Advances in MgAgSb thermoelectrics: from materials to devices

Liangjun Xie; Ran He; Jiehe Sui; Kornelius Nielsch; Zihang Liu

doi:10.1039/d5sc07399e

. 2026 Feb 20;17(12):5820–5839. doi: 10.1039/d5sc07399e

Advances in MgAgSb thermoelectrics: from materials to devices

Liangjun Xie ^a, Ran He ^a,^✉, Jiehe Sui ^b, Kornelius Nielsch ^a, Zihang Liu ^c

PMCID: PMC12926705 PMID: 41737690

Abstract

Thermoelectric materials have attracted considerable attention due to their significant potential in waste heat recovery and solid-state cooling, which are critical for emerging technologies such as the Internet of Things, 5G communications, and thermal management of advanced electronics. In the field of low-temperature thermoelectric materials and devices, MgAgSb-based devices have emerged as a promising alternative to commercial Bi₂Te₃-based devices, owing to their superior performance near room temperature, abundant elemental availability, and environmental compatibility. Over the past decade, substantial progress has been achieved in elucidating and optimizing the thermoelectric properties of MgAgSb and its devices. This review presents a comprehensive summary of recent developments in the intrinsic properties, synthesis process refinements, and performance optimization strategies of MgAgSb, as well as interface engineering, geometric optimization, and stability enhancement in MgAgSb-based devices, while critically addressing current challenges and prospective pathways toward the practical implementation of MgAgSb-based thermoelectrics.

α-MgAgSb has emerged as a promising next-generation p-type thermoelectric material . This review summarizes recent progress in the fundamental understanding, property optimization, and thermoelectric device applications of MgAgSb.

1. Introduction

Thermoelectric materials enable the direct conversion of thermal energy into electrical energy, offering significant potential for waste heat recovery and solid-state cooling applications.^1–5 In particular, low-temperature thermoelectric materials have attracted considerable attention for solid-state cooling, driven by advancements in electronic chips, the Internet of Things, and 5G technologies.^6–10 It is reported that the total waste-heat potential in the European Union is approximately 300 TWh per year, of which one-third corresponds to low-temperature waste heat below 200 °C and an additional 25% falls within the 200–500 °C range.¹¹ These findings clearly demonstrate the substantial potential for low-temperature waste-heat recovery using thermoelectric technology. For several decades, the pursuit of this objective has primarily depended on Bi₂Te₃-based thermoelectric materials. Nevertheless, Te, the essential constituent element of these compounds, is both scarce¹² (Fig. 1A) and environmentally hazardous, which substantially constrains their further development and large-scale deployment. Until recently, attributed to the unparalleled advantages of excellent thermoelectric performance, earth-abundant constituent elements,¹² environmental friendliness, and favorable mechanical stability,^13–16 Mg-based thermoelectric devices, comprising p-type MgAgSb and n-type Mg₃(Bi, Sb)₂, have emerged as promising next-generation candidates to replace commercial Bi₂Te₃.^{13,14,16–20} Of particular significance, MgAgSb achieves a markedly higher figure of merit (ZT) than other thermoelectric materials in the 400–600 K temperature range^21–34 (Fig. 1B), underscoring its unique and indispensable role. Consequently, MgAgSb-based power generation devices deliver unmatched performance under temperature differences of ∼300 K (ref. 13 and 35–47) (Fig. 1C). However, compared with other advanced energy conversion technologies, such as solar cells,^48,49 the primary obstacle limiting the widespread commercialization of thermoelectric devices is their relatively low conversion efficiency, which originates from the intrinsically low ZT of the materials. Theoretically, achieving high thermoelectric performance requires simultaneously optimizing electronic transport while suppressing thermal transport.^50,51 However, the strong coupling between charge carriers and phonons fundamentally constrains the ability to independently tune these properties, thereby hindering the realization of significantly higher ZT values. To address these, substantial progress has been made in enhancing the performance of MgAgSb through strategies such as microstructure engineering,^{14,16,17,52,53} composite material optimization,^15,54 and advanced synthesis technologies,^{13,14,53,55–59} which have been partially summarized and discussed in several reviews.^60–63 Concurrently, device-level advancements have focused on thermoelectric interface materials (TEiMs) design,^64–69 module geometry optimization,^18,68 and investigations into operational stability.⁷⁰ These developments have profound implications not only for the thermoelectric field but also for other functional material systems. MgAgSb research offers valuable insights into the synthesis of challenging materials and provides innovative ideas for interface material design, particularly concerning the electrical properties of semiconductor materials. Given its broad relevance, a comprehensive and generalized review of these advancements is essential. In the first section of this review, we provide a comprehensive overview of recent advances in the fundamental understanding and property optimization of MgAgSb, encompassing intrinsic electronic and thermal transport characteristics, state-of-the-art synthesis and processing strategies, and the pivotal role of defect engineering in tailoring performance. The second section is devoted to progress in the development of thermoelectric power generation and cooling devices, with particular emphasis on innovations in TEiM design, device geometry optimization, and long-term operational stability. Finally, we critically assess the remaining scientific and technological challenges and present an outlook on prospective research directions and opportunities for the future advancement of MgAgSb-based thermoelectrics.

2. Advances in thermoelectric performance optimization of MgAgSb

2.1. Understanding the structural complexity and phase evolution in MgAgSb

As early as 1941, Nowotny and Sibert elucidated the crystal structure of MgAgSb via X-ray diffraction (XRD) analysis, establishing its structural analogy to MgCuAs, with both adopting a tetragonal Cu₂Sb-type configuration.⁷¹ Subsequent investigations employing variable-temperature XRD by Kirkham et al. and variable-temperature synchrotron radiation by Mi et al. systematically resolved the temperature-dependent structural evolution of MgAgSb, revealing the existence of three distinct phases.^72,73 The high-temperature γ-MgAgSb phase adopts a conventional half-Heusler structure, isostructural with MgCuSb, wherein the Mg–Sb framework forms a NaCl-type rock-salt sublattice and Ag atoms occupy half of the octahedral interstices; it crystallizes in the space group F4̄3m, contains 16 atoms per unit cell, and exhibits a theoretical density of 5.61 g cm⁻³ (Fig. 2A). The intermediate-temperature β-MgAgSb phase adopts a tetragonal Cu₂Sb-type lattice (space group P4/nmm) with 6 atoms per unit cell, a theoretical density of 6.26 g cm⁻³, and metallic character (Fig. 2B). The low-temperature α-MgAgSb phase is a distorted half-Heusler variant, in which the Mg–Sb rock-salt sublattice undergoes a 45° rotation about the c-axis; it crystallizes in the space group I4̄c2, contains 48 atoms per unit cell, and has a theoretical density of 6.31 g cm⁻³ (Fig. 2C). With increasing temperature, MgAgSb undergoes structural evolution with critical phase-transition points. The ZT value drops sharply when MgAgSb transforms into the β phase due to its metallic electronic structure, and then gradually rises again once the temperature exceeds the β–γ phase transition (Fig. 2D). As a result, the practical operating temperature window of MgAgSb is largely confined to the lower-temperature region around 300 °C. More critically, the pronounced structural complexity of MgAgSb results in an intrinsically low solubility for most extrinsic dopants, which in turn renders its phase-transition temperature insensitive to doping. This characteristic further limits the manipulation of phase transition temperature and the potential application of MgAgSb at elevated temperatures.

Ying et al. computed the electronic band structure and density of states of α-MgAgSb using density functional theory (DFT) within the VASP framework, revealing that MgAgSb is an indirect, narrow-bandgap semiconductor with E_g ≈ 0.26 eV.⁷⁵ The valence band maximum is located at the X point, while the conduction band minimum lies at the G point (Fig. 2E). Notably, the material exhibits a high band degeneracy (N_v = 8; Fig. 2F), and the flatness of the valence band maximum confers a large single-band effective mass, contributing to an enhanced Seebeck coefficient. Using the Bardeen–Shockley deformation potential theory, Liu et al. determined that MgAgSb possesses a low deformation potential (Fig. 2G), indicative of weak electron–phonon coupling.⁷⁶ This characteristic, coupled with its structurally induced complexity, enables unusually high carrier mobility. The synergistic interplay of high band degeneracy, large effective mass, and small deformation potential underpins the excellent electrical transport performance of MgAgSb.

To investigate the intrinsic mechanism underlying the low thermal conductivity of MgAgSb, Ying et al. theoretically and experimentally confirmed the coexistence of both global and local weak chemical bonds in α-MgAgSb, revealing that low-frequency optical phonon vibrations with “rattling-like” thermal damping are the primary origin of its reduced lattice thermal conductivity.⁷⁷ Liu et al. elucidated the mechanism behind the low lattice thermal conductivity of MgAgSb through DFT calculations, identifying factors such as weak chemical bonding, strong anharmonic coupling between the longitudinal acoustic branch and the longitudinal optical branch, and high anharmonic behavior in the longitudinal acoustic branch (Fig. 3A and B).⁷⁸ Li et al. employed neutron scattering experiments alongside ab initio calculations to demonstrate that the ultralow lattice thermal conductivity of MgAgSb arises primarily from the strong scattering of transverse phonons by the distorted Mg–Sb rock-salt sublattice.⁷⁹ Consequently, longitudinal phonons dominate the heat transport and thus principally determine the κ_lat value. Moreover, observed phonon softening further elucidates the anharmonic nature of the atomic vibrations within the lattice (Fig. 3C and D).

2.2. Synthesis strategies for enhancing thermoelectric properties

Since Kirkham et al. first reported and systematically investigated the promising thermoelectric properties of MgAgSb in 2012,⁷³ efforts to optimize its thermoelectric performance have mainly focused on refining preparation and synthesis methods to improve phase purity, owing to its intrinsically distorted crystal lattice and complex phase composition. The low formation energy of Ag₃Sb is one of the key factors responsible for its easy formation in MgAgSb, which in turn degrades thermoelectric performance. To address this challenge, in 2014, Zhao et al. introduced a two-step ball-milling strategy to avoid the direct contact and reaction between Ag and Sb raw materials, thereby producing MgAgSb with significantly enhanced phase purity. The ZT of the resulting MgAgSb reached 0.7 at room temperature, with an average ZT of 1.1.⁸⁰ Since then, high-energy ball-milling mechanical alloying has become the predominant approach for MgAgSb synthesis. Subsequently, extensive investigations were conducted on carrier regulation through element doping to optimize MgAgSb performance,^{60,76,78,81–87} systematically evaluating the effectiveness of different dopants and the impact of doping at various lattice sites on carrier mobility. Zhang et al. further improved the two-step ball-milling process by enhancing milling efficiency and reducing impurity phases.^13,14,53 In the high-energy ball-milling mechanical alloying process, they replaced the traditional V-belt with a timing belt to increase the rotational speed and used tungsten carbide balls to increase the collision energy (Fig. 4A), thereby significantly improving the purity of the ball-milled powder. Subsequent high-temperature annealing facilitated substantial grain growth (Fig. 4B and C), which enhanced carrier mobility and power factor. Under this synthesis approach, the resulting MgAgSb exhibited a ZT_ave of 1.4 in the temperature range of 300–573 K.

The thermoelectric properties of MgAgSb are highly sensitive to multiple synthesis parameters, including the ball-milling process, raw material particle size, composition, sintering temperature, and applied pressure during sintering, which collectively contribute to the variations in material properties reported by different researchers. Boor et al. systematically investigated the factors influencing MgAgSb performance during synthesis. By comparing traditional planetary ball milling with high-energy ball milling, they demonstrated that high-energy ball milling more readily yields MgAgSb with lower impurity-phase content and identified Ag₃Sb as the primary impurity responsible for deteriorated thermoelectric performance.⁵⁷ Further studies on the influence of MgAg precursors on the final MgAgSb synthesis revealed that the quality of MgAg produced in the first ball-milling step critically determines the performance of the final MgAgSb. The particle sizes of Mg and Ag were found to strongly influence the quality of the MgAg precursor. To address this, a sintering step was incorporated after the initial MgAg ball milling to improve precursor quality and reduce the Ag₃Sb impurity content, resulting in a peak ZT of approximately 1.2 at 500 K.⁵⁶ Moreover, the Boor research group established clear synthesis–composition–property relationships (Fig. 4D), enabling the reproducible preparation of high-performance MgAgSb (ZT = 1.34 at 561 K).⁵⁵ They also reported that, within the Mg–Ag–Sb phase diagram, the homogeneity range for MgAgSb is extremely narrow (<0.1 at%), meaning that the TE performance of MgAgSb is highly sensitive to impurity phases, primarily due to their adverse effect on carrier mobility. Other notable findings include: cleaning the ball-milling jar after the first milling step improves performance reproducibility; secondary phases such as Mg₃Sb₂ and Sb exert only a minor influence on the TE performance of MgAgSb, whereas Ag and Ag₃Sb substantially degrade performance. Additionally, the intense cold welding of the powders during the ball milling process of MgAgSb was identified as the main cause of impurity formation, since it hindered contact and reaction between the raw materials and the fractured powders. To address this issue, Li et al. introduced stearic acid, a classical ball-milling aid, into MgAgSb. By reducing the extent of cold welding, sufficient milling was achieved with significantly less time. As a result, the required ball milling duration was shortened from the conventional 20 hours to only 5 hours, while maintaining high performance and greatly reducing lattice thermal conductivity.⁸⁸

Although two-step high-energy ball milling proved to be the most successful means of synthesizing high-performance MgAgSb, this process is very time-consuming and labor-intensive, and is one of the most significant limiting factors preventing the replacement of commercial Bi₂Te₃ by MgAgSb for large-scale applications. Aiming for a faster and scalable fabrication route, Ying et al. used the high-temperature melting method to prepare MgAgSb.⁷⁵ To eliminate impurity phases during long-term annealing at the phase transition temperature, indium (In) was used to replace antimony (Sb) to further optimize the carrier concentration. Ultimately, the prepared samples achieved a ZT peak value of 1.1 at 525 K. Similarly, Huang et al. utilized high-temperature melting and low-temperature annealing of Ta tubes to achieve higher-quality pure MgAgSb with larger grain sizes and lower oxygen content than those produced by high-energy ball milling.⁷⁴ They obtained an average power factor of 25 µW cm⁻¹ K⁻² and an average ZT value of 1.1 in the temperature range of 300 to 550 K. The comparable ZT achieved by the high-temperature melting method make competitive alternative to high-energy ball milling. However, the specific techniques of Ta tube limit the large-scale materials production for practical applications.

