Journal of Applied Oral Science logoLink to Journal of Applied Oral Science
. 2009 Jun;17(3):184–189. doi: 10.1590/S1678-77572009000300010

EFFECT OF AN ADDITIONAL HYDROPHILIC VERSUS HYDROPHOBIC COAT ON THE QUALITY OF DENTINAL SEALING PROVIDED BY TWO-STEP ETCH-AND-RINSE ADHESIVES

Safira Marques de Andrade Silva 1, Marcela Rocha de Oliveira Carrilho 2,✉, Luiz Marquezini Junior 3, Fernanda Cristina Pimentel Garcia 4, Adriana Pigozzo Manso 5, Marcelo Corrêa Alves 6, Ricardo Marins de Carvalho 7
PMCID: PMC4399529  PMID: 19466248

Abstract

Objective:

To test the hypothesis that the quality of the dentinal sealing provided by two-step etch-and-rinse adhesives cannot be altered by the addition of an extra layer of the respective adhesive or the application of a more hydrophobic, non-solvated resin.

Material and Methods:

full-crown preparations were acid-etched with phosphoric acid for 15 s and bonded with Adper Single Bond (3M ESPE), Excite DSC (Ivoclar/Vivadent) or Prime & Bond NT (Dentsply). The adhesives were used according to the manufacturers' instructions (control groups) or after application to dentin they were a) covered with an extra coat of each respective system or b) coated with a non-solvated bonding agent (Adper Scotchbond Multi-Purpose Adhesive, 3M ESPE). Fluid flow rate was measured before and after dentin surfaces were acid-etched and bonded with adhesives.

Results:

None of the adhesives or experimental treatments was capable to block completely the fluid transudation across the treated dentin. Application of an extra coat of the adhesive did not reduce the fluid flow rate of adhesive-bonded dentin (p>0.05). Conversely, the application of a more hydrophobic non-solvated resin resulted in significant reductions in the fluid flow rate (p<0.05) for all tested adhesives.

Conclusions:

The quality of the dentinal sealing provided by etch-and-rinse adhesives can be significantly improved by the application of a more hydrophobic, non-solvated bonding agent.

Keywords: Adhesives permeability, Dentinal sealing, Hydrophobic coating

INTRODUCTION

In adhesive dentistry the concept of clinical progress has been often earmarked by procedural simplification. Classical multi-step adhesives have been, increasingly, replaced by simplified "single-step" systems that are, apparently, simpler and faster to use. Simplification of contemporary dental adhesives has occurred, however, at the expenses of an increasing incorporation of hydrophilic monomers (i.e. HEMA, BPDM, MDP, Phenyl-P). Not coincidentally, these contemporary hydrophilic adhesives have shown to draw water from hydrated dentin through an apparently intact, polymerized adhesive layer7,11,24. If the dentinal fluid passes through the adhesive, it may accumulate on its own surface, thereby interfering with coupling to the resin composites4,27. Thus, instead of creating a perfect sealing of dentin, polymerized hydrophilic adhesives actually behave as permeable membranes that potentially allow outward and inward fluid flow4,6,7,10,11,24,27.

Deficient sealing of dentin may be analysed from several perspectives. One can argue that placing adhesive comonomer mixtures in an inhospitable environment such as the water-wet acid-etched dentin will inexorably result in the formation of porous polymers that are prone to absorb water 9,15. Conversely, the use of more hydrophobic, less permeable resins such as the dentin bonding adhesives may supposedly prevent this problem and further improve the durability of resin-dentin bonds, because these materials tend to exhibit much lower ability to absorb water 15. However, the use of hydrophobic monomers as bonding agents to dentin is not effective yet as they are not miscible to acid-etched dentin that is intentionally saturated with water 3,20.

