Nanoscale Research Letters logoLink to Nanoscale Research Letters
. 2014 Mar 13;9(1):118. doi: 10.1186/1556-276X-9-118

Ni-doped TiO2 nanotubes for wide-range hydrogen sensing

Zhaohui Li 1, Dongyan Ding 1,✉, Qiang Liu 1, Congqin Ning 2, Xuewu Wang 3
PMCID: PMC3984682  PMID: 24624981

Abstract

Doping of titania nanotubes is one of the efficient way to obtain improved physical and chemical properties. Through electrochemical anodization and annealing treatment, Ni-doped TiO2 nanotube arrays were fabricated and their hydrogen sensing performance was investigated. The nanotube sensor demonstrated a good sensitivity for wide-range detection of both dilute and high-concentration hydrogen atmospheres ranging from 50 ppm to 2% H2. A temperature-dependent sensing from 25°C to 200°C was also found. Based on the experimental measurements and first-principles calculations, the electronic structure and hydrogen sensing properties of the Ni-doped TiO2 with an anatase structure were also investigated. It reveals that Ni substitution of the Ti sites could induce significant inversion of the conductivity type and effective reduction of the bandgap of anatase oxide. The calculations also reveal that the resistance change for Ni-doped anatase TiO2 with/without hydrogen absorption was closely related to the bandgap especially the Ni-induced impurity level.

Keywords: TiO2 Nanotubes, Ni doping, Hydrogen sensor, First-principles calculations

Background

There is a strong need to develop robust hydrogen sensors for use in hydrogen cars, chemical production, and spacecraft fuel cells as well as other long-term applications [1,2]. A key requirement for these sensors is the ability to selectively detect hydrogen at lower temperatures with minimal power use and weight. Due to nanostructure-enhanced sensing capability, metal oxide nanotubes have played an increasingly important role in the last few years as gas sensing materials. Oxide nanotube has become a potential candidate for the development of the targeted robust hydrogen sensors [3-5].

TiO2-based gas sensors have been widely used mainly because of their inert surface properties and the change of electrical resistance after adsorption of hydrogen [6]. As a wide bandgap semiconductor material [7,8], anatase TiO2 (Eg ≈ 3.2 eV) usually suffers from a poor electrical conductivity and resistance increase of electronic devices; therefore, anatase TiO2 oxide seems to be probably hard to become an ideal material used for hydrogen detecting. However, existing literatures have demonstrated that the above problem can be effectively addressed through using element dopants [9]. Several groups have reported that modification of TiO2 with metal/non-metal ion such as N, Cr, Pt, Nb, Co, and polyaniline [8-17] could adjust energy band to optimum values and thus high conductivity paths may be achieved. Furthermore, some theoretical calculations have been also performed to suggest that metal/non-metal ion doping in TiO2 could have significant impact on the bandgap alteration.

TiO2 doped with certain amount of Ni has been reported. Yao et al. reported that the substitution of Ti4+ ions in the anatase or rutile TiO2 lattice with a certain amount of Ni2+ could expand the optical absorption range by changing bandgaps [18]. Wisitsoraat et al. reported that TiO2 thin films doped with 0 to 10 wt.% content NiOx could have a gas-sensing capability for ethanol, acetone, and CO at 300°C [19]. Nakhate et al. used hydrothermal method to prepare Ni-TiO2 film and studied the effect of Ni doping concentration on the photoactivity for methylene blue degradation [20]. Patil et al. found that the nanostructured 2.5% Ni-doped TiO2 thin film was very sensitive to liquified petroleum gas at 250°C [21]. Park et al. reported that electronic structure of Ni-doped TiO2 oxide could have a paramagnetic ground state and Chen et al. explored the ferromagnetic mechanism of Ni-doped TiO2 by series of density functional calculations [22,23].

To date, rare works have been reported on the hydrogen sensing properties of Ni-doped TiO2 oxides except for our recent work on the fabrication of Ni-doped TiO2 nanotubes and demonstration of the nanotubes' hydrogen sensing capability at elevated temperatures [24]. Furthermore, there is no theoretical investigation on hydrogen adsorption in Ni-doped TiO2 oxide. In the present work, Ni-doped TiO2 nanotubes annealed at 525°C were fabricated for hydrogen sensing testings at both room temperature and elevated temperatures. In addition, a first-principles study on the surface adsorption models of the Ni-doped TiO2 oxide was also carried out to for a better understanding of the good hydrogen sensing capability of the Ni-doped oxide.