2.3. Defect engineering and composite strategy optimization

In thermoelectric materials, defect structures are deliberately engineered to achieve the selective scattering of charge carriers and phonons, thereby enhancing the overall figure of merit. In the case of MgAgSb, both computational and experimental studies have consistently identified Ag vacancies, an intrinsic defect, as the dominant factor responsible for its inherent p-type semiconductor behavior.^83,89,90 Moreover, a high concentration of Ag vacancies plays a crucial role in suppressing lattice thermal conductivity. Liu et al. demonstrated that Ag vacancies are highly sensitive to the sintering temperature, enabling the precise tuning of carrier concentration and the power factor through controlled thermal processing.⁸³ Given the high volatility of Mg, Li et al. extended these investigations to Mg–Ag antisite defects and their tunability.¹⁷ Experimental observations revealed the presence of Mg–Ag antisite defects within the lattice, forming interconnected nanoscale regions embedded in the matrix. This unique microstructural feature serves as an efficient phonon-scattering network while largely preserving carrier transport pathways. To further promote the formation of such defects, Zn doping was employed to reduce their formation energy. This strategy effectively suppressed the Ag-rich secondary phase, enhanced phonon scattering, and improved carrier mobility, thereby lowering the lattice thermal conductivity. As a result, an average ZT of approximately 0.75 was achieved in the low-temperature range of 200–400 K. Building upon defect engineering, Xie et al. realized an ultralow lattice thermal conductivity by constructing multi-scale structural defects in α-MgAgSb through high-energy ball milling followed by low-temperature sintering.¹⁶ The resulting microstructure, comprising ultrafine nanocrystals, high-density dislocations, and randomly distributed micro- and nanopores, facilitated multi-scale phonon scattering (Fig. 5A–C), yielding a lattice thermal conductivity as low as 0.46 W m⁻¹ K⁻¹ at 300 K, surpassing the typical lower bound for such materials. Although this approach caused a slight reduction in electrical performance, it produced an unprecedented ZT of ∼0.94 at 300 K and an average ZT of ∼1.16 over the range from room temperature to 473 K. In a complementary approach, Liao et al. exploited sintering pressure as a means to regulate the size of micropores within MgAgSb, thereby achieving an optimal trade-off between carrier mobility and lattice thermal conductivity.⁵² Samples processed at 80 MPa exhibited a high room-temperature mobility of 87.7 cm² V⁻¹ s⁻¹ and a low lattice thermal conductivity of 0.452 W m⁻¹ K⁻¹ at 423 K, resulting in an average ZT of 1.11 across the temperature range of 323–573 K. As different defects exhibit different dimensions and sizes, their phonon-scattering behaviors are related to the phonon wavelengths they interact with. For example, Ag vacancies and Mg–Ag antisite defects primarily scatter high-frequency phonons, thereby suppressing the lattice thermal conductivity at elevated temperatures. To achieve phonon scattering across the entire frequency spectrum, constructing hierarchical (multi-scale) defect structures becomes essential, which has already been demonstrated in the work of Xie et al.¹⁶

Using a rapid microwave-assisted synthesis approach, Xin et al. incorporated SnTe nanoinclusions into the MgAgSb matrix, which significantly enhanced the Seebeck coefficient by effectively suppressing the bipolar effect.⁵⁴ Simultaneously, the introduction of a multiscale hierarchical architecture markedly reduced the lattice thermal conductivity (Fig. 5D–F). Consequently, MgAgSb containing 3 at% SnTe exhibited a 53% increase in ZT (∼1.0 at 548 K) compared with pristine MgAgSb. Building on the carrier injection effect associated with metal–semiconductor ohmic contacts, Xie et al. introduced homogeneously distributed in situ MgCuSb nanoprecipitates within the MgAgSb matrix to optimize the carrier concentration of MgCuSb/MgAgSb composites (Fig. 5G–I), thereby decoupling interdependent electronic transport parameters.¹⁵ This strategy yielded a record-high average power factor (PF_ave) of 27.2 µW cm⁻¹ K⁻² for MgCu_0.1Ag_0.87Sb_0.99 in the temperature range of 300–550 K, surpassing all previously reported values for the MgAgSb system and approaching those of classical Bi₂Te₃-based materials. On this basis, Jiao et al. examined the high-temperature stability of MgAgSb and found that prolonged annealing at 548 K induced the formation of significant amounts of Ag₃Sb secondary phase, which increased thermal conductivity and reduced the Seebeck coefficient, thereby severely degrading ZT.⁹¹ To counteract this, Cu enrichment at grain boundaries was employed to lower grain-boundary energy, enabling both thermodynamic and kinetic stabilization of the nanostructure. As a result, the final compound remained thermally stable after 14 days of annealing at 548 K.

3. Progress in MgAgSb-based thermoelectric devices

3.1. Developed interface materials

For thermoelectric (TE) devices, overall conversion efficiency and cooling performance depend not only on the intrinsic TE properties of the bulk materials but also on the performance of the interfacial materials. Pei et al. calculated the relationship between interfacial resistivity (ρ_c) and conversion efficiency, showing that efficiency decreases sharply as ρ_c increases.^92–95 Thus, minimizing ρ_c is essential for achieving high conversion efficiency. Equally important is the thermal and chemical stability of the interface, particularly for TE power-generation modules, whose hot-side junctions operate continuously at elevated temperatures. Such conditions provide sufficient energy for atomic reactions and diffusion across the joining interface.^96–99 In these environments, high-reactivity electrode materials (e.g., Cu) and solders (e.g., Sn, Ag, Cu alloys) can diffuse into the TE material, severely degrading its performance because semiconductors are highly sensitive to trace amounts of impurity elements.^100,101 Therefore, in addition to achieving a low ρ_c, ensuring high interfacial stability is critical, especially for TE power-generation applications.

Over the past several years, the selection strategy of TEiM in the TE region has undergone considerable development, and interestingly, the TEiM of MgAgSb is exactly a typical representative case study. Initially, trial-and-error methods were used to choose a metal with a familiar coefficient of thermal expansion (CTE) of TE materials as TEiM. For MgAgSb, Kraemer et al.⁶⁹ selected Ag as the TEiM of MgAgSb due to the comparable CTE (∼20 × 10⁻⁶ K⁻¹) and showed a relatively low interfacial resistivity of ∼10 µΩ cm² (Fig. 6A and B). This value is within an acceptable range. Moreover, the excellent wettability and native low resistivity of Ag make it the most used TEiM of MgAgSb for a long while. Ying et al.^18,102 and Liu et al.¹⁰³ all selected Ag as TEiM of MgAgSb to fabricate the TE power generation and cooling device and obtain high conversion efficiency and maximum temperature difference. However, the conversion efficiency of the MgAgSb/Mg₃Sb_0.7Bi_1.3 device that takes Ag as TEiM shows a great reduction after long-term operating at 523 K. The formed Ag₃Sb at the Ag/MgAgSb interface is considered to be a potential cause (Fig. 6C and D). Subsequent aging experiments of the Ag/MgAgSb interface conducted by Xie et al. suggested that ρ_c of the Ag/MgAgSb interface will dramatically increase to even ∼1000 µΩ cm² after aging at ∼553 K for just 12 hours.⁶⁸ The formation of cracks induced by the formation of the impurity phase of Ag₃Sb at the Ag/MgAgSb interface, and the high and varied CTE of Ag₃Sb with temperature, is the main reason (Fig. 6E and F). Similar experimental results were obtained by Zhang et al., and they found that cross section area of TE junctions with TEiM is an important factor that dramatically affects ρ_c of the Ag/MgAgSb interface.¹⁴

To avoid the high interfacial resistivity caused by chemical reaction at the interface, a high-throughput method for TEiM selection has been proposed by Chen et al.,¹⁰⁴ by mixing TEiM candidate alloys into TE materials and then aging the as-sintered bulks at operating temperature for a certain time, the thickness of the interface reaction/diffusion layer (IRL) certified by SEM was indicated to evaluate the interface diffusion and reaction behavior between potential candidates and TE materials, as a select criterion. Wu et al. applied such methods to MgAgSb, and AgMg compounds, which were filtered out according to the limited IRL⁶⁷ (Fig. 7A and B). After that, tiny Mn was alloyed with AgMg to form AgMgMn_0.1 for CTE optimization. Benefited from weak interface reaction and matched CTE (Fig. 7C), a high bonding strength of 34.5 MPa and a low contact resistivity of 4.5 µΩ cm² were obtained for the AgMgMn_0.1/MgAgSb interface. Similarly, Zou et al. creatively used a high-throughput screening approach to alternately stack ten kinds of metal candidate powders with MgAgSb powders to form bulk samples with a segmented structure by one-step sintering at 573 K.⁶⁴ Such a segmented structure allows direct characterization of interfacial resistivity and determines the elemental diffusion and chemical reaction by electrical and elemental analysis scanning across all aged interfaces (Fig. 7D–F). The selected Co/MgAgSb exhibits a low interfacial resistivity of 2.5 µΩ cm², high bonding strength of 60.6 MPa, and high thermal stability at 573 K. The interfacial microstructure and calculated interfacial reactions, as well as diffusion behaviors, indicated that the excellent electrical, mechanical, and chemical stability of the Co/MgAgSb junction is mainly attributed to the formation of strong covalent bonds between Co and Sb atoms, thereby maintaining an inert and stable interface.

Although high-throughput methods can effectively select stable and low-resistivity TEiMs, this process entails synthesis, processing, and long-term annealing at elevated temperatures, which is time- and cost-consuming. More importantly, the chemical reaction at the interface could not be easily predicted by the junction during the short-term aging process. Additionally, the limited availability of elements restricts the range of material choices. To address this challenge, Xie et al., taking MgAgSb as a case study from the perspective of the Gibbs energy of the interface structure of TEiM and TE materials, developed a universal TEiM screening strategy based on phase diagram predictions by density functional theory, combining the phase diagram with electrical resistivity and melting points of potential reaction products (Fig. 8).⁶⁸ By using the established screen strategy, semimetal MgCuSb as a reliable TEiM for high-performance MgAgSb was discovered. The MgCuSb/MgAgSb junction exhibits low interfacial contact resistivity (1 µΩ cm²) even after annealing at 553 K for 16 days. Moreover, the university of this TEiM screen strategy was verified in several representative TE materials—Bi₂Te₃, Zn₄Sb₃, CoSb₃, and NbFeSb—from room temperature to high temperature.

Considering that Sb diffusion from MgAgSb to the TEiM will induce Sb deficiency in MgAgSb and impair the TE performance of MgAgSb. Li et al. directly employ Sb as the TEiM in MgAgSb.⁶⁵ Specifically, the Sb/MgAgSb junction exhibits a self-optimized ρ_c even exposed to 573 K for 30 days in air (decreasing from 20.8 µΩ cm² to 7.9 µΩ cm²). The structural evolution analysis indicates that Mg diffusion from MgAgSb into the Sb TEiM leads to Mg deficiency and thereby an increased carrier concentration in MgAgSb, which is the main reason for optimized ρ_c. Except for excellent thermal stability and self-optimized ρ_c, low cost and high wettability are two other advantages for large-scale applications and assembly of MgAgSb-based TE module. Based on a similar idea, that is, considering the inherent high chemical reactivity and volatility of Mg,⁶⁶ Chen et al. developed Mg₂Ni as a unified contact layer for both MgAgSb and Mg₃(Bi, Sb)₂. Benefits from comparable CTE between Mg₂Ni and MgAgSb, the Mg₂Ni/MgAgSb junction exhibits an excellent low ρ_c and high reliability. As shown in Fig. 9, the ρ_c of the Mg₂Ni/MgAgSb junction increases from ∼1.7 µΩ cm² to ∼5.1 µΩ cm² even after annealing at 573 K for 30 days.

3.2. MgAgSb-based cooling devices

Initially, MgAgSb has long been considered a promising p-type material for power generation. However, it was only recently that n-type Mg₃(Bi, Sb)₂ with high performance near room temperature was developed.¹⁰⁶ Consequently, Liu et al. combined the Mg₃(Bi, Sb)₂ to fabricate an eight-pair Mg-based cooling device for the first time.¹⁹ At a high-temperature end temperature of 325 K, the device achieved a maximum temperature difference of 56.5 K and a maximum cooling power of 3.0 W, demonstrating significant cooling application potential. Xie et al. improved the room temperature ZT value of MgAgSb by constructing multi-scale defects. The seven pairs of Mg-based devices they constructed achieved a maximum temperature difference of 52 K at the high temperature end of 300 K, and a cooling efficiency coefficient of performance (COP) of 8.3 at a temperature difference of 5 K, which is slightly lower than that of Bi₂Te₃.¹⁶ Thanks to the performance optimization of n-type Mg₃(Bi, Sb)₂, the Mg-based device fabricated by Ying et al. achieved a maximum temperature difference of 52 K at a high temperature of 302 K.¹⁸ Zhang et al. utilized n-type Bi₂Te₃ as the n-type leg and combined it with devices prepared using MgAgSb optimized for near-room-temperature performance, achieving a maximum temperature difference of 60 K at the high-temperature end of 300 K.¹⁴ Another two-pair TE cooling device prepared by Li et al., which consists of MgAgSb and commercial n-type Bi₂Te₃, obtained a temperature difference of 47 K at T_h = 300 K.¹⁷ Overall, regardless of whether MgAgSb is combined with n-type Mg₃(Bi, Sb)₂ or Bi₂Te₃ to fabricate cooling devices, satisfactory cooling performance can be achieved. However, compared to Bi₂Te₃-based devices, there is still some room for improvement. Therefore, a higher TE cooling performance is anticipated once the TE performance of MgAgSb at room temperature is enhanced.

3.3. MgAgSb-based power generation devices

In 2015, Kraemer et al. were the first to investigate the conversion efficiency of single-leg MgAgSb-based thermoelectric devices, reporting a remarkable efficiency of up to 8.5% under a temperature difference of 225 K.⁶⁹ This performance exceeded that of conventional Bi₂Te₃-based devices, highlighting the strong potential of MgAgSb as a promising candidate for room-temperature thermoelectric power generation. More recently, advancements in the low-temperature thermoelectric performance of n-type Mg₃(Bi, Sb)₂ have paved the way for the fabrication of all-Mg-based multi-leg thermoelectric modules. Following these developments, MgAgSb-based thermoelectric generators have undergone rapid progress, with device-level conversion efficiency improving significantly (Fig. 12). This growth can be attributed to three main factors:

(1) Enhancement of thermoelectric performance in n-type and/or p-type materials. In 2021, Ying et al. fabricated the first four-pair Mg-based thermoelectric generator, achieving a maximum conversion efficiency of 7% under a temperature difference of 250 K by integrating segmented n-type Mg₃(Bi, Sb)₂ and p-type MgAgSb.¹⁰² Around the same time, Liu et al. reported a higher efficiency of 7.3% at a ΔT of 300 K in a seven-pair Mg-based device, enabled by performance-optimized Mg₃(Bi, Sb)₂ doped with Cu.¹⁰³ Subsequently, Zhang et al. achieved a notable conversion efficiency of 12% at 300 K using seven-pair devices constructed with MgAgSb synthesized through an optimized preparation process.¹³ From the perspective of practical application, Xie et al. further improved device-level performance by tailoring the geometric structure of the module based on power factor enhancement strategies. Their eight-pair Mg-based device delivered a maximum output power of 1.03 W and a peak conversion efficiency of 7.6% at a temperature difference of 300 K.¹⁵

(2) Development of thermoelectric interface materials (TEiM) for MgAgSb. Reducing interfacial contact resistivity plays a crucial role in minimizing parasitic electrical losses and enhancing overall device performance. Wu et al. reported a conversion efficiency of 9.1% and an output power of 0.5 W at a temperature difference of 325 K by employing AgMgMn_0.1 as a TEiM for MgAgSb.⁶⁷ Similarly, Xie et al. achieved a conversion efficiency of 9.25% and an output power of 0.53 W at ΔT = 300 K using MgCuSb as the TEiM of MgAgSb.⁶⁸ Furthermore, Li et al.,⁶⁵ Zuo et al.,⁶⁴ and Chen et al.⁶⁶ explored alternative TEiMs including Sb, Co, and Mg₂Ni, achieving conversion efficiencies of 8.1% (294 K), 10.2% (287 K), and 10.8% (300 K), respectively.

(3) Optimization of device geometry. It is well established that the p-type and n-type legs in a thermoelectric device typically exhibit different transport properties, which prevents the device from reaching optimal performance under uniform temperature gradients and current conditions. To address this mismatch, careful geometric design is required to maximize device efficiency. However, Ying et al. revealed that¹⁰⁷ the large temperature gradient and short distance between the hot and cold ends induced intense thermal radiation and convection during actual operation, which severely disturbed the intended heat flow and resulted in lower conversion efficiency. To mitigate this undesired heat transfer, Ying et al. systematically investigated the influence of the fill factor (FF) on device performance. They found that increasing the FF from 16% to 64% led to a significant improvement in conversion efficiency by reducing undesired heat (Fig. 10). This result was subsequently validated by Xie et al., further confirming the critical role of geometric optimization in thermoelectric device design.⁶⁸

In addition to the single-stage module, Xie et al. developed a segmented thermoelectric module in which MgAgSb and Mg₃SbBi serve as the low-temperature segment, while n- and p-type skutterudites form the high-temperature segment¹⁰⁸ (Fig. 11). This design was proposed to address the limited operating temperature range of MgAgSb, resulting from its low phase-transition temperature. Owing to the use of proven TEiMs, an optimized geometric design, and an expanded operating temperature window, the module achieved a high conversion efficiency of 12.4% at T_C = 293 K and ΔT = 540 K. This work opens a promising avenue for MgAgSb-based thermoelectric devices in medium-temperature waste-heat recovery.

