One-Pot Microbial Method to Synthesize Dual-Doped Graphene and Its Use as High-Performance Electrocatalyst

Abstract

A novel strategy to synthesize nitrogen (N) and sulfur (S)-doped graphene (G) is developed through sulfate-reducing bacteria treating graphene oxide (GO). The N, S-doped G demonstrates significantly improved electrocatalytic properties and electrochemical sensing performances in comparison with single-doped graphene due to the synergistic effects of dual dopants on the properties of graphene.

Graphene has hold a great promise for its potential applications in electrochemistry due to its large theoretical specific surface area (2620 m²g⁻¹), excellent electrical conductivity and high electrocatalytic activities¹,². Particularly, it has been recognized that the doping of heteroatoms into graphene is an efficient method to enhance its electrocatalytic performances³. Both theoretical calculations and experimental results have proved that the introduction of more electronegative nitrogen (N) atoms into sp² hybridized carbon (C) frameworks in graphene is generally effective in modifying their electrical properties and chemical activities⁴. For instance, the spin density and charge distribution of C atom will be influenced by the neighbor N dopants⁵,⁶, inducing the “activation region” on graphene surface, which is expected to directly participate in catalytic reactions, and/or provide more nucleation sites to anchor the catalytically active metal nanoparticles⁷. Recent findings have also shown that the doping of sulfur (S) atom into the graphene materials caused the changed spin density of graphene, which resulted in the excellent catalytic activity, long-term stability, and high tolerance in alkaline media of the S-doped graphene (S-G) for oxygen reduction reaction (ORR)⁷,⁸. Furthermore, N, S-doped graphene (N, S-G) had been realized and demonstrated excellent catalytic activity⁹. Although great progresses have been made in the synthesis of different types of doped graphene materials, these approaches require high temperature (900 °C) treatment and toxic chemical (i.e., THF)³,⁴,⁵,⁶,⁷,⁸,⁹. Therefore, low-temperature and facile approaches are highly desired for the large-scale production of doped graphene materials with excellent catalytic performances.

In this work, we report for the first time a novel approach to synthesize N, S-G through a one-pot reduction of GO by microbial respiration of sulfate-reducing bacteria (SRB) under the mild conditions (37°C) and its promising applications as high-performance electrocatalysts for the electrochemical sensing of heavy metal ions. SRB, a diverse group of heterotrophic and mixotrophic bacteria¹⁰, is ubiquitous in marine sediments¹¹,¹²,¹³,¹⁴, hydrothermal vents¹⁵, waste landfills and even in the human body such as mouth¹⁶,¹⁷ and bowel¹⁸, and plays an important role in the global cycling of C and S. These microbes mainly use S as a terminal electron acceptor for the degradation of organisms during anaerobic respiration¹⁹. Considering that graphene oxide (GO) has shown the property as electron acceptor²⁰,²¹,²²,²³,²⁴, it is possible to realize the reduction of GO by microbial respiration of SRB. Our findings have shown that N, S-G could be obtained through sulfate-reducing bacteria treating GO and exhibited high electrocatalytic activity towards the reduction of heavy metal ions such as cadmium ion (Cd²⁺) and lead ion (Pb²⁺). We also fabricated an electrochemical sensing platform for ultrasensitive simultaneous determination of Cd²⁺ and Pb²⁺ with N, S-G as electrocatalyst. This study not only gives insight into the synergistic effect of multi-element dopants on the properties of graphene, but also opens the possibility of developing new types of graphene-based functional materials with excellent electrochemical properties by a facile and low-temperature approach.

Results

The synthetic route of N, S-G is described in Fig. 1A. The microbial reduction is initiated by mixing GO dispersion with SRB and fresh culture medium²⁵, and the mixture is then incubated under an anaerobic condition in constant temperature incubator (37°C). After that, the color of GO dispersion changes from brown to black (Fig. 1A), indicative of the restoration of sp² carbon sites and re-establishment of the electronic conjugation network. The transmission electron microscope (TEM) image shows that N, S-G maintains a monolayer and flexible structure (Fig. 1B). The reduction degree of GO is monitored by time-dependent UV-vis spectroscopy. As shown in Fig. 1C, with increase of reaction time, the UV-vis absorption peak of GO dispersion at 231 nm corresponding to π → π* transitions of aromatic C = C bonds gradually shifts to 267 nm after microbial reduction treatment at 37°C for 6 days. The absorption peak in the full spectral region increases with reaction time and keeps almost unchanged after the sixth day (Fig. S2), demonstrating the completion of microbial reduction of GO.

