. 2015 Jun 25;6:7383. doi: 10.1038/ncomms8383

Lead iodide perovskite light-emitting field-effect transistor

Xin Yu Chin 1, Daniele Cortecchia 2,3, Jun Yin 1,4, Annalisa Bruno 1,3, Cesare Soci 1,4,a
PMCID: PMC4491174  PMID: 26108967

Abstract

Despite the widespread use of solution-processable hybrid organic–inorganic perovskites in photovoltaic and light-emitting applications, determination of their intrinsic charge transport parameters has been elusive due to the variability of film preparation and history-dependent device performance. Here we show that screening effects associated to ionic transport can be effectively eliminated by lowering the operating temperature of methylammonium lead iodide perovskite (CH3NH3PbI3) field-effect transistors. Field-effect carrier mobility is found to increase by almost two orders of magnitude below 200 K, consistent with phonon scattering-limited transport. Under balanced ambipolar carrier injection, gate-dependent electroluminescence is also observed from the transistor channel, with spectra revealing the tetragonal to orthorhombic phase transition. This demonstration of CH3NH3PbI3 light-emitting field-effect transistors provides intrinsic transport parameters to guide materials and solar cell optimization, and will drive the development of new electro-optic device concepts, such as gated light-emitting diodes and lasers operating at room temperature.

Inline graphicHybrid organic–inorganic perovskites have shown great potential for use in optoelectronic applications. Here, the authors create solution-processed lead iodide perovskite light-emitting field-effect transistors and demonstrate both ambipolar behaviour and gate-assisted electroluminescence.

Organolead halide perovskites are emerging solution-processable materials with outstanding optoelectronic properties1,2,3,4,5,6,7. Among them, methylammonium lead iodide CH3NH3PbI3 has proven to be an exceptional light harvester for hybrid organic–inorganic solar cells3,8,9,10,11,12,13,14,15, which in just 4 years achieved an impressive National Renewable Energy Laboratory (NREL)-certified power conversion efficiency of 20.1%, and remarkable performance in a variety of device architectures16. Thanks to their cost-effectiveness and ease of processing, hybrid perovskites have naturally attracted a vast interest for applications beyond photovoltaic energy conversion, such as water splitting17, light-emitting diodes18,19,20 and tunable, electrically pumped lasers6,21,22,23. So far, transport parameters of perovskite materials were mostly deduced from the study of photovoltaic devices, which indicated ambipolar transport3,24,25, of holes and electrons within the perovskite active region, and long electron–hole pair diffusion length4,5,26.

First-principle calculations for this class of materials predict that hole mobility is up to 3,100 cm2 V−1 s−1 and electron mobility is 1,500 cm2 V−1 s−1 with concentration of 1016 cm−3 at 400 K (ref. 27), and high-frequency mobility of 8 cm2 V−1 s−1 was determined in CH3NH3PbI3 spin-coated thin film by THz spectroscopy28, a remarkably high value for solution-processed materials. A combination of resistivity and Hall measurement further revealed that the mobility of ∼66 cm2 V−1 s−1 is achievable in CH3NH3PbI3 (ref. 29).

Recent publications on organolead halide perovskite single crystals also reported extremely low trap densities, leading to a noticeable enhancement of photogenerated carrier lifetime and mobility30,31,32.

However, very recently ion drift was shown to play a dominant role on charge transport properties33, stimulating an ongoing debate about the carrier character and the origin of anomalous hysteresis, together with the role of polarization, ferroelectric and trap-state filling effects in organolead halide perovskite devices investigated at room temperature34,35,36,37.

Despite the rapid advancement of optoelectronic applications, a big gap remains in understanding the fundamental transport properties of organolead halide perovskites, namely charge carrier character, mobility and charge transport mechanisms. To fill this gap, studies of basic field-effect transistor (FET) devices are urgently needed. Historically, related tin(II)-based 2D hybrid perovskites have attracted major interest for FET fabrication because of their attractive layered structure, with demonstrated field-effect mobilities up to 0.62 cm2 V−1 s−1 and Ion/Ioff ratio above 104 (ref. 38). Improvement of mobility can be achieved by substitution of organic cation in hybrid perovskite, yielding FET saturation-regime mobility as high as 1.4 cm2 V−1 s−1, and nearly an order of magnitude lower linear-regime mobility39. Further improvement was demonstrated through melt processed deposition technique, where saturation and linear mobilities of 2.6 and 1.7 cm2 V−1 s−1 with Ion/Ioff of 106 were achieved40. Conversely, only rare examples of 3D hybrid perovskites FETs can be found in the literature (see Supplementary Information in ref. 15), with limited hole mobility of the order of ∼10−5 cm2 V−1 s−1 in the case of CH3NH3PbI3 and strong hysteresis due to ionic transport, which so far have hindered the development of FET applications. Nonetheless, high photoluminescence efficiency22 and widely tunable band gap from visible to infrared29,41 make CH3NH3PbI3 extremely attractive for the fabrication of solution processable light-emitting field-effect transistors (LE-FET), a device concept that may be integrated in heterogeneous optolectronic systems, such as flexible electroluminescent displays42 or electrically pumped lasers43.

Here we report the fabrication and characterization of CH3NH3PbI3 FETs, and their operation as light-emitting FETs yielding gate-assisted electroluminescence (EL). Low-temperature measurements were used to effectively remove screening effects arising from ionic transport, allowing the determination of intrinsic transport parameters such as carrier density and mobility. Field-effect mobility of CH3NH3PbI3 is found to increase by almost two orders of magnitude from room temperature down to 78 K, a behaviour consistent with phonon scattering-limited transport of conventional inorganic semiconductors. We also confirm the ambipolar nature of charge transport in CH3NH3PbI3, which yields close to ideal ambipolar transistor characteristics and EL from the transistor channel under balanced injection conditions. This demonstration of CH3NH3PbI3 light-emitting FETs provides an essential guideline for materials optimization through chemical synthesis and future improvements of solar cell performance. And the novel device concept opens up new opportunities for the development of electro-optic devices based on CH3NH3PbI3, such as gated light-emitting devices.