While the water-wet bonding technique 13 is not modified to permit hydrophobic adhesives to be coaxed into acid-etched dentin, the intrinsic permeability of two-step etch-and-rinse adhesives24,25 should be minimized, which is thought to be important in prolonging the integrity of the resultant resin-dentin bonds. Studies have demonstrated that three-step etch-and-rinse adhesives and two-step self-etching systems, which deliberately indicate the application of multiple coats of their primer solution and/or a coat of a more hydrophobic resin over the hybridized dentin, seem to constitute overlying adhesive layers and hybrid layers that are naturally less permeable than those formed when using the most simplified, "single-step" systems5,6,7. Thus, the objective of this study was to evaluate whether the ability of two-step etch-and-rinse adhesives to seal dentin may be changed when these systems are covered with an extra coat of the same two-step etch-and-rinse system or a coat of a more hydrophobic non-solvated bonding agent. The null hypotheses tested were that the quality of the dentinal sealing provided by two-step etch-and-rinse adhesives cannot be altered by the application of: 1) an extra coat of the respective two-step etch-and-rinse system or 2) a coat of a more hydrophobic, non-solvated bonding agent.

MATERIAL AND METHODS

Teeth Preparation

Fifty-four non-carious human third molars extracted for orthodontics reasons were collected after the patients' informed consent had been obtained under a protocol reviewed and approved by the Human Research Ethics Committee of the Bauru School of Dentistry, University of São Paulo. These teeth were stored in saline containing 1% thymol at 4°C and used within no longer than 6 months after extraction.

Crown preparations with chamfer margins located on the cementum/enamel junction (CEJ) were performed in the extracted teeth with diamond burs under copious air-spray (4137 KG Sorensen, Barueri, SP, Brazil). From prepared teeth, crown-segments were further obtained by transversally sectioning the teeth roots at 2 mm below the CEJ using a slow-speed diamond saw (IMPTECH PC 10, Boksburg, Republic of South Africa), under water cooling. The pulp tissue was carefully removed with a pair of small forceps. Care was taken to avoid touching the pulp chamber walls for consequently not crushing the predentine toward the dentinal tubules, which could alter the final permeability of dentin (Dr. David Pashley, personal communication). The resulting crown-segments were glued to Plexiglass slabs using a viscous cyanoacrylate (Zapit, Dental Ventures of American, Corona, CA, USA), which also covered the entire peripheral cementum. Each Plexiglass slab was penetrated by a short length of 18-gauge stainless steel tubing, which ended flush with the top of the Plexiglass slab. This tube permitted the pulp chamber to be filled with water and to be connected to an automated flow-recording device (Flodec System, De Marco Engineering, Geneva, Switzerland) (Figure 1).

FIGURE 1. Schematic presentation of the fluid-filtration apparatus used to perform repeated measurements of the permeability of dentin surfaces after acid-etching and after resin-bonding.

FIGURE 1

Open in a new tab

Bonding Procedures

Three two-step etch-and-rinse adhesives were evaluated in this study: Adper Single Bond (SB - 3M ESPE, St. Paul, MN, USA), Excite DSC (EX – Ivoclar/Vivadent, Schaan, Liechtenstein) and Prime & Bond NT (PB - Dentsply DeTrey, Konstanz, Germany) (Table 1).

TABLE 1. Composition, manufacturers' instructions and batch number of the adhesives used in this study.

Adhesivess Composition Manufacturers' recommended protocol Batch number
Excite HEMA, phosphoric acid, acrylate, (Bis GMA), dimethacrylate, highly dispersed silica, catalysts, stabilizers, ethanol Apply a generous amount of Excite. Gently agitate the adhesive for at least 10 s. Dry gently for 1-3 s. Cure for 10 s. E30108
Adper Single Bond HEMA, BisGMA, dimethacrylate, copolymer with methacrylic function, polyacrylic & polyitaconic acids, photoinitiators, water and ethanol Apply 2 consecutive coats of Single Bond, dry gently for 2-5 s. Cure for 10 s. 3HW
Prime & Bond NT Resin di and tri methacrylate, amorphous functional silica, PENTA, cetylamine hydrofluoride, photoinitiators, stabilizers, acetone Apply 3 consecutive coats of Prime & Bond NT. This surface should remain fully wet for 20 s. Gently dry with air for at least 5 s. Cure adhesive for 10 s. 534320
Adper Scotchbond Multi Purpose Adhesive Bis-GMA, HEMA, initiators Apply adhesive and light cure for 10 s. 5PH
Open in a new tab

The crown-segments were randomly divided into nine groups of six specimens each (n=6), corresponding to the three adhesives applied in three different conditions: 1) according to the manufacturers' instructions (controls); 2) with an additional coat of the respective adhesive and 3) with a coat of a more hydrophobic non-solvated resin bonding agent (Adper Scotchbond Multi-Purpose Adhesive, 3M ESPE).

