs and HUVECs. It also significantly stimulated the expression of genes related to osteogenic differentiation in hBMSCs and angiogenic differentiation in HUVECs. Studies in vivo revealed that after implantation of the Cu-TCPP-TCP scaffold into femoral defects in rabbits, the scaffold effectively promoted regeneration of the femur. So, Cu2+-stimulated angiogenesis is essential for the formation of new bone tissue and plays an important role in determining the success or failure of implanted bone tissue grafts [107]. In conclusion, osteogenic bioactivity of the TCP scaffold, photothermal properties of Cu-TCPP nanosheets, and angiogenic activity of Cu2+ all enable the multifunctional properties of the Cu-TCPP-TCP scaffold.
2.4. Vascular-Promoting Cell
2.4.1. Human Umbilical Vein Endothelial Cells
HUVECs are one of the stem cells derived from umbilical cord tissue who play an important role in angiogenesis that can prevent the need for pre-formed channels or growth factor-induced angiogenesis [108]. It is one of the most popular endothelial cell lines and is widely used to study, thanks to low cost, ease of isolation, and strong angiogenic potential [109]. Cidonio et al. [110] fabricated a 3D scaffold printed with a bioink based on Laponite (LAP) nanoclay and, subsequently, seeded with human umbilical vein endothelial cells and loaded with VEGF. LAP nanoclay, the nanocomposites, can be used as a bioink to make hydrogels to maintain cell activity and create functional 3D implants [111]. Seven days after implantation of the scaffold into the chick chorioal lantoic membrane (CAM), the 3D-printed scaffold, which was equipped with VEGF and HUVECs, was extensively bound to the CAM. In addition, neovascularization penetrated the pores of the printed structures with numerous capillaries around the scaffolds. Moreover, the combination of VEGF and HUVECs had a significantly enhanced effect compared to the individual loading VEGF or HUVECs. This suggests that the interaction of VEGF and HUVECs can be mutually optimized to reduce vascular leakage caused by excessive stimulation of vascular permeability by VEGF [112].
2.4.2. Mesenchymal Stem Cells
Mesenchymal stem cells (MSCs) are a group of adult stem cells of mesodermal origin that can be derived from the placenta, liver, bone marrow, umbilical cord blood, adipose tissue, and heart [113]. MSCs in adult tissues often work as progenitor cells because they are highly proliferative and can differentiate into specific lineages, such as bone cells, endothelial cells, etc. They are considered to be one of the most appropriate cell sources for tissue engineering [114,115].
Although it was demonstrated that cartilage tissue, printed with bioink that contains MSCs, is well-vascularized in vivo because of its capability to secrete a variety of vascular growth factors such as VEGF, FGF-2, and PDGF et al., angiogenesis is often limited in peripheral areas, with no persistent vascularity in the core area of the cartilage [116]. Since angiogenesis plays a crucial role in bone regeneration [21,107,117], it is important to design a 3D-printed scaffold with a controlled internal structure that can guide the repair and vascularization of the core region within the cartilage. Daly et al. [118] used Pluronic ink as a sacrificial bioink to form a network of interconnected microchannels within a GelMA hydrogel, which was filled with MSCs to ensure vascularization of the core region. Four weeks after implantation of the scaffold with microchannel into the bone defect, μCT angiography showed a significant increase in the level of vascularization in the core region of the defect. This design provides the possibility to solve the difficulty of blood vessel formation within cartilage and other tissues.
In addition, a system of co-culture of osteoblasts and angiogenic cells was proposed, which can achieve complementary osteogenesis and angiogenesis [119]. For example, Rong et al. [120] chose induction media to co-culture bi-directionally induced human umbilical cord mesenchymal stem cells (hUCMSCs). HUCMSCs are one of the MSCs that originate from the umbilical cord of newborns. It can secrete cytokines which are related to processes such as inflammation, immune regulation, angiogenesis, and wound healing [121]. The os-hUCMSCs (osteogenically induced hUCMSCs) and en-hUCMSCs (angiogenically induced hUCMSCs) were pre-induced for 3 days before co-culture was performed. In co-culture, pre-induced os-hUCMSCs and en-hUCMSCs were mixed in different ratios and, subsequently, doped into 3D-printed TCP scaffolds. Loading the scaffolds into the defective part of rat skull for 4 weeks showed that the scaffolds had the best osteogenic ability in vitro and in vivo, where the ratio of os-hUCMSCs and en-hUCMSCs was 3:1. The higher ratio the mixed en-hUCMSCs was, the more vascular tubules were formed on the matrix gel. However, this experiment was performed to guide the clinical application of hUCMSCs by directly using human-derived cells in non-immunodeficient SD rats and without postoperative immunosuppression. So, this process will inevitably cause immune rejection. In addition, the genome and proteome of bidirectionally differentiated hUCMSCs need to be further investigated.
In addition to pro-vascularization properties, MSCs in hydrogels also possess immunomodulatory as well as regulatory collagen deposition capabilities. Table 3 lists the mechanisms by which HUVECs and MSCs function in hydrogels and briefly depicts the ways in which researchers have applied them to hydrogels.
Table 3.
Cells | Functions | Mechanism | Methodology | Merits | Reference |
---|---|---|---|---|---|
HUVECs | Vascularization | Prevent the need for pre-formed channels or growth factor-induced angiogenesis. | HUVECs was seeded in the Laponite (LAP) nanoclay with VEGF. | Low cost, ease of isolation, and strong angiogenic potential | [110] |
MSCs | Vascularization | Increase the expression of vascular growth factors. | A 3D-printed GelMA hydrogel scaffold with a controlled internal structure which was filled with MSCs. |
|
[118] |
Immunomodulation | Promote paracrine activity during inflammation and induce a shift from an M1-type phenotype to an M2-type phenotype in macrophages. | A scaffold which was composed by the aloe vera–sodium alginate (AV-ALG) hydrogel-coated endometrial mesenchymal stem cells (eMSCs) and 3D melt electrospun wire nets. | [122] | ||
Regulation of collagen deposition |
|
2.5. Other Materials
Some other additives were demonstrated to exert a certain degree of pro-vascularization.
2.5.1. Desferrioxamine
Desferrioxamine (DFO) is an iron chelator that can bind and assist in the removal of iron ions, and is often used as a hypoxia-mimetic compound under oxygenated conditions. HIF-1α, which is produced during hypoxia, acts as a cellular transcription factor, and was demonstrated to be essential for the regulation of genes related to angiogenesis and osteogenesis [123,124,125]. When DFO was activated, it would lead to the activation of a cascade of pro-angiogenic genes, such as VEGF. Thus, DFO can promote both angiogenesis and bone regeneration when used in fracture models [126,127,128]. Yan et al. [21] designed a bionic degradable polycaprolactone (PCL) scaffold using 3D printing technology. The printed PCL scaffold has macropore and multidirectional channel structure. PCL is one of the most commonly polymers that is used in 3D-printed scaffolds with good biocompatibility and biodegradability. It can control the release of DFO by surface degradation and layer-by-layer assembly techniques [129,130]. Results in vitro showed that the scaffold enhanced the angiogenic activity of HUVECs and the osteogenic activity of BMSCs. Studies in vivo indicated that after implantation of the scaffold at the site of femoral defects in rats, it enhanced rapid vascular invasion and accelerated osseointegration. Overall, DFO gave the scaffold consistent ability to promote angiogenesis and osteogenesis in vitro and in vivo. However, the sample size of this study was too small and a larger sample size is needed to validate the results.
2.5.2. Catalase
It was demonstrated that H2O2 is produced by cells in a hypoxic state and will contribute to an environment of oxidative stress and ischemia [131,132]. Catalase can break down hydrogen peroxide and produce oxygen, which not only reduces the damage caused by H2O2, but the oxygen that it produces also helps to induce angiogenesis [133]. Rija et al. [22] intercalated catalase in hydrogels to form functional decellularized adipose tissue-alginate (DAT-A) hydrogels using 3D printing technology. Figure 3 shows the abbreviated manufacturing process.
DAT was widely used in research and clinical applications due to its excellent biocompatibility and degradability. Its main components are collagen and sulfated glycosaminoglycans (GAG) containing hyaluronic acid (HA) [134,135]. In addition, DAT was shown to enhance the extracellular matrix (ECM) and cells, cell–cell interactions, and stem cell differentiation [136]. After implanting the scaffold subcutaneously in rats for 4 weeks, tissue growth increased at the implantation site (≥45%), inflammation reduced (≥40%), and induction in angiogenesis increased (≥40%), as compared to the control group. This demonstrated that the scaffold could successfully promote angiogenesis and tissue regeneration.
2.5.3. Decellularized Extracellular Matrix
Decellularized extracellular matrix (dECM) bioinks with rheological and gel are promising materials for generating functional human tissues [137]. During decellularization, some of the functions of the ECM are preserved, which facilitate the induced differentiation of pluripotent stem cells on dECM scaffolds into tissue-specific cell types [138,139].
In previous studies, various tissue-specific dECMs (fat, muscle, liver, cartilage, and blood vessels, etc.) were successfully fabricated into printable bioinks [134,140,141]. These successful examples enabled skin-derived decellularized extracellular matrix (S-dECM) to be attempted for the formulation of bioinks based on 3D cell printing for skin tissue engineering. Kim et al. [23] used S-dECM bioink to print and fabricate 3D pre-vascularized skin patches for wound healing with infusion of adipose-derived stem cells (ASCs) and endothelial progenitor cells (EPCs). The 3D-printed skin patches loaded with EPCs+ASCs showed a rapid pre-vascularization in vitro within 3 days. Immunofluorescence results after 3 weeks of implantation in mice revealed that wounds with implanted patches exhibited enhanced wound closure, neovascularization, and robust blood flow. In comparison to injection of EPCs + ASCs alone, 3D-printed skin patches using dECM bioink showed significant formation of CD31-positive blood vessels, thus promoting skin repair.
Extracellular matrix associated with cardiac tissues is also widely studied and used in 3D bioprinting today. For example, decellularized cardiac extracellular matrix hydrogel (cECM) is a promising biomaterial for myocardial repair, which can improve cardiac function and progenitor cell delivery [142]. Bejleri et al. [24] fabricated a 3D-bioprinted patch containing cECM for the delivery of pediatric cardiac progenitor cells hCPCs. The patch is printed with bioinks consisting of cECM, hCPCs, and GelMA. Compared to hCPCs grown in pure GelMA patches, the addition of cECM within patch results in a 30-fold increase in cardiogenic gene expression of hCPCs. As seen in the improved endothelial cell tube formation, the media from GelMA-cECM patches revealed an increased angiogenic potential (>2-fold) compared to the GelMA alone group.
Overall, the successful fabrication of vascularized tissue is key to tissue engineering. Still, it is difficult to create a tissue engineering scaffold that is recognized to be very effective in promoting vascularization. Among the many additives added to 3D-printed scaffolds, most of their pro-angiogenic mechanisms are related to vascular growth factors, especially VEGF, such as stimulating VEGF expression in various ways, enhancing VEGF activity, or binding to VEGF to enhance its stability, and so on. Although VEGF plays an irreplaceable role in vasculogenesis and angiogenesis, there are also many other factors or pathways that can contribute to pro-vascularization.
2.5.4. Angiogenic Peptides
Angiogenic peptides (AP) are synthetic peptides that are functionally equivalent to VEGF. AP and VEGF are known to bind to the same receptors to initiate angiogenesis. However, AP can be synthesized on a larger scale and is less expensive than VEGF, thus enabling greater use to promote angiogenesis [143]. Wang et al. [20] made a dual-delivery bone tissue engineering scaffold by low-temperature 3D printing of β-tricalcium phosphate and osteogenic peptide (OP) containing water/PLGA/DCM emulsion—and coating AP on the scaffold surface. After implanting the scaffold into a rat cranial bone defect model for 3 months, the scaffold not only induced an improvement in new bone formation but also a regeneration of blood vessels with larger diameters compared to the control group. The scaffold achieved the dual function of enhancing bone tissue regeneration and vascularization.
3. Antibacterial
Human skin and mucosal surfaces are covered by a variety of microbiota, which can be divided into two main groups—resident and transient flora. The resident flora consists of relatively fixed types of microorganisms, while the transient flora consists of non-pathogenic or potentially pathogenic microorganisms [144]. It was experimentally demonstrated that the most common bacterial species is Staphylococcus aureus (37%), followed by Pseudomonas aeruginosa (17%), Aspergillus (10%), and Escherichia coli (6%) [145]. The attachment of bacteria to the surface of various substances leads to the formation of biofilms, which allows bacteria to evade the action of antibiotics and causes immune responses [146] and various complications such as the failure of wound healing. In addition, if bacterial membranes adhere to medical implants, they can lead to the failure of the insertion, which can also result in a significant socio-economic burden [147,148]. Furthermore, because any implants will lack blood and lymphatic supply, they have low blood flow and oxygen delivery, making it difficult for leukocytes to exert antimicrobial action. Although many methods were designed to promote vascularization for normal immune surveillance, implants are still at risk of developing infected lesions until an adequate vascular supply is available [149,150]. Therefore, it is imperative to include materials with antimicrobial activity in stents to confer antimicrobial ability to prevent and mitigate infection in implanted stents. Although different substances have different antimicrobial mechanisms, they all show goodness in vivo and in vitro antimicrobial effects. Figure 4 enumerates the different additives incorporated in the hydrogel according to the different antimicrobial mechanisms.
3.1. Disruption of Bacterial Cell Membranes
3.1.1. Silver Ion
Silver (Ag) is widely used as an antimicrobial agent to prevent infections during wound healing. Today, silver is mainly used in the form of metallic silver nanoparticles (AgNPs). AgNPs were experimentally demonstrated to have antibacterial activity against bacteria, yeast, and fungi [151,152]. In a study, Ching et al. provided several possible antimicrobial mechanisms: (1) anchoring of AgNps on bacterial membranes leading to rupture of bacterial membranes and leakage of bacterial contents, resulting in bacterial cell death; (2) nanoparticles can penetrate into bacterial membranes and interact with biomolecules, resulting in bacterial dysfunction; (3) AgNps may catalyze the reduction in O2 to reactive oxygen species (ROS), leading to downregulation of antioxidant enzyme expression, DNA damage, and apoptosis [153]. Incorporating AgNPs into hydrogel matrices is by physical doping, but it will lead to rapid release of Ag+ into the surrounding environment [154,155].
To solve this problem and to exploit the antibacterial ability of Ag+, as we can see in Figure 5, Wu et al. [85] designed a superporous polyacrylamide (PAM)/Hydroxypropyl Methyl Cellulose (HPMC) hydrogel with antibacterial ability by using Ag+-ethylene interactions and 3D printing technology.
The Ag+-ethylene interaction plays an important role in the dispersion, release, and cross-linking of AgNPs in the hydrogel matrix and their cross-linking with the PAM network. Also, this interaction facilitates the cytocompatibility and antimicrobial activity of AgNPs cross-linked hydrogels and reduces the toxicity of Ag+. In addition, HPMC was chosen to be incorporated into the formed hydrogels, mainly due to high water absorption and retention properties [156]. It can confer a rapid water absorption rate to the hydrogel to facilitate the retention of more exudate, or extend its use to prevent surface drying of the wound [157]. Antimicrobial experiments in vitro showed that AgNPs cross-linked dressing showed a significant zone of inhibition against both Staphylococcus aureus and Escherichia coli bacterial colonies compared with the control group of hydrogel dressing containing HPMC and chitosan. Meanwhile, the wounds had smoother surface during healing and minimal scar morphology after 14 days of healing. Histological analysis indicated that the AgNPs cross-linked hydrogel dressing could inhibit the formation of scar tissue.
3.1.2. Photothermal Materials
To improve the antimicrobial properties of stents, photothermal therapy (PTT) attracted extensive interest from researchers as a promising antimicrobial method [158]. Due to its low side effects, deep tissue penetration, and rapid therapeutic effect, it was widely explored for use in the treatment of tumor and implant infections. However, since most photothermal agents do not have the ability to induce tissue regeneration, the development of photothermal agents should promote tissue generation and inhibit bacteria. Nie et al. [25] fabricated a personalized MXene composite hydrogel scaffold GelMA/β-TCP/sodium alginate (Sr2+)/MXene (Ti3C2) (GTAM) with both photothermal antibacterial and osteogenic capabilities using 3D printing technology. As a new class of transition metal carbide/nitride/carbon nitride, it has an ultrathin structure, excellent physicochemical properties, good biocompatibility, excellent near-infrared absorption and photothermal conversion efficiency, low toxicity, and good biodegradability [159,160]. Therefore, MXene was widely used in biomedical applications such as photodynamic therapy (PDT) [161], antibacterial [162], and drug delivery [163], etc. It was noted that MXenes can kill microorganisms such as Gram-positive and negative bacteria by disrupting bacterial membranes directly through physical contact [162,164], especially when supplemented with NIR irradiation for higher antimicrobial efficiency [165]. In vitro antibacterial experiments showed that the GelMA/β-TCP/sodium alginate (Sr2+) (GTA) scaffold did not have antibacterial properties, regardless of NIR light irradiation. Although the physical contact of GTAM had certain antibacterial activity, the antibacterial ability was relatively weak, and only the GTAM+NIR group had significant bacterial inhibitory ability. In vivo antibacterial experiments showed that the GTAM scaffold had effective photothermal conversion abilities, and its antibacterial activity was excellent against both G (+) and G (−) bacteria under 808 nm NIR irradiation. On the other hand, GTAM composite bioink was mixed with rat bone marrow mesenchymal stem cells (rBMSCs) and then 3D-bioprinted at low temperature. The scaffolds showed good biocompatibility and promoted the proliferation and differentiation of rBMSCs. The scaffold was implanted into the mandibular defect of rats, and the treatment results under 808 nm NIR irradiation revealed significant bacterial clearance and osteogenesis-promoting effects at the implantation site. In conclusion, this bifunctional 3D-printed composite hydrogel scaffold with both antibacterial ability and the ability to promote precise bone tissue remodeling and regeneration is a novel but very promising biomaterial.
3.2. Destruction of Bacterial Cell Walls
Vancomycin + Ceftazidime
Vancomycin belongs to a group of glycopeptide antibiotics, which can exert a strong bactericidal ability by inhibiting cell wall biosynthesis through specific binding to the dipeptide d-Ala-d-Ala (AA) at the end of bacterial cell wall precursors [166,167]. Additionally, Ceftazidime can inhibit bacterial peptidoglycan synthesis by inhibiting penicillin-binding proteins, leading to cell wall instability and inhibition of synthesis and cell death [168]. Yu et al. [26] incorporated the combination of two types of antibiotics (vancomycin and ceftazidime) into a 3D-printed scaffold to give the scaffold a sustained release of different antibiotics. They fabricated a mesh-like PCL scaffold by using 3D printing technology and poly(lactic-co-glycolic-acid) (PLGA) nanofibers with a hybrid sheath core structure by using co-axial electrospinning technique. Subsequently, they fabricated this nanofiber membrane in two layers, namely, an electrospun PLGA/vancomycin/ceftazidime layer and a coaxially spun PLGA/BMP-2 layer. After implantation of the scaffold into the femoral defect in rabbits, the drug release profile showed that in vivo release of both antibiotics from the PLGA nanofibers showed a similar trend: the drugs were released explosively on day 1, and the release concentration decreased on day 7 until day 28 when the drug release gradually increased and the release was maintained until day 42. The concentrations of both antibiotics remained well above the 90% minimum inhibitory concentration throughout the study period. BMP-2 also showed a release profile similar to that of the antibiotics. With the stimulation of the scaffold, an abundance of growth factors was induced within the bioactive membrane of the femur. Excellent bone healing ability was found in both radiological examination and biomechanical assessment. Mechanical properties tests showed that femurs in the PCL-PLGA/antibiotic group and the PCL-PLGA/antibiotic/BMP-2 group exhibited torsional strength almost identical to that of healthy femurs. However, the experiment still has some shortcomings: the bone defect model was not an infected bone defect model and the antimicrobial effect was assumed based on the detection of local antibiotic concentrations rather than a direct test of its antimicrobial performance in vivo or in vitro. Furthermore, despite the satisfactory osseointegration, it was unknown whether the antibiotic-loaded nanofibers would behave differently when encountering the healing of large human bone defects that are much more complex.
3.3. Inhibits Bacterial DNA Replication
Levofloxacin
Levofloxacin, one of the quinolone antibiotics, is a broad-spectrum antibiotic used in the treatment of bone infections to combat and prevent osteomyelitis, penetrate bone trabeculae and bone cortex, and minimize the risk of bacterial resistance [169]. It exerts its antimicrobial action mainly by inhibiting bacterial helicase activity, which leads to the inability of DNA to replicate and synthesize properly, ultimately causing bacterial death. Sadaba et al. [27] produced poly (lactic acid) (PLA) scaffolds with 3D printing technology and, subsequently, added PDA-coated BaSO4 particles within the scaffolds and adsorbed levofloxacin to impart antimicrobial properties to the scaffolds. Inorganic particle enhancers such as BaSO4 particles can improve the mechanical properties of the polymer and impart additional specific properties to the scaffold [170]. PDA is an adhesive that often acts as a substrate coating to be conjugated with biologically active materials, e.g., small molecule drugs and proteins, to anchor them to the scaffold surface. The PLA/PD-BaSO4 scaffold containing levofloxacin effectively inhibited bacterial growth on agar disks inoculated with Staphylococcus aureus, and a significant zone of inhibition was observed. Mechanical property analysis of the scaffolds revealed that the composite had simultaneously high stiffness, strength, ductility, and toughness, whereas in non-traditional polymer/inorganic composites, increases in stiffness and strength usually led to significant decreases in ductility and toughness. These advantages of levofloxacin-PLA/PD-BaSO4 demonstrate its potential for use in bone reconstruction applications.
3.4. Inhibit Bacterial Protein Synthesis
Minocycline
Minocycline, which is one of the semi-synthetic tetracycline, has broad-spectrum antimicrobial properties. It exerts its antibacterial effects by inhibiting protein synthesis in bacteria [171]. In addition, minocycline has anti-inflammatory, antioxidant, and anti-apoptotic effects [172]. Compared to common biomaterials, drug delivery platforms incorporating minocycline can promote cell adhesion and proliferation, cytoplasmic diffusion, etc. [172,173]. Martin et al. [28] utilized 3D printing technology to prepare a PLA scaffold and combined the scaffold with collagen, minocycline, and bio-inspired citrate hydroxyapatite nanoparticles (cHA) to finally obtain a multifunctional 3D-printed scaffold. Hydroxyapatite nanoparticles were added to the surface of the scaffold to mimic the composition of natural bone and positively modulate osteoblasts [28,174], so that the multifunctional scaffold structure was closer to the human bone structure. The scaffold has properties such as uniform macropores, adequate wettability, and excellent compressive strength. To evaluate the antibacterial properties of the scaffold, two different antibacterial tests were performed against S. aureus. The results of the agar disc diffusion test showed that the scaffold group with the addition of minocycline effectively inhibited the growth of bacteria, and formed a significant zone of bacterial inhibition. In addition, scanning electron microscopy (SEM) evaluated the effect of scaffolds on the activity of S. aureus biofilm formation. The surface of PLA-Col scaffolds was completely covered by S. aureus biofilm, while no staphylococci were detected on the surface of the scaffold group with the addition of minocycline. In addition, the response of hBMSCs to these scaffolds showed that the addition of cHA significantly stimulated the adhesion, proliferation, and osteogenesis-related gene expression of hMSCs. Overall, the PLA scaffolds obtained by 3D printing successfully combined desirable antibacterial/antibacterial biofilm properties with osteogenic properties. They also maintained morphological and mechanical properties similar to those of human bone, offering the possibility for further clinical trials.
