Optimized antimicrobial and antiproliferative activities of titanate nanofibers containing silver

Abstract

Titanate nanofibers containing silver have been demonstrated through the experiments reported herein to have effective antifungal and antiproliferative activities in the presence of UV light. The titanate nanofibers containing silver can be fabricated by means of ion exchange followed by a topochemical process in an environment suitable for reductive reactions. Excellent antibacterial, antifungal, and antiproliferative activities could be demonstrated by both Ag₂Ti₅O₁₁ · xH₂O and Ag/titanate (UV light irradiation) due to their unique structures and compositions, which have photocatalytic activities to generate reactive oxygen species and capabilities to continuously release the silver ions. Therefore these materials have the potential to produce a membrane for the treatment of superficial malignant tumor, esophageal cancer, or cervical carcinoma. They may also hold utility if incorporated into a coating on stents in moderate and advanced stage esophageal carcinoma or for endoscopic retrograde biliary drainage. These approaches may significantly reduce infections, inhibit tumor growth, and importantly, improve quality of life and prolong survival time for patients with tumors.

Introduction

Silver has long been known to be able to exhibit a strong toxicity to a wide spectrum of microorganisms with minimal perturbation to normal human cells. More specifically, silver ions have been revealed to be the most useful form of silver in terms of reported antibactericidal activity.^1–5 Before the introduction of the modern compounds containing silver, dilute solutions of silver nitrate were adopted to treat infections as early as in the nineteenth century. Nevertheless, silver existing in this form or in an ionic state in solution is not stable because the silver ions can easily be reduced to silver clusters, which results in significant loss of their antibactericidal effects. Silver-based compounds such as sulfadiazine silver (C₁₀H₉AgN₄O₂S) and mild silver protein (Argyrol^®; Argyrol Pharmaceuticals, Seattle, WA) have been used extensively in various bactericidal applications.^6–9 For example, these silver-based compounds have been shown to be effective in the care of burns, severe chronic osteomyelitis, urinary tract infections, and central venous catheter infections.^10,11 Because these silver-based organic compounds are quite unstable, however, especially when exposed to heat or light irradiation, controlling dosage and obtaining consistent therapeutic outcomes is very challenging. Recently, other materials containing silver, such as Ag₂S/Ag heterodimers, silicon nanowires decorated with silver nanoparticles and Ag/SiO₂ nanocomposites, have been reported and some preliminarily antimicrobial activities have been demonstrated.^12–14 One shortcoming of these systems relates to the relatively low concentration of silver ions present since they can be released only through the dissolution process. This is dependent on the surrounding environment and includes parameters such as pH, temperatures, solvents, redox conditions, and ionic strength. Indeed, even the storage time of composites containing silver could influence their release rate of silver ions.⁴ Moreover, practical applications of various silver-based materials are often hampered by the ease of oxidation of silver nanoparticles to form silver oxide, which may cause loss of antibacterial activity.⁵ Therefore, it is essential to design and construct a new carrier for stable silver ions which can store and release silver ions in a controllable manner.

Protonated titanate usually has a layered atomic structure which is clearly capable of exchanging ions, especially monovalent cations such as Na⁺, K⁺, Ag⁺, and Cs⁺.^15–18 The basic framework is built up from a structure unit of four TiO₆ octahedra arranged in a line by means of edge sharing. The units are combined with each other from above and below to form a zigzag string of octahedra. The formed string is then joined with other strings by corner sharing to make a staggered sheet containing 2-dimensional (2D) galleries inside.¹⁹ Titanates of this structure have very pronounced ion-exchanging properties, allowing almost stoichiometric amounts of alkaline ions to be exchanged.^20–24 Due to its good biocompatibility, titanates have been used in various biological processes including biocatalysts, biosensors, controlled drug delivery, and bioscaffolds for cell cultures.^25–29 Furthermore, the light irradiation can cause titanates to generate reactive oxygen species (ROS) which are capable of damaging DNA, cell membranes, and cellular proteins,⁵ and may lead to the death of microorganisms. The metallic silver nanoparticles growing on the surface of titanates can not only promote this photocatalytic process, but also enhance the absorption of the photons in the visible light region, to generate the ROS. The oxidation of silver nanoparticles can be avoided in the reductive chemical environment that was shaped during the photocatalytic process, thereby maintaining their antibacterial activity. By means of the above, the combination of the silver ions and the photocatalytic effects may serve to construct new functional materials for antimicrobial, antifungal, and antiproliferative applications, and potentially may also offer synergistic functions.