Methods

Materials and film fabrication

Equiatomic NiTi (nominal composition 50.8 at.% Ni) plates with a size of 15 mm × 10 mm × 1 mm were first ground and polished with #2000 SiC emery papers and then ultrasonically cleaned with absolute alcohol. Finally, they were rinsed with deionized water and further dried in a nitrogen stream. Electrochemical anodization at 30 V was carried out with a non-aqueous electrolyte of 5% ethylene glycol/glycerol containing 0.30 M (NH4)2SO4 and 0.4 M NH4F. The anodization was conducted for 90 min. The as-anodized samples were rinsed in sequence with ethanol and deionized water and dried in an air stream. They were then annealed at 525°C for 1 h in air to obtain crystallized nanotubes. Circular Pt electrodes with a thickness of 200 nm were deposited onto surfaces of the crystallized nanotube samples through sputtering. Conductive wires were connected to the Pt electrode with conductive paste. The nanotube samples (with corresponding alloy substrate) were put in a ceramic boat for further sensing test.

Characterization of nanostructure films

The phase structures of the as-annealed samples were characterized by X-ray diffraction (XRD, D/max 2,550 V). Grazing incident diffraction (GID) with an incident angle of 1° was carried out during the XRD testing. The surface morphologies of the as-anodized and as-annealed nanotube samples were examined using a scanning electron microscope (SEM; FEI SIRION 200, FEI Company, Hillsboro, OR, USA) equipped with energy dispersive X-ray (EDX; Oxford INCA, Oxford Instruments, Abingdon, Oxfordshire, UK). Surface compositions and composition distribution along the depth of the Ni-doped nanotubes were characterized with X-ray photoelectron spectroscopy (XPS; ESCALAB 250, Thermo Fisher Scientific, Hudson, NH, USA).

Analytical determinations of hydrogen sensors

A Keithley 2700 multimeter (Keithley Instruments Inc., Cleveland, OH, USA) was used to record the resistance variation of the nanotube sensor in the N2 atmospheres containing a certain concentration of hydrogen. All of the hydrogen sensing testings were carried out under laboratory condition with a room temperature of 25°C and constant humidity at 45% in air. Since N2 background atmosphere could not support a repeatable sensing response of the oxide sensor, we directly use the environmental air as the recovering atmosphere. The sensor was put on a hot plate, and the testing atmosphere was fed directly toward the sensing surface. The gas feeding tube had an outer diameter of 8 mm and the distance between the tube mouth and the sensor was 10 mm. The total flow rate of the testing atmosphere was 1 L/min. Sensor response in this paper is defined as S = (R − R0) / R0, in which R and R0 represent the resistance of the sensor in air and tested gas, respectively. A schematic diagram of the sensor structure and testing system is shown in Figure 1.

Figure 1.

Figure 1

Open in a new tab

Schematic diagram of the Ni-TiO 2 nanotube sensor and testing system.

Results

After anodization, the samples were characterized using SEM and EDX. Figure 2 presents the surface morphology of the nanotube arrays after anodic oxidation process and annealing at elevated temperatures. The anodization process resulted in the formation of aligned nanotubes with a diameter of about 30 nm and length of about 220 nm (Figure 2a,d). In comparison with the as-anodized nanotubes (Figure 2a), the tubular surface morphology of the oxide nanotubes annealed at 525°C did not change apparently (Figure 2b). This suggests that the nanotube arrays could bear such a high temperature. With an increase of the heat treatment temperature to 625°C, the top ends of nanotubes became slightly collapsed (Figure 2c), although they could still keep their tubular structures.

Figure 2.

Figure 2

Open in a new tab

SEM images of Ni-doped TiO2 nanotubes. (a) After anodization. (b) Annealed at 525°C. (c) Annealed at 625°C. (d) Cross-section image of the nanotubes annealed at 525°C.

Figure 3a presents EDX analysis of the middle part of the nanotubes annealed at 525°C. It indicates that the nanotubes consisted of three elements, i.e., Ni, Ti, and O. The atomic percentage of the Ni, Ti, and O elements in the nanotubes was 7.92%, 24.29%, and 67.79%, respectively. Figure 3b presents XRD pattern of the Ni-doped TiO2 annealed at 525°C. The 2θ of 26° and 42° corresponded to the diffraction peak of Ni-doped anatase TiO2 phase, indicating that the heat treatment at 525°C resulted in a crystallization of the amorphous nanostructures to anatase phase. The strong diffraction peaks corresponding to NiTi and Ni were also found due to the formation of thin layer (several hundreds of nanometers in thickness) of the nanotube array on alloy substrate. In comparison with undoped TiO2 nanotubes [5,7], the Ni-doped nanotubes almost had the same crystallization temperature, which suggests that the doping of Ni element did not significantly affect the amorphous-to-anatase phase transformation of the anodic oxide [25].

Figure 3.