Beyond the extensively investigated n-type Mg₃(Bi, Sb)₂, several other low-temperature n-type thermoelectric materials—such as Bi₈₅Sb₁₅, Mg₂(Si, Sn), and Ag₂Se—have been coupled with MgAgSb to construct power generation devices. Notably, the Bi₈₅Sb₁₅/MgAgSb device developed by Chen et al. delivered an output power density of 76.8 mW cm⁻² and a conversion efficiency of 1.76% within the 200–300 K temperature range.¹⁰⁹ Likewise, Wieder et al. reported that a MgAgSb/Mg₂(Si, Sn) device attained a conversion efficiency of 6.4% and an output power of 0.68 W under a temperature gradient of 275 K.¹¹⁰ Furthermore, a uni-couple MgAgSb/Ag₂Se system achieved an efficiency of approximately 1.9% at a temperature differential of ∼82 K,¹¹² underscoring the broad applicability and versatility of MgAgSb-based architectures for low-temperature thermoelectric energy harvesting.

3.4. Stability and reliability of MgAgSb devices

Thermoelectric devices are widely regarded as having the potential for exceptionally long service lifetimes, primarily because they perform solid-state energy conversion without relying on moving parts or mechanical motion during operation. This durability is exemplified by the long-term operation of the isotope thermoelectric battery aboard Voyager 1.¹¹³ However, extended operation under high temperature differentials subjects these devices to thermal shocks, temperature-gradient-driven element diffusion, and accelerated interfacial reactions between components. These factors collectively pose serious challenges to the long-term stability of device performance. As a result, degradation over time has become a critical issue, drawing increasing attention in recent research. As previously discussed, the operational stability of thermoelectric devices is principally governed by two factors: the intrinsic thermoelectric properties of the constituent materials and the thermal/electrical resistances at the TEiM-material interfaces. For devices comprising p-type MgAgSb and n-type Mg₃(Bi, Sb)₂, Ying et al. reported that employing Ag as a barrier layer led to interfacial second-phase formation during operation, thereby increasing interface resistance and causing a ∼10% reduction in output power after 32 000 thermal cycles within the 323–500 K range.¹⁸ From a materials standpoint, p-type MgAgSb generally exhibits excellent long-term stability; however, Jiao et al. demonstrated that its ZT value undergoes slight degradation during prolonged high-temperature annealing, warranting continued investigation.⁹¹ Conversely, n-type Mg₃(Bi, Sb)₂ is well known to be susceptible to reactions with water and oxygen, resulting in diminished thermoelectric performance.^114–116 Their stability, therefore, remains a major concern. Xie et al. further revealed that Mg volatilization in Mg₃(Bi, Sb)₂ under long-term high-temperature operation in vacuum environments markedly increases internal resistance, thereby reducing device output power.⁶⁸ To mitigate such degradation pathways, Ying et al. applied an HfO₂ protective coating via atomic layer deposition (ALD) to the device (Fig. 11A), which effectively preserved structural integrity, maintaining 93% of the module's initial output power even after re-soldering and approximately 65 000 cycles in air (Fig. 13B).⁷⁰ Additionally, extended service testing of Mg-based modules in air underscored the critical role of solder stability in performance retention, highlighting for the first time the necessity of advanced joining technologies to ensure long-term device reliability (Fig. 13C).

4. Summary and outlooks

Following sustained research efforts, the intrinsic crystallographic characteristics and electronic band structure of MgAgSb, together with the fundamental mechanisms governing its high carrier mobility and intrinsically low lattice thermal conductivity, have been comprehensively elucidated. Correspondingly, synthesis methodologies have undergone substantial refinement, encompassing advanced phonon-engineering strategies such as the introduction of multi-scale phonon scattering centers through point defects and hierarchical defect structures, as well as the integration of second-phase composite approaches. These measures have collectively yielded marked enhancements in the PF and/or ZT. On the device level, the systematic development of thermoelectric interface materials—drawing on a variety of representative design strategies—has facilitated the fabrication of MgAgSb-based interfaces tailored to diverse operational demands. When combined with optimized geometrical configurations, these advances have enabled the performance of Mg-based thermoelectric generators to significantly outperform those of conventional Bi₂Te₃-based devices within the temperature range of room temperature to 573 K, while Mg-based thermoelectric cooling modules have demonstrated cooling efficiencies on par with their Bi₂Te₃ counterparts. Owing to their abundance of constituent elements, superior mechanical robustness, and promising functional properties, Mg-based thermoelectric materials exhibit substantial potential for broad application. Nonetheless, several critical challenges persist, which presently constrain their full-scale technological deployment.

(1) Cost of raw materials. An often-overlooked limitation lies in the economic burden imposed by the use of silver (Ag) as a constituent element. Despite its higher crustal abundance relative to tellurium (Te), silver's classification as a precious metal substantially elevates the production cost of MgAgSb, placing it above that of most conventional thermoelectric materials.

(2) Low-temperature TE performance. Although the room-temperature ZT of MgAgSb has been enhanced through multi-scale defect engineering and optimization of synthesis protocols, it remains notably inferior to that of p-type Bi₂Te₃. Consequently, the overall cooling performance of Mg-based devices continues to lag behind that of commercial Bi₂Te₃ counterparts, representing a significant barrier to their large-scale deployment. Hence, further elevating the ZT of MgAgSb at room and sub-ambient temperatures emerges as a critical imperative for future research.

(3) Device stability. In terms of the application of Mg-based power generation devices, ensuring long-term operational stability of the devices under real-world conditions warrants paramount attention. This encompasses not only the intrinsic stability of both p-type and n-type materials, but also the environmental resilience of TEiMs—particularly their oxidation resistance in air—and, most critically, the thermal and chemical stability of the solder joints.

In summary, the past decade has witnessed remarkable advancements in MgAgSb, encompassing optimization of the synthesis process, engineering of interface materials, and design and fabrication of devices. Nevertheless, substantial challenges persist, and concerted efforts remain imperative to surmount the barriers hindering its large-scale practical deployment.

Author contributions

Liangjun Xie: conceptualization, writing – original draft, writing – review & editing. Ran He: conceptualization, review, supervision, and funding acquisition. Jiehe Sui: review and supervision. Kornelius Nielsch: review and supervision. Zihang Liu: conceptualization, review and editing, supervision, and funding acquisition.

Conflicts of interest

There are no conflicts to declare.

Acknowledgments

This work was funded by the National Natural Science Foundation of China (No. 22409043 and U23A20556) and European Union’s Horizon European Research Council Programme (ERC Starting Grant, TENTATION, 101116340).

Biographies

Biography

Liangjun Xie is a postdoctoral researcher at the Leibniz Institute for Solid State and Materials Research (IFW Dresden), Germany, supported by the Alexander von Humboldt Fellowship since 2026. He received his PhD from the Harbin Institute of Technology in 2023. His research focuses on Mg-based thermoelectric materials for thermoelectric cooling and power generation.

Biography

Ran He has led a research group at the Leibniz Institute for Solid State and Materials Research at IFW Dresden, Germany, since 2020. He earned his PhD degree from the University of Houston in 2016. He then worked as a postdoctoral researcher at the Leibniz Institute for Solid State and Materials Research at IFW Dresden. He led a German Research Foundation (DFG) project and was awarded a European Research Council Starting Grant in 2023. His research focuses on electronic and phononic structures of solids, semiconductor energy materials, and nonequilibrium synthesis of thermoelectric materials.

Biography

Jiehe Sui is a professor at the School of Materials Science and Engineering, Harbin Institute of Technology. He received his PhD degree from Harbin Institute of Technology in 2006. From 2013 to 2015, he served as a visiting scholar at the University of Houston, USA. He received the funding of the 2016 National Natural Science Fund for Excellent Young Scientists. His research focuses on thermoelectric materials optimization and thermoelectric device fabrication, particularly for energy conversion applications. To date, he has authored over 260 SCI-indexed papers, including Science, Joule, and Nature Communications.

Biography

Kornelius Nielsch has been Director of the Institute for Metallic Materials (IMW) at the Leibniz Institute for Solid State and Materials Research Dresden (IFW) since 2015, where he leads a research group working on sustainable thermoelectric materials and devices for thermoelectric cooling. Professor Nielsch received his diploma in physics from the University of Duisburg in 1997 and his PhD in physics from Martin Luther University Halle-Wittenberg, Germany, in 2002. From 2002 to 2003, he was a postdoctoral fellow at MIT after which he took up the position of group leader at the Max Planck Institute for Microstructure Physics in Halle, Germany, in 2003. Kornelius Nielsch then moved to the Institute of Applied Physics at the University of Hamburg, where he was Professor of Experimental Physics from 2007 to 2015. From 2009 until 2015, he has coordinated the Priority Program on Nanostructured Thermoelectrics, and he is currently coordinating the Marie Curie Doctoral Network on Mg-based alloys for thermoelectric cooling in collaboration with 15 partner institutions across Europe.

Biography

Zihang Liu is a full professor at the School of Materials Science and Engineering, Harbin Institute of Technology. He received the funding of the 2021 National Natural Science Fund for Excellent Young Scientists (Overseas). He completed his PhD in materials science and engineering at the Harbin Institute of Technology. He worked as a postdoctoral fellow at the University of Houston, USA, and the National Institute for Materials Science, Japan, from March 2017 to August 2021. His research interests include thermoelectric materials and devices, DFT calculations, as well as flexible materials for applications in energy conversion and storage. As the first author or corresponding author, he has published over 50 papers in high-quality journals, including Science, Joule, Nature Communications, and Proceedings of the National Academy of Sciences of the United States of America, with a total number of citations exceeding 8000.

Data availability

No primary research results, software or code have been included and no new data were generated or analysed as part of this review.

