. 2025 Nov 5;16(46):5009–5018. doi: 10.1039/d5py00959f

Exploring transamidation and chemical recycling of β-amino amide-derived covalent adaptable networks

Loc Tan Nguyen a, Adithya Tharayil a, Nezha Badi a, Johan M Winne b,✉, Filip E Du Prez a,✉
PMCID: PMC12604615  PMID: 41230435

Abstract

The growing environmental challenge of non-recyclable thermosets underscores the urgent need for sustainable alternatives. Covalent adaptable networks (CANs) containing dynamic β-amino amide moieties have emerged as promising reprocessable polymer networks, combining mechanical robustness with recyclability. In this work, we elucidate the exchange kinetics of both the well-established (retro)-aza-Michael addition and a newly identified transamidation pathway that is operative in β-amino amides. Systematic catalyst screening reveals that acidic catalysts significantly enhance viscoelastic control, thereby improving (re)processing efficiency. Furthermore, we introduce a chemical recycling protocol that enables the recovery of the original amino building blocks with up to 86% purity, demonstrating their direct use as feedstock in material (re)synthesis. These insights advance the fundamental understanding of dynamic bond exchange in β-amino amide based CANs and establish a viable route towards circular thermoset materials for numerous applications.

This study explores a newly identified transamidation exchange in the β-amino amide dynamic covalent chemistry and the chemical recycling of β-amino amide-derived covalent adaptable networks.graphic file with name d5py00959f-ga.jpg

Introduction

Since their first introduction in the early 20th century, synthetic thermosets have undergone a remarkable development, playing a pivotal role in modern industry nowadays.1 Their cross-linked polymeric structures impart a unique combination of low weight and high mechanical strength, making them indispensable in demanding applications ranging from aviation components to wind turbine blades.2 However, the permanent network structure also renders thermosets intrinsically non-reprocessable, consequently consigning them to permanent waste at their end-of-life. This fact results in widespread challenges from both environmental and regulatory perspectives.3,4

Covalent adaptable networks (CANs), also referred to as dynamic covalent polymer networks, have emerged in recent decades as a promising approach to reconcile the durability of thermosets with reprocessability.5–7 By incorporating exchangeable (or dynamic) linkages, CANs facilitate reprocessability of thermosets under specific stimuli such as heat or light, while (ideally) retaining the superior properties of polymeric networks.6,8 A wide range of dynamic chemistry platforms have been introduced in CANs, including transesterifications,9,10 and vinylogous urethane,11,12 Diels–Alder,13,14 dithioacetal,15 and imine exchange,16,17 a few of which have progressed toward commercial products.18,19 Despite this progress, their practical adoption is still constrained due to their dynamicity–performance trade-off.20,21 While dynamic bonds endow CANs with recyclability, they are typically labile (low activation energies – Ea), which can lead to premature bond exchange (i.e., flow or creep) under reaction conditions.22 As a consequence, this phenomenon leads to an undesirable loss in the designated performance of CANs, thus often making them unsuitable for replacing conventional thermosets. Addressing this long-standing limitation requires the development of suitable dynamic covalent chemistry (DCC) and/or technologies that combine robustness with controlled exchange reactivity.

Polyamides, long recognized for their outstanding thermal and chemical stability, are particularly attractive for advancing CAN performance.23 However, this inherent stability of amide bonds also implies their relative inertness towards exchange reactions, resulting in their limited exploration as a DCC-platform in CANs to date. In 2021, one of the first amide-based DCCs for CAN was reported by us and others through a dicarboxamide-imide equilibrium, governed by the imide ring size as an entropic factor,24,25 facilitating reprocessing of materials through dissociative transamidation at elevated temperatures (>150 °C) with high Ea ranging from 120 to 200 kJ mol−1. In the meantime, this DCC has shown its industrial potential in providing both creep resistance and recyclability, applicable for a wide range of applications.26 Subsequently, Xu et al. introduced dynamic maleic acid–tertiary amide linkages, where reversible amidation between maleic anhydrides and secondary amines enabled efficient monomer recovery (>94% yield) and closed-loop chemical recycling of cross-linked polymeric materials.27 Although both platforms demonstrate the feasibility of recycling polyamide networks, their reliance on specific monomers (e.g., glutarate ester or secondary amine building blocks) may restrict broader applicability.

Building on our earlier investigation of dynamic β-amino esters (BAEs),28 we recently developed reversible β-amino amides (BAAs) as the next-generation platform for recyclable polyamide networks (Fig. 1A).29 BAA-based CANs (BAANs) and their epoxy-derived materials exhibit excellent creep resistance (up to 120 °C) and hydrolytic stability under both acidic and basic conditions, while maintaining reprocessability.29,30 Our initial study showed that BAAs undergo reversible dissociation into acrylamides and amines above 140 °C. However, their exchange kinetics and the effect of catalysis have not been studied in detail so far. Notably, in the related BAE networks, neighboring amino groups act as internal catalysts that also promote transesterification in the presence of hydroxyl groups in addition to retro-Michael reactions,28,31 raising the question whether an analogous transamidation process could occur in BAA-promoted DCC.