Figure 1.

(A) Schematic illustration of the formation of N, S-G by one-pot microbial reduction process. (B) TEM image of N, S-G. (C) UV-vis absorption spectra of GO aqueous dispersion before (a) and after (b) reduction. (D) FT-IR spectra and (E) Raman spectra of GO (a) and N, S-G (b), respectively.

Fig. 1D are the Fourier Transform Infrared (FT-IR) spectra of GO and N, S-G. The spectrum of GO shows the presence of C–O (v (epoxy or alkoxy)) at 1069 cm⁻¹, C–OH (v (carboxyl)) at 1398 cm⁻¹, C = C at 1621 cm⁻¹, and C = O in carboxylic acid and carbonyl moieties (v (carbonyl)) at 1725 cm⁻¹, respectively. After bacteria treatment, the adsorption bands of oxygen functionalities disappear, and only the peak of C = C remains, suggesting that GO has been effectively reduced²⁶. The thermal stability of N, S-G examined by thermal gravimetric analysis (TGA) also proves the removal of thermally labile oxygen functional groups by the microbial reduction (Fig. S3). Fig. 1E shows the Raman spectra of GO and N, S-G. The spectrum of GO displays two prominent peaks at 1349 and 1599 cm⁻¹, corresponding to the well-documented D and G bands, respectively. The intensity ratio of D band to G band (I_D/I_G) of GO is about 1.02. The G band of N, S-G shifts to 1586 cm⁻¹, and its I_D/I_G increases to 1.40 due to the defects introduced by N and S dually doping and the realization of deoxygenation of GO²⁷.

X-ray photoemission (XPS) is a powerful tool to identify the surface chemical composition and the valence state in bulk material²⁸. The full range XPS analysis of N, S-G shows the presence of C, O, N and S (Fig. 2A)²⁹. The degree of GO reduction is described via the atomic ratio of carbon and oxygen (C/O) obtained by taking the ratio of C 1s to O 1s peak areas in XPS spectra. After microbial reduction, the C/O increases from 2.12 to 4.02²⁹,³⁰,³¹. Moreover, the intensity of C-O/C-O-C peak decreases and the C-C sp² bond becomes predominant (Fig. S4), indicating that most of the oxygen-containing functional groups are removed and the conjugated graphene networks are restored. The XPS analysis also confirms the successful doping of N and S atoms into the graphene networks as well²⁹. The high resolution XPS spectrum of N 1s (Fig. 2B) reveals the presence of three nitrogen functional groups, and an atomic percentage of doped nitrogen to be about 6.11%. Three nitrogen peaks are observed for pyridinic N, pyrrolic N and graphitic N with binding energies of 400.01 eV, 401.45 eV and 402.50 eV, respectively. Among these nitrogen configurations, the pyridinic N is the main form, which is believed to enhance the electrochemical properties of N-doped graphene³². Moreover, the binding energies of S 2p are also used to analyze the S doping in synthesized graphene (Fig. 2C). The peaks at 164.02 eV and 167.92 eV suggest the doping in the form of sulfide bonds (-C-S-C-, 78%) and oxidized sulfur bonds (-C-SO-C- or -C-SO₂-C-, 22%), respectively⁸,³³. The calculated doping concentration of sulfur is 1.1% (atom %).

Figure 2. (A) XPS survey spectrum of GO and N, S-G. (B) Curve fit of N 1s spectrum of N, S-G, (C) Curve fit of S 2p spectrum of N, S-G.