References

Snyder G. J. Toberer E. S. Complex Thermoelectric Materials. Nat. Mater. 2008;7:105–114. doi: 10.1038/nmat2090. [DOI] [PubMed] [Google Scholar]
Jiang B. Yu Y. Cui J. Liu X. Xie L. Liao J. Zhang Q. Huang Y. Ning S. Jia B. Zhu B. Bai S. Chen L. Pennycook S. J. He J. High-Entropy-Stabilized Chalcogenides with High Thermoelectric Performance. Science. 2021;371:830–834. doi: 10.1126/science.abe1292. [DOI] [PubMed] [Google Scholar]
He J. Tritt T. M. Advances in thermoelectric materials research: Looking back and moving forward. Science. 2017;357:eaak9997. doi: 10.1126/science.aak9997. [DOI] [PubMed] [Google Scholar]
Shi X. L. Li N. H. Li M. Chen Z. G. Toward Efficient Thermoelectric Materials and Devices: Advances, Challenges, and Opportunities. Chem. Rev. 2025;125(16):7525–7724. doi: 10.1021/acs.chemrev.5c00060. [DOI] [PubMed] [Google Scholar]
Shen K. Yang Q. Qiu P. Zhou Z. Yang S. Wei T. R. Shi X. Ductile P-Type AgCu(Se,S,Te) Thermoelectric Materials. Adv. Mater. 2024:e2407424. doi: 10.1002/adma.202407424. [DOI] [PubMed] [Google Scholar]
Liu S. Qin Y. Wen Y. Shi H. Qin B. Hong T. Gao X. Cao Q. Chang C. Zhao L. D. Efforts Toward the Fabrication of Thermoelectric Cooling Module Based on N-Type and P-Type PbTe Ingots. Adv. Funct. Mater. 2024;34:2315707. doi: 10.1002/adfm.202315707. [DOI] [Google Scholar]
Jiang F. Lin C. Cheng J. Yu H. Zhou Y. Ma X. Wu L. Ye S. Chen J. Zhi S. Xu Y. Zhao P. Wang X. Cao F. Zhang Q. Mao J. Prefer-Oriented Ag2Se Crystal for High-Performance Thermoelectric Cooling. Adv. Funct. Mater. 2024;35:2415000. doi: 10.1002/adfm.202415000. [DOI] [Google Scholar]
Zhu Y. Yu Y. Zhang H. Qin Y. Wang Z.-Y. Zhan S. Liu D. Lin N. Tao Y. Hong T. Wang S. Ge Z.-H. Wuttig M. Zhao L.-D. Large Mobility Enables Higher Thermoelectric Cooling and Power Generation Performance in n-type AgPb18+xSbTe20 Crystals. J. Am. Chem. Soc. 2023;145:24931–24939. doi: 10.1021/jacs.3c09655. [DOI] [PubMed] [Google Scholar]
He B. He Y. Wang W. Sun Y. Kong S. Huang J. Ru Y. Qin B. Ren H. He J. Zhao T. Li J. Lu J. Zhao L. D. Liu M. Strain-coupled, crystalline polymer-inorganic interfaces for efficient magnetoelectric sensing. Science. 2025;389:623–631. doi: 10.1126/science.adt2741. [DOI] [PubMed] [Google Scholar]
Zhao K. Yue Z. Wuliji H. Chen H. Deng T. Lei J. Qiu P. Chen L. Shi X. Modeling critical thermoelectric transports driven by band broadening and phonon softening. Nat. Commun. 2024;15:776. doi: 10.1038/s41467-024-45093-6. [DOI] [PMC free article] [PubMed] [Google Scholar]
Papapetrou M. Kosmadakis G. Cipollina A. La Commare U. Micale G. Industrial waste heat: Estimation of the technically available resource in the EU per industrial sector, temperature level and country. Appl. Therm. Eng. 2018;138:207–216. [Google Scholar]
Photographic Periodic Table, Abundance in Earth's Crust of the elements, https://periodictable.com/Properties/A/CrustAbundance.an.html
Zhang X. Zhu H. Dong X. Fan Z. Yao Y. Chen N. Yang J. Guo K. Hao J. He L. Li G. Zhao H. High-performance MgAgSb/Mg3(Sb,Bi)2-based thermoelectrics with η = 12% at T ≤ 583 K. Joule. 2024;8:3324–3335. [Google Scholar]
Zhang X. Chen N. Guo K. Zhang Q. Zhao Q. Xu J. Zhu H. Zhao H. High cooling and power generation performance of α-MgAgSb with intrinsic low lattice thermal conductivity. Mater. Today Phys. 2024;44:101451. [Google Scholar]
Xie L. Peng G. Sun Y. Liu Z. Li F. Zhu Y. Zhu J. Wu H. Qu N. Shi W. Jiao L. Guo F. Cai W. Wu H. Sui J. Semiconductor-Semimetal Composite Engineering Enabling Record-High Thermoelectric Power Density for Low-Temperature Energy Harvesting. Adv. Funct. Mater. 2024;34:2401763. doi: 10.1002/adfm.202401763. [DOI] [Google Scholar]
Xie L. Yang J. Liu Z. Qu N. Dong X. Zhu J. Shi W. Wu H. Peng G. Guo F. Zhang Y. Cai W. Wu H. Zhu H. Zhao H. Liu Z. Sui J. Highly efficient thermoelectric cooling performance of ultrafine-grained and nanoporous materials. Mater. Today. 2023;65:5–13. doi: 10.1016/j.mattod.2023.03.021. [DOI] [Google Scholar]
Li J. Li G. Chen Q. Feng J. Feng T. Xi L. Liu W. Zhang W. Liu R. Sun R. Manipulating Anti-Site Defects in α-MgAgSb for Thermoelectric Cooling Enhancement. Interdiscip. Mater. 2025;4(5):719–727. [Google Scholar]
Ying P. Wilkens L. Reith H. Rodriguez N. P. Hong X. Lu Q. Hess C. Nielsch K. He R. A Robust Thermoelectric Module Based on MgAgSb/Mg3(Sb, Bi)2 with a Conversion Efficiency of 8.5% and A Maximum Cooling of 72 K. Energy Environ. Sci. 2022;15:2557–2566. doi: 10.1039/D2EE00883A. [DOI] [Google Scholar]
Liu Z. Gao W. Oshima H. Nagase K. Lee C.-H. Mori T. Maximizing the Performance of N-type Mg3Bi2 Based Materials for Room-Temperature Power Generation and Thermoelectric Cooling. Nat. Commun. 2022;13:1120. doi: 10.1038/s41467-022-28798-4. [DOI] [PMC free article] [PubMed] [Google Scholar]
Dong X. Jiao L. Tong H. Wu H. Liang H. Zhang X. Wang L. Wen Q. Liu M. Ge Z. Guo F. Luo D. Zhu Y.-K. Liu Z. Cai W. Sui J. Heavy doping driven ultra-low lattice thermal conductivity and mechanical enhancement in Mg3(Bi, Sb)2 for efficient power generation. Acta Mater. 2025;300:121451. doi: 10.1016/j.actamat.2025.121451. [DOI] [Google Scholar]
Zhu G. Liu W. Lan Y. Joshi G. Wang H. Chen G. Ren Z. The effect of secondary phase on thermoelectric properties of Zn4Sb3 compound. Nano Energy. 2013;2:1172–1178. doi: 10.1016/j.nanoen.2013.04.010. [DOI] [Google Scholar]
Wang M. Zhang Q. Pang K. Yuan M. Pan Q. Li R. Miao L. Tan X. Hu H. Wu J. Sun P. Liu G. Q. Jiang J. Robust Homogeneous Segmented Power Generator Driven by Sb2Te3-Based Thermoelectrics. Adv. Mater. 2025;37:e2503128. doi: 10.1002/adma.202503128. [DOI] [PubMed] [Google Scholar]
Du J. Sun Y. Guo F. Tong H. Yu Z. Liu Z. Zhu J. Sui J. Enhanced Thermoelectric Cooling Performance of (Bi, Sb)2Te3 Through Platinum Doping. Mater. Today Phys. 2025;53:101705. doi: 10.1016/j.mtphys.2025.101705. [DOI] [Google Scholar]
Hu J. Sun Y. Wu H. Yu Z. Zhu J. Guo F. Liu Z. Cai W. Sui J. All-Mg3Sb2-Based Module for Thermoelectric Power Generation. Adv. Funct. Mater. 2024;35:2418244. doi: 10.1002/adfm.202418244. [DOI] [PubMed] [Google Scholar]
Naderloo R. H. Villoro R. B. Mattlat D. A. Ying P. Song S. Bayesteh S. Nielsch K. Scheu C. Ren Z. Zhu H. Zhang S. He R. Performance advancements in P-type TaFeSb-based thermoelectric materials through composition and composite optimizations. Energy Environ. Sci. 2025;18:738–749. doi: 10.1039/D4EE04819A. [DOI] [Google Scholar]
Dharmaiah P. Heo M. Nagarjuna C. Jung S.-J. Won S. O. Lee K. H. Kim S. K. Kim J.-S. Ahn B. Kim H.-S. Baek S.-H. Enhancement of thermoelectric properties in p-type ZnSb alloys through Cu-doping. J. Alloys Compd. 2024;1004:175739. doi: 10.1016/j.jallcom.2024.175739. [DOI] [Google Scholar]
Ai X. Xue W. Giebeler L. Pérez N. Lei B. Zhang Y. Zhang Q. Nielsch K. Wang Y. He R. Interstitial Defect Modulation Promotes Thermoelectric Properties of p-Type HfNiSn. Adv. Energy Mater. 2024;14:2401345. doi: 10.1002/aenm.202401345. [DOI] [Google Scholar]
Zhu H. Li W. Nozariasbmarz A. Liu N. Zhang Y. Priya S. Poudel B. Half-Heusler alloys as emerging high power density thermoelectric cooling materials. Nat. Commun. 2023;14:3300. doi: 10.1038/s41467-023-38446-0. [DOI] [PMC free article] [PubMed] [Google Scholar]
Ren G. K. Wang S. Zhou Z. Li X. Yang J. Zhang W. Lin Y. H. Yang J. Nan C. W. Complex electronic structure and compositing effect in high performance thermoelectric BiCuSeO. Nat. Commun. 2019;10:2814. doi: 10.1038/s41467-019-10476-7. [DOI] [PMC free article] [PubMed] [Google Scholar]
Li M. Islam S. M. K. N. Yahyaoglu M. Pan D. Shi X. Chen L. Aydemir U. Wang X. Ultrahigh figure-of-merit of Cu2Se incorporated with carbon coated boron nanoparticles. InfoMat. 2019;1:108–115. doi: 10.1002/inf2.12006. [DOI] [Google Scholar]
Liu M. Guo M. Lyu H. Lai Y. Zhu Y. Guo F. Yang Y. Yu K. Dong X. Liu Z. Cai W. Wuttig M. Yu Y. Sui J. Doping strategy in metavalently bonded materials for advancing thermoelectric performance. Nat. Commun. 2024;15:8286. doi: 10.1038/s41467-024-52645-3. [DOI] [PMC free article] [PubMed] [Google Scholar]
Luo H. Shi X. L. Liu Y. Li M. Zhang M. Luo X. Wang M. Huang X. Hu L. Chen Z. G. Metavalent alloying and vacancy engineering enable state-of-the-art cubic GeSe thermoelectrics. Nat. Commun. 2025;16:3136. doi: 10.1038/s41467-025-58387-0. [DOI] [PMC free article] [PubMed] [Google Scholar]
Shi H. Wen Y. Bai S. Chang C. Su L. Gao T. Liu S. Liu D. Qin B. Qin Y. Liang H. Qian X. Hou Z. Gao X. Zhou T. Tan Q. Zhao L. D. Crystal symmetry modification enables high-ranged in-plane thermoelectric performance in n-type SnSe crystals. Nat. Commun. 2025;16:1788. doi: 10.1038/s41467-025-57125-w. [DOI] [PMC free article] [PubMed] [Google Scholar]
Gao T. Wen Y. Bai S. Su L. Shi H. Liu R. Wang S. Hu Y. Liu S. Liu D. Liu S. Liang C. Feng X. Wang X. Qin Y. Gao X. Qin B. Chang C. Bai P. Zhao L. D. Extending the temperature range of the Cmcm phase of SnSe for high thermoelectric performance. Science. 2025;390:1266–1271. doi: 10.1126/science.adt0831. [DOI] [PubMed] [Google Scholar]
Pang K. Miao L. Zhang Q. Pan Q. Liu Y. Shi H. Li J. Zhou W. Zhang Z. Zhang Y. Wu G. Tan X. Noudem J. G. Wu J. Sun P. Hu H. Liu G. Q. Jiang J. Gradient Nanotwins and Enhanced Weighted Mobility Synergistically Upgrade Bi0.5Sb1.5Te3 Thermoelectric and Mechanical Performance. Adv. Funct. Mater. 2024;34:2315591. doi: 10.1002/adfm.202315591. [DOI] [Google Scholar]
Hu X. Jood P. Ohta M. Kunii M. Nagase K. Nishiate H. Kanatzidis M. G. Yamamoto A. Power Generation from Nanostructured PbTe-based Thermoelectrics: Comprehensive Development from Materials to Modules. Energy Environ. Sci. 2016;9:517–529. doi: 10.1039/C5EE02979A. [DOI] [Google Scholar]
Cheng J. Yin L. Wang X. Duan S. Zhao P. Ma X. Li X. Bao X. Zhi S. Mao J. Cao F. Zhang Q. Realizing a Superior Conversion Efficiency of approximately 11.3% in the Group IV-VI Thermoelectric Module. Small. 2024;20:e2312145. doi: 10.1002/smll.202312145. [DOI] [PubMed] [Google Scholar]
Xie L. Ming C. Song Q. Wang C. Liao J. Wang L. Zhu C. Xu F. Sun Y. Y. Bai S. Chen L. Lead-free and scalable GeTe-based thermoelectric module with an efficiency of 12% Sci. Adv. 2023;9:eadg7919. doi: 10.1126/sciadv.adg7919. [DOI] [PMC free article] [PubMed] [Google Scholar]
Shi W. Qin D. Sun Y. Wu H. Tong H. Xie L. Liu Z. Zhang Q. Cai W. Guo F. Sui J. Batch Fabrication and Interface Stabilization Accelerate Application of Skutterudite Thermoelectric Module for Power Generation. Adv. Energy Mater. 2024;14:2303698. doi: 10.1002/aenm.202303698. [DOI] [Google Scholar]
Xia J. Yang J. Wang Y. Jia B. Li S. Sun K. Zhao Q. Mao D. Li H. F. He J. Synergistic Entropy Engineering with Vacancies: Unraveling the Cocktail Effect for Extraordinary Thermoelectric Performance in SnTe-Based Materials. Adv. Funct. Mater. 2024;34:2401635. doi: 10.1002/adfm.202401635. [DOI] [Google Scholar]
Hu J. Sun Y. Shi W. Wu H. Zhu J. Cheng J. Jiao L. Jiang X. Xie L. Qu N. Li F. Yu Z. Zhang Q. Liu Z. Guo F. Cai W. Sui J. Realizing Ultrahigh Conversion Efficiency of approximately 9.0% in YbCd2Sb2/Mg3Sb2 Zintl Module for Thermoelectric Power Generation. Adv. Mater. 2024;36:e2411738. doi: 10.1002/adma.202411738. [DOI] [PubMed] [Google Scholar]
Deng Q. Zhang F. Yang X. Li R. Xia C. Nan P. Chen Y. Ge B. Ang R. He J. Ordered Grain Boundary Reconstruction Induces High-Efficiency Thermoelectric Power Generation in SnTe. Energy Environ. Sci. 2024;17:9467–9478. doi: 10.1039/D4EE04639K. [DOI] [Google Scholar]
Wan S. Song Q. Chen H. Zhang Q. Liao J. Xia X. Wang C. Qiu P. Chen B. Bai S. Chen L. High-efficiency segmented thermoelectric power generation modules constructed from all skutterudites. Cell Rep. Phys. Sci. 2023;4:101651. doi: 10.1016/j.xcrp.2023.101651. [DOI] [Google Scholar]
Wu X. Lin Y. Han Z. Li H. Liu C. Wang Y. Zhang P. Zhu K. Jiang F. Huang J. Fan H. Cheng F. Ge B. Liu W. Interface and Surface Engineering Realized High Efficiency of 13% and Improved Thermal Stability in Mg3Sb1.5Bi0.5-Based Thermoelectric Generation Devices. Adv. Energy Mater. 2022;12:2203039. doi: 10.1002/aenm.202203039. [DOI] [Google Scholar]
Liu R. Xing Y. Liao J. Xia X. Wang C. Zhu C. Xu F. Chen Z. G. Chen L. Huang J. Bai S. Thermal-inert and ohmic-contact interface for high performance half-Heusler based thermoelectric generator. Nat. Commun. 2022;13:7738. doi: 10.1038/s41467-022-35290-6. [DOI] [PMC free article] [PubMed] [Google Scholar]
Fu Y. Zhang Q. Hu Z. Jiang M. Huang A. Ai X. Wan S. Reith H. Wang L. Nielsch K. Jiang W. Mg3(Bi, Sb)2-based Thermoelectric Modules for Efficient and Reliable Waste-Heat Utilization up to 750 K. Energy Environ. Sci. 2022;15:3265–3274. doi: 10.1039/D2EE01038K. [DOI] [Google Scholar]
Liu D. Wang D. Hong T. Wang Z. Wang Y. Qin Y. Su L. Yang T. Gao X. Ge Z. Qin B. Zhao L.-D. Lattice Plainification Advances Highly Effective SnSe Crystalline Thermoelectrics. Science. 2023;380:841–846. doi: 10.1126/science.adg7196. [DOI] [PubMed] [Google Scholar]
Zhang Z. Ji R. Kroll M. Hofstetter Y. J. Jia X. Becker-Koch D. Paulus F. Löffler M. Nehm F. Leo K. Vaynzof Y. Efficient Thermally Evaporated γ-CsPbI3 Perovskite Solar Cells. Adv. Energy Mater. 2021;11(29):2100299. doi: 10.1002/aenm.202100299. [DOI] [Google Scholar]
Ji R. Zhang Z. Deconinck M. Hofstetter Y. J. Shi J. Paulus F. Raval P. Reddy G. N. M. Vaynzof Y. Spontaneous Formation of 1D/3D Perovskite Heterojunctions for Efficient Inverted Perovskite Solar Cells. Adv. Energy Mater. 2024;14(12):2304126. doi: 10.1002/aenm.202304126. [DOI] [Google Scholar]
Zhu T. Liu Y. Fu C. Heremans J. P. Snyder J. G. Zhao X. Compromise and Synergy in High-Efficiency Thermoelectric Materials. Adv. Mater. 2017;29(14):1605884. doi: 10.1002/adma.201605884. [DOI] [PubMed] [Google Scholar]
Snyder G. J. Snyder A. H. Figure of merit ZT of a thermoelectric device defined from materials properties. Energy Environ. Sci. 2017;10:2280–2283. doi: 10.1039/C7EE02007D. [DOI] [Google Scholar]
Liao Y. Chen J.-L. Liu C. Liang J. Zhou Q. Wang P. Miao L. Sintering Pressure as a “Scalpel” to Enhance the Ehermoelectric Performance of MgAgSb. J. Mater. Chem. C. 2022;10:3360–3367. doi: 10.1039/D1TC05617D. [DOI] [Google Scholar]
Guo K. Zhang X. Fan Z. Wang Y. Yang J. Zhu H. Chen J. Zhao Q. Li Z. Wang S. Zhang Q. Yao Y. He L. Zhao H. Rational manipulation of Ag vacancies for lattice plainification and superior thermoelectric performance in α-MgAgSb. Chem. Eng. J. 2025;507:160515. doi: 10.1016/j.cej.2025.160515. [DOI] [Google Scholar]
Xin J. Yang J. Li S. Basit A. Sun B. Li S. Long Q. Li X. Chen Y. Jiang Q. Thermoelectric Performance of Rapidly Microwave-Synthesized α-MgAgSb with SnTe Nanoinclusions. Chem. Mater. 2019;31:2421–2430. [Google Scholar]
Duparchy A. Millerand L. Camut J. Tumminello S. Kamila H. Deshpande R. Cowley A. Mueller E. de Boor J. Establishing Synthesis-Composition-Property Relationships for Enhanced and Reproducible Thermoelectric Properties of MgAgSb. J. Mater. Chem. A. 2022;10:21716–21726. doi: 10.1039/D2TA05936C. [DOI] [Google Scholar]
Rodriguez-Barber I. Camut J. Luhmann L. Cowley A. Mueller E. de Boor J. On the influence of AgMg precursor formation on MgAgSb microstructure and thermoelectric properties. J. Alloys Compd. 2021;860:158384. [Google Scholar]