Fig. 1. (A) Schematic representation of a previous study on materials including dynamic covalent β-amino amide chemistry.29 (B) Representation of the present work: investigating transamidation, catalytic effects, and chemical recycling of CANs based on β-amino amide groups.

Fig. 1

Open in a new tab

The current study started with an explicit study of the reversible Michael addition kinetics, further investigating the dynamic exchange, influence of catalysts, and the chemical recyclability of BAANs (Fig. 1B). Initially, small-molecule model studies were conducted to elucidate exchange pathways and their kinetics. Then, catalysts of different chemical nature – ranging from acidic to basic nature – were introduced into BAANs, followed by rheological analysis to assess their effect on the viscoelasticity behavior. Based on the newly acquired insights, we also investigated chemical degradation strategies to recover original amino building blocks from the BAANs as recycled feedstock resources. These studies provide mechanistic insights into BAA-based DCC, including the experimental verification of an unusual transamidation pathway, and further identify BAANs as high-performance polyamide networks with the potential for recycling and reprocessing.

Results and discussion

Insights into the dynamicity of the β-amino amide group

Although the dissociation of BAA was reported to occur at elevated temperatures beyond 140 °C,29 we further investigate herein the exchange kinetics through small-molecule studies. For this purpose, N-benzyl-3-(methyl(octyl)amino)propenamide (M) was synthesized as the model BAA compound via the straightforward aza-Michael addition (details are given in section S3, Fig. S1–S3). Firstly, the (retro)-aza-Michael exchange was studied in a controlled exchange reaction between M and excess benzylamine (10 eq.). As shown in Fig. 2A, the exchange was monitored via proton nuclear magnetic resonance (1H-NMR), by following the conversion over time of proton A (from M at 2.3 ppm) into proton R (at 2.9 ppm), which is attributed to the (retro)-aza-Michael exchange product RA. The formation of RA was further confirmed by electrospray ionization mass spectrometry (ESI-MS, Fig. S4).

Fig. 2. Reaction schemes and representative 1H-NMR spectra with the insets showing Arrhenius plots of the kinetic studies for: (A) reversible aza-Michael and (B) transamidation exchange of β-amino amide.

Fig. 2

Open in a new tab

Kinetic studies were conducted at varying temperatures from 120 to 180 °C, enabling the determination of reaction constants at each temperature (Fig. S5 and Table S1). Based on these data, an Arrhenius plot was constructed, revealing an activation energy (Ea) of 61.5 kJ mol−1, consistent with reported values for (most) reversible Michael adducts ranging from 50 to 80 kJ mol−1.28,32,33

Subsequently, we uncovered an unsuspected transamidation pathway operating in these reactions by repeating the same exchange experiment with BAA M and an excess of octylamine (10 eq.). Interestingly, alongside the expected (reversible) aza-Michael exchange product, analysis of the reaction mixture by 1H-NMR spectroscopy also revealed new resonances that are characteristic of a transamidation reaction: benzylic proton B at 4.4 ppm (from M) is indeed being converted into methylene proton T (at 3.3 ppm) belonging to the trans-amidated adduct TA (Fig. 2B). The formation of TA was observed at temperatures above 140 °C, and thus showed similar kinetics to the (retro)-aza-Michael pathway. It is worth noting that the asymmetric structure of the model compound M – with aliphatic and benzylic substituents – allowed for the exclusive monitoring of transamidation by 1H-NMR, since the possible (retro)-aza-Michael product (i.e., N-benzyl-3-(octylamino)propanamide) would exhibit identical proton resonances. The formation of the transamidation product TA was additionally confirmed by ESI-MS (Fig. S6). From the integration in the NMR measurements, Arrhenius plots (Fig. S7 and Table S2) revealed an Ea of 47.4 kJ mol−1, which is a bit higher than the one reported for the transesterifications of BAE (35 kJ mol−1).28

Unlike transesterification, such direct transamidation is more challenging and typically requires catalysts, or high temperatures, and is thus unexpected in these systems.34–38 Herein, we propose two possible reasonable mechanistic pathways, which are presented in Fig. 3 and are both related to a neighbouring group effect of the β-amine functionality.

Fig. 3. Proposed mechanism of the exchange of β-amino amide: (A) (retro)-aza-Michael addition and (B) transamidation via two possible pathways.

Fig. 3

Open in a new tab

While the dissociation of BAA is linked to the reversible nature of Michael nucleophilic addition via the formation of a zwitterionic intermediate after a proton transfer (Fig. 3A),39 the transamidation can possibly be enhanced by intramolecular hydrogen bonding between a protonated β-amino group and the amide carbonyl (Fig. 3B-top). Although direct transamidation begins with a high-enthalpy nucleophilic attack of an amine on the carbonyl carbon,40 the resulting tetrahedral intermediate is stabilized by an intramolecular hydrogen bond and thus a general acid catalysis, thereby lowering the energy barrier. In β-amino amides, such intramolecular interactions form an entropically favorable, six-membered pseudo-ring via hydrogen bonding,41 potentially accelerating the transamidation exchange. Interestingly, a benchmark exchange reaction performed on an amide lacking this β-amino group (i.e., n-octyloctanamide) also showed a minor conversion to the trans-amidated product after 2 h at 160 °C (Fig. S8). This observation suggests that the effect of hydrogen bonding by a protonated amine moiety, i.e., the general acid catalysis ‘charge relay’ type acylation mechanism between amide and an additional (partially) protonated amine group, can also facilitate transamidation at elevated temperature. This effect is further enhanced by the proximity of neighboring amino groups in β-amino amides (vide supra).