Herein, we report a facial synthesis process to prepare layered 1-dimensional (1D) titanates containing silver in different forms. The optimized forms of these materials were successfully screened for antimicrobial, antifungal, and antiproliferative applications. Through ion exchange and the controlled reduction processes, we demonstrate that silver species can be inserted into the layered titanates and then reduced to elemental silver nanoparticles. The average particle size and particle size distribution of silver nanoparticles can be tuned by using chemical (NaBH₄) or UV-light reduction processes. Interestingly, the experimental results indicate that silver titanate and Ag/titanate in the presence of UV-light irradiation have better antimicrobial, antifungal, and antiproliferative activities. These promising results indicate the synergistic effects that can be obtained through ROS being released from the photocatalysis process along with the silver ions that are released from the ion-exchange process. As a semiconducting material, layered titanates play a dual role, acting as a silver ion reservoir, as well as a photocatalyst.

Materials and Methods

Materials

All reagents used were of analytical grade. TiF₄ and the NaBH₄ were obtained from Sigma-Aldrich (St Louis, MO). All aqueous solutions were prepared with double-distilled water.

Synthesis of titanates and Ag/titanates

The layered protonated pentatitanate (H₂Ti₅O₁₁ · H₂O) was prepared according to a procedure reported previously.³⁰ In a typical experiment, 30 mL of 0.040 M TiF₄ aqueous solution containing 10 g of NaOH was kept in a Teflon- lined autoclave at 180°C for 48–50 hours and then the white gellike product was washed thoroughly with a 0.50 M HCl solution and deionized water. To generate the Ag/titanate with the Ag⁺ nutrients from the interlayer space, typically, 0.5 g of white H₂Ti₅O₁₁ · H₂O product was added to 12.5 mL of AgNO₃ aqueous solution with a concentration of 0.01–0.1 M and stirred vigorously in the dark for 30–52 hours. In the wake of the H⁺/Ag⁺ exchange, the sample was washed thoroughly with deionized water to remove externally adsorbed Ag⁺. Afterwards, the titanate with Ag⁺ in the galleries was redispersed in 25 mL of deionized water and exposed to UV light (Xe 300 W, 320–400 nm) for 8–14 hours. As a parallel reduction method, NaBH₄ aqueous solution (0.02–0.05 M) was applied and stirred vigorously for 20 minutes. After the reaction, the Ag/titanate nanocomposites were washed with deionized water three times. It should be noted that all the ion-exchange and redox processes were performed at room temperature.

Characterization methods and instruments

Scanning electron microscopy with energy-dispersive X-ray spectroscopy (SEM/EDX, JSM-5600 LV [JEOL, Tokyo, Japan]; FESEM/EDX, JSM-6700F [JEOL]) and transmission electron microscopy (TEM, JEM 2010, 200 kV [JEOL]) were used to examine the dimension, morphology, and chemical composition of the samples. Surface binding elements were analyzed with X-ray photoelectron spectroscopy (XPS, Kratos Axis Ultra DLD, Manchester, UK). All binding energies were referenced to the C1s speak (285.0 eV) arising from surface hydrocarbons (or possible adventitious hydrocarbon). Prior to peak deconvolution, X-ray satellites and inelastic background (Shirley-type) were subtracted for all spectra. The UV-vis absorption spectra of protonated pentatitanate, silver titanate, and Ag/titanate nanostructures were examined with a UV-vis spectrophotometer (Cary-500; Varian Inc, Palo Alto, CA).

Antibacterial activity assay

E. coli DH-5α was selected as an indicator experimental bacteria. Luria Bertani (LB) broth was used as the culture medium. Bacteria were aerobically cultivated in LB broth for 20 hours at 37°C. A sterile cotton swab was used to inoculate E. coli DH-5α on to the surface of LB broth plates. The titanate-based compounds (2 mg) were suspended in sterile water and placed over the surface of the plates to keep in contact with E. coli. Each compound was divided into two groups, with one group being kept in the dark while the other was exposed to natural light for 2 hours per day. We took this approach so that the bacteria would not be killed by ultraviolet rays and the compounds could be excited by the minimal ultraviolet light present in the natural light. The diameter of inhibition zone was measured after 24 hours of incubation at 37°C, which enabled evaluation of the anti-bacterial activity.

