CoxFey@C Composites with Tunable Atomic Ratios for Excellent Electromagnetic Absorption Properties

Hualiang Lv 1, Guangbin Ji 1,a, Haiqian Zhang 1, Meng Li 1, Zhongzheng Zuo 1, Yue Zhao 1, Baoshan Zhang 2, Dongming Tang 2, Youwei Du 3
PMCID: PMC4676003  PMID: 26659124

Abstract

The shell on the nano-magnetic absorber can prevent oxidation, which is very important for its practical utilization. Generally, the nonmagnetic shell will decrease the integral magnetic loss and thus weaken the electromagnetic absorption. However, maintaining the original absorption properties of the magnetic core is a major challenge. Here, we designed novel and facile CoxFey@C composites by reducing CoxFe3−xO4@phenolic resin (x = 1, 0.5 and 0.25). High saturation magnetization value (Ms) of CoxFey particle, as a core, shows the interesting magnetic loss ability. Meanwhile, the carbon shell may increase the integral dielectric loss. The resulting composite shows excellent electromagnetic absorption properties. For example, at a coating thickness of 2 mm, the RLmin value can reach to −23 dB with an effective frequency range of 7 GHz (11–18 GHz). The mechanisms of the improved microwave absorption properties are discussed.

Solving the oxidization problem of magnetic metal has aroused extreme attention in the field of electromagnetic absorption. It is well known that an ideal electromagnetic absorber should have a high impedance matching (more electromagnetic waves can be incident on the absorber with less reflection) and strong electromagnetic wave attenuation1,2,3,4. Of all the absorbers, magnetic materials have aroused more attention than pure dielectric absorbers because they have clear impedance matching properties and a desired magnetic loss ability5. Thus, many works related to magnetic materials have been widely studied in recent years. Currently, coin-like iron with a minimum reflection loss of −53 dB was reported by our group6 and the sphere-like CoxFe3−xO4 with an optimal reflection loss value of −41.098 dB7 has been produced by Ji et al. Meanwhile, Tong and coworkers reported a flower-like Co with a RLmin value of −40.25 dB8. Nevertheless, despite the fact that these magnetic absorbers have achieved fascinating electromagnetic absorption properties, most magnetic metals (i.e.: Fe, Co, Ni) are restricted by the poor chemical stability and easily convert into nonmagnetic oxide, i.e. α-Fe2O3, Co2O3, etc. This process will seriously affect their magnetic properties and magnetic loss ability. Moreover, many stable ferrites such as CoFe2O4 have poor absorption properties due to their low Ms (usually below 100 emu/g). It should be explained that a high Ms is beneficial to impedance matching behavior and permeability values including the real part (μ′) and the imaginary part (μ″)9,10. The big μ′ and μ″ values are thought to be the main reason why the magnetic materials are superior to the dielectric materials (i.e.: ZnO, CuS, TiO2) according to the following equations11:

graphic file with name srep18249-m1.jpg
graphic file with name srep18249-m2.jpg

Here, M represents magnetization, H is the external magnetic field, and σ stands for the phase lag angle of magnetization behind external magnetic field. From equations (1, 2), we conclude that a high magnetization value is quite important. To solve the oxidation problem, a core-shell structure may be an effective strategy. For example, Yang et al. utilized the SiO2 shell to protect the cube-like Fe out of air12. Similarly, the SiO2 shell has been widely used in other types of absorbers including Ni and Fe3O413,14. Unfortunately, these results revealed that an insulated SiO2 coating shell is harmful to the integral μ′, μ″ as well as to dielectric. Thus, other efforts have focused on replacing SiO2 with improved high dielectric loss materials.

Most dielectric materials (e.g. TiO2 and ZnO) are form shells and show high chemical stability due to their matched lattice and surface free energy15. Next, the high dielectric loss shell can make up a slight decrease in the magnetic loss. Among these absorbers, Fe3O4-based core-structures have been widely studied including Fe3O4@ZrO216, Fe3O4@TiO217, Fe3O4@SnO218, and Fe3O4@CuSiO319. Of course, other magnetic/dielectric structures have also been reported including Fe@SnO220 and Co@ZnO21. In fact, these pristine magnetic cores did not show the interesting complex permeability value due to their smaller Ms. After introducing the non-magnetic material, the integral magnetic loss ability will further decrease. Therefore, a high Ms magnetic core is needed. Of the magnetic materials, FeCo shows a higher Ms than most magnetic materials. In our previous work, we successfully synthesized the hexagonal cone-like Fe50Co50 with a high Ms value of 225 emu/g—higher than the theoretical value of 218 emu/g. Surprisingly, the corresponding μ′ of Fe50Co50 is more than 2 at the early frequency region, which is larger than most of magnetic materials (usually at 1.5). Furthermore, the Fe50Co50 displays better air-stability at room temperature than Fe or Co single state22.

