Synthesis, characterization, and immune efficacy of layered double hydroxide@SiO₂ nanoparticles with shell-core structure as a delivery carrier for Newcastle disease virus DNA vaccine

Abstract

Layered double hydroxide (LDH)@SiO₂ nanoparticles were developed as a delivery carrier for the plasmid DNA expressing the Newcastle disease virus F gene. The LDH was hydrotalcite-like materials. The plasmid DNA encapsulated in the LDH@SiO₂ nanoparticles (pFDNA-LDH@SiO₂-NPs) was prepared by the coprecipitation method, and the properties of pFDNA-LDH@SiO₂-NPs were characterized by transmission electron microscopy, zeta potential analyzer, Fourier transform infrared spectroscopy, and X-ray diffraction analysis. The results demonstrated that the pFDNA-LDH@SiO₂-NPs had a regular morphology and high stability with a mean diameter of 371.93 nm, loading capacity of 39.66%±0.45%, and a zeta potential of +31.63 mV. A release assay in vitro showed that up to 91.36% of the total plasmid DNA could be sustainably released from the pFDNA-LDH@SiO₂-NPs within 288 hours. The LDH@SiO₂ nanoparticles had very low toxicity. Additionally, their high transfection efficiency in vitro was detected by fluorescent microscopy. Intranasal immunization of specific pathogen-free chickens with pFDNA-LDH@SiO₂-NPs induced stronger cellular, humoral, and mucosal immune responses and achieved a greater sustained release effect than intramuscular naked plasmid DNA, and the protective efficacy after challenge with the strain F₄₈E₉ with highly virulent (mean death time of chicken embryos ≤60 hours, intracerebral pathogenicity index in 1 -day-old chickens >1.6) was 100%. Based on the results, LDH@SiO₂ nanoparticles can be used as a delivery carrier for mucosal immunity of Newcastle disease DNA vaccine, and have great application potential in the future.

Introduction

Newcastle disease (ND) is a highly pathogenic viral disease of avian species.¹ The disease continues to negatively impact poultry producers by infecting birds worldwide.² The causative agent of ND is an ND virus (NDV).³ All strains of NDV belong to the family Paramyxoviridae and consist of single-stranded, non-segmented, and negative-sense RNA genomes. NDV has six genes that produce six structural proteins, ie, fusion (F), hemagglutinin-neuraminidase (HN), RNA-dependent RNA (large) polymerase (L), nucleocapsid (N), phosphoprotein (P), and the matrix (M).⁴ The F protein is supposed to play a major role in the virulence of NDV strains. It allows the binding and fusion of NDV to the host cell membrane, enabling the virus to enter host cells and induces immunity.⁵

Currently, vaccine immunization is still an effective way to resist NDV infection. The NDV-attenuated live vaccines and inactivated vaccines have played an important role in prevention and control of ND. However, these conventional vaccines have several disadvantages, such as poor immunogenicity, partial virus toxicity reservation, and induction of respiratory pathological changes. DNA vaccination was supposed to be a promising strategy for activating immune responses against NDV infection.⁶ Since the discovery of gene immunization in 1990, genes from different viruses have been delivered into animals, showing satisfactory effects.^7,8 Therefore, DNA vaccines have become popular in the field. The plasmid carrier used in construction of a DNA vaccine should replicate in Escherichia coli in high copy and express the gene efficiently within the animal body. Currently, DNA vaccines are administered in the form of either aqueous solutions or lyophilized powders. However, because of their high hydrophilicity and therefore a low distribution coefficient between oil and water phases,^9,10 it is difficult for DNA vaccines to transfer across cell membranes after intramuscular injection, limiting the amount of vaccine to be captured by antigen-presenting cells to induce immune responses.¹¹ Other factors that limit the clinical applications of these novel DNA vaccines include the difficulties associated with DNA stability and delivery, resulting in low levels of DNA vaccine expression and weak immune responses,^12–14 especially in large animal models.¹⁵ Therefore, effective strategies which can improve the efficacy of DNA vaccines, such as the use of a powerful adjuvant to enhance immunogenicity, optimization of the delivery methods, and selection of suitable target for effective antigen presentation, etc, are desirable.^16,17

With the development of nanotechnology and antigen delivery systems, biomaterials-based nanoparticles (NPs) can offer several advantages over the limitations of other traditional antigen delivery systems. These include stabilization of antigen, delivery of antigen, fewer probable side effects, and activation of innate immunity.¹⁸ Many structurally stable materials have been investigated for drug delivery. For instance, silica materials, which are biocompatible, have been the representative materials to enable the biological use of inorganic NPs.^19–21 It has been shown that silica is able to store and gradually release such therapeutic drugs as antibiotics and proteins in the controlled release applications.^22–24 Furthermore, silica has been used to improve the biocompatibility of some drug delivery systems, such as magnetic NPs,^25–27 biopolymers,²⁸ and micelles.²⁹

Layered double hydroxide (LDH), commonly known as hydrotalcite-like materials and anionic clays, is a family of layered nanomaterials that has been widely applied in catalysts, absorption, pharmaceutics, and photochemistry. In recent years, the synthesis of LDH-based nanocomposites has received much attention because of the potential uses of nanocomposite-based engineering materials.³⁰ The use of LDH materials in preparing polymer nanocomposites is a new field. LDH is a host–guest material consisting of positively charged metal hydroxide sheets with intercalated anions and water molecules. The formula of LDH molecules can be expressed as follows: [M²⁺_1−xM³⁺x(OH)₂]^x+Aⁿ⁻_x/n·mH2O, where M²⁺ and M³⁺ are divalent and trivalent metal ions, respectively, Aⁿ⁻ is an interchangeable compensating anion entrapped in the interlayer space, m is the number of molecules of co-intercalated water per formula weight of the compound, and x is defined as the M³⁺/(M²⁺ + M³⁺) ratio.³¹ Over the past decade, LDHs have attracted much attention in drug delivery and gene therapy owing to their good biocompatibility, no toxicity, and controlled release property. Yuan and Shi synthesized LDH nanofiller (LDH-SA). The nanofiller was used to prepare a UV-cured exfoliated polymer/LDH nanocomposite, which possesses the combined advantages of both LDH and silsesquioxane.³² Kang et al found that the LDH nanosheets could be stabilized by alginate molecules in aqueous media and that the LDH nanosheets in the nanocomposites could be redispersed in aqueous media.³³

Recently, nanocomposite materials with shell-core structure produced by combining two kinds of nanometer materials have received much attention, as these materials incorporate the virtues of the individual materials. In this study, LDH@SiO₂-NPs with shell-core structures were developed to encapsulate the F gene of NDV into a eukaryotic expression plasmid pVAX1-F(o) by a coprecipitation method for enhancing the efficacy of a DNA vaccine against NDV. The bioactivity and safety of the resulting NPs (pFDNA-LDH@SiO₂-NPs) were studied by in vitro transfection and cytotoxicity analyses. In addition, we assessed the ability of the pFDNA-LDH@SiO₂-NPs to induce immune responses and protect specific pathogen-free (SPF) chickens from NDV infection after intranasal administration. We found that the carrier has the advantage of LDH to protect the plasmid DNA against nuclease degradation, realizing the long-acting mechanism of DNA vaccine within the chicken’s body.