3.5. Destruction of Biological Components within Bacteria
3.5.1. NO
NO is a natural molecule that plays an important role in inflammation, cell proliferation, angiogenesis, and wound healing [175]. In addition, NO can play a bactericidal role by damaging DNA, proteins, and lipids of microorganisms. If NO is released in a controlled manner for a long time, it can inhibit bacterial growth on the surface of biological materials [176]. Kabirian et al. [29] designed a 3D-printed small-diameter vascular graft (SDVG) with a NO releasing coating to implant the implant into a CAM. The CAM assay is a cost-effective, simple, and rapid method to assess the biocompatibility and angiogenic capacity of biomaterials and can even be used as a bioreactor [177]. The grafts were printed from polylactic acid and coated with blending of 10 wt% S-nitroso-N-acetyl-D-penicillamine mixed in a polymer matrix consisting of poly (ethylene glycol) (PEG) and PCL to achieve controlled release of NO. The NO release profile showed a burst release of NO on the first day of implantation, followed by a continuous release of NO within the normal physiological range for the next 14 days. The results of in vitro antimicrobial assays showed that the NO-releasing coating inhibited the growth of bacteria and formed a significant inhibition circle. The results of CFU counting method revealed that after 24 h of incubation, microorganisms were reduced by 99.99–100% in the presence of NO-releasing grafts, while bacteria in the control group proliferated stably. In addition, the NO-releasing grafts and control grafts were biocompatible in vitro and in vivo. Compared to controls, NO-releasing SDVGs greatly enhanced the proliferation of ECs and showed significant angiogenic potential in vivo. In conclusion, the NO-releasing 3D-printed SDVGs with accelerated healing and bactericidal properties are a very promising graft.
3.5.2. Natural Plants
The occurrence of antibiotic resistance and multidrug resistance in drug-resistant strains of bacteria reduced the success of traditional synthetic antibiotic therapy. So, a new alternative treatment method derived from natural herbs is an option [178]. Satureja cuneifolia (SC) is a natural aromatic plant with anti-Alzheimer’s, anti-diabetic, antioxidant, and anti-microbial properties [179,180]. In addition, it was experimentally demonstrated that SC is rich in phenolic compounds with antimicrobial activity, which are strongly oxidizing and can cause protein coagulation and destroy bacterial proteins thus exerting antimicrobial effects [181]. Ilhan et al. [30] used a 3D printing technique to make SA/PEG composite scaffold and loaded methanol extract of SC into it. The production of 3D-printed scaffold and tissue application of wound dressing are shown in Figure 6. Sodium alginate (SA) in the composite scaffold was all at 9% (w/v) concentration, while PEG was added at different concentrations of 1, 3, and 5% (w/v). Phenolic acids and flavonoids in the methanolic extract of SC were analyzed in previous studies. The results show that SC was able to express strong biological activity [182].
The 3D-printed scaffolds showed excellent antimicrobial ability, especially forming a significant inhibition circle around Staphylococcus aureus (Gram-positive bacteria), as they contained antimicrobial SC extracts. In addition, the scaffolds exhibited good biocompatibility and low cytotoxicity, and the incorporation of SC generated ideal porosity and mechanical properties of the scaffolds. In conclusion, the SA/PEG/SC 3D scaffold showed great potential for diabetic wound healing and bacterial infection and is expected to be an ideal tissue-engineered wound dressing.
3.5.3. Nanodiamonds
Nanodiamonds (NDS) are increasingly being applied in biomedicine, considering their ability to create a tunable surface [183], and good biocompatibility [184]. Nanodiamond, as an antimicrobial agent, attracted extensive research interest. Regarding its antimicrobial mechanism, the active oxygen-containing groups on the surface of NDS promote their interaction with cellular components to quickly kill Gram-positive and negative bacteria and prevent bacterial adhesion [185]. Nowadays, NDS are mostly incorporated into implants in the form of material coatings or films to function [186,187]. Rifai et al. [31] fabricated selective laser melting titanium (SLM-Ti) scaffolds by using 3D printing and selective laser melting (SLM), and applied nanodiamond (ND) coating on the scaffolds for functionalization modification. As one of the mostly used techniques for manufacturing metal implants, SLM technology often uses powdered metals bonded in a layer-by-layer process to create complex structures, using mainly stainless steel, cobalt-chromium, and titanium. The metals used are mainly stainless steel, cobalt-chromium, and titanium, among others, as they have good biocompatibility and mechanical stability. The concentrations of ND coated on the stent surface varied from 0.075, 0.75, to 7.5% w/v. The results of in vitro antimicrobial assays showed that after 18 h of growth of S. aureus attached to the uncoated and ND-coated stents, the stent group with the lowest ND concentration of 0.075% w/v had the most S. aureus attached, compared to the uncoated control group. After the ND concentration was increased to 0.75% w/v, the density of S. aureus was reduced by 50%, compared to the stent group with ND of 0.075% w/v. The highest ND concentration (7.5% w/v) group showed even an 88% reduction in S. aureus adhesion. SEM micrographs also confirmed that there was less S. aureus adhesion as the ND concentration increased. After inoculating human skin fibroblasts (HDF) and osteoblasts (OB) on four groups of scaffolds and culturing them for 3 days, the maximum HDF and OB cell densities were found on samples at the highest concentration of ND (7.5% w/v), with a 32% and 29% increase in density, respectively, compared to the control group. Overall, with the use of 3D-printed SLM-Ti in orthopedic implants, modifying its surface with ND provides a simple, rapid, and beneficial cell-implant interface.
3.6. Multi-Mechanism Antibacterial
3.6.1. Chitosan
Chitosan (CS) is a natural polysaccharide derived from deacetylation of chitin, and consists mainly of d-glucosamine and N-acetyl-d-glucosamine [188]. Chitosan is now widely used in biomedical applications, including tissue engineering, infection control, and wound healing [188,189]. Its hemostatic and antimicrobial functions can accelerate the transition from the hemostatic to the inflammatory phase after wound trauma and modulate the inflammatory response [190]. Its antimicrobial activity results from the interaction of the positive charge it carries with ions on the surface of negatively charged cells. Such activity disrupts bacterial cell membranes, prevents the transport of cellular material, increases the internal osmotic pressure, and causes the rupture of microbial cells, among other things. In addition, it interacts with bacterial DNA and prevents DNA transcription, thus inhibiting microbial ribonucleic acid (RNA) synthesis [191]. Intini et al. [32] fabricated a 3D chitosan scaffold and implanted it into the skin defects of diabetic rats. Twenty days after implantation, it was shown that the scaffold exhibited good biocompatibility and cytocompatibility. Both MTT assay and neutral red analysis showed that the chitosan matrix was non-cytotoxic. Seeded normal human skin fibroblast (Nhdf) and keratinocyte (HaCaT) cells were viable to grow and colonize the 3D chitosan matrix. An analysis of epidermal wounds in rats revealed that after 7 days, the wounds looked approximately 50% less than the initial area in both animals treated or untreated with chitosan scaffolds, with no significant difference between the two. After 10 days, the wounds treated with chitosan scaffolds had healed, while in the control animals, there was still crusting. After 14 days, the wounds were completely healed in all groups, with only scars visible. Overall, treatment with chitosan scaffolds improved and accelerated wound healing compared to untreated animals, and no signs of infection were observed, probably due to its inherent antimicrobial activity. Histological analysis of the wounds also showed that the chitosan group exhibited more intense tissue reorganization and more mature tissue formation on the wounds.
3.6.2. Zinc Ions
Zinc (Zn) ions, one of the chemical bactericides, have good antimicrobial activity and play an important role in tissue differentiation [192]. The antimicrobial activity of Zn particles was investigated and reported in numerous articles, but mostly in the form of Zn oxide nanoparticles [193,194,195]. Zn oxide nanoparticles are a potential broad-spectrum nano antibiotic to demonstrate their strong antibacterial properties against Escherichia coli [196], Staphylococcus aureus [197,198], and Klebsiella pneumoniae [199], etc. However, its antimicrobial mechanism is complex, and the antimicrobial effect exhibited may be the result of several different mechanisms acting together. For example, Li et al. [200] suggested that due to the negative charge of the bacterial film, an electrostatic reaction between the film and the oppositely charged ZnO nanoparticles leads to the rupture of the film eventually triggering bacterial death. It was also suggested that ZnO nanoparticles can release free Zn2+ to disrupt the internal ionic homeostasis of the bacterium and, subsequently, lead to the death of the bacterium. However, there is no unified conclusion on which mechanism is the main one.
Li et al. [81] used 3D printing and bilayer modification techniques to fabricate a 3D ceramic implant with excellent mechanical properties, broad-spectrum antibacterial, and anti-infective properties. They made yttrium oxide-stabilized zirconium oxide (3Y-ZrO2) nanopowder into 3Y-ZrO2 ceramic by 3D printing, mold plasticity, and sintering. The mechanical properties were enhanced by uniformly coating ISO resin onto the ceramic by a thermal spraying process at high temperature and pressure. Subsequently, ZnO nanosolution was dropped on this ceramic to finally produce ZnO-ISO bilayer modified ceramics [201]. Impact test, bending test, tensile test, and compression test of ISO resin modified ceramics showed that mechanical properties of ISO resin modified ceramics were significantly improved. In addition, the ISO resin did not inhibit the growth of Staphylococcus aureus and Escherichia coli. There was no significant difference in the number of bacterial colonies between the ISO resin-modified ceramic group and the unmodified ceramic group. However, the ZnO-ISO bilayer modified ceramics showed excellent antibacterial performance against both S. aureus and E. coli. There was almost no colony formation after treatment of bacteria with ZnO-ISO bilayer modified ceramics. Finally, 14 days after implantation of the bilayer-modified ceramics made by 3D bioprinting, the mice in both the experimental and control groups were normal, with no significant differences in all examinations. This indicates that the ISO resin material has excellent biocompatibility. This study successfully designed a 3D ceramic implant combining excellent mechanical properties and good antimicrobial properties through the bilayer modification technique. But its long-term effects in vivo and in vivo antimicrobial properties are still unknown.
3.6.3. Copper Ions
Copper (Cu) is one of the important elements involved in physiological processes in living organisms and can act as a cofactor for key metabolic enzymes [202,203]. In addition, Cu2+ was shown to have efficient antibacterial activity against various bacteria, including Staphylococcus aureus and Escherichia coli [204]. The mechanism may be that when Cu2+ is present as a free ion, it will generate highly toxic hydroxyl radicals from hydrogen peroxide and superoxide [205,206]. The generated hydroxyl radicals can oxidize with most bacterial macromolecules to exert antibacterial effects [207,208]. In addition, Cu2+ can be associated with affecting the bacterial outer membrane potential, leading to the rupture of the bacterial membrane, and eventually to bacterial death. Vidakis et al. [83] used 3D printing technology to prepare nanocomposites of medical grade polyamide 12 (PA12) with Cu2+ oxide (cuprous oxide) in different ratios (choosing 0.5 wt.%, 1.0 wt.%, 2.0 wt.%, 4.0 wt.%, and 6.0 wt.% weight ratio loading of cuprous oxide). Additionally, 3D printing technology, also known as additive manufacturing (AM) technology, was used in a wide range of these applications [209,210]. Fused filament fabrication (FFF), as one of the AM technologies, is based on thermoplastic polymers and/or composite materials [211,212]. The medical-grade PA12 material used in this experiment is often used as a matrix material, together with metal and oxide fillers in AM applications that require antimicrobial properties in 3D scaffolds [213,214]. In addition, PA12 is commonly used in 3D-printed tissue engineering experiments, as it has excellent toughness properties, the capability to extend extensively before fracture, and the excellent thermodynamic properties [215,216]. As shown in Figure 7 and Figure 8, after culturing the scaffolds in Petri dishes containing Gram-negative Escherichia coli and Gram-positive Staphylococcus aureus for 24 h, all groups showed good antibacterial activity. The group with a cuprous oxide ratio of 4.0 wt.% showed the highest antibacterial effect against both bacteria.
Other than the above antimicrobial materials and their antimicrobial mechanisms, many other materials can be used as scaffold additives to impart antimicrobial properties to 3D-printed tissue engineering. In conclusion, excellent antimicrobial properties of scaffolds are the prerequisite and foundation for scaffolds to implant and function in vivo, and more antimicrobial materials and different antimicrobial mechanisms can be applied in 3D printed tissue engineering scaffolds.
4. Immunomodulation
Immunomodulation refers to the physiological function of the body to recognize and exclude antigenic foreign substances, and maintain its own physiological dynamic balance and relative stability. It is often divided into humoral and cellular immunity, involving various immune cells, such as lymphocytes, macrophages, and NK cells. The immune regulation involved in tissue engineering repair is mostly anti-inflammatory, that is, the regulation of macrophage polarization. Macrophages are one of the main cells that regulate non-specific immune responses, and polarized macrophages play a very important role in inflammatory responses, injury repair, and angiogenesis [217]. Macrophages can be regulated to differentiate into two types—classically activated (M1 type) and alternatively activated (M2 type) [218,219]. M1 type macrophages can be activated by lipopolysaccharide (LPS), T lymphocyte-derived lymphokines, and cytokines involved in T cell-mediated immune responses [220]. After activation, they can secrete pro-inflammatory factors, recruit inflammatory cells against pathogens, and assume many important roles in the early stages of inflammation [221]. However, sustained M1-type activation can cause tissue damage and lead to inflammatory diseases. In contrast, M2-type macrophages are mainly activated by Th2 cytokines such as IL-4, IL-13, and prostaglandin E2, which are responsible for suppressing the inflammatory response and tissue repair effects to restore the tissue to its original state [222,223]. However, excessive activation of the M2 type, in turn, can cause excessive tissue repair and cause fibrosis, among other things. Therefore, finding substances that can balance the polarization of M1-M2 type macrophages is the key to the successful application of tissue engineering [224,225].
4.1. Adrenocorticosteroids
4.1.1. Dexamethasone
Dexamethasone (DEX) is a synthetic corticosteroid chemical that is commonly used clinically as an anti-inflammatory agent. It was shown to exert anti-inflammatory effects through various pathways, such as reducing the expression of cyclooxygenase 2 (COX-2). It inhibits prostaglandin production, inflammatory signaling, and neutrophil and macrophage exudation and aggregation to the site of inflammation to exert anti-inflammatory effects [226,227]. Although it was demonstrated that long-term administration of DEX can attenuate the tissue inflammatory response, there are significant side effects such as osteoporosis, gastrointestinal bleeding, and immunosuppression due to long-term systemic exposure to high concentrations of glucocorticoid drugs [228,229]. Therefore, constructing a hybrid scaffold by using 3D printing processing and adding DEX to the scaffold can be a good way to achieve a high dose in the target tissue and a low dose systemically, which can exert anti-inflammatory effects and reduce its side effects at the same time. However, since DEX is a lipophilic substance, its water solubility is low and it is not efficient when loaded into scaffolds [230,231]. Therefore, it is important to utilize a safe medium to load DEX more efficiently into scaffolds. Lee et al. [33] designed a robust and biodegradable 3D tubular scaffold by the combination of electrostatic spinning technique (ELSP) and 3D printing technique, and, subsequently, loaded DEX onto this scaffold using a mild surface modification reaction of PDA, polyethyleneimine (PEI), and carboxymethyl β-cyclodextrin (βCD). Carboxymethyl-βCD is a cyclic oligosaccharide with a hydrophilic outer surface and a central lipophilic lumen [232]. Therefore, carboxymethyl-βCD can form inclusion complexes with DEX, which not only allows massive loading of DEX, but also regenerates tracheal tissue after transplantation and has anti-inflammatory activity [233,234]. To introduce carboxymethyl-βCD, they used PDA and PEI chemical modifications to introduce an amine-rich surface on the PCL scaffold, thus allowing carboxymethyl-βCD to graft through amide bonds [235,236]. Compression tests of this composite scaffold demonstrated that the fabricated 3D tubular scaffold has stronger mechanical properties than natural rabbit tracheal tissue. In addition, atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS) analysis showed that the surface treatment of the scaffold was successful because a large amount of DEX was loaded onto the scaffold [232]. In addition, they quantified the amount of tumor necrosis factor-α (TNF-α) and IL-6 secreted by cells on RAW 264.7 cells before and after LPS treatment by ELISA. As shown in Figure 9, cells on the membrane expressed high amounts of TNF-α and IL-6 under LPS treatment. However, cells on PCLDPβ+DEX expressed significantly lower amounts of TNF-α and IL-6 than cells on PCL, suggesting that the DEX-containing scaffold exhibited significantly enhanced anti-inflammatory activity.
Four weeks after implantation of the stent at the tracheal defect in rabbits, the PCLDPβ stent loaded with DEX exhibited higher cell adhesion and stronger tracheal mucosa regeneration, and formed a more patent airway. In conclusion, this 3D tubular scaffold loaded with DEX has good potential for regeneration of tracheal tissue and anti-inflammatory effects, offering the possibility of future tracheal transplantation therapy.
4.1.2. Prednisolone
As one of the adrenocorticosteroids, prednisolone and DEX have similar anti-inflammatory effects. prednisolone can inhibit the accumulation of inflammatory cells (including macrophages and leukocytes) at sites of inflammation, and their phagocytosis. Furthermore, it can prevent the release of lysosomal enzymes, and the synthesis and release of chemical mediators of inflammation. Farto-Vaamonde et al. [34] utilized two different ways to load prednisolone or DEX into a 3D-printed PLA scaffold. The first one immerses the pre-printed 3D PLA scaffold in a prednisolone solution, which covers its surface with prednisolone and allows for rapid release to exert its antimicrobial properties. The second one immerses the polylactic acid filament in DEX solution to make the polylactic acid swells reversibly. The melting of the polylactic acid during the subsequent 3D printing process helps the effective integration of DEX in the printed filament. It can also achieve continuous slow release for osteoinduction. These two loading methods offer the possibility to generate different drug concentration gradients in the same scaffold and allow different drugs to exhibit different release patterns. The ability of the scaffold to attenuate the inflammatory response was tested by macrophages stimulated with LPS. The blank scaffolds did not attenuate the levels of PEG2 and TNFα, which were similar to those of the positive controls (positive control refers to stimulated macrophage cells). Differently, all scaffolds surface loaded with prednisolone caused a significant decrease in PEG2 and TNFα levels, as effective as free drug dispersed in cell culture medium (ANOVA p < 0.001; multiple range test p < 0.05). By contrast, scaffolds loaded with DEX did not significantly change the inflammatory response. In addition, all scaffolds showed good biocompatibility with fibroblasts, macrophages, and hMSCs, and loading of various drugs did not impair the printability or mechanical properties of the scaffolds.
4.2. Metal Ions
4.2.1. Copper Ions
Copper is one of the essential trace elements and plays an essential regulatory role in the maintenance of physiological homeostasis [237]. In addition to the previously mentioned pro-vascularizing and antibacterial effects, Cu is also important in immune regulation. Many studies demonstrated the positive role of Cu2+ in the fight against arthritis, and Cu2+ deficiency decreases bone strength and increases the incidence of osteoarthritis [238,239]. The mechanism is that Cu2+ plays an important part in regulating the polarization of macrophages. It can inhibit the activation of macrophages and suppress the synthesis and release of inflammatory factors [240]. Lin et al. [84] made Cu-BGC scaffolds by incorporating different concentrations of Cu2+ (0.781–25 mg/mL) into bioactive microcrystalline glass using 3D printing technology. After attaching chondrocytes to the scaffold for 12 h, a significant increase occurred on the proliferation of chondrocytes in the Cu-BGC group, as compared to the BGC group and the blank control group. After detecting the HIF pathway using RT-qPCR analysis, the expression level of HIF-1α was significantly enhanced in the Cu-BGC group after 3 days of incubation in ionic extracts, as compared to the other two groups. The relevant genes and HIF-1α genes were subsequently examined in chondrocytes cultured under different concentrations of Cu2+. The final results showed that Cu2+ ions released from the Cu-BGC scaffold played an important role in promoting chondrocyte proliferation and differentiation and activating the HIF pathway for cartilage repair. Subsequently, the immunomodulatory effect of the scaffold was evaluated by studying the expression of inflammatory cytokines and macrophage surface markers. The results showed that on days 1 and 3, the expression of pro-inflammatory cytokine genes was suppressed and that of anti-inflammatory cytokine genes was increased in macrophages cultured with Cu-BGC ionic extract at a range of concentrations (0.781–25 mg/mL), as compared to the BGC and CTR groups. In addition, the expression of M1 surface marker (iNOS) was significantly suppressed and the expression of M2 surface marker (CD206) was significantly enhanced in macrophages of this group. All these results suggest that the ionic extract of Cu-BGC can promote the shift of macrophages from a pro-inflammatory M1 phenotype to an anti-inflammatory M2 phenotype. Finally, the scaffold was implanted into the cartilage defect on the femoral condyle of rabbits, and in vivo histological studies also showed that the Cu-BGC scaffold group significantly improved cartilage regeneration and enhanced the recovery of the osteochondral interface. Overall, the Cu2+, released from this Cu-BGC scaffold, triggered the immune response and suppressed the inflammatory response in osteochondral tissue—by activating the HIF signaling pathway, reducing damage to cartilage tissue, and promoting chondrocyte proliferation and maturation. This may provide a way to prevent and treat osteoarthritis associated with osteochondral defects in the future.
4.2.2. Magnesium Ions
Mg ions are one of the main ions important for maintaining normal physiological functions in humans, and they serves as a cofactor for more than 300 enzymes to play a vital role in regulating the physiological functions of the heart and nerves, and regulate blood pressure and immune regulation [93,241,242]. It was demonstrated in many studies that nuclear factor-κB (NF-κB) is a central regulator of inflammation-induced cytokine production. Also, IκBα shares an activation pathway with NF-κB. Mg2+ increase IκBα levels, but lead to reduced NF-κB activation and secretion of cytokines such as interleukin-6 (IL-6) and tumor necrosis factor α [243,244,245]. In addition, it was also found that the Notch1 pathway promotes inflammatory macrophage polarization [246,247], and the interaction of Mg2+ and Icariin can synergistically inhibit Notch1 protein expression to exert anti-inflammatory effects. Wang et al. [80] fabricated porous, 3D, Ti6Al4V scaffolds (PT) and placed them in a 72-well plate. The solutions were prepared: (a) 5 wt.% SF aqueous solution, (b) 1 mg/mL icariin in 5 wt.% SF aqueous solution, (c) 4 mg/mL Mg-MOF-74 in 5 wt.% SF aqueous solution, and (d) 4 mg/mL ICA@MOF in 5 wt.% SF aqueous solution. The four solutions were slowly injected into the PT in the 72-well plate until the PT was completely submerged by the solution. Finally, four groups of samples were achieved: (a) PT/SF (Ti/SF); (b) PT/SF/MOF (Ti/SF/MOF); (c) PT/SF/icariin (Ti/SF/I); (d) PT/SF/ICA@MOF (Ti/SF/MOF/I). Icariin was demonstrated to induce the differentiation of monocytes into macrophages and can function as an inhibitor of the NF-κB signaling pathway through upregulation of the PI3K/Akt pathway, thereby significantly inhibiting the release of pro-inflammatory cytokines such as IL-6 and TNF-α [248,249]. Furthermore, MOFs that are incorporated in scaffolds have excellent drug delivery capabilities due to their excellent chemical properties, biodegradability, and high porosity [250]. MOF-74, one of the MOFs, has low cytotoxicity and controlled drug release properties and can be used as a drug release platform [251]. To further verify the polarization of macrophages, immunofluorescence staining was used to monitor iNOS (green, M1 marker) and Arg-1 (red, M2 marker) in Raw264.7 cultured for 4 days. The results showed that the majority of macrophages in the Ti/SF group were of M1 phenotype (green). M2-type macrophages dominated (red), especially in the Ti/SF/MOF/I group. This was mainly due to the release of a certain concentration of Mg2+ in the MOF of this group. Although the concentration of icariin was higher in the Ti/SF/I group, its anti-inflammatory effect was weaker than that of the Ti/SF/MOF/I group, probably because icariin has an optimal concentration and too high concentration may cause cytotoxic side effects and waste of resources, etc. Subsequently, they examined the expression content of Notch1 protein in each group using cellular immunofluorescence and Western blotting. Figure 10 shows that the level of Notch1 protein in the Ti/SF/MOF/I group containing ICA@MOF was significantly lower than the other three groups.
