Scientific Reports logoLink to Scientific Reports
. 2015 Jan 5;5:7580. doi: 10.1038/srep07580

Ultra-low percolation threshold in ferrite-metal cofired ceramics brings both high permeability and high permittivity

Liang Wang 1, Yang Bai 1,a, Xuefei Lu 1, Jiang-Li Cao 1, Li-Jie Qiao 1
PMCID: PMC4650947  PMID: 25557935

Abstract

High permeability and high permittivity are hard to be achieved simultaneously, either in single-phased materials or in composite materials, such as ferrite-ferroelectric ceramic composites and ferrite-metal percolative composites. In this work, ultra-low percolation threshold is achieved in NiZnCu ferrite-Ag cofired ceramics, which endows the composite with both high permeability and high permittivity by minimizing the negative effect of nonmagnetic conductive fillers on magnetic properties. The percolation threshold is controlled by the temperature matching between ferrite densification and Ag melting. A thin and long percolative net forms between large ferrite grains under a proper cofiring process, which brings a low percolation threshold of 1.21vol%, more than one order of magnitude lower than the theoretical value of 16vol%. Near the ultra-low threshold, the composite exhibits a high permeability of 585 and a high permittivity of 78.

Permittivity and permeability are the two most important features for electromagnetic materials. Recently, the trend in electronics towards small size and high integration promotes the demand for multifunctional electromagnetic materials, such as those with both high permeability and permittivity. Since the desired property cannot be obtained in single-phased materials, people turn to composites, including ferrite-ferroelectric ceramic composites and ceramics-metal percolative composites, but the achievements were still not satisfying. In ferrite-ferroelectric ceramic composites, the permeability and permittivity are determined by the values of each phase and the volume ratio1,2,3,4,5,6. However, the dilution effect prevents producing high permeability and high permittivity simultaneously, although the ferrite phase has high permeability and the ferroelectric phase has high permeability, which follows the effective medium theory. When there is 10 vol% ferroelectric ceramics, the permeability of the composite will be only 1/5 of that of the pure ferrite; and vice versa. For example, Zheng et al. prepared the composites with semiconductive ferrite grains coated by insulating ferroelectric thin films and a ultra-high permittivity of ~75000 was achieved due to a microstructure similar to boundary layer capacitor, while the permeability of 162 is not high enough5. Actually, the percolation system is an efficient way to modify the electromagnetic properties nonmonotonically. When the amount of conductive fillers in an insulating matrix approaches a threshold, the composite exhibits a giant permittivity due to the formation of percolative capacitor6. This has been well proved in various composite materials, such as polymer-metal composites7,8,9,10, polymer-carbon composites11,12,13,14 and ceramic-metal composites6,15,16,17. However, up to now, the percolation system fails to produce high permeability. In 2005, Shen et al. developed a ferrite-Ni-polymer three-phased composite with electric and magnetic double percolation, and enhanced the permeability by adding Ni in this serial of composites, but the permeability is still low (μ ≈ 30) due to the nonmagnetic polymer matrix18. Here, we prepared NiZnCu ferrite-Ag cofired ceramics with an ultra-low percolation threshold of 1.21 vol%, which is one order of magnitude lower than the reported values of ceramic based composites. Because the ultra-low Ag amount minimizes the negative effect of nonmagnetic conductive filler on the magnetic properties of ferrite matrix, the composite exhibits a really high permeability of 585 and a high permittivity of 78 near the ultra-low threshold.

In this work, Ag with melting point of 961°C was used as conductive filler in the composites because of the high conductivity and high resistance to oxidation. Two types of NiZnCu ferrites, Ni0.2Zn0.6Cu0.2Fe2O4 (NCZ1) and Ni0.35Zn0.6Cu0.05Fe2O4 (NCZ2), were used as soft magnetic matrix; they had different densification temperatures of 935°C and 1050°C, but similar electromagnetic properties. To control the morphology of Ag filler, the samples were prepared by two-step sintering strategy19, where they were heated to a higher temperature T1, immediately cooled to a lower temperature T2, and then hold for two hours.

Results and discussions

At the percolation threshold, the conductive fillers connect each other and form a conductive net in the insulating matrix, so that the composite abruptly changes from a dielectric to a conductor. The break of resistivity is clear in the dependence of electric resistivity (Fig. 1), so that the percolation threshold fc of the samples was characterized and listed in Table 1. In the conductivity measurement, no electrode was pasted on both sides of the sample to confirm the formation of fully percolative net. If electrodes were pasted on both sides of the sample, partial percolation net would also induce a conductive character in the measurement and lead to a false value of percolation threshold. The NCZ2-Ag composite has fc = 9.5 vol%, which is lower than the theoretical value of 16 vol%, but is similar to Shen's result18. On the contrary, the NCZ1-Ag composites have much lower fc, which originates from the distinctive morphology of Ag in the composites. It originates from the remarkably different Ag morphology. Ag forms a long and thin net homogeneously in the NZC1 ferrite matrix (Fig. 2 (a), (b)); while it is agglomerated to droplets and dispersed among NCZ2 grains (Fig. 2 (c), (d)).