Figure 3

Open in a new tab

The phase structure and composition analysis of the Ni-doped TiO2 nanotubes. (a) EDX analysis pattern of the as-annealed samples. (b) XRD pattern of the as-anodized samples and as-annealed samples.

Figure 4 presents XPS spectrum of the Ni-TiO2 nanotubes annealed at 525°C. The oxide nanotubes consisted of Ti, O, and Ni elements, which is in agreement with our EDX analysis. The 2p3/2 and 2p1/2 peaks in the Ti 2p spectrum (Figure 4a) are characteristic of titanium oxide. The peaks located at 458.6 and 464.4 eV are assigned to Ti 2p electrons of Ti4+ ions [18,25]. However, no peak corresponding to metallic state (Ti0) was detected. As widely reported in literatures, the most intense Ni 2p3/2 and Ni 2p1/2 peaks (located at about 852.4 and 869.7 eV, respectively) are characteristic of metallic Ni [26,27], which should be mainly attributed to the alloy substrate. In the Ni 2p3/2 region, the peak at 855.6 eV could be attributed to Ni2+ ions in an oxygen-containing environment [27]. This reveals that Ni was doped in the TiO2 lattice. The Ni dopant mainly existed as Ni2+ and bonded with O2−[28].

Figure 4.

Figure 4

Open in a new tab

XPS analysis of the Ni-doped nanotubes. (a) Ni 2p spectrum (b) Ti 2p spectrum, and (c) O 1 s spectrum.

Longitudinal composition of Ni-Ti-O oxide nanotubes was characterized by XPS with an etching depth up to 20 nm. The atomic percentage of the Ni, Ti, and O elements was 7.11%, 24.12%, and 62.97%, respectively. It could be found that the chemical compositions of the three elements only slightly varied with our EDX results. The atomic ratio of Ni and Ti elements was much lower than the original atomic ratio of the NiTi alloy substrate. Obviously, during the anodization process, Ni element could be easily corroded in the electrolyte solution.

Figure 5 shows the saturation or maximal response of the Ni-doped nanotube sensors to the hydrogen-containing atmosphere and air background at operating temperatures of 25°C, 100°C, and 200°C. In comparison with the previously reported Ni-doped TiO2 nanotubes annealed at 425°C [24], the nanotubes annealed at 525°C here could have a better hydrogen sensing capability by showing an enhanced response and there were no baseline drift phenomena. At 25°C, the nanotube sensor could only detect the atmosphere with more than 1,000 ppm hydrogen. The response increased with increase of hydrogen concentration (Figure 5a). In response to the 1,000 and 2,000 ppm dilute hydrogen atmospheres, 0.6% and 17% changes in resistance could be found, respectively. In addition, for the 2% hydrogen atmosphere, a 25% change in resistance and response time (defined as the time taken for the sensor's resistance to reach the 90% of the steady-state resistance) of 80 s could be found. The sensor could detect as low as 50 ppm hydrogen atmosphere at 100°C and 200°C (Figure 5b,c), which demonstrated a much better sensing capability than the nanotubes annealed at lower temperature.

Figure 5.

Figure 5

Open in a new tab

Response curves of the Ni-doped TiO2 sensor exposed to various hydrogen concentrations. (a) 25°C (b) 100°C, and (c) 200°C.

Figure 6 shows a temperature-dependent sensing of the Ni-doped TiO2 sensor to 1,000 ppm hydrogen atmospheres. It also found that the sensor response speed increases with the increase of temperatures.

Figure 6.

Figure 6

Open in a new tab

Response curves of Ni-doped TiO 2 sensor exposed to 1,000 ppm dilute hydrogen atmosphere at different temperatures.

At 25°C, only 0.6% change in resistance could be found for the 1,000 ppm H2 atmosphere. The response was much smaller than the response at 100°C and 200°C. A 14% change in resistance could be found at 100°C, and a 40% change in resistance at 200°C was found. Obviously, the nanotube sensor had a remarkable performance by showing a wide detection range and a quick response/recovery at elevated temperatures.

Discussion

To explore the effect of Ni doping on the bandgap and interaction of hydrogen with TiO2 oxide, the first-principles calculations were performed with the CASTEP code [29] based on density functional theory. According to Mitsui et al., hydrogen molecule adsorbed on the Pt catalyst could separate into hydrogen atoms and then diffuse to oxide nanotube [30]. The hydrogen sensing performance of TiO2-based nanotubes is dependent on the formation of a surface electron accumulation layer induced by the chemisorption of hydrogen atoms on the nanotube surface. Many research has shown that anatase TiO2 (101) is the most stable and frequently exposed surface of anatase oxide, and the diffusion of hydrogen atoms in anatase TiO2 (101) is much easier than in other crystal planes [31-33]. Therefore, in the present study, we investigate the interaction of hydrogen atom with Ni-doped anatase TiO2 (101) surface.