Materials and methods

Preparation of the plasmid DNA encapsulated in the SiO₂ NPs

The eukaryotic expression plasmid pVAX1-F(o) DNA that carries the F gene of NDV was provided by the State Key Laboratory of Veterinary Biotechnology, Harbin Veterinary Research Institute of Chinese Academy of Agricultural Sciences, Harbin, People’s Republic of China. Extraction and purification of a large amount of the plasmid DNA were carried out as previously described.^34,35 Ninety milliliters of anhydrous ethanol, 12.5 mL of deionized water, and 2.0 mL of ammonia water were added to a 120 mL beaker. The reaction mixture was vigorously stirred using a magnetic stirrer at room temperature, followed by adding 10 mL of tetraethyl orthosilicate and stirring at 200 rpm for 2 hours at room temperature. Then, SiO₂ NPs were collected by centrifugation, washed three times with anhydrous ethanol, and desiccated in the air.

SiO₂ NPs (145 mg) were added into the 1.0% 3-aminopropyl-triethoxysilane (APTES) ethanol solution, and the reaction mixture was then stirred at room temperature for 12 hours. The APTES-SiO₂-NPs were precipitated with anhydrous ethanol and dried as described above.

The plasmid DNA-loaded NPs were developed as follows (Figure S1): 4 mg of APTES-SiO₂-NPs were added into 4 mL of phosphate-buffered saline (PBS) buffer (pH 7.4), and 0.01 mL of plasmid DNA was then pipetted to the reaction mixture. The mixture was incubated at room temperature for 15 minutes. The NPs were collected by centrifugation at 10,000 rpm and 4°C for 15 minutes and then washed with PBS three times. The plasmid DNA-loaded NPs, ie, pFDNA-SiO₂-NPs, were obtained.

The pFDNA-SiO₂-NPs were prepared by mixing APTES-SiO₂-NPs and DNA in PBS (pH 7.4) at different mass ratios (w/w) with a final DNA concentration of 24,510.9 ng/μL. The mixture was incubated at room temperature for 15 minutes. The connection of NPs with the plasmid was detected by agarose gel electrophoresis, which was run with a 0.8% agarose gel at 90 V for 20 minutes. The mixture was then incubated at room temperature for 48 hours and centrifuged at 10,000 rpm and 4°C for 10 minutes. The precipitates were collected, then washed with PBS buffer (pH 7.4) twice and TE buffer once, followed by centrifugation at 10,000 rpm and 4°C for 10 minutes. In order to prove that the SiO₂ can bind with plasmid DNA and release DNA completely, the supernatant solution underwent agarose gel electrophoresis using 0.8% (w/v) gel containing ethidium bromide at 90 V for 20 minutes.

Preparation of LDH@SiO₂-NPs encapsulating plasmid DNA

LDH@SiO₂-NPs encapsulating plasmid DNA were prepared via the following procedures with two solutions.

Solution I

For solution I, 6.3 g NaOH, 9.1 g NaNO₃, and 0.8 g pFDNA-SiO₂-NPs were dissolved together in deionized water with a final volume of 72 mL.

Solution II

For solution II, 0.06 mol/L Mg (NO₃)₂⋅6H₂O and 0.03 mol/L Al (NO₃)₃⋅9H₂O were dissolved together in deionized water with a final volume of 63 mL. Solution II was slowly dripped into solution I and stirred at 200 rpm at room temperature for 2.5 hours. All the operational procedures were done under N₂ protection to avoid oxidation. The pFDNA-LDH@SiO₂-NPs were rinsed with deionized water and dried at room temperature.

Characterization of the pFDNA-LDH@SiO₂-NPs

Morphology and loading capacity

The prepared pFDNA-SiO₂-NPs and pFDNA-LDH@SiO₂-NPs were visualized through transmission electron microscopy (TEM) (JEM-200EX; Hitachi Ltd., Tokyo, Japan) to assess their morphological and surface characteristics.³⁶ The particle size and zeta potentials of both pFDNA-SiO₂-NPs and pFDNA-LDH@SiO₂-NPs were measured using a Zeta Sizer 2000 from Malvern Instruments (Malvern, UK). The loading capacity (LC) of the pFDNA-LDH@SiO₂-NPs was calculated as follows:³⁷

$$\mathrm{LC}(\%)=({\mathrm{W}}_0-{\mathrm{W}}_1)/{\mathrm{W}}_{\mathrm{n}}\times 100\%,$$ (1)

where W₀ is the total amount of the plasmid DNA added, W₁ is the amount of free plasmid DNA released from the pFDNA-LDH@SiO₂-NPs, and W_N is the weight of the pFDNA-LDH@SiO₂-NPs. All the measurements were performed in triplicate.

Fourier transform infrared spectroscopy and X-ray diffraction analyses of the LDH and pFDNA-LDH@SiO₂-NPs

The changes in the major groups of the LDH and pFDNA-LDH@SiO₂-NPs were characterized through Fourier transform infrared spectroscopy (FTIR) (Spectrum One; PerkinElmer Inc., Waltham, MA, USA). Analysis of the X-ray diffraction (XRD) was performed using a D8 Advance diffractometer (Bruker Optik GmbH, Ettlingen, Germany) with Cu target and Kα radiation (λ =0.15418 nm) at 40 kV and 50 mA. The 2θ angle was scanned between 5° and 80° at 25°C.

In vitro release of the pFDNA-LDH@SiO₂-NPs

The in vitro cumulative release of the plasmid DNA from the pFDNA-LDH@SiO₂-NPs was studied by the Coomassie Brilliant Blue G-250 method. Briefly, 0.1 g of dried pFDNA-LDH@SiO₂-NPs was fully mixed with 1.0 mL of PBS buffer (pH 7.4) and stirred at 180 rpm and 4°C. At the predetermined time intervals (0, 6, 12, 24, 36, 48, 72, 96, 120, 144, 168, 192, 216, 240, 264, and 288 hours), 100 μL of sample solution was taken away and the same volume of fresh PBS was added. The sample was centrifuged at 10,000 rpm and 4°C for 10 minutes. The concentration of the plasmid DNA in the supernatant was determined with an ultraviolet spectrophotometer. The release curve of plasmid DNA from pFDNA-LDH@SiO₂-NPs was derived by plotting the release time on the x-axis against the amount of plasmid DNA accumulatively released from pFDNA-LDH@SiO₂-NPs on the y-axis.