Results

Thin film characterization

Deposition methods of solution-processed organo-lead hybrid perovskite have direct consequences on the morphology of thin film, hence on charge transport properties of the material2. Here we used the solvent engineering technique recently reported for optimized solar cell fabrication14 to deposit a compact and uniform CH3NH3PbI3 perovskite layer (∼150 nm thick) on top of heavily p-doped Si with thermally grown SiO2 (Fig. 1a). The resulting thin films are of very high quality: they consist of closely packed, large domains with grain size up to 200 nm, as seen in the top view scanning electron microscope (SEM) image in Fig. 1b. They crystallize in a perfect tetragonal structure, as revealed by the X-ray diffraction analysis in Fig. 1c. A film roughness of RRMS=10.8 nm was evaluated by atomic force microscopy (AFM; Supplementary Fig. 1). Availability of such high-quality films is essential to minimize the influence of metal contacts and charge carrier scattering across the film, so as to obtain intrinsic transport parameters from FET measurements. The device structure used in this study is shown in Fig. 1d. A bottom gate, bottom contact configuration was employed to allow deposition of active materials to be the last step in the fabrication. This is to minimize exposure of CH3NH3PbI3 to moisture in the environment, and to avoid potential overheating during the metal electrode deposition.

Figure 1. FET device configuration and thin-film characterization.

Figure 1

Open in a new tab

(a,b) Cross-sectional (a) and top-view (b) scanning electron miscroscope micrographs of the CH3NH3PbI3 thin film. Scale bars, 1 μm. (c) X-ray diffraction pattern of CH3NH3PbI3 film on SiO2/Si(p++) substrate, confirming the tetragonal structure of the perovskite and space group I4/mcm. (d) Schematic of the bottom-gate, bottom contact LE-FET configuration used in this study.

Low-temperature FET characterization

As reported in the literature, transport characteristics of flat-junction CH3NH3PbI3 solar cells are often subject to strong hysteresis44, which so far hindered a complete understanding of the electrical response, and the determination of intrinsic transport parameters of the perovskite34,35,36. The origin of this anomalous behaviour has been attributed to capacitive effects associated with ferroelectricity arising from the spontaneous polarization of methylammonium cation and lattice distortion effects, diffusion of excess ions as interstitial defects, and trapping/de-trapping of charge carriers at the interface34,35,36,44. Photocurrent hysteresis in CH3NH3PbI3 planar heterojunction solar cells was found to originate from trap states on the surface and grain boundaries of the perovskite materials, which can be effectively eliminated by fullerene passivation36. Recently, hysteresis-free photovoltaic devices with well-reproducible PCEs were achieved in single crystals30,31 and millimeter-scale grain size thin films32. Piezoelectric microscopy revealed the reversible switching of the ferroelectric domains by poling with DC biases45, but a recent observation of field-switchable photovoltaic effect suggested that ion drift under the electric field in the perovskite layer induces the formation of p–i–n structures33, as observed by electron beam-induced current measurement and Kelvin probe force microscopy24,25. A weakened switchable photovoltaic effect at low temperature and the lack of photovoltage dependence with respect to the lateral electrode spacing suggest that ferroelectric photovoltaic effect may not play dominant role in the observed field-switchable photovoltaic behaviour33. Theoretical calculations further reveal that charged Pb, I and methylammonium vacancies have low formation energies40,41, suggesting that the high ionicity of this materials may lead to p- and n-type self-doping.

We found that reducing the operating temperature of our devices is an effective way to reduce hysteresis effects due to ionic transport/screening, allowing to record transport characteristics typical of conventional ambipolar semiconductor FETs (Fig. 2). The complete temperature evolution of ambipolar FET characteristics, from room temperature down to 78 K, is provided in Supplementary Figs 2 and 3 of the Supplementary Information. While above 198 K the output characteristics show either weak or no gate voltage dependence, at and below 198 K the devices display ‘textbook' n-type output characteristics. Similarly, typical p-type output characteristics are observed at 98 K and lower temperatures (Fig. 2b and Supplementary Fig. 3). Both p- and n-type transfer characteristics are independent of gate field from room temperature down to 258 K. This is reflected in the measurement by large hysteresis loops, which do not close when transitioning from the hole- to the electron-dominated transport gate voltage ranges and vice versa. Below 258 K, however, both n- and p-type transfer characteristics show a closed hysteresis loop. Hysteresis of n- and p-type transfer characteristics is substantially reduced below 198 and 98 K, respectively, consistent with the observation of ambipolar output characteristics (Fig. 2b and Supplementary Fig. 3). Induced carrier density of ∼3.8 × 1016 cm−2, maximum Ion/Ioff∼105 and current density of ∼830 A cm−2 (estimated for a ∼2 nm accumulation layer thickness) are obtained from standard transistor analysis at 198 K. These values are comparable to those previously reported for 2D hybrid organic–inorganic perovskites characterized at room temperature39,40. Note that, although our low-temperature measurements clearly demonstrate the ambipolar nature of CH3NH3PbI3, previous studies have shown that carrier concentration can vary by up to six orders of magnitudes depending on the ratio of the methylammonium halide and lead iodine precursors and thermal annealing conditions, thus resulting in preferential p-type or n-type transport characteristics46.

Figure 2. FET characteristics.

Figure 2

Open in a new tab

(a,b) Transfer (a) and output (b) characteristics obtained at 78 K. The n-type output characteristics (right panel) were measured at Vgs=40–100 V (Vgs=40 V black, Vgs=60 V red, Vgs=80 V blue, Vgs=100 V magenta), whereas the p-type output characteristics (left panel) are measured at Vgs=−40 V to −100 V (Vgs=−40 V black, Vgs=−60 V red, Vgs=−80 V blue, Vgs=−100 V magenta). Solid and dashed curves are measured with forward and backward sweeping, respectively. See Supplementary Information for the full set of FET characteristics as a function of temperature.