Antifungal activity assay

To assess antifungal activity, the in vitro minimal inhibitory concentrations (MICs) of the titanate-based compounds were determined by using Candida albicans strain SC5314. These yeast cells were cultivated on Yeast Extract Peptone Dextrose (YPD) medium plates at 30°C overnight to obtain single colonies. These single colonies were then resuspended in YPD broth to a density of 1.0 × 10⁸ cells/mL. The MICs of the cells were determined by a microdilution test based on the macrodilution referential method of the National Committee for Clinical Laboratory Standards.³¹ Cells (100 μL; 5.0 × 10⁴ cells/mL) were then added into wells in a 96-well plate in rows A and B. Row A contained 200 μL of yeast cells and the titanate-based compounds for testing, while row B contained 200 μL of yeast cells only. Row C contained 200 μL of RPMI 1640 medium (Gibco, Langley, OK) as a blank control while row D contained 200 μL of RPMI 1640 medium, as well as titanate-based compounds. The titanate-based compounds to be tested were dispersed in phosphate buffer solution (PBS) and the two-fold serial dilutions were prepared in RPMI 1640 medium with a final concentration ranging from 200 to 0.390 μg/mL. Fluconazole (FLC) served as the positive control with final concentrations ranging between 64.0 and 0.125 μg/mL. Each titanate-based compound was divided into two groups with one group being kept in the dark while the other was exposed to ultraviolet light (λ = 365 nm, UVA, ENF-280C/FE, Spectroline, Westbury, NY) for 2 hours. The plates were then incubated at 30°C for 24 hours without being shaken and the growth of cells was determined by measuring the optical density at wavelength of 620 nm. The MIC₈₀ and MIC₅₀ of the target additives (titanate-based compounds or FLC) were defined as an approximately 80% and 50% reduction in terms of the growth of cells compared with the growth of cells with no target additive.

Antiproliferative activity assay

The in vitro antiproliferative activities of protonated pentatitanate (H₂Ti₅O₁₁ · H₂O) and corresponding silver-containing titanate nanofibers were studied on a human liver cancer cell line (Hep G2) by employing the Alamar Blue assay.^32,33 Parallel control groups without titanate-based inorganic compounds were also studied. Each titanate-based compound was further separated into two groups, with one group being kept in the dark while the other was exposed to ultraviolet light (λ = 365 nm, UVA) for 2 hours per day. Hep G2 cells were cultivated in DMEM and 10% fetal bovine serum (FBS) at 37°C in 5% CO₂. Cells were then added into 96 well plates (1 × 10⁵ cells/mL, 100 μL) and the medium was replaced with DMEM and 10% FBS containing titanate-based compounds 24 hours later. Titanate-based compounds were tested over concentrations ranging from 3.125 μg/mL to 200 μg/mL. Then cells were incubated for 24 hours before 10 μL Alamar Blue was added and the plates were then incubated in the dark for a further 4 hours. Mitomycin C (MMC) was used as positive control in the cell viability assays. The optical density was monitored at 570 nm (absorbance) and 630 nm (reference absorbance) in a microplate reader (Elx-808; Biotek, Winooski, VT). The calculated IC₅₀ values were expressed as the concentration of titanate-based compounds (μg/mL) under which 50% of cell death was observed, compared with the controls.

Results and discussion

A series of experiments was conducted to prepare silver titanate and Ag/titanate nanocomposites with the process shown in Scheme 1. The major steps involved are: (a) initial protonated pentatitanate with ion-exchanging capabilities (idealized structure viewed in the [010] direction; open and filled red circles denote H⁺ or H₃O⁺ at y = 0 and 1/2, respectively); (b) replacement of proton H⁺ by Ag⁺ in the interlayer space (open and filled blue circles denote Ag⁺); and (c) partial intercalated Ag⁺ cations were transferred to the outside of the galleries and then reduced to form silver clusters/nanoparticles by using titanates as the heterogeneous nucleation substrate. Some water molecules may also exist in the galleries in a quasi-liquid state, but these are not shown in the diagram. It should be noted that another similar process, reduction with NaBH₄, can be applied to the same cations to form more, relatively large, silver nanoparticles growing on the layered substrate. The basic structure of host lamellar [Ti₅O₁₁ ²⁻]_∞ does not change throughout the process from (A) to (C) in Scheme 1, except that the interlayer distance may vary with the degree of cation interaction, as well as by the amount of free interlayer water introduced.