In vitro expression of the pFDNA-LDH@SiO₂-NPs

293 T cells, human embryonic kidney cells which were transformed with SV40T antigen, were incubated in a six-well plate at 37°C with 5% CO₂ until the cell growth reached 80% confluence for subsequent use. The cells underwent the following treatments: 1) naked DNA control treatment, in which 4 μg DNA was incubated with the cells according to the instructions of a Lipofectamine™ 2000 reagent kit; 2) pFDNA-LDH@SiO₂-NP treatment. The pFDNA-LDH@SiO₂-NPs containing 4 μg of plasmid DNA were added and incubated with the cells for 5 hours; 3) blank LDH@SiO₂-NPs control, in which LDH@SiO₂ at the amount equivalent to that in pFDNA-LDH@SiO₂-NPs was added and incubated with the cells for 5 hours; and 4) cell control, in which Dulbecco’s Modified Eagle’s Medium (DMEM) containing 1% serum was added. After being initially transfected, the cells were incubated for 72 hours in DMEM containing 1% serum. All the transfection experiments were performed in triplicate.

Evaluation of the safety of the pFDNA-LDH@SiO₂-NPs

In vitro cytotoxicity of the pFDNA-LDH@SiO₂-NPs

In vitro cytotoxicity of the pFDNA-LDH@SiO₂-NPs was evaluated as described previously.^36,38 Chicken embryo kidney cells were first cultured in DMEM, then diluted to the final cell concentration of 2×10⁶ cells/mL, transferred to 96-well plates at 200 μL per well, and cultured at 37°C for 5 hours. After discarding the supernatant in the wells, 50 μL of pFDNA-LDH@SiO₂-NPs (diluted in DMEM culture at 1 mg/mL) was added into the wells, followed by incubation at 37°C for 2 hours. Then, 10 μL of WST-8 reagents was added and incubated for 5 hours. The 96-well plates were read at 450 nm with a microplate reader. The survival rate of the cells was calculated as described previously.³⁶

Safety of the pFDNA-LDH@SiO₂-NPs

Fifteen 7-day-old SPF chickens obtained from Harbin Veterinary Research Institute Laboratory Animal Center (Harbin, People’s Republic of China) were randomly divided into three groups: chickens in group 1 were immunized intramuscularly (IM) with the pFDNA-LDH@SiO₂-NPs containing 2 mg of the plasmid DNA; chickens in group 2 were immunized intranasally (IN) with the pFDNA-LDH@SiO₂-NPs containing 2 mg of the plasmid DNA; and chickens in group 3 were immunized IM with the PBS solution as control group. These three groups of chickens were bred under the same conditions. Any behavioral abnormalities in the chickens, including feed intake, water intake, and mental state, were continuously observed and recorded for 3 weeks.

Immunization of SPF chickens

A total of 100 4-week-old SPF chickens were randomly divided into five groups with 20 chickens per group. The chickens in groups 1, 2, and 3 were treated with PBS buffer, blank LDH@SiO₂-NPs IM, and 200 μg of naked plasmid DNA (0.1 mL) IM, respectively. Chickens in groups 4 and 5 were treated with 0.2 mL of pDNA-LDH@SiO₂-NPs containing 200 μg of plasmid DNA IM and IN, respectively. Booster immunization was performed 14 days later with the same doses. Care of laboratory animals and experimentation on animals were in accordance with animal ethics guidelines and approved protocols. All animal studies were approved by the Animal Ethics Committee of the Harbin Veterinary Research Institute of the Chinese Academy of Agricultural Sciences (CAAS), China (SCXK [H] 2013-001).

Detection of IgG antibody in the serum of the immunized chickens

Blood samples were collected from the wing veins of chickens in the five groups at 7, 14, 21, 28, 35, 42, 49, and 56 days after the first treatment. The serum samples were obtained by centrifugation at 3,000 rpm and 4°C for 10 minutes. The titer of the NDV-specific IgG in sera was estimated by hemagglutination inhibition test.

Detection of IgA antibody in mucosa extracts of the immunized chickens

Serum, tracheal fluid, bile, and Harderian glands were collected from two chickens from each of the five groups immunized at 7, 14, 21, 28, 35, 42, 49, and 56 days after the first treatment. IgA antibody was detected by enzyme-linked immunosorbent assay (ELISA) sandwich technique according to the instruction manual of an NDV IgA ELISA Kit (Rapidbio Co, Ltd, West Hills, USA). Briefly, samples were added to microtiter plates coated with purified antigen, followed by adding standard and HRP-labeled antigen. The reaction was stopped by addition of 3,3′,5,5′-tetramethylbenzidine, and the absorbance at 450 nm was measured with a microplate reader.

Lymphocyte proliferation in the immunized chickens

To assess the cellular immune responses of the immunized chickens at 7, 14, 21, 28, 35, and 42 days after the first treatment, lymphocyte proliferation of the immunized chickens was assayed by 3-(4, 5)-dimethylthiahiazo (-z-y1)-3, 5-diphenytetrazoliumromide (MTT) colorimetric assay as described previously.³⁶ The stimulation index (SI) was determined using the following formula:³⁹

$$\mathrm{SI}=\mathrm{OD}570\mathrm{T}/\mathrm{OD}570\mathrm{C},$$ (2)

where OD570 T is the mean value of the tested groups (pFDNA-LDH@SiO₂-NPs IN, pFDNA-LDH@SiO₂-NPs IM, naked plasmid pVAX1-F(o) IM, blank LDH@SiO₂-NPs IM) and OD570 C is the mean value of the control group (PBS IM).

Protective efficacy

The ability of pFDNA-LDH@SiO₂-NPs to protect chickens against the infection of NDV strain F₄₈E₉ was determined. Strain F₄₈E₉ is highly virulent (mean death time of chicken embryos ≤60 hours, intracerebral pathogenicity index in 1 -day-old chickens >1.6). Protection was determined as described previously.³⁶ Five chickens were randomly selected from every immunized group when the level of NDV-specific antibody in serum was increased to 6.0 log 2. The chickens infected IM with 0.1 mL of the highly virulent NDV strain F₄₈E₉ had a viral titer of 10⁴.⁵ 50% egg infectious dose/0.1 mL for challenge studies. The clinical signs of illness and death were monitored daily for 35 days. The infected chickens and the corresponding negative control chickens were euthanized. Their duodena and myocardia were collected and examined by histological staining.