Temperature-dependent electron and hole mobilities were extracted from the forward sweeping of transfer characteristics at Vds=20 V and Vds=−20 V using the standard transistor equation at linear regime47. The resulting values are shown in Fig. 3a. Note that mobilities were not extracted from backward sweeping curves to avoid misleading results due to the large hysteresis. Also, mobilities at higher Vds (that is, in the saturation regime) were not extracted due to the difficulty to identify linear and saturation regimes at all investigated temperatures. A statistical analysis of the distribution of mobility values extracted from independent measurements across four different devices is shown in Supplementary Fig 4. Although some variability in the absolute values of electron and hole mobilities is observed from device to device, their relative magnitude and temperature dependence show consistent trends. From Fig. 3a, both electron and hole mobilities increase by a factor of ∼100 from room temperature to 198 K. Below 198 K, there is no further improvement of electron mobility, whereas hole mobility shows an additional tenfold increase. We attribute the improvement of mobility at low temperature to the removal of screening effects arising from the ionic transport of methylammonium cations. The phonon energy of methylammonium cation was estimated to be ∼14.7 meV from previous combination of density function theory (DFT) and Raman studies48. The observation of weak improvement of field-effect mobilities below 198 K (Ethermal=16.7 meV) is therefore consistent with the quenching of phonon interactions related to the organic cations. This is also in agreement with the weakening of field-switchable photovoltaic effects at low temperature33, strongly suggesting that field-effect transport is phonon limited at room temperature. Despite the remarkable improvement of field-effect mobilities, hysteresis was not completely removed at the lowest temperature investigated. This could be due to the untreated semiconductor–dielectric interface, which is known to affect semiconductor film morphology, number of trap states and surface dipoles, similar to the case of organic FET devices47. The reduction of trap density in single crystal30,31 and large grain size thin films32 enormously enhances stability of photovoltaic devices. Thus, improvement of bulk crystallinity is also expected to reduce hysteresis of FETs, with proper control of the morphology of the semiconductor–dielectric interface, where the nanometre thin field-effect transport channel is created47. Both hole and electron mobilities extracted in the linear regime at 78 K are slightly smaller than the corresponding saturation regime mobilities (μe,linear/μe,saturation=6.7 × 10−2/7.2 × 10−2 cm2 V−1 s−1 and μh,linear/μh,saturation=6.6 × 10−3/2.1 × 10−2 cm2 V−1 s−1, extracted at Vds=± 20 V for linear regime and Vds=±80 V for saturation regime from Fig. 2a). A previous study of spin-coated hybrid perovskite channels indicated linear regime mobility values 1 to 2 orders of magnitude lower than in the saturation regime39. The suppression of the linear regime mobility is presumably associated to grain-boundary effects, which give rise to a large concentration of traps. Thus, our reported linear regime mobilities set a lower limit for electron and hole mobilities of CH3NH3PbI3.

Figure 3. Experimental and theoretical field-effect mobility and band structures of CH3NH3PbI3.

Figure 3

Open in a new tab

(a) Temperature dependence of field-effect electron and hole mobilities, extracted from the forward sweeping of transfer characteristics at Vds=20 V and Vds=−20 V, respectively. (b) Calculated temperature dependence hole (red curves) and electron (black curves) mobility in tetragonal (T=300 to 160 K) and orthorhombic (T=160 to 77 K) phases of CH3NH3PbI3. The crystal unit cells of the two phases are shown as insets. (c, d) Band structures of the tetragonal (c) and orthorhombic (d) phases obtained by DFT-Perdew–Burke–Ernzerhof method with (solid curves) and without (dotted curves; W/o) spin-orbital coupling (SOC).

DFT modelling and mobility computation

To better understand the transport data, we estimated the mobility of CH3NH3PbI3 for both tetragonal and orthorhombic crystallographic phases using semi-classical Boltzmann transport theory49, upon deducing charge carrier effective masses and electron (hole)-phonon coupling. Electron and hole effective masses listed in Supplementary Table 1 were derived by quadratic fitting of the band structure dispersion (Fig. 3c,d); the corresponding fitting parameters are summarized in Supplementary Table 2. The average effective mass of electrons (tetragonal: 0.197 m0, orthorhombic: 0.239 m0) is consistently smaller than the one of holes (tetragonal: 0.340 m0, orthorhombic: 0.357 m0), similar to a previous report48,50. The resulting mobilities (Fig. 3b) increase at lower temperatures due to the Boltzmann activation energy (see Computational Methods section), in agreement with the trend of our experimental results. Although the calculated mobilities are substantially larger than the experimental values in Fig. 3a, calculations reflect fairly well the relative magnitude of electron versus hole mobility, as well as the different mobility of the two crystallographic phases. Within the entire temperature range investigated, electron mobilities exceed hole mobilities by approximately a factor of two, and increase by nearly one order of magnitude below the phase transition temperature (μe=2,577−11,249 cm−2 V−1 s−1 and μh=1,060−4,630 cm−2 V−1 s−1 for the orthorhombic phase and μe=466−2,046 cm−2 V−1 s−1 and μh=140−614 cm−2 V−1 s−1 for the tetragonal phase). The small experimental values can be partly attributed to the increase of effective masses by elastic carrier−phonon scattering, which is expected in real crystals because of defects and disorder induced by the organic components, as well as carrier–carrier scattering at high-electron and hole concentrations51. Formation of segregation pathways for hole and electron transport owing to the ferroelectric methylammonium cation could also elongate the carrier drifting path, hence lower carrier mobilities52. In addition, polycrystalline domains typical of solution-processed CH3NH3PbI3 thin films (Fig. 1a,b) are likely to weaken the electronic coupling between grains, requiring charge carriers to hop along and across domain boundaries, further reducing the effective carrier mobility. This is consistent with observation of giant photoinduced modulation of the dielectric constant, which was attributed to localized polaron hopping with relatively small activation energy53.

EL characteristics of LE-FET

The excellent ambipolar characteristics shown by the CH3NH3PbI3 FET at low temperature (Fig. 2) are rather encouraging for the realization of light-emitting devices operating under balanced carrier injection6,18,19,20,21,22,23. In particular, large carrier injection via charge accumulation at the semiconductor–dielectric interface is known to be an effective way to achieve bright and fast-switchable EL, and to optimize the spatial location of the carrier recombination zone in organic gate-assisted LE-FETs54,55. In LE-FET devices, ambipolar channels are formed simultaneously by proper source-drain and gate biasing. Under perfectly balanced conditions, holes and electrons injected from opposite electrodes recombine in the middle of the FET channel, thus defining a very narrow radiative emission zone, as depicted in Fig. 1d. The brightness of emission as well as the spatial position of the radiative recombination zone can be tuned by gate and drain-source biases47. LE-FET structures have proved to improve the lifetime and efficiency of light-emitting materials, thanks to the large electrical injection achievable, and the possibility to optimize and balance charge carrier recombination compared with conventional LED devices42,56. Combined with the ease of integration as nanoscale light sources in optoelectronic and photonic devices, this makes LE-FETs a very promising concept for applications in optical communication systems, solid-state lighting and electrically pumped lasers56,57.