In this study, the CoxFey@C composite was obtained easily by using CoxFe3−xO4 as the core. The carbon shell with tunable thickness in the final composite has the following advantages versus other dielectric materials. 1) Most dielectric shells cannot exist in the acid or alkaline environment while carbon can endure such unfriendly conditions. 2) The higher dielectric loss ability makes the composite exhibit multiple-attenuation ability. 3) The lower density of the carbon shell may lead to a light-weight absorber. 4) The electromagnetic absorption properties can be easily tuned by adjusting the carbon shell thickness. Such a composite offers high stability and strong absorption performance. In additional, the high Ms of CoxFey may result in the magnetic loss. Furthermore, the Co and Fe atomic ratio can be tuned by adjusting the x value in the CoxFe3−xO4.

Results

Detailed information about the representative CoxFe3−xO4 (CoFe2O4 nanospheres) is listed in Fig. 1a–d. From Fig. 1a, all diffraction peaks can be matched well with the CoFe2O4 planes (PDF card No.: 22–1086). At the same time, the nanoscale CoFe2O4 presents a 60–80 nm sphere (Fig. 1b–d).

Figure 1. The XRD patterns (a) TEM images (b,c) and size distribution (d) of the pure CoFe2O4.

Figure 1

Open in a new tab

The XRD patterns of these samples are shown in Fig. 2. We infer that the carbon shell does not influence the crystal structure of CoFe2O4. That is, the CoFe2O4@C and CoFe2O4 share identical diffraction peaks. As for the CoxFey@C composite, the obvious diffraction peaks at 44.6 and 64.9° belong to the iron-cobalt phase. No any other impurity peaks including Fe or Co oxidation peaks can be observed indicating the high-purity of these samples. The inset reveals that the main diffraction peaks exhibit a slight left shift from S1 to S3, which is consistent with Aguirre’s report23. To demonstrate the anti-oxidation of CoxFey@C, sample S1 has been further characterized on different days (Fig. 2b). Obviously, there is little change after S1 is exposed to air for 15, 30, and 45 days. The atomic ratios of each sample tested by ICP (Co/Fe ratio: S1: 1/1.97; S2: 1/5.01; and S3: 1/11.05) are close to the initial Fe3+ and Co2+ ratio (S1: CoFe2; S2: CoFe5; and S3: CoFe11).

Figure 2. The XRD patterns of S0-S1 samples (a) and the XRD dates of the S1 tested at different days (b).

Figure 2

Open in a new tab

The detailed core-shell structures of these products were investigated by TEM. In Fig. 3a, the carbon shell with a shell thickness of 9 nm is obvious. As described in Fig. 3b, CoFe2 was surrounded by a clear carbon layer. The thickness of the carbon shell is up to 23 nm (see Fig. 3d). Meanwhile, it is worth noting that the size of the S1 is slightly decreased versus the original CoFe2O4. Such a change may be attributed to the loss of the O element and the structure shrinkage during reduction. As for S2 and S3, the corresponding carbon shell thicknesses are 16 and 12 nm, respectively.

Figure 3. The TEM images of the S0 (a), S1 (b–d), S2 (e) and S2 (f).

Figure 3

Open in a new tab

Actually, the thickness of the carbon is tunable by adjusting the mass of resorcinol as seen in Fig. 4a,b. When the resorcinol dosage reduces to 0.25 and 0.1 g, the carbon shell thickness of S1 decreases to 19 and 16 nm, respectively (See Fig. 4).

Figure 4. The TEM images of S1 prepared with different resorcinol mass (a) 0.25 g (b) 0.1 g.

Figure 4

Open in a new tab

Figure 5 compares the magnetization loops of the composites. Generally, the Ms value of pure CoFe2O4 is below 80 emu/g24. When CoFe2O4 was coated with nonmagnetic carbon, the magnetization values decrease abruptly. Here, the magnetization value of S0 is only 37 emu/g, which dampens its magnetic loss ability. However, the magnetization values of S1-S3 still remain at high (160~170 emu/g), close to the Ms value of bulk Co (162 emu/g). The larger magnetization value is not only beneficial for impedance matching, but also results in strong magnetic loss ability. It is also known that a high coercive force value (Hc) will make the resonance peak shift to a high frequency region. Figure 5b confirms that all the Hc values of CoxFey@C composites are bigger than 100 Oe, and S3 has the highest Hc value of 175 Oe. The other two samples are 134 and 167 Oe for S1 and S2, respectively.