Discussion

Considering the unique doped structure⁸,³², N, S-G is expected to possess excellent electrochemical properties³⁴,³⁵,³⁶,³⁷,³⁸,³⁹. In this work, the as-synthesized N, S-G has been applied to fabricate a highly sensitive electrochemical platform to determine trace Cd²⁺ and Pb²⁺ by differential pulse anodic stripping voltammetry (DPASV). For the fabrication of modified electrodes, 2 mL of a 0.1% Nafion ethanol solution was added into 2 ml of a 1.0 mg/mL N, S-G dispersion to give an uniform (N, S-G)-Nafion suspension. Then 5 μL suspension was dropped onto a clean glass carbon electrode (GCE) to form (N,S-G)-Nafion modified GCE ((N,S-G)-Nafion/GCE). The Bi film coated (N,S-G)-Nafion/GCE (Bi/(N,S-G)-Nafion/GCE) was fabricated by electrodepositing Bi on (N,S-G)-Nafion/GCE using Bi(NO₃)₃ solution at −1.2 V for 300 s (Fig. S5). Compared with the bare GCE and Nafion modified GCE (Nafion/GCE) which show distorted peaks and small peak currents of metals, both of Bi/GCE and (N,S-G)-Nafion/GCE demonstrated enhanced response signals due to efficient metal deposition (Fig. 3A)⁴⁰. Furthermore, well-defined reduction peaks with the largest peak currents for target metal ions were obtained at Bi/(N, S-G)-Nafion/GCE due to the synergistic effect of Bi film and N, S-G.

Figure 3.

(A) DPASV of 15 μg L⁻¹ of Cd²⁺ and Pb²⁺ on (a) GCE, (b) Bi/GCE, (c) Nafion/GCE, (d) (N, S-G)-Nafion/GCE and (e) Bi/(N, S-G)-Nafion/GCE. (B) DPASV of simultaneous analysis of Pb²⁺ and Cd²⁺ with concentrations of 30, 24, 18, 15, 12 and 9 μg L⁻¹, respectively. (C) The calibration curve of Cd²⁺ and Pb²⁺, respectively. Supporting electrolyte: 0.2 M acetate buffer (pH 4.6), deposition potential: −1.2 V, deposition time: 300 s. (D) DPASV of 15 μg L⁻¹ of Cd²⁺ and Pb²⁺ on rGO-Nafion/GCE, Bi/(S-G)-Nafion/GCE, Bi/(N-G)-Nafion/GCE, and Bi/(N, S-G)-Nafion/GCE (from bottom to upper).

The resulting calibration plots are linear over the range from 9.0 to 30.0 μg L-1 for the simultaneous determination of Pb²⁺ and Cd²⁺ (Fig. 3B). The DPASVs of Pb²⁺ and Cd²⁺ with different concentrations on Bi/(N, S-G)-Nafion/GCE are illustrated in Fig. 3C. The Bi/(N,S-G)-Nafion/GCE demonstrates excellent sensitivity and selectivity. The detection limits are 0.016 μg L⁻¹ for Cd²⁺ and 0.018 μg L⁻¹ for Pb²⁺, respectively, which are lower than previously reported results (Table S1).

In order to demonstrate the advantages of N, S-G, chemically reduced GO, N-doped graphene (N-G) and S-G were also synthesized (Supporting Information (SI)), and Bi/rGO-Nafion/GCE, Bi/(N-G)-Nafion/GCE) and Bi/(S-G)-Nafion/GCE electrodes were also prepared under the similar procedure as that of Bi/(N, S-G)-Nafion/GCE. The DPASV characteristics of different electrodes show that heteroatom (N or S) doping into graphene leads to more intensive peak current of Pb²⁺ and Cd²⁺ on Bi/(N-G)-Nafion/GCE or Bi/(S-G)-Nafion/GCE than that on Bi/rGO-Nafion/GCE (Fig. 3D).More importantly, compared with Bi/(N-G)-Nafion/GCE or Bi/(S-G)-Nafion/GCE, Bi/(N, S-G)-Nafion/GCE shows enhanced electrochemical signals by about 36% or 23% for Pb²⁺, and 110% or 91% for Cd²⁺, respectively. The signal enhancement should be attributed to N and S atoms doped into the carbon lattice of graphene. The electrical conductivity measurement shows that the electrical conductivity of GO and N-, S-doped GO are 1 × 10⁻⁴ and 2.8 S/m, respectively. Therefore, we think that N-doping causes an atomic-scale structural deformation, and N atom can act as an electron donor that increases the n-type conductivity of graphite structure⁴¹,⁴². Moreover, S atom has a close electroneutrality to C atom and the C-S bonds are predominately at the edge or the defect sites, which causes the activity enhancement due to the changed spin density and charge distribution⁸. Hence, the multi-element doping leads to the greatly enhanced electrocatalytic activity and electrochemical sensing performances.