Indeed, our CH3NH3PbI3 FETs emit light when operated in their ambipolar regime at low temperature (78–178 K). Typical EL spectra are displayed in Fig. 4. Note that no light emission could be observed above 198 K, most likely due to the ionic screening effects discussed earlier, so that low-temperature operation is necessary at this stage. Ionic screening is likely to be reduced in films with higher crystallinity as those recently reported30,31, potentially enabling perovskite LE-FET operation up to room temperature. The emission spectra of the LE-FET are consistent with direct recombination of injected electrons and holes into the perovskite-active region. At the lowest temperature investigated (78 K), the EL spectrum shows three peaks centred at 750 nm (Peak 1), 780 nm (Peak 2) and 800 nm (Peak 3), with distinct amplitudes and spectral positions at the various temperatures. Although Peak 1 and Peak 3 appear only below 158 K, Peak 2 dominates the EL spectra at higher temperatures. A similar behaviour was very recently observed in photoluminescence spectra of CH3NH3PbI3 films and single crystals58,59, and related to the structural transition from a low-temperature orthorhombic phase to a high-temperature tetragonal phase occurring around 162 K. Occurrence of this phase transition is predicted by density functional theory60,61 (see also DFT calculations in Fig. 3c,d) and was confirmed to occur in the temperature ranges of 150–170 K for CH3NH3PbI3 and 120–140 K for hybrid CH3NH3PbI3−xClx by light absorption studies6. Thus, their characteristic temperature dependence suggests that Peak 1 and Peak 3 in our EL measurements are due to bound excitons in the low-temperature orthorhombic phase, whereas Peak 2 may be related to free excitons in the high temperature, smaller bandgap tetragonal phase59. To quantify the relative intensity and spectral energy of the three emission peaks as a function of temperature, we analysed the EL spectra by a deconvoluted Gaussian fitting (see Gaussian curves in Fig. 4 and corresponding fitted parameters in Supplementary Fig. 5). Although Peak 1 shows the expected blue shift at the lowest temperatures, its temperature dependence in the intermediate range 118–178 K is rather complicated (Supplementary Fig. 5a). Peak 2 position slightly blue shifts over the whole temperature region, whereas Peak 3 shows a significant red shift in the 138–78 K region. Moreover, although the Gaussian full-width at half-maximum of Peak 1 reduces at lower temperatures, the full-width at half-maximum of Peak 2 and Peak 3 shows the opposite behaviour (Supplementary Fig. 5b), as previously seen in low-temperature photoluminescence measurements58,59. At this stage, the anomalous spectral shift and broadening of the EL peaks and the nature of the three peaks as a function of temperature are not completely understood, and further investigations are needed to reveal their nature.

Figure 4. Low-temperature electroluminescence spectra of CH3NH3PbI3 LE-FET.

Figure 4

Open in a new tab

EL spectra collected at Vds=100 V, Vgs=100 V, normalized to their maximum peak. The spectra were fitted by three Gaussian curves (solid lines). The shift in peak position of the 750 nm peak (Peak 1, blue triangles), the 780 nm peak (Peak 2, red circles) and the 800 nm peak (Peak 3, black squares) is indicated by the dashed lines.

Light emission from FET channel

To achieve simultaneous hole and electron injection in a LE-FET, the local gate potential at drain and source electrodes must be larger than the threshold voltage of either of the charge carrier (that is, |Vd|>|Vth,h| and Vs>Vth,e, or Vd>Vth,e and |Vs|>|Vth,h|)47. Under this condition, drain-source and gate voltages are tuned to control the injected current density of both carriers, which manipulate the spatial position of the emission zone as well as the EL intensity47. Figure 5 shows microscope images of the emission zone of the LE-FET recorded at 158 K under different biasing conditions. Despite the grainy light emission pattern due to the polycrystalline nature of the film (Fig. 1a,b), the EL emission zone can be clearly identified from the images. For a fixed gate bias of Vgs=100 V (Fig. 5a–c), the emission zone is mainly concentrated near the drain electrode when Vds is small (Fig. 5a). This is due to the limited injection of holes resulting from the relative low absolute local gate potential at the drain electrode |Vd|. By increasing Vds, |Vd| increases, thus more holes are injected into the active channel and the EL intensity increases (Fig. 5b). Further increase of hole injection extends the emission area to the centre of the channel, enhancing the EL intensity even further (Fig. 5c). Conversely, for a fixed drain-source voltage of Vds=100 V (Fig. 5d–f), the injected electron and hole current densities can no longer be regulated independently. Figure 5d shows extremely bright emission from nearby the drain electrodes because of the overwhelming density of injected electrons recombining with a comparatively lower density of injected holes. Decreasing the gate voltage reduces the local gate potential at the source electrode Vs and increases |Vd|, thus decreasing electron injection and increasing hole injection. This pushes the emission zone to the centre of the active channel and reduces the EL intensity as overall current density decreases (Fig. 5e). A further reduction of gate voltage pushes the emission zone closer to the source electrode, further weakening the EL intensity (see Fig. 5f). Continuous-frame videos showing the variation of EL intensity and position of the emission zone sweeping Vds from 0 to 100 V at constant Vgs=100 V and sweeping Vgs from 0 to 100 V at constant Vds=100 V are provided as Supplementary Movies 1 and 2. This demonstrates that full control of charge carrier injection and recombination in CH3NH3PbI3 LE-FET can be easily achieved by adjusting its biasing conditions.

Figure 5. Optical images of CH3NH3PbI3 LE-FET emission zone at T=158 K.