Statistical analysis

All experiments were performed in triplicate. Data were presented as mean values ± standard deviation. Mean values were analyzed using the one-sided Student’s t-test. The significance level was set at P<0.05.

Results

Characterization of the pFDNA-SiO₂-NPs

Physical features of NP-based vaccines such as particle size, morphology, and charge distributions contribute greatly to the efficacy of vaccination. As shown in Figure 1A, a spherical and uniform-size nature was revealed for the typical pFDNA-SiO₂-NPs by TEM. The prepared NPs had uniform morphology and good dispersion. Measurement of these particles showed a relatively narrow size distribution of 90±11 nm (Figure 1B). The zeta potential of SiO₂ NPs, APTES-SiO₂-NPs, and pFDNA-SiO₂-NPs were −21.08 mV, +28.37 mV, and +11.43 mV, respectively.

Figure 1.

Transmission electron microscopy photomicrograph (magnification 50,000×) (A) and particle size distribution (B) of the pFDNA-SiO₂-NPs.

Abbreviation: pFDNA-SiO₂-NPs, Newcastle disease virus F gene encapsulated in the SiO₂ nanoparticles.

Figure 2A shows the agarose gel electrophoresis image for the pFDNA-SiO₂-NP complexes, which demonstrated the ability of SiO₂ NPs to immobilize DNA with high efficiency. Through changing the number of particles, we could adjust the amounts of DNA binding to the particle surface.

Figure 2.

Detection of SiO₂ nanoparticles loaded with plasmid DNA for connection, release, and protection properties.

Notes: (A) Agarose gel electrophoresis of the amino-modified silica-DNA complexes. Maker (M): DL 15,000 marker. Lane 1: plasmid DNA. Lanes 2–8: the mass ratios of SiO₂ to plasmid DNA were 1:5, 1:1, 5:1, 10:1, 20:1, 30:1, and 40:1, respectively. (B) Stability analysis of the plasmid DNA binding with SiO₂ nanoparticles. (C) Analysis of protection of the plasmid DNA from DNase I digestion. Maker (M): DL 15,000 marker. Lane 1: plasmid DNA. Lanes 2–8: the mass ratios of SiO₂ to plasmid DNA were 1:5, 1:1, 5:1, 10:1, 20:1, 30:1, and 40:1, respectively.

Figure 2B shows that lanes 2–8 clearly had plasmid DNA binding equivalent to the control in lane 1, demonstrating that the DNA can be stabilized and released from the pFDNA-SiO₂-NP complexes after being placed at room temperature for 48 hours and that the integrity of plasmid DNA could be maintained.

The ability of the SiO₂ to protect the plasmid DNA from DNase I degradation was demonstrated by the fact that SiO₂ encapsulation could protect the plasmid DNA from DNase I digestion (Figure 2C, lanes 2–8), but the naked plasmid DNA was completely degraded by DNase I (Figure 2C, lane 1), suggesting that the encapsulation of plasmid DNA into SiO₂ may ensure the effective entry and high stability of plasmid DNA in the mucosal environment.

Characterization of the pFDNA-LDH@SiO₂-NPs

Size and zeta potential analysis

Typical pFDNA-SiO₂-NPs, LDH, and pFDNA-LDH@SiO₂-NPs showed a uniform appearance as revealed by TEM (Figure 3). The pFDNA-SiO₂-NPs were round with good dispersion (Figure 3A). Plain LDH NPs were thin, hexagonal, and plate-like in shape (Figure 3B) with sizes in the range from 78 to 207 nm, an average particle size of 99.1 nm, and zeta potential of 31.47 mV (Figure 4A). Figure 3C shows that the addition of 0.7 g of pFDNA-SiO₂-NPs caused the loss of the core from the core-shell structure. Figure 3E shows that addition of 0.9 g of pFDNA-SiO₂-NPs could result in too much core. The addition of 0.8 g of pFDNA-SiO₂-NPs could produce effective coating (Figure 3D), and the shell LDH had no obvious plate-like structure but was coated on the surface in a stacking way. The pFDNA-LDH@SiO₂-NPs showed a distribution from 220 to 400 nm and had an average particle size of 371.93 nm (Figure 4B). The zeta potentials of LDH and pFDNA-LDH@SiO₂-NPs were +31.47 and +31.63 mV, respectively. Both of these had similarly high zeta potentials, revealing that LDH does not change the zeta potential of NPs. The LC of the pFDNA-LDH@SiO₂-NPs was calculated to be 39.66%±0.45% (n=3).

Figure 3.

Transmission electron photomicrographs of the pFDNA-SiO₂-NPs (A), LDH (B), and pFDNA-LDH@SiO₂-NPs (C–E). Note: Magnification: 100,000×.

Abbreviations: LDH, layered double hydroxide; NPs, nanoparticles; pFDNA-LDH@SiO₂-NPs, Newcastle disease virus F gene encapsulated in LDH@SiO₂-NPs; pFDNA-SiO₂-NPs, Newcastle disease virus F gene encapsulated in the SiO₂ nanoparticles.

Figure 4.

Size distribution of LDH (A) and pFDNA-LDH@SiO₂-NPs (B).

Notes: Measurement of these particles showed a narrow distribution pattern of LDH and pFDNA-LDH@SiO₂-NPs, and their average diameters were 99.1 nm and 371.93 nm, respectively.

Abbreviations: LDH, layered double hydroxide; NPs, nanoparticles; pFDNA-LDH@SiO₂-NPs, Newcastle disease virus F gene encapsulated in LDH@SiO₂-NPs.