Alternatively, in a scenario that cannot be definitely excluded at this time, the transamidation pathway can possibly also proceed via the formation of a zwitterionic lactam intermediate (Fig. 3B-bottom). While such lactamization is expected to show a high enthalpic barrier due to the involved ring strain, the intramolecular nucleophilic attack of the β-amino group on a carbonyl carbon could be accelerated through a favorable entropic factor, also known as the neighboring group participation effect.42–45 The low activation enthalpy seen in the kinetic plots (Fig. 2B) is thus actually not indicative of such a reversible ring formation scenario, as is the already mentioned slow exchange in simple amides. In an attempt to further probe our mechanistic rationales, we performed studies to force the formation of β-lactam intermediates, but these transient species could not be isolated or observed due to their unstable (short-lived) nature in our various attempts.46

Overall, these model studies reveal that the dynamic behavior of BAANs not only arises from the reversible nature of BAA but also from a significant, kinetically comparable transamidation in the presence of β-amino groups. Although free amines are absent in our designated BAA networks, they could be released during BAA dissociation at elevated temperatures and potentially participate in transamidation exchange (vide supra).

Catalytic effects on the viscoelasticity of BAAN

Due to the highly endothermic nature of their exchange reactions, most CANs derived from aza-Michael adducts, especially BAAN, require high (re)processing temperatures (typically above 180 °C), implying limitations in terms of energy demand and risk of thermal degradation.29,47 With the aim to lower this thermal processing window, we therefore sought to exploit catalytic effects on the viscoelastic behavior of BAAN. A series of BAAN were prepared from a (2,2,4- and 2,4,4)-trimethyl hexamethylenediamine tetra-ester functional crosslinker (TMH-4E, Fig. S9) and priamine as illustrated in Fig. 4A. Various catalysts (5 mol% relative to BAA moieties) were added during network formation, including one organic base (i.e., 1,5,7-triazabicyclo[4.4.0]dec-5-ene, TBD) and three acids (i.e., p-toluenesulfonic acid, pTsOH; methane sulfonic acid, MSA and trifluoromethanesulfonic acid, TfOH). As protonated amines possibly play a role in both exchange pathways (see Fig. 3), the addition of protic acids could be beneficial for the exchange. Synthetic details are provided in section S3, and the complete cross-linking reactions were confirmed by Fourier-transform infrared spectroscopy (FTIR) (Fig. S10). The obtained polymer networks are further referred to as N–X, where X is the additional catalyst, and N-Blank refers to the catalyst-free reference network. These networks were shaped into 1–2 mm thick samples via compression molding (180 °C, 3 tons, 30 min) and subsequently subjected to rheological stress relaxation measurements. The relaxation behavior was evaluated using the Kohlrausch–Williams–Watts (KWW) stretched exponential model to construct Arrhenius plots (Fig. S11–15).

Fig. 4. (A) Synthesis of β-amino amide-based dynamic networks prepared using the catalysts displayed in the frame, and (B) their relaxation times at 200 °C determined from the KWW stretched exponential model. (C) Visualization of the compression molding of N-MSA and N-blank at varying temperatures.

Fig. 4

Open in a new tab

In general, the addition of catalyst(s) linearly shifted the Arrhenius plots to a modified relaxation time (τ), while it maintained the temperature-dependent viscoelasticity (i.e., Ea) comparable to that of the benchmark network (N-Blank) (Fig. S16A). While all acidic catalysts lower the stress relaxation time (τ), the base TBD hampers BAAN's dynamicity, resulting in slower relaxation profiles, indeed indicating a kinetic role of protonated amine intermediates. More specifically, in comparison with the catalyst-free network N-Blank with a τ of 138 s at 200 °C, the addition of 5 mol% TBD into the network resulted in a τ of 194 s (Fig. 4B, Fig. S16B). In contrast, the addition of an identical molar amount of acidic catalyst significantly accelerated stress relaxation, reducing the relaxation time by more than fourfold for the N-MSA network (τ = 29 s). It should be noted here that the most pronounced acceleration was not observed for the network incorporating the stronger acid TfOH (pKa(H2O) ≈ −14, compared to pKa(H2O) ≈ −1.9 for MSA). In fact, this observation is attributed to strong interactions between TfOH and amino moieties in the network, which are known to reduce molecular mobility and thus limit catalytic effectiveness.48