In summary, we report a one-pot strategy to synthesize a new type of graphene material doped with both N and S atoms through the microbial reduction of GO by SRB. The N, S-doped G demonstrated significantly improved electrocatalytic properties and electrochemical sensing performances in comparison with single-doped graphene due to the synergistic effects of dual dopants. For the simultaneous determination of Cd²⁺ and Pb²⁺, the N, S-G takes several advantages such as high sensitivity and selectivity, wide linear range and low detection limit. These results are significant because they not only give insight into the synergistic effect of multi-element dopants on the properties of graphene, but also open a way to develop new graphene functional materials with excellent electrochemical property by a simple, economical and environmentally friendly approach.

Methods

Bacterial cultures

The strain of SRB was isolated by the following procedure. Moist oily soil from Shengli oilfield of China was added to API-RP38 culture medium, and cultivated for 48 h until the medium turned black. The supernatant solution was then inoculated in fresh medium. This procedure was repeated for several times. The isolated SRB was light yellow under anaerobic conditions at 37°C in the culture medium.

The API-RP38 culture medium in the experiment contained (per liter of ultrapure water)²⁴: 4.0 mL sodium lactate, 1.0 g yeast extract, 0.2 g magnesium sulfate (MgSO₄·7H₂O), 0.1 g vitamin C(Vc), 0.01 g potassium diphosphate (K₂HPO₄) and 10.0 g sodium chloride (NaCl). The pH was adjusted to 7.0 ~ 7.2 by the appropriate addition of 1 M sodium hydroxide (NaOH). The solution was sterilized with an autoclave at 121°C for 20 min and then cooled to room temperature. After cooling, 0.2 g FeSO₄·(NH4)₂SO₄·6H₂O sterilized using ultraviolet light was added to the solution.

Microbial reduction of GO

The microbial reduction was initiated by mixing 100 mL of as-prepared GO solution (0.1 mg·mL⁻¹) aseptically with 20 mL culture of sulfate-reducing bacteria and 30 mL fresh culture medium. The mixture was incubated in anaerobic conditions at 37°C constant temperature incubator for several days. The resulting stable black dispersion was centrifuged (14000 rpm) and washed with 1 M HCl aqueous solution to remove the organic matter, cell debris and ultrapure water for several times, respectively. Finally, the resulting solid was dried at 80 °C under vacuum.

Preparation of N-G and S-G

For the preparation of N-G, a 10 mL portion of 2 mg/mL homogeneous GO aqueous dispersion was mixed with 2 mL ammonia, sealed in a 100-mL Teflon-lined autoclave and then maintained at 180 °C for 12 h. The autoclave was then naturally cooled to room temperature. The as-prepared graphene materials were taken out and dried at 80 °C under vacuum for 48 h to obtain N-G with doping concentration of nitrogen about 6.20% (atom %). For the preparation of S-G, 0.0404 g GO and 0.0201 g benzyl disulfide (BDS) were first ultrasonically dispersed in 50 ml ethanol for about 30 min. The resulting suspension was filtered to obtain uniform thin films. The films were placed into a quartz tube and annealed at 900 °C in argon atmosphere to obtain S-G with doping concentration of sulfur about 1.1% (atom %)2.

Fabrication of the (N, S-G)-Nafion composite film

The GCE was first polished with 0.3 and 0.05 μm alumina slurries and rinsed thoroughly with ultrapure water, then sonicated in 1:1 ethanol, 1:1 nitric acid and ultrapure water for 5 min, respectively, and dried at room temperature. Next, a 2 ml of 1.0 mg·mL⁻¹ N, S-G solution was mixed with equal volume of 0.1% Nafion-ethanol solution by ultrasonication for 15 min to give 0.50 mg·mL⁻¹ suspension. Finally, an aliquot of 5 μL of the mixture was coated on the pretreated GCE electrode and dried at room temperature to obtain (N, S-G)-Nafion/GCE. (N-G)-Nafion, (S-G)-Nafion, and rGO-Nafion composite films were also synthesized under the similar procedure.