Camut J. Barber Rodriguez I. Kamila H. Cowley A. Sottong R. Mueller E. de Boor J. Insight on the Interplay between Synthesis Conditions and Thermoelectric Properties of α-MgAgSb. Materials. 2019;12:1857. doi: 10.3390/ma12111857. [DOI] [PMC free article] [PubMed] [Google Scholar]
Back S. Y. Meikle S. Mori T. Comprehensive study of α-MgAgSb: Microstructure, carrier transport properties, and thermoelectric performance under ball milling techniques. J. Mater. Sci. Technol. 2025;227:57–66. [Google Scholar]
Qiu F. Chen J.-L. Liao Y. Zhang Z. Liang J. Miao L. Zhou Q. Peng Y. Liu C. Gao J. Realization of high cryogenic thermoelectric performance for MgAgSb base alloy by regulation heat-treatment process. Appl. Phys. Lett. 2024;124:173902. doi: 10.1063/5.0203816. [DOI] [Google Scholar]
Liu Z. Mao J. Sui J. Ren Z. High thermoelectric performance of α-MgAgSb for power generation. Energy Environ. Sci. 2018;11:23–44. doi: 10.1039/C7EE02504A. [DOI] [Google Scholar]
Ivanov A. A. Kaplar E. P. Prilepo Y. P. Murav’ev V. V. Ustinov V. S. Progress in the Research on Promising High-Performance Thermoelectric Materials. Nanobiotechnol. Rep. 2021;16:268–281. doi: 10.1134/S263516762103006X. [DOI] [Google Scholar]
Iqbal Y. Wang J. Wang C. Muhammad P. Zada A. Khan M. Maab H. Khan Q. Maqbool M. ThermoelectricMgAgSballoys for sustainable energy application. Int. J. Energy Res. 2022;46:22266–22284. doi: 10.1002/er.8600. [DOI] [Google Scholar]
Wang L. Yin L. Mao J. Zhang Q. Sui J. Liu Z. Half-Heusler compounds and devices for mid-high temperature thermoelectric applications. MRS Bull. 2025;50:945–955. [Google Scholar]
Zuo W. Chen H. Yu Z. Fu Y. Ai X. Cheng Y. Jiang M. Wan S. Fu Z. Liu R. Cheng G. Xu R. Wang L. Xu F. Zhang Q. Makarov D. Jiang W. Atomic-scale interface strengthening unlocks efficient and durable Mg-based thermoelectric devices. Nat. Mater. 2025;24:735–742. doi: 10.1038/s41563-025-02167-0. [DOI] [PubMed] [Google Scholar]
Li A. Wang L. Li J. Wu X. Mori T. Self-optimized contact in air-robust thermoelectric junction towards long-lasting heat harvesting. Nat. Commun. 2025;16:1502. doi: 10.1038/s41467-025-56861-3. [DOI] [PMC free article] [PubMed] [Google Scholar]
Chen S. Zhang T. Cheng J. Ma B. Ma X. Li X. Yin L. Wen L. Mao J. Cao F. Zhang Q. Unified contact layer and low-temperature transient liquid phase interconnection for high-performance all-Mg-based thermoelectric devices. Natl. Sci. Rev. 2025;12:nwaf227. doi: 10.1093/nsr/nwaf227. [DOI] [PMC free article] [PubMed] [Google Scholar]
Wu X. Lin Y. Liu C. Wang Y. Li H. Ge B. Liu W. A high performance eco-friendly MgAgSb-based thermoelectric power generation device near phase transition temperatures. Energy Environ. Sci. 2024;17:2879–2887. doi: 10.1039/D4EE00019F. [DOI] [Google Scholar]
Xie L. Yin L. Yu Y. Peng G. Song S. Ying P. Cai S. Sun Y. Shi W. Wu H. Qu N. Guo F. Cai W. Wu H. Zhang Q. Nielsch K. Ren Z. Liu Z. Sui J. Screening strategy for developing thermoelectric interface materials. Science. 2023;382:921–928. doi: 10.1126/science.adg8392. [DOI] [PubMed] [Google Scholar]
Kraemer D. Sui J. McEnaney K. Zhao H. Jie Q. Ren Z. F. Chen G. High Thermoelectric Conversion Efficiency of MgAgSb-Based Material with Hot-Pressed Contacts. Energy Environ. Sci. 2015;8:1299–1308. doi: 10.1039/C4EE02813A. [DOI] [Google Scholar]
Ying P. Villoro R. B. Bahrami A. Wilkens L. Reith H. Mattlat D. A. Pacheco V. Scheu C. Zhang S. Nielsch K. He R. Performance Degradation and Protective Effects of Atomic Layer Deposition for Mg-based Thermoelectric Modules. Adv. Funct. Mater. 2024;34:2406473. doi: 10.1002/adfm.202406473. [DOI] [Google Scholar]
Nowotny H. Sibert W. Ternäre Valenzverbindungen in den Systemen Kupfer(Silber)-Arsen(Antimon, Wismut)-Magnesium. Int. J. Mater. Res. 1941;33:391–394. [Google Scholar]
Mi J.-L. Ying P.-J. Sist M. Reardon H. Zhang P. Zhu T.-J. Zhao X.-B. Iversen B. B. Elaborating the Crystal Structures of MgAgSb Thermoelectric Compound: Polymorphs and Atomic Disorders. Chem. Mater. 2017;29:6378–6388. doi: 10.1021/acs.chemmater.7b01768. [DOI] [Google Scholar]
Kirkham M. J. dos Santos A. M. Rawn C. J. Lara-Curzio E. Sharp J. W. Thompson A. J. Ab Initio Determination of Crystal Structures of the Thermoelectric Material MgAgSb. Phys. Rev. B: Condens. Matter Mater. Phys. 2012;85:144120. doi: 10.1103/PhysRevB.85.144120. [DOI] [Google Scholar]
Huang Y. Lei J. Chen H. Zhou Z. Dong H. Yang S. Gao H. Wei T.-R. Zhao K. Shi X. Intrinsically high thermoelectric performance in near-room-temperature α-MgAgSb materials. Acta Mater. 2023;249:118847. doi: 10.1016/j.actamat.2023.118847. [DOI] [Google Scholar]
Ying P. Liu X. Fu C. Yue X. Xie H. Zhao X. Zhang W. Zhu T. High Performance α-MgAgSb Thermoelectric Materials for Low Temperature Power Generation. Chem. Mater. 2015;27:909–913. [Google Scholar]
Liu Z. Wang Y. Mao J. Geng H. Shuai J. Wang Y. He R. Cai W. Sui J. Ren Z. Lithium Doping to Enhance Thermoelectric Performance of MgAgSb with Weak Electron-Phonon Coupling. Adv. Energy Mater. 2016;6:1502269. doi: 10.1002/aenm.201502269. [DOI] [Google Scholar]
Ying P. Li X. Wang Y. Yang J. Fu C. Zhang W. Zhao X. Zhu T. Hierarchical Chemical Bonds Contributing to the Intrinsically Low Thermal Conductivity in α-MgAgSb Thermoelectric Materials. Adv. Funct. Mater. 2017;27:1604145. doi: 10.1002/adfm.201604145. [DOI] [Google Scholar]
Liu Z. Zhang Y. Mao J. Gao W. Wang Y. Shuai J. Cai W. Sui J. Ren Z. The Microscopic Origin of Low Thermal Conductivity for Enhanced Thermoelectric Performance of Yb Doped MgAgSb. Acta Mater. 2017;128:227–234. doi: 10.1016/j.actamat.2017.02.015. [DOI] [Google Scholar]
Li X. Liu P. F. Zhao E. Zhang Z. Guidi T. Le M. D. Avdeev M. Ikeda K. Otomo T. Kofu M. Nakajima K. Chen J. He L. Ren Y. Wang X. L. Wang B. T. Ren Z. Zhao H. Wang F. Ultralow thermal conductivity from transverse acoustic phonon suppression in distorted crystalline alpha-MgAgSb. Nat. Commun. 2020;11:942. doi: 10.1038/s41467-020-14772-5. [DOI] [PMC free article] [PubMed] [Google Scholar]
Zhao H. Sui J. Tang Z. Lan Y. Jie Q. Kraemer D. McEnaney K. Guloy A. Chen G. Ren Z. High Thermoelectric Performance of MgAgSb-Based Materials. Nano Energy. 2014;7:97–103. doi: 10.1016/j.nanoen.2014.04.012. [DOI] [Google Scholar]
Shuai J. Kim H. S. Lan Y. Chen S. Liu Y. Zhao H. Sui J. Ren Z. Study on Thermoelectric Performance by Na Doping in Nanostructured Mg1-xNaxAg0.97Sb0.99. Nano Energy. 2015;11:640–646. doi: 10.1016/j.nanoen.2014.11.027. [DOI] [Google Scholar]
Sui J. Shuai J. Lan Y. Liu Y. He R. Wang D. Jie Q. Ren Z. Effect of Cu Concentration on Thermoelectric Properties of Nanostructured p-type MgAg0.97−xCuxSb0.99. Acta Mater. 2015;87:266–272. doi: 10.1016/j.actamat.2015.01.018. [DOI] [Google Scholar]
Liu Z. Geng H. Mao J. Shuai J. He R. Wang C. Cai W. Sui J. Ren Z. Understanding and manipulating the intrinsic point defect in α-MgAgSb for higher thermoelectric performance. J. Mater. Chem. A. 2016;4:16834–16840. doi: 10.1039/C6TA06832D. [DOI] [Google Scholar]
Liu Z. Shuai J. Mao J. Wang Y. Wang Z. Cai W. Sui J. Ren Z. Effects of Antimony Content in MgAg0.97Sbx on Output Power and Energy Conversion Efficiency. Acta Mater. 2016;102:17–23. doi: 10.1016/j.actamat.2015.09.033. [DOI] [Google Scholar]
Liu Z. Gao W. Meng X. Li X. Mao J. Wang Y. Shuai J. Cai W. Ren Z. Sui J. Mechanical properties of nanostructured thermoelectric materials α-MgAgSb. Scr. Mater. 2017;127:72–75. [Google Scholar]
Liu Z. Wang Y. Gao W. Mao J. Geng H. Shuai J. Cai W. Sui J. Ren Z. The Influence of Doping Sites on Achieving Higher Thermoelectric Performance for Nanostructured α-MgAgSb. Nano Energy. 2017;31:194–200. doi: 10.1016/j.nanoen.2016.11.010. [DOI] [Google Scholar]
Liu Y. Zhou D. Z. Li Y. Q. Hong A. J. Sui J. H. Liu J. M. Ren Z. F. Unusual consequences of donor and acceptor doping on the thermoelectric properties of the MgAg0.97Sb0.99 alloy. J. Mater. Chem. A. 2018;6:2600–2611. doi: 10.1039/C7TA08657A. [DOI] [Google Scholar]
Li A. Wang L. Li J. Mori T. Global softening to manipulate sound velocity for reliable high-performance MgAgSb thermoelectrics. Energy Environ. Sci. 2024;17(22):8810–8819. [Google Scholar]
Feng Z. Zhang J. Yan Y. Zhang G. Wang C. Peng C. Ren F. Wang Y. Cheng Z. Ag-Mg antisite defect induced high thermoelectric performance of alpha-MgAgSb. Sci. Rep. 2017;7:2572. doi: 10.1038/s41598-017-02808-8. [DOI] [PMC free article] [PubMed] [Google Scholar]
Pang Z. Zhang X. Wang C. Investigation on native defects of α -MgAgSb and its effects on thermoelectric properties using first principles calculations. Curr. Appl. Phys. 2017;17:1279–1287. doi: 10.1016/j.cap.2017.06.010. [DOI] [Google Scholar]
Jiao L. Xie L. Zhu Y.-K. Wang L. Sun Y. Yu Y. Ivanova A. Khovaylo V. Guo F. Cai W. Sui J. Liu Z. Grain boundary segregation mediated highly stable and high performance nanostructured MgAgSb bulk thermoelectric materials. Trans. Mater. Res. 2025;1:100016. doi: 10.1016/j.tramat.2025.100016. [DOI] [Google Scholar]
Bu Z. Zhang X. Hu Y. Chen Z. Lin S. Li W. Xiao C. Pei Y. A Record Thermoelectric Efficiency in Tellurium-Free Modules for Low-Grade Waste Heat Recovery. Nat. Commun. 2022;13:237. doi: 10.1038/s41467-021-27916-y. [DOI] [PMC free article] [PubMed] [Google Scholar]
Bjørk R. The Universal Influence of Contact Resistance on the Efficiency of a Thermoelectric Generator. J. Electron. Mater. 2015;44:2869–2876. [Google Scholar]
Li Y. Shi Y. Luo D. Wang X. Yan Y. Impacts of distributed thermal and electric contact resistance on performance and geometric optimization of thermoelectric generators. Appl. Therm. Eng. 2024;246:122873. doi: 10.1016/j.applthermaleng.2024.122873. [DOI] [Google Scholar]
Rao Y. Xu C. Voss M. Ying P. Reith H. Nielsch K. Bechtold T. Hohlfeld D. Fabrication and Characterization of a Thermoelectric Generator with High Aspect Ratio Thermolegs for Electrically Active Implants. Adv. Mater. Technol. 2023;9:2301157. doi: 10.1002/admt.202301157. [DOI] [Google Scholar]
Xing T. Song Q. Qiu P. Zhang Q. Gu M. Xia X. Liao J. Shi X. Chen L. High efficiency GeTe-based materials and modules for thermoelectric power generation. Energy Environ. Sci. 2021;14:995–1003. doi: 10.1039/D0EE02791J. [DOI] [Google Scholar]
Chu J. Gu M. Liu R. Bai S. Shi X. Chen L. Interfacial behaviors of p-type CeyFexCo4–xSb12/Nb thermoelectric joints. Funct. Mater. Lett. 2020;13:2051020. [Google Scholar]
Gu M. Xia X. Li X. Huang X. Chen L. Microstructural evolution of the interfacial layer in the Ti–Al/Yb0.6Co4Sb12 thermoelectric joints at high temperature. J. Alloys Compd. 2014;610:665–670. [Google Scholar]
Zhao D. Li X. He L. Jiang W. Chen L. Interfacial evolution behavior and reliability evaluation of CoSb3/Ti/Mo–Cu thermoelectric joints during accelerated thermal aging. J. Alloys Compd. 2009;477:425–431. [Google Scholar]
Yin L. Li X. Bao X. Cheng J. Chen C. Zhang Z. Liu X. Cao F. Mao J. Zhang Q. CALPHAD accelerated design of advanced full-Zintl thermoelectric device. Nat. Commun. 2024;15:1468. doi: 10.1038/s41467-024-45869-w. [DOI] [PMC free article] [PubMed] [Google Scholar]
Li F. Li S. Wu H. Zhu Y.-K. Shi W. Bao X. Jin Y. Wang L. Dong X. Guo F. Cai W. Zhu J. Liu Z. Sui J. Phase penetration: key drivers in barrier layer failure of Hf-free Half-Heusler thermoelectric modules. Sci. China Mater. 2025:1–8. [Google Scholar]
Ying P. He R. Mao J. Zhang Q. Reith H. Sui J. Ren Z. Nielsch K. Schierning G. Towards Tellurium-free Thermoelectric Modules for Power Generation from Low-grade Heat. Nat. Commun. 2021;12:1121. doi: 10.1038/s41467-021-21391-1. [DOI] [PMC free article] [PubMed] [Google Scholar]
Liu Z. Sato N. Gao W. Yubuta K. Kawamoto N. Mitome M. Kurashima K. Owada Y. Nagase K. Lee C.-H. Yi J. Tsuchiya K. Mori T. Demonstration of Ultrahigh Thermoelectric Efficiency of ∼7.3% in Mg3Sb2/MgAgSb Module for Low-Temperature Energy Harvesting. Joule. 2021;5:1196–1208. [Google Scholar]
Gu M. Bai S. Wu J. Liao J. Xia X. Liu R. Chen L. A high-throughput strategy to screen interfacial diffusion barrier materials for thermoelectric modules. J. Mater. Res. 2019;34:1179–1187. doi: 10.1557/jmr.2019.12. [DOI] [Google Scholar]
Chetty R. Babu J. Mori T. Improving Thermoelectric Conversion Efficiency of Mg3(Sb, Bi)2-Based TE Materials via Interface Contact Layer Optimization. ACS Appl. Energy Mater. 2024;7:12112–12118. doi: 10.1021/acsaem.4c02794. [DOI] [Google Scholar]
Yang J. Li G. Zhu H. Chen N. Lu T. Gao J. Guo L. Xiang J. Sun P. Yao Y. Yang R. Zhao H. Next-Generation Thermoelectric Cooling Modules Based on High-Performance Mg3(Bi, Sb)2 Material. Joule. 2022;6:193–204. doi: 10.1016/j.joule.2021.11.008. [DOI] [Google Scholar]
Ying P. Reith H. Nielsch K. He R. Geometrical Optimization and Thermal-Stability Characterization of Te-Free Thermoelectric Modules Based on MgAgSb/Mg3(Bi, Sb)2. Small. 2022;18:e2201183. doi: 10.1002/smll.202201183. [DOI] [PubMed] [Google Scholar]
Xie L. Tong H. Peng G. Wu H. Shi W. Yu K. Hu J. Jiao L. Dong X. Guo F. Cai W. Zhang Y. Wu H. Liu Z. Sui J. Boosting carrier mobility in MgAgSb via in-situ InSb nanoprecipitates for high-efficiency segmented thermoelectric module. Nat. Commun. 2025;16:7484. doi: 10.1038/s41467-025-62902-8. [DOI] [PMC free article] [PubMed] [Google Scholar]
Chen J.-L. Liao Y. Zhou Q. Liang J. Miao L. Zhu Y. Wang S. He W. Nishiate H. Lee C.-H. Murata M. Lai H. Li Z. Realizing high conversion efficiency in shallow cryogenic thermoelectric module based on n-type BiSb and p-type MgAgSb materials. Mater. Today Phys. 2022;28:100855. [Google Scholar]
Wieder A. Camut J. Duparchy A. Deshpande R. Cowley A. Müller E. de Boor J. High-performance tellurium-free thermoelectric module for moderate temperatures using α-MgAgSb/Mg2(Si, Sn) Mater. Today Energy. 2023;38:101420. doi: 10.1016/j.mtener.2023.101420. [DOI] [Google Scholar]
Patra S. Patro P. Gupta P. Singh S. Singh A. Harvesting low grade waste heat through environment friendly n-Ag2Se/p-MgAgSb based thermoelectric module. Emergent Mater. 2025;8(5):3741–3752. doi: 10.1007/s42247-024-00841-8. [DOI] [Google Scholar]
Tian G. Shi W. Guo R. Guo R. Zhang W. Liu D. Xue C. Facile Y-type Micro Ag2Se/MgAgSb flexible thermoelectric device based on lift-off technology. Sci. Rep. 2024;14:28247. doi: 10.1038/s41598-024-78925-y. [DOI] [PMC free article] [PubMed] [Google Scholar]
Whiting C. E. Woerner D. F. The Graph Becomes the Dataset: Compiling Historical and Current RTG Data into One Place. Nucl. Technol. 2024:1–8. [Google Scholar]
Zhang Z. Ming C. Song Q. Wang L. Chen H. Liao J. Wang C. Chen L. Bai S. Grain boundary modulation improved thermal stability of high thermoelectric performance Mg3(Sb,Bi)2-based compounds. Acta Mater. 2025;287:120806. doi: 10.1016/j.actamat.2025.120806. [DOI] [Google Scholar]
Geng Y. Li Z. Lin Z. Liu Y. Lai Q. Wu X. Hu L. Liu F. Yu Y. Zhang C. Inhibiting Mg Diffusion and Evaporation by Forming Mg-Rich Reservoir at Grain Boundaries Improves the Thermal Stability of N-Type Mg3Sb2 Thermoelectrics. Small. 2024;20:e2305670. doi: 10.1002/smll.202305670. [DOI] [PubMed] [Google Scholar]
Wu X. Ma X. Yao H. Liang K. Zhao P. Hou S. Yin L. Yang H. Sui J. Lin X. Cao F. Zhang Q. Mao J. Revealing the Chemical Instability of Mg3Sb2-xBix-Based Thermoelectric Materials. ACS Appl. Mater. Interfaces. 2023;15:50216–50224. doi: 10.1021/acsami.3c12290. [DOI] [PubMed] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Data Availability Statement

