. 2011 Mar 8;11:8. doi: 10.1186/1472-6831-11-8

Effect of nanoporous TiO2 coating and anodized Ca2+ modification of titanium surfaces on early microbial biofilm formation

Victoria Fröjd 1,3, Paula Linderbäck 4, Ann Wennerberg 1,3, Luis Chávez de Paz 2, Gunnel Svensäter 2, Julia R Davies 2,✉
PMCID: PMC3061963  PMID: 21385428

Abstract

Background

The soft tissue around dental implants forms a barrier between the oral environment and the peri-implant bone and a crucial factor for long-term success of therapy is development of a good abutment/soft-tissue seal. Sol-gel derived nanoporous TiO2 coatings have been shown to enhance soft-tissue attachment but their effect on adhesion and biofilm formation by oral bacteria is unknown.

Methods

We have investigated how the properties of surfaces that may be used on abutments: turned titanium, sol-gel nanoporous TiO2 coated surfaces and anodized Ca2+ modified surfaces, affect biofilm formation by two early colonizers of the oral cavity: Streptococcus sanguinis and Actinomyces naeslundii. The bacteria were detected using 16S rRNA fluorescence in situ hybridization together with confocal laser scanning microscopy.

Results

Interferometry and atomic force microscopy revealed all the surfaces to be smooth (Sa ≤ 0.22 μm). Incubation with a consortium of S. sanguinis and A. naeslundii showed no differences in adhesion between the surfaces over 2 hours. After 14 hours, the level of biofilm growth was low and again, no differences between the surfaces were seen. The presence of saliva increased the biofilm biovolume of S. sanguinis and A. naeslundii ten-fold compared to when saliva was absent and this was due to increased adhesion rather than biofilm growth.

Conclusions

Nano-topographical modification of smooth titanium surfaces had no effect on adhesion or early biofilm formation by S. sanguinis and A. naeslundii as compared to turned surfaces or those treated with anodic oxidation in the presence of Ca2+. The presence of saliva led to a significantly greater biofilm biovolume but no significant differences were seen between the test surfaces. These data thus suggest that modification with sol-gel derived nanoporous TiO2, which has been shown to improve osseointegration and soft-tissue healing in vivo, does not cause greater biofilm formation by the two oral commensal species tested than the other surfaces.

Background

Titanium dental implants are commonly used to replace lost teeth and much work has been focused on the optimization of the physico-chemical and mechanical properties of implant materials to improve their integration with host bone and soft-tissues. The soft tissue barrier around dental implants serves as a protective seal between the oral environment and the underlying peri-implant bone and one factor proposed to be of importance for the long-term therapeutic success of implant therapy is the development of a good abutment/soft-tissue seal [1]. Various surface modifications of implants, including micro-topographical and chemical surface alterations, have been investigated for their effects on tissue healing and recently, interest has turned to modifications on the nanometer level of resolution [2]. Nanofeatured surfaces are regarded as those with structures smaller than 100 nm in at least one dimension, and nanofeatures have been characterized on at least four commercially available implants [3]. Sol-gel derived nanoporous TiO2 coatings have been shown to enhance soft-tissue attachment in rat and dog models [4-6] and an experimental study in human indicated that a significantly greater proportion of oral mucosa was in contact with a nanoporous TiO2 surface than with an unmodified surfaces [7].

Surfaces in the oral cavity are rapidly covered with a pellicle of proteins and glycoproteins derived from saliva and gingival crevicular fluid as well as secreted microbial products [8]. The composition, as well as the configuration and density of the proteins in the pellicle, is largely dependent on the physical and chemical nature of the underlying surface and thus the properties of the surface influence bacterial adhesion though the pellicle. Numerous microorganisms in the planktonic phase will be transported to the surface but it is the properties of the conditioning film together with adherence properties of bacteria that determine which organisms attach and initiate biofilm formation. Biofilm formation on tooth surfaces is initiated by adhesion of early colonizers, such as S. sanguinis and A. naeslundii [9]. The initial colonizers promote the adhesion of secondary colonizers by co-aggregation and microbial interactions leading to maturation of the biofilm [10]. The microbiota of healthy implants is thought to be similar to that seen on tooth surfaces [11,12] and Streptococcus spp. and Actinomyces naeslundii have been identified as early colonizers on a range of implant material surfaces in vivo [13]. As is the case for dental plaque, the capacity for growth and metabolism are the ecological determinants of survival and persistence of oral bacteria on dental implant surfaces. Multiplication and metabolism of adhering micro-organisms ultimately results in the development of a structurally organized microbial community that is in a state of balance with the host [14]. Oral disease may occur when local environmental factors in the biofilm drive the selection and enrichment of putative pathogens belonging to the resident microbiota thus initiating an inflammatory response inducing progressive bone resorption at dental implants [15].