Scheme 1.

Schematic representations of “nutrients from galleries” principle to generate Ag/titanate nanocomposites: (A) represents the pristine protonated pentatitanate (H₂Ti₅O₁₁ · H₂O); (B) silver titanate (Ag₂Ti₅O₁₁ · xH₂O) prepared by exchange of protons with Ag⁺ cations; partial (C) or fully (D) Ag⁺ cations exchange with protons in the layered space and the formation of the silver nanoparticles on titanate substrates with the redox process. The unit cell (a–d; enclosed by dotted lines) are C-based centered monoclinic, which is projected along [010] direction.

Note: Open and filled circles indicate the locations at y = 0 and ½, respectively.

Figure 1 shows the TEM images (A–D) and corresponding digital camera photographs (e–h) of the: initial protonated pentatitanate (H₂Ti₅O₁₁ · H₂O) nanofibers as the starting structural basis (A); fully Ag⁺ exchanged titanate (B); controlled partial reverse Ag⁺ exchange and generation of Ag nanoparticles on titanate substrate through interlayer mass transfer and outside redox process in UV-light irradiation (C); and the product of fully reverse Ag⁺ exchange and silver nanoparticles growth (D). The detailed information on preparation, structure, and properties of pristine protonated titanate (H₂Ti₅O₁₁ · H₂O) was illustrated in a previous publication; the bulk product dispersed in water appears as a stable milky solution, as indicated in the digital camera image (E).³⁰ Due to its layered structure and high ion-exchanging capability, the protonated titanate nanofibers can be used as an excellent Ag⁺ nutrients reservoir, as well as a template for further silver nanoparticles growth.

Figure 1.

TEM images and digital camera photographs of protonated pentatitanate (H₂Ti₅O₁₁ · H₂O) (A and E), titanate after Ag⁺ cations exchange (B and F), partial reduction of Ag⁺ cations from the layered space with the UV light irradiation (C and G), and reduction of Ag⁺ cations with NaBH₄ agent (D and H).

Titanate with fully Ag⁺/H⁺ exchange was easily prepared by dispersing H₂Ti₅O₁₁ · H₂O nanostructures in AgNO₃ aqueous solution (0.01–0.1 M) and stirring this vigorously in the dark for 30 hours at room temperature. The silver titanate generated maintains the original nanofiber morphology well, with a relatively clean surface, meaning that no silver nanoparticles are present at this stage (see Figure 1B). Compared with the original pure protonated titanate, the corresponding photograph of silver titanate (see Figure 1F) shows a very slight yellowness. The XPS data also support the conclusion that all of the silver is in the monovalent state (see Figure 3A). Interestingly, if UV-light irradiation (300 W Xe, 320–400 nm) was applied to the as-prepared silver titanate aqueous solution, the color of the silver titanate would gradually change from slightly yellow to grey within 8–14 hours, as illustrated in Figure 1G. Based on the TEM observation in Figure 1C, the change of color is mainly caused by the formation of silver nanoparticles on titanate substrate, so that we can conclude that Ag⁺ cations should be transferred from the galleries and then reduced by UV light. In UV-light irradiation, the photocatalytic nature of layered titanate can release reducing species, according to:

Figure 3.

X-ray photoelectron spectroscopy spectra of Ag 3d: (A) titanate after Ag⁺ cation exchange, (B) partial reduction of Ag⁺ cations from the layered space with UV light irradiation, and (C) reduction of Ag⁺ cations with NaBH₄ agent.