As can be observed from the dissociation pathway of BAA (Fig. 3A), the β-amino group must be protonated to complete the dissociation, although the reversion of BAA is initiated by the deprotonation at the α-carbon position. Therefore, the Brønsted acids here act as a proton source, which favors such reversion. On the other hand, the strongly basic catalyst or additive TBD will compete for protons with the amines, thereby reducing the abundance of protonated amines and hampering the exchange process. Moreover, the amines released during BAA dissociation can enable further transamidation exchange, enhancing the overall network dynamicity and stress relaxation behavior. This increased relaxation ability implies improved processability, such as reduced processing time or lower processing temperature. To examine this, the N-Blank and N-MSA networks were cut into small pieces and subjected to the same compression molding process at variable temperatures ranging from 180 to 160 °C. While both samples were fully processable at 180 °C, cut samples of N-Blank failed to heal completely after 30 min at 170 °C (Fig. 4C). In contrast, N-MSA retained its (re)processability, resulting in homogeneous remolded samples at lower temperatures (160 °C). Notably, although the presence of catalysts might compromise the thermal stability of the materials, no significant impact was observed at the catalyst loading used (5 mol%), as revealed by thermogravimetric analysis of N-MSA and N-Blank (Fig. S17). This demonstrates the enhanced (re)processability of the acid-catalysed CAN, implying beneficial energy savings.

Chemical recycling

At the final stage of this study, it was attempted to chemically degrade the BAANs for the recovery of amino building blocks, which was previously demonstrated in a related BAE platform.49–51 This chemical degradation process was expected to be enhanced by the double exchange pathway described earlier. The degradation tests were performed on a P-BAAN network, prepared using only priamine as an amino building block (Fig. S18 and 19). The tests were conducted by immersing P-BAAN in an amino compound, either octylamine or ethanolamine, at 140 °C. As shown in Fig. 5A, depolymerization should involve both possible amine exchange reaction pathways: (retro)-aza-Michael pathway (RP) and/or transamidation pathway (TP), in which an additional excess of amines acts as a kinetic trap to enable the recovery of the amino building block of the CANs (priamine).

Fig. 5. The chemical degradation of the P-BAAN. (A) Schematic overview of the network depolymerization pathways; (B) overlaid 1H-NMR spectra of pristine (top) and recovered (bottom) priamine. (C) Visualization of pristine P-BAAN and chemically recycled P-BAAN.

Fig. 5

Open in a new tab

Full dissolution of P-BAAN was observed to be significantly faster when heating was done in ethanolamine (after 2 h at 140 °C) than in octylamine (after 4 h at 140 °C), which could be attributed to the acceleration effect of the (proton-donating) hydroxyl group in ethanolamine (Fig. S20).52 Moreover, a benchmark experiment conducted with DMSO as an ‘inert’ solvent did not affect the integrity of the network under identical conditions, even after 24 h at 140 °C (Fig. S21). To isolate the recovered priamine, the degraded crude product in ethanolamine was further subjected to DCM–water extraction. Although the dissolution was visualized after 2 h, the depolymerization proceeded at a much longer time scale. Specifically, incomplete depolymerization was observed by matrix-assisted laser desorption/ionization time-of-flight analysis, which primarily detected mono- and di-Michael adducts of priamine after 3 days (Fig. S22). The purity of recovered priamine, assuming Michael adducts as impurities, was quantified by 1H-NMR spectroscopy (Fig. 6).

Fig. 6. 1H-NMR spectroscopy studies and estimated purities of the degraded crude in ethanolamine (after workup, DCM/H2O) at different time intervals. The purity was estimated (purity = a/(a + b) × 100%) by considering the Michael adducts as impurities (left structures).

Fig. 6

Open in a new tab

After 3 days, priamine was recovered with 48% purity, which gradually increased over time. After 10 days of depolymerization, a recovery purity of 86% was achieved with a yield of 84 wt% relative to the total priamine used for P-BAAN synthesis, in which a mono-Michael adduct was the main residual impurity (Fig. 5B and Fig. S23). It is recognized that such impurity may potentially influence material properties (e.g., crosslink density), especially over multiple recycling cycles. On the other hand, as a proof of concept, this recovered amino compound was subsequently used as a feedstock to (re)synthesize recycled P-BAAN (Fig. 5C and Table 1).

Table 1. Overall properties of the pristine and recycled β-amino amide network.

Samples T g  a (°C) T d5%  b (°C) m iso 180, 1 h  c (%) Swelling degreed (%) Soluble fractiond (%) Modulus (MPa)e ν e  e (10−3 mol m−3)
Pristine P-BAAN −25 320 1.4 477 ± 09 3.2 ± 2.2 0.286 0.029
Recycled P-BAAN −26 319 1.2 436 ± 36 4.4 ± 1.9 0.292 0.027
Open in a new tab
a

Determined from DSC analysis with a heating rate of 10 °C min−1.

b

TGA onset temperatures after 5% weight loss (Td5%) under an air atmosphere.

c

Weight loss after isothermal TGA at 200 °C for 1 hour under an air atmosphere.

d

Swelling degree and soluble fraction obtained from solubility tests in chloroform using at least four samples at room temperature.

e

Storage modulus and cross-linking density (νe) from dynamic mechanical thermal analysis. νe was calculated using the rubber elasticity equation: E′ = 3νeRT, where R is the gas constant and T is the absolute temperature at Tg + 50 °C.

While a brownish coloration and slightly increased soluble fraction (attributed to residual impurities) were observed, the recycled P-BAAN showed desirable chemical characteristics comparable to pristine P-BAAN, as shown using FTIR spectroscopy analysis (Fig. S24). Moreover, the chemically recycled P-BAAN largely retained its thermal and thermomechanical properties (Fig. S25–28), highlighting the potential for the chemical recycling of BAA-derived CANs.