Figure 5

Open in a new tab

(a–c) Frame images extracted from a video recorded while sweeping Vds from 0 to 100 V at constant Vgs=100 V; the corresponding values of Vds are indicated in the panels. (d–f) Frame images extracted from a video recorded while sweeping Vgs from 0 to 100 V at constant Vds=100 V; the corresponding values of Vgs are indicated in the panels; note that the contrast of the metal contacts was slightly enhanced for clarity. See Supplementary Movies 1 and 2 for the source real-time videos of the measurements. Scale bars, 200 μm.

In summary, we fabricated high-quality hybrid perovskite FETs and used them to determine intrinsic transport parameters of CH3NH3PbI3, which are of great relevance to electro-optic devices (including solar cells). Our main findings include the ambipolar nature of charge transport, the understanding of the origin and suppression of screening effects associated to the presence of ionic cations, the direct determination of electron and hole mobilities and their temperature dependence, and the effect of structural phase transition on the electronic properties of CH3NH3PbI3, all in good agreement with first-principle DFT calculations. Furthermore, bright EL owing to radiative recombination within the transistor channel was demonstrated under balanced charge injection. We believe this demonstration of a CH3NH3PbI3 LE-FET paves the way to the realization of solution-processed hybrid perovskite light-emitting devices such as high-brightness light-emitting diodes and electrical injection lasers. More work will be needed in this direction to minimize ionic screening, improve thin film crystallinity and optimize device architecture, for instance employing staggered FET configurations to increase carrier injection density47 or integrating surface microstructures for light management.

Methods

Perovskite deposition

The organic precursor methylammonium iodide CH3NH3I was synthetized by mixing 10 ml of methylamine solution (CH3NH2, 40% in methanol, Tokyo Chemical Industry, Co., Ltd) and 14 ml of hydroiodic acid (57% wt in water, Sigma-Aldrich). The reaction was accomplished in ice bath for 2 h under magnetic stirring, and the solvent removed with a rotary evaporator (1 h at 60 mbar and 60 °C). The product was purified by dissolution in ethanol and recrystallization with diethylether, repeating the washing cycle six times. After filtration, the resulting white powder was dried in vacuum oven at 60 °C for 24 h. Thin film of CH3NH3PbI3 deposited on clean electrodes pre-patterned SiO2 substrates. A 20% wt CH3NH3PbI3 solution was prepared mixing stoichiometric amounts of CH3NH3I and PbI2 (99%, Sigma-Aldrich) in a solvent mixture of γ-butyrolactone and dimethylsulfoxide (7:3 volume ratio) and stirred overnight at 100 °C. To obtain continuous and uniform films, the solvent engineering technique was used14. The solution was spin-coated on the substrate using a two-step ramp: 1,000 r.p.m. for 10 s, 5,000 r.p.m. for 20 s. Toluene was drop-casted on the substrate during the second step. The resulting film was finally annealed at 100 °C for 30 min.

Perovskite characterization

Morphological analysis was performed with a FEI Helios 650 Nanolab SEM with 10 KV acceleration voltage and a scanning probe microscope Digital Instrument Dimension V (AFM analysis). The software WSxM was used for editing and plotting of the AFM images. The X-ray diffraction structural spectra were obtained using a diffractometer BRUKER D8 ADVANCE with Bragg-Brentano geometry employing Cu Kα radiation (l=1.54,056 Å), a step increment of 0.02°, 1 s of acquisition time and sample rotation of 5 min−1.

FET fabrication

Heavily p-doped Si substrates with thermally grown SiO2 (500 nm) layer were cleaned by two rounds of sonication in acetone and iso-propyl alcohol (20 min each round, and then dried under nitrogen flow. Interdigitated electrodes (L=80 and 100 μm, W=20 mm) were patterned using conventional photolithography. Electrodes of Ni (10 nm) and Au (50 nm) were thermally evaporated. The substrates were then undergoing lift-off process to obtain the desired electrodes. Before the spin coating of the active materials, an oxygen plasma cleaning treatment was performed on the substrate, for 1 min, to improve the wetting of the surface and obtain flatter and homogeneous perovskite thin film (see perovskite deposition).

Temperature-dependent FET measurements

FET devices were mounted into a liquid nitrogen-cooled Linkam Stage (FTIR 600) that allow to scan FET operating temperature of the device from 300 K down to 77 K. The FET electrical characteristics were acquired with Agilent B2902A Precision Source/Measure Unit in dark environment. The data were then analysed with OriginPro software.

EL measurement

The EL spectra were acquired using the Nikon eclipse LV100 microscope with LU plan fluor × 10 objectives, whereas the FET were enclosed in the Linkam Stage and FET electrical behaviour was controlled using Agilent B2902A Precision Source/Measure Unit. EL emission signal was focused into optic fibre that coupled to USB2000 Ocean Optics to record EL spectra. All EL spectra were measured with 1 s integration time over three averages. The optical images and videos were taken and acquired by Thorlabs DCC1545M High-Resolution USB2.0 CMOS Camera with weak illumination to enhance the optical contrast.

Computational method

The DFT calculations have been carried out by the Perdew–Burke–Ernzerhof generalized gradient approximation using plane-wave self-consistent field (PWSCF) code implemented in the Quantum ESPRESSO package62. For the structural optimization and band structure calculations, ultrasoft pseudopotentials including scalar-relativistic or full-relativistic effect were used to describe electron–ion interactions with electronic orbitals of H (1s1); O, N and C (2s2, 2p2); I (5s2, 5p2) and Pb (5d10, 6s2, 6p2)63. The plane wave energy cutoff of wave function (charge) was set to be 40 (300) Ry. The crystal cell parameters were a=b=8.81 Å, and c=12.99 Å for tetragonal phase (I4/mcm space group); and a=8.77 Å, b=8.56 Å and c=12.97 Å for the orthorhombic phase (Pnma space group) of bulk CH3NH3PbI3. The Monkhort-Pack scheme k-meshes are 4 × 4 × 4 for these two phases. The crystal cell and atomic positions were optimized until forces on single atoms were smaller than 0.01 eV Å−1. The molecular graphics viewer VESTA was used to plot molecular structures.