Figure 1. The frequency dependence of electric resistivity of (a) NCZ1-Ag and (b) NCZ2-Ag composites, as well (c) their composition dependence.

Figure 1

Open in a new tab

Table 1. The percolation thresholds of the composites.

    T1 (°C) T2 (°C) heating rate (°C/min) fc
1 NCZ1 1050 935 10 3.5%
2 NCZ1 1100 935 10 1.3%
3 NCZ1 1150 935 10 2%
4 NCZ1 1100 935 1 2.5%
5 NCZ1 1100 935 5 2%
6 NCZ1 1150 1035 10 2%
7 NCZ1 1150 1135 10 2%
8 NCZ2 1200 1050 10 9.5%
Open in a new tab

Figure 2. The backscattered electron (a & c) images and energy-dispersive x-ray spectroscopy (b & d) of NZC1-Ag (a & b) and NZC2-Ag composites (c & d) both with 2 vol% Ag.

Figure 2

Open in a new tab

In the backscattered electron images, the white part is silver and the grey part is ferrite. The inset in (c) shows the wetting angle of Ag on ferrite at 970°C.

The fc in a percolation system is not only affected by the volume ratio of conductive fillers but also by the morphology. If there are spherical fillers, the theoretical fc is ~16 vol%. If the fillers have large aspect ratio, the fc drops dramatically20. The fc for rodlike fillers with radius of r and length of L can be expressed as:

graphic file with name srep07580-m1.jpg

where B = 2.7, V = πr2L and Vex = πrL2 21. It was reported that the polymer-carbon nanotubes composites had ultra-low low fc of ~1 vol%11,12. However, such low fc has never been reported in ceramic based composite, because carbon nanotubes will burn out in the high temperature sintering process. In this work, the long and thin percolative net is formed in NCZ1-Ag composite under a well controlled cofiring process, and endows it with an ultra-low fc.

The fc is determined by the Ag morphology in composites, which is controlled by the temperature matching between ferrite densification and Ag melting. NZC1 ferrite has largely densified when Ag melts, i.e. grains grow obviously and stack compactly. In a dense microstructure, liquid Ag extends along the narrow grain gaps because of the extruding of large ferrite grains, so that a thin and long percolative net forms easily, as illustrated in Fig. 3. On the contrary, NZC2 ferrite does not begin densifying as Ag melts, whose measured relative density is only 62% at 960°C. In a loose matrix full of pores and gaps, liquid Ag is agglomerated to droplets to minimize the surface energy due to the poor wettability with ferrite (inset in Fig. 2 (c)). Finally, spherical Ag fillers are dispersed among ferrite grains (Fig. 3), which works against forming percolative net.

Figure 3. Schematic of Ag melting process in dense or loose matrix.

Figure 3

Open in a new tab

The sintering process also affects the percolative character by microstructure modification. As shown in Table 1, faster heating rate improves the growth of large grains and helps limiting the Ag particle distribution, so the fc is lower. If T1 ≥ 1150°C or T2 ≥ 1035°C, Ag agglomeration occurs to prevent forming percolative net. To achieve ultra-low fc, T1 = 1100°C and T2 = 935°C are selected for further investigation.

The permittivity of the NCZ1-Ag composites with 0~1.25 vol% Ag is shown in Fig. 4. The permittivity increases rapidly above fAg>1.1 vol% and reaches a maximum of 78 at fAg = 1.2 vol%, which is much higher than that of pure ferrite (~19). The variation of permittivity can be characterized by the power law as follow,

graphic file with name srep07580-m2.jpg

where εmis the permittivity of ferrite matrix, s is the critical exponent22,23. Then a precise percolation threshold of fc = 1.21% and s = 0.11 are obtained based on the fitting of experimental data. Such low threshold is similar to some carbon nanotube-polymer composites11, but is much lower than the reported values in ceramic based composites6,15,16,17.

Figure 4. Variation of the permittivity of NZC1-Ag composites with Ag volume ration.

Figure 4

Open in a new tab

The frequency dependence of permittivity and loss tangent is shown in Fig. 5. The permittivity decreases with increasing frequency, following the percolation theory that as fAg→fc,

graphic file with name srep07580-m3.jpg

where w = 2πv, v is the frequency, and u is a constant. In addition, at the percolation threshold, the dielectric loss is still small. The Maxwell-Wangner effect also contributes for the permittivity in low frequency range.