Conclusion

In summary, this work has elucidated the bond exchange kinetics and further reveals an interesting transamidation exchange pathway in β-amino amides. Catalyst screening highlights the advantage of using acidic catalysis for the acceleration of stress relaxation and consequently enhancing processability, and points toward mechanisms that involve protonated amine species. Notably, the addition of 5 mol% methane sulfonic acid enables the obtained β-amino amide network to relax the applied stress up to four times faster at 200 °C, while extending the processability window in comparison with the catalyst-free network. Furthermore, capitalizing on the finding of dual amine exchange reactions on BAAs, the chemical recycling of the amino building block (priamine) from the cross-linked material was demonstrated. Priamine could be restored with a purity of 86% and a yield of 84 wt%, and was successfully employed to resynthesize CANs without significant changes in chemical and thermal properties. The findings in this study not only expand the mechanistic understanding of β-amino amide dynamic chemistry but also establish a more practical route toward recyclable, high-performance thermosets.

Author contributions

The manuscript was written through contributions of all authors. All authors have given approval to the final version of the manuscript.

Conflicts of interest

There are no conflicts to declare.

Supplementary Material

PY-016-D5PY00959F-s001

Acknowledgments

The authors would like to thank Bernhard De Meyer for technical support and Dr Stephan Maes for fruitful discussions. This project received funding from the European Research Council (ERC) under the European Union's Horizon 2020 research and innovation programme 101021081 (ERC-AdG-2020, CiMaC-project), and from the Research Foundation Flanders (FWO – G0A1R25N).

The NMR expertise centre (Ghent University) is also acknowledged for providing support and access to the NMR infrastructure funded by FWO (I006920N) and the Bijzonder Onderzoeksfonds (BOF.BAS.2022.0023.01).

Data availability

The data supporting this article have been included as part of the supplementary information (SI). Supplementary information is available. See DOI: https://doi.org/10.1039/d5py00959f.