Abbreviation: au, arbitrary units.

$${Ag}^{+}+{e_{CB}}^{-}\to {Ag}^{(0)}$$ (1)

$${h_{VB}}^{+}+H_{2}O\to H^{+}+HO.$$ (2)

even though

$${Ag}^{(0)}+{h_{VB}}^{+}\to {Ag}^{+}$$ (3)

process may also exist in the presence of oxygen. As is revealed by the TEM image in Figure 1C, silver nanoparticles randomly grow on the titanate nanofibers and are approximately 10–20 nm with a spherical or hemispherical morphology. The high-resolution TEM (HRTEM) image shown in Figure 2 also provides evidence of the metal silver nanoparticles deposited on the titanate substrate. Measuring the lattice fringes of the HRTEM image shows that these were spaced at 0.25 nm on average, which is very close to the {111} lattice spacing of the face-centered cubic (fcc) silver crystals. Furthermore, the lattice spacing of the 1D titanate substrate is 0.63 nm on average (see Figure 2). Due to the meso-stable crystal structure, as well as surface properties of the titanate, zero valence silver clusters could easily form the nuclei on titanate nanofibers. Based on the TEM results (see Figure 1c), the silver ions did not penetrate too deeply into the bulk solution before they were reduced to a zero valance state, at which point they formed nanoparticles on the surface of the titanate substrate. Considering the ion balance inside the galleries, the H⁺ or H₃O⁺ produced by the redox reaction could be exchanged into the galleries in the process of the reaction, resulting in distortion of titanate lattice (see Figure 2). Therefore, in the current step, the cation exchange and the redox reaction are dynamic processes. Each stage of the process could be executed in a controllable way by adjusting external parameters such as UV-light intensity or irradiation time.

Figure 2.

High resolution TEM image of Ag/titanate nanocomposite formed by UV light irradiation (300 W Xe, 320–400 nm).

The XPS analysis indicates that about 34.84% of the silver cations have been reduced to a zero valence state, as shown in Figure 3b. Moreover, the release of Ag⁺ nutrients from the galleries and the following redox process could be more thoroughly completed by introducing some reduction agents such as NaBH₄ (0.05 M in deionized water). As indicated in the TEM image (Figure 1D), a large amount of silver nanostructures was found on the titanate nanosubstrates. The color of the Ag/titanate nano-composite at this stage has changed to black, which contributes mainly to a mass of polydispersed silver nanoparticles on the substrates (Figure 1H). Consistent with the electron microscopy image and mechanism analyses, the deconvolution of Ag 3d_5/2 peak indicates that 45.91% of the original silver cations have been reduced to Ag⁽⁰⁾, which has a typical binding energy at 368.2 eV, as depicted in Figure 3C. Accordingly, spectrophotometric measurements were also performed in order to follow the ion exchange and the reduction of Ag⁺. Figure 4 shows the absorbance spectra of the various titanate-based compounds, which matches well with the observations shown in Figure 1.

Figure 4.

UV-visible absorption spectra of (A) protonated pentatitanate (H₂Ti₅O₁₁ · H₂O), (B) titanate after Ag⁺ cations exchange, (C) partial reduction of Ag⁺ cations from the layered space with the UV light irradiation, and (D) reduction of Ag⁺ cations with NaBH₄ agent.

Antimicrobial, antifungal, and antiproliferative activities

Studies examining bacterial inhibition zones in the presence of the titanate-based compounds were performed. The results for Ag/titanate in the presence of NaBH₄ reduction (A), Ag/titanate in the presence of UV light irradiation (B), and Ag₂Ti₅O11 · xH₂O (C), and pure H₂Ti₅O₁₁ · H₂O (D) tested against E. coli, are presented as images in Figure 5. The Ag/titanate in the presence of UV light irradiation and Ag₂Ti₅O₁₁ · xH₂O showed the highest antibacterial activity. The samples irradiated by the UV light have enhanced effects compared with the samples without UV light irradiation. The fully protonated titanate (H₂Ti₅O₁₁ · H₂O) nanofibers showed the least effective antibacterial activity.

Figure 5.

Comparison of the inhibition zone test for the titanate-based compounds: Ag/titanate by NaBH₄ reduction (A), Ag/titanate by UV light irradiation (B), Ag₂Ti₅O₁₁ · xH₂O (C), and pure H₂Ti₅O₁₁ · H₂O (D).