Figure 5. The M-H loops (a) −10 kOe-10 kOe (b) −400 Oe-400 Oe.

Figure 5

Open in a new tab

Figure 6 describes the relationship between the RL data and frequency of these samples. As seen in Fig. 6a–d, the absorption peaks of each sample move to the lower frequency region as the thickness increases. This can be explained by the 1/4 wavelength equation25.

Figure 6. The reflection loss data (a–d) and effective frequency region (e–h) of S0–S3.

Figure 6

Open in a new tab
graphic file with name srep18249-m3.jpg

Here, tm and fm are the matching thickness and frequency of the RLmin peaks, and c is the velocity of light. With the carbon modification, all samples enhance the electromagnetic absorption properties versus pure CoFe2O4 (See Fig. S1). However, the CoxFey@C composites (S1~S3) offer an interesting RLmin value and effective frequency width at all the tested frequency. For example, it is clear that in Fig. 6, the optimal RLmin value of S0 is no more than −20 dB at a larger coating layer of 3 mm (RLmin<−10 dB means 90% of attenuation). But, the optimal RLmin value for S3 is close to −38 dB with a relatively thin coating layer of 2.5 mm. The optimal RLmin values of S1 and S2 are up to −28 and −27 dB with a thickness of 3.0 and 2.0 mm, respectively.

The effective frequency range for an ideal electromagnetic absorber (RLmin < −10 dB) is another important factor to evaluate in the performance of the absorber (Fig. 6 e-h). The yellow area is indexed to the effective frequency width. It is apparent that the yellow area of the S1-S3 samples is much broader than that of the S0. Under a thin coating thickness of 2 mm, the frequency width of the S1-S3 samples is larger than 2 GHz. In particular, the frequency width of S1 is up to 7 GHz (from 11 to 18 GHz) while the S0 is no more than 1 GHz (17–18 GHz). In addition, the as-prepared S1 composite shows a superior absorption property among other similar composites as illustrated in Table 126,27,28,29,30.

Table 1. The comparison of the RLmin and effective frequency of other reported magnetic@dielectric composites.

Sample Thickness RLmin Effective Frequency Ref.
FeNi@C 2.0 mm −33.0 dB <1.0 GHz 26
Fe3O4@C 2.0 mm −20.7 dB ∼4.8 GHz 27
Fe@C 2.7 mm −25.0 dB <3.0 GHz 28
Ni@C 2.0 mm −32.0 dB ∼4.3 GHz 29
Fe55Co45@C 2.5 mm −15.8 dB ∼2.0 GHz 30
Fe60Co40@C 2.5 mm −16.4 dB ∼5.0 GHz 30
This study 2.0 mm −30.0 dB ∼7.0 GHz  
Open in a new tab

Discussion

In Fig. 7, the relevant electromagnetic parameters explain the enhancement of the electromagnetic absorption properties. When these magnetic cores are coated with the high dielectric carbon, ε′ and ε″ increase but to different extents. Within the tested frequency range, the ε′ value of the CoxFey@C samples are quite a bit bigger than that of S0 (6.2-4). This implies the increasing energy storage ability. The corresponding ε′ values are ranged from 11.5-7, 14-13, and 19.5-7.4 for S1, S2, and S3, respectively. It is generally believed that ε″ is related to its dielectric ability. As shown in Fig. 7b, these CoxFey@C composites achieve an ideal ε″ value across most of the frequency spectrum. The obvious resonance peaks are benefit the high ε″ values. Because of this, the ε″ values of the S1-S3 samples span a wide range. For instance, 1–10.5 for S1, 0.3–9 for S2 and 2–5 for S3—the S0 sample has a relatively narrow region of 2–2.8 (Fig. S2). In this framework, the larger ε″ of S1-S3 mainly come from the high dielectric carbon shell.

Figure 7. The electromagnetic parameters of S0-S3: real part (a)/imaginary part (b) of permittivity and real part (c) and imaginary part (d) of permeability.