FTIR and XRD analyses of the LDH and pFDNA-LDH@SiO₂-NPs

As shown in Figure 5A, compared with the FTIR spectra between the LDH and pFDNA-LDH@SiO₂-NPs, the sharp and strong characteristic bands appeared between 400 cm⁻¹ and 1,000 cm⁻¹, attributed to the Mg-O and Al-O bonds. The weak peak at 460 cm⁻¹ was attributed to SiO₂ NPs, but it was covered by the strong peak of LDH at 450 cm⁻¹, therefore no peak at 460 cm⁻¹ was found in the pFDNA-LDH@SiO₂-NP scanning. The pFDNA-LDH@SiO₂-NPs showed an obviously stronger peak, at 1,640 cm^–1, than LDH did, because SiO₂ NPs had a strong characteristic band at this wavelength. The weak peaks at 1,640 cm⁻¹ and 1,380 cm⁻¹ are the characteristics of hydroxyl and nitrate ion in the LDH layer, respectively. The results of XRD pattern analysis showed that the SiO₂@LDH-NPs were complexes of LDH crystallite and SiO₂ (Figure 5B). The positions of both peaks were generally the same; however, the XRD pattern for pFDNA-LDH@SiO₂-NPs showed the characteristic peak at 20°, demonstrating that the appearance of crystal SiO₂ and the structure of LDH are not changed after silica coating. Both LDH@SiO₂-NPs and LDH displayed the characteristic crystalline peaks, obtaining (003), (006), (009), and (110). The characteristic peak (015, 018) was asymmetrical. The XRD patterns of the LDH exhibited the typical diffractions including (003) and (006), indicative of the presence of LDH crystallite. The spike of the characteristic peaks was narrow and sharp, illustrating that the LDH was a single crystalline phase with a high degree of crystallinity.

Figure 5.

Fourier transform infrared spectroscopy spectrum (A) and XRD curve (B) for each of the LDH and pFDNA-LDH@SiO₂-NPs.

Notes: The XRD patterns of the pFDNA-LDH@SiO₂-NPs exhibited typical diffractions of LDH including (003) and (006), indicative of the presence of LDH crystallite. The characteristic peak at 20° of pFDNA-LDH@SiO₂-NPs showed the existence of SiO₂.

Abbreviations: LDH, layered double hydroxide; NPs, nanoparticles; pFDNA-LDH@SiO₂-NPs, Newcastle disease virus F gene encapsulated in LDH@SiO₂-NPs; XRD, X-ray diffraction.

In vitro release of the pFDNA-LDH@SiO₂-NPs

As shown in Figure 6, the amount of DNA released from the pFDNA-LDH@SiO₂-NPs was increased to 47.36%±1.95% (n=3) from 0 to 48 hours, revealing that the burst release mainly takes place during the first 48 hours and is followed by a slow and continuous release, maintained for longer than 96 hours, reaching 64.27%±1.52% but not changing significantly after 96 hours. At 288 hours, the amount of plasmid DNA released from the pFDNA-SiO₂-NPs reached 91.36%±1.1%.

Figure 6.

In vitro release profiles of DNA from pFDNA-LDH@SiO₂-NPs in phosphate-buffered saline (pH 7.4).

Notes: The experiment was repeated three times and measured in triplicate. Data are presented as the mean ± standard deviation (n=3).

Abbreviations: LDH, layered double hydroxide; NPs, nanoparticles; pFDNA-LDH@SiO₂-NPs, Newcastle disease virus F gene encapsulated in LDH@SiO₂-NPs.

In vitro expression of the pFDNA-LDH@SiO₂-NPs

The pFDNA-LDH@SiO₂-NP group (Figure 7A) and the naked plasmid DNA group (Figure 7B) could be expressed in the cells and the specific fluorescence could be observed. However, no fluorescence signals were observed in the blank LDH@SiO₂-NP group (Figure 7C) or the negative cell control group (Figure 7D). These results indicate that plasmid DNA can be effectively encapsulated by LDH@SiO₂, and that the plasmid DNA encapsulated in pFDNA-LDH@SiO₂-NPs can be expressed in vitro.

Figure 7.

In vitro expression of the pFDNA-LDH@SiO₂-NPs in 293 T cells assayed by indirect immunofluorescence (×40).

Notes: (A) Naked plasmid pVAX1-F(o) DNA group. (B) Transfected pFDNA-LDH@SiO₂-NPs group. (C) Blank LDH@SiO₂-NPs group. (D) 293 T cell group as the negative control.

Abbreviations: LDH, layered double hydroxide; NPs, nanoparticles; pFDNA-LDH@SiO₂-NPs, Newcastle disease virus F gene encapsulated in LDH@SiO₂-NPs.

Evaluation of the safety of the pFDNA-LDH@SiO₂-NPs

In vitro cytotoxicity of the pFDNA-LDH@SiO₂-NPs The survival rate of chicken embryo kidney cells in the pFDNA-LDH@SiO₂-NP group was 84.12%±1.26%, and there were no significant changes in cell morphology as compared with that of the control cells. All the results show that the pFDNA-LDH@SiO₂-NPs cause low cytotoxicity and are very safe for these cells.

Safety of the pFDNA-LDH@SiO₂-NPs

Compared with those in the control group, the feeding, water intake, and other behaviors were normal in the chickens immunized IM and IN with the pFDNA-LDH@SiO₂-NPs, implying that immunization of the chickens with a high dose of pFDNA-LDH@SiO₂-NPs is safe. The chickens from the three groups were euthanized, and their duodena, proventriculi, and myocardia were then taken out for pathological section analysis. The results are shown in Figure 8.

Figure 8.

Histopathological analyses of normal duodena, proventriculi, and myocardia.

Notes: (A) Tissues of duodena were immunized with pFDNA-LDH@SiO₂-NPs IM (a), pFDNA-LDH@SiO₂-NPs IN (b), and PBS IM (c). (B) Tissues of proventriculi were immunized with pFDNA-LDH@SiO₂-NPs IM (a), pFDNA-LDH@SiO₂-NPs IN (b), and PBS IM (c). (C) Tissues of myocardia were immunized with pFDNA-LDH@SiO₂-NPs IM (a), pFDNA-LDH@SiO₂-NPs IN (b), and PBS IM (c).

Abbreviations: IM, intramuscularly; IN, intranasally; LDH, layered double hydroxide; NPs, nanoparticles; PBS, phosphate-buffered saline; pFDNA-LDH@SiO₂-NPs, Newcastle disease virus F gene encapsulated in LDH@SiO₂-NPs.

Immune efficacy of the pFDNA-LDH@SiO₂-NPs

Serum IgG antibody level

Table 1 shows that the serum IgG antibody titers in both the PBS IM and blank LDH@SiO₂-NPs IM groups were not significantly changed in the 8 weeks (less than 2.0 log 2, P>0.05). pFDNA-LDH@SiO₂-NPs administered IN and IM showed lower levels of antibody titers during the first 2 weeks post-immunization, while the antibody titers quickly increased at the 3rd week post-immunization in chickens immunized with the pFDNA-LDH@SiO₂-NPs IN and IM and peaked at the 5th week post-immunization. Serum IgG antibody titers in the pFDNA-LDH@SiO₂-NPs IN chickens remained significantly higher (P<0.01) than those in the pFDNA-LDH@SiO₂-NPs IM and naked plasmid pVAX1-F IM vaccinated chickens until the 8th week post-immunization, suggesting that the plasmid DNA had a sustained release. All the data show that plasmid DNA can be released slowly from pFDNA-LDH@SiO₂-NPs and specifically stimulates B lymphocytes to increase serum antibody titers.