References

  1. Klun B. Rozman U. Ogrizek M. Kalčíková G. The First Plastic Produced, but the Latest Studied in Microplastics Research: The Assessment of Leaching, Ecotoxicity and Bioadhesion of Bakelite Microplastics. Environ. Pollut. 2022;307:119454. doi: 10.1016/j.envpol.2022.119454. [DOI] [PubMed] [Google Scholar]
  2. Wang S. Feng H. Li B. Lim J. Y. C. Rusli W. Zhu J. Hadjichristidis N. Li Z. Knoevenagel C Created by potrace 1.16, written by Peter Selinger 2001-2019 C Metathesis Enabled Glassy Vitrimers with High Rigidity, Toughness, and Malleability. J. Am. Chem. Soc. 2024;146(23):16112–16118. doi: 10.1021/jacs.4c03503. [DOI] [PMC free article] [PubMed] [Google Scholar]
  3. Stewart K. A. Lessard J. J. Cantor A. J. Rynk J. F. Bailey L. S. Sumerlin B. S. High-Performance Polyimine Vitrimers from an Aromatic Bio-Based Scaffold. RSC Appl. Polym. 2023;1(1):10–18. doi: 10.1039/D3LP00019B. [DOI] [PMC free article] [PubMed] [Google Scholar]
  4. Fortman D. J. Brutman J. P. De Hoe G. X. Snyder R. L. Dichtel W. R. Hillmyer M. A. Approaches to Sustainable and Continually Recyclable Cross-Linked Polymers. ACS Sustainable Chem. Eng. 2018;6(9):11145–11159. doi: 10.1021/acssuschemeng.8b02355. [DOI] [Google Scholar]
  5. Kloxin C. J. Bowman C. N. Covalent Adaptable Networks: Smart, Reconfigurable and Responsive Network Systems. Chem. Soc. Rev. 2013;42(17):7161–7173. doi: 10.1039/C3CS60046G. https://dx.doi.org/10.1039/c3cs60046g [DOI] [PubMed] [Google Scholar]
  6. Bowman C. Du Prez F. Kalow J. Introduction to Chemistry for Covalent Adaptable Networks. Polym. Chem. 2020;11(33):5295–5296. doi: 10.1039/D0PY90102D. [DOI] [Google Scholar]
  7. Zhang V. Kang B. Accardo J. V. Kalow J. A. Structure–Reactivity–Property Relationships in Covalent Adaptable Networks. J. Am. Chem. Soc. 2022;144(49):22358–22377. doi: 10.1021/jacs.2c08104. [DOI] [PMC free article] [PubMed] [Google Scholar]
  8. Kloxin C. J. Scott T. F. Adzima B. J. Bowman C. N. Covalent Adaptable Networks (CANs): A Unique Paradigm in Cross-Linked Polymers. Macromolecules. 2010;43(6):2643–2653. doi: 10.1021/ma902596s. [DOI] [PMC free article] [PubMed] [Google Scholar]
  9. Montarnal D. Capelot M. Tournilhac F. Leibler L. Silica-Like Malleable Materials from Permanent Organic Networks. Science. 2011;334(6058):965–968. doi: 10.1126/science.1212648. [DOI] [PubMed] [Google Scholar]
  10. Delahaye M. Winne J. M. Du Prez F. E. Internal, Catalysis in Covalent Adaptable Networks: Phthalate Monoester Transesterification As a Versatile Dynamic Cross-Linking Chemistry. J. Am. Chem. Soc. 2019;141(38):15277–15287. doi: 10.1021/jacs.9b07269. [DOI] [PubMed] [Google Scholar]
  11. Denissen W. Rivero G. Nicolaÿ R. Leibler L. Winne J. M. Du Prez F. E. Vinylogous, Urethane Vitrimers. Adv. Funct. Mater. 2015;25(16):2451–2457. doi: 10.1002/adfm.201404553. [DOI] [Google Scholar]
  12. Engelen S. Dolinski N. D. Chen C. Ghimire E. Lindberg C. A. Crolais A. E. Nitta N. Winne J. M. Rowan S. J. Du Prez F. E. Vinylogous, Urea—Urethane Vitrimers: Accelerating and Inhibiting Network Dynamics through Hydrogen Bonding. Angew. Chem., Int. Ed. 2024;63(9):e202318412. doi: 10.1002/anie.202318412. [DOI] [PubMed] [Google Scholar]
  13. Terryn S. Brancart J. Roels E. Verhelle R. Safaei A. Cuvellier A. Vanderborght B. Van Assche G. Structure–Property Relationships of Self-Healing Polymer Networks Based on Reversible Diels–Alder Chemistry. Macromolecules. 2022;55(13):5497–5513. doi: 10.1021/acs.macromol.2c00434. [DOI] [Google Scholar]
  14. Zhang G. Zhao Q. Yang L. Zou W. Xi X. Xie T. Exploring Dynamic Equilibrium of Diels–Alder Reaction for Solid State Plasticity in Remoldable Shape Memory Polymer Network. ACS Macro Lett. 2016;5(7):805–808. doi: 10.1021/acsmacrolett.6b00357. [DOI] [PubMed] [Google Scholar]
  15. Yang B. Ni T. Wu J. Fang Z. Yang K. He B. Pu X. Chen G. Ni C. Chen D. Zhao Q. Li W. Li S. Li H. Zheng N. Xie T. Circular 3D Printing of High-Performance Photopolymers through Dissociative Network Design. Science. 2025;388(6743):170–175. doi: 10.1126/science.ads3880. [DOI] [PubMed] [Google Scholar]
  16. Dağlar Ö. Eisenreich F. Tomović Ž. Chemical and Solvent–Based Recycling of High–Performance Epoxy Thermoset Utilizing Imine–Containing Secondary Amine Hardener. Adv. Funct. Mater. 2024;34(49):2408299. doi: 10.1002/adfm.202408299. [DOI] [Google Scholar]
  17. Vilanova-Pérez A. De la Flor S. Fernández-Francos X. Serra À. Roig A. Biobased Imine Vitrimers Obtained by Photo and Thermal Curing Procedures–Promising Materials for 3D Printing. ACS Appl. Polym. Mater. 2024;6(6):3364–3372. doi: 10.1021/acsapm.3c03234. [DOI] [PMC free article] [PubMed] [Google Scholar]