The effective masses for electron (Inline graphic) and hole (Inline graphic) were estimated by fitting of the dispersion relation of Inline graphicfrom band structures in Fig. 3 along the directions Γ-X, Γ-Z and Γ-M for tetragonal phase and Γ-X and Γ-Z for orthorhombic phase together with average values in these different routes. The carrier lifetime was evaluated by the semi-classical Boltzmann transport theory49. The only contribution of acoustic phonons was considered in evaluating scattering lifetime, where the charge carrier density (n) and mobility (μ) are approximated as27,64

graphic file with name ncomms8383-m4.jpg
graphic file with name ncomms8383-m5.jpg
graphic file with name ncomms8383-m6.jpg
graphic file with name ncomms8383-m7.jpg
graphic file with name ncomms8383-m8.jpg

kB is the Boltzmann constant, e is the elementary charge, T is the temperature, ℏ is the Planck constant and ξ is the reduced chemical potential; m* is the density of state effective mass, Inline graphic is the conductivity effective mass, Inline graphic is the band effective mass; B is the bulk modulus (B=∂2E/∂V2), Inline graphicis the electron−phonon (or hole−phonon) coupling energy (Inline graphic, n, m and l power integer indices, Eg is the electronic band gap and ζ the reduced carrier energy. Note that the generalized gradient approximation method including spin-orbital coupling yields largely underestimated values of the band gaps. Detailed estimate of the band gap values would require many-body perturbation theory (GW method)49,50. However, as the band structure is not significantly affected by GW correction, our calculations of the effective mass and mobility are still reliable.

Additional information

How to cite this article: Chin, X.Y. et al. Lead iodide perovskite light-emitting field-effect transistor. Nat. Commun. 6:7383 doi: 10.1038/ncomms8383 (2015).

Supplementary Material

Supplementary Information

Supplementary Figures 1-5 and Supplementary Tables 1-2

ncomms8383-s1.pdf (877.9KB, pdf)
Supplementary Movie 1

Drain-source-modulated light emission from the FET channel. Video recorded while loop-sweeping Vds from 0 to 100 V at constant Vgs=100 V.

Download video file (7.4MB, mov)
Supplementary Movie 2

Gate-modulated light emission from the FET channel. Video recorded while loop-sweeping Vgs from 0 to 100 V at constant Vds = 100 V.

Download video file (6.8MB, mov)

Acknowledgments

Research was supported by NTU (NAP startup grant M4080511), the Singapore Ministry of Education (MOE2013-T2-044 and MOE2011-T3-1-005) and the Singapore-Berkeley Research Initiative for Sustainable Energy (SinBeRISE) CREATE Programme. We are grateful to Nripan Mathews, Pablo Boix, Mario Caironi and Annamaria Petrozza for the useful discussions, to Stefano Vezzoli and Saleem Umar for their help with electroluminescence measurements, and to Liu Hailong for assistance with SEM imaging.

Footnotes

Author contributions C.S. and X.Y.C. generated the original idea and designed the experiment. X.Y.C. fabricated the FET devices and gathered all transport and electroluminescence data. D.C. synthesized the perovskite precursors, prepared and characterized the films. J.Y. performed DFT modelling and mobility calculations. A.B. analysed the electroluminescence data. All the authors contributed to interpretation of the results and writing of the manuscript. A.B. and C.S. supervised the work.