During the bonding procedures, the hydrostatic pressure in the pulp chamber was null (0 cm H2O) in order to avoid excessive fluid contamination of the bonding area 10. The extra coat of the respective two-step etch-and-rinse adhesive (i.e. SB, EX or PB) or the more hydrophobic adhesive (i.e. Adper Scotchbond Multi-Purpose Adhesive) was always added right after the tested adhesives had been applied according to manufacturers' instructions. All dentin surfaces were checked to ensure complete covering with adhesives before the photo-activation was performed. Adhesives were, then, photo-cured for 10s with a light intensity of 500mW/cm2 (Degulux Soft-start, DEGUSSA HÜLS).

Fluid Flow Measurement

An in vitro fluid transport model was used to measure the fluid conductance induced by hydrostatic pressure, following the general guidelines reported by Pashley and Depew 19 (Figure 1). Each crown-segment was connected via polyethylene tubing to the Flodec device (Flodec System, De Marco Engineering, Geneva, Switzerland) under a constant physiological hydrostatic pressure (20 cm H2O)8. A pressure gradient between the water reservoir and the specimen induced fluid movement through the specimen. The rate of fluid movement was measured by following the displacement of a tiny air bubble that was introduced into a glass capillary located between the water reservoir and the specimen. Displacement of the air bubble was detected via a laser diode incorporated in the Flodec device. The linear displacement was automatically converted to fluid flow (μL min-1) via the computer software program. The rate fluid flow across dentin was measured two times, sequentially, as follows: 1) after the dentin surface was acid-etched with 35% phosphoric acid gel (3M ESPE) for 15 s for the determination of maximum baseline conductance, and 2) after dentin was hybridized following one of the described bonding procedures. All fluid flow measurements were made with the specimen immersed in water to minimize interferences derived from evaporative water fluxes14. For each specimen, the fluid flow (μL.min-1) across the adhesive-bonded dentin was expressed as a percentage of the maximum permeability derived from the acid-etched dentin (assigned as 100%). This allowed each specimen to serve as its own control, since the same surface area was used in all two measurements6,18.

Statistical Analysis

The percentage fluid flow across the adhesive-bonded dentin for control and experimental groups were analyzed by a two-way ANOVA, having as main factors: the adhesives (i.e. SB, EX and PB) and the experimental dentin treatments (i.e. adhesives application according to manufacturers' instructions, with an extra coat of the respective adhesive or with a coat of a more hydrophobic resin). Post hoc multiple comparisons were performed using Tukey's tests. Statistical significance was preset at α = 0.05

RESULTS

Fluid conductance results expressed as percentages of the maximum permeability that occurred in the baseline acid-etched dentin are summarized in table 2. None of the adhesives or experimental bonding treatments was able to interrupt completely the transudation of fluid across the adhesive-bonded interface. Reduction in the fluid conductance of acid-etched dentin after adhesives/treatment application was in the range of 53% to 78%. Regardless of the adhesive system, the application of an extra coat of the respective two-step etch-and-rinse system did not reduce significantly the fluid conductance of dentin when compared to that exhibited by the control groups (p>0.05). Conversely, the application of a relatively more hydrophobic nonsolvated bonding resin reduced significantly the fluid conductance of dentin (p<0.05), irrespectively to the applied adhesive.

TABLE 2. Fluid flow (in percentage) across bonded-dentin when using two-step etch-and-rinse adhesives that were applied as recommended by manufacturers (controls) or coated with an extra coat of the respective two-step etch-and-rinse adhesive or with a more hydrophobic bonding resin.

TREATMENTS
Adhesives Manufacturers' recommendation Extra coat of the respective adhesive Coat of a hydrophobic resin
SB 38 ± 14 A 45 ± 11 A 22 ± 9 B
EX 47 ± 9 A 41 ± 15 A 27 ± 10 B
PB 39 ± 13 A 38 ± 19 A 32 ± 14 B
Open in a new tab

Values (Mean ± SD) are expressed as a percentage of the maximum permeability (acid-etched dentin). Groups identified by different letters were statically different (p<0.05).