Overall, the Ti/SF/MOF/I group had the highest M2 macrophage intensity and the lowest Notch1 protein expression level, which was mainly due to the synergistic immunomodulatory effects of Mg2+ and icariin released continuously from SF/ICA@MOF. In addition, they implanted the composite PT scaffold into the distal femoral medulla of osteoporotic rats and showed abundant new bone formation at both the peripheral and internal sites of the implantation site. The scaffold had good mechanical properties and biocompatibility, which significantly improved bone metabolism and promoted osseointegration. The scaffold greatly exerted anti-inflammatory effects and significantly improved osteoporotic integration using the sustained controlled release of icariin and Mg2+ from MOFs, offering the possibility of clinical practice for titanium prostheses in patients with osteoporosis.
4.3. Animal Sources
4.3.1. Interleukin-4
Interleukin-4 (IL-4) is one of the cytokines of the T helper (Th2) family of cells [252]. The activation of the typical pathway of IL-4 production causes phosphorylation of STAT6 and upregulation of GATA-binding protein 3 (GATA3) expression [253], which, in turn, constitutes a major factor in the transcriptional regulation of Th2 cells. Therefore, IL-4 can activate the production of Th2 cytokine and, thus, promotes the polarization of M2-type macrophages. In addition, IL-4 has the ability to antagonize the Th1-driven pro-inflammatory immune response, as evidenced by the downregulation of the synthesis of pro-inflammatory cytokines such as IL-10 and TNF-α [254] and the inhibition of pro-inflammatory chemokines [255]. Therefore, IL-4 was used in 3D-printed tissue engineering due to its excellent immunomodulatory ability. Wang et al. [35] used GelMA-Dextran (PGelDex) as bioink and incorporated both IL-4-loaded Ag-coated gold nanorods (AgGNRs) and hMSCs to confer anti-infective and immunomodulatory functions to the scaffold. Subsequently, to verify the immunomodulatory efficacy of IL-4, they performed an inflammation-inducing treatment of the bioink with IFN-γ and LPS. After 24 h of incubation, qRT-PCR analysis showed a significant decrease in M1 macrophage markers and a significant increase in M2 macrophage markers in the IL-4 and IL-4+MSC groups, as compared to the control group. The results suggested that bioink loaded with IL-4 and MSCs successfully polarized M1 macrophages to M2 type and exerted anti-inflammatory effects. There were many studies demonstrating the possible therapeutic inflammatory and immunomodulatory functions of MSCs [256], but their specific intrinsic molecular pathways and mechanisms of action are still under further investigation. Overall, they loaded two functional agents, namely IL-4@AgGNRs and MSCs, in the hydrogel. AgGNRs have the ability to eliminate the infection. Additionally, the synergistic effect of IL-4 and MSCs could induce the polarization of macrophage phenotype from M1 to M2 phenotype. Ultimately, a composite scaffold was made with simultaneous antibacterial, anti-inflammatory, and cytoarchitectural properties.
4.3.2. Mesenchymal Stem Cells
The function of MSCs in the immune regulation in tissue repair was demonstrated in various disease models [257,258]. However, their specific intrinsic anti-inflammatory molecular mechanisms are still under investigation due to their complex and diverse cell composition. It was suggested that it can act as a modulator of the inflammatory response, with paracrine activity being markedly promoted during inflammation [257]. It can result in the secretion of large amounts of cytokines and factors that induce a shift from an M1-type pro-inflammatory phenotype to an M2-type anti-inflammatory phenotype in macrophages [259], and a reduction in the production of pro-inflammatory cytokines by macrophages [260]. Paul et al. [122] used hydrogel-coated endometrial mesenchymal stem cells (eMSCs) and 3D melt electrospun wire nets to generate tissue-engineered scaffolds as a potential therapy for pelvic organ prolapse (POP). They firstly fabricated 3D-printed PCL mesh by using melt electrospinning (MES) at different temperatures, followed by optimizing the aloe vera-SA (AV-ALG) composite hydrogel ratio to 1:1 (1% AV-1% ALG), and finally bioprinted purified eMSCs in this composite hydrogel onto the MES-printed mesh. Implantation of the scaffold into the subcutaneous tissue of NSG mice for 1 week revealed that eMSCs printed onto MES promoted tissue integration and eMSCs retention. Detection of macrophage phenotype at the implantation site revealed a significant reduction in CCR7M1-type macrophages within the MES-Hyd group and MES-Hyd-eMSCs group, as compared to the control MES group. This suggests that AV-ALG hydrogel inhibits macrophage responses and functions to reduce inflammation compared to the MES control group. Furthermore, the addition of eMSCs further reduced the M1 inflammatory macrophage response and increased the M2 macrophages, as compared to the MES-Hyd group. Macrophage quantification showed significantly higher total F4/80+ macrophages in the control MES group and the MES-Hyd-eMSCs group compared with MES-Hyd, where the majority of the MES-only group were M1-type macrophages, whereas the majority of the F4/80 macrophages in the MES-Hyd-eMSCs group were anti-inflammatory M2-type macrophages of the CD206 phenotype. Overall, the addition of eMSCs to the scaffold exerted a regulatory role on the inflammatory response and provided a suitable candidate for tissue engineering repair of POP.
4.3.3. Ac2-26 Peptide
Ac2-26 peptide, the peptide located at the N-terminal end of ANXA1 of 26 amino acids, was found to inhibit TNF-α production in monocytes, inhibit NF-κB signaling of the proinflammatory pathway [261], and promote phagocytosis of neutrophils [262,263]. Xu et al. [36] fabricated a polylactic acid/4-arm polyethylene glycol hydrogel (PCL@tetra-PEG) composite scaffold as a tissue engineered meniscus (TEM). The PCL scaffold was fabricated with tapering porous and heterogeneous structures, and BMSCs were then seeded on them. The PCL@tetra-PEG scaffold was subsequently generated in a metal mold using a rotation-immersion method, in which tetra-PEG hydrogel not only improves the biomechanical properties of the PCL@tetra-PEG scaffold to fit the native meniscus, but also helps achieve different regional encapsulation and spatiotemporal zonal release of two human growth factors (CTGF and TGF-β3). Significantly, the simultaneous encapsulation of Ac2-26 peptide within the composite scaffold can perform anti-inflammatory and antioxidant effects, regulate the complex microenvironment, and promote tissue regeneration.
In vitro inflammatory cell model experiments showed that high concentrations of Ac2-26 peptide could effectively inhibit the production of ROS, and reactive nitrogen species (RNS) in macrophages which were induced by LPS. The Western Blot results showed that the expression of M1-type macrophage markers iNOS and COX-2 were significantly increased after LPS treatment. In contrast, after 12 h of Ac2-26 peptide treatment, the expression of iNOS and COX-2 decreased significantly as compared with the control group, and the higher the concentration of Ac2-26 peptide was, the more obvious the down-regulation of iNOS expression was. Moreover, in contrast to M1 markers, M2-type markers including Arg-1 and IL-10 were significantly upregulated after Ac2-26 peptide treatment. All these results indicated that Ac2-26 peptide promoted the phenotypic transformation of macrophage phenotype from M1 to M2 type, and exerted anti-inflammatory and antioxidant effects, to favor the promotion of tissue regeneration. Moreover, they used immunofluorescence and qPCR to assess the role of different types of pores on inducing tissue differentiation at the defect. It showed that the progressive pore meniscal scaffold was more favorable for inducing fibrocartilage differentiation of MSCs, and could induce in vitro expression of COL-1 and COL-2 with more heterogeneity than that of the homogeneous pore meniscal scaffold.
4.4. Plant Sources
4.4.1. Curcumin
Curcumin, a hydrophobic polyphenol, is the main component of turmeric. Demethoxycurcumin and bis-demethoxycurcumin can also be extracted from turmeric, but they both have lower activity levels than curcumin [264,265]. Curcumin was demonstrated to have the ability to target and regulate several molecules, including inflammatory cytokines, growth factors, and apoptosis-related proteins. It has multiple functions such as anti-inflammatory, antioxidant, and antitumor effects. The mechanism of its anti-inflammatory effects was investigated by its inhibitory effect on cytokine production and expression [266,267]. It was found that curcumin can exert anti-inflammatory activity in LPS/interferon-γ (IFN-γ)-treated macrophages through several mechanisms, for example, by blocking (NF-κB and signal transducer and activator of transcription 1 (STAT1) signaling pathways, thereby inhibiting LPS-induced IL-6 expression in RAW264.7 cells [268]. In addition, flavin derivatives can also inhibit NO, TNF-α, and IL-1β expression by suppressing the mitogen-activated protein kinase (MAPK)/NF-κB pathway in IFN-γ/LPS-stimulated macrophages [269]. Chen et al. [37] made mesoporous CS (MesoCS/curcumin) scaffolds with curcumin. MesoCS nanoparticles were first prepared using a template [270], followed by dissolving turmeric as a stock solution in 0.5 M NaOH to a concentration of 0 mg/mL, 2 mg/mL, 5 mg/mL, and 10 mM (i.e., C0, C2, C5, and C10, respectively), and finally, mixing the scaffolds at the same 0.4 mL/g liquid/powder ratio to make the scaffolds. The hMSCs were cultured in this composite scaffold and the expression levels of TNF-α and IL-1 were detected after LPS treatment for 1, 3, and 7 days. The results showed that the expression levels of TNF-α and IL-1 were significantly inhibited in the C2 and C5 groups, as compared with the C0 group (p < 0.05). The expression levels of TNF-α were not significantly decreased in the C10 group. This suggests that scaffolds containing certain concentrations of curcumin have significant anti-inflammatory potential to inhibit LPS-induced TNF-α and IL-1 expression. In contrast, high doses of curcumin (C10) may cause apoptosis mediated by metal ions (e.g., Ca ions) [271,272]. Furthermore, the MesoCS/curcumin scaffold showed good biocompatibility and physical properties, and the addition of curcumin did not alter the crystalline properties of MesoCS. Overall, the MesoCS/curcumin scaffold prepared in this study is expected to be a new material for bone tissue engineering and bone regenerative medicine. Although the side effects of curcumin such as hemodilution [273] and decreased blood glucose [274] remain to be addressed, the scaffold will have great potential for further clinical practice.
4.4.2. Isoflavones
Isoflavones are among the most common phytohormones and soybean and its products are the largest dietary source of them [275]. Genistein, one of the classes of isoflavones, has a wide range of biological activities, such as inhibition of cancer growth [276], promotion of osteoblast and alkaline phosphatase activity [277], and immunomodulation [278,279]. The excellent immunomodulatory effects of genistein are attributed to its multiple anti-inflammatory mechanisms, such as its ability to eliminate free radicals produced by macrophages during inflammation, thereby reducing the release of various inflammatory mediators induced by ROS [280,281]. It has the ability to inhibit the phosphorylation of IκB, an inhibitor of NF-κB, thereby reducing the degradation of IκB, inhibiting NF-κB activation, and, subsequently, reducing the pro-inflammatory cytokine production [282,283] among others. Sarkar et al. [38] loaded three soy isoflavones (Genistein, Daidzein, and Glycitein) in a 5:4:1 ratio, mimicking their original ratios in soy, on 3D-printed TCP scaffolds with pores. In vitro release profile showed controlled release in acidic and physiological buffered media over 16 days. Results of osteosarcoma cell culture experiments showed a 90% reduction in osteosarcoma (MG-63) cell viability and proliferation capacity after 11 days of cultivation, which implies the potential preventive ability of the scaffold against osteosarcoma cell lines. In addition, the scaffold showed good biocompatibility: the scaffold exhibited the ability to promote osteoblast proliferation and differentiation under both static and dynamic conditions. Finally, the scaffold was examined for in vivo immunomodulatory capacity. Twenty-four hours after implantation of the scaffold into the defective distal femur of rats, H&E staining examination revealed reduced neutrophil recruitment at the implantation site. Overall, they conferred in vitro chemopreventive, osteoclast-promoting, and immunomodulatory abilities to the scaffold by incorporating isoflavones and designing a versatile bone graft substitute. The downside is that the anti-inflammatory properties of this experiment were not analyzed for macrophages, polarization, and inflammatory factor concentrations. Long-term in vivo studies are needed.
4.4.3. Quercetin
Quercetin is a flavonoid monomeric compound found in natural plants with various physiological effects such as anti-inflammatory, antioxidant, antitumor, and osteogenic [284,285]. Quercetin was found to impact the M1/M2 phenotype transition in macrophages, inhibiting M1 phenotype polarization and promoting its polarization to the M2 phenotype [286]. Because it can induce phosphorylation of protein kinase B and promote signal transduction and nuclear translocation of transcriptional activator protein 6 (STAT6), it can increase the expression of the M2 phenotype upon binding to anti-inflammatory cytokine-related genes [287]. In addition, there were experiments that demonstrated that quercetin can block the NF-κB signaling pathway, thus promoting M2 polarization for anti-inflammatory repair effects [288]. Wang et al. [39] fabricated layered micro/nano surfaces on the surface of Ti6Al4V implants using 3D printing technique, alkali heat treatment, and hydrothermal treatment after deposition of titanium dioxide (TiO2) on this surface. This increased the adsorption of specific substances on Ti6Al4V implants and made them more biocompatible. Since quercetin has an excellent ability to chelate metal cations [289], it can be adsorbed as a monomer on TiO2, effectively creating a quercetin coating on the surface of the 3D-printed Ti6Al4V implant. SEM results of 24-h adhesion of RAW 264.7 cells in vitro showed that macrophages on the quercetin-containing coating group were mostly polarized to the M2 phenotype and had more pseudopods. This indicated there were more adequate attachments and diffusions. RBMSCs proliferation also showed similar results. Representative cytokine concentrations secreted by macrophages with M1/M2 phenotypes were further examined by ELISA. The M1 phenotype secreted reduced concentrations of IL-1β cytokines, whereas the M2 phenotype secreted increased concentrations of VEGF-α cytokines. Furthermore, after 7 days of cell adhesion, the addition of quercetin coating elevated the ALP expression on the surface of the motifs, as compared with the control group, thus revealing that quercetin does have the function of promoting osteogenic differentiation of rbMSCs. Finally, the scaffold was implanted into the femoral condylar defect in rats. Two weeks later, the control group showed a severe inflammatory response compared with the group loaded with quercetin. A large quantity of inflammatory cells such as monocytes, neutrophils, and macrophages, and a significant expression of the M1 macrophage biomarker IL-1β, was found in the implantation site. In contrast, inflammatory cells were significantly reduced, and IL-1β expression was significantly decreased in the loaded quercetin scaffold. These indicated the superior anti-inflammatory effect of quercetin at the site of inflammation in vivo. Overall, the loading of quercetin conferred osteointegration-promoting and immunomodulatory properties to the 3D-printed titanium implants, offering the possibility of future applications in clinical osteointegration.
5. Regulation of Collagen Deposition
Collagen, the most abundant protein in mammals (25–30% of total protein mass), is one of the main components of connective tissue. It is closely related to disease and aging, cell proliferation, migration and differentiation, and fibrosis formation [290]. More than 20 types of collagen were identified, of which the most abundant and well-studied are type I, type II, and type III collagens [291]. In addition, collagen is mostly found in the interstitial matrix of thin-walled organs and serves as a scaffolding structure to stabilize and maintain tissue integrity. Therefore, imbalance of collagen metabolism plays a crucial role in the development of certain diseases. In the middle and late stages of injury repair, however, an imbalance in the ratio of type I to type III collagen (type I collagen replaces type III collagen), and often leads to fibrotic lesions and scar formation [292,293]. Collagen metabolism is regulated by signaling pathways such as TGF-β/Smad, PI3K/Akt, MAPK, and NF-κB, and each pathway interacts with each other to mediate collagen metabolism [294,295,296]. Therefore, there are many studies that regulate collagen deposition by adding some kind of signaling pathway modulating substance to 3D-printed tissue engineering scaffolds or adding some kind of collagen-containing substance directly to the scaffold to make the collagen deposition at the scaffold implantation injury repair with specific tissue specificity. Thus, they can better promote efficient and scar-free repair at the implantation site and promote tissue regeneration.
5.1. Direct Regulation
5.1.1. Collagen
As mentioned above, different types and ratios of collagen deposition play different roles in different periods of wound repair. So, it is crucial to form tissue-specific collagen deposition at the implantation injury site, to promote regeneration of wound repair tissue, and to avoid scar tissue formation due to excessive collagen deposition. Martin et al. [28] used 3D printing technology to prepare a PLA-collagen -minocycline-nanohydroxyapatite scaffold; the specific preparation process was mentioned in the Section 3. They added collagen directly to the 3D-printed scaffold. The scaffold had good osteogenic properties, morphological and mechanical properties matching those of bone trabeculae. The addition of collagen enhanced the structural strength of the scaffold and formed a scaffold support closer to the scaffold itself. It also had a positive effect on bone differentiation and metabolism.
5.1.2. Extracellular Matrix
In spite of the good effects from direct addition of collagen to scaffolds, rapid degradation and shrinkage are inevitable after long-term implantation, and so, their lifespan is very limited [297,298]. The application of dECM as an ink for 3D bioprinting can be a good solution. Extracellular matrix is mainly composed of various components such as collagen, non-collagen, and elastin [299], and collagen as the main component can not only give the extracellular matrix the function of directly regulating collagen deposition, but also avoid the degradation and shrinkage process caused by a single collagen. Kim et al. [23] used S-dECM bioink to print and fabricate 3D pre-vascularized skin patches for wound healing with infusion of ASCs and EPCs. After implanting the patches into mice for 2 weeks, the 3D cell-printed skin tissues using dECM as bioink were very stable, had less shrinkage, and contained abundant type I and III collagen, as well as fibronectin with better cellular integrity as compared to the single collagen group. In addition, the cytoskeleton of tissue repair and epithelialization (KGF-1)-related gene expression levels were also higher in the dECM-as-bioink group. Therefore, using extracellular matrix as a 3D bioprinting ink could better regulate collagen deposition and promote tissue repair and regeneration. However, the issue of cell-related immunogenicity of its heterologous tissues should not be ignored, and the cells of donor tissues need to be completely removed, and so, the use of dECM as bioink for preclinical or even clinical applications still needs to be carefully experimented and considered before use.
5.2. Indirect Regulation
5.2.1. Copper Ion
Cu2+ is one of the essential ions for the human body. As mentioned above, Cu ions have antibacterial, immunomodulatory, and pro-vascularizing effects, and play a huge role in human metabolic processes. It was demonstrated that Cu2+ ions can upregulate HIF-1 expression by activating and binding to the α-subunit of HIF-1 factor, and inhibiting the activity of HIF-1 and the inhibitory factor of HIF-1 [104,300]. The activation of the HIF pathway further stimulates the expression of SOX-9, which leads to increased levels of COL II and ACAN expression in chondrocytes increased [301,302]. This regulates collagen deposition and promotes chondrocyte synthesis and development. Lin et al. [84] fabricated Cu-BGC scaffolds by doping different concentrations of Cu2+ (0.781–25 mg/mL) into bioactive microcrystalline glass with 3D printing technology. The results showed that the expression of SOX9 in cartilage was significantly increased after treatment with Cu2+. In addition, the expression of COL II and ACAN genes in chondrocytes was also significantly elevated after day 3 of Cu2+ treatment. In vitro results also showed that Cu2+ concentration in the range of 0.5–16 ppm significantly increased the expression of COL II and NCAD proteins. Chondrocyte proliferation and maturation were stimulated and elevated compared to the control group.
5.2.2. Silk Fiber
In addition to the above-mentioned pro-vascularization functions, SF was also shown to be able to regulate collagen deposition to some extent. As one of the filamentous proteins, Antheraea assama SF can improve cell fate and promote ECM secretion owing to its Arg-Gly-Asp (RGD) content. Bandyopadhyay et al. [40] mixed a blend of SF from mulberry (Bombyx mori) and non-mulberry (Antheraea assama) silk with gelatin as inks for 3D bioprinting to simulate the extracellular microenvironment of the meniscus. Subsequently, EDC and NHS were chemically cross-linked to enhance their stability and mechanical strength. Finally, porcine meniscal fibrocartilage cells were seeded in the scaffold. After 7 days, the expression of sox-9, aggrecan, and collagen II genes were significantly increased. After 21 days, a significant increase in the secretion of sGAG and the deposition of ECM components (i.e., collagen) was detected. This suggests that Antheraea assama SF can indirectly regulate collagen deposition by promoting the secretion of ECM for implant site-specific collagen deposition.
5.2.3. Curcumin
Curcumin is one of the main active components of the rhizome of the turmeric plant. In addition to the above-mentioned functions of promoting angiogenesis, immunomodulation, and antioxidation, Bose et al. [41] also demonstrated that curcumin has the function of inhibiting the NF-κβ signaling pathway, thus promoting osteoblast differentiation and the secretion of ECM. They fabricated a PCL-PEG+curcumin-coated TCP scaffold using 3D printing technology. After implanting the scaffold into rats for 6 weeks, this scaffold group showed significant new bone formation and mineralization, as compared with the control group. Tissue staining showed various types of type II collagen, and the scaffold implantation greatly promoted ECM formation and angiogenesis. The results suggest that curcumin promotes the formation and deposition of ECM by promoting osteogenesis, thereby indirectly and specifically regulating collagen deposition.
5.2.4. Mesenchymal Stem Cells
MSCs are multipotent differentiated cells that can be induced to differentiate into stromal cells, osteoblasts, hepatocytes, and other cells and were widely used in disease models to regulate wound healing and tissue regeneration [303,304]. It was demonstrated that MSCs play a major role in regulating collagen production and inhibiting scar formation during the proliferative and mature phases of injury repair.
The main mechanisms of MSCs for scar inhibition are as follows. 1. Inhibition of inflammation in scar tissue. In detail, excessive inflammatory response is one of the main causes of scar formation. MSCs can shorten the inflammatory period and reduce the inflammatory response by acting as a chemotactic agent for various cytokines that contribute to wound healing, such as TNF, IL-8, PDGF [305]. In the meanwhile, they can immunomodulate inflammatory cells in scar formation by secreting various factors and extracellular vesicles [306]. 2. MSCs can affect fibroblast activity in scar formation and can reduce scar formation by inhibiting the gene expression of TGF-β1 and decreasing type I collagen production [307]. In addition, MSCs can inhibit fibroblast proliferation and migration, as well as inhibit angiogenesis in scar tissue. 3. MSCs can play a positive role in collagen remodeling in scar tissue, and can regulate the expression of matrix metalloproteinase (MMP) by secreting tissue inhibitor metalloproteinase (TIMP), thereby delaying or reducing scar formation [308]. In details, in a rat skin burn model, MSCs not only promoted the proliferation of epithelial cells at the skin wound, but also increased the expression of CK19, PCNA, Col I, and Col III [309]. Paul et al. [122] used hydrogel-coated eMSCs and 3D melt electrospun wire nets to generate tissue-engineered scaffolds for POP. The specific production process was mentioned in the previous section. Picro Sirius red staining in Figure 11 shows collagen deposition in and around the reticular area of the MES-Hyd-eMSCs group as compared to MES and MES-Hyd alone. MES-Hyd shows no collagen within the first week of implantation.
The fate of the mesh after 1 week of implantation in vivo was assessed by SEM in Figure 12, showing little degradation of the scaffold after 1 week, as expected for a PCL-based mesh. The deposition of new collagen fibers appeared lower in MES alone (Figure 12A–C) and MES_Hyd (Figure 12D–F). On the other hand, MES_Hyd_eMSCs showed better evidence of tissue integration and new collagen deposition (Figure 12G–I).
All these results suggest that the addition of MSCs to scaffolds can better regulate collagen deposition and promote tissue integration and regeneration. Additionally, among the many different sources of MSCs, human gingival mesenchymal stem cells (hGMSCs) are abundant and readily available [310,311]. In addition, gingival cells have a mechanism similar to fetal tissue healing, and exhibit greater ability to heal scar-free wounds than dermal fibroblasts [312]. Shafiee et al. [313] fabricated a bionic medical polycaprolactone (mPCL) dressing with hGMSCs using 3D printing technology. The medical polycaprolactone dressing has a pore structure and excellent mechanical properties that mimic the layered structure of skin collagen fibers. This facilitates skin wound healing and reduces scar formation. After implantation of the dressing containing hGMSCs into rats for 6 weeks, wound contraction was significantly reduced in the mPCL dressing group, as compared with the control group. Tissue regeneration was significantly improved by granulation and re-epithelialization. In addition, Masson staining showed significant collagen I deposition in the wound area, and the collagen I deposition exhibited an ordered, directionally dispersed narrower form. Overall, mPCL dressings containing hGMSCs resulted in more rapid wound healing, regulated collagen deposition, and reduced scar formation in the rat model.