References

  1. Green M. A., Ho-Baillie A. & Snaith H. J. The emergence of perovskite solar cells. Nat. Photon 8, 506–514 (2014). [Google Scholar]
  2. Gao P., Gratzel M. & Nazeeruddin M. K. Organohalide lead perovskites for photovoltaic applications. Energy Environ. Sci. 7, 2448–2463 (2014). [Google Scholar]
  3. Lee M., Miyasaka T., Murakami T., Snaith H. & Teuscher J. Efficient hybrid solar cells based on meso-superstructured organometal halide perovskites. Science 338, 643–647 (2012). [DOI] [PubMed] [Google Scholar]
  4. Stranks S. D. et al. Electron-hole diffusion lengths exceeding 1 micrometer in an organometal trihalide perovskite absorber. Science 342, 341–344 (2013). [DOI] [PubMed] [Google Scholar]
  5. Xing G. et al. Long-range balanced electron- and hole-transport lengths in organic-inorganic CH3NH3PbI3. Science 342, 344–347 (2013). [DOI] [PubMed] [Google Scholar]
  6. D'Innocenzo V., Srimath Kandada A. R., De Bastiani M., Gandini M. & Petrozza A. Tuning the light emission properties by band gap engineering in hybrid lead halide perovskite. J. Am. Chem. Soc. 136, 17730–17733 (2014). [DOI] [PubMed] [Google Scholar]
  7. Gonzalez-Pedro V. et al. General working principles of CH3NH3PbX3 perovskite solar cells. Nano Lett. 14, 888–893 (2014). [DOI] [PubMed] [Google Scholar]
  8. Liu M., Johnston M. B. & Snaith H. J. Efficient planar heterojunction perovskite solar cells by vapour deposition. Nature 501, 395–398 (2013). [DOI] [PubMed] [Google Scholar]
  9. Zhou H. et al. Interface engineering of highly efficient perovskite solar cells. Science 345, 542–546 (2014). [DOI] [PubMed] [Google Scholar]
  10. Kim H.-S., Im S. H. & Park N.-G. Organolead halide perovskite: new horizons in solar cell research. J. Phys. Chem. C 118, 5615–5625 (2014). [Google Scholar]
  11. Kojima A., Teshima K., Shirai Y. & Miyasaka T. Organometal halide perovskites as visible-light sensitizers for photovoltaic cells. J. Am. Chem. Soc. 131, 6050–6051 (2009). [DOI] [PubMed] [Google Scholar]
  12. Burschka J. et al. Sequential deposition as a route to high-performance perovskite-sensitized solar cells. Nature 499, 316–319 (2013). [DOI] [PubMed] [Google Scholar]
  13. Boix P. P., Nonomura K., Mathews N. & Mhaisalkar S. G. Current progress and future perspectives for organic/inorganic perovskite solar cells. Mater. Today 17, 16–23 (2014). [Google Scholar]
  14. Jeon N. J. et al. Solvent engineering for high-performance inorganic–organic hybrid perovskite solar cells. Nat. Mater. 13, 897–903 (2014). [DOI] [PubMed] [Google Scholar]
  15. Heo J. H. et al. Efficient inorganic-organic hybrid heterojunction solar cells containing perovskite compound and polymeric hole conductors. Nat. Photon 7, 486–491 (2013). [Google Scholar]
  16. Salim T. et al. Perovskite-based solar cells: impact of morphology and device architecture on device performance. J. Mater. Chem. A 3, 8943–8969 (2015). [Google Scholar]
  17. Luo J. et al. Water photolysis at 12.3% efficiency via perovskite photovoltaics and Earth-abundant catalysts. Science 345, 1593–1596 (2014). [DOI] [PubMed] [Google Scholar]
  18. Tan Z.-K. et al. Bright light-emitting diodes based on organometal halide perovskite. Nat. Nano 9, 687–692 (2014). [DOI] [PubMed] [Google Scholar]
  19. Gil-Escrig L. et al. Efficient photovoltaic and electroluminescent perovskite devices. Chem. Commun. 51, 569–571 (2015). [DOI] [PubMed] [Google Scholar]
  20. Hoye R. L. Z. et al. Enhanced performance in fluorene-free organometal halide perovskite light-emitting diodes using tunable, low electron affinity oxide electron injectors. Advan. Mater. 27, 1414–1419 (2015). [DOI] [PMC free article] [PubMed] [Google Scholar]
  21. Sutherland B. R., Hoogland S., Adachi M. M., Wong C. T. O. & Sargent E. H. Conformal organohalide perovskites enable lasing on spherical resonators. ACS Nano 8, 10947–10952 (2014). [DOI] [PubMed] [Google Scholar]
  22. Deschler F. et al. High photoluminescence efficiency and optically pumped lasing in solution-processed mixed halide perovskite semiconductors. J. Phys. Chem. Lett. 5, 1421–1426 (2014). [DOI] [PubMed] [Google Scholar]
  23. Xing G. et al. Low-temperature solution-processed wavelength-tunable perovskites for lasing. Nat. Mater. 13, 476–480 (2014). [DOI] [PubMed] [Google Scholar]
  24. Edri E. et al. Elucidating the charge carrier separation and working mechanism of CH3NH3PbI3−xClx perovskite solar cells. Nat. Commun. 5, 3461 (2014). [DOI] [PubMed] [Google Scholar]
  25. Bergmann V. W. et al. Real-space observation of unbalanced charge distribution inside a perovskite-sensitized solar cell. Nat. Commun. 5, 5001 (2014). [DOI] [PubMed] [Google Scholar]
  26. Giorgi G., Fujisawa J.-I., Segawa H. & Yamashita K. Small photocarrier effective masses featuring ambipolar transport in methylammonium lead iodide perovskite: a density functional analysis. J. Phys. Chem. Lett. 4, 4213–4216 (2013). [DOI] [PubMed] [Google Scholar]
  27. He Y. P. & Galli G. Perovskites for solar thermoelectric applications: a first principle study of CH3NH3Al3 (A=Pb and Sn). Chem. Mater. 26, 5394–5400 (2014). [Google Scholar]
  28. Wehrenfennig C., Eperon G. E., Johnston M. B., Snaith H. J. & Herz L. M. High charge carrier mobilities and lifetimes in organolead trihalide perovskites. Advan. Mater. 26, 1584–1589 (2014). [DOI] [PMC free article] [PubMed] [Google Scholar]
  29. Stoumpos C. C., Malliakas C. D. & Kanatzidis M. G. Semiconducting tin and lead iodide perovskites with organic cations: phase transitions, high mobilities, and near-infrared photoluminescent properties. Inorg Chem. 52, 9019–9038 (2013). [DOI] [PubMed] [Google Scholar]
  30. Dong Q. et al. Electron-hole diffusion lengths > 175 μm in solution grown CH3NH3PbI3 single crystals. Science 347, 967–970 (2015). [DOI] [PubMed] [Google Scholar]
  31. Shi D. et al. Low trap-state density and long carrier diffusion in organolead trihalide perovskite single crystals. Science 347, 519–522 (2015). [DOI] [PubMed] [Google Scholar]
  32. Nie W. et al. High-efficiency solution-processed perovskite solar cells with millimeter-scale grains. Science 347, 522–525 (2015). [DOI] [PubMed] [Google Scholar]
  33. Xiao Z. et al. Giant switchable photovoltaic effect in organometal trihalide perovskite devices. Nat. Mater. 14, 193–198 Advance online publication (2014). [DOI] [PubMed] [Google Scholar]
  34. Frost J. M., Butler K. T. & Walsh A. Molecular ferroelectric contributions to anomalous hysteresis in hybrid perovskite solar cells. APL Mater. 2, 081506 (2014). [Google Scholar]