Roughened titanium abutment surfaces have been shown to increase plaque formation in vivo [16]. However in comparison, smooth abutment surfaces with surface roughness values of < 0.3 μ m do not promote biofilm formation in vivo to the same extent [17]. Smooth, turned (TU) titanium, nanoporous TiO2 coated (SG) and anodized Ca2+ modified (OC) surfaces have all been shown to be suitable for osseointegration as well as soft-tissue healing [7,18,19]. In this study, we show that there are no significant differences in early biofilm formation by S. sanguinis and A. naeslundii, on these three smooth surfaces. However, the presence of saliva led to development of a significantly greater biofilm biovolume by these two colonizers on all surfaces than when saliva was not present.

Methods

Preparation of titanium surfaces

Commercially pure turned titanium discs (grade 4), with a diameter of 8 mm and a central hole, were divided into four groups. The original turned discs served as controls (TU) and the other groups were each modified in one of three different ways: sol-gel treatment to create a nanoporous TiO2 coat (SG), heat-treated in a similar way to the sol-gel treated discs (HT), or anodically oxidized and calcium treated (OC).

For the sol-gel treatment (SG), discs were cleaned in a basic hydrogen peroxide solution (H2O; 30% H2O2, and 25% NH4OH in the ratio 5:1:1) at 85°C for five minutes. After extensive rinsing in distilled water, discs were dried in flowing N2. The sol was prepared by mixing solution 1 [10.22 g tetraisopropylorthotitanate, (Merck, Hohenbrunn, Germany) dissolved in 15 ml ethanol] with solution 2 [15 ml of ethanol, 170 μl H2O and 840 μl HNO3]. After mixing for one hour, 100 μl PEG 400 (Merck, Hohenbrunn, Germany) was added and the solution stirred vigorously. The clear sol was kept at room temperature during aging and the dip-coating process. Dip-coating was performed with using a computer-controlled stepper motor stage with a dipping speed of 30 mm/min, and the discs were sintered in an oven at 500°C (air) for 30 minutes. After heating the discs were ultrasonically cleaned in ethanol for four minutes and finally dried in flowing N2. The heat-treated surfaces (HT) which served as controls for the SG surfaces were sintered at 500°C (air) as described above. The anodically oxidized and calcium incorporated (OC) surfaces were prepared by anodic oxidation with an electrolyte consisting of sodium glycerophosphate hydrate (C3H6(OH)2PO4Na2 × H2O) and calcium acetate (Ca(CH3COO)2) [20,21].

Characterization of titanium surfaces

To investigate surface roughness on the micrometer level, three discs of each surface were investigated at ten sites using an optical interferometer (MicroXamTM, PhaseShift, Tucson, USA). Each measurement was performed over a 200 × 260 μm area. A high-pass Gaussian filter (50 × 50 μm) was used to separate roughness from errors of form and waviness [22]. The evaluation was performed with the Surfascan software and the images were produced using SPIP™ (Scanning Probe Image Processor, Image Metrology, Denmark). Three different three-dimensional parameters were used to characterize the surface: average height deviation [Sa(μm)], a spatial parameter - density of summits [Sds(1/μm2)] and a hybrid parameter including variation in height and spatial direction [Sdr (%)].

The topography of model silica surfaces, dip-coated as for the SG surfaces, was characterized using atomic force microscopy (AFM 3100, Nanoscope III, Digital Instruments). To characterize the topography on the nanometer level of resolution, the two-dimensional surface parameter, average height deviation [Ra (nm)], was applied. Thickness of the SG coating was measured with null ellipsometry at λ = 632 nm (Auto-El-III, Rudolph Research, USA). The assumed refractive index of TiO2 in anastase crystal structure was n = 2.49.

Bacterial strains and culture

For biofilm assays the oral type strain Streptococcus sanguinis ATCC 10556 and Actinomyces naeslundii isolated from dental plaque [23] were used. All strains were routinely maintained on blood agar or in Todd-Hewitt broth (TH) at 37°C in 5% CO2.