5.2.5. Granulocyte Colony-Stimulating Factor
Granulocyte colony-stimulating factor (G-CSF) is a hematopoietic factor produced by lymphocytes, macrophages, and endothelial cells, and it promotes the proliferation and differentiation of bone marrow hematopoietic cells [314]. In addition, as an anti-inflammatory protein, endometrial stem cell-derived G-CSF can reduce scar formation by reducing Gli2 protein expression levels to regulate collagen deposition and reduce endometrial fibrosis [315,316]. However, G-CSF has a short half-life in vivo due to receptor-mediated clearance, renal metabolic elimination, and enzymatic degradation [317,318]. Furthermore, due to the continuous migration of G-CSF in the uterine cavity, it cannot maintain a consistently high concentration at the endometrial injury to achieve good therapeutic efficacy. Therefore, to maintain the long-term drug concentration of G-CSF at the site of endometrial injury and to reduce the adverse consequences of a single high-dose administration, it is of great significance to construct a sustained release system of G-CSF. Wen et al. [42] made G-CSF-loaded slow-release microsphere (G-CSF-SRM) hydrogel scaffolds with 3D printing technology. They mixed recombinant human G-CSF, dextrose, and polyethylene glycol in a mass ratio of 1:5:50, and stirred and freeze-dried them. Then, the obtained G-CSF-dextran-PLGA microspheres were processed by curing, hardening, and freeze-drying to complete the G-CSF microsphere preparation. Finally, the prepared G-CSF microspheres were mixed and printed with 20% gelatin and 4% SA to make a 3D-printed G-CSF-SRM hydrogel scaffold. The in vitro cumulative release of G-CSF over time was measured by ELISA. It showed that G-CSF was continuously released from the microspheres for more than 1 month, and the drug release became slow and regular after the explosive release just after implantation. Five weeks after implantation of the scaffold at the endometrial injury in rats, HE staining results showed that the number of endometrial cells and good endometrial regeneration were significantly increased in the group implanted with 3D-printed G-CSF-SRM hydrogel scaffold, whose endometrial thickness and number of glands were significantly higher than the remaining four groups. However, their inflammatory cells and inflammatory factors IL-1β, IL-6, TNF-α expression levels were lower. In addition, Masson staining results showed that this group had relatively less collagen deposition and less fibrosis. Thus, endometrial inflammatory cell infiltration and endometrial fibrosis were significantly reduced due to G-CSF, which effectively prevented fibrous exudation-mediated adhesion and scar formation.
5.2.6. Piezoelectric Effect
It was demonstrated that bioelectricity plays a crucial role in promoting wound healing [319]. However, the gradual weakening of bioelectric stimulation with wound healing may cause disruption of gene regulation, leading to downregulation of the wound healing cascade and eventually disorganized deposition of collagen fibers and abnormal remodeling of the ECM, which delayed wound healing and resulted in the formation of scar tissue [320,321]. Therefore, to solve these problems, Liang et al. [43] fabricated a novel ZnO nanoparticle-modified PVDF/SA piezoelectric hydrogel 3D scaffold (ZPFSA). As one of the commonly used piezoelectric materials, polyvinylidene fluoride (PVDF) has excellent piezoelectric properties, biocompatibility, thermal stability, and resistance to chemical irritation [322]. However, since PVDF is a superhydrophobic polymer, it is contrary to the wetting behaviors of hydrogels and preparing them as hydrogels is a great challenge [323]. Therefore, the incorporation of SA precisely reduces the hydrophobicity of PVDF and creates the possibility of preparing hydrogels from its 3D printing. Moreover, the addition of nanoparticles can enhance the piezoelectric properties of PVDF by promoting the polarization of PVDF [324]. The 3D-printed ZPFSA scaffold was implanted into the defective skin on the back of rats, and the immunohistochemical results showed that the CD31 expression in the ZPFSA 0.5 group was higher than the other groups on day 7 after implantation. This indicated that the wound tissue in the ZPFSA 0.5 group had active angiogenesis to ensure adequate blood supply to the wound. α-SMA is an α-smooth muscle actin secreted by myofibroblasts, which has high expression in the middle and late stages of tissue healing and proliferation to promote wound contraction. However, at the end of wound healing, myofibroblast apoptosis causes a gradual decrease in α-SMA expression to prevent excessive contraction of collagen fibers and formation of scar tissue [325]. At day 14 after implantation, the wound in the ZPFSA0.5 group was close to healing and its α-SMA content was maintained at a low level. The other groups were still in the late stage of healing and had higher α-SMA content. Thus, the ZPFSA0.5 group reduced the possibility of scar formation by accelerating wound healing. In addition, immunohistochemical results showed that the expression of three growth factors, EGF, VEGF, and TGF-β, was higher in the ZPFSA 0.5 group than in the other groups, implying that the electrical stimulation was generated by the ZPFSA piezoelectric scaffold when receiving stress. This could promote the production of cellular growth factors, which greatly accelerated the wound healing process and effectively prevented the formation of scar tissue.
6. Future Perspective and Concluding Remarks
This review outlined current important advances in 3D bioprinting of tissue and/or organ engineering. The different additives were classified into four categories according to the different functions they conferred on the scaffold: vascularization, antibacterial, immunomodulation, and regulation of collagen deposition. The mechanisms and the methods of incorporating bioinks were detailed. Many additives can fulfill two or more functions from their excellent properties. For example, many metal ions can not only be antibacterial, but also perform immunomodulatory functions. Extracellular matrix can not only promote vascularization, but also regulate collagen deposition and reduce scar tissue formation, etc. All these summaries offer the possibility of adding small amounts of additives to achieve multiple effects in the future, which will facilitate 3D-bioprinted scaffolds to perform their functions and promote tissue regeneration more efficiently and effortlessly. However, although many experiments in animals or in vitro achieved good outcomes, only a few printed scaffolds were applied to human experiments for research. We think there are many reasons for this; for example: these constructs need to be specific to the relevant characteristics of the graft site (appropriate cell type, ideal mechanical properties, and other required associated cues, such as neovascularization, low inflammatory properties, sterility, and appropriate collagen deposition), which is often a challenge for transplantation [326]. So, future work can be dedicated to the suitable scaffolds to general clinics. Suitable additives can be used according to the different specific environments of the implantation site, thus achieving specific functional modulation, or even meeting one additive to achieve multiple functions, greatly improving transplantation success, reducing the complexity and economic cost of bioprinting, and, finally, facilitating the translation of the constructs from animal experiments to the clinic. Looking forward to the future, it is bright to design the tissue-specific 3D-bioprinted scaffolds and add efficient additives to achieve multi-functions, and then use them in tissue regeneration in human treatment.
Abbreviations
3D | Three dimensional | VEGF | vascular endothelial growth factor |
BMP-2 | bone morphogenetic protein-2 | SF | silk fiber |
nHAp | nano-hydroxyapatite | EDC | 1-ethyl-3-(3-(dimethylamino) propyl) carbodiimide |
NHS | N-hydroxysuccinimide | FGF-2 | Fibroblast growth factor-2 |
SO3 | sulfonic acid group | α-SMA | α-smooth muscle actin |
PDGF | platelet-derived growth factor | SMC | Smooth muscle cell |
ECs | endothelial cells | PLL | poly-L-lysine |
GelMA | Gelatin methacrylate | HAMA | Hyaluronic acid methacrylate |
HIF-1α | hypoxia-inducible factor-1α | MDSCs | muscle-derived stem cells |
SDF-1 | stroma cell-derived factor-1 | HS | Heparan sulfate |
ISH | In situ hybridization | hBMSCs | human bone marrow stromal cells |
KDR | kinase insert domain-containing receptor | CPC | calcium phosphate cement |
MS | Mesoporous Silica | rhBMP-2 | recombinant human bone morphogenetic protein-2 |
μCT | Micro-computerised Tomography | NO | nitric oxide |
PDA | polydopamine | HUVECs | human umbilical vein endothelial cells |
TCP | Tricalcium phosphate | MOFs | metal organic frameworks |
CAM | chorioal lantoic membrane | MSCs | Mesenchymal stem cells |
hUCMSCs | human umbilical cord mesenchymal stem cells | DFO | Desferrioxamine |
PCL | Polycaprolactone | DAT-A | decellularized adipose tissue-alginate |
GAG | glycosaminoglycans | HA | hyaluronic acid |
dECM | decellularized extracellular matrix | ASCs | adipose-derived stem cells |
EPCs | endothelial progenitor cells | AP | Angiogenic peptides |
OP | osteogenic peptide | ROS | reactive oxygen species |
PAM | polyacrylamide | HPMC | Hydroxypropyl Methyl Cellulose |
PTT | photothermal therapy | PDT | photodynamic therapy |
PLGA | poly(lactic-co-glycolic-acid) | PLA | poly (lactic acid) |
cHA | citrate hydroxyapatite nanoparticles | SEM | scanning electron microscopy |
SDVG | small-diameter vascular graft | PEG | poly (ethylene glycol) |
SC | Satureja cuneifolia | NDS | Nanodiamonds |
SLM | selective laser melting | RNA | ribonucleic acid |
AM | additive manufacturing | FFF | Fused filament fabrication |
PA12 | polyamide 12 | LPS | lipopolysaccharide |
DEX | Dexamethasone | COX-2 | cyclooxygenase 2 |
ELSP | electrostatic spinning technique | βCD | β-cyclodextrin |
PEI | polyethyleneimine | AFM | atomic force microscopy |
XPS | X-ray photoelectron spectroscopy | eMSCs | endometrial mesenchymal stem cells |
POP | pelvic organ prolapse | MES | melt electrospinning |
TNF-α | tumor necrosis factor-α | RNS | reactive nitrogen species |
NF-κB | nuclear factor-κB | STAT1 | signal transducer and activator of transcription 1 |
MAPK | mitogen-activated protein kinase | MMP | matrix metalloproteinase |
TIMP | tissue inhibitor metalloproteinase | hGMSCs | human gingival mesenchymal stem cells |
mPCL | medical polycaprolactone | G-CSF | Granulocyte colony-stimulating factor |
PVDF | polyvinylidene fluoride |
Author Contributions
W.F., M.L. and R.Y., writing—original draft, M.Y. and Y.W. (Yuhui Wang), writing—review and editing; W.F., Y.J. and Y.W. (Ying Wang), figure drawing; K.Z. and Q.F., conceptualization, writing—review and editing, funding acquisition. All authors have read and agreed to the published version of the manuscript.
Institutional Review Board Statement
Not applicable.
Informed Consent Statement
Not applicable.
Data Availability Statement
Not applicable.
Conflicts of Interest
The authors declare no conflict of interest.
Funding Statement
This work was supported by the National Natural Scientific Foundation of China (No. 82170694), the Interdisciplinary Program of Shanghai Jiao Tong University (No. YG2022ZD020) and the Natural Science Foundation of Shanghai (No. 20ZR1442100).
Footnotes
Disclaimer/Publisher’s Note: The statements, opinions and data contained in all publications are solely those of the individual author(s) and contributor(s) and not of MDPI and/or the editor(s). MDPI and/or the editor(s) disclaim responsibility for any injury to people or property resulting from any ideas, methods, instructions or products referred to in the content.
References
- 1.Hosseini V., Maroufi N.F., Saghati S., Asadi N., Darabi M., Ahmad S.N.S., Hosseinkhani H., Rahbarghazi R. Current progress in hepatic tissue regeneration by tissue engineering. J. Transl. Med. 2019;17:383. doi: 10.1186/s12967-019-02137-6. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 2.Ozbolat I.T., Peng W., Ozbolat V. Application areas of 3D bioprinting. Drug Discov. Today. 2016;21:1257–1271. doi: 10.1016/j.drudis.2016.04.006. [DOI] [PubMed] [Google Scholar]
- 3.Beheshtizadeh N., Lotfibakhshaiesh N., Pazhouhnia Z., Hoseinpour M., Nafari M. A review of 3D bio-printing for bone and skin tissue engineering: A commercial approach. J. Mater. Sci. 2020;55:3729–3749. doi: 10.1007/s10853-019-04259-0. [DOI] [Google Scholar]
- 4.Hassan M., Dave K., Chandrawati R., Dehghani F., Gomes V.G. 3D printing of biopolymer nanocomposites for tissue engineering: Nanomaterials, processing and structure-function relation. Eur. Polym. J. 2019;121:109340. doi: 10.1016/j.eurpolymj.2019.109340. [DOI] [Google Scholar]
- 5.Aljohani W., Ullah M.W., Zhang X., Yang G. Bioprinting and its applications in tissue engineering and regenerative medicine. Int. J. Biol. Macromol. 2018;107:261–275. doi: 10.1016/j.ijbiomac.2017.08.171. [DOI] [PubMed] [Google Scholar]
- 6.Jang T.S., Jung H.D., Pan H.M., Han W.T., Chen S., Song J. 3D printing of hydrogel composite systems: Recent advances in technology for tissue engineering. Int. J. Bioprint. 2018;4:126. doi: 10.18063/ijb.v4i1.126. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 7.Ganguly S., Margel S. 3D printed magnetic polymer composite hydrogels for hyperthermia and magnetic field driven structural manipulation. Prog. Polym. Sci. 2022;131:101574. doi: 10.1016/j.progpolymsci.2022.101574. [DOI] [Google Scholar]
- 8.Groll J., Burdick J.A., Cho D.W., Derby B., Gelinsky M., Heilshorn S.C., Jüngst T., Malda J., Mironov V.A., Nakayama K., et al. A definition of bioinks and their distinction from biomaterial inks. Biofabrication. 2018;11:013001. doi: 10.1088/1758-5090/aaec52. [DOI] [PubMed] [Google Scholar]
- 9.Yilmaz B., Al Rashid A., Mou Y.A., Evis Z., Koç M. Bioprinting: A review of processes, materials and applications. Bioprinting. 2021;23:e00148. doi: 10.1016/j.bprint.2021.e00148. [DOI] [Google Scholar]
- 10.Kabirian F., Mozafari M. Decellularized ECM-derived bioinks: Prospects for the future. Methods. 2020;171:108–118. doi: 10.1016/j.ymeth.2019.04.019. [DOI] [PubMed] [Google Scholar]
- 11.Hospodiuk M., Dey M., Sosnoski D., Ozbolat I.T. The bioink: A comprehensive review on bioprintable materials. Biotechnol Adv. 2017;35:217–239. doi: 10.1016/j.biotechadv.2016.12.006. [DOI] [PubMed] [Google Scholar]
- 12.Gungor-Ozkerim P.S., Inci I., Zhang Y.S., Khademhosseini A., Dokmeci M.R. Bioinks for 3D bioprinting: An overview. Biomater. Sci. 2018;6:915–946. doi: 10.1039/C7BM00765E. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 13.Bhowmik M., Kumari P., Sarkar G., Bain M.K., Bhowmick B., Mollick M.M.R., Mondal D., Maity D., Rana D., Bhattacharjee D., et al. Effect of xanthan gum and guar gum on in situ gelling ophthalmic drug delivery system based on poloxamer-407. Int. J. Biol. Macromol. 2013;62:117–123. doi: 10.1016/j.ijbiomac.2013.08.024. [DOI] [PubMed] [Google Scholar]
- 14.Ganguly S., Das T.K., Mondal S., Das N.C. Synthesis of polydopamine-coated halloysite nanotube-based hydrogel for controlled release of a calcium channel blocker. RSC Adv. 2016;6:105350–105362. doi: 10.1039/C6RA24153K. [DOI] [Google Scholar]
- 15.Sarkar G., Orasugh J.T., Saha N.R., Roy I., Bhattacharyya A., Chattopadhyay A.K., Rana D., Chattopadhyay D. Cellulose nanofibrils/chitosan based transdermal drug delivery vehicle for controlled release of ketorolac tromethamine. New J. Chem. 2017;41:15312–15319. doi: 10.1039/C7NJ02539D. [DOI] [Google Scholar]
- 16.Qiang W., Zhang Y., Li B., Liang C.J.J.o.M.C.B. Controlled dual delivery of low doses of BMP-2 and VEGF in a silk fibroin–nanohydroxyapatite scaffold for vascularized bone regeneration. J. Mater. Chem. B. 2017;5:6963–6972. doi: 10.1039/c7tb00949f. [DOI] [PubMed] [Google Scholar]
- 17.Xiong S., Zhang X., Lu P., Wu Y., Wang Q., Sun H., Heng B., Bunpetch V., Zhang S., Ouyang H.J.S.R. A Gelatin-sulfonated Silk Composite Scaffold based on 3D Printing Technology Enhances Skin Regeneration by Stimulating Epidermal Growth and Dermal Neovascularization. Sci. Rep. 2017;7:4288. doi: 10.1038/s41598-017-04149-y. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 18.An G., Guo F., Liu X., Wang Z., Zhu Y., Fan Y., Xuan C., Li Y., Wu H., Shi X., et al. Functional reconstruction of injured corpus cavernosa using 3D-printed hydrogel scaffolds seeded with HIF-1α-expressing stem cells. Nat. Commun. 2020;11:2687. doi: 10.1038/s41467-020-16192-x. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 19.Jiang J., Liu X., Chen H., Dai C., Niu X., Dai L., Chen X., Zhang S. 3D printing collagen/heparin sulfate scaffolds boost neural network reconstruction and motor function recovery after traumatic brain injury in canine. Biomater. Sci. 2020;8:6362–6374. doi: 10.1039/D0BM01116A. [DOI] [PubMed] [Google Scholar]
- 20.Wang C., Lai J., Li K., Zhu S., Lu B., Liu J., Tang Y., Wei Y. Cryogenic 3D printing of dual-delivery scaffolds for improved bone regeneration with enhanced vascularization. Bioact. Mater. 2021;6:137–145. doi: 10.1016/j.bioactmat.2020.07.007. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 21.Yan Y., Chen H., Zhang H., Guo C., Yang K., Chen K., Cheng R., Qian N., Sandler N., Zhang Y.S., et al. Vascularized 3D printed scaffolds for promoting bone regeneration. Biomaterials. 2019;190:97–110. doi: 10.1016/j.biomaterials.2018.10.033. [DOI] [PubMed] [Google Scholar]
- 22.Rijal G., Kim B.S., Pati F., Ha D.H., Kim S.W., Cho D.W. Robust tissue growth and angiogenesis in large-sized scaffold by reducing H(2)O(2)-mediated oxidative stress. Biofabrication. 2017;9:015013. doi: 10.1088/1758-5090/9/1/015013. [DOI] [PubMed] [Google Scholar]
- 23.Kim B.S., Kwon Y.W., Kong J.S., Park G.T., Gao G., Han W., Kim M.B., Lee H., Kim J.H., Cho D.W. 3D cell printing of in vitro stabilized skin model and in vivo pre-vascularized skin patch using tissue-specific extracellular matrix bioink: A step towards advanced skin tissue engineering. Biomaterials. 2018;168:38–53. doi: 10.1016/j.biomaterials.2018.03.040. [DOI] [PubMed] [Google Scholar]
- 24.Bejleri D., Streeter B.W., Nachlas A.L.Y., Brown M.E., Gaetani R., Christman K.L., Davis M.E. A Bioprinted Cardiac Patch Composed of Cardiac-Specific Extracellular Matrix and Progenitor Cells for Heart Repair. Adv. Healthc. Mater. 2018;7:e1800672. doi: 10.1002/adhm.201800672. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 25.Nie R., Sun Y., Lv H., Lu M., Huangfu H., Li Y., Zhang Y., Wang D., Wang L., Zhou Y. 3D printing of MXene composite hydrogel scaffolds for photothermal antibacterial activity and bone regeneration in infected bone defect models. Nanoscale. 2022;14:8112–8129. doi: 10.1039/D2NR02176E. [DOI] [PubMed] [Google Scholar]
- 26.Yu Y.H., Lee D., Hsu Y.H., Chou Y.C., Ueng S.W., Chen C.K., Liu S.J. A Three-Dimensional Printed Polycaprolactone Scaffold Combined with Co-Axially Electrospun Vancomycin/Ceftazidime/Bone Morphological Protein-2 Sheath-Core Nanofibers for the Repair of Segmental Bone Defects During the Masquelet Procedure. Int. J. Nanomed. 2020;15:913–925. doi: 10.2147/IJN.S238478. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 27.Sadaba N., Larrañaga A., Orpella-Aceret G., Bettencourt A.F., Martin V., Biggs M., Ribeiro I.A.C., Ugartemendia J.M., Sarasua J.R., Zuza E. Benefits of Polydopamine as Particle/Matrix Interface in Polylactide/PD-BaSO(4) Scaffolds. Int. J. Mol. Sci. 2020;21:5480. doi: 10.3390/ijms21155480. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 28.Martin V., Ribeiro I.A., Alves M.M., Gonçalves L., Claudio R.A., Grenho L., Fernandes M.H., Gomes P., Santos C.F., Bettencourt A.F. Engineering a multifunctional 3D-printed PLA-collagen-minocycline-nanoHydroxyapatite scaffold with combined antimicrobial and osteogenic effects for bone regeneration. Mater. Sci. Eng. C Mater. Biol. Appl. 2019;101:15–26. doi: 10.1016/j.msec.2019.03.056. [DOI] [PubMed] [Google Scholar]
- 29.Kabirian F., Brouki Milan P., Zamanian A., Heying R., Mozafari M. Nitric oxide-releasing vascular grafts: A therapeutic strategy to promote angiogenic activity and endothelium regeneration. Acta Biomater. 2019;92:82–91. doi: 10.1016/j.actbio.2019.05.002. [DOI] [PubMed] [Google Scholar]
- 30.Ilhan E., Cesur S., Guler E., Topal F., Albayrak D., Guncu M.M., Cam M.E., Taskin T., Sasmazel H.T., Aksu B., et al. Development of Satureja cuneifolia-loaded sodium alginate/polyethylene glycol scaffolds produced by 3D-printing technology as a diabetic wound dressing material. Int. J. Biol. Macromol. 2020;161:1040–1054. doi: 10.1016/j.ijbiomac.2020.06.086. [DOI] [PubMed] [Google Scholar]
- 31.Rifai A., Tran N., Reineck P., Elbourne A., Mayes E., Sarker A., Dekiwadia C., Ivanova E.P., Crawford R.J., Ohshima T., et al. Engineering the Interface: Nanodiamond Coating on 3D-Printed Titanium Promotes Mammalian Cell Growth and Inhibits Staphylococcus aureus Colonization. ACS Appl. Mater. Interfaces. 2019;11:24588–24597. doi: 10.1021/acsami.9b07064. [DOI] [PubMed] [Google Scholar]
- 32.Intini C., Elviri L., Cabral J., Mros S., Bergonzi C., Bianchera A., Flammini L., Govoni P., Barocelli E., Bettini R., et al. 3D-printed chitosan-based scaffolds: An in vitro study of human skin cell growth and an in-vivo wound healing evaluation in experimental diabetes in rats. Carbohydr. Polym. 2018;199:593–602. doi: 10.1016/j.carbpol.2018.07.057. [DOI] [PubMed] [Google Scholar]
- 33.Lee S.J., Choi J.S., Eom M.R., Jo H.H., Kwon I.K., Kwon S.K., Park S.A. Dexamethasone loaded bilayered 3D tubular scaffold reduces restenosis at the anastomotic site of tracheal replacement: In vitro and in vivo assessments. Nanoscale. 2020;12:4846–4858. doi: 10.1039/C9NR10341D. [DOI] [PubMed] [Google Scholar]
- 34.Farto-Vaamonde X., Auriemma G., Aquino R.P., Concheiro A., Alvarez-Lorenzo C. Post-manufacture loading of filaments and 3D printed PLA scaffolds with prednisolone and dexamethasone for tissue regeneration applications. Eur. J. Pharm. Biopharm. 2019;141:100–110. doi: 10.1016/j.ejpb.2019.05.018. [DOI] [PubMed] [Google Scholar]
- 35.Wang M., Li W., Luo Z., Tang G., Mu X., Kuang X., Guo J., Zhao Z., Flores R.S., Jiang Z., et al. A multifunctional micropore-forming bioink with enhanced anti-bacterial and anti-inflammatory properties. Biofabrication. 2022;14:024105. doi: 10.1088/1758-5090/ac5936. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 36.Xu B., Ye J., Fan B.S., Wang X., Zhang J.Y., Song S., Song Y., Jiang W.B., Wang X., Yu J.K. Protein-spatiotemporal partition releasing gradient porous scaffolds and anti-inflammatory and antioxidant regulation remodel tissue engineered anisotropic meniscus. Bioact. Mater. 2023;20:194–207. doi: 10.1016/j.bioactmat.2022.05.019. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 37.Chen Y.C., Shie M.Y., Wu Y.A., Lee K.A., Wei L.J., Shen Y.F. Anti-inflammation performance of curcumin-loaded mesoporous calcium silicate cement. J. Formos. Med. Assoc. = Taiwan Yi Zhi. 2017;116:679–688. doi: 10.1016/j.jfma.2017.06.005. [DOI] [PubMed] [Google Scholar]
- 38.Sarkar N., Bose S. Controlled release of soy isoflavones from multifunctional 3D printed bone tissue engineering scaffolds. Acta Biomater. 2020;114:407–420. doi: 10.1016/j.actbio.2020.07.006. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 39.Liu N., Wang H., Fu Z., Zhang C., Hui W., Wu J., Zhang Y., Zhang S. Quercetin-Coating Promotes Osteogenic Differentiation, Osseointegration and Anti-Inflammatory Properties of Nano-Topographic Modificated 3D-Printed Ti6Al4V Implant. Front. Bioeng. Biotechnol. 2022;10:933135. doi: 10.3389/fbioe.2022.933135. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 40.Bandyopadhyay A., Mandal B.B. A three-dimensional printed silk-based biomimetic tri-layered meniscus for potential patient-specific implantation. Biofabrication. 2019;12:015003. doi: 10.1088/1758-5090/ab40fa. [DOI] [PubMed] [Google Scholar]
- 41.Bose S., Sarkar N., Banerjee D. Effects of PCL, PEG and PLGA polymers on curcumin release from calcium phosphate matrix for in vitro and in vivo bone regeneration. Mater. Today. Chem. 2018;8:110–120. doi: 10.1016/j.mtchem.2018.03.005. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 42.Wen J., Hou B., Lin W., Guo F., Cheng M., Zheng J., He P., Ji W. 3D-printed hydrogel scaffold-loaded granulocyte colony-stimulating factor sustained-release microspheres and their effect on endometrial regeneration. Biomater. Sci. 2022;10:3346–3358. doi: 10.1039/D2BM00109H. [DOI] [PubMed] [Google Scholar]
- 43.Liang J., Zeng H., Qiao L., Jiang H., Ye Q., Wang Z., Liu B., Fan Z. 3D Printed Piezoelectric Wound Dressing with Dual Piezoelectric Response Models for Scar-Prevention Wound Healing. ACS Appl. Mater. Interfaces. 2022;14:30507–30522. doi: 10.1021/acsami.2c04168. [DOI] [PubMed] [Google Scholar]
- 44.Agarwal S., Saha S., Balla V.K., Pal A., Barui A., Bodhak S. Current Developments in 3D Bioprinting for Tissue and Organ Regeneration–A Review. Front. Mech. Eng. 2020;6:589171. doi: 10.3389/fmech.2020.589171. [DOI] [Google Scholar]
- 45.Santos-Beato P., Midha S., Pitsillides A.A., Miller A., Torii R., Kalaskar D.M. Biofabrication of the osteochondral unit and its applications: Current and future directions for 3D bioprinting. J. Tissue Eng. 2022;13:20417314221133480. doi: 10.1177/20417314221133480. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 46.Eming S.A., Brachvogel B., Odorisio T., Koch M. Regulation of angiogenesis: Wound healing as a model. Prog. Histochem. 2008;42:115–170. doi: 10.1016/j.proghi.2007.06.001. [DOI] [PubMed] [Google Scholar]
- 47.Xie H., Cui Z., Wang L., Xia Z., Hu Y., Xian L., Li C., Xie L., Crane J., Wan M. PDGF-BB secreted by preosteoclasts induces CD31hiEmcnhi vessel subtype in coupling osteogenesis. Nat. Med. 2014;20:1270–1278. doi: 10.1038/nm.3668. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 48.Fahimipour F., Rasoulianboroujeni M., Dashtimoghadam E., Khoshroo K., Tahriri M., Bastami F., Lobner D., Tayebi L.J.D.M. 3D printed TCP-based scaffold incorporating VEGF-loaded PLGA microspheres for craniofacial tissue engineering. Dent. Mater. 2017;33:1205–1216. doi: 10.1016/j.dental.2017.06.016. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 49.Lee H., Jang T.-S., Han G., Kim H.-W., Jung H.-D. Freeform 3D printing of vascularized tissues: Challenges and strategies. J. Tissue Eng. 2021;12:20417314211057236. doi: 10.1177/20417314211057236. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 50.Bianco P. Stem cells and bone: A historical perspective. Bone. 2015;70:2–9. doi: 10.1016/j.bone.2014.08.011. [DOI] [PubMed] [Google Scholar]
- 51.Martino M.M., Briquez P.S., Maruyama K., Hubbell J.A. Extracellular matrix-inspired growth factor delivery systems for bone regeneration. Adv. Drug Deliv. Rev. 2015;94:41–52. doi: 10.1016/j.addr.2015.04.007. [DOI] [PubMed] [Google Scholar]
- 52.Weng T., Zhang W., Xia Y., Wu P., Yang M., Jin R., Xia S., Wang J., You C., Han C., et al. 3D bioprinting for skin tissue engineering: Current status and perspectives. J. Tissue Eng. 2021;12:20417314211028574. doi: 10.1177/20417314211028574. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 53.Henning R.J. Therapeutic angiogenesis: Angiogenic growth factors for ischemic heart disease. Future Cardiol. 2016;12:585–599. doi: 10.2217/fca-2016-0006. [DOI] [PubMed] [Google Scholar]
- 54.Ribatti D., Vacca A., Nico B., Roncali L., Dammacco F. Postnatal vasculogenesis. Mech. Dev. 2001;100:157–163. doi: 10.1016/S0925-4773(00)00522-0. [DOI] [PubMed] [Google Scholar]
- 55.Shen X., Zhang Y., Gu Y., Xu Y., Liu Y., Li B., Chen L. Sequential and sustained release of SDF-1 and BMP-2 from silk fibroin-nanohydroxyapatite scaffold for the enhancement of bone regeneration. Biomater. 2016;106:205–216. doi: 10.1016/j.biomaterials.2016.08.023. [DOI] [PubMed] [Google Scholar]
- 56.Wenk E., Wandrey A.J., Merkle H.P., Meinel L. Silk fibroin spheres as a platform for controlled drug delivery. J. Control. Release. 2008;132:26–34. doi: 10.1016/j.jconrel.2008.08.005. [DOI] [PubMed] [Google Scholar]
- 57.Zelzer E., Mclean W., Ng Y.S., Fukai N., Reginato A.M., Lovejoy S., D’Amore P.A., Olsen B.R. Skeletal defects in VEGF(120/120) mice reveal multiple roles for VEGF in skeletogenesis. Development. 2002;129:1893. doi: 10.1242/dev.129.8.1893. [DOI] [PubMed] [Google Scholar]
- 58.Gerber H.P., Vu T.H., Ryan A.M., Kowalski J., Werb Z., Ferrara N.J.N.M. VEGF couples hypertrophic cartilage remodeling, ossification and angiogenesis during endochondral bone formation. Nat. Med. 1999;5:623–628. doi: 10.1038/9467. [DOI] [PubMed] [Google Scholar]
- 59.Tiede S., Ernst N., Bayat A., Paus R., Zechel C.J.A.o.A.-a.A. Basic fibroblast growth factor: A potential new therapeutic tool for the treatment of hypertrophic and keloid scars. Ann. Anat. Anat. Anz. 2009;191:33–44. doi: 10.1016/j.aanat.2008.10.001. [DOI] [PubMed] [Google Scholar]
- 60.Wu J., Ye J., Zhu J., Xiao Z., He C., Shi H., Wang Y., Lin C., Zhang H., Zhao Y.J.B. Heparin-Based Coacervate of FGF2 Improves Dermal Regeneration by Asserting a Synergistic Role with Cell Proliferation and Endogenous Facilitated VEGF for Cutaneous Wound Healing. Biomacromolecules. 2016;17:2168–2177. doi: 10.1021/acs.biomac.6b00398. [DOI] [PubMed] [Google Scholar]
- 61.Claffey K.P., Abrams K., Shih S.C., Brown L.F., Mullen A., Keough M.J.L.I. Fibroblast Growth Factor 2 Activation of Stromal Cell Vascular Endothelial Growth Factor Expression and Angiogenesis. Lab. Investig. 2001;81:61. doi: 10.1038/labinvest.3780212. [DOI] [PubMed] [Google Scholar]
- 62.Wang Y., Kim H.J., Vunjak-Novakovic G., Kaplan D.L. Stem cell-based tissue engineering with silk biomaterials. Biomaterials. 2006;27:6064–6082. doi: 10.1016/j.biomaterials.2006.07.008. [DOI] [PubMed] [Google Scholar]
- 63.Wang X., Gu Y., Xiong Z., Cui Z., Zhang T. Silk-molded flexible, ultrasensitive, and highly stable electronic skin for monitoring human physiological signals. Adv. Mater. 2014;26:1336–1342. doi: 10.1002/adma.201304248. [DOI] [PubMed] [Google Scholar]
- 64.Shen W., Chen X., Chen J., Yin Z., Heng B.C., Chen W., Ouyang H.W. The effect of incorporation of exogenous stromal cell-derived factor-1 alpha within a knitted silk-collagen sponge scaffold on tendon regeneration. Biomaterials. 2010;31:7239–7249. doi: 10.1016/j.biomaterials.2010.05.040. [DOI] [PubMed] [Google Scholar]
- 65.Benjamin L.E., Hemo I., Keshet E. A plasticity window for blood vessel remodeling is defined by pericyte coverage of the preformed endothelial network and is regulated by PDGF-B and VEGF. Development. 1998;125:1591–1598. doi: 10.1242/dev.125.9.1591. [DOI] [PubMed] [Google Scholar]
- 66.Nih L.R., Gojgini S., Carmichael S.T., Segura T. Dual-function injectable angiogenic biomaterial for the repair of brain tissue following stroke. Nat. Mater. 2018;17:642–651. doi: 10.1038/s41563-018-0083-8. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 67.Nie J.J., Qiao B., Duan S., Xu C., Chen B., Hao W., Xu F.J. Unlockable Nanocomplexes with Self-Accelerating Nucleic Acid Release for Effective Staged Gene Therapy of Cardiovascular Diseases. Adv. Mater. 2018;30:1801570. doi: 10.1002/adma.201801570. [DOI] [PubMed] [Google Scholar]
- 68.Liu B., Lee B.W., Nakanishi K., Villasante A., Williamson R., Metz J., Kim J., Kanai M., Bi L., Brown K., et al. Cardiac recovery via extended cell-free delivery of extracellular vesicles secreted by cardiomyocytes derived from induced pluripotent stem cells. Nat. Biomed. Eng. 2018;2:293–303. doi: 10.1038/s41551-018-0229-7. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 69.Hudalla G.A., Koepsel J.T., Murphy W.L. Surfaces that sequester serum-borne heparin amplify growth factor activity. Adv. Mater. 2011;23:5415–5418. doi: 10.1002/adma.201103046. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 70.You J., Shin D.S., Patel D., Gao Y., Revzin A. Multilayered heparin hydrogel microwells for cultivation of primary hepatocytes. Adv. Healthc. Mater. 2014;3:126–132. doi: 10.1002/adhm.201300054. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 71.Zhao B., Katagiri T., Toyoda H., Takada T., Yanai T., Fukuda T., Chung U.I., Koike T., Takaoka K., Kamijo R. Heparin potentiates the in vivo ectopic bone formation induced by bone morphogenetic protein-2. J. Biol. Chem. 2006;281:23246–23253. doi: 10.1074/jbc.M511039200. [DOI] [PubMed] [Google Scholar]
- 72.Jiao X., Billings P.C., O’Connell M.P., Kaplan F.S., Shore E.M., Glaser D.L. Heparan sulfate proteoglycans (HSPGs) modulate BMP2 osteogenic bioactivity in C2C12 cells. J. Biol. Chem. 2007;282:1080–1086. doi: 10.1074/jbc.M513414200. [DOI] [PubMed] [Google Scholar]
- 73.Silva C., Carretero A., Soares da Costa D., Reis R.L., Novoa-Carballal R., Pashkuleva I. Design of protein delivery systems by mimicking extracellular mechanisms for protection of growth factors. Acta Biomater. 2017;63:283–293. doi: 10.1016/j.actbio.2017.08.042. [DOI] [PubMed] [Google Scholar]
- 74.Zhang W., Feng C., Yang G., Li G., Ding X., Wang S., Dou Y., Zhang Z., Chang J., Wu C., et al. 3D-printed scaffolds with synergistic effect of hollow-pipe structure and bioactive ions for vascularized bone regeneration. Biomaterials. 2017;135:85–95. doi: 10.1016/j.biomaterials.2017.05.005. [DOI] [PubMed] [Google Scholar]
- 75.Yin S., Zhang W., Zhang Z., Jiang X. Recent Advances in Scaffold Design and Material for Vascularized Tissue-Engineered Bone Regeneration. Adv. Healthc. Mater. 2019;8:e1801433. doi: 10.1002/adhm.201801433. [DOI] [PubMed] [Google Scholar]
- 76.Li H., Xue K., Kong N., Liu K., Chang J. Silicate bioceramics enhanced vascularization and osteogenesis through stimulating interactions between endothelia cells and bone marrow stromal cells. Biomaterials. 2014;35:3803–3818. doi: 10.1016/j.biomaterials.2014.01.039. [DOI] [PubMed] [Google Scholar]
- 77.Li C., Jiang C., Deng Y., Li T., Li N., Peng M., Wang J. RhBMP-2 loaded 3D-printed mesoporous silica/calcium phosphate cement porous scaffolds with enhanced vascularization and osteogenesis properties. Sci. Rep. 2017;7:41331. doi: 10.1038/srep41331. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 78.Gu Y., Zhang J., Zhang X., Liang G., Xu T., Niu W. Three-dimensional Printed Mg-Doped β-TCP Bone Tissue Engineering Scaffolds: Effects of Magnesium Ion Concentration on Osteogenesis and Angiogenesis In Vitro. Tissue Eng. Regen. Med. 2019;16:415–429. doi: 10.1007/s13770-019-00192-0. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 79.Ma L., Cheng S., Ji X., Zhou Y., Zhang Y., Li Q., Tan C., Peng F., Zhang Y., Huang W. Immobilizing magnesium ions on 3D printed porous tantalum scaffolds with polydopamine for improved vascularization and osteogenesis. Mater. Sci. Eng. C Mater. Biol. Appl. 2020;117:111303. doi: 10.1016/j.msec.2020.111303. [DOI] [PubMed] [Google Scholar]
- 80.Wang W., Xiong Y., Zhao R., Li X., Jia W. A novel hierarchical biofunctionalized 3D-printed porous Ti6Al4V scaffold with enhanced osteoporotic osseointegration through osteoimmunomodulation. J. Nanobiotechnol. 2022;20:68. doi: 10.1186/s12951-022-01277-0. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 81.Li C., Ai F., Miao X., Liao H., Li F., Liu M., Yu F., Dong L., Li T., Wang X. “The return of ceramic implants”: Rose stem inspired dual layered modification of ceramic scaffolds with improved mechanical and anti-infective properties. Mater. Sci. Eng. C Mater. Biol. Appl. 2018;93:873–879. doi: 10.1016/j.msec.2018.08.044. [DOI] [PubMed] [Google Scholar]
- 82.Dang W., Ma B., Li B., Huan Z., Ma N., Zhu H., Chang J., Xiao Y., Wu C. 3D printing of metal-organic framework nanosheets-structured scaffolds with tumor therapy and bone construction. Biofabrication. 2020;12:025005. doi: 10.1088/1758-5090/ab5ae3. [DOI] [PubMed] [Google Scholar]
- 83.Vidakis N., Petousis M., Michailidis N., Grammatikos S., David C.N., Mountakis N., Argyros A., Boura O. Development and Optimization of Medical-Grade Multi-Functional Polyamide 12-Cuprous Oxide Nanocomposites with Superior Mechanical and Antibacterial Properties for Cost-Effective 3D Printing. Nanomaterials. 2022;12:534. doi: 10.3390/nano12030534. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 84.Lin R., Deng C., Li X., Liu Y., Zhang M., Qin C., Yao Q., Wang L., Wu C. Copper-incorporated bioactive glass-ceramics inducing anti-inflammatory phenotype and regeneration of cartilage/bone interface. Theranostics. 2019;9:6300–6313. doi: 10.7150/thno.36120. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 85.Wu Z., Hong Y. Combination of the Silver-Ethylene Interaction and 3D Printing To Develop Antibacterial Superporous Hydrogels for Wound Management. ACS Appl. Mater. Interfaces. 2019;11:33734–33747. doi: 10.1021/acsami.9b14090. [DOI] [PubMed] [Google Scholar]
- 86.Schwarz K., Ricci B.A., Punsar S., Karvonen M.J. Inverse relation of silicon in drinking water and atherosclerosis in Finland. Lancet. 1977;1:538–539. doi: 10.1016/S0140-6736(77)91393-9. [DOI] [PubMed] [Google Scholar]
- 87.Pietak A.M., Reid J.W., Stott M.J., Sayer M. Silicon substitution in the calcium phosphate bioceramics. Biomaterials. 2007;28:4023–4032. doi: 10.1016/j.biomaterials.2007.05.003. [DOI] [PubMed] [Google Scholar]
- 88.Kim N., Lee H., Han G., Kang M., Park S., Kim D.E., Lee M., Kim M.-J., Na Y., Oh S., et al. 3D-Printed Functional Hydrogel by DNA-Induced Biomineralization for Accelerated Diabetic Wound Healing. Adv. Sci. 2023;2:2300816. doi: 10.1002/advs.202300816. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 89.Shi M., Zhou Y., Shao J., Chen Z., Song B., Chang J., Wu C., Xiao Y. Stimulation of osteogenesis and angiogenesis of hBMSCs by delivering Si ions and functional drug from mesoporous silica nanospheres. Acta Biomater. 2015;21:178–189. doi: 10.1016/j.actbio.2015.04.019. [DOI] [PubMed] [Google Scholar]
- 90.Gorustovich A.A., Roether J.A., Boccaccini A.R. Effect of bioactive glasses on angiogenesis: A review of in vitro and in vivo evidences. Tissue Eng. Part B Rev. 2010;16:199–207. doi: 10.1089/ten.teb.2009.0416. [DOI] [PubMed] [Google Scholar]
- 91.Gerhardt L.C., Widdows K.L., Erol M.M., Burch C.W., Sanz-Herrera J.A., Ochoa I., Stämpfli R., Roqan I.S., Gabe S., Ansari T., et al. The pro-angiogenic properties of multi-functional bioactive glass composite scaffolds. Biomaterials. 2011;32:4096–4108. doi: 10.1016/j.biomaterials.2011.02.032. [DOI] [PubMed] [Google Scholar]
- 92.Nieves J.W. Bone. Maximizing bone health-magnesium, BMD and fractures. Nat. Rev. Endocrinol. 2014;10:255–256. doi: 10.1038/nrendo.2014.39. [DOI] [PubMed] [Google Scholar]
- 93.de Baaij J.H., Hoenderop J.G., Bindels R.J. Magnesium in man: Implications for health and disease. Physiol. Rev. 2015;95:1–46. doi: 10.1152/physrev.00012.2014. [DOI] [PubMed] [Google Scholar]
- 94.Maier J.A., Bernardini D., Rayssiguier Y., Mazur A. High concentrations of magnesium modulate vascular endothelial cell behaviour in vitro. Biochim. Biophys. Acta. 2004;1689:6–12. doi: 10.1016/j.bbadis.2004.02.004. [DOI] [PubMed] [Google Scholar]
- 95.Bernardini D., Nasulewic A., Mazur A., Maier J.A. Magnesium and microvascular endothelial cells: A role in inflammation and angiogenesis. Front. Biosci. A J. Virtual Libr. 2005;10:1177–1182. doi: 10.2741/1610. [DOI] [PubMed] [Google Scholar]
- 96.Romani A.M.P. Beneficial Role of Mg(2+) in Prevention and Treatment of Hypertension. Int. J. Hypertens. 2018;2018:9013721. doi: 10.1155/2018/9013721. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 97.Wang W., Yeung K.W.K. Bone grafts and biomaterials substitutes for bone defect repair: A review. Bioact. Mater. 2017;2:224–247. doi: 10.1016/j.bioactmat.2017.05.007. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 98.Tarafder S., Dernell W.S., Bandyopadhyay A., Bose S. SrO- and MgO-doped microwave sintered 3D printed tricalcium phosphate scaffolds: Mechanical properties and in vivo osteogenesis in a rabbit model. J. Biomed. Mater. Res. Part B Appl. Biomater. 2015;103:679–690. doi: 10.1002/jbm.b.33239. [DOI] [PubMed] [Google Scholar]
- 99.Zou F., Zhao N., Fu X., Diao J., Wang Y. Enhanced osteogenic differentiation and biomineralization in mouse mesenchymal stromal cells on a β-TCP robocast scaffold modified with collagen nanofibers. RSC Adv. 2016;6:23588–23598. doi: 10.1039/C5RA26670J. [DOI] [Google Scholar]
- 100.Tao W., Zeng X., Wu J., Zhu X., Yu X., Zhang X., Zhang J., Liu G., Mei L. Polydopamine-Based Surface Modification of Novel Nanoparticle-Aptamer Bioconjugates for In Vivo Breast Cancer Targeting and Enhanced Therapeutic Effects. Theranostics. 2016;6:470–484. doi: 10.7150/thno.14184. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 101.Li H., Peng F., Wang D., Qiao Y., Xu D., Liu X. Layered double hydroxide/poly-dopamine composite coating with surface heparinization on Mg alloys: Improved anticorrosion, endothelialization and hemocompatibility. Biomater. Sci. 2018;6:1846–1858. doi: 10.1039/C8BM00298C. [DOI] [PubMed] [Google Scholar]
- 102.Shi M., Chen Z., Farnaghi S., Friis T., Mao X., Xiao Y., Wu C. Copper-doped mesoporous silica nanospheres, a promising immunomodulatory agent for inducing osteogenesis. Acta Biomater. 2016;30:334–344. doi: 10.1016/j.actbio.2015.11.033. [DOI] [PubMed] [Google Scholar]
- 103.Sen C.K., Khanna S., Venojarvi M., Trikha P., Ellison E.C., Hunt T.K., Roy S. Copper-induced vascular endo-thelial growth factor expression and wound healing. Am. J. Physiol. Heart Circ. Physiol. 2002;282:H1821–H1827. doi: 10.1152/ajpheart.01015.2001. [DOI] [PubMed] [Google Scholar]
- 104.Kornblatt A.P., Nicoletti V.G., Travaglia A. The neglected role of copper ions in wound healing. J. Inorg. Biochem. 2016;161:1–8. doi: 10.1016/j.jinorgbio.2016.02.012. [DOI] [PubMed] [Google Scholar]
- 105.Wu M.X., Yang Y.W. Metal-Organic Framework (MOF)-Based Drug/Cargo Delivery and Cancer Therapy. Adv. Mater. 2017;29:1606134. doi: 10.1002/adma.201606134. [DOI] [PubMed] [Google Scholar]
- 106.Wang D., Zhou J., Shi R., Wu H., Chen R., Duan B., Xia G., Xu P., Wang H., Zhou S., et al. Biodegradable Core-shell Dual-Metal-Organic-Frameworks Nanotheranostic Agent for Multiple Imaging Guided Combination Cancer Therapy. Theranostics. 2017;7:4605–4617. doi: 10.7150/thno.20363. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 107.Piard C., Baker H., Kamalitdinov T., Fisher J. Bioprinted osteon-like scaffolds enhance in vivo neovascularization. Biofabrication. 2019;11:025013. doi: 10.1088/1758-5090/ab078a. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 108.Melero-Martin J.M., Khan Z.A., Picard A., Wu X., Paruchuri S., Bischoff J. In vivo vasculogenic potential of human blood-derived endothelial progenitor cells. Blood. 2007;109:4761–4768. doi: 10.1182/blood-2006-12-062471. [DOI] [PubMed] [Google Scholar]
- 109.Staton C.A., Reed M.W., Brown N.J. A critical analysis of current in vitro and in vivo angiogenesis assays. Int. J. Exp. Pathol. 2009;90:195–221. doi: 10.1111/j.1365-2613.2008.00633.x. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 110.Cidonio G., Glinka M., Kim Y.H., Kanczler J.M., Lanham S.A., Ahlfeld T., Lode A., Dawson J.I., Gelinsky M., Oreffo R.O.C. Nanoclay-based 3D printed scaffolds promote vascular ingrowth ex vivo and generate bone mineral tissue in vitro and in vivo. Biofabrication. 2020;12:035010. doi: 10.1088/1758-5090/ab8753. [DOI] [PubMed] [Google Scholar]
- 111.Farahani R.D., Dubé M., Therriault D. Three-Dimensional Printing of Multifunctional Nanocomposites: Manufacturing Techniques and Applications. Adv. Mater. 2016;28:5794–5821. doi: 10.1002/adma.201506215. [DOI] [PubMed] [Google Scholar]
- 112.Bates D.O. Vascular endothelial growth factors and vascular permeability. Cardiovasc. Res. 2010;87:262–271. doi: 10.1093/cvr/cvq105. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 113.Park S.S. Cell Therapy Applications for Retinal Vascular Diseases: Diabetic Retinopathy and Retinal Vein Occlusion. Investig. Ophthalmol. Vis. Sci. 2016;57:ORSFj1–ORSFj10. doi: 10.1167/iovs.15-17594. [DOI] [PubMed] [Google Scholar]
- 114.Pittenger M.F., Martin B.J. Mesenchymal stem cells and their potential as cardiac therapeutics. Circ. Res. 2004;95:9–20. doi: 10.1161/01.RES.0000135902.99383.6f. [DOI] [PubMed] [Google Scholar]
- 115.Pittenger M.F., Mackay A.M., Beck S.C., Jaiswal R.K., Douglas R., Mosca J.D., Moorman M.A., Simonetti D.W., Craig S., Marshak D.R. Multilineage potential of adult human mesenchymal stem cells. Sciences. 1999;284:143–147. doi: 10.1126/science.284.5411.143. [DOI] [PubMed] [Google Scholar]
- 116.Sheehy E.J., Mesallati T., Kelly L., Vinardell T., Buckley C.T., Kelly D.J. Tissue Engineering Whole Bones Through Endochondral Ossification: Regenerating the Distal Phalanx. BioRes. Open Access. 2015;4:229–241. doi: 10.1089/biores.2015.0014. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 117.Kanczler J.M., Oreffo R.O. Osteogenesis and angiogenesis: The potential for engineering bone. Eur. Cells Mater. 2008;15:100–114. doi: 10.22203/eCM.v015a08. [DOI] [PubMed] [Google Scholar]
- 118.Daly A.C., Pitacco P., Nulty J., Cunniffe G.M., Kelly D.J. 3D printed microchannel networks to direct vascularisation during endochondral bone repair. Biomaterials. 2018;162:34–46. doi: 10.1016/j.biomaterials.2018.01.057. [DOI] [PubMed] [Google Scholar]
- 119.Deng Y., Jiang C., Li C., Li T., Peng M., Wang J., Dai K. 3D printed scaffolds of calcium silicate-doped β-TCP synergize with co-cultured endothelial and stromal cells to promote vascularization and bone formation. Sci. Rep. 2017;7:5588. doi: 10.1038/s41598-017-05196-1. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 120.Rong Q., Li S., Zhou Y., Geng Y., Liu S., Wu W., Forouzanfar T., Wu G., Zhang Z., Zhou M. A novel method to improve the osteogenesis capacity of hUCMSCs with dual-directional pre-induction under screened co-culture conditions. Cell Prolif. 2020;53:e12740. doi: 10.1111/cpr.12740. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 121.Li J., Mao Q., He J., She H., Zhang Z., Yin C. Human umbilical cord mesenchymal stem cells improve the reserve function of perimenopausal ovary via a paracrine mechanism. Stem Cell Res. Ther. 2017;8:55. doi: 10.1186/s13287-017-0514-5. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 122.Paul K., Darzi S., McPhee G., Del Borgo M.P., Werkmeister J.A., Gargett C.E., Mukherjee S. 3D bioprinted endometrial stem cells on melt electrospun poly ε-caprolactone mesh for pelvic floor application promote anti-inflammatory responses in mice. Acta Biomater. 2019;97:162–176. doi: 10.1016/j.actbio.2019.08.003. [DOI] [PubMed] [Google Scholar]
- 123.Wang Y., Wan C., Deng L., Liu X., Cao X., Gilbert S.R., Bouxsein M.L., Faugere M.C., Guldberg R.E., Gerstenfeld L.C., et al. The hypoxia-inducible factor alpha pathway couples angiogenesis to osteogenesis during skeletal development. J. Clin. Investig. 2007;117:1616–1626. doi: 10.1172/JCI31581. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 124.Wan C., Gilbert S.R., Wang Y., Cao X., Shen X., Ramaswamy G., Jacobsen K.A., Alaql Z.S., Eberhardt A.W., Gerstenfeld L.C., et al. Activation of the hypoxia-inducible factor-1alpha pathway accelerates bone regeneration. Proc. Natl. Acad. Sci. USA. 2008;105:686–691. doi: 10.1073/pnas.0708474105. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 125.Kusumbe A.P., Ramasamy S.K., Adams R.H. Coupling of angiogenesis and osteogenesis by a specific vessel subtype in bone. Nature. 2014;507:323–328. doi: 10.1038/nature13145. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 126.Shen X., Wan C., Ramaswamy G., Mavalli M., Wang Y., Duvall C.L., Deng L.F., Guldberg R.E., Eberhart A., Clemens T.L., et al. Prolyl hydroxylase inhibitors increase neoangiogenesis and callus formation following femur fracture in mice. J. Orthop. Res. 2009;27:1298–1305. doi: 10.1002/jor.20886. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 127.Farberg A.S., Sarhaddi D., Donneys A., Deshpande S.S., Buchman S.R. Deferoxamine enhances bone regeneration in mandibular distraction osteogenesis. Plast. Reconstr. Surg. 2014;133:666–671. doi: 10.1097/01.prs.0000438050.36881.a9. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 128.Donneys A., Weiss D.M., Deshpande S.S., Ahsan S., Tchanque-Fossuo C.N., Sarhaddi D., Levi B., Goldstein S.A., Buchman S.R. Localized deferoxamine injection augments vascularity and improves bony union in pathologic fracture healing after radiotherapy. Bone. 2013;52:318–325. doi: 10.1016/j.bone.2012.10.014. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 129.Sukanya V.S., Mohanan P.V. Degradation of Poly(ε-caprolactone) and bio-interactions with mouse bone marrow mesenchymal stem cells. Colloids Surfaces. B Biointerfaces. 2018;163:107–118. doi: 10.1016/j.colsurfb.2017.12.039. [DOI] [PubMed] [Google Scholar]
- 130.Orozco-Castellanos L., Marcos-Fernández A., Martínez-Richa A. Hydrolytic degradation of poly(ε-caprolactone) with different end groups and poly(ε-caprolactone-co-γ-butyrolactone): Characterization and kinetics of hydrocortisone delivery. Polym. Adv. Technol. 2011;22:430–436. doi: 10.1002/pat.1531. [DOI] [Google Scholar]
- 131.Ragu S., Faye G., Iraqui I., Masurel-Heneman A., Kolodner R.D., Huang M.E. Oxygen metabolism and reactive oxygen species cause chromosomal rearrangements and cell death. Proc. Natl. Acad. Sci. USA. 2007;104:9747–9752. doi: 10.1073/pnas.0703192104. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 132.Poole K.M., Nelson C.E., Joshi R.V., Martin J.R., Gupta M.K., Haws S.C., Kavanaugh T.E., Skala M.C., Duvall C.L. ROS-responsive microspheres for on demand antioxidant therapy in a model of diabetic peripheral arterial disease. Biomaterials. 2015;41:166–175. doi: 10.1016/j.biomaterials.2014.11.016. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 133.Fraisl P., Mazzone M., Schmidt T., Carmeliet P. Regulation of angiogenesis by oxygen and metabolism. Dev. Cell. 2009;16:167–179. doi: 10.1016/j.devcel.2009.01.003. [DOI] [PubMed] [Google Scholar]
- 134.Pati F., Jang J., Ha D.H., Won Kim S., Rhie J.W., Shim J.H., Kim D.H., Cho D.W. Printing three-dimensional tissue analogues with decellularized extracellular matrix bioink. Nat. Commun. 2014;5:3935. doi: 10.1038/ncomms4935. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 135.Choi J.S., Kim B.S., Kim J.Y., Kim J.D., Choi Y.C., Yang H.J., Park K., Lee H.Y., Cho Y.W. Decellularized extracellular matrix derived from human adipose tissue as a potential scaffold for allograft tissue engineering. J. Biomed. Mater. Res. Part. A. 2011;97:292–299. doi: 10.1002/jbm.a.33056. [DOI] [PubMed] [Google Scholar]
- 136.Brown C.F., Yan J., Han T.T., Marecak D.M., Amsden B.G., Flynn L.E. Effect of decellularized adipose tissue particle size and cell density on adipose-derived stem cell proliferation and adipogenic differentiation in composite methacrylated chondroitin sulphate hydrogels. Biomed. Mater. 2015;10:045010. doi: 10.1088/1748-6041/10/4/045010. [DOI] [PubMed] [Google Scholar]
- 137.De Santis M.M., Alsafadi H.N., Tas S., Bölükbas D.A., Prithiviraj S., Da Silva I.A.N., Mittendorfer M., Ota C., Stegmayr J., Daoud F., et al. Extracellular-Matrix-Reinforced Bioinks for 3D Bioprinting Human Tissue. Adv. Mater. 2021;33:e2005476. doi: 10.1002/adma.202005476. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 138.Ross E.A., Williams M.J., Hamazaki T., Terada N., Clapp W.L., Adin C., Ellison G.W., Jorgensen M., Batich C.D. Embryonic stem cells proliferate and differentiate when seeded into kidney scaffolds. J. Am. Soc. Nephrol. JASN. 2009;20:2338–2347. doi: 10.1681/ASN.2008111196. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 139.Cortiella J., Niles J., Cantu A., Brettler A., Pham A., Vargas G., Winston S., Wang J., Walls S., Nichols J.E. Influence of acellular natural lung matrix on murine embryonic stem cell differentiation and tissue formation. Tissue Eng. Part A. 2010;16:2565–2580. doi: 10.1089/ten.tea.2009.0730. [DOI] [PubMed] [Google Scholar]
- 140.Lee H., Han W., Kim H., Ha D.H., Jang J., Kim B.S., Cho D.W. Development of Liver Decellularized Extracellular Matrix Bioink for Three-Dimensional Cell Printing-Based Liver Tissue Engineering. Biomacromolecules. 2017;18:1229–1237. doi: 10.1021/acs.biomac.6b01908. [DOI] [PubMed] [Google Scholar]
- 141.Choi Y.J., Kim T.G., Jeong J., Yi H.G., Park J.W., Hwang W., Cho D.W. 3D Cell Printing of Functional Skeletal Muscle Constructs Using Skeletal Muscle-Derived Bioink. Adv. Healthc. Mater. 2016;5:2636–2645. doi: 10.1002/adhm.201600483. [DOI] [PubMed] [Google Scholar]
- 142.French K.M., Boopathy A.V., DeQuach J.A., Chingozha L., Lu H., Christman K.L., Davis M.E. A naturally derived cardiac extracellular matrix enhances cardiac progenitor cell behavior in vitro. Acta Biomater. 2012;8:4357–4364. doi: 10.1016/j.actbio.2012.07.033. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 143.Kumar V.A., Liu Q., Wickremasinghe N.C., Shi S., Cornwright T.T., Deng Y., Azares A., Moore A.N., Acevedo-Jake A.M., Agudo N.R., et al. Treatment of hind limb ischemia using angiogenic peptide nanofibers. Biomaterials. 2016;98:113–119. doi: 10.1016/j.biomaterials.2016.04.032. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 144.Rahim K., Saleha S., Zhu X., Huo L., Basit A., Franco O.L. Bacterial Contribution in Chronicity of Wounds. Microb. Ecol. 2017;73:710–721. doi: 10.1007/s00248-016-0867-9. [DOI] [PubMed] [Google Scholar]
- 145.Bessa L.J., Fazii P., Di Giulio M., Cellini L. Bacterial isolates from infected wounds and their antibiotic susceptibility pattern: Some remarks about wound infection. Int. Wound J. 2015;12:47–52. doi: 10.1111/iwj.12049. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 146.Davies D. Understanding biofilm resistance to antibacterial agents. Nat. Rev. Drug Discov. 2003;2:114–122. doi: 10.1038/nrd1008. [DOI] [PubMed] [Google Scholar]
- 147.Veerachamy S., Yarlagadda T., Manivasagam G., Yarlagadda P.K. Bacterial adherence and biofilm formation on medical implants: A review. Proc. Inst. Mech. Engineers. Part H J. Eng. Med. 2014;228:1083–1099. doi: 10.1177/0954411914556137. [DOI] [PubMed] [Google Scholar]
- 148.Cyphert E.L., Zhang N., Learn G.D., Hernandez C.J., von Recum H.A. Recent Advances in the Evaluation of Antimicrobial Materials for Resolution of Orthopedic Implant-Associated Infections In Vivo. ACS Infect. Dis. 2021;7:3125–3160. doi: 10.1021/acsinfecdis.1c00465. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 149.VanEpps J.S., Younger J.G. Implantable Device-Related Infection. Shock. 2016;46:597–608. doi: 10.1097/SHK.0000000000000692. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 150.Schierholz J.M., Beuth J. Implant infections: A haven for opportunistic bacteria. J. Hosp. Infect. 2001;49:87–93. doi: 10.1053/jhin.2001.1052. [DOI] [PubMed] [Google Scholar]
- 151.Kim J.S., Kuk E., Yu K.N., Kim J.H., Park S.J., Hu J.L., Kim S.H., Park Y.K., Yong H.P., Hwang C.Y. Antimicrobial effects of silver nanoparticles. Nanomed. Nanotechnol. Biol. Med. 2007;3:95–101. doi: 10.1016/j.nano.2006.12.001. [DOI] [PubMed] [Google Scholar]
- 152.Guzman M., Dille J., Godet S. Synthesis and antibacterial activity of silver nanoparticles against gram-positive and gram-negative bacteria. Nanomed. Nanotechnol. Biol. Med. 2012;8:37–45. doi: 10.1016/j.nano.2011.05.007. [DOI] [PubMed] [Google Scholar]
- 153.Qing Y., Cheng L., Li R., Liu G., Zhang Y., Tang X., Wang J., Liu H., Qin Y. Potential antibacterial mechanism of silver nanoparticles and the optimization of orthopedic implants by advanced modification technologies. Int. J. Nanomed. 2018;13:3311–3327. doi: 10.2147/IJN.S165125. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 154.García-Astrain C., Chen C., Burón M., Palomares T., Eceiza A., Fruk L., Corcuera M., Gabilondo N. Biocompatible hydrogel nanocomposite with covalently embedded silver nanoparticles. Biomacromolecules. 2015;16:1301–1310. doi: 10.1021/acs.biomac.5b00101. [DOI] [PubMed] [Google Scholar]
- 155.Dubey P., Matai I., Kumar S.U., Sachdev A., Bhushan B., Gopinath P. Perturbation of cellular mechanistic system by silver nanoparticle toxicity: Cytotoxic, genotoxic and epigenetic potentials. Adv. Colloid Interface Sci. 2015;221:4–21. doi: 10.1016/j.cis.2015.02.007. [DOI] [PubMed] [Google Scholar]
- 156.Kangari H., Abedini-Talemi A., Akbarzadeh-Bagheban A., Rahmani S. Comparison of Two Marketed Hydroxypropyl Methylcellulose Based Artificial Tear Drops in Young Patients with Dry Eye Syndrome. Nov. Biomed. 2015;3:193–199. [Google Scholar]
- 157.Powers J.G., Morton L.M., Phillips T.J. Dressings for chronic wounds. Dermatol. Ther. 2013;26:197–206. doi: 10.1111/dth.12055. [DOI] [PubMed] [Google Scholar]
- 158.Li Y., Liu X., Li B., Zheng Y., Han Y., Chen D.F., Yeung K.W.K., Cui Z., Liang Y., Li Z., et al. Near-Infrared Light Triggered Phototherapy and Immunotherapy for Elimination of Methicillin-Resistant Staphylococcus aureus Biofilm Infection on Bone Implant. ACS Nano. 2020;14:8157–8170. doi: 10.1021/acsnano.0c01486. [DOI] [PubMed] [Google Scholar]
- 159.Soleymaniha M., Shahbazi M.A., Rafieerad A.R., Maleki A., Amiri A. Promoting Role of MXene Nanosheets in Biomedical Sciences: Therapeutic and Biosensing Innovations. Adv. Healthc. Mater. 2019;8:e1801137. doi: 10.1002/adhm.201801137. [DOI] [PubMed] [Google Scholar]
- 160.Parajuli D., Murali N., Karki B., Samatha K., Kim A.A., Park M., Pant B. Advancements in MXene-Polymer Nanocomposites in Energy Storage and Biomedical Applications. Polymers. 2022;14:3433. doi: 10.3390/polym14163433. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 161.Pan S., Yin J., Yu L., Zhang C., Zhu Y., Gao Y., Chen Y. 2D MXene-Integrated 3D-Printing Scaffolds for Augmented Osteosarcoma Phototherapy and Accelerated Tissue Reconstruction. Adv. Sci. 2020;7:1901511. doi: 10.1002/advs.201901511. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 162.Rasool K., Helal M., Ali A., Ren C.E., Gogotsi Y., Mahmoud K.A. Antibacterial Activity of Ti₃C₂Tx MXene. ACS Nano. 2016;10:3674–3684. doi: 10.1021/acsnano.6b00181. [DOI] [PubMed] [Google Scholar]
- 163.Han X., Huang J., Lin H., Wang Z., Li P., Chen Y. 2D Ultrathin MXene-Based Drug-Delivery Nanoplatform for Synergistic Photothermal Ablation and Chemotherapy of Cancer. Adv. Healthc. Mater. 2018;7:e1701394. doi: 10.1002/adhm.201701394. [DOI] [PubMed] [Google Scholar]
- 164.Yang C., Luo Y., Lin H., Ge M., Shi J., Zhang X. Niobium Carbide MXene Augmented Medical Implant Elicits Bacterial Infection Elimination and Tissue Regeneration. ACS Nano. 2021;15:1086–1099. doi: 10.1021/acsnano.0c08045. [DOI] [PubMed] [Google Scholar]
- 165.Zada S., Lu H., Yang F., Zhang Y., Cheng Y., Tang S., Wei W., Qiao Y., Fu P., Dong H., et al. V(2)C Nanosheets as Dual-Functional Antibacterial Agents. ACS Appl. Bio Mater. 2021;4:4215–4223. doi: 10.1021/acsabm.1c00008. [DOI] [PubMed] [Google Scholar]
- 166.Rao J., Lahiri J., Isaacs L., Weis R.M., Whitesides G.M. A trivalent system from vancomycin.D-ala-D-Ala with higher affinity than avidin.biotin. Sciences. 1998;280:708–711. doi: 10.1126/science.280.5364.708. [DOI] [PubMed] [Google Scholar]
- 167.He W., Bai J., Chen X., Suo D., Wang S., Guo Q., Yin W., Geng D., Wang M., Pan G., et al. Reversible dougong structured receptor-ligand recognition for building dynamic extracellular matrix mimics. Proc. Natl. Acad. Sci. USA. 2022;119:e2117221119. doi: 10.1073/pnas.2117221119. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 168.Andrei S., Valeanu L., Chirvasuta R., Stefan M.G. New FDA approved antibacterial drugs: 2015–2017. Discov. 2018;6:e81. doi: 10.15190/d.2018.1. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 169.Cicuéndez M., Doadrio J.C., Hernández A., Portolés M.T., Izquierdo-Barba I., Vallet-Regí M. Multifunctional pH sensitive 3D scaffolds for treatment and prevention of bone infection. Acta Biomater. 2018;65:450–461. doi: 10.1016/j.actbio.2017.11.009. [DOI] [PubMed] [Google Scholar]
- 170.Zuza E., Meaurio E., Sarasua J.R. Biodegradable Polylactide-Based Composites. IntechOpen; London, UK: 2016. [Google Scholar]
- 171.Garrido-Mesa N., Zarzuelo A., Gálvez J. Minocycline: Far beyond an antibiotic. Br. J. Pharmacol. 2013;169:337–352. doi: 10.1111/bph.12139. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 172.Silva T., Grenho L., Barros J., Silva J.C., Pinto R.V., Matos A., Colaço B., Fernandes M.H., Bettencourt A., Gomes P.S. A minocycline-releasing PMMA system as a space maintainer for staged bone reconstructions-in vitro antibacterial, cytocompatibility and anti-inflammatory characterization. Biomed. Mater. 2017;12:035009. doi: 10.1088/1748-605X/aa68b8. [DOI] [PubMed] [Google Scholar]
- 173.Ferreira M., Rzhepishevska O., Grenho L., Malheiros D., Gonçalves L., Almeida A.J., Jordão L., Ribeiro I.A., Ramstedt M., Gomes P., et al. Levofloxacin-loaded bone cement delivery system: Highly effective against intracellular bacteria and Staphylococcus aureus biofilms. Int. J. Pharm. 2017;532:241–248. doi: 10.1016/j.ijpharm.2017.08.089. [DOI] [PubMed] [Google Scholar]
- 174.Dou X.C., Zhu X.P., Zhou J., Cai H.Q., Tang J., Li Q.L. Minocycline-released hydroxyapatite-gelatin nanocomposite and its cytocompatibility in vitro. Biomed. Mater. 2011;6:025002. doi: 10.1088/1748-6041/6/2/025002. [DOI] [PubMed] [Google Scholar]
- 175.Luo J.D., Chen A.F. Nitric oxide: A newly discovered function on wound healing. Acta Pharmacol. Sin. 2005;26:259–264. doi: 10.1111/j.1745-7254.2005.00058.x. [DOI] [PubMed] [Google Scholar]
- 176.Fang F.C. Perspectives series: Host/pathogen interactions. Mechanisms of nitric oxide-related antimicrobial activity. J. Clin. Investig. 1997;99:2818–2825. doi: 10.1172/JCI119473. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 177.Moreno-Jiménez I., Hulsart-Billstrom G., Lanham S.A., Janeczek A.A., Kontouli N., Kanczler J.M., Evans N.D., Oreffo R.O. The chorioallantoic membrane (CAM) assay for the study of human bone regeneration: A refinement animal model for tissue engineering. Sci. Rep. 2016;6:32168. doi: 10.1038/srep32168. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 178.Sharifi-Rad J., Sharifi-Rad M., Hoseini-Alfatemi S.M., Iriti M., Sharifi-Rad M., Sharifi-Rad M. Composition, Cytotoxic and Antimicrobial Activities of Satureja intermedia C.A.Mey Essential Oil. Int. J. Mol. Sci. 2015;16:17812–17825. doi: 10.3390/ijms160817812. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 179.Skocibusić M., Bezić N. Phytochemical analysis and in vitro antimicrobial activity of two Satureja species essential oils. Phytother. Res. PTR. 2004;18:967–970. doi: 10.1002/ptr.1489. [DOI] [PubMed] [Google Scholar]
- 180.Jafari F., Ghavidel F., Zarshenas M.M. A Critical Overview on the Pharmacological and Clinical Aspects of Popular Satureja Species. J. Acupunct. Meridian Stud. 2016;9:118–127. doi: 10.1016/j.jams.2016.04.003. [DOI] [PubMed] [Google Scholar]
- 181.Sait U., Uca N., Kartal M.U., Altun M.L., Sayar E. GC-MS Analysis and Antibacterial Activity of Cultivated Satureja cuneifolia Ten. Essential Oil. Turk. J. Chem. 2014;30:253–259. [Google Scholar]
- 182.Pt A., Ek B., Acgc D., Eb E., Aa F., Mk G., Sa H., Lg I.J.A.J.o.C. Anti-Alzheimer, antidiabetic and antioxidant potential of Satureja cuneifolia and analysis of its phenolic contents by LC-MS/MS. Arab. J. Chem. 2020;13:4528–4537. [Google Scholar]
- 183.Mochalin V.N., Shenderova O., Ho D., Gogotsi Y. The properties and applications of nanodiamonds. Nat. Nanotechnol. 2011;7:11–23. doi: 10.1038/nnano.2011.209. [DOI] [PubMed] [Google Scholar]
- 184.Amaral M., Dias A.G., Gomes P.S., Lopes M.A., Silva R.F., Santos J.D., Fernandes M.H. Nanocrystalline diamond: In vitro biocompatibility assessment by MG63 and human bone marrow cells cultures. J. Biomed. Mater. Res. Part A. 2008;87:91–99. doi: 10.1002/jbm.a.31742. [DOI] [PubMed] [Google Scholar]
- 185.Wehling J., Dringen R., Zare R.N., Maas M., Rezwan K. Bactericidal activity of partially oxidized nanodiamonds. ACS Nano. 2014;8:6475–6483. doi: 10.1021/nn502230m. [DOI] [PubMed] [Google Scholar]
- 186.Papo M.J., Catledge S.A., Vohra Y.K., Machado C. Mechanical wear behavior of nanocrystalline and multilayer diamond coatings on temporomandibular joint implants. J. Mater. Sci. Mater. Med. 2004;15:773–777. doi: 10.1023/B:JMSM.0000032817.05997.d2. [DOI] [PubMed] [Google Scholar]
- 187.Catledge S.A., Thomas V., Vohra Y.K. Nanostructured diamond coatings for orthopaedic applications. Woodhead Publ. Ser. Biomater. 2013;2013:105–150. doi: 10.1533/9780857093516.2.105. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 188.Ueno H., Mori T., Fujinaga T. Topical formulations and wound healing applications of chitosan. Adv. Drug Deliv Rev. 2001;52:105–115. doi: 10.1016/S0169-409X(01)00189-2. [DOI] [PubMed] [Google Scholar]
- 189.Azad A.K., Sermsintham N., Chandrkrachang S., Stevens W.F. Chitosan membrane as a wound-healing dressing: Characterization and clinical application. J. Biomed. Mater. Res. Part B Appl. Biomater. 2004;69:216–222. doi: 10.1002/jbm.b.30000. [DOI] [PubMed] [Google Scholar]
- 190.Ahmed S., Ikram S. Chitosan Based Scaffolds and Their Applications in Wound Healing. Achiev. Life Sci. 2016;10:27–37. doi: 10.1016/j.als.2016.04.001. [DOI] [Google Scholar]
- 191.Kucharska M., Sikora M., Brzoza-Malczewska K., Owczarek M. Chitin and Chitosan. Wiley; Hoboken, NJ, USA: 2019. Antimicrobial Properties of Chitin and Chitosan; pp. 169–187. [DOI] [Google Scholar]
- 192.Thian E.S., Konishi T., Kawanobe Y., Lim P.N., Choong C., Ho B., Aizawa M. Zinc-substituted hydroxyapatite: A biomaterial with enhanced bioactivity and antibacterial properties. J. Mater. Sci. Mater. Med. 2013;24:437–445. doi: 10.1007/s10856-012-4817-x. [DOI] [PubMed] [Google Scholar]
- 193.Voicu G., Miu D., Ghitulica C.D., Jinga S.I., Holban A.M. Co doped ZnO thin films deposited by spin coating as antibacterial coating for metallic implants. Ceram. Int. 2019;46:3904–3911. doi: 10.1016/j.ceramint.2019.10.118. [DOI] [Google Scholar]
- 194.Liu Y., He L., Mustapha A., Li H., Hu Z.Q., Lin M. Antibacterial activities of zinc oxide nanoparticles against Escherichia coli O157:H7. J. Appl. Microbiol. 2009;107:1193–1201. doi: 10.1111/j.1365-2672.2009.04303.x. [DOI] [PubMed] [Google Scholar]
- 195.Chhabra H., Deshpande R., Kanitkar M., Jaiswal A., Kale V.P., Bellare J.R. A nano zinc oxide doped electrospun scaffold improves wound healing in a rodent model. RSC Adv. 2015;6:1428–1439. doi: 10.1039/C5RA21821G. [DOI] [Google Scholar]
- 196.Jin S.E., Hwang W., Lee H.J., Jin H.E. Dual UV irradiation-based metal oxide nanoparticles for enhanced antimicrobial activity in Escherichia coli and M13 bacteriophage. Int. J. Nanomed. 2017;12:8057–8070. doi: 10.2147/IJN.S144236. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 197.Liu J., Rojas-Andrade M.D., Chata G., Peng Y., Roseman G., Lu J.E., Millhauser G.L., Saltikov C., Chen S. Photo-enhanced antibacterial activity of ZnO/graphene quantum dot nanocomposites. Nanoscale. 2017;10:158–166. doi: 10.1039/C7NR07367D. [DOI] [PubMed] [Google Scholar]
- 198.Raja A., Ashokkumar S., Pavithra Marthandam R., Jayachandiran J., Khatiwada C.P., Kaviyarasu K., Ganapathi Raman R., Swaminathan M. Eco-friendly preparation of zinc oxide nanoparticles using Tabernaemontana divaricata and its photocatalytic and antimicrobial activity. J. Photochem. Photobiol. B Biol. 2018;181:53–58. doi: 10.1016/j.jphotobiol.2018.02.011. [DOI] [PubMed] [Google Scholar]
- 199.Bhande R.M., Khobragade C.N., Mane R.S., Bhande S. Enhanced synergism of antibiotics with zinc oxide nanoparticles against extended spectrum β-lactamase producers implicated in urinary tract infections. J. Nanoparticle Res. 2013;15:1413. doi: 10.1007/s11051-012-1413-4. [DOI] [Google Scholar]
- 200.Li M., Lin D., Zhu L. Effects of water chemistry on the dissolution of ZnO nanoparticles and their toxicity to Escherichia coli. Environ. Pollut. 2013;173:97–102. doi: 10.1016/j.envpol.2012.10.026. [DOI] [PubMed] [Google Scholar]
- 201.Liao H., Miao X., Ye J., Wu T., Deng Z., Li C., Jia J., Cheng X., Wang X. Falling Leaves Inspired ZnO Nanorods-Nanoslices Hierarchical Structure for Implant Surface Modification with Two Stage Releasing Features. ACS Appl. Mater. Interfaces. 2017;9:13009–13015. doi: 10.1021/acsami.7b00666. [DOI] [PubMed] [Google Scholar]
- 202.Lutsenko S. Human copper homeostasis: A network of interconnected pathways. Curr. Opin. Chem. Biol. 2010;14:211–217. doi: 10.1016/j.cbpa.2010.01.003. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 203.Hasan N.M., Lutsenko S. Regulation of copper transporters in human cells. Curr. Top. Membr. 2012;69:137–161. doi: 10.1016/b978-0-12-394390-3.00006-9. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 204.Noyce J.O., Michels H., Keevil C.W. Potential use of copper surfaces to reduce survival of epidemic meticillin-resistant Staphylococcus aureus in the healthcare environment. J. Hosp. Infect. 2006;63:289–297. doi: 10.1016/j.jhin.2005.12.008. [DOI] [PubMed] [Google Scholar]
- 205.Kadiiska M.B., Mason R.P. In vivo copper-mediated free radical production: An ESR spin-trapping study. Spectrochim. Acta. Part A Mol. Biomol. Spectrosc. 2002;58:1227–1239. doi: 10.1016/S1386-1425(01)00713-2. [DOI] [PubMed] [Google Scholar]
- 206.Jiménez Del Río M., Vélez-Pardo C. Transition metal-induced apoptosis in lymphocytes via hydroxyl radical generation, mitochondria dysfunction, and caspase-3 activation: An in vitro model for neurodegeneration. Arch. Med. Res. 2004;35:185–193. doi: 10.1016/j.arcmed.2004.01.001. [DOI] [PubMed] [Google Scholar]
- 207.Warnes S.L., Caves V., Keevil C.W. Mechanism of copper surface toxicity in Escherichia coli O157:H7 and Salmonella involves immediate membrane depolarization followed by slower rate of DNA destruction which differs from that observed for Gram-positive bacteria. Environ. Microbiol. 2012;14:1730–1743. doi: 10.1111/j.1462-2920.2011.02677.x. [DOI] [PubMed] [Google Scholar]
- 208.Hodgkinson V., Petris M.J. Copper homeostasis at the host-pathogen interface. J. Biol. Chem. 2012;287:13549–13555. doi: 10.1074/jbc.R111.316406. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 209.Dilberoglu U.M., Gharehpapagh B., Yaman U., Dolen M. The Role of Additive Manufacturing in the Era of Industry 4.0. Procedia Manuf. 2017;11:545–554. doi: 10.1016/j.promfg.2017.07.148. [DOI] [Google Scholar]
- 210.Gisario A., Kazarian M., Martina F., Mehrpouya M. Metal additive manufacturing in the commercial aviation industry: A review. J. Manuf. Syst. 2019;53:124–149. doi: 10.1016/j.jmsy.2019.08.005. [DOI] [Google Scholar]
- 211.Vidakis N., Petousis M., Maniadi A., Koudoumas E., Liebscher M., Tzounis L. Mechanical Properties of 3D-Printed Acrylonitrile-Butadiene-Styrene TiO(2) and ATO Nanocomposites. Polymers. 2020;12:1589. doi: 10.3390/polym12071589. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 212.Ford S., Despeisse M. Additive manufacturing and sustainability: An exploratory study of the advantages and challenges. J. Clean. Prod. 2016;137:1573–1587. doi: 10.1016/j.jclepro.2016.04.150. [DOI] [Google Scholar]
- 213.Turner R.D., Wingham J.R., Paterson T.E., Shepherd J., Majewski C. Use of silver-based additives for the development of antibacterial functionality in Laser Sintered polyamide 12 parts. Sci. Rep. 2020;10:892. doi: 10.1038/s41598-020-57686-4. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 214.Li Y.D., Guan J.P., Tang R.C., Qiao Y.F. Application of Natural Flavonoids to Impart Antioxidant and Antibacterial Activities to Polyamide Fiber for Health Care Applications. Antioxidants. 2019;8:301. doi: 10.3390/antiox8080301. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 215.Wencke Y.L., Kutlu Y., Seefeldt M., Esen C., Ostendorf A., Luinstra G.A. Additive manufacturing of PA12 carbon nanotube composites with a novel laser polymer deposition process. J. Appl. Polym. Sci. 2021;138:50395. doi: 10.1002/app.50395. [DOI] [Google Scholar]
- 216.Espera A.H., Valino A.D., Palaganas J.O., Souza L., Chen Q., Advincula R.C. 3D Printing of a Robust Polyamide-12-Carbon Black Composite via Selective Laser Sintering: Thermal and Electrical Conductivity. Macromol. Mater. Eng. 2019;304:1800718. doi: 10.1002/mame.201800718. [DOI] [Google Scholar]
- 217.Liu Y.C., Zou X.B., Chai Y.F., Yao Y.M. Macrophage polarization in inflammatory diseases. Int. J. Biol. Sci. 2014;10:520–529. doi: 10.7150/ijbs.8879. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 218.Sridharan R., Cameron A.R., Kelly D.J., Kearney C.J., Today F.O.B.J.M. Biomaterial based modulation of macrophage polarization: A review and suggested design principles. Mater. Today. 2015;18:313–325. doi: 10.1016/j.mattod.2015.01.019. [DOI] [Google Scholar]
- 219.Fernandes T.L., Gomoll A.H., Lattermann C., Hernandez A.J., Bueno D.F., Amano M.T. Macrophage: A Potential Target on Cartilage Regeneration. Front. Immunol. 2020;11:111. doi: 10.3389/fimmu.2020.00111. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 220.Stout R.D., Watkins S.K., Suttles J. Functional plasticity of macrophages: In situ reprogramming of tumor-associated macrophages. J. Leukoc. Biol. 2009;86:1105–1109. doi: 10.1189/jlb.0209073. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 221.Arnold L., Henry A., Poron F., Baba-Amer Y., van Rooijen N., Plonquet A., Gherardi R.K., Chazaud B. Inflammatory monocytes recruited after skeletal muscle injury switch into antiinflammatory macrophages to support myogenesis. J. Exp. Med. 2007;204:1057–1069. doi: 10.1084/jem.20070075. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 222.Mantovani A., Sica A., Allavena P., Garlanda C., Locati M. Tumor-associated macrophages and the related myeloid-derived suppressor cells as a paradigm of the diversity of macrophage activation. Hum. Immunol. 2009;70:325–330. doi: 10.1016/j.humimm.2009.02.008. [DOI] [PubMed] [Google Scholar]
- 223.Troidl C., Möllmann H., Nef H., Masseli F., Voss S., Szardien S., Willmer M., Rolf A., Rixe J., Troidl K., et al. Classically and alternatively activated macrophages contribute to tissue remodelling after myocardial infarction. J. Cells Mol. Med. 2009;13:3485–3496. doi: 10.1111/j.1582-4934.2009.00707.x. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 224.Yunna C., Mengru H., Lei W., Weidong C. Macrophage M1/M2 polarization. Eur. J. Pharmacol. 2020;877:173090. doi: 10.1016/j.ejphar.2020.173090. [DOI] [PubMed] [Google Scholar]
- 225.Viola A., Munari F., Sánchez-Rodríguez R., Scolaro T., Castegna A. The Metabolic Signature of Macrophage Responses. Front. Immunol. 2019;10:1462. doi: 10.3389/fimmu.2019.01462. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 226.Saklatvala J. Glucocorticoids: Do we know how they work? Arthritis Res. 2002;4:146–150. doi: 10.1186/ar398. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 227.Lasa M., Brook M., Saklatvala J., Clark A.R. Dexamethasone destabilizes cyclooxygenase 2 mRNA by inhibiting mitogen-activated protein kinase p38. Mol. Cells Biol. 2001;21:771–780. doi: 10.1128/MCB.21.3.771-780.2001. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 228.Oray M., Abu Samra K., Ebrahimiadib N., Meese H., Foster C.S. Long-term side effects of glucocorticoids. Expert Opin. Drug Saf. 2016;15:457–465. doi: 10.1517/14740338.2016.1140743. [DOI] [PubMed] [Google Scholar]
- 229.Kim D.H., Martin D.C. Sustained release of dexamethasone from hydrophilic matrices using PLGA nanoparticles for neural drug delivery. Biomaterials. 2006;27:3031–3037. doi: 10.1016/j.biomaterials.2005.12.021. [DOI] [PubMed] [Google Scholar]
- 230.Rodrigues P.O., Becker A.C., Dellagnelo V.A., Benetti C.N., Pereira E.M., Wagner T.M., Silva M.A.S. Pharmacodynamic and Pharmacokinetic Studies of β-Cyclodextrin:Dexamethasone Acetate Complexes in Mice. Braz. Arch. Biol. Technol. 2014;57:887–894. doi: 10.1590/S1516-8913201400874. [DOI] [Google Scholar]
- 231.Loftsson T., Stefánsson E. Cyclodextrins in ocular drug delivery: Theoretical basis with dexamethasone as a sample drug. J. Drug Deliv. Sci. Technol. 2007;17:3–9. doi: 10.1016/S1773-2247(07)50001-8. [DOI] [Google Scholar]
- 232.Lopez R.F., Collett J.H., Bentley M.V. Influence of cyclodextrin complexation on the in vitro permeation and skin metabolism of dexamethasone. Int. J. Pharm. 2000;200:127–132. doi: 10.1016/S0378-5173(00)00365-3. [DOI] [PubMed] [Google Scholar]
- 233.Loftsson T., Fririksdóttir H., Thórisdóttir S., Stefánsson E. The effect of hydroxypropyl methylcellulose on the release of dexamethasone from aqueous 2-hydroxypropyl-β-cyclodextrin formulations. Int. J. Pharm. 1994;104:181–184. doi: 10.1016/0378-5173(94)90194-5. [DOI] [Google Scholar]
- 234.Doile M.M., Fortunato K.A., Schmücker I.C., Schucko S.K., Silva M.A., Rodrigues P.O. Physicochemical properties and dissolution studies of dexamethasone acetate-beta-cyclodextrin inclusion complexes produced by different methods. AAPS PharmSciTech. 2008;9:314–321. doi: 10.1208/s12249-008-9042-z. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 235.Zhao C., Zuo F., Liao Z., Qin Z., Du S., Zhao Z. Mussel-inspired one-pot synthesis of a fluorescent and water-soluble polydopamine-polyethyleneimine copolymer. Macromol. Rapid Commun. 2015;36:909–915. doi: 10.1002/marc.201500021. [DOI] [PubMed] [Google Scholar]
- 236.Sang J.L., Jo H.H., Lim K.S., Lim D., Su A.P. Heparin coating on 3D printed poly (l-lactic acid) biodegradable cardiovascular stent via mild surface modification approach for coronary artery implantation. Chem. Eng. J. 2019;378:122116. [Google Scholar]
- 237.Bost M., Houdart S., Oberli M., Kalonji E., Huneau J.F., Margaritis I. Dietary copper and human health: Current evidence and unresolved issues. J. Trace Elem. Med. Biol. Organ Soc. Miner. Trace Elem. GMS. 2016;35:107–115. doi: 10.1016/j.jtemb.2016.02.006. [DOI] [PubMed] [Google Scholar]
- 238.Medeiros D.M. Copper, iron, and selenium dietary deficiencies negatively impact skeletal integrity: A review. Exp. Biol. Med. 2016;241:1316–1322. doi: 10.1177/1535370216648805. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 239.Goggs R., Vaughan-Thomas A., Clegg P.D., Carter S.D., Innes J.F., Mobasheri A., Shakibaei M., Schwab W., Bondy C.A. Nutraceutical therapies for degenerative joint diseases: A critical review. Crit. Rev. Food Sci. Nutr. 2005;45:145–164. doi: 10.1080/10408690590956341. [DOI] [PubMed] [Google Scholar]
- 240.Solier S., Müller S., Cañeque T., Versini A., Mansart A., Sindikubwabo F., Baron L., Emam L., Gestraud P., Pantoș G.D., et al. A druggable copper-signalling pathway that drives inflammation. Nature. 2023;617:386–394. doi: 10.1038/s41586-023-06017-4. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 241.Pham P.C., Pham P.A., Pham S.V., Pham P.T., Pham P.M., Pham P.T. Hypomagnesemia: A clinical perspective. Int. J. Nephrol. Renov. Dis. 2014;7:219–230. doi: 10.2147/IJNRD.S42054. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 242.McLean R.M. Magnesium and its therapeutic uses: A review. Am. J. Med. 1994;96:63–76. doi: 10.1016/0002-9343(94)90117-1. [DOI] [PubMed] [Google Scholar]
- 243.Rice N.R., Ernst M.K. In vivo control of NF-kappa B activation by I kappa B alpha. EMBO J. 1993;12:4685–4695. doi: 10.1002/j.1460-2075.1993.tb06157.x. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 244.Rechsteiner M., Rogers S.W. PEST sequences and regulation by proteolysis. Trends Biochem. Sci. 1996;21:267–271. doi: 10.1016/S0968-0004(96)10031-1. [DOI] [PubMed] [Google Scholar]
- 245.Didonato J.A., Mercurio F., Karin M. Phosphorylation of IκB α precedes but is not sufficient for its dissociation from NF-κB. Mol. Cells Biol. 1995;15:1302–1311. doi: 10.1128/MCB.15.3.1302. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 246.Nakano T., Katsuki S., Chen M., Decano J.L., Halu A., Lee L.H., Pestana D.V.S., Kum A.S.T., Kuromoto R.K., Golden W.S., et al. Uremic Toxin Indoxyl Sulfate Promotes Proinflammatory Macrophage Activation Via the Interplay of OATP2B1 and Dll4-Notch Signaling. Circulation. 2019;139:78–96. doi: 10.1161/CIRCULATIONAHA.118.034588. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 247.Kim M.J., Park J.S., Lee S.J., Jang J., Park J.S., Back S.H., Bahn G., Park J.H., Kang Y.M., Kim S.H., et al. Notch1 targeting siRNA delivery nanoparticles for rheumatoid arthritis therapy. J. Control. Release Off. 2015;216:140–148. doi: 10.1016/j.jconrel.2015.08.025. [DOI] [PubMed] [Google Scholar]
- 248.Xu C.Q., Liu B.J., Wu J.F., Xu Y.C., Duan X.H., Cao Y.X., Dong J.C. Icariin attenuates LPS-induced acute inflammatory responses: Involvement of PI3K/Akt and NF-kappaB signaling pathway. Eur. J. Pharmacol. 2010;642:146–153. doi: 10.1016/j.ejphar.2010.05.012. [DOI] [PubMed] [Google Scholar]
- 249.Sun X., Deng X., Cai W., Li W., Shen Z., Jiang T., Huang J. Icariin inhibits LPS-induced cell inflammatory response by promoting GRα nuclear translocation and upregulating GRα expression. Life Sci. 2018;195:33–43. doi: 10.1016/j.lfs.2018.01.006. [DOI] [PubMed] [Google Scholar]
- 250.Horcajada P., Gref R., Baati T., Allan P.K., Maurin G., Couvreur P., Férey G., Morris R.E., Serre C. Metal-organic frameworks in biomedicine. Chem. Rev. 2012;112:1232–1268. doi: 10.1021/cr200256v. [DOI] [PubMed] [Google Scholar]
- 251.Hu Q., Yu J., Liu M., Liu A., Dou Z., Yang Y. A low cytotoxic cationic metal-organic framework carrier for controllable drug release. J. Med. Chem. 2014;57:5679–5685. doi: 10.1021/jm5004107. [DOI] [PubMed] [Google Scholar]
- 252.Frazer K.A., Ueda Y., Zhu Y., Gifford V.R., Garofalo M.R., Mohandas N., Martin C.H., Palazzolo M.J., Cheng J.F., Rubin E.M. Computational and biological analysis of 680 kb of DNA sequence from the human 5q31 cytokine gene cluster region. Genome Res. 1997;7:495–512. doi: 10.1101/gr.7.5.495. [DOI] [PubMed] [Google Scholar]
- 253.Bao K., Reinhardt R.L. The differential expression of IL-4 and IL-13 and its impact on type-2 immunity. Cytokine. 2015;75:25–37. doi: 10.1016/j.cyto.2015.05.008. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 254.Hershey G.K. IL-13 receptors and signaling pathways: An evolving web. J. Allergy Clin. Immunol. 2003;111:677–690; quiz 691. doi: 10.1067/mai.2003.1333. [DOI] [PubMed] [Google Scholar]
- 255.Brombacher F. The role of interleukin-13 in infectious diseases and allergy. BioEssays News Rev. Mol. Cells Dev. Biol. 2000;22:646–656. doi: 10.1002/1521-1878(200007)22:7<646::AID-BIES7>3.0.CO;2-9. [DOI] [PubMed] [Google Scholar]
- 256.Nauta A.J., Fibbe W.E. Immunomodulatory properties of mesenchymal stromal cells. Blood. 2007;110:3499–3506. doi: 10.1182/blood-2007-02-069716. [DOI] [PubMed] [Google Scholar]
- 257.Lo Sicco C., Reverberi D., Balbi C., Ulivi V., Principi E., Pascucci L., Becherini P., Bosco M.C., Varesio L., Franzin C., et al. Mesenchymal Stem Cell-Derived Extracellular Vesicles as Mediators of Anti-Inflammatory Effects: Endorsement of Macrophage Polarization. Stem Cells Transl. Med. 2017;6:1018–1028. doi: 10.1002/sctm.16-0363. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 258.Dimarino A.M., Caplan A.I., Bonfield T.L. Mesenchymal stem cells in tissue repair. Front. Immunol. 2013;4:201. doi: 10.3389/fimmu.2013.00201. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 259.Zhao J., Li X., Hu J., Chen F., Qiao S., Sun X., Gao L., Xie J., Xu B. Mesenchymal stromal cell-derived exosomes attenuate myocardial ischaemia-reperfusion injury through miR-182-regulated macrophage polarization. Cardiovasc. Res. 2019;115:1205–1216. doi: 10.1093/cvr/cvz040. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 260.Song N., Scholtemeijer M., Shah K. Mesenchymal Stem Cell Immunomodulation: Mechanisms and Therapeutic Potential. Trends Pharmacol. Sci. 2020;41:653–664. doi: 10.1016/j.tips.2020.06.009. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 261.Reischl S., Lee J.H., Miltschitzky J.R.E., Vieregge V., Walter R.L., Twardy V., Kasajima A., Friess H., Kamaly N., Neumann P.A. Ac2-26-Nanoparticles Induce Resolution of Intestinal Inflammation and Anastomotic Healing via Inhibition of NF-κB Signaling in a Model of Perioperative Colitis. Inflamm. Bowel Dis. 2021;27:1379–1393. doi: 10.1093/ibd/izab008. [DOI] [PubMed] [Google Scholar]
- 262.Pupjalis D., Goetsch J., Kottas D.J., Gerke V., Rescher U. Annexin A1 released from apoptotic cells acts through formyl peptide receptors to dampen inflammatory monocyte activation via JAK/STAT/SOCS signalling. EMBO Mol. Med. 2011;3:102–114. doi: 10.1002/emmm.201000113. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 263.Huang J.J., Xia C.J., Wei Y., Yao Y., Dong M.W., Lin K.Z., Yu L.S., Gao Y., Fan Y.Y. Annexin A1-derived peptide Ac2-26 facilitates wound healing in diabetic mice. Wound Repair Regen. 2020;28:772–779. doi: 10.1111/wrr.12860. [DOI] [PubMed] [Google Scholar]
- 264.Tsekova P.B., Spasova M.G., Manolova N.E., Markova N.D., Rashkov I.B. Electrospun curcumin-loaded cellulose acetate/polyvinylpyrrolidone fibrous materials with complex architecture and antibacterial activity. Mater. Sci. Eng. C Mater. Biol. Appl. 2017;73:206–214. doi: 10.1016/j.msec.2016.12.086. [DOI] [PubMed] [Google Scholar]
- 265.Ahsan H., Parveen N., Khan N.U., Hadi S.M. Pro-oxidant, anti-oxidant and cleavage activities on DNA of curcumin and its derivatives demethoxycurcumin and bisdemethoxycurcumin. Chem. Biol. Interact. 1999;121:161–175. doi: 10.1016/S0009-2797(99)00096-4. [DOI] [PubMed] [Google Scholar]
- 266.Pulido-Moran M., Moreno-Fernandez J., Ramirez-Tortosa C., Ramirez-Tortosa M. Curcumin and Health. Molecules. 2016;21:264. doi: 10.3390/molecules21030264. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 267.Karuppagounder V., Arumugam S., Thandavarayan R.A., Sreedhar R., Giridharan V.V., Afrin R., Harima M., Miyashita S., Hara M., Suzuki K., et al. Curcumin alleviates renal dysfunction and suppresses inflammation by shifting from M1 to M2 macrophage polarization in daunorubicin induced nephrotoxicity in rats. Cytokine. 2016;84:1–9. doi: 10.1016/j.cyto.2016.05.001. [DOI] [PubMed] [Google Scholar]
- 268.Kim S.J. Curcumin suppresses the production of interleukin-6 in Prevotella intermedia lipopolysaccharide-activated RAW 264.7 cells. J. Periodontal Implant Sci. 2011;41:157–163. doi: 10.5051/jpis.2011.41.3.157. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 269.Lee K.H., Chow Y.L., Sharmili V., Abas F., Alitheen N.B., Shaari K., Israf D.A., Lajis N.H., Syahida A. BDMC33, A curcumin derivative suppresses inflammatory responses in macrophage-like cellular system: Role of inhibition in NF-κB and MAPK signaling pathways. Int. J. Mol. Sci. 2012;13:2985–3008. doi: 10.3390/ijms13032985. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 270.Huang C.Y., Huang T.H., Kao C.T., Wu Y.H., Chen W.C., Shie M.Y. Mesoporous Calcium Silicate Nanoparticles with Drug Delivery and Odontogenesis Properties. J. Endod. 2017;43:69–76. doi: 10.1016/j.joen.2016.09.012. [DOI] [PubMed] [Google Scholar]
- 271.Moustapha A., Pérétout P.A., Rainey N.E., Sureau F., Geze M., Petit J.M., Dewailly E., Slomianny C., Petit P.X. Curcumin induces crosstalk between autophagy and apoptosis mediated by calcium release from the endoplasmic reticulum, lysosomal destabilization and mitochondrial events. Cell Death Discov. 2015;1:15017. doi: 10.1038/cddiscovery.2015.17. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 272.Lemos D.R., Babaeijandaghi F., Low M., Chang C.K., Lee S.T., Fiore D., Zhang R.H., Natarajan A., Nedospasov S.A., Rossi F.M. Nilotinib reduces muscle fibrosis in chronic muscle injury by promoting TNF-mediated apoptosis of fibro/adipogenic progenitors. Nat. Med. 2015;21:786–794. doi: 10.1038/nm.3869. [DOI] [PubMed] [Google Scholar]
- 273.Kim D.C., Ku S.K., Bae J.S. Anticoagulant activities of curcumin and its derivative. BMB Rep. 2012;45:221–226. doi: 10.5483/BMBRep.2012.45.4.221. [DOI] [PubMed] [Google Scholar]
- 274.Zhang D.W., Fu M., Gao S.H., Liu J.L. Curcumin and diabetes: A systematic review. Evid. Based Complement. Altern. Med. Ecam. 2013;2013:636053. doi: 10.1155/2013/636053. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 275.Setchell K.D. Phytoestrogens: The biochemistry, physiology, and implications for human health of soy isoflavones. Am. J. Clin. Nutr. 1998;68:1333s–1346s. doi: 10.1093/ajcn/68.6.1333S. [DOI] [PubMed] [Google Scholar]
- 276.Banerjee S., Li Y., Wang Z., Sarkar F.H. Multi-targeted therapy of cancer by genistein. Cancer Lett. 2008;269:226–242. doi: 10.1016/j.canlet.2008.03.052. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 277.Jia T.L., Wang H.Z., Xie L.P., Wang X.Y., Zhang R.Q. Daidzein enhances osteoblast growth that may be mediated by increased bone morphogenetic protein (BMP) production. Biochem. Pharmacol. 2003;65:709–715. doi: 10.1016/S0006-2952(02)01585-X. [DOI] [PubMed] [Google Scholar]
- 278.Li H.Y., Pan L., Ke Y.S., Batnasan E., Jin X.Q., Liu Z.Y., Ba X.Q. Daidzein suppresses pro-inflammatory chemokine Cxcl2 transcription in TNF-α-stimulated murine lung epithelial cells via depressing PARP-1 activity. Acta Pharmacol. Sin. 2014;35:496–503. doi: 10.1038/aps.2013.191. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 279.Smith B.N., Dilger R.N. Immunomodulatory potential of dietary soybean-derived isoflavones and saponins in pigs. J. Anim. Sci. 2018;96:1288–1304. doi: 10.1093/jas/sky036. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 280.Lai H.H., Yen G.C. Inhibitory effect of isoflavones on peroxynitrite-mediated low-density lipoprotein oxidation. Biosci. Biotechnol. Biochem. 2002;66:22–28. doi: 10.1271/bbb.66.22. [DOI] [PubMed] [Google Scholar]
- 281.García-Lafuente A., Guillamón E., Villares A., Rostagno M.A., Martínez J.A. Flavonoids as anti-inflammatory agents: Implications in cancer and cardiovascular disease. Inflamm. Res. 2009;58:537–552. doi: 10.1007/s00011-009-0037-3. [DOI] [PubMed] [Google Scholar]
- 282.Eo H., Ann J.Y., Lim Y. Dietary Supplementation of Genistein Attenuates Inflammatory Responses and Oxidative Stress during Cutaneous Wound Healing in Diabetic Mice. J. Agric. Sci. 2015;7:80. doi: 10.5539/jas.v7n2p80. [DOI] [Google Scholar]
- 283.Barnes P.J., Karin M. Nuclear factor-kappaB: A pivotal transcription factor in chronic inflammatory diseases. N. Engl. J. Med. 1997;336:1066–1071. doi: 10.1056/NEJM199704103361506. [DOI] [PubMed] [Google Scholar]
- 284.Russo M., Spagnuolo C., Tedesco I., Bilotto S., Russo G.L. The flavonoid quercetin in disease prevention and therapy: Facts and fancies. Biochem. Pharmacol. 2012;83:6–15. doi: 10.1016/j.bcp.2011.08.010. [DOI] [PubMed] [Google Scholar]
- 285.Zhou Y., Wu Y., Ma W., Jiang X., Takemra A., Uemura M., Xia L., Lin K., Xu Y. The effect of quercetin delivery system on osteogenesis and angiogenesis under osteoporotic conditions. J. Mater. Chemistry. B. 2017;5:612–625. doi: 10.1039/C6TB02312F. [DOI] [PubMed] [Google Scholar]
- 286.Wang Y., Li C., Wan Y., Qi M., Chen Q., Sun Y., Sun X., Fang J., Fu L., Xu L., et al. Quercetin-Loaded Ceria Nanocomposite Potentiate Dual-Directional Immunoregulation via Macrophage Polarization against Periodontal Inflammation. Small. 2021;17:e2101505. doi: 10.1002/smll.202101505. [DOI] [PubMed] [Google Scholar]
- 287.Hu Y., Gui Z., Zhou Y., Xia L., Lin K., Xu Y. Quercetin alleviates rat osteoarthritis by inhibiting inflammation and apoptosis of chondrocytes, modulating synovial macrophages polarization to M2 macrophages. Free Radic. Biol. Med. 2019;145:146–160. doi: 10.1016/j.freeradbiomed.2019.09.024. [DOI] [PubMed] [Google Scholar]
- 288.Tan R.Z., Wang C., Deng C., Zhong X., Yan Y., Luo Y., Lan H.Y., He T., Wang L. Quercetin protects against cisplatin-induced acute kidney injury by inhibiting Mincle/Syk/NF-κB signaling maintained macrophage inflammation. Phytother. Res. PTR. 2020;34:139–152. doi: 10.1002/ptr.6507. [DOI] [PubMed] [Google Scholar]
- 289.Sun S., Chen W., Cao W., Zhang F., Song J., Tian C. Research on the chelation between quercetin and Cr(III) ion by Density Functional Theory (DFT) method. J. Mol. Struct. THEOCHEM. 2008;860:40–44. doi: 10.1016/j.theochem.2008.03.020. [DOI] [Google Scholar]
- 290.Ricard-Blum S. The collagen family. Cold Spring Harb. Perspect. Biol. 2011;3:a004978. doi: 10.1101/cshperspect.a004978. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 291.Theocharis A.D., Skandalis S.S., Gialeli C., Karamanos N.K. Extracellular matrix structure. Adv. Drug Deliv Rev. 2016;97:4–27. doi: 10.1016/j.addr.2015.11.001. [DOI] [PubMed] [Google Scholar]
- 292.Friedman S.L. Evolving challenges in hepatic fibrosis. Nat. Rev. Gastroenterol. Hepatol. 2010;7:425–436. doi: 10.1038/nrgastro.2010.97. [DOI] [PubMed] [Google Scholar]
- 293.Coelho N.M., McCulloch C.A. Contribution of collagen adhesion receptors to tissue fibrosis. Cell Tissue Res. 2016;365:521–538. doi: 10.1007/s00441-016-2440-8. [DOI] [PubMed] [Google Scholar]
- 294.Zhang Y.P., Li W.B., Wang W.L., Liu J., Song S.X., Bai L.L., Hu Y.Y., Yuan Y.D., Zhang M. siRNA against plasminogen activator inhibitor-1 ameliorates bleomycin-induced lung fibrosis in rats. Acta Pharmacol. Sin. 2012;33:897–908. doi: 10.1038/aps.2012.39. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 295.Sefat F., Denyer M.C., Youseffi M. Effects of different transforming growth factor beta (TGF-β) isomers on wound closure of bone cell monolayers. Cytokine. 2014;69:75–86. doi: 10.1016/j.cyto.2014.05.010. [DOI] [PubMed] [Google Scholar]
- 296.Mueller S., Phillips J., Onar-Thomas A., Romero E., Zheng S., Wiencke J.K., McBride S.M., Cowdrey C., Prados M.D., Weiss W.A., et al. PTEN promoter methylation and activation of the PI3K/Akt/mTOR pathway in pediatric gliomas and influence on clinical outcome. Neuro-Oncology. 2012;14:1146–1152. doi: 10.1093/neuonc/nos140. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 297.Tsai P.C., Zhang Z., Florek C., Michniak-Kohn B.B. Constructing Human Skin Equivalents on Porcine Acellular Peritoneum Extracellular Matrix for In Vitro Irritation Testing. Tissue Eng. Part A. 2016;22:111–122. doi: 10.1089/ten.tea.2015.0209. [DOI] [PubMed] [Google Scholar]
- 298.Stark H.J., Boehnke K., Mirancea N., Willhauck M.J., Pavesio A., Fusenig N.E., Boukamp P. Epidermal homeostasis in long-term scaffold-enforced skin equivalents. J. Investig. Dermatol. Symp. Proc. 2006;11:93–105. doi: 10.1038/sj.jidsymp.5650015. [DOI] [PubMed] [Google Scholar]
- 299.Karsdal M.A., Detlefsen S., Daniels S.J., Nielsen M.J., Krag A., Schuppan D. Is the Total Amount as Important as Localization and Type of Collagen in Liver Fibrosis Attributable to Steatohepatitis? Hepatology. 2020;71:346–351. doi: 10.1002/hep.30969. [DOI] [PubMed] [Google Scholar]
- 300.Feng W., Ye F., Xue W., Zhou Z., Kang Y.J. Copper regulation of hypoxia-inducible factor-1 activity. Mol. Pharmacol. 2009;75:174–182. doi: 10.1124/mol.108.051516. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 301.Duval E., Leclercq S., Elissalde J.M., Demoor M., Galéra P., Boumédiene K. Hypoxia-inducible factor 1alpha inhibits the fibroblast-like markers type I and type III collagen during hypoxia-induced chondrocyte redifferentiation: Hypoxia not only induces type II collagen and aggrecan, but it also inhibits type I and type III collagen in the hypoxia-inducible factor 1alpha-dependent redifferentiation of chondrocytes. Arthritis Rheum. 2009;60:3038–3048. doi: 10.1002/art.24851. [DOI] [PubMed] [Google Scholar]
- 302.Agarwal S., Loder S., Brownley C., Cholok D., Mangiavini L., Li J., Breuler C., Sung H.H., Li S., Ranganathan K., et al. Inhibition of Hif1α prevents both trauma-induced and genetic heterotopic ossification. Proc. Natl. Acad. Sci. USA. 2016;113:E338–E347. doi: 10.1073/pnas.1515397113. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 303.Wynn T.A., Ramalingam T.R. Mechanisms of fibrosis: Therapeutic translation for fibrotic disease. Nat. Med. 2012;18:1028–1040. doi: 10.1038/nm.2807. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 304.Uccelli A., Moretta L., Pistoia V. Mesenchymal stem cells in health and disease. Nat. Reviews. Immunol. 2008;8:726–736. doi: 10.1038/nri2395. [DOI] [PubMed] [Google Scholar]
- 305.Wu M., Ji S., Xiao S., Kong Z., Fang H., Zhang Y., Ji K., Zheng Y., Liu H., Xia Z. JAM-A promotes wound healing by enhancing both homing and secretory activities of mesenchymal stem cells. Clin. Sci. 2015;129:575–588. doi: 10.1042/CS20140735. [DOI] [PubMed] [Google Scholar]
- 306.Zhang J., Guan J., Niu X., Hu G., Guo S., Li Q., Xie Z., Zhang C., Wang Y. Exosomes released from human induced pluripotent stem cells-derived MSCs facilitate cutaneous wound healing by promoting collagen synthesis and angiogenesis. J. Transl. Med. 2015;13:49. doi: 10.1186/s12967-015-0417-0. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 307.Wang X., Ma Y., Gao Z., Yang J. Human adipose-derived stem cells inhibit bioactivity of keloid fibroblasts. Stem Cell Res. Ther. 2018;9:40. doi: 10.1186/s13287-018-0786-4. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 308.Aoki M., Miyake K., Ogawa R., Dohi T., Akaishi S., Hyakusoku H., Shimada T. siRNA knockdown of tissue inhibitor of metalloproteinase-1 in keloid fibroblasts leads to degradation of collagen type I. J. Investig. Dermatol. 2014;134:818–826. doi: 10.1038/jid.2013.396. [DOI] [PubMed] [Google Scholar]
- 309.Zhang B., Wang M., Gong A., Zhang X., Wu X., Zhu Y., Shi H., Wu L., Zhu W., Qian H., et al. HucMSC-Exosome Mediated-Wnt4 Signaling Is Required for Cutaneous Wound Healing. Stem Cells. 2015;33:2158–2168. doi: 10.1002/stem.1771. [DOI] [PubMed] [Google Scholar]
- 310.Sun Q., Nakata H., Yamamoto M., Kasugai S., Kuroda S. Comparison of gingiva-derived and bone marrow mesenchymal stem cells for osteogenesis. J. Cells Mol. Med. 2019;23:7592–7601. doi: 10.1111/jcmm.14632. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 311.Moshaverinia A., Xu X., Chen C., Ansari S., Zadeh H.H., Snead M.L., Shi S. Application of stem cells derived from the periodontal ligament or gingival tissue sources for tendon tissue regeneration. Biomaterials. 2014;35:2642–2650. doi: 10.1016/j.biomaterials.2013.12.053. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 312.Chaussain Miller C., Septier D., Bonnefoix M., Lecolle S., Lebreton-Decoster C., Coulomb B., Pellat B., Godeau G. Human dermal and gingival fibroblasts in a three-dimensional culture: A comparative study on matrix remodeling. Clin. Oral Investig. 2002;6:39–50. doi: 10.1007/s00784-001-0143-2. [DOI] [PubMed] [Google Scholar]
- 313.Shafiee A., Cavalcanti A.S., Saidy N.T., Schneidereit D., Friedrich O., Ravichandran A., De-Juan-Pardo E.M., Hutmacher D.W. Convergence of 3D printed biomimetic wound dressings and adult stem cell therapy. Biomaterials. 2021;268:120558. doi: 10.1016/j.biomaterials.2020.120558. [DOI] [PubMed] [Google Scholar]
- 314.Cavalcante M.B., Costa Fda S., Barini R., Araujo Júnior E. Granulocyte colony-stimulating factor and reproductive medicine: A review. Iran. J. Reprod. Med. 2015;13:195–202. [PMC free article] [PubMed] [Google Scholar]
- 315.Malashchenko V.V., Meniailo M.E., Shmarov V.A., Gazatova N.D., Melashchenko O.B., Goncharov A.G., Seledtsova G.V., Seledtsov V.I. Direct anti-inflammatory effects of granulocyte colony-stimulating factor (G-CSF) on activation and functional properties of human T cell subpopulations in vitro. Cells Immunol. 2018;325:23–32. doi: 10.1016/j.cellimm.2018.01.007. [DOI] [PubMed] [Google Scholar]
- 316.Lin X., Zhang Y., Pan Y., He S., Dai Y., Zhu B., Wei C., Xin L., Xu W., Xiang C., et al. Endometrial stem cell-derived granulocyte-colony stimulating factor attenuates endometrial fibrosis via sonic hedgehog transcriptional activator Gli2. Biol. Reprod. 2018;98:480–490. doi: 10.1093/biolre/ioy005. [DOI] [PubMed] [Google Scholar]
- 317.Zhao S., Zhang Y., Tian H., Chen X., Cai D., Yao W., Gao X. Extending the serum half-life of G-CSF via fusion with the domain III of human serum albumin. BioMed Res. Int. 2013;2013:107238. doi: 10.1155/2013/107238. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 318.Choi S.H., Park T.G. G-CSF loaded biodegradable PLGA nanoparticles prepared by a single oil-in-water emulsion method. Int. J. Pharm. 2006;311:223–228. doi: 10.1016/j.ijpharm.2005.12.023. [DOI] [PubMed] [Google Scholar]
- 319.Zhao M., Song B., Pu J., Wada T., Reid B., Tai G., Wang F., Guo A., Walczysko P., Gu Y., et al. Electrical signals control wound healing through phosphatidylinositol-3-OH kinase-gamma and PTEN. Nature. 2006;442:457–460. doi: 10.1038/nature04925. [DOI] [PubMed] [Google Scholar]
- 320.Sorg H., Tilkorn D.J., Hager S., Hauser J., Mirastschijski U. Skin Wound Healing: An Update on the Current Knowledge and Concepts. Eur. Surg. Res. Eur. Chir. Forschung. Rech. Chir. Eur. 2017;58:81–94. doi: 10.1159/000454919. [DOI] [PubMed] [Google Scholar]
- 321.Rhett J.M., Ghatnekar G.S., Palatinus J.A., O’Quinn M., Yost M.J., Gourdie R.G. Novel therapies for scar reduction and regenerative healing of skin wounds. Trends Biotechnol. 2008;26:173–180. doi: 10.1016/j.tibtech.2007.12.007. [DOI] [PubMed] [Google Scholar]
- 322.Kang G.-d., Cao Y.-m. Application and modification of poly(vinylidene fluoride) (PVDF) membranes—A review. J. Membr. Sci. 2014;463:145–165. doi: 10.1016/j.memsci.2014.03.055. [DOI] [Google Scholar]
- 323.Efome J.E., Rana D., Matsuura T., Lan C.Q. Enhanced performance of PVDF nanocomposite membrane by nanofiber coating: A membrane for sustainable desalination through MD. Water Res. 2016;89:39–49. doi: 10.1016/j.watres.2015.11.040. [DOI] [PubMed] [Google Scholar]
- 324.Devi P.I., Ramachandran K. Dielectric studies on hybridised PVDF–ZnO nanocomposites. J. Exp. Nanosci. 2011;6:281–293. doi: 10.1080/17458080.2010.497947. [DOI] [Google Scholar]
- 325.Xu Q., Guo L., Gao Y., Zhou D., Greiser U., Creagh-Flynn J., Zhang H., Dong Y., Cutlar L. Injectable hyperbranched poly(β-amino ester) hydrogels with on-demand degradation profiles to match wound healing processes. Chem. Sci. 2018;9:2179–2187. doi: 10.1039/C7SC03913A. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 326.Jang T.-S., Park S.J., Lee J.E., Yang J., Park S.-H., Jun M.B.-G., Kim Y.W., Aranas C., Choi J.P., Zou Y., et al. Topography-Supported Nanoarchitectonics of Hybrid Scaffold for Systematically Modulated Bone Regeneration and Remodeling. Adv. Funct. Mater. 2022;32:2206863. doi: 10.1002/adfm.202206863. [DOI] [Google Scholar]
Associated Data
This section collects any data citations, data availability statements, or supplementary materials included in this article.
Data Availability Statement
Not applicable.