Based on the our XPS results, the adsorption of atomic hydrogen was simulated by placing the H atom on different surface sites in a (1 × 1) unit cell (which includes three titanium atoms, one nickel atom, and eight oxygen atoms) modeling high hydrogen coverage [31]. Spin-polarized DFT calculations were performed within the generalized gradient approximation (GGA) and the periodic plane wave approach, using the Perdew-Burke-Ernzerhof (PBE) exchange-correlation functional and ultrasoft pseudopotentials [34-36]. Bulk anatase TiO2 belongs to the tetragonal D4h19/amd space group with lattice parameters of a = 3.782 Å and c = 9.502 Å [37]. We applied the projector-augmented wave method with 3 × 3 × 1 k-point grids and cut-off energy of 380 eV, which ensures an energy convergence to within 1 to 2 meV/atom. To simulate surfaces, a vacuum region of 15 Å was embedded along the surface normal to eliminate the unwanted interaction between the slab and its period images. In different geometry optimizations of two-dimensional periodic slab, the lattice constants were fixed at these values, while the positions of all of the Ti, Ni, and O atoms were allowed to vary.

Figure 7 shows the surface sites model. The O fills either twofold (O2C) or threefold (O3C-1 and O3C-2) coordinated sites. The Ti fills fivefold (Ti5C) or sixfold (Ti6C) coordinated sites, and the Ni fills fivefold (Ni5C) or sixfold (Ni6C) coordinated sites. As for the H adsorption, seven candidate models [32] had been taken into account with the H adsorbed on Ti5C, Ti6C, Ni5C, Ni6C, O2C, and O3C-1, and O3C-2 sites. To determine the most energetically favorable model, adsorption energy (Eads), which is defined as reversible energy needed to separate an adsorption system into a Ni-doped surface (Esurf) and free hydrogen (EH), is calculated using the following equation:

Figure 7.

Figure 7

Open in a new tab

Atomic geometries of Ni-doped TiO2 (101) surface. The gray, red and blue balls represent O, Ti, and Ni atoms, respectively. O2C, O3C, Ti5C, Ti6C, Ni5C, and Ni6C mean the most probable sites for the adsorption.

ΔEads=EH+surf−Esurf−EH. (1)

where Esurf is the energy of the Ni-doped TiO2 (101) surface, EH + surf is the total energy of the adsorption model, and EH is the energy of dissociated atomic hydrogen (−12.62 eV).

The adsorption energies of the above seven calculated models for H adsorption on Ni-doped TiO2 (101) surface are shown in Table 1. Theoretically dissociated atomic hydrogen impinging on the surface from the gas phase could adsorb to any of the exposed oxygen, nickel, or titanium sites. But our simulation results indicate that in comparison with the other sites, atomic hydrogen could easily stick to the surface oxygen atoms particularly at O2C site, which is consistent with results from Islam et al. [31]. This is because the structural deformation induced by H adsorption at O2C site is more evident in comparison with the two-dimensional solid surface of Ni-doped TiO2 (101) [31]. A preferred model of the hydrogen adsorption on O2C site of Ni-doped (101) surface is shown in Figure 8.

Table 1.

Hydrogen adsorption energy for different models

Ni-TiO 2 O 2C O 3C-1 O 3C-2 Ni 5C Ni 6C Ti 5C Ti 6C
ΔEads −4.73 −3.48 −1.22 −1.77 −3.87 −3.88 −3.88
Open in a new tab

Figure 8.

Figure 8

Open in a new tab

Calculated structures of Ni-doped TiO 2 (101) surface adsorption of one dissociated hydrogen atom at O 2C site.

To investigate the doping effect of Ni on the electronic structures, the band structure was calculated by replacing one Ti site of TiO2 lattice with a Ni atom (Figure 9a). The energy zero refers to the Fermi level. Compared to the bandgap value of 2.40 eV for undoped TiO2[22,23], the remarkable feature in the energy band for the Ni-doped TiO2 was that the bandgap greatly decreased to 0.26 eV. This implies that high-concentration Ni doping in anatase TiO2 could result in a narrow bandgap and reveal metallic characteristic in comparison with the low-concentration doping system [18,19]. Therefore, the electron transfer rate in the Ni-doped oxide could be greatly enhanced and electrons could be easily excited from valence band to conduction band [38,39], which enabled better conductivity when the oxide was exposed to the hydrogen-containing atmospheres. This may be a major reason for our nanotube sensor to have improved hydrogen sensing properties at room temperature. In our work, we use Pt as the electrodes to dissociate hydrogen molecular and use a higher crystallization temperature to obtain more anatase phases. The Pt electrode and the increase of anatase phase should have also enhanced the hydrogen sensing behavior of the Ni-doped TiO2[5,7].