Figure 5. Frequency dependence of (a) permittivity and (b) loss for NCZ1-Ag composites.

Figure 5

Open in a new tab

Fig. 6 shows the permeability of the NZC1-Ag and NZC2-Ag composites. The permeability decreases with increasing Ag amount. Introducing nonmagnetic Ag in the soft magnetic ferrite matrix will interrupt the magnetic lines of force and produces the demagnetizing field, which can be regarded as an increase of equivalent magnetocrystalline anisotropy. The effects of magnetocrystalline anisotropy K1 and saturation magnetization Ms on the permeability follow24,

graphic file with name srep07580-m4.jpg

Since the induced field around metal inclusions weakens rapidly with distance, the thin percolation net can minimize the negative effect on magnetic property. The NCZ1-Ag composite has a high permeability of 585 near the fc, about 55% of pure ferrite's permeability. By contrast, for NCZ2-Ag composite, the permeability drops ~80%, from 735 to 130. It indicates that the ultra-low fc is efficient to maintain a high permeability in a ferrite-metal composite. That is helpful to produce composites with both high permeability and permittivity.

Figure 6. Frequency dependence of permeability for NCZ1-Ag and NCZ2-Ag composites.

Figure 6

Open in a new tab

In summary, the NiZnCu ferrite-Ag cofired ceramics were successfully prepared and its percolation threshold was decreased to an ultra-low value of 1.21 vol%, one order of magnitude lower than the theoretical value, and is much lower than previous reports in ceramic based composites. The fc is determined by the Ag morphology in composites, which is controlled by the temperature matching between ferrite densification and Ag melting. If Ag melts in a dense matrix, it tends to form a long and thin conductive net, so that the fc drops to a very low value. The composite exhibits a really high permeability of 585 and a high permittivity of 78 near the fc. This work provides a way to produce materials with both high permeability and permittivity to promote the development of multifunctional and miniaturizated electronic products. In addition, it founds a simple and effective method to control the percolation threshold in a large range for ceramic based composites, which is helpful to enhance their performance and widen the application.

Methods

Preparation of cofired ceramic composite

The Ni0.4-xZn0.6CuxFe2O4 (where x = 0.05 and 0.2) powders were prepared by the solid reaction method. The analytical grade raw materials of Fe2O3, NiO, ZnO and CuO were weighted according to the molecular formula and mixed in ball mill for 4 h using a planet mill. After calcined at 760°C for 4 h, the obtained ferrite powders were mixed with spherical silver powder (1 μm, 99.9%) in ball mill. Then, the mixture was granulated using 5% polyvinyl alcohol solution as binder-lubricant. After dry-press, the pellet and toroidal samples were sintered in a two-step sintering strategy.

Characterization of the samples

The bulk density of the sintered samples was measured using Archimedes' method. The wettability was measured by the high temperature wetting angle measurement instrument (OCA 20LHT-SV). The microstructure of the samples was observed by scanning electron microscope (SEM, JSM-6510A). The permeability, permittvity and conductivity were measured by Agilent 4294A impedance analyzers.

Author Contributions

Y.B. designed the experiments and analyzed the results. L.W. prepared the samples and characterized the samples. X.L. characterized some of the samples. J.L.C. analyzed some results. L.J.Q. guided the work and analysis. Y.B. wrote the paper.

Acknowledgments

This work was supported by grants from the National Science Foundation of China (51172020 and 51372018), the National Youth Top-Notch Talent Support Program, the Program for New Century Excellent Talents in University (NCET-12-0780), the Fundamental Research Funds for the Central Universities (FRF-TP-09-028A), Beijing Higher Education Young Elite Teacher Project (YETP0414), and the Program for Changjiang Scholars and Innovative Research Team in University (IRT1207).