  18. ASTP Innovations; , Aromatic Thermosetting coPolyesters (ATSP) EsthermTM resins. https://www.atspinnovations.com/ (accessed 2025-07-01)
  19. Mallinda; , VITRIMAX (accessed 2024-09-17). https://mallinda.com/ (accessed 2025-07-01)
  20. Van Lijsebetten F. Debsharma T. Winne J. M. Du Prez F. E. A Highly Dynamic Covalent Polymer Network without Creep: Mission Impossible? Angew. Chem., Int. Ed. 2022;61(48):e202210405. doi: 10.1002/anie.202210405. [DOI] [PubMed] [Google Scholar]
  21. Maes S. Badi N. Winne J. M. Du Prez F. E. Taking, Dynamic Covalent Chemistry out of the Lab and into Reprocessable Industrial Thermosets. Nat. Rev. Chem. 2025;9(3):144–158. doi: 10.1038/s41570-025-00686-7. [DOI] [PubMed] [Google Scholar]
  22. Li L. Chen X. Jin K. Rusayyis M. B. Torkelson J. M. Arresting Elevated-Temperature Creep and Achieving Full Cross-Link Density Recovery in Reprocessable Polymer Networks and Network Composites via Nitroxide-Mediated Dynamic Chemistry. Macromolecules. 2021;54(3):1452–1464. doi: 10.1021/acs.macromol.0c01691. [DOI] [Google Scholar]
  23. Mondal S. Wong A. J. Wagh M. A. Alperstein L. Sanjayan G. J. Sumerlin B. S. Creep Resistance in Doubly Crosslinked Dynamic Covalent Networks. Polym. Chem. 2024;15(18):1826–1832. doi: 10.1039/D4PY00276H. [DOI] [Google Scholar]
  24. Van Lijsebetten F. Spiesschaert Y. Winne J. M. Du Prez F. E. Reprocessing of Covalent Adaptable Polyamide Networks through Internal Catalysis and Ring-Size Effects. J. Am. Chem. Soc. 2021;143(38):15834–15844. doi: 10.1021/jacs.1c07360. [DOI] [PubMed] [Google Scholar]
  25. Chen Y. Zhang H. Majumdar S. van Benthem R. A. T. M. Heuts J. P. A. Sijbesma R. P. Dynamic Polyamide Networks via Amide–Imide Exchange. Macromolecules. 2021;54(20):9703–9711. doi: 10.1021/acs.macromol.1c01389. [DOI] [PMC free article] [PubMed] [Google Scholar]
  26. Debuyck J. Daelman B. Scurani G. Fischer S. M. Du Prez F. E. Low-Viscosity, Dynamic Amidoamine Hardeners with Tunable Curing Kinetics for Epoxy Adhesives. Macromolecules. 2025;58(17):9209–9216. doi: 10.1021/acs.macromol.5c01676. [DOI] [Google Scholar]
  27. Qin B. Liu S. Huang Z. Zeng L. Xu J.-F. Zhang X. Closed-Loop Chemical Recycling of Cross-Linked Polymeric Materials Based on Reversible Amidation Chemistry. Nat. Commun. 2022;13(1):7595. doi: 10.1038/s41467-022-35365-4. [DOI] [PMC free article] [PubMed] [Google Scholar]
  28. Taplan C. Guerre M. Du Prez F. E. Covalent, Adaptable Networks Using β-Amino Esters as Thermally Reversible Building Blocks. J. Am. Chem. Soc. 2021;143(24):9140–9150. doi: 10.1021/jacs.1c03316. [DOI] [PubMed] [Google Scholar]
  29. Nguyen L. T. Portone F. Du Prez F. E. β-Amino Amide Based Covalent Adaptable Networks with High Dimensional Stability. Polym. Chem. 2024;15(1):11–16. doi: 10.1039/D3PY01175E. [DOI] [Google Scholar]
  30. Nguyen L. T. Maes S. Du Prez F. E. Enabling the Reprocessability and, Debonding of Epoxy Thermosets Using Dynamic Poly(B–Amino Amide) Curing Agents. Adv. Funct. Mater. 2024;35(19):2419240. doi: 10.1002/adfm.202419240. [DOI] [Google Scholar]
  31. Lee G. Song H. Y. Choi S. Kim C. B. Hyun K. Ahn S. Harnessing β-Hydroxyl Groups in Poly(β-Amino Esters) toward Robust and Fast Reprocessing Covalent Adaptable Networks. Macromolecules. 2022;55(23):10366–10376. doi: 10.1021/acs.macromol.2c01872. [DOI] [Google Scholar]
  32. Stubbs C. J. Khalfa A. L. Chiaradia V. Worch J. C. Dove A. P. Intrinsically Re-Curable Photopolymers Containing Dynamic Thiol-Michael Bonds. J. Am. Chem. Soc. 2022;144(26):11729–11735. doi: 10.1021/jacs.2c03525. [DOI] [PMC free article] [PubMed] [Google Scholar]
  33. Zhang B. Chakma P. Shulman M. P. Ke J. Digby Z. A. Konkolewicz D. Probing the Mechanism of Thermally Driven Thiol-Michael Dynamic Covalent Chemistry. Org. Biomol. Chem. 2018;16(15):2725–2734. doi: 10.1039/C8OB00397A. [DOI] [PubMed] [Google Scholar]
  34. Liu Y. Shi S. Achtenhagen M. Liu R. Szostak M. Metal-Free Transamidation of Secondary Amides via Selective N–C Cleavage under Mild Conditions. Org. Lett. 2017;19(7):1614–1617. doi: 10.1021/acs.orglett.7b00429. [DOI] [PubMed] [Google Scholar]
  35. Larsen M. B. Herzog S. E. Quilter H. C. Hillmyer M. A. Activated Polyacrylamides as Versatile Substrates for Postpolymerization Modification. ACS Macro Lett. 2018;7(1):122–126. doi: 10.1021/acsmacrolett.7b00896. [DOI] [PubMed] [Google Scholar]
  36. Li G. Ji C.-L. Hong X. Szostak M. Highly Chemoselective, Transition-Metal-Free Transamidation of Unactivated Amides and Direct Amidation of Alkyl Esters by N–C/O–C Cleavage. J. Am. Chem. Soc. 2019;141(28):11161–11172. doi: 10.1021/jacs.9b04136. [DOI] [PubMed] [Google Scholar]