DISCUSSION

The present results indicated the application of an extra coat of the respective two-step adhesive did not reduce the fluid flow across the adhesive-bonded dentin and, thus, did not improve the quality of dentinal sealing. Nevertheless, the simulated conversion of two-step etch-and-rinse adhesives into three-step adhesives, by applying a relatively hydrophobic bonding agent over the primed dentin, significantly reduced the fluid flow across adhesive-bonded interfaces, thereby improving the quality of dentinal sealing. In concert, these results determine the rejection of the first anticipated hypothesis and the acceptance of the second anticipated hypothesis.

Ideally, the dental adhesives should render dentin impermeable, or at least they should reproduce the natural permeability of dentin when this is covered with enamel and/or cementum. However, our results showed that even the most effective treatment used for blocking fluid transudation across the adhesive-bonded dentin (i.e. adhesive + hydrophobic resin) was not able to seal perfectly the dentin. Actually, several previous studies have reported the deficient ability of dental adhesives to keep dentin perfectly sealed 2,6,7. In addition, some of these studies showed that the smear layer/smear plugs formed in dentin as a result of the operative procedures may be, at short-terms, more effective in sealing the dentinal tubules than the majority of the current dental adhesives 3,18,19. This suggests that an impervious dentinal sealing may not be easily achieved if bonding procedures are performed after the removal of smear layer/smear plugs by either acid etchants or calcium-chelant agents 3,10,29. Supposedly, at short-terms, the channels/pathways around the resin tags or the overlying adhesive layer seem to offer less resistance to water movement than do the contiguous channels through the smear plugs/smear layer complex 3. According to our previous findings, the resin tags seem not to hybridize perfectly with the surrounding water-filled interfibrillar spaces 26.

Dentinal tubules that become freely unobstructed by the acid etching can readily permit the transudation of dentinal fluid from the pulp toward the surface. Whenever this dentinal fluid transudation occurs, that is, during the infiltration of hydrophilic adhesives11 or after adhesive polymerization7,24, it may create nanoleakage channels within adhesives25 by inducing phase separation of adhesive components 23, interfering with resin monomers conversion12,23 and resin polymers crosslinking, frequently permitting the elution of residual monomers from the polymerized adhesive 9. Depending on the number and density of these channels and porosities, they may account for a significant increase in the hole-free volume of dental adhesives, which in turn is thought to be intimately related with the extent and rate of water diffusion in these polymeric materials 15. If the dentinal fluid passes through the adhesive, it will accumulate on top of hybrid layer and interfere with coupling to resin composites 4,11. Nanoleakage channels reported for most of adhesives 27,31 are, therefore, not only an evidence of material permeability and corrosion, but also a virtual sign of the inability of these adhesives to provide a perfect sealing to dentin.

Deficient sealing of dentin can be also analyzed from the perspective of adhesives polarity 7,14. The two-step etch-and-rinse adhesives used in this study are basically composed of highly hydrophilic monomers (i.e, HEMA, PENTA). Studies on the kinetics of water diffusion have shown a positive correlation between the magnitude of water sorption and the degree of hydrophilicity of experimental adhesives 15. It is suggested that the absorbed water may form hydrogen bonds with the hydrophilic and ionic domains (i.e. hydroxyl, carboxyl and phosphate groups) present in these hydrophilic adhesives28. The water molecules that attach to the polymer chain via hydrogen bonding, referred as "bound" molecules, it is thought to disrupt the interchain hydrogen bonding, induce swelling, and plasticize the polymer1. Thus, while it is alarming, it is not surprising to notice that an additional coat of the two-step etch-and-rinse adhesives was not enough to prevent fluid transudation across adhesive-bonded dentin. In fact, in a recent study on the water permeation through multiple layers of organic resin coatings, Nguyen and co-workers16 observed that by increasing the number of coats of a hydrophilic resin can only extend the required time for water to permeate completely these coatings, but it did not impede water to move across them.