No primary research results, software or code have been included and no new data were generated or analysed as part of this review.

[cit1] Snyder G. J. Toberer E. S. Complex Thermoelectric Materials. Nat. Mater. 2008;7:105–114. doi: 10.1038/nmat2090. [DOI] [PubMed] [Google Scholar]

[cit2] Jiang B. Yu Y. Cui J. Liu X. Xie L. Liao J. Zhang Q. Huang Y. Ning S. Jia B. Zhu B. Bai S. Chen L. Pennycook S. J. He J. High-Entropy-Stabilized Chalcogenides with High Thermoelectric Performance. Science. 2021;371:830–834. doi: 10.1126/science.abe1292. [DOI] [PubMed] [Google Scholar]

[cit3] He J. Tritt T. M. Advances in thermoelectric materials research: Looking back and moving forward. Science. 2017;357:eaak9997. doi: 10.1126/science.aak9997. [DOI] [PubMed] [Google Scholar]

[cit4] Shi X. L. Li N. H. Li M. Chen Z. G. Toward Efficient Thermoelectric Materials and Devices: Advances, Challenges, and Opportunities. Chem. Rev. 2025;125(16):7525–7724. doi: 10.1021/acs.chemrev.5c00060. [DOI] [PubMed] [Google Scholar]

[cit5] Shen K. Yang Q. Qiu P. Zhou Z. Yang S. Wei T. R. Shi X. Ductile P-Type AgCu(Se,S,Te) Thermoelectric Materials. Adv. Mater. 2024:e2407424. doi: 10.1002/adma.202407424. [DOI] [PubMed] [Google Scholar]

[cit6] Liu S. Qin Y. Wen Y. Shi H. Qin B. Hong T. Gao X. Cao Q. Chang C. Zhao L. D. Efforts Toward the Fabrication of Thermoelectric Cooling Module Based on N-Type and P-Type PbTe Ingots. Adv. Funct. Mater. 2024;34:2315707. doi: 10.1002/adfm.202315707. [DOI] [Google Scholar]

[cit7] Jiang F. Lin C. Cheng J. Yu H. Zhou Y. Ma X. Wu L. Ye S. Chen J. Zhi S. Xu Y. Zhao P. Wang X. Cao F. Zhang Q. Mao J. Prefer-Oriented Ag2Se Crystal for High-Performance Thermoelectric Cooling. Adv. Funct. Mater. 2024;35:2415000. doi: 10.1002/adfm.202415000. [DOI] [Google Scholar]

[cit8] Zhu Y. Yu Y. Zhang H. Qin Y. Wang Z.-Y. Zhan S. Liu D. Lin N. Tao Y. Hong T. Wang S. Ge Z.-H. Wuttig M. Zhao L.-D. Large Mobility Enables Higher Thermoelectric Cooling and Power Generation Performance in n-type AgPb18+xSbTe20 Crystals. J. Am. Chem. Soc. 2023;145:24931–24939. doi: 10.1021/jacs.3c09655. [DOI] [PubMed] [Google Scholar]

[cit9] He B. He Y. Wang W. Sun Y. Kong S. Huang J. Ru Y. Qin B. Ren H. He J. Zhao T. Li J. Lu J. Zhao L. D. Liu M. Strain-coupled, crystalline polymer-inorganic interfaces for efficient magnetoelectric sensing. Science. 2025;389:623–631. doi: 10.1126/science.adt2741. [DOI] [PubMed] [Google Scholar]

[cit10] Zhao K. Yue Z. Wuliji H. Chen H. Deng T. Lei J. Qiu P. Chen L. Shi X. Modeling critical thermoelectric transports driven by band broadening and phonon softening. Nat. Commun. 2024;15:776. doi: 10.1038/s41467-024-45093-6. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit11] Papapetrou M. Kosmadakis G. Cipollina A. La Commare U. Micale G. Industrial waste heat: Estimation of the technically available resource in the EU per industrial sector, temperature level and country. Appl. Therm. Eng. 2018;138:207–216. [Google Scholar]

[cit12] Photographic Periodic Table, Abundance in Earth's Crust of the elements, https://periodictable.com/Properties/A/CrustAbundance.an.html

[cit13] Zhang X. Zhu H. Dong X. Fan Z. Yao Y. Chen N. Yang J. Guo K. Hao J. He L. Li G. Zhao H. High-performance MgAgSb/Mg3(Sb,Bi)2-based thermoelectrics with η = 12% at T ≤ 583 K. Joule. 2024;8:3324–3335. [Google Scholar]

[cit14] Zhang X. Chen N. Guo K. Zhang Q. Zhao Q. Xu J. Zhu H. Zhao H. High cooling and power generation performance of α-MgAgSb with intrinsic low lattice thermal conductivity. Mater. Today Phys. 2024;44:101451. [Google Scholar]

[cit15] Xie L. Peng G. Sun Y. Liu Z. Li F. Zhu Y. Zhu J. Wu H. Qu N. Shi W. Jiao L. Guo F. Cai W. Wu H. Sui J. Semiconductor-Semimetal Composite Engineering Enabling Record-High Thermoelectric Power Density for Low-Temperature Energy Harvesting. Adv. Funct. Mater. 2024;34:2401763. doi: 10.1002/adfm.202401763. [DOI] [Google Scholar]

[cit16] Xie L. Yang J. Liu Z. Qu N. Dong X. Zhu J. Shi W. Wu H. Peng G. Guo F. Zhang Y. Cai W. Wu H. Zhu H. Zhao H. Liu Z. Sui J. Highly efficient thermoelectric cooling performance of ultrafine-grained and nanoporous materials. Mater. Today. 2023;65:5–13. doi: 10.1016/j.mattod.2023.03.021. [DOI] [Google Scholar]

[cit17] Li J. Li G. Chen Q. Feng J. Feng T. Xi L. Liu W. Zhang W. Liu R. Sun R. Manipulating Anti-Site Defects in α-MgAgSb for Thermoelectric Cooling Enhancement. Interdiscip. Mater. 2025;4(5):719–727. [Google Scholar]

[cit18] Ying P. Wilkens L. Reith H. Rodriguez N. P. Hong X. Lu Q. Hess C. Nielsch K. He R. A Robust Thermoelectric Module Based on MgAgSb/Mg3(Sb, Bi)2 with a Conversion Efficiency of 8.5% and A Maximum Cooling of 72 K. Energy Environ. Sci. 2022;15:2557–2566. doi: 10.1039/D2EE00883A. [DOI] [Google Scholar]

[cit19] Liu Z. Gao W. Oshima H. Nagase K. Lee C.-H. Mori T. Maximizing the Performance of N-type Mg3Bi2 Based Materials for Room-Temperature Power Generation and Thermoelectric Cooling. Nat. Commun. 2022;13:1120. doi: 10.1038/s41467-022-28798-4. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit20] Dong X. Jiao L. Tong H. Wu H. Liang H. Zhang X. Wang L. Wen Q. Liu M. Ge Z. Guo F. Luo D. Zhu Y.-K. Liu Z. Cai W. Sui J. Heavy doping driven ultra-low lattice thermal conductivity and mechanical enhancement in Mg3(Bi, Sb)2 for efficient power generation. Acta Mater. 2025;300:121451. doi: 10.1016/j.actamat.2025.121451. [DOI] [Google Scholar]

[cit21] Zhu G. Liu W. Lan Y. Joshi G. Wang H. Chen G. Ren Z. The effect of secondary phase on thermoelectric properties of Zn4Sb3 compound. Nano Energy. 2013;2:1172–1178. doi: 10.1016/j.nanoen.2013.04.010. [DOI] [Google Scholar]

[cit22] Wang M. Zhang Q. Pang K. Yuan M. Pan Q. Li R. Miao L. Tan X. Hu H. Wu J. Sun P. Liu G. Q. Jiang J. Robust Homogeneous Segmented Power Generator Driven by Sb2Te3-Based Thermoelectrics. Adv. Mater. 2025;37:e2503128. doi: 10.1002/adma.202503128. [DOI] [PubMed] [Google Scholar]

[cit23] Du J. Sun Y. Guo F. Tong H. Yu Z. Liu Z. Zhu J. Sui J. Enhanced Thermoelectric Cooling Performance of (Bi, Sb)2Te3 Through Platinum Doping. Mater. Today Phys. 2025;53:101705. doi: 10.1016/j.mtphys.2025.101705. [DOI] [Google Scholar]

[cit24] Hu J. Sun Y. Wu H. Yu Z. Zhu J. Guo F. Liu Z. Cai W. Sui J. All-Mg3Sb2-Based Module for Thermoelectric Power Generation. Adv. Funct. Mater. 2024;35:2418244. doi: 10.1002/adfm.202418244. [DOI] [PubMed] [Google Scholar]

[cit25] Naderloo R. H. Villoro R. B. Mattlat D. A. Ying P. Song S. Bayesteh S. Nielsch K. Scheu C. Ren Z. Zhu H. Zhang S. He R. Performance advancements in P-type TaFeSb-based thermoelectric materials through composition and composite optimizations. Energy Environ. Sci. 2025;18:738–749. doi: 10.1039/D4EE04819A. [DOI] [Google Scholar]

[cit26] Dharmaiah P. Heo M. Nagarjuna C. Jung S.-J. Won S. O. Lee K. H. Kim S. K. Kim J.-S. Ahn B. Kim H.-S. Baek S.-H. Enhancement of thermoelectric properties in p-type ZnSb alloys through Cu-doping. J. Alloys Compd. 2024;1004:175739. doi: 10.1016/j.jallcom.2024.175739. [DOI] [Google Scholar]

[cit27] Ai X. Xue W. Giebeler L. Pérez N. Lei B. Zhang Y. Zhang Q. Nielsch K. Wang Y. He R. Interstitial Defect Modulation Promotes Thermoelectric Properties of p-Type HfNiSn. Adv. Energy Mater. 2024;14:2401345. doi: 10.1002/aenm.202401345. [DOI] [Google Scholar]

[cit28] Zhu H. Li W. Nozariasbmarz A. Liu N. Zhang Y. Priya S. Poudel B. Half-Heusler alloys as emerging high power density thermoelectric cooling materials. Nat. Commun. 2023;14:3300. doi: 10.1038/s41467-023-38446-0. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit29] Ren G. K. Wang S. Zhou Z. Li X. Yang J. Zhang W. Lin Y. H. Yang J. Nan C. W. Complex electronic structure and compositing effect in high performance thermoelectric BiCuSeO. Nat. Commun. 2019;10:2814. doi: 10.1038/s41467-019-10476-7. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit30] Li M. Islam S. M. K. N. Yahyaoglu M. Pan D. Shi X. Chen L. Aydemir U. Wang X. Ultrahigh figure-of-merit of Cu2Se incorporated with carbon coated boron nanoparticles. InfoMat. 2019;1:108–115. doi: 10.1002/inf2.12006. [DOI] [Google Scholar]

[cit31] Liu M. Guo M. Lyu H. Lai Y. Zhu Y. Guo F. Yang Y. Yu K. Dong X. Liu Z. Cai W. Wuttig M. Yu Y. Sui J. Doping strategy in metavalently bonded materials for advancing thermoelectric performance. Nat. Commun. 2024;15:8286. doi: 10.1038/s41467-024-52645-3. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit32] Luo H. Shi X. L. Liu Y. Li M. Zhang M. Luo X. Wang M. Huang X. Hu L. Chen Z. G. Metavalent alloying and vacancy engineering enable state-of-the-art cubic GeSe thermoelectrics. Nat. Commun. 2025;16:3136. doi: 10.1038/s41467-025-58387-0. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit33] Shi H. Wen Y. Bai S. Chang C. Su L. Gao T. Liu S. Liu D. Qin B. Qin Y. Liang H. Qian X. Hou Z. Gao X. Zhou T. Tan Q. Zhao L. D. Crystal symmetry modification enables high-ranged in-plane thermoelectric performance in n-type SnSe crystals. Nat. Commun. 2025;16:1788. doi: 10.1038/s41467-025-57125-w. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit34] Gao T. Wen Y. Bai S. Su L. Shi H. Liu R. Wang S. Hu Y. Liu S. Liu D. Liu S. Liang C. Feng X. Wang X. Qin Y. Gao X. Qin B. Chang C. Bai P. Zhao L. D. Extending the temperature range of the Cmcm phase of SnSe for high thermoelectric performance. Science. 2025;390:1266–1271. doi: 10.1126/science.adt0831. [DOI] [PubMed] [Google Scholar]