Assay for adhesion and early biofilm formation

Immediately prior to bacterial inoculation, discs were cleaned in an ultrasonic bath with Extran MA01® (Merck, Darmstadt, Germany) diluted 1:40 in distilled water, treated with ethanol, and placed in polystyrene 6-well (flat-bottomed) titer plates (MULTIWELL™, Becton Dickinson, Franklin Lakes, NJ, USA). Overnight broth cultures were diluted 1:50 in fresh, pre-warmed Todd Hewitt broth at 37°C in 5% CO2 and grown to the mid-exponential growth phase (OD600 nm≈0.6). Cultures were then diluted to give final concentrations of approximately 1 × 108 cells/ml for S. sanguinis and 1 × 107 cells/ml for A. naeslundii. 1.5 ml of S. sanguinis and 4.5 ml of A. naeslundii suspensions were then inoculated into the wells. The microtiter plate was sealed with paraffin tape and incubated at 37°C on a rotary shaker at 300 rpm in 5% CO2. Following incubation for 2 and 14 h, the surfaces were rinsed three times with 10 mM potassium phosphate buffer, pH 7.5 (PBS) to remove loosely bound cells. The adherent bacteria were fixed in 4% paraformaldehyde for 16S rRNA hybridization. All biofilm experiments were carried out using independent bacterial cultures three times for each surface type.

For the saliva experiments, unstimulated whole saliva was collected from a healthy volunteer with good oral health, centrifuged for 10 minutes to pellet mucins and bacteria, and the supernatant filter-sterilized (pore size 0.22 μm). Aliquots of bacterial suspensions (1.5 ml of S. sanguinis and 4.5 ml of A. naeslundii) were centrifuged and the pellet resuspended in 6 ml of the sterile saliva. Bacterial suspensions (containing 107 colony-forming-units per ml as shown by culturing) were then added to the wells. Plates were shaken gently for 14 hours at 37°C in an atmosphere of 5% CO2. After this time, surfaces were rinsed three times with 3 ml PBS, fixed with 4% paraformaldehyde and incubated overnight at 4°C.

16S rRNA FISH and confocal laser scanning microscopy

Fixed bacteria on the discs were washed with cold, sterile PBS and subjected to cell membrane permeabilization with 100 μl lysozyme (Sigma, St Louis, MO, USA) [(70 U μl-1) in 100 mM Tris-HCl, pH 7.5 (Sigma, St Louis, MO, USA) containing 5 mM EDTA (Merck, Damstadt, Germany)] for 9 minutes at 37°C. After rinsing with ultra-pure water, the bacteria were dehydrated through a series of ethanol washes. Hybridization buffer [0.9 M NaCl, 20 mM Tris-HCl buffer, pH 7.5, with 0.01% sodium dodecyl sulfate (SDS) and 25% formamide] containing 20 ng of labeled oligonucleotide probe ml-1 was pipetted onto the titanium discs. The probe cocktail consisted of the streptococcal probe STR493 (5'-GTTAGCCGTCCCTTTCTGG-3') [24], fluorescently labeled green with ATTO-488 to assess the amount of S. sanguinis, and a red-labeled ATTO-565 probe EUB338 (5'-GCTGCCTCCCGTAGGAGT-3') [25] to assess total biofilm volume. Hybridization was carried out at 47°C in a humid chamber for 90 minutes. The surfaces were washed three times with 20 mM Tris-HCl (pH 7.5) containing 5 mM EDTA and 0.01% sodium dodecyl sulfate, and twice with 159 mM NaCl, for 30 and 15 minutes, at 47°C under gentle shaking. Finally, the titanium surfaces were washed with ice-cold ultra-pure water, mounted and glued onto glass slides for analysis using inverted confocal scanning laser microscopy (CSLM) (Eclipse TE2000, Nikon Corporation, Tokyo, Japan). Green fluorescence was provided by an Ar laser (488 nm laser excitation) and red fluorescence was given by a G-HeNe laser (543 nm laser excitation). CLSM images were acquired with an oil immersion objective (×60). Each stack had a substratum coverage field area of 215 × 215 μm, and the z-step was 2 μm. Images were obtained from 15 randomly selected sites per disc.

Image analysis

The image stacks were converted into TIFF format and analyzed using the bioImage_L software [26] to calculate the structural parameters of the biofilm. S. sanguinis takes up both the universal probe EUB338 (red) (Figure 1a) and the streptococcus specific STR493 probe (green) (Figure 1b) and in the images presented these cells appear yellow due to co-localization of the probes (Figure 1c). A. naeslundii, which takes up only the EUB338 probe, appears red (Figure 1c). Since the software used could not identify yellow cells, the biovolume of S. sanguinis was quantified using the numbers of green cells. The biofilm biovolume of A. naeslundii was then calculated indirectly by subtracting the S. sanguinis (green) biofilm biovolume from the total.