Table 1.

IgG antibody titers in serum samples of specific pathogen-free chickens immunized with PBS IM, LDH@SiO₂-NPs IM, naked plasmid pVAX1-F(o) DNA IM, pFDNA-LDH@ SiO₂-NPs IM, and pFDNA-LDH@SiO₂-NPs IN (unit: log 2), respectively

Group	Weeks post-immunization
	1	2	3	4	5	6	7	8
pFDNA-LDH@SiO2-NPs IN	3.333±0.577a	4.667±0.577a	6.000±0a	7.667±0.577a	8.667±0.577a	8.667±0.577a	7.667±1.155a	7.333±0.577a
pFDNA-LDH@SiO2-NPs IM	3.333±0.577a	4.667±0.577a	5.000±0a	5.333 ±1.155b	7.333±0.577a	6.333±0.577b	7.000±0a	5.667±0.577b
Naked plasmid pVAX1-F(o) DNA IM	3.000±1.000a	4.667±0.577a	4.667±0.577a	5.667±0.577b	3.000±1.000b	2.667±1.155c	3.000±1.000b	3.000±1.000c
Blank LDH@SiO2-NPs IM	2.000±1.000b	1.667±0.577b	2.000±1.000b	1.667 ±1.155c	1.667±1.155c	2.000±0d	2.000±1.000b	1.667±0.577d
PBS IM	1.333±0.577b	1.333±0.577b	1.667±0.577b	1.000±0c	1.333±0.577c	1.333±0.577d	1.667±1.155b	1.000±0d

Notes: Values are presented as mean ± standard deviation of five experiments in each group. Values within the same column with the different superscript letters are significantly different (P<0.05; Student’s t-test).

Abbreviations: IM, intramuscularly; IN, intranasally; LDH, layered double hydroxide; NPs, nanoparticles; PBS, phosphate-buffered saline; pFDNA-LDH@SiO₂-NPs, Newcastle disease virus F gene encapsulated in LDH@SiO₂-NPs.

IgA antibody level in mucosa extracts

The changes of IgA antibody levels in serum, bile, tracheal fluid, and Harderian glands post-immunization are shown in Figure 9. The IgA antibody levels in the pFDNA-LDH@SiO₂-NPs IN, pFDNA-LDH@SiO₂-NPs IM and naked plasmid DNA IM groups were significantly higher than those in the blank LDH@SiO₂-NPs IM and PBS IM groups (P<0.01). The chickens immunized with the pFDNA-LDH@SiO₂-NPs IN had significantly higher IgA antibody titers (P<0.01) and longer period of IgA antibody secretion in serum (Figure 9A), tracheal fluid (Figure 9B), bile (Figure 9C), and Harderian glands (Figure 9D) than the chickens of other groups. The IgA antibody titers in the pFDNA-LDH@SiO₂-NPs IM group were significantly higher and their secretion period longer than in the naked plasmid DNA IM group (P<0.05). It can be clearly observed that pFDNA-LDH@SiO₂ -NPs were able to induce quicker and better mucosal immune responses than the naked plasmid DNA vaccine.

Figure 9.

IgA antibody levels in serum (A), tracheal fluid (B), bile (C), and Harderian glands (D) of specific pathogen-free chickens immunized with PBS IM, blank LDH@SiO₂-NPs IM, naked plasmid pVAX1-F(o) DNA IM, pFDNA-LDH@SiO₂-NPs IM, and pFDNA-LDH@SiO₂-NPs IN.

Notes: IgA antibody levels are presented as mean ± standard deviation of five experiments. Data with different small letters show significant difference (P<0.05).

Abbreviations: IM, intramuscularly; IN, intranasally; LDH, layered double hydroxide; NPs, nanoparticles; PBS, phosphate-buffered saline; pFDNA-LDH@SiO₂-NPs, Newcastle disease virus F gene encapsulated in the LDH@SiO₂-NPs.

Lymphocyte proliferation assay

As shown in Table 2, there were no significant differences between chickens immunized with the pFDNA-LDH@SiO₂-NPs IN or IM and chickens immunized with the naked plasmid pVAX1-F(o) DNA IM at the 3rd week post-immunization (P>0.05). The chickens immunized with the pFDNA-LDH@SiO₂-NPs IN had significantly higher SI than chickens immunized with the pFDNA-LDH@SiO₂-NPs IM and the naked plasmid pVAX1-F(o) DNA IM (P<0.05) at the 4th week post-immunization; the higher SI was maintained until the 6th week post-immunization (P<0.05). It was clear that the pFDNA-LDH@SiO₂-NPs significantly enhanced the immune function of T lymphocytes in the immunized chickens.

Table 2.

The stimulation index of T lymphocyte proliferation in specific pathogen-free chickens post-immunization

Group	Stimulation index
	7 days post-immunization	14 days post-immunization	21 days post-immunization	28 days post-immunization	35 days post-immunization	42 days post-immunization
pFDNA-LDH@SiO2-NPs IN	0.522±0.021a	0.689±0.029a	1.110±0.019a	1.444±0.039a	1.866±0.07a	2.056±0.042a
pFDNA-LDH@SiO2-NPs IM	0.517±0.003a	0.690±0.014a	1.104±0.028a	1.234±0.071b	1.745±0.096b	1.803±0.028b
Naked plasmid pVAX1-F(o) DNA IM	0.515±0.031a	0.671±0.017a	1.009±0.007a	1.228±0.057b	1.566±0.037c	1.606±0.025c
Blank LDH@SiO2-NPs IM	0.402±0.007b	0.478±0.004b	0.727±0.075c	0.805±0.047c	1.121±0.281d	1.044±0.055d
PBS IM	0.364±0.03b	0.441±0.030b	0.701±0.056c	0.743±0.028d	1.100±0.021d	1.008±0.023d

Notes: Values are presented as mean ± standard deviation of five experiments in each group. Values within the same column with the different superscript letters are significantly different (P<0.05; Student’s t-test).

Abbreviations: IM, intramuscularly; IN, intranasally; LDH, layered double hydroxide; NPs, nanoparticles; PBS, phosphate-buffered saline; pFDNA-LDH@SiO₂-NPs, Newcastle disease virus F gene encapsulated in LDH@SiO₂-NPs.