Figure 7

Open in a new tab

It is widely believed that pure carbon has excellent electric conduction properties. As a result, the carbon shell will increase the ε″ value after being composited with materials. Meanwhile, the metallic feature of the CoxFey alloy core will strengthen the electric conduction and therefore further increase its ε″ value. In addition, the presence of resonance peaks among the S1~S3 samples also favor the intensity ε″ value.

Many factors may cause these resonance peaks, including ionic, electronic, atomic, interface and dipole relaxation polarization31. Whereas at high frequency regions, these resonance peaks are impossible to separate from electronic and atomic polarization (below GHz)32. Therefore, they probably result from the interface and dipole polarization. The presence interface between the CoxFey core and carbon shell is apt to induce interface polarization according to similar literature33,34. At the same time, the loss of O during the reduction process may generate many lattice defects. These lattice defects act as polarization centers that are reflected in increasing ε′ values. Meanwhile, these dipoles will alter their direction under an external electromagnetic field. This procedure increases the attenuation of the electromagnetic energy ability35. At the same time, the carbon shell and FexCoy shows different electrical conductivity and polarity properties. Under the external magnetic field, the composite will lead to strong interface polarization effects. Figure 7c,d reveal the real/imaginary values of permeability (μ′/μ″). The higher magnetization values of the CoxFey@C composites are significantly better at magnetic loss. The μ′ value of the S1 is up to 1.6-0.9, 1.3-1.0 for S2 and 1.6-1.1 for S3—values that are much larger than S0 (1.1-0.9). Meanwhile, the CoxFey@C composites share better magnetic loss advantages with all the μ″ values of CoxFey@C samples located at 0.7-0.1 and quite bigger than S0 (below 0.1) and other types of pure magnetic materials including hollow cobalt (~0.2)36, nanoring-like Fe3O4 (0-0.4)37, and hexagonal flake Fe (0.15-0.3)38.

In addition, there are at least two resonance peaks in these composites. These peaks are susceptible to magnetic loss due to eddy current effects, natural resonance and exchange resonance39. While eddy current effects can attenuate a small part of incidence electromagnetic wave, it also generates eddy current and hinders electromagnetic waves entering the absorber. The eddy current can be expressed as40:

graphic file with name srep18249-m4.jpg

If the resonance peak comes from the eddy current, C0 will be a constant. As seen from Fig. 8, these values of C0 change with increasing frequency and thus can rule out the eddy current. For CoxFey@C nanocomposites, the natural resonance is always weak and can be neglected. The small size (less than 100 nm) can arouse strong exchange resonance. In particular, the lower magnetic anisotropy may increase the magnetic moment coupling and lead to obvious exchange resonance. Thus, we can deduce that both peaks are exchange resonance.

Figure 8. The C0-f curve of S1–S3.

Figure 8

Open in a new tab

The enhanced electromagnetic absorption property is directly controlled by the impedance matching ratio and attenuation constant α. This means that the integrated attenuation effect of magnetic and dielectric loss is based on the following equation41,42:

graphic file with name srep18249-m5.jpg

Versus S0, the larger ε′ and ε″ values of S1-S3 are not favorable for impedance matching. Due to the contribution of magnetization properties, the impedance matching ratio values of S1-S3 are smaller than S0, Nevertheless, the CoxFey@C composites present fascinating attenuation ability according to Fig. 9a. Figure 9b confirms all the tested frequencies, and the attenuation values of S1-S0 are much bigger than S0.

Figure 9. The impedance matching (a) and attenuation constant (b) of S0–S3.

Figure 9

Open in a new tab

Based on this discussion, we conclude that the enhanced electromagnetic absorption mechanism can be ascribed to the following aspects. First, the high Ms of CoxFey core can retain high magnetization values in the composite and further improve the impedance matching. Meanwhile, the obvious magnetic loss also raises the electromagnetic wave loss ability that originates from its high magnetization. Nevertheless, the magnetization value of S0 decreases to a lower value (less than 40 emu/g) after the carbon coating. Such a lower magnetization value make it weak at magnetic loss in each μ′ and μ″ value. Second, ultra-small size of the CoxFey alloy is apt to form an obvious exchange resonance that effectively suppresses current eddy effects. These multi-resonance peaks also play a vital role on the RLmin value and frequency width. Third, due to the high dielectric loss carbon shell, the presence interface between CoxFey and carbon may lead to remarkable interface polarization. The presence of lattice defects resulted from the loss of O that cause dipole polarization. The appearance of multi-resonance in the imaginary part is very favorable for electromagnetic wave