References

  1. Qi X. et al. ferroelectric ferromagnetic composite material with significant permeability and permittivity. Adv. Func. Mater. 14, 920–926 (2004). [Google Scholar]
  2. Shen J. H., Bai Y., Zhou J. & Li L. T. Magnetic properties of a novel ceramic ferroelectric-ferromagnetic composite. J. Am. Ceram. Soc. 88, 3440–3443 (2005). [Google Scholar]
  3. Bai Y. et al. A ferromagnetic ferroelectric cofired ceramic for hyper-frequency. J. Appl. Phys. 101, 083907 (2007). [Google Scholar]
  4. Huang J. Q. et al. A percolative ferromagnetic-ferroelectric composite with significant dielectric and magnetic properties. Adv. Mater. 19, 437–440 (2007). [Google Scholar]
  5. Zheng H. et al. Super high threshold percolative ferroelectric/ferromagnetic composite ceramics with outstanding permittivity and initial permeability. Angew. Chem. Int. Ed. 48, 8927–8930 (2009). [DOI] [PubMed] [Google Scholar]
  6. Pecharromán C. et al. New percolative BaTiO3-Ni composites with a high and frequency-independent dielectric constant (εr ≈ 80000). Adv. Mater. 13, 1541–1544 (2001). [Google Scholar]
  7. Panda M., Srinivas V. & Thakur A. K. Surface and interfacial effect of filler particle on electrical properties of polyvinylidene fluoride/nickel composites. Appl. Phys. Lett. 93, 242908 (2008). [Google Scholar]
  8. Deepa K. S. et al. Effect of interparticle distance and interfacial area on the properties of insulator conductor composites. Appl. Phys. Lett. 94, 142902 (2009). [Google Scholar]
  9. Huang X., Jiang P. & Xie L. Ferroelectric polymer/silver nanocomposites with high dielectric constant and high thermal conductivity. Appl. Phys. Lett. 95, 242901 (2009). [Google Scholar]
  10. Li Y. et al. Large dielectric constant and high thermal conductivity in poly(vinylidene fluoride)/barium titanate/silicon carbide three-phase nanocomposites. ACS Appl. Mater. Interfaces 3, 4396–4403 (2011). [DOI] [PubMed] [Google Scholar]
  11. Yuan J. K. et al. High dielectric permittivity and low percolation threshold in polymer composites based on SiC-carbon nanotubes micro/nano hybrid. Appl. Phys. Lett. 98, 032901 (2011). [Google Scholar]
  12. He F., Lau S., Chan H. L. & Fan J. High dielectric permittivity and low percolation threshold in nanocomposites based on poly(vinylidenefluoride) and exfoliated graphite nanoplates. Adv. Mater. 21, 710–715 (2009). [Google Scholar]
  13. Dang Z. M. et al. Giant dielectric permittivity in functionalized carbon- nanotube/electroactive-polymer nanocomposites, Adv. Mater. 19, 852–857 (2007). [Google Scholar]
  14. Huang Y. Y. & Terentjev E. M. Tailoring the electrical properties of carbon nanotube-polymer composites. Adv. Funct. Mater. 20, 4062–4068 (2010). [Google Scholar]
  15. Wang Z. et al. Ag nanoparticle dispersed PbTiO3 percolative composite thin film with high permittivity. Appl. Phys. Lett. 93, 222901 (2008). [Google Scholar]
  16. George S., James J. & Sebastian M. T. Giant permittivity of a bismuth zinc niobate–silver composite. J. Am. Ceram. Soc. 90, 3522–3528 (2007). [Google Scholar]
  17. Shi Z. C. et al. Random composites of nickel networks supported by porous alumina toward double negative materials. Adv. Mater. 24, 2349–2352 (2012). [DOI] [PubMed] [Google Scholar]
  18. Shen Y., Yue Z. X., Li M. & Nan C. W. Enhanced initial permeability and dielectric constant in a double-percolating Ni0.3Zn0.7Fe1.95O4-Ni-polymer composite. Adv. Funct. Mater. 15, 1100–1103 (2005). [Google Scholar]
  19. Chen I. W. & Wang X. H. Sintering dense nanocrystalline ceramics without final-stage grain growth. Nature 404, 168–171 (2000). [DOI] [PubMed] [Google Scholar]
  20. Li J. et al. Correlations between percolation threshold, dispersion state, and aspect ratio of carbon nanotubes. Adv. Func. Mater. 17, 3207–3215 (2007). [Google Scholar]
  21. Nan C. W. Physics of inhomogeneous inorganic materials. Prog. Mater. Sci. 37, 1–116 (1993). [Google Scholar]
  22. Dang Z. M., Lin Y. H. & Nan C. W. Novel ferroelectric polymer composites with high dielectric constants. Adv. Mater. 15, 1625–1629 (2003). [Google Scholar]
  23. Pecharroman C. & Moya J. S. Experimental evidence of a giant capacitance in insulator-conductor composites at the percolation threshold. Adv. Mater. 12, 294–297 (2000). [Google Scholar]
  24. Bai Y., Zhang W. J., Qiao L. J. & Zhou J. The low-fired Y-type hexagonal ferrite for hyper frequency applications. J. Adv. Ceram. 1, 100–109 (2012). [Google Scholar]

Articles from Scientific Reports are provided here courtesy of Nature Publishing Group