The results in Figure 6A show that both Ag₂Ti₅O₁₁ · xH₂O and Ag/titanate (UV light irradiation) have excellent anti-fungal activity, as is revealed by the MIC₅₀ values. For all titanate compounds containing silver, UV light irradiation can significantly enhance the antifungal activity. The MIC₅₀ values of the samples irradiated by UV light are at least two-fold lower than those of the samples without UV light irradiation. The less than ideal antifungal activity of Ag/titanate (NaBH₄ reduction) might be due to the existence of fewer silver ions between the layers of the titanate nanofibers and the relatively large size of the silver nanoparticles decorating the surface. As a control sample, the fully protonated titanate (H₂Ti₅O₁₁ · H₂O) nanofibers show the worst antifungal activity, as expected, due to its low photocatalytic property and the absence of the silver ions. It should be noted that even though the FLC drug has the lowest MIC₅₀ values (0.25 μg/mL respectively) in the presence of UV light irradiation, it is a small organic molecule and has undesirable effects including induction of drug resistance and instability. In view of this, the titanate nanofibers containing silver developed through the process reported here are still highly attractive and have no associated antimicrobial resistance issues as they are in a purely inorganic phase and have a totally different mechanism underpinning their antifungal activity.

Figure 6.

Antifungal (A) and antiproliferative (B) activities of titanate-based compounds, which are Ag/titanate by NaBH₄ reduction, Ag/titanate by UV light irradiation, Ag₂Ti₅O₁₁ · xH₂O, and pure H₂Ti₅O₁₁ · H₂O.

Silver ions can readily deactivate bacteria by reacting with the thiol functional groups in proteases, which causes loss of integrity of the membrane, and then leads to malfunction of the permeability barrier.⁵ This ultimately leads to the collapse of the bacterial membrane and the death of microorganisms. Furthermore, just like traditional photosensitizers, which have been widely applied in photodynamic therapy, titanate containing silver can also release highly reactive ROS to incapacitate the bacteria as well. For titanate nanofibers containing silver, the prolonged time of UV light irradiation may cause the formation of more silver nanoparticles on the surface of titanate nanofibers. However, this effect has been shown to be insignificant due to the relatively slow reduction process induced by UV light, which usually takes more than 10 hours. More interestingly, the as-prepared titanate nanocomposites containing silver also demonstrated good antiproliferative activities when tested in the human liver cancer cell line Hep G2 as a model target. As indicated in Figure 6B, both Ag₂Ti₅O₁₁ · xH₂O and Ag/titanate (UV light irradiation) have better antiproliferative effects than those observed with Ag/titanate (NaBH₄ reduction) and plain titanate nanofibers, with the IC₅₀ values being 32.28 and 37.51 μg/mL, respectively, without UV light irradiation. Moreover, the IC₅₀ values can be further lowered to 4.79 and 2.53 μg/mL due to ROS-mediated cell damage; this is consistent with the antifungal activities discussed above. These promising antiproliferative activities of the inorganic titanates containing silver are also comparable to those found with purely organic drugs such as mitomycin C (MMC, C₁₅H₁₈N₄O₅); the IC₅₀ values were 10.16 μg/mL (with UV light irradiation) and 12.21 μg/mL (without UV light irradiation), respectively.

The titanates containing silver developed in the process reported here appear to be quite unique, with the layered titanates having at least three functions: (i) acting as a reservoir for silver ions, which can be released continuously through the ion-exchange process; (ii) stabilizing the silver nanoparticles through the formation of silver-titanate nanocomposites; and (iii) generating ROS through the photocatalytic process, which can not only effectively enhance the antibacterial, antifungal, and antiproliferative activities, but also provide an environmentally friendly approach to in situ production of silver nanoparticles and avoid the oxidation of the silver species.

Conclusion

In conclusion, a series of titanate nanostructures containing silver with tailored compositions was successfully prepared through the ion-exchange method and controlled topochemical processes described, while their antibacterial, antifungal, and antiproliferative activities have been investigated in vitro. From the results, both Ag₂Ti₅O₁₁ · xH₂O and Ag/titanate (UV light irradiation) have demonstrated excellent antibacterial, antifungal, and antiproliferative functional activities due to their unique structures and compositions, which include having photocatalytic activity to generate ROS and the ability to release silver ions continuously.

The soft chemistry strategy adopted in this working process may pave the way for the development of highly efficient, low-cost, and stable antimicrobial and antiproliferative agents with promise in applications such as producing a membrane for the treatment of superficial malignant tumors, esophageal cancer, or cervical carcinoma, and so on. They may also hold utility if incorporated into a coat on stents in moderate and advanced stage esophageal carcinoma or stents for endoscopic retrograde biliary drainage. These approaches may significantly reduce infections, inhibit tumor growth and, importantly, improve quality of life, and prolong survival time for patients with tumors.