Clearly, the present results indicated that the permeability of two-step etch-and-rinse dental adhesives can be reduced if they are coated with a resin relatively more hydrophobic. The bonding agent of the Adper Scotchbond Multi-Purpose is based not only on HEMA, but on Bis-GMA (60-70% - 3M ESPE Technical Profile) and its application over the tested two-step etch-and-rinse adhesives not only increased the time necessary for water to permeate the bonded interfaces, but it may also reduce the percentage of fluid transudation across such interfaces, thereby improving the acid-etched dentin sealing. Undoubtedly, this result corroborates with the notion that three-step etch-and-rinse adhesives, which recommend a separate application of a bonding agent composed of hydrophobic and crosslinking monomers to the primed tooth surface, produce resin-dentin bonds that are more durable than those formed with two-step etch-and-rinse ones29. Again, the trend to simplification of adhesives showed to be incompatible with a good dentinal sealing.

Although Bis-GMA forms a polymeric backbone is relatively more hydrophobic, less prone to absorb water than do the highly hydrophilic monomers such as HEMA, PENTA, BPDM, Phenyl-P and others16; neither Bis-GMA nor its derivatives co-momonors (i.e. Bis-GMA-E) and other more hydrophobic monomers (i.e.UDMA) used in dentistry exhibit functional groups (i.e. hydroxyls) that are prone to form hydrogen-bond with water molecules22, thereby being able to absorb and retain in their resultant polymers a certain amount of water9. This could explain why the application of the bonding agent of the Adper Scotchbond Multi-Purpose cannot completely annul the permeability of bonded dentin6,15. In fact, the first in vitro study that quantified fluid movement across dentin before and after adhesive bonding showed that the application of Adper Scotchbond MultiPurpose to acid-etched dentin, followed by a 2-mm thick layer of resin composite (Z350, 3M ESPE) did not reduce completely the permeability of dentin, allowing a residual hydraulic conductance of 17% 2. Since in the present study we did not apply a resin composite over the bonded dentin, we speculate that the residual fluid movement observed for the groups wherein Adper Scotchbond Multi-Purpose was applied (22-32%; Table 2) would indirectly correspond to the maximum capacity of this material to reduce the permeability of the acid-etched dentin that has been previously primed with a more hydrophilic, two-step etch-and-rinse adhesive system.

Recently, it has been pointed out that the defective dentinal sealing and fluid conductance across resin-bonded dentin may be significantly affected by the solvent used to saturate the acid-etched dentin20. The high permeability of dental adhesives bonded to water-saturated dentin (i.e. water-wet bonding technique) probably occur at the expense of a sub-optimal resin infiltration into collagen interfibrillar spaces, both within the intertubular dentin and the circumferential dentin surrounding resin tags3. Accordingly, the combined use of water-wet bonding technique and hydrophilic resins compromise the requirements for perfect sealing and durable coupling between resin composites and adhesive-bonded dentin3. Thus, the development of a bonding technique that combines the use of hydrophobic resins applied to acid-etched dentin that is saturated with an anhydrous solvent, such as ethanol, could be effective to alleviate the water sorption seen in dentin bonded with hydrophilic simplified adhesives21. Application of hydrophobic experimental dental adhesives to ethanol-saturated dentin has shown strong evidences of reduction in bonded dentin permeability and 3 improvements in the durability of resin-dentin bonds17. While it is a promising clinical approach, additional investigations on the performance and technique sensitivity of ethanol-wet bonding technique associated with hydrophobic adhesives are undoubtedly necessary.

ACKNOWLEDGEMENTS

This manuscript is in partial fulfillment of requirements for the PhD degree for Safira de Marques de Andrade e Silva, Dental School of Piracicaba, University of Campinas, Brazil. This study was supported by grants CNPq (#474226/03-4, 305300/04-0 - P.I. Ricardo Carvalho and #300615/2007-8, 473164/2007-8 - P.I. Marcela Carrilho) FAPESP (#03/11721-9, 03/04672-1 - P.I. Safira Silva).