Figure 1.

Figure 1

Open in a new tab

16S rRNA fluorescence in situ hybridization images of S. sanguinis and A. naeslundii in mono- and dual-species biofilms. CSLM images showing dual-species biofilms of S. sanguinis and A. naeslundii (a) stained with the red EUB338 16S rRNA FISH probe, (b) stained with the green STR493 16S rRNA FISH probe or (c) stained with both the probes. The bar shows 4 μm.

Statistical analysis

The non-parametric Mann-Whitney U test was used to analyze differences in biofilm biovolume between the test and control surfaces and p-values < 0.05 were considered significant.

Results and Discussion

Characterization of the titanium surfaces

Characterization of surface orientation by interferometry revealed that the nanoporous (SG) surface as well as the heat-treated (HT) and anodic oxidized Ca2+ incorporated (OC) surfaces were isotropic while the turned surface (TU) was anisotropic (with oriented surface topography) (Figure 2, left column). Measurements of surface parameters (Figure 2, right column), revealed that the nanoporous (SG) surface had an average surface height deviation (Sa) of 0.16 ± 0.04 μm while the developed surface area [27] and summit density (Sds) were 3 ± 1% and 0.13 ± 0.005 summits/μm2 respectively. This topography was similar to that of the heat-treated control (HT) (Sa 0.16 ± 0.02 μm, Sdr 3 ± 1%, Sds 0.12 ± 0.007 summits/μm2) and the turned (TU) (Sa 0.18 ± 0.02 μm, Sdr 4 ± 1%, Sds 0.13 ± 0.022 summits/μm2) surfaces. The anodic oxidized Ca2+ incorporated (OC) surface however, had higher values for average height deviation (0.22 ± 0.01 μm), developed surface area ratio (15 ± 2%), and summit density (0.23 ± 0.003 summits/μm2). Thus, the OC surface had somewhat greater microtopographical structures than the other surfaces investigated and had a greater potential surface area for bacterial interactions. However, despite the differences on the microscale level of roughness between the TU, SG and HT on the one hand and the OC surface on the other, all were categorized as smooth (i.e. Sa < 0.5 μ m) [28].

Figure 2.

Figure 2

Open in a new tab

Interferometry images and surface characteristics of the smooth titanium surfaces. Images from interferometry were produced with SPIP™. The average height deviation (Sa), density of summits (Sds) and surface enlargement (Sdr) are shown for the different surfaces; SG (sol-gel derived nanoporous TiO2 coated), HT (heat-treated), TU (turned) and OC (anodically oxidized Ca2+ incorporated) surfaces.

Atomic force microscopy surface imaging of sol-gel derived nanoporous TiO2 surfaces showed that the particles were well distributed and organized (Figure 3). The coating led to the formation of nanostructures of a few nanometers up to 100 nm with Ra 1.58 nm. The thickness of the nanoporous TiO2 coating, was 90 nm ± 10 nm as measured by ellipsometry.

Figure 3.

Figure 3

Open in a new tab

Characterization of the nanoporous TiO2 coated surface using atomic force microscopy. A representative AFM image of the nanoporous TiO2 coated surface. Note the homogeneous and evenly distributed nanofeatures.

Properties of smooth surfaces do not influence adhesion and early biofilm formation by S. sanguinis and A. naeslundii

The main objective of the present study was to investigate microbial adhesion to nanoporous TiO2 (SG) surfaces and compare this to other smooth titanium surfaces used for implant abutments. The model used is compatible with CLSM since the discs can be mounted on glass-slides and viewed directly in the microscope. The amount of bacteria on the surfaces after 2 hours of incubation was considered to represent the level of bacterial adhesion to the surface. After 2 hours, A. naeslundii and S. sanguinis were present on all surfaces as sparsely distributed cell clusters (Figure 3b - upper panel). The biofilm biovolume on the SG surface was similar to that on the HT control and the TU surface. The OC surface however, showed a slightly higher level of adhesion but this was not-significantly different from that on the other surfaces (p = 0.05) (Figure 4a). Thus it appears that the higher level of microscale roughness seen for the OC surface was not sufficient to protect the bacteria from removal forces. Similar results were obtained in an in vivo study where surfaces with a Sa = 0.21 μm showed somewhat greater levels of adhering microorganisms than those with a Sa in the range 0.05-0.13 μm [29] and an average roughness in height (Ra) of 0.2 μm has been proposed as a threshold for significant bacterial adhesion [17]. The proportion of A. naeslundii was greater than that of S. sanguinis on all surfaces (approximately 85% of the biofilm biovolume) suggesting that, under these conditions, A. naeslundii was better able to adhere than S. sanguinis.