[cit35] Pang K. Miao L. Zhang Q. Pan Q. Liu Y. Shi H. Li J. Zhou W. Zhang Z. Zhang Y. Wu G. Tan X. Noudem J. G. Wu J. Sun P. Hu H. Liu G. Q. Jiang J. Gradient Nanotwins and Enhanced Weighted Mobility Synergistically Upgrade Bi0.5Sb1.5Te3 Thermoelectric and Mechanical Performance. Adv. Funct. Mater. 2024;34:2315591. doi: 10.1002/adfm.202315591. [DOI] [Google Scholar]

[cit36] Hu X. Jood P. Ohta M. Kunii M. Nagase K. Nishiate H. Kanatzidis M. G. Yamamoto A. Power Generation from Nanostructured PbTe-based Thermoelectrics: Comprehensive Development from Materials to Modules. Energy Environ. Sci. 2016;9:517–529. doi: 10.1039/C5EE02979A. [DOI] [Google Scholar]

[cit37] Cheng J. Yin L. Wang X. Duan S. Zhao P. Ma X. Li X. Bao X. Zhi S. Mao J. Cao F. Zhang Q. Realizing a Superior Conversion Efficiency of approximately 11.3% in the Group IV-VI Thermoelectric Module. Small. 2024;20:e2312145. doi: 10.1002/smll.202312145. [DOI] [PubMed] [Google Scholar]

[cit38] Xie L. Ming C. Song Q. Wang C. Liao J. Wang L. Zhu C. Xu F. Sun Y. Y. Bai S. Chen L. Lead-free and scalable GeTe-based thermoelectric module with an efficiency of 12% Sci. Adv. 2023;9:eadg7919. doi: 10.1126/sciadv.adg7919. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit39] Shi W. Qin D. Sun Y. Wu H. Tong H. Xie L. Liu Z. Zhang Q. Cai W. Guo F. Sui J. Batch Fabrication and Interface Stabilization Accelerate Application of Skutterudite Thermoelectric Module for Power Generation. Adv. Energy Mater. 2024;14:2303698. doi: 10.1002/aenm.202303698. [DOI] [Google Scholar]

[cit40] Xia J. Yang J. Wang Y. Jia B. Li S. Sun K. Zhao Q. Mao D. Li H. F. He J. Synergistic Entropy Engineering with Vacancies: Unraveling the Cocktail Effect for Extraordinary Thermoelectric Performance in SnTe-Based Materials. Adv. Funct. Mater. 2024;34:2401635. doi: 10.1002/adfm.202401635. [DOI] [Google Scholar]

[cit41] Hu J. Sun Y. Shi W. Wu H. Zhu J. Cheng J. Jiao L. Jiang X. Xie L. Qu N. Li F. Yu Z. Zhang Q. Liu Z. Guo F. Cai W. Sui J. Realizing Ultrahigh Conversion Efficiency of approximately 9.0% in YbCd2Sb2/Mg3Sb2 Zintl Module for Thermoelectric Power Generation. Adv. Mater. 2024;36:e2411738. doi: 10.1002/adma.202411738. [DOI] [PubMed] [Google Scholar]

[cit42] Deng Q. Zhang F. Yang X. Li R. Xia C. Nan P. Chen Y. Ge B. Ang R. He J. Ordered Grain Boundary Reconstruction Induces High-Efficiency Thermoelectric Power Generation in SnTe. Energy Environ. Sci. 2024;17:9467–9478. doi: 10.1039/D4EE04639K. [DOI] [Google Scholar]

[cit43] Wan S. Song Q. Chen H. Zhang Q. Liao J. Xia X. Wang C. Qiu P. Chen B. Bai S. Chen L. High-efficiency segmented thermoelectric power generation modules constructed from all skutterudites. Cell Rep. Phys. Sci. 2023;4:101651. doi: 10.1016/j.xcrp.2023.101651. [DOI] [Google Scholar]

[cit44] Wu X. Lin Y. Han Z. Li H. Liu C. Wang Y. Zhang P. Zhu K. Jiang F. Huang J. Fan H. Cheng F. Ge B. Liu W. Interface and Surface Engineering Realized High Efficiency of 13% and Improved Thermal Stability in Mg3Sb1.5Bi0.5-Based Thermoelectric Generation Devices. Adv. Energy Mater. 2022;12:2203039. doi: 10.1002/aenm.202203039. [DOI] [Google Scholar]

[cit45] Liu R. Xing Y. Liao J. Xia X. Wang C. Zhu C. Xu F. Chen Z. G. Chen L. Huang J. Bai S. Thermal-inert and ohmic-contact interface for high performance half-Heusler based thermoelectric generator. Nat. Commun. 2022;13:7738. doi: 10.1038/s41467-022-35290-6. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit46] Fu Y. Zhang Q. Hu Z. Jiang M. Huang A. Ai X. Wan S. Reith H. Wang L. Nielsch K. Jiang W. Mg3(Bi, Sb)2-based Thermoelectric Modules for Efficient and Reliable Waste-Heat Utilization up to 750 K. Energy Environ. Sci. 2022;15:3265–3274. doi: 10.1039/D2EE01038K. [DOI] [Google Scholar]

[cit47] Liu D. Wang D. Hong T. Wang Z. Wang Y. Qin Y. Su L. Yang T. Gao X. Ge Z. Qin B. Zhao L.-D. Lattice Plainification Advances Highly Effective SnSe Crystalline Thermoelectrics. Science. 2023;380:841–846. doi: 10.1126/science.adg7196. [DOI] [PubMed] [Google Scholar]

[cit48] Zhang Z. Ji R. Kroll M. Hofstetter Y. J. Jia X. Becker-Koch D. Paulus F. Löffler M. Nehm F. Leo K. Vaynzof Y. Efficient Thermally Evaporated γ-CsPbI3 Perovskite Solar Cells. Adv. Energy Mater. 2021;11(29):2100299. doi: 10.1002/aenm.202100299. [DOI] [Google Scholar]

[cit49] Ji R. Zhang Z. Deconinck M. Hofstetter Y. J. Shi J. Paulus F. Raval P. Reddy G. N. M. Vaynzof Y. Spontaneous Formation of 1D/3D Perovskite Heterojunctions for Efficient Inverted Perovskite Solar Cells. Adv. Energy Mater. 2024;14(12):2304126. doi: 10.1002/aenm.202304126. [DOI] [Google Scholar]

[cit50] Zhu T. Liu Y. Fu C. Heremans J. P. Snyder J. G. Zhao X. Compromise and Synergy in High-Efficiency Thermoelectric Materials. Adv. Mater. 2017;29(14):1605884. doi: 10.1002/adma.201605884. [DOI] [PubMed] [Google Scholar]

[cit51] Snyder G. J. Snyder A. H. Figure of merit ZT of a thermoelectric device defined from materials properties. Energy Environ. Sci. 2017;10:2280–2283. doi: 10.1039/C7EE02007D. [DOI] [Google Scholar]

[cit52] Liao Y. Chen J.-L. Liu C. Liang J. Zhou Q. Wang P. Miao L. Sintering Pressure as a “Scalpel” to Enhance the Ehermoelectric Performance of MgAgSb. J. Mater. Chem. C. 2022;10:3360–3367. doi: 10.1039/D1TC05617D. [DOI] [Google Scholar]

[cit53] Guo K. Zhang X. Fan Z. Wang Y. Yang J. Zhu H. Chen J. Zhao Q. Li Z. Wang S. Zhang Q. Yao Y. He L. Zhao H. Rational manipulation of Ag vacancies for lattice plainification and superior thermoelectric performance in α-MgAgSb. Chem. Eng. J. 2025;507:160515. doi: 10.1016/j.cej.2025.160515. [DOI] [Google Scholar]

[cit54] Xin J. Yang J. Li S. Basit A. Sun B. Li S. Long Q. Li X. Chen Y. Jiang Q. Thermoelectric Performance of Rapidly Microwave-Synthesized α-MgAgSb with SnTe Nanoinclusions. Chem. Mater. 2019;31:2421–2430. [Google Scholar]

[cit55] Duparchy A. Millerand L. Camut J. Tumminello S. Kamila H. Deshpande R. Cowley A. Mueller E. de Boor J. Establishing Synthesis-Composition-Property Relationships for Enhanced and Reproducible Thermoelectric Properties of MgAgSb. J. Mater. Chem. A. 2022;10:21716–21726. doi: 10.1039/D2TA05936C. [DOI] [Google Scholar]

[cit56] Rodriguez-Barber I. Camut J. Luhmann L. Cowley A. Mueller E. de Boor J. On the influence of AgMg precursor formation on MgAgSb microstructure and thermoelectric properties. J. Alloys Compd. 2021;860:158384. [Google Scholar]

[cit57] Camut J. Barber Rodriguez I. Kamila H. Cowley A. Sottong R. Mueller E. de Boor J. Insight on the Interplay between Synthesis Conditions and Thermoelectric Properties of α-MgAgSb. Materials. 2019;12:1857. doi: 10.3390/ma12111857. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit58] Back S. Y. Meikle S. Mori T. Comprehensive study of α-MgAgSb: Microstructure, carrier transport properties, and thermoelectric performance under ball milling techniques. J. Mater. Sci. Technol. 2025;227:57–66. [Google Scholar]

[cit59] Qiu F. Chen J.-L. Liao Y. Zhang Z. Liang J. Miao L. Zhou Q. Peng Y. Liu C. Gao J. Realization of high cryogenic thermoelectric performance for MgAgSb base alloy by regulation heat-treatment process. Appl. Phys. Lett. 2024;124:173902. doi: 10.1063/5.0203816. [DOI] [Google Scholar]

[cit60] Liu Z. Mao J. Sui J. Ren Z. High thermoelectric performance of α-MgAgSb for power generation. Energy Environ. Sci. 2018;11:23–44. doi: 10.1039/C7EE02504A. [DOI] [Google Scholar]

[cit61] Ivanov A. A. Kaplar E. P. Prilepo Y. P. Murav’ev V. V. Ustinov V. S. Progress in the Research on Promising High-Performance Thermoelectric Materials. Nanobiotechnol. Rep. 2021;16:268–281. doi: 10.1134/S263516762103006X. [DOI] [Google Scholar]

[cit62] Iqbal Y. Wang J. Wang C. Muhammad P. Zada A. Khan M. Maab H. Khan Q. Maqbool M. ThermoelectricMgAgSballoys for sustainable energy application. Int. J. Energy Res. 2022;46:22266–22284. doi: 10.1002/er.8600. [DOI] [Google Scholar]

[cit63] Wang L. Yin L. Mao J. Zhang Q. Sui J. Liu Z. Half-Heusler compounds and devices for mid-high temperature thermoelectric applications. MRS Bull. 2025;50:945–955. [Google Scholar]

[cit64] Zuo W. Chen H. Yu Z. Fu Y. Ai X. Cheng Y. Jiang M. Wan S. Fu Z. Liu R. Cheng G. Xu R. Wang L. Xu F. Zhang Q. Makarov D. Jiang W. Atomic-scale interface strengthening unlocks efficient and durable Mg-based thermoelectric devices. Nat. Mater. 2025;24:735–742. doi: 10.1038/s41563-025-02167-0. [DOI] [PubMed] [Google Scholar]

[cit65] Li A. Wang L. Li J. Wu X. Mori T. Self-optimized contact in air-robust thermoelectric junction towards long-lasting heat harvesting. Nat. Commun. 2025;16:1502. doi: 10.1038/s41467-025-56861-3. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit66] Chen S. Zhang T. Cheng J. Ma B. Ma X. Li X. Yin L. Wen L. Mao J. Cao F. Zhang Q. Unified contact layer and low-temperature transient liquid phase interconnection for high-performance all-Mg-based thermoelectric devices. Natl. Sci. Rev. 2025;12:nwaf227. doi: 10.1093/nsr/nwaf227. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit67] Wu X. Lin Y. Liu C. Wang Y. Li H. Ge B. Liu W. A high performance eco-friendly MgAgSb-based thermoelectric power generation device near phase transition temperatures. Energy Environ. Sci. 2024;17:2879–2887. doi: 10.1039/D4EE00019F. [DOI] [Google Scholar]

[cit68] Xie L. Yin L. Yu Y. Peng G. Song S. Ying P. Cai S. Sun Y. Shi W. Wu H. Qu N. Guo F. Cai W. Wu H. Zhang Q. Nielsch K. Ren Z. Liu Z. Sui J. Screening strategy for developing thermoelectric interface materials. Science. 2023;382:921–928. doi: 10.1126/science.adg8392. [DOI] [PubMed] [Google Scholar]

[cit69] Kraemer D. Sui J. McEnaney K. Zhao H. Jie Q. Ren Z. F. Chen G. High Thermoelectric Conversion Efficiency of MgAgSb-Based Material with Hot-Pressed Contacts. Energy Environ. Sci. 2015;8:1299–1308. doi: 10.1039/C4EE02813A. [DOI] [Google Scholar]

[cit70] Ying P. Villoro R. B. Bahrami A. Wilkens L. Reith H. Mattlat D. A. Pacheco V. Scheu C. Zhang S. Nielsch K. He R. Performance Degradation and Protective Effects of Atomic Layer Deposition for Mg-based Thermoelectric Modules. Adv. Funct. Mater. 2024;34:2406473. doi: 10.1002/adfm.202406473. [DOI] [Google Scholar]

[cit71] Nowotny H. Sibert W. Ternäre Valenzverbindungen in den Systemen Kupfer(Silber)-Arsen(Antimon, Wismut)-Magnesium. Int. J. Mater. Res. 1941;33:391–394. [Google Scholar]

[cit72] Mi J.-L. Ying P.-J. Sist M. Reardon H. Zhang P. Zhu T.-J. Zhao X.-B. Iversen B. B. Elaborating the Crystal Structures of MgAgSb Thermoelectric Compound: Polymorphs and Atomic Disorders. Chem. Mater. 2017;29:6378–6388. doi: 10.1021/acs.chemmater.7b01768. [DOI] [Google Scholar]

[cit73] Kirkham M. J. dos Santos A. M. Rawn C. J. Lara-Curzio E. Sharp J. W. Thompson A. J. Ab Initio Determination of Crystal Structures of the Thermoelectric Material MgAgSb. Phys. Rev. B: Condens. Matter Mater. Phys. 2012;85:144120. doi: 10.1103/PhysRevB.85.144120. [DOI] [Google Scholar]

[cit74] Huang Y. Lei J. Chen H. Zhou Z. Dong H. Yang S. Gao H. Wei T.-R. Zhao K. Shi X. Intrinsically high thermoelectric performance in near-room-temperature α-MgAgSb materials. Acta Mater. 2023;249:118847. doi: 10.1016/j.actamat.2023.118847. [DOI] [Google Scholar]

[cit75] Ying P. Liu X. Fu C. Yue X. Xie H. Zhao X. Zhang W. Zhu T. High Performance α-MgAgSb Thermoelectric Materials for Low Temperature Power Generation. Chem. Mater. 2015;27:909–913. [Google Scholar]