REFERENCES

  • 1.Adamson MJ. Thermal expansion and swelling of cured epoxy resin used in graphite/epoxy composite materials. J Mater Sci. 1980;15:1736–1745. [Google Scholar]
  • 2.Bouillaguet S, Duroux B, Ciucchi B, Sano H. Ability of adhesive systems to seal dentin surfaces: an in vitro study. J Adhes Dent. 2000;2(3):201–208. [PubMed] [Google Scholar]
  • 3.Carrilho MR, Tay FR, Sword J, Donnelly AM, Agee K, Nishitani Y, et al. Dentin sealing provided by smear layer/smear plugs versus adhesive resins/resin tags. Eur J Oral Sci. 2007;115(4):321–329. doi: 10.1111/j.1600-0722.2007.00465.x. [DOI] [PubMed] [Google Scholar]
  • 4.Carvalho RM, Pegoraro TA, Tay FR, Pegoraro LF, Silva NR, Pashley DH. Adhesive permeability affects coupling of resin cements that utilize self-etching primers to dentine. J Dent. 2004;32(1):55–65. doi: 10.1016/j.jdent.2003.08.003. [DOI] [PubMed] [Google Scholar]
  • 5.Cheong C, King NM, Pashley DH, Ferrari M, Toledano M, Tay FR. Incompatibility of self-etch adhesives with chemical/dual-cured composites: two-step vs one-step systems. Oper Dent. 2003;28(6):747–755. [PubMed] [Google Scholar]
  • 6.Chersoni S, Acquaviva GL, Prati C, Ferrari M, Grandini S, Pashley DH, et al. In vivo fluid movement through dentin adhesives in endodontically treated teeth. J Dent Res. 2005;84(3):223–227. doi: 10.1177/154405910508400303. [DOI] [PubMed] [Google Scholar]
  • 7.Chersoni S, Suppa P, Grandini S, Goracci C, Monticelli F, Yiu C, et al. In vivo and in vitro permeability of one-step self-etch adhesives. J Dent Res. 2004;83(6):459–464. doi: 10.1177/154405910408300605. [DOI] [PubMed] [Google Scholar]
  • 8.Ciucchi B, Bouillaguet S, Holz J, Pashley D. Dentinal fluid dynamics in human teeth, in vivo. J Endod. 1995;21(4):191–194. doi: 10.1016/S0099-2399(06)80564-9. [DOI] [PubMed] [Google Scholar]
  • 9.Ferracane JL. Hygroscopic and hydrolytic effects in dental polymer networks. Dent Mater. 2006;22(3):211–222. doi: 10.1016/j.dental.2005.05.005. [DOI] [PubMed] [Google Scholar]
  • 10.Hashimoto M, Ito S, Tay FR, Svizero NR, Sano H, Kaga M, et al. Fluid movement across the resin-dentin interface during and after bonding. J Dent Res. 2004;83(11):843–848. doi: 10.1177/154405910408301104. [DOI] [PubMed] [Google Scholar]
  • 11.Itthagarun A, Tay FR. Self-contamination of deep dentin by dentin fluid. Am J Dent. 2000;13(4):195–200. [PubMed] [Google Scholar]
  • 12.Jacobsen T, Soderholm KJ. Some effects of water on dentin bonding. Dent Mater. 1995;11(2):132–136. doi: 10.1016/0109-5641(95)80048-4. [DOI] [PubMed] [Google Scholar]
  • 13.Kanca J., 3rd Effect of resin primer solvents and surface wetness on resin composite bond strength to dentin. Am J Dent. 1992;5(4):213–215. [PubMed] [Google Scholar]
  • 14.King NM, Tay FR, Pashley DH, Hashimoto M, Ito S, Brackett WW, et al. Conversion of one-step to two-step self-etch adhesives for improved efficacy and extended application. Am J Dent. 2005;18(2):126–134. [PubMed] [Google Scholar]
  • 15.Malacarne J, Carvalho RM, Goes MF, Svizero N, Pashley DH, Tay FR, et al. Water sorption/solubility of dental adhesive resins. Dent Mater. 2006;22(10):973–980. doi: 10.1016/j.dental.2005.11.020. [DOI] [PubMed] [Google Scholar]
  • 16.Nguyen T, Byrd E, Bentz D, Lin CJ. In situ measurement of water at the organic coating/substrate interface. Proc Org Coat. 1996;27:181–193. [Google Scholar]