Figure 4.

Figure 4

Open in a new tab

Biofilm formation by S. sanguinis and A. naeslundii over 2- and 14-hours on the smooth titanium surfaces. (a) Graphs showing the mean ± sd of biofilm volume generated from three independent sets of experiments. SG (sol-gel derived nanoporous TiO2 coated), HT (heat-treated), TU (turned) and OC (anodically oxidized and Ca2+ incorporated). No significant differences were seen between the surfaces at each time point. (b) Representative images from CSLM of 2- and 14-hour biofilms visualized with 16S rRNA FISH using oligonucleotide probes targeting S. sanguinis (STR493 - green) and all bacteria (EUB338 - red). Since both the red EUB338 and the green STR493 probe were taken up by S. sanguinis, the cells appear yellow whereas A. naeslundii which incorporates only the EUB338 probe appears red. The scale bars represent 10 μm.

After 14 hours in the presence of TH growth medium, the adhered bacteria have started to divide and grow and the levels of microbial coverage are thus considered to reflect the initial stages of biofilm formation. However, the levels of growth seen here between two and 14 hours were low and this may reflect the fact that on contact with a surface, planktonic bacteria undergo a transition from exponential growth to a much slower growth rate [30]. No differences in the levels of coverage between the different surfaces could be observed (Figure 4b, lower panel). In accordance with these observations, no differences in the overall biofilm biovolume between the four surfaces were detected. The relative proportion of S. sanguinis had increased to 31%, although the levels were still lower than those of A. naeslundii (69%). Thus, although the initial levels of adhesion were slightly higher on the OC surface, possibly due to the greater surface area, this was not sustained as the biofilm began to develop.

Saliva enhances adhesion of S. sanguinis and A. naeslundii in dual-species biofilms

To investigate if saliva affected surface adhesion, S. sanguinis and A. naeslundii were suspended in sterile saliva before exposure to the surfaces. This increased the adherence of both species to all surfaces after 2 hours (Figure 5b, upper panel). The bacteria were present as clusters, probably due to aggregation of cells covered with salivary proteins. The increase was up to 11-fold (Figure 5a) as compared to in the absence of saliva (Figure 4a) suggesting that saliva promoted the adhesion of these two species. In contrast, in previous studies pre-coating of titanium surfaces with experimental salivary pellicles was shown not to affect the adherence of A. naeslundii [31]. This difference may be attributed to the fact that in the study of Lima et al. 2008, bacteria were suspended in nutrient broth rather than saliva.

Figure 5.

Figure 5

Open in a new tab

Biofilm formation by S. sanguinis and A. naeslundii in the presence of saliva over 2- and 14-hours on the smooth titanium surfaces. (a) Graphs showing the mean ± sd of biofilm volume generated from three independent sets of experiments. SG (sol-gel derived nanoporous TiO2 coated), HT (heat-treated), TU (turned) and OC (anodically oxidized and Ca2+ incorporated). No significant differences were seen between the surfaces at each time point. (b) Representative images from CSLM of two- and 14-hour biofilms visualized with 16S rRNA FISH using oligonucleotide probes targeting Streptococcus sanguinis (STR493 - green) and all bacteria (EUB338 - red). Since both the red EUB338 and the green STR493 probe were taken up by S. sanguinis, the cells appear yellow whereas A. naeslundii which incorporates only the EUB338 probe appears red. The scale bars represent 25 μm.

After 14 hours no major change was seen in the biofilm biovolume indicating that no growth had occurred in the presence of saliva. However, these data are likely to underestimate biofilm formation and growth in vivo since in biofilms on dental implant surfaces recruitment of a range of other bacterial species would allow a concerted action to degrade salivary glycoproteins and thus provide nutrients for growth [32]. The different surfaces showed no differences in total biofilm biovolume (p < 0.05) and the proportion of the bacterial species was similar at both 2 and 14 hours, with A. naeslundii constituting about 80% of the biovolume.