Protection against the infection of NDV strain F₄₈E₉

Within 2–5 days, the highly virulent NDV strain F₄₈E₉ had killed all the chickens treated with either PBS IM or blank LDH@SiO₂-NPs IM (Table 3). In contrast, strain F₄₈E₉ killed only 60%, 40%, and 0% of the chickens treated with the naked plasmid pVAX1-F(o) DNA IM, pFDNA-LDH@SiO₂-NPs IM, and pFDNA-LDH@SiO₂-NPs IN, respectively (Table 3). Two chickens of the pFDNA-LDH@SiO₂-NPs IM group died, and the protective efficacy was 60%. There were no clinical signs in chickens immunized with the pFDNA-LDH@SiO₂-NPs IN after being challenged with the strain F₄₈E₉, and no pathological and histopathological changes were found in their duodena (Figure 10A) and myocardia (Figure 10B).

Table 3.

Protection of the immunized specific pathogen-free chickens after being challenged with the highly virulent Newcastle disease virus strain F₄₈E₉

Treatment	Number of dead chickens/total number of chickens	Mortality (%)	Protection (%)
PBS IM	5/5	100	0
Blank LDH@SiO2-NPs IM	5/5	100	0
Naked plasmid pVAX1-F(o) DNA IM	3/5	60	40
pFDNA-LDH@SiO2-NPs IM	2/5	40	60
pFDNA-LDH@SiO2-NPs IN	0/5	0	100

Abbreviations: IM, intramuscularly; IN, intranasally; LDH, layered double hydroxide; NPs, nanoparticles; PBS, phosphate-buffered saline; pFDNA-LDH@SiO₂-NPs, Newcastle disease virus F gene encapsulated in LDH@SiO₂-NPs.

Figure 10.

Histopathological analyses of the duodena and myocardia of chickens challenged with the highly virulent NDV strain F₄₈E₉.

Notes: (A) Tissues of the duodena from chickens immunized with pFDNA-LDH@SiO₂-NPs IN. (B) Tissues of the myocardia from chickens immunized with pFDNA-LDH@SiO₂-NPs IN. (C) Tissues of the duodena from chickens immunized with pFDNA-LDH@SiO₂-NPs IM, naked plasmid pVAX1-F(o) DNA IM, or PBS IM. (D) Tissues of the myocardia from chickens in groups immunized with the pFDNA-LDH@SiO₂-NPs IM, naked plasmid pVAX1-F(o) DNA IM, or PBS IM.

Abbreviations: IM, intramuscularly; IN, intranasally; LDH, layered double hydroxide; NDV, Newcastle disease virus; NPs, nanoparticles; PBS, phosphate-buffered saline; pFDNA-LDH@SiO₂-NPs, NDV F gene encapsulated in the LDH@SiO₂-NPs.

The dead chickens from the pFDNA-LDH@SiO₂-NPs IM, naked plasmid pVAX1-F(o) DNA IM, or PBS IM groups had the typical pathological changes of ND, such as mucosal hemorrhages in proventriculus papillae, heart fat, duodena, and whole intestines. Much serious hemorrhaging on the mucous layer of duodena was found through examination of the histopathology slide (Figure 10C). Other pathological changes such as incomplete intestinal wall and intestinal villus and follicular cell necrosis were seen (Figure 10D). Together, these findings show that the pFDNA-LDH@SiO₂-NPs IN quickly induced an effective mucosal immune response and protected chickens against NDV infection.

Discussion

NDV infection is still one of the infectious avian diseases worldwide with serious long-term morbidities and mortalities. Currently, the effective strategies for prevention and control of NDV infection are still limited. However, DNA-based vaccines have emerged as a new kind of vaccine and have shown promising potential against NDV infection.

Like most vaccines, NDV vaccines do not prevent the vaccinated animals from becoming infected with a virulent NDV and subsequently shedding the virus,⁴⁰ but the amount of virus shed in the feces of vaccinated animals was lower than that of non-vaccinated birds.⁴¹ Current measures for the control of ND primarily depend on flock vaccination and culling of infected or suspected infected birds. Although current vaccines can protect infected birds, virus replication and shedding may still happen, albeit at a reduced level.⁴²

Various approaches have been applied to improve the systemic immune response to infectious bacteria or viruses. Among them, DNA vaccination has been demonstrated to be one effective way to elicit protective immunity against pathogens. DNA vaccines that mimic live attenuated vaccines in their ability to induce both humoral and cellular immune responses may prove to be a useful alternative.⁴³ The potential for DNA vaccines to overcome maternal immunity, stability issues, costs, and the non-requirement of cold chain has highlighted the promise of DNA vaccines. Here, we have developed an NDV-specific DNA NP vaccine and shown that it is better than a naked DNA vaccine. It is able to protect plasmid DNA from degradation by DNase and allows the plasmid DNA to be expressed and thus enhance the mucosal immune response and antibody immune responses.

Nowadays, many NP carriers such as microemulsions, liposomes, inorganic NPs, virosomes, virus-like particles, and polymeric microparticles have been applied in vaccinology.⁴⁴ Due to the similarity of their size to that of a pathogen, these particles can be taken up by antigen-presenting cells^45,46 and thus enter living cells. Therefore, delivery systems play a major role in enhancing antigen processing and stimulating immunity. Zhao et al previously reported that the F gene of NDV in plasmid DNA encapsulated in chitosan³⁶ or PLGA⁴⁷ NPs could be stabilized and sustainably released from the plasmid DNA and induced stronger mucosal immune responses than non-encapsulated plasmid DNA. In recent years, the shell-core nanocomposite has been developed as a new type of composite material and is a hot topic of current research.^48,49 In order to apply the biodegradable NPs as a delivery vector for veterinary virus vaccines, in this study, we determined whether biodegradable NPs can be used to deliver newly developed DNA vaccines. LDH@SiO₂ shell-core nanocomposite was first synthesized as a carrier for the F gene plasmid DNA of NDV delivery systems. The plasmid DNA carrying the F gene of NDV was then encapsulated into the LDH@SiO₂-NPs by a complex coacervation method. The advantages of pFDNA-LDH@SiO₂-NPs prepared using a complex coprecipitation method include mild preparation condition, protection of plasmid DNA from degradation, remaining solvent in the course of NP preparation, and ease of obtaining high-quality SiO₂ NPs. The NPs that had the desired size and retained the bioactivity of the loaded plasmid DNA were produced under the optimal preparation conditions. The average sizes of the pFDNA-SiO₂-NPs, LDH, and pFDNA-LDH@SiO₂-NPs were 90.5, 99.1, and 371.93 nm, respectively, and the zeta potentials were +1.43, +31.47, and +31.63 mV, respectively. LDH@SiO₂-NPs were demonstrated to be able to bind and protect the plasmid DNA by DNA protection assays. LC for incorporating DNA into NPs is an important parameter, because it determines both the effectiveness of the gene delivery and subsequent expression levels of encoded genes in vitro and in vivo.⁵⁰ In this study, the prepared pFDNA-LDH@SiO₂-NPs showed a large surface area with an LC of 39.66%±0.45 %. These results show that the prepared pFDNA-LDH@SiO₂-NPs have the potential to serve as a DNA vaccine delivery system.