  35. Snaith H. J. et al. Anomalous hysteresis in perovskite solar cells. J. Phys. Chem. Lett. 5, 1511–1515 (2014). [DOI] [PubMed] [Google Scholar]
  36. Shao Y., Xiao Z., Bi C., Yuan Y. & Huang J. Origin and elimination of photocurrent hysteresis by fullerene passivation in CH3NH3PbI3 planar heterojunction solar cells. Nat. Commun. 5, 5784 (2014). [DOI] [PubMed] [Google Scholar]
  37. Unger E. L. et al. Hysteresis and transient behavior in current-voltage measurements of hybrid-perovskite absorber solar cells. Energy Environ. Sci. 7, 3690–3698 (2014). [Google Scholar]
  38. Kagan C. R., Mitzi D. B. & Dimitrakopoulos C. D. Organic-inorganic hybrid materials as semiconducting channels in thin-film field-effect transistors. Science 286, 945–947 (1999). [DOI] [PubMed] [Google Scholar]
  39. Mitzi D. B., Dimitrakopoulos C. D. & Kosbar L. L. Structurally tailored organic−inorganic perovskites:  optical properties and solution-processed channel materials for thin-film transistors. Chem. Mater. 13, 3728–3740 (2001). [Google Scholar]
  40. Mitzi D. B. et al. Hybrid field-effect transistor based on a low-temperature melt-processed channel layer. Advan. Mater. 14, 1772–1776 (2002). [Google Scholar]
  41. Noh J. H., Im S. H., Heo J. H., Mandal T. N. & Seok S. I. Chemical management for colorful, efficient, and stable inorganic–organic hybrid nanostructured solar cells. Nano Lett. 13, 1764–1769 (2013). [DOI] [PubMed] [Google Scholar]
  42. Capelli R. et al. Organic light-emitting transistors with an efficiency that outperforms the equivalent light-emitting diodes. Nat. Mater. 9, 496–503 (2010). [DOI] [PubMed] [Google Scholar]
  43. Verlaak S., Cheyns D., Debucquoy M., Arkhipov V. & Heremans P. Numerical simulation of tetracene light-emitting transistors: a detailed balance of exciton processes. Appl. Phys. Lett. 85, 2405 (2004). [Google Scholar]
  44. Egger D. A., Edri E., Cahen D. & Hodes G. Perovskite solar cells: Do we know what we do not know? J. Phys. Chem. Lett. 6, 279–282 (2015). [DOI] [PubMed] [Google Scholar]
  45. Kutes Y. et al. Direct observation of ferroelectric domains in solution-processed CH3NH3PbI3 perovskite thin films. J. Phys. Chem. Lett. 5, 3335–3339 (2014). [DOI] [PubMed] [Google Scholar]
  46. Wang Q. et al. Qualifying composition dependent p and n self-doping in CH3NH3PbI3. Appl. Phys. Lett. 105, 163508 (2014). [Google Scholar]
  47. Zaumseil J. & Sirringhaus H. Electron and ambipolar transport in organic field-effect transistors. Chem. Rev. 107, 1296–1323 (2007). [DOI] [PubMed] [Google Scholar]
  48. Amat A. et al. Cation-induced band-gap tuning in organohalide perovskites: interplay of spin–orbit coupling and octahedra tilting. Nano Lett. 14, 3608–3616 (2014). [DOI] [PubMed] [Google Scholar]
  49. Wang H., Pei Y. Z., LaLonde A. D. & Snyder G. J. Weak electron-phonon coupling contributing to high thermoelectric performance in n-type PbSe. Proc. Natl Acad. Sci. USA 109, 9705–9709 (2012). [DOI] [PMC free article] [PubMed] [Google Scholar]
  50. Umari P., Mosconi E. & De Angelis F. Relativistic GW calculations on CH3NH3PbI3 and CH3NH3SnI3 perovskites for solar cell applications. Sci. Rep. 4, 4467 (2014). [DOI] [PMC free article] [PubMed] [Google Scholar]
  51. Ma J. & Wang L. W. Nanoscale charge localization induced by random orientations of organic molecules in hybrid perovskite CH3NH3PbI3. Nano Lett. 15, 248–253 (2014). [DOI] [PubMed] [Google Scholar]
  52. Frost J. M. et al. Atomistic origins of high-performance in hybrid halide perovskite solar cells. Nano Lett. 14, 2584–2590 (2014). [DOI] [PMC free article] [PubMed] [Google Scholar]
  53. Juarez-Perez E. J. et al. Photoinduced giant dielectric constant in lead halide perovskite solar cells. J. Phys. Chem. Lett. 5, 2390–2394 (2014). [DOI] [PubMed] [Google Scholar]
  54. Bisri S. Z., Piliego C., Gao J. & Loi M. A. Outlook and Emerging Semiconducting Materials for Ambipolar Transistors. Advanced Materials 26, 1176–1199 (2014). [DOI] [PubMed] [Google Scholar]
  55. Swensen J. S., Soci C. & Heeger A. J. Light emission from an ambipolar semiconducting polymer field-effect transistor. Appl. Phys. Lett. 87, 253511 (2005). [Google Scholar]
  56. Muccini M. A bright future for organic field-effect transistors. Nat. Mater. 5, 605–613 (2006). [DOI] [PubMed] [Google Scholar]
  57. Chen Z. Y. et al. Origin of the different transport properties of electron and hole polarons in an ambipolar polyselenophene-based conjugated polymer. Phys. Rev. B 84, 115211 (2011). [Google Scholar]
  58. Wu K. W. et al. Temperature-dependent excitonic photoluminescence of hybrid organometal halide perovskite films. Phys. Chem. Chem. Phys. 16, 22476–22481 (2014). [DOI] [PubMed] [Google Scholar]
  59. Fang H.-H. et al. Photophysics of organic-inorganic hybrid lead iodide perovskite single crystals. Advan. Funct. Mater., Published online (2015). [Google Scholar]
  60. Even J., Pedesseau L. & Katan C. Analysis of multivalley and multibandgap absorption and enhancement of free carriers related to exciton screening in hybrid perovskites. J. Phys. Chem. C 118, 11566–11572 (2014). [Google Scholar]
  61. Wang Y. et al. Density functional theory analysis of structural and electronic properties of orthorhombic perovskite CH3NH3PbI3. Phys. Chem. Chem. Phys. 16, 1424–1429 (2014). [DOI] [PubMed] [Google Scholar]
  62. Giannozzi P. et al. QUANTUM ESPRESSO: a modular and open-source software project for quantum simulations of materials. J. Phys. Condens. Mat. 21, 395502 (2009). [DOI] [PubMed] [Google Scholar]
  63. Garrity K. F., Bennett J. W., Rabe K. M. & Vanderbilt D. Pseudopotentials for high-throughput DFT calculations. Comp. Mater. Sci. 81, 446–452 (2014). [Google Scholar]
  64. Ravich Y. I., Efimova B. A. & Tamarche V. i. Scattering of Current Carriers and Transport Phenomena in Lead Chacogenides. Phys. Status Solidi B 43, 11–33 (1971). [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Supplementary Materials

Supplementary Information

Supplementary Figures 1-5 and Supplementary Tables 1-2

ncomms8383-s1.pdf (877.9KB, pdf)
Supplementary Movie 1

Drain-source-modulated light emission from the FET channel. Video recorded while loop-sweeping Vds from 0 to 100 V at constant Vgs=100 V.

Download video file (7.4MB, mov)
Supplementary Movie 2

Gate-modulated light emission from the FET channel. Video recorded while loop-sweeping Vgs from 0 to 100 V at constant Vds = 100 V.

Download video file (6.8MB, mov)