The model used here enabled the different surfaces to be tested in the presence of saliva. The use of 16S rRNA FISH allows detection of interspecies variations in adhesion and growth as well as the spatial relationships between bacteria on various surfaces. In addition, the extensive rinsing during the 16S rRNA FISH procedure ensures that only truly adhered bacteria are present on the surface during quantification. One drawback of the model is that the gently shaking used here may not accurately reflect the shear forces present at a surface exposed in the oral cavity. However, this could be overcome through the use of a flow-chamber model [33].

Conclusions

Nano-topographical modification of smooth titanium surfaces did not cause significantly greater adhesion and biofilm formation by S. sanguinis and A. naeslundii in vitro than was found on turned surfaces or those treated with Ca2+ incorporation during anodic oxidation. In the presence of saliva, adhesion was increased more than ten-fold compared to in the absence of saliva and no differences were seen between the surfaces. These data suggest that modification with sol-gel derived nanoporous TiO2, which has been shown to improve soft-tissue healing in vivo, does not lead to greater adhesion and initial biofilm formation by the two commensal species tested than the other surfaces. However, it cannot be excluded that over a longer time period in the presence of other bacterial species, greater differences in biofilm formation on the different surfaces may be seen.

List of abbreviations

CLSM: confocal laser scanning micrscopy; PBS: 10 mM potassium phosphate buffer, pH 7.5; FISH: fluorescence in situ hybridization; TU: turned surfaces; OC: anodically oxidized Ca2+ incorporated surfaces; SG: sol-gel derived nanoporous TiO2 coated surfaces; HT: heat-treated surfaces.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

VF participated in planning the study, performed most of the laboratory work, and participated in the data analysis and drafting of the manuscript. PL prepared the sol-gel derived surfaces and participated in the drafting of the manuscript. AW participated in the study planning and the drafting of the manuscript. LCP participated in the experimental design and drafting of the manuscript. GS participated in study design, data analysis and drafting of the manuscript. JRD participated in data analysis and drafting of the manuscript. All authors have read and approved the final manuscript.

Pre-publication history

The pre-publication history for this paper can be accessed here:

http://www.biomedcentral.com/1472-6831/11/8/prepub

Contributor Information

Victoria Fröjd, Email: victoria.frojd@mah.se.

Paula Linderbäck, Email: palin@ifm.liu.se.

Ann Wennerberg, Email: ann.wennerberg@mah.se.

Luis Chávez de Paz, Email: luis.chavez.de.paz@mah.se.

Gunnel Svensäter, Email: gunnel.svensater@mah.se.

Julia R Davies, Email: julia.davies@mah.se.

Acknowledgements

This study was supported by The Swedish Dental Society, the Hjalmar Svensson Research Foundation, the Swedish Research Council (AW), and the Knowledge Foundation, Sweden.