The FTIR and XRD analyses of pFDNA-LDH@SiO₂-NPs showed that LDH and pFDNA-LDH@SiO₂-NPs had an obvious absorption peak and that the synthesized LDH had a simple crystal phase and high crystallinity.

It was reported previously that the swelling of the NPs and pH values of the released medium may influence the release profile of the gene from NPs.⁵¹ Hence, the release analysis study was conducted by incubating pFDNA-LDH@SiO₂-NPs in PBS (pH 7.4) and the cumulatively released amounts were monitored at different time intervals. Figure 7 shows that the plasmid DNA could be released slowly from the pFDNA-LDH@SiO₂-NPs. These results indicate that the LDH@SiO₂-NPs can be used as a controlled release carrier, prolonging the expression duration of the genes within the body.

We showed that the expression of NDV-specific antigen, F gene, was detected in vitro transfected assay. In the meantime, the in vitro cytotoxicity studies also showed that the pFD-NA-LDH@SiO₂-NPs had low cytotoxicity and high safety. In vivo safety tests showed that the pFDNA-LDH@SiO₂-NPs were safe for use either IN or IM and no pathological changes were observed in the immunized chickens. These findings show that the production procedures of NPs are safe and that LDH@SiO₂-NPs can retain the bioactivity of plasmid DNA.

A previous report showed that the main factor eliciting mucosal immune response for effective mucosal vaccines is the quick and strong release of a specific secretory IgA (sIgA).⁵² This is particularly critical for prevention of ND because the transmission routes of NDV are mainly the respiratory and digestive tracts. The nasal mucosa is the first portal of entry for the inhaled antigens, which can lead to both efficient mucosal and systemic immune responses.⁵³ Intranasal immunization is a very effective way of eliciting mucosal and systemic immune responses.^54,55 Therefore, the ability of LDH@SiO₂-NPs to elicit a mucosal immune response was investigated. Our results revealed that pFDNA-LDH@SiO₂-NPs given IN induced stronger mucosal immune responses and a more sustained release of plasmid DNA than the naked plasmid DNA. Furthermore, the IgA antibody levels in the pFDNA-LDH@SiO₂-NPs IN chickens were much higher than in our previously reported results (P<0.05).^36,47

The LDH@SiO₂-coupled NDV DNA vaccines could also induce a humoral immune response which lasts for a longer period of time. Our results showed that a high level of IgG antibody titers was detected in chickens given pFDNA-LDH@SiO₂-NPs IN. The cellular immune response is essential for virus clearance⁵⁶ even though the specific cellular immunity is not sufficient by itself to protect against virulent NDV.⁵⁷ Lymphocyte homeostasis is required for the maintenance of normal immune function. In our study, lymphocyte proliferation assay showed that the chickens immunized IN with the pFDNA-LDH@SiO₂-NPs had a significantly higher SI than the chickens in other groups (P<0.05). These results clearly demonstrate that the pFDNA-LDH@SiO₂-NPs significantly enhanced the immune function of T lymphocytes in the immunized chickens.

In summary, intranasal immunization of SPF chickens with the pFDNA-LDH@SiO₂-NPs induced stronger cellular, humoral, and mucosal immune responses and achieved a sustained release effect. Additionally, neither clinical signs nor mortality were observed in chickens immunized IN with the pFDNA-LDH@SiO₂-NPs. After being challenged with the virulent strain F₄₈E₉, the protective efficacy of pFDNA-LDH@SiO₂-NPs was as high as 100%.

This work has laid a good foundation for using LDH@SiO₂-NPs with a shell-core structure as a delivery carrier in mucosal immunization for vaccines. In addition, this study has also shown that LDH@SiO₂-NPs can be a promising technology for needle-free vaccination with great application potential. However, despite its favorable bioavailability, biodegradable nature, and long-term antigen release profile, a successful LDH@SiO₂-encapsulated vaccine is yet to be developed and introduced for use in both animals and humans. Currently, the NPs used in the field of DNA vaccine delivery are still at an early stage of their development. A lot of challenges remain, such as a lack of understanding of how the physiochemical properties of NPs affect the targeted delivery of plasmid DNA and how the surface charge and additional targeting may influence the uptake of vaccines, and the cost of preparing these NPs must be reduced. We believe that, with the development of technologies in biomedical and material sciences, these challenges can be eventually resolved in the future, and that LDH@SiO₂-NPs with a shell-core structure will be widely applied as delivery carriers in the fields of vaccine antigens and biomedicine.

Conclusion

In this study, the biodegradable LDH@SiO₂-NPs were prepared in order to find effective vaccine delivery systems and immunostimulants. In vitro cellular experiments showed that LDH@SiO₂-NPs with a shell-core structure as a delivery carrier for NDV DNA vaccine not only protected the plasmid DNA from degradation, but also exhibited high transfection efficiency. Animal experiments showed that intranasal immunization of SPF chickens with pFDNA-LDH@SiO₂-NPs caused much stronger cellular, humoral, and mucosal immune responses and achieved the sustained release effect than the pFDNA-LDH@SiO₂-NPs IM, naked plasmid pVAX1-F (o) DNA, and blank LDH@SiO₂-NPs. Further, immunization with pFDNA-LDH@SiO₂-NPs also induced significantly efficient T-cell proliferation. Our results indicate that LDH@SiO₂-NPs can serve as a promising DNA vaccine delivery carrier for needle-free vaccination and have great application potential.

Supplementary material

Figure S1

Preparation of pFDNA-LDH@SiO2-NPs.

Abbreviations: APTES, 3-aminopropyl-triethoxysilane; LDH, layered double hydroxide; NPs, nanoparticles; pFDNA-LDH@SiO₂-NPs, Newcastle disease virus F gene encapsulated in LDH@SiO₂-NPs; pFDNA-SiO₂-NPs, Newcastle disease virus F gene encapsulated in SiO₂-NPs; TEOS, tetraethyl orthosilicate.