[cit76] Liu Z. Wang Y. Mao J. Geng H. Shuai J. Wang Y. He R. Cai W. Sui J. Ren Z. Lithium Doping to Enhance Thermoelectric Performance of MgAgSb with Weak Electron-Phonon Coupling. Adv. Energy Mater. 2016;6:1502269. doi: 10.1002/aenm.201502269. [DOI] [Google Scholar]

[cit77] Ying P. Li X. Wang Y. Yang J. Fu C. Zhang W. Zhao X. Zhu T. Hierarchical Chemical Bonds Contributing to the Intrinsically Low Thermal Conductivity in α-MgAgSb Thermoelectric Materials. Adv. Funct. Mater. 2017;27:1604145. doi: 10.1002/adfm.201604145. [DOI] [Google Scholar]

[cit78] Liu Z. Zhang Y. Mao J. Gao W. Wang Y. Shuai J. Cai W. Sui J. Ren Z. The Microscopic Origin of Low Thermal Conductivity for Enhanced Thermoelectric Performance of Yb Doped MgAgSb. Acta Mater. 2017;128:227–234. doi: 10.1016/j.actamat.2017.02.015. [DOI] [Google Scholar]

[cit79] Li X. Liu P. F. Zhao E. Zhang Z. Guidi T. Le M. D. Avdeev M. Ikeda K. Otomo T. Kofu M. Nakajima K. Chen J. He L. Ren Y. Wang X. L. Wang B. T. Ren Z. Zhao H. Wang F. Ultralow thermal conductivity from transverse acoustic phonon suppression in distorted crystalline alpha-MgAgSb. Nat. Commun. 2020;11:942. doi: 10.1038/s41467-020-14772-5. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit80] Zhao H. Sui J. Tang Z. Lan Y. Jie Q. Kraemer D. McEnaney K. Guloy A. Chen G. Ren Z. High Thermoelectric Performance of MgAgSb-Based Materials. Nano Energy. 2014;7:97–103. doi: 10.1016/j.nanoen.2014.04.012. [DOI] [Google Scholar]

[cit81] Shuai J. Kim H. S. Lan Y. Chen S. Liu Y. Zhao H. Sui J. Ren Z. Study on Thermoelectric Performance by Na Doping in Nanostructured Mg1-xNaxAg0.97Sb0.99. Nano Energy. 2015;11:640–646. doi: 10.1016/j.nanoen.2014.11.027. [DOI] [Google Scholar]

[cit82] Sui J. Shuai J. Lan Y. Liu Y. He R. Wang D. Jie Q. Ren Z. Effect of Cu Concentration on Thermoelectric Properties of Nanostructured p-type MgAg0.97−xCuxSb0.99. Acta Mater. 2015;87:266–272. doi: 10.1016/j.actamat.2015.01.018. [DOI] [Google Scholar]

[cit83] Liu Z. Geng H. Mao J. Shuai J. He R. Wang C. Cai W. Sui J. Ren Z. Understanding and manipulating the intrinsic point defect in α-MgAgSb for higher thermoelectric performance. J. Mater. Chem. A. 2016;4:16834–16840. doi: 10.1039/C6TA06832D. [DOI] [Google Scholar]

[cit84] Liu Z. Shuai J. Mao J. Wang Y. Wang Z. Cai W. Sui J. Ren Z. Effects of Antimony Content in MgAg0.97Sbx on Output Power and Energy Conversion Efficiency. Acta Mater. 2016;102:17–23. doi: 10.1016/j.actamat.2015.09.033. [DOI] [Google Scholar]

[cit85] Liu Z. Gao W. Meng X. Li X. Mao J. Wang Y. Shuai J. Cai W. Ren Z. Sui J. Mechanical properties of nanostructured thermoelectric materials α-MgAgSb. Scr. Mater. 2017;127:72–75. [Google Scholar]

[cit86] Liu Z. Wang Y. Gao W. Mao J. Geng H. Shuai J. Cai W. Sui J. Ren Z. The Influence of Doping Sites on Achieving Higher Thermoelectric Performance for Nanostructured α-MgAgSb. Nano Energy. 2017;31:194–200. doi: 10.1016/j.nanoen.2016.11.010. [DOI] [Google Scholar]

[cit87] Liu Y. Zhou D. Z. Li Y. Q. Hong A. J. Sui J. H. Liu J. M. Ren Z. F. Unusual consequences of donor and acceptor doping on the thermoelectric properties of the MgAg0.97Sb0.99 alloy. J. Mater. Chem. A. 2018;6:2600–2611. doi: 10.1039/C7TA08657A. [DOI] [Google Scholar]

[cit88] Li A. Wang L. Li J. Mori T. Global softening to manipulate sound velocity for reliable high-performance MgAgSb thermoelectrics. Energy Environ. Sci. 2024;17(22):8810–8819. [Google Scholar]

[cit89] Feng Z. Zhang J. Yan Y. Zhang G. Wang C. Peng C. Ren F. Wang Y. Cheng Z. Ag-Mg antisite defect induced high thermoelectric performance of alpha-MgAgSb. Sci. Rep. 2017;7:2572. doi: 10.1038/s41598-017-02808-8. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit90] Pang Z. Zhang X. Wang C. Investigation on native defects of α -MgAgSb and its effects on thermoelectric properties using first principles calculations. Curr. Appl. Phys. 2017;17:1279–1287. doi: 10.1016/j.cap.2017.06.010. [DOI] [Google Scholar]

[cit91] Jiao L. Xie L. Zhu Y.-K. Wang L. Sun Y. Yu Y. Ivanova A. Khovaylo V. Guo F. Cai W. Sui J. Liu Z. Grain boundary segregation mediated highly stable and high performance nanostructured MgAgSb bulk thermoelectric materials. Trans. Mater. Res. 2025;1:100016. doi: 10.1016/j.tramat.2025.100016. [DOI] [Google Scholar]

[cit92] Bu Z. Zhang X. Hu Y. Chen Z. Lin S. Li W. Xiao C. Pei Y. A Record Thermoelectric Efficiency in Tellurium-Free Modules for Low-Grade Waste Heat Recovery. Nat. Commun. 2022;13:237. doi: 10.1038/s41467-021-27916-y. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit93] Bjørk R. The Universal Influence of Contact Resistance on the Efficiency of a Thermoelectric Generator. J. Electron. Mater. 2015;44:2869–2876. [Google Scholar]

[cit94] Li Y. Shi Y. Luo D. Wang X. Yan Y. Impacts of distributed thermal and electric contact resistance on performance and geometric optimization of thermoelectric generators. Appl. Therm. Eng. 2024;246:122873. doi: 10.1016/j.applthermaleng.2024.122873. [DOI] [Google Scholar]

[cit95] Rao Y. Xu C. Voss M. Ying P. Reith H. Nielsch K. Bechtold T. Hohlfeld D. Fabrication and Characterization of a Thermoelectric Generator with High Aspect Ratio Thermolegs for Electrically Active Implants. Adv. Mater. Technol. 2023;9:2301157. doi: 10.1002/admt.202301157. [DOI] [Google Scholar]

[cit96] Xing T. Song Q. Qiu P. Zhang Q. Gu M. Xia X. Liao J. Shi X. Chen L. High efficiency GeTe-based materials and modules for thermoelectric power generation. Energy Environ. Sci. 2021;14:995–1003. doi: 10.1039/D0EE02791J. [DOI] [Google Scholar]

[cit97] Chu J. Gu M. Liu R. Bai S. Shi X. Chen L. Interfacial behaviors of p-type CeyFexCo4–xSb12/Nb thermoelectric joints. Funct. Mater. Lett. 2020;13:2051020. [Google Scholar]

[cit98] Gu M. Xia X. Li X. Huang X. Chen L. Microstructural evolution of the interfacial layer in the Ti–Al/Yb0.6Co4Sb12 thermoelectric joints at high temperature. J. Alloys Compd. 2014;610:665–670. [Google Scholar]

[cit99] Zhao D. Li X. He L. Jiang W. Chen L. Interfacial evolution behavior and reliability evaluation of CoSb3/Ti/Mo–Cu thermoelectric joints during accelerated thermal aging. J. Alloys Compd. 2009;477:425–431. [Google Scholar]

[cit100] Yin L. Li X. Bao X. Cheng J. Chen C. Zhang Z. Liu X. Cao F. Mao J. Zhang Q. CALPHAD accelerated design of advanced full-Zintl thermoelectric device. Nat. Commun. 2024;15:1468. doi: 10.1038/s41467-024-45869-w. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit101] Li F. Li S. Wu H. Zhu Y.-K. Shi W. Bao X. Jin Y. Wang L. Dong X. Guo F. Cai W. Zhu J. Liu Z. Sui J. Phase penetration: key drivers in barrier layer failure of Hf-free Half-Heusler thermoelectric modules. Sci. China Mater. 2025:1–8. [Google Scholar]

[cit102] Ying P. He R. Mao J. Zhang Q. Reith H. Sui J. Ren Z. Nielsch K. Schierning G. Towards Tellurium-free Thermoelectric Modules for Power Generation from Low-grade Heat. Nat. Commun. 2021;12:1121. doi: 10.1038/s41467-021-21391-1. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit103] Liu Z. Sato N. Gao W. Yubuta K. Kawamoto N. Mitome M. Kurashima K. Owada Y. Nagase K. Lee C.-H. Yi J. Tsuchiya K. Mori T. Demonstration of Ultrahigh Thermoelectric Efficiency of ∼7.3% in Mg3Sb2/MgAgSb Module for Low-Temperature Energy Harvesting. Joule. 2021;5:1196–1208. [Google Scholar]

[cit104] Gu M. Bai S. Wu J. Liao J. Xia X. Liu R. Chen L. A high-throughput strategy to screen interfacial diffusion barrier materials for thermoelectric modules. J. Mater. Res. 2019;34:1179–1187. doi: 10.1557/jmr.2019.12. [DOI] [Google Scholar]

[cit105] Chetty R. Babu J. Mori T. Improving Thermoelectric Conversion Efficiency of Mg3(Sb, Bi)2-Based TE Materials via Interface Contact Layer Optimization. ACS Appl. Energy Mater. 2024;7:12112–12118. doi: 10.1021/acsaem.4c02794. [DOI] [Google Scholar]

[cit106] Yang J. Li G. Zhu H. Chen N. Lu T. Gao J. Guo L. Xiang J. Sun P. Yao Y. Yang R. Zhao H. Next-Generation Thermoelectric Cooling Modules Based on High-Performance Mg3(Bi, Sb)2 Material. Joule. 2022;6:193–204. doi: 10.1016/j.joule.2021.11.008. [DOI] [Google Scholar]

[cit107] Ying P. Reith H. Nielsch K. He R. Geometrical Optimization and Thermal-Stability Characterization of Te-Free Thermoelectric Modules Based on MgAgSb/Mg3(Bi, Sb)2. Small. 2022;18:e2201183. doi: 10.1002/smll.202201183. [DOI] [PubMed] [Google Scholar]

[cit108] Xie L. Tong H. Peng G. Wu H. Shi W. Yu K. Hu J. Jiao L. Dong X. Guo F. Cai W. Zhang Y. Wu H. Liu Z. Sui J. Boosting carrier mobility in MgAgSb via in-situ InSb nanoprecipitates for high-efficiency segmented thermoelectric module. Nat. Commun. 2025;16:7484. doi: 10.1038/s41467-025-62902-8. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit109] Chen J.-L. Liao Y. Zhou Q. Liang J. Miao L. Zhu Y. Wang S. He W. Nishiate H. Lee C.-H. Murata M. Lai H. Li Z. Realizing high conversion efficiency in shallow cryogenic thermoelectric module based on n-type BiSb and p-type MgAgSb materials. Mater. Today Phys. 2022;28:100855. [Google Scholar]

[cit110] Wieder A. Camut J. Duparchy A. Deshpande R. Cowley A. Müller E. de Boor J. High-performance tellurium-free thermoelectric module for moderate temperatures using α-MgAgSb/Mg2(Si, Sn) Mater. Today Energy. 2023;38:101420. doi: 10.1016/j.mtener.2023.101420. [DOI] [Google Scholar]

[cit111] Patra S. Patro P. Gupta P. Singh S. Singh A. Harvesting low grade waste heat through environment friendly n-Ag2Se/p-MgAgSb based thermoelectric module. Emergent Mater. 2025;8(5):3741–3752. doi: 10.1007/s42247-024-00841-8. [DOI] [Google Scholar]

[cit112] Tian G. Shi W. Guo R. Guo R. Zhang W. Liu D. Xue C. Facile Y-type Micro Ag2Se/MgAgSb flexible thermoelectric device based on lift-off technology. Sci. Rep. 2024;14:28247. doi: 10.1038/s41598-024-78925-y. [DOI] [PMC free article] [PubMed] [Google Scholar]

[cit113] Whiting C. E. Woerner D. F. The Graph Becomes the Dataset: Compiling Historical and Current RTG Data into One Place. Nucl. Technol. 2024:1–8. [Google Scholar]

[cit114] Zhang Z. Ming C. Song Q. Wang L. Chen H. Liao J. Wang C. Chen L. Bai S. Grain boundary modulation improved thermal stability of high thermoelectric performance Mg3(Sb,Bi)2-based compounds. Acta Mater. 2025;287:120806. doi: 10.1016/j.actamat.2025.120806. [DOI] [Google Scholar]

[cit115] Geng Y. Li Z. Lin Z. Liu Y. Lai Q. Wu X. Hu L. Liu F. Yu Y. Zhang C. Inhibiting Mg Diffusion and Evaporation by Forming Mg-Rich Reservoir at Grain Boundaries Improves the Thermal Stability of N-Type Mg3Sb2 Thermoelectrics. Small. 2024;20:e2305670. doi: 10.1002/smll.202305670. [DOI] [PubMed] [Google Scholar]

[cit116] Wu X. Ma X. Yao H. Liang K. Zhao P. Hou S. Yin L. Yang H. Sui J. Lin X. Cao F. Zhang Q. Mao J. Revealing the Chemical Instability of Mg3Sb2-xBix-Based Thermoelectric Materials. ACS Appl. Mater. Interfaces. 2023;15:50216–50224. doi: 10.1021/acsami.3c12290. [DOI] [PubMed] [Google Scholar]

PERMALINK

Advances in MgAgSb thermoelectrics: from materials to devices

Liangjun Xie

Ran He

Jiehe Sui

Kornelius Nielsch

Zihang Liu

Abstract

1. Introduction

2. Advances in thermoelectric performance optimization of MgAgSb

2.1. Understanding the structural complexity and phase evolution in MgAgSb

2.2. Synthesis strategies for enhancing thermoelectric properties

2.3. Defect engineering and composite strategy optimization

3. Progress in MgAgSb-based thermoelectric devices

3.1. Developed interface materials

Fig. 9. Evolution of interface resistivity of recently developed TEiMs of MgAgSb with aging time.64–68,105.

3.2. MgAgSb-based cooling devices

3.3. MgAgSb-based power generation devices

Fig. 12. Power generation performance of MgAgSb-based TE devices.13–15,18,19,64–68,70,102,103,107,109–111 (A and B) are the temperature difference dependence of maximum conversion efficiency and output power density, respectively.

3.4. Stability and reliability of MgAgSb devices

4. Summary and outlooks

Author contributions

Conflicts of interest

Acknowledgments

Biographies

Biography

Liangjun Xie.

Biography

Ran He.

Biography

Jiehe Sui.

Biography

Kornelius Nielsch.

Biography

Zihang Liu.

Data availability

References

Associated Data

Data Availability Statement

ACTIONS

PERMALINK

RESOURCES

Similar articles

Cited by other articles

Links to NCBI Databases

Fig. 9. Evolution of interface resistivity of recently developed TEiMs of MgAgSb with aging time.^64–68,105.

Fig. 12. Power generation performance of MgAgSb-based TE devices.^{13–15,18,19,64–68,70,102,103,107,109–111} (A and B) are the temperature difference dependence of maximum conversion efficiency and output power density, respectively.