References

  1. Abrahamsson I, Berglundh T, Glantz PO, Lindhe J. The mucosal attachment at different abutments. An experimental study in dogs. J Clin Periodontol. 1998;25:721–727. doi: 10.1111/j.1600-051X.1998.tb02513.x. [DOI] [PubMed] [Google Scholar]
  2. Mendonca G, Mendonca DB, Aragao FJ, Cooper LF. Advancing dental implant surface technology--from micron- to nanotopography. Biomaterials. 2008;29:3822–3835. doi: 10.1016/j.biomaterials.2008.05.012. [DOI] [PubMed] [Google Scholar]
  3. Wennerberg A, Albrektsson T. On implant surfaces: a review of current knowledge and opinions. Int J Oral Maxillofac Implants. 2010;25:63–74. [PubMed] [Google Scholar]
  4. Areva S, Paldan H, Peltola T, Narhi T, Jokinen M, Linden M. Use of sol-gel-derived titania coating for direct soft tissue attachment. J Biomed Mater Res A. 2004;70:169–178. doi: 10.1002/jbm.a.20120. [DOI] [PubMed] [Google Scholar]
  5. Paldan H, Areva S, Tirri T, Peltola T, Lindholm TC, Lassila L, Pelliniemi LJ, Happonen RP, Narhi TO. Soft tissue attachment on sol-gel-treated titanium implants in vivo. J Mater Sci Mater Med. 2008;19:1283–1290. doi: 10.1007/s10856-007-3234-z. [DOI] [PubMed] [Google Scholar]
  6. Rossi S, Tirri T, Paldan H, Kuntsi-Vaattovaara H, Tulamo R, Narhi T. Peri-implant tissue response to TiO2 surface modified implants. Clin Oral Implants Res. 2008;19:348–355. doi: 10.1111/j.1600-0501.2007.01478.x. [DOI] [PubMed] [Google Scholar]
  7. Wennerberg A, Frojd V, Olsson M, Nannmark U, Emanuelsson L, Johansson P, Josefsson Y, Kangasniemi I, Peltola T, Tirri T, Nanoporous TiO(3) Thin Film on Titanium Oral Implants for Enhanced Human Soft Tissue Adhesion: A Light and Electron Microscopy Study. Clin Implant Dent Relat Res. 2009. [DOI] [PubMed]
  8. Buscher J, van der Mei H. In: Community Structure and Co-operation in Biofilms. Allison D, Gilbert P, Lappin-Scott H, Wilson M, editor. Cambridge: Cambridge University Press; 2000. Initial microbial adhesion events: mechanisms and implications; pp. 25–36. full_text. [Google Scholar]
  9. Kolenbrander PE, Andersen RN, Blehert DS, Egland PG, Foster JS, Palmer RJ Jr. Communication among oral bacteria. Microbiol Mol Biol Rev. 2002;66:486–505. doi: 10.1128/MMBR.66.3.486-505.2002. table of contents. [DOI] [PMC free article] [PubMed] [Google Scholar]
  10. Marsh PD. Dental plaque: biological significance of a biofilm and community life-style. J Clin Periodontol. 2005;32(Suppl 6):7–15. doi: 10.1111/j.1600-051X.2005.00790.x. [DOI] [PubMed] [Google Scholar]
  11. Leonhardt A, Renvert S, Dahlen G. Microbial findings at failing implants. Clin Oral Implants Res. 1999;10:339–345. doi: 10.1034/j.1600-0501.1999.100501.x. [DOI] [PubMed] [Google Scholar]
  12. Tanner A, Maiden MF, Lee K, Shulman LB, Weber HP. Dental implant infections. Clin Infect Dis. 1997;25(Suppl 2):S213–217. doi: 10.1086/516243. [DOI] [PubMed] [Google Scholar]
  13. Al-Ahmad A, Wiedmann-Al-Ahmad M, Faust J, Bachle M, Follo M, Wolkewitz M, Hannig C, Hellwig E, Carvalho C, Kohal R. Biofilm formation and composition on different implant materials in vivo. J Biomed Mater Res B Appl Biomater. 2010;95:101–109. doi: 10.1002/jbm.b.31688. [DOI] [PubMed] [Google Scholar]
  14. Marsh PD. Are dental diseases examples of ecological catastrophes? Microbiology. 2003;149:279–294. doi: 10.1099/mic.0.26082-0. [DOI] [PubMed] [Google Scholar]
  15. Schou S, Holmstrup P, Hjorting-Hansen E, Lang NP. Plaque-induced marginal tissue reactions of osseointegrated oral implants: a review of the literature. Clin Oral Implants Res. 1992;3:149–161. doi: 10.1034/j.1600-0501.1992.030401.x. [DOI] [PubMed] [Google Scholar]
  16. Quirynen M, van der Mei HC, Bollen CM, Schotte A, Marechal M, Doornbusch GI, Naert I, Busscher HJ, van Steenberghe D. An in vivo study of the influence of the surface roughness of implants on the microbiology of supra- and subgingival plaque. J Dent Res. 1993;72:1304–1309. doi: 10.1177/00220345930720090801. [DOI] [PubMed] [Google Scholar]
  17. Bollen CM, Papaioanno W, Van Eldere J, Schepers E, Quirynen M, van Steenberghe D. The influence of abutment surface roughness on plaque accumulation and peri-implant mucositis. Clinical oral implants research. 1996;7:201–211. doi: 10.1034/j.1600-0501.1996.070302.x. [DOI] [PubMed] [Google Scholar]