Figure 9.

Figure 9

Open in a new tab

Band structure of the (101) surface. (a) Before and (b) after hydrogen adsorption at Ni-doped TiO2 surfaces. The Fermi level is set to 0.

As shown in Figure 9a, the relative position of the Fermi level of Ni-doped TiO2 dramatically shifts down closer to the valance band maximum. This directly proves that the highly doped TiO2 is a p-type semiconductor [40]. These characteristics are consistent with the previous reports by Wisitsoraat and Ganesh as well as Wang et al. [19,41,42]. Generally, when a p-type semiconductor was exposed to reducing gases such as CO and H2, the reducing gases donated electrons to the valence band by reducing the number of holes and thus increasing the electrical resistance [37,43-45]. In our experiment, the resistance of the Ni-doped TiO2 nanotubes increased after exposure to hydrogen-containing atmosphere. This result well accords with our simulation result.

After H adsorption, the bandgap of the Ni-doped TiO2 further decreased to 0.088 eV (Figure 9b). It indicates that hydrogen atom could easily adsorbed in the Ni-doped TiO2 oxide to result in a smaller bandgap. This means that Ni doping could make the hydrogen adsorption easier in terms of energy. The ease of hydrogen adsorption in the Ni-doped TiO2 system would naturally lead to enhanced hydrogen sensing behavior.

The total density of states (TDOS) and partial density of states (PDOS) of the Ni-doped TiO2 oxide were calculated. Figure 10 shows DOS of the Ni-doped TiO2 (101) surface before and after hydrogen adsorption. The energy zero refers to the Fermi level. Adsorption of hydrogen resulted in a significant change of band structure. The Fermi level shifted towards low-energy direction. The Ni 3d states at the top of the valence band were greatly enhanced, and Ti 3d states at the bottom of the conduction band were slightly weakened.

Figure 10.

Figure 10

Open in a new tab

Total and partial DOS of the (101) surface. (a) Before and (b) after hydrogen adsorption at Ni-doped TiO2 surfaces.

It can be found that the top of the valence bands were dominated by the O 2p orbital, the bottom of conduction bands was dominated by the Ti 3d orbital, and the impurity band was dominated by the Ni 3d orbital [46]. In comparison with undoped anatase TiO2[10,45], one important feature of the Ni-doped system is that this oxide had an acceptor impurity level (Ni2+ inside TiO2 lattice) and half-metallic state formation before and after adsorption. As a 3d transition metal, Ni has more valence electrons than those of Ti and Ni dopants. Thus, it creates defect states in the bandgap, leading to an impurity level. In undoped or pure TiO2, the electrons usually cannot be easily excited from the valence band to the conduction band until a sufficient amount of energy is available. In Ni-doped TiO2, impurity level generated in the bandgap could give a migration pathway for the hydrogen to overcome activation barrier [30]. As a result, more electrons could be elevated to conduction band and thus lead to a higher sensitivity [37,46,47].

In our experiment, we found that the hydrogen sensing properties of the Ni-doped TiO2 nanotubes were enhanced with increase of the working temperature. This is because an increased operating temperature could accelerate the diffusivity of the hydrogen atoms into the nanotubes and thus lead to a higher sensitivity [48]. The Ni-doped TiO2 oxide was theoretically found to have favorable hydrogen-oxide interaction compared to pure TiO2 oxide. Our simulation results may shed light on better understanding of gas-sensing behaviors of various kinds of doped TiO2 oxides.

Conclusions

Ni-doped titania nanotubes with anatase-phase structures were fabricated through anodization and annealing at 525°C. The doped nanotubes were found to be sensitive to hydrogen atmospheres in the temperature range from room temperature to 200°C. A wide-range sensing of 50 ppm to 2% H2 with the robust nanotube sensor was realized. First-principles simulation of the electronic properties and hydrogen sensing behavior revealed that Ni doping played an important role in improving the hydrogen response of anatase TiO2 by narrowing the bandgap, the mechanism of which was clarified with theoretical surface models. The simulation results verified the change of the semiconductor characteristic and resistance before and after hydrogen interaction.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

ZL participated in the experiment design, carried out the experiments, tested the thin films, and wrote the manuscript. DD, LQ, CN, and WX designed the experiments and testing methods and helped to proofread the manuscript. All authors read and approved the final manuscript.

Contributor Information

Zhaohui Li, Email: lizhaohui@sjtu.edu.cn.

Dongyan Ding, Email: dyding@sjtu.edu.cn.

Qiang Liu, Email: lqshjt@sjtu.edu.cn.

Congqin Ning, Email: cqning@mail.sic.ac.cn.

Xuewu Wang, Email: wangxuew@ecust.edu.cn.