  • 17.Nishitani Y, Yoshiyama M, Donnelly AM, Agee KA, Sword J, Tay FR, et al. Effects of resin hydrophilicity on dentin bond strength. J Dent Res. 2006;85(11):1016–1021. doi: 10.1177/154405910608501108. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 18.Pashley DH, Carvalho RM, Pereira JC, Villanueva R, Tay FR. The use of oxalate to reduce dentin permeability under adhesive restorations. Am J Dent. 2001;14(2):89–94. [PubMed] [Google Scholar]
  • 19.Pashley DH, Depew DD. Effects of the smear layer, Copalite, and oxalate on microleakage. Oper Dent. 1986;11(3):95–102. [PubMed] [Google Scholar]
  • 20.Pashley DH, Tay FR, Carvalho RM, Rueggeberg FA, Agee KA, Carrilho M, et al. From dry bonding to water-wet bonding to ethanol-wet bonding. A review of the interactions between dentin matrix and solvated resins using a macromodel of the hybrid layer. Am J Dent. 2007;20(1):7–20. [PubMed] [Google Scholar]
  • 21.Sadek FT, Pashley DH, Ferrari M, Tay FR. Tubular occlusion optimizes bonding of hydrophobic resins to dentin. J Dent Res. 2007;86(6):524–528. doi: 10.1177/154405910708600607. [DOI] [PubMed] [Google Scholar]
  • 22.Santerre JP, Shajii L, Leung BW. Relation of dental composite formulations to their degradation and the release of hydrolyzed polymeric-resin-derived products. Crit Rev Oral Biol Med. 2001;12(2):136–151. doi: 10.1177/10454411010120020401. [DOI] [PubMed] [Google Scholar]
  • 23.Spencer P, Wang Y. Adhesive phase separation at the dentin interface under wet bonding conditions. J Biomed Mater Res. 2002;62(3):447–456. doi: 10.1002/jbm.10364. [DOI] [PubMed] [Google Scholar]
  • 24.Tay FR, Frakenberger R, Kreijci I, Bouillaguet S, Pashley DH, Carvalho RM, et al. Single-bottle adhesives behave as permeable membranes after polymerization. I. In vivo evidence. J Dent. 2004;32:611–621. doi: 10.1016/j.jdent.2004.04.006. [DOI] [PubMed] [Google Scholar]
  • 25.Tay FR, Pashley DH. Water treeing-a potential mechanism for degradation of dentin adhesives. Am J Dent. 2003;16(1):6–12. [PubMed] [Google Scholar]
  • 26.Tay FR, Pashley DH, Kapur RR, Carrilho MR, Hur YB, Garrett LV, et al. Bonding BisGMA to dentin-a proof of concept for hydrophobic dentin bonding. J Dent Res. 2007;86(11):1034–1039. doi: 10.1177/154405910708601103. [DOI] [PubMed] [Google Scholar]
  • 27.Tay FR, Suh BI, Pashley DH, Prati C, Chuang SF, Li F. Factors contributing to the incompatibility between simplified-step adhesives and self-cured or dual-cured composites. Part II. Single-bottle, total-etch adhesive. J Adhes Dent. 2003;5(4):91–105. [PubMed] [Google Scholar]
  • 28.Van Landuyt KL, Snauwaert J, De Munck J, Coutinho E, Poitevin A, Yoshida Y, et al. Origin of interfacial droplets with one-step adhesives. J Dent Res. 2007;86(8):739–744. doi: 10.1177/154405910708600810. [DOI] [PubMed] [Google Scholar]
  • 29.Van Meerbeek B, De Munck J, Yoshida Y, Inoue S, Vargas M, Vijay P, et al. Buonocore memorial lecture. Adhesion to enamel and dentin: current status and future challenges. Oper Dent. 2003;28(3):215–235. [PubMed] [Google Scholar]
  • 30.Yiu CK, Pashley EL, Hiraishi N, King NM, Goracci C, Ferrari M, et al. Solvent and water retention in dental adhesive blends after evaporation. Biomaterials. 2005;26(34):6863–6872. doi: 10.1016/j.biomaterials.2005.05.011. [DOI] [PubMed] [Google Scholar]
  • 31.Yoshida E, Uno S, Nodasaka Y, Kaga M, Hirano S. Relationship between water status in dentin and interfacial morphology in all-in-one adhesives. Dent Mater. 2007;23(5):556–560. doi: 10.1016/j.dental.2006.03.014. [DOI] [PubMed] [Google Scholar]

Articles from Journal of Applied Oral Science are provided here courtesy of Bauru School of Dentistry