Fabrication of Bi/(N, S-G)-Nafion/GCE

The three electrodes were immersed into a 50 mL electrochemical cell, containing 0.2 mol L⁻¹ acetate buffer (pH 4.6), 175 μg L⁻¹ Bi (III) and appropriate target metals. The (N, S-G)-Nafion modified GC electrode with Bi film was plated in situ by spiking the sample with the required concentration of Bi(III) and simultaneously depositing Bi³⁺ and the target metals on the surface of the electrode at −1.2 V under stirring for 300 s. Following the conditioning step, the stirring was stopped and after 10 s equilibration period, the voltammogram was recorded by applying a positive-going potential scan from −1.2 to 0.2 V (with a step increment of 8 mV, amplitude of 50 mV, and pulse period of 0.2 s). Prior to the next cycle, a cleaning step (120 s at 0.3 V, with solution stirring) was used to remove the target metals and bismuth film. Bi/(N-G or S-G or RGO)-Nafion/GCE was also synthesized under the similar procedure.

Chemicals and apparatus

Nafion (5 wt% in low aliphatic alcohols) was purchased from DuPont, and then diluted to 0.1 wt% Nafion with ethanol. Cd(NO₃)₂,Pb(NO₃)₂, Bi(NO₃)₃, CH₃COOH,CH₃COONa were purchased from Shanghai Sinopharm Chemical Reagent Co. Ltd. Benzyl disulfide (BDS) was purchased from Aladdin Chemistry Co. Ltd. All chemicals employed in this work were of analytical reagent grade and used without any further purification. Stock solutions of Cd²⁺ and Pb²⁺ were obtained by diluting the corresponding standard stock solutions prepared with Cd(NO₃)₂ and Pb(NO₃)₂ in 1.0 wt% HNO₃, respectively. Bi (NO₃)₃ was used for the Bi film electrode (BiFE) by diluting the corresponding standard stock solution. A 0.2 M acetate buffer (pH 4.6) prepared by mixing appropriate amounts of CH₃COOH and CH₃COONa was used to prepare the solution of supporting electrolyte. Unless otherwise stated, all solutions were prepared with ultrapure water (>18 MΩ) from an AJF-1001-P system.

Electrodeposition differential pulse anodic stripping voltammetry (DPASV) and electrochemical impedance spectroscopy (EIS) were performed with a CHI 660C electrochemical workstation (CH Instrument Company). The working electrodes were electrodes modified by synthesized functional materials, and the auxiliary and reference electrodes were Pt wire and saturated calomel electrode (SCE), respectively. Fourier transform infrared (FT–IR) spectra were obtained on a Fourier Transform InfraRed spectrometer (EQUINOX 55). UV-vis detection was carried out on a Specord 50 UV-vis spectrophotometer (Germany). Thermogravimetric analyze (TGA) of sample was performed on a Pyris1 TGA thermogravimetric analyzer (Perkin-Elmer Thermal Analysis). X-ray diffraction (XRD) data was recorded with X-ray diffraction (XRD, X'Pert PRO) with Cu Kα radiation. X-ray photoelec-tron spectroscopy (XPS) analysis was carried on a VG Multilab 2000 X-ray photoelectron spectrometer. SEM images were obtained from a Hitachi S-4800 Field scanning electron microscope (FSEM). TEM images were obtained from a Tecnai G20 transmission electron microscope (TEM).

Author Contributions

P.G., F.X. and S.W. contributed equally. H.L., S.W., Y.G. and J.G. proposed, planned, and designed the project. P.G., F.X. and Q.L. performed the material preparation, characterizations, and catalytic tests. P.G., F.X., Q.L., H.L., S.W., Y.G., J.G. and Y.L. contributed to writing the manuscript.

Supplementary Material

Supplementary Information

One-Pot Microbial Method to Synthesize Dual-Doped Graphene and Its Use as High-Performance Electrocatalyst