Acknowledgements

This work was supported by Shanghai Pujiang Program (No. 07pj14047). We thank the contribution from SEM lab at Instrumental Analysis Center of SJTU.

References

  1. Dresselhaus MS, Thomas IL. Energy and power. Nature. 2001;9:332–337. doi: 10.1038/35104599. [DOI] [PubMed] [Google Scholar]
  2. Higuchi T, Nakagomi S, Kokubun Y. Field effect hydrogen sensor device with simple structure based on GaN. Sens Actuators B. 2009;9:79–85. doi: 10.1016/j.snb.2009.04.031. [DOI] [Google Scholar]
  3. Lin S, Li D, Wu J, Li X, Akbar SA. A selective room temperature formaldehyde gas sensor using TiO2 nanotube arrays. Sensors Actuators B. 2011;9:505–509. doi: 10.1016/j.snb.2011.02.046. [DOI] [Google Scholar]
  4. Varghese OK, Gong D, Paulose M, Ong KG, Dickey EC, Grimes CA. Extreme changes in the electrical resistance of titania nanotubes with hydrogen exposure. Adv Mater. 2003;9:624–627. doi: 10.1002/adma.200304586. [DOI] [Google Scholar]
  5. Şennik E, Çolak Z, Kılınç N, Öztürk ZZ. Synthesis of highly ordered TiO2 nanotubes for a hydrogen sensor. Int J Hydrog Energy. 2010;9:4420–4427. doi: 10.1016/j.ijhydene.2010.01.100. [DOI] [Google Scholar]
  6. Varghese OK, Gong D, Paulose M, Ong KG, Grimes CA. Hydrogen sensing using titania nanotubes. Sens Actuator B. 2003;9:338–344. doi: 10.1016/S0925-4005(03)00222-3. [DOI] [Google Scholar]
  7. Mor GK, Varghese OK, Paulose M, Shankar K, Grimes CA. A review on highly ordered vertically oriented TiO2 nanotube arrays: fabrication, material properties, and solar energy applications. Sol Energy Mater Sol Cells. 2075;9:2011. [Google Scholar]
  8. Nikolay T, Larina L, Shevaleevskiy O, Ahn BT. Electronic structure study of lightly Nb-doped TiO2 electrode for dye-sensitized solar cells. Energy Environ Sci. 2011;9:1480–1486. doi: 10.1039/c0ee00678e. [DOI] [Google Scholar]
  9. Asahi R, Morikawa T, Ohwaki T, Aoki K, Taga Y. Visible-light photocatalysis in nitrogen-doped titanium dioxide. Science. 2001;9:269–271. doi: 10.1126/science.1061051. [DOI] [PubMed] [Google Scholar]
  10. Srivastava S, Kumar S, Singh VN, Singh M, Vijay YK. Synthesis and characterization of TiO2 doped polyaniline composites for hydrogen gas sensing. Int J Hydrog Energy. 2011;9:6343–6355. doi: 10.1016/j.ijhydene.2011.01.141. [DOI] [Google Scholar]
  11. Hong X, Wang Z, Cai W, Lu F, Zhang J, Yang Y, Ma N, Liu Y. Visible-light-activated nanoparticle photocatalyst of iodine-doped titanium dioxide. Chem Mater. 2005;9:1548–1552. doi: 10.1021/cm047891k. [DOI] [Google Scholar]
  12. Yasuhiro S, Takeo H, Makoto E. H2 sensing performance of anodically oxidized TiO2 thin films equipped with Pd electrode. Sens Actuator B. 2007;9:219–220. doi: 10.1016/j.snb.2006.09.039. [DOI] [Google Scholar]
  13. Yu JC, Yu J, Ho W, Jiang Z, Zhang L. Effects of F− doping on the photocatalytic activity and microstructures of nanocrystalline TiO2 powders. Chem Mater. 2002;9:3808–3816. doi: 10.1021/cm020027c. [DOI] [Google Scholar]
  14. Jaćimović J, Horváth E, Náfrádi R, Gaál N, Nikseresht N, Berger H, Forró L, Magrez A. From nanotubes to single crystals: Co doped TiO2. Appl Phys Lett. 2013;9:032111. [Google Scholar]
  15. Li XZ, Li FB. Study of Au/Au3+-TiO2 photocatalysts towards visible photooxidation for water and wastewater treatment. Environ Sci Technol. 2001;9:2381–2387. doi: 10.1021/es001752w. [DOI] [PubMed] [Google Scholar]
  16. Li FB, Li XZ. The enhancement of photodegradation efficiency using Pt-TiO2 catalyst. Chemosphere. 2002;9:1103–1111. doi: 10.1016/S0045-6535(02)00201-1. [DOI] [PubMed] [Google Scholar]
  17. Ghicov A, Macak JM, Tsuchiya H, Kunze J, Haeublein V, Frey L, Schmuki P. Ion implantation and annealing for an efficient N-doping of TiO2 nanotubes. Nano Lett. 2006;9:1080–1082. doi: 10.1021/nl0600979. [DOI] [Google Scholar]
  18. Yao Z, Jia F, Tian S, Li C, Jiang Z, Bai X. Microporous Ni-doped TiO2 film photocatalyst by plasma electrolytic oxidation. ACS Appl Mater Interfaces. 2010;9:2617–2622. doi: 10.1021/am100450h. [DOI] [PubMed] [Google Scholar]
  19. Wisitsoraat A, Tuantranont A, Comini E, Sberveglieri G, Wlodarski W. Characterization of n-type and p-type semiconductor gas sensors based on NiOx doped TiO2 thin films. Thin Sol Film. 2009;9:2775–2780. doi: 10.1016/j.tsf.2008.10.090. [DOI] [Google Scholar]
  20. Nakhate GG, Nikam VS, Kanade KG, Arbuj S, Kale BB, Baegc JO. Hydrothermally derived nanosized Ni-doped TiO2: a visible light driven photocatalyst for methylene blue degradation. Mater Chem Phys. 2010;9:976–981. doi: 10.1016/j.matchemphys.2010.08.007. [DOI] [Google Scholar]
  21. Patil LA, Suryawanshi DN, Pathan IG, Patil DM. Nickel doped spray pyrolyzed nanostructured TiO2 thin films for LPG gas sensing. Sens Actuator B. 2013;9:514–521. [Google Scholar]
  22. Park MS, Kwon SK, Min BI. Electronic structures of doped anatase TiO2: Ti1-xMxO2 (M = Co, Mn, Fe, Ni) Phys Rev B. 2002;9:161201. [Google Scholar]
  23. Chen J, Lu GH, Cao H, Wang T, Xu Y. Ferromagnetic mechanism in Ni-doped anatase TiO2. Appl Phys Lett. 2008;9:172504. doi: 10.1063/1.3002291. [DOI] [Google Scholar]
  24. Li Z, Ding D, Liu Q, Ning C. Hydrogen sensing with Ni-doped TiO2 nanotubes. Sensor. 2013;9:8393–8402. doi: 10.3390/s130708393. [DOI] [PMC free article] [PubMed] [Google Scholar]
  25. Chen X, Mao SS. Titanium dioxide nanomaterials: synthesis, properties, modifications, and applications. Chem Rev. 2007;9:2891–2959. doi: 10.1021/cr0500535. [DOI] [PubMed] [Google Scholar]
  26. Wu Y, Cai S, Wang D, He W, Li Y. Syntheses of water-soluble octahedral, truncated octahedral, and cubic Pt–Ni nanocrystals and their structure-activity study in model hydrogenation reactions. J Am Chem Soc. 2012;9:8975–8981. doi: 10.1021/ja302606d. [DOI] [PubMed] [Google Scholar]
  27. Pino L, Vita A, Cipiti F, Cipitì F, Laganà M, Recupero V. Catalytic performance of Ce1-xNixO2 catalysts for propane oxidative steam reforming. Catal Lett. 2008;9:121–130. doi: 10.1007/s10562-007-9357-5. [DOI] [Google Scholar]
  28. Kim DH, Chung YC, Kim YS, Lee KS, Kim SJ. Photocatalytic activity of Ni 8 wt%-doped TiO2 photocatalyst synthesized by mechanical alloying under visible light. J Am Ceram Soc. 2006;9:515–518. doi: 10.1111/j.1551-2916.2005.00782.x. [DOI] [Google Scholar]
  29. Segall MD, Lindan PLD, Probert MJ, Pickard CJ, Hasnip PJ, Clark SJ, Payne MC. First-principles simulation: ideas, illustrations and the CASTEP code. J Phys Condens Matter. 2002;9:2717–2744. doi: 10.1088/0953-8984/14/11/301. [DOI] [Google Scholar]
  30. Mitsui T, Rose MK, Fomin E, Ogletree DF, Salmeron M. Dissociative hydrogen adsorption on palladium requires aggregates of three or more vacancies. Nature. 2003;9:705–707. doi: 10.1038/nature01557. [DOI] [PubMed] [Google Scholar]
  31. Islam MM, Calatayud M, Pacchioni G. Hydrogen adsorption and diffusion on the anatase TiO2 (101) surface: a first-principles investigation. J Phys Chem C (ACS Publ) 2011;9:6809–6814. doi: 10.1021/jp200408v. [DOI] [Google Scholar]
  32. Gong XQ, Selloni A. Role of steps in the reactivity of the anatase TiO2 (101) surface. J Catal. 2007;9:134–139. doi: 10.1016/j.jcat.2007.04.011. [DOI] [Google Scholar]
  33. Selloni A, Vittadini A, Grätzel M. The adsorption of small molecules on the TiO2 anatase (101) surface by first-principles molecular dynamics. Surf Sci. 1998;9:219–222. [Google Scholar]
  34. Perdew JP, Burke K, Ernzerhof M. Generalized gradient approximation made simple. Phys Rev Lett. 1996;9:3865–3868. doi: 10.1103/PhysRevLett.77.3865. [DOI] [PubMed] [Google Scholar]
  35. Vanderbilt D. Soft self-consistent pseudopotentials in a generalized eigenvalue formalism. Phys Rev B. 1990;9:7892–7895. doi: 10.1103/PhysRevB.41.7892. [DOI] [PubMed] [Google Scholar]
  36. Pack DJ, Monkhorst JH. “Special points for Brillouin-zone integrations”–a reply. Phys Rev B. 1977;9:1748–1749. doi: 10.1103/PhysRevB.16.1748. [DOI] [Google Scholar]
  37. Burdett JK, Hughbanks T, Miller GJ, Richardson JW Jr, Smith JV. Structural–electronic relationships in inorganic solids: powder neutron diffraction studies of the rutile and anatase polymorphs of titanium dioxide at 15 and 295 K. J Am Chem Soc. 1987;9:3639–3646. doi: 10.1021/ja00246a021. [DOI] [Google Scholar]
  38. Huang Y, Rettner CT, Auerbach DJ, Wodtke AM. Vibrational promotion of electron transfer. Science. 2000;9:111–114. doi: 10.1126/science.290.5489.111. [DOI] [PubMed] [Google Scholar]
  39. Linsebigler AL, Lu G, Yates JT. Photocatalysis on TiO2 surfaces: principles, mechanisms, and selected results. Chem Rev. 1995;9:735–738. doi: 10.1021/cr00035a013. [DOI] [Google Scholar]
  40. Kim KK, Bae JJ, Park HK, Kim SM, Geng HZ, Park KA. Fermi level engineering of single-walled carbon nanotubes by AuCl3 doping. J Am Chem Soc. 2008;9:12757–12761. doi: 10.1021/ja8038689. [DOI] [PubMed] [Google Scholar]
  41. Ganesh I, Gupta AK, Kumar PP, Sekhar PSC, Radha K, Padmanabham G, Sundararajan G. Preparation and characterization of Ni-doped TiO2 materials for photocurrent and photocatalytic applications. Sci World J. 2012;9:1–2016. doi: 10.1100/2012/127326. [DOI] [PMC free article] [PubMed] [Google Scholar]
  42. Wang Y, Hao Y, Cheng H, Ma J, Xu B, Li W, Cai S. The photoelectrochemistry of transition metal-ion-doped TiO2 nanocrystalline electrodes and higher solar cell conversion efficiency based on Zn2+-doped TiO2 electrode. J Mater Sci. 1999;9:2773–2779. doi: 10.1023/A:1004658629133. [DOI] [Google Scholar]
  43. Chris G, de Walle V. Hydrogen as a cause of doping in zinc oxide. Phys Rev Lett. 2000;9:1012–1015. doi: 10.1103/PhysRevLett.85.1012. [DOI] [PubMed] [Google Scholar]
  44. Batzill M, Diebold U. The surface and materials science of tin oxide. Prog Surf Sci. 2005;9:47–154. doi: 10.1016/j.progsurf.2005.09.002. [DOI] [Google Scholar]
  45. Coey JMD, Venkatesan M, Fitzgerald CB. Donor impurity band exchange in dilute ferromagnetic oxides. Nat Mater. 2005;9:173–179. doi: 10.1038/nmat1310. [DOI] [PubMed] [Google Scholar]
  46. Ma X, Wu Y, Lu Y, Xu J, Wang Y, Zhu Y. Effect of compensated codoping on the photoelectrochemical properties of anatase TiO2 Photocatalyst. J Phys Chem C (ACS Publ) 2011;9:16963–16969. doi: 10.1021/jp202750w. [DOI] [Google Scholar]
  47. Diebold U. The surface science of titanium dioxide. Surf Sci Rep. 2003;9:53–229. doi: 10.1016/S0167-5729(02)00100-0. [DOI] [Google Scholar]
  48. Liu H, Ding D, Ning C, Li Z. Wide-range hydrogen sensing with Nb-doped TiO2 nanotubes. Nanotechnology. 2012;9:015502. doi: 10.1088/0957-4484/23/1/015502. [DOI] [PubMed] [Google Scholar]