  18. Frojd V, Franke-Stenport V, Meirelles L, Wennerberg A. Increased bone contact to a calcium-incorporated oxidized commercially pure titanium implant: an in-vivo study in rabbits. Int J Oral Maxillofac Surg. 2008;37:561–566. doi: 10.1016/j.ijom.2008.01.020. [DOI] [PubMed] [Google Scholar]
  19. Frojd V, Wennerberg A, Franke-Stenport V. Importance of Ca2+ modifications for osseointegration of smooth and moderately rough anodized titanium implants - a removal torque and histological evaluation in rabbit. Submitted. 2010. [DOI] [PubMed]
  20. Sul YT, Johansson CB, Albrektsson T. Oxidized titanium screws coated with calcium ions and their performance in rabbit bone. The International journal of oral & maxillofacial implants. 2002;17:625–634. [PubMed] [Google Scholar]
  21. Sul YT, Johansson CB, Jeong Y, Albrektsson T. The electrochemical oxide growth behaviour on titanium in acid and alkaline electrolytes. Med Eng Phys. 2001;23:329–346. doi: 10.1016/S1350-4533(01)00050-9. [DOI] [PubMed] [Google Scholar]
  22. Wennerberg A, Albrektsson T. Suggested guidelines for the topographic evaluation of implant surfaces. Int J Oral Maxillofac Implants. 2000;15:331–344. [PubMed] [Google Scholar]
  23. Wickstrom C, Svensater G. Salivary gel-forming mucin MUC5B--a nutrient for dental plaque bacteria. Oral Microbiol Immunol. 2008;23:177–182. doi: 10.1111/j.1399-302X.2007.00407.x. [DOI] [PubMed] [Google Scholar]
  24. Franks AH, Harmsen HJ, Raangs GC, Jansen GJ, Schut F, Welling GW. Variations of bacterial populations in human feces measured by fluorescent in situ hybridization with group-specific 16S rRNA-targeted oligonucleotide probes. Appl Environ Microbiol. 1998;64:3336–3345. doi: 10.1128/aem.64.9.3336-3345.1998. [DOI] [PMC free article] [PubMed] [Google Scholar]
  25. Amann RI, Krumholz L, Stahl DA. Fluorescent-oligonucleotide probing of whole cells for determinative, phylogenetic, and environmental studies in microbiology. J Bacteriol. 1990;172:762–770. doi: 10.1128/jb.172.2.762-770.1990. [DOI] [PMC free article] [PubMed] [Google Scholar]
  26. Chavez de Paz LE. Image analysis software based on color segmentation for characterization of viability and physiological activity of biofilms. Appl Environ Microbiol. 2009;75:1734–1739. doi: 10.1128/AEM.02000-08. [DOI] [PMC free article] [PubMed] [Google Scholar]
  27. van Loosdrecht MC, Lyklema J, Norde W, Schraa G, Zehnder AJ. The role of bacterial cell wall hydrophobicity in adhesion. Appl Environ Microbiol. 1987;53:1893–1897. doi: 10.1128/aem.53.8.1893-1897.1987. [DOI] [PMC free article] [PubMed] [Google Scholar]
  28. Albrektsson T, Wennerberg A. Oral implant surfaces: Part 1--review focusing on topographic and chemical properties of different surfaces and in vivo responses to them. Int J Prosthodont. 2004;17:536–543. [PubMed] [Google Scholar]
  29. Quirynen M, Bollen CM, Papaioannou W, Van Eldere J, van Steenberghe D. The influence of titanium abutment surface roughness on plaque accumulation and gingivitis: short-term observations. Int J Oral Maxillofac Implants. 1996;11:169–178. [PubMed] [Google Scholar]
  30. Mah TF, O'Toole GA. Mechanisms of biofilm resistance to antimicrobial agents. Trends Microbiol. 2001;9:34–39. doi: 10.1016/S0966-842X(00)01913-2. [DOI] [PubMed] [Google Scholar]
  31. Lima EM, Koo H, Vacca Smith AM, Rosalen PL, Del Bel Cury AA. Adsorption of salivary and serum proteins, and bacterial adherence on titanium and zirconia ceramic surfaces. Clin Oral Implants Res. 2008;19:780–785. doi: 10.1111/j.1600-0501.2008.01524.x. [DOI] [PubMed] [Google Scholar]
  32. Wickstrom C, Herzberg MC, Beighton D, Svensater G. Proteolytic degradation of human salivary MUC5B by dental biofilms. Microbiology. 2009;155:2866–2872. doi: 10.1099/mic.0.030536-0. [DOI] [PMC free article] [PubMed] [Google Scholar]
  33. Hauser-Gerspach I, Kulik EM, Weiger R, Decker EM, Von Ohle C, Meyer J. Adhesion of Streptococcus sanguinis to dental implant and restorative materials in vitro. Dent Mater J. 2007;26:361–366. doi: 10.4012/dmj.26.361. [DOI] [PubMed] [Google Scholar]