  37. Trachsel L. Konar D. Hillman J. D. Davidson C. L. G. Sumerlin B. S. Diversification of Acrylamide Polymers via Direct Transamidation of Unactivated Tertiary Amides. J. Am. Chem. Soc. 2024;146(2):1627–1634. doi: 10.1021/jacs.3c12174. [DOI] [PubMed] [Google Scholar]
  38. Eldred S. E. Stone D. A. Gellman S. H. Stahl S. S. Catalytic Transamidation under Moderate Conditions. J. Am. Chem. Soc. 2003;125(12):3422–3423. doi: 10.1021/ja028242h. [DOI] [PubMed] [Google Scholar]
  39. Ratzenböck K. Uher J. M. Fischer S. M. Edinger D. Schallert V. Žagar E. Pahovnik D. Slugovc C. Exploiting Retro Oxa-Michael Chemistry in Polymers. Polym. Chem. 2023;14(5):651–661. doi: 10.1039/D2PY01345B. [DOI] [Google Scholar]
  40. Lanigan R. M. Sheppard T. D. Recent Developments in Amide Synthesis: Direct Amidation of Carboxylic Acids and Transamidation Reactions. Eur. J. Org. Chem. 2013;2013(33):7453–7465. doi: 10.1002/ejoc.201300573. [DOI] [Google Scholar]
  41. Dorigo A. E. Houk K. N. Transition Structures for Intramolecular Hydrogen-Atom Transfers: The Energetic Advantage of Seven-Membered over Six-Membered Transition Structures. J. Am. Chem. Soc. 1987;109(7):2195–2197. doi: 10.1021/ja00241a056. [DOI] [Google Scholar]
  42. Chen S. Ding D. Yin L. Wang X. Krause J. A. Liu W. Overcoming Copper Reduction Limitation in Asymmetric Substitution: Aryl-Radical-Enabled Enantioconvergent Cyanation of Alkyl Iodides. J. Am. Chem. Soc. 2024;146(46):31982–31991. doi: 10.1021/jacs.4c11888. [DOI] [PMC free article] [PubMed] [Google Scholar]
  43. Gedey S. Van der Eycken J. Fülöp F. Liquid-Phase Combinatorial Synthesis of Alicyclic β -Lactams via Ugi Four-Component Reaction. Org. Lett. 2002;4(11):1967–1969. doi: 10.1021/ol025986r. [DOI] [PubMed] [Google Scholar]
  44. Cuminet F. Caillol S. Dantras É. Leclerc É. Ladmiral V. Neighboring Group Participation and Internal Catalysis Effects on Exchangeable Covalent Bonds: Application to the Thriving Field of Vitrimer Chemistry. Macromolecules. 2021;54(9):3927–3961. doi: 10.1021/acs.macromol.0c02706. [DOI] [Google Scholar]
  45. Levchik S. V. Weil E. D. Lewin M. Thermal Decomposition of Aliphatic Nylons. Polym. Int. 1999;48(7):532–557. doi: 10.1002/(SICI)1097-0126(199907)48:7<532::AID-PI214>3.0.CO;2-R. [DOI] [Google Scholar]
  46. Bryskier A. New Concepts in the Field of Cephalosporins: C-3′ Quaternary Ammonium Cephems (Group IV) Clin. Microbiol. Infect. 1997;3:S1–S6. doi: 10.1111/j.1469-0691.1997.tb00642.x. [DOI] [Google Scholar]
  47. Engelen S. Van Lijsebetten F. Aksakal R. Winne J. M. Du Prez F. E. Enhanced Viscosity Control in Thermosets Derived from Epoxy and Acrylate Monomers Based on Thermoreversible Aza-Michael Chemistry. Macromolecules. 2023;56(17):7055–7064. doi: 10.1021/acs.macromol.3c01198. [DOI] [Google Scholar]
  48. Van Lijsebetten F. Maes S. Winne J. M. Du Prez F. E. Thermoswitchable Catalysis to Inhibit and Promote Plastic Flow in Vitrimers. Chem. Sci. 2024;15(19):7061–7071. doi: 10.1039/D4SC00417E. [DOI] [PMC free article] [PubMed] [Google Scholar]
  49. Miao R. Ding Y. Liu J. Liu J. Xin Z. Bao C. Mechanically Robust and Chemically Recyclable Poly(β-Amino Esters)-Based Thermosetting Plastics. ACS Appl. Polym. Mater. 2024;6(21):13439–13448. doi: 10.1021/acsapm.4c02945. [DOI] [Google Scholar]
  50. Unal K. Maes D. Stricker L. Lorenz K. Du Prez F. E. Imbernon L. Winne J. M. Foam-to-Elastomer Recycling of Polyurethane Materials through Incorporation of Dynamic Covalent TAD–Indole Linkages. ACS Appl. Polym. Mater. 2024;6(5):2604–2615. doi: 10.1021/acsapm.3c02791. [DOI] [Google Scholar]
  51. Nguyen L. T. Du Prez F. E. Direct, Restoration of Photocurable Cross-Linkers for Repeated Light-Based 3D Printing of Covalent Adaptable Networks. Mater. Horiz. 2024;11(24):6408–6415. doi: 10.1039/D4MH00823E. [DOI] [PMC free article] [PubMed] [Google Scholar]
  52. Van Guyse J. F. R. Leiske M. N. Verjans J. Bernhard Y. Hoogenboom R. Accelerated Post–Polymerization Amidation of Polymers with Side–Chain Ester Groups by Intramolecular Activation. Angew. Chem., Int. Ed. 2022;61(29):e202201781. doi: 10.1002/anie.202201781. [DOI] [PubMed] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Supplementary Materials

PY-016-D5PY00959F-s001
PY-016-D5PY00959F-s001.pdf (2.2MB, pdf)

Data Availability Statement

The data supporting this article have been included as part of the supplementary information (SI). Supplementary information is available. See DOI: https://doi.org/10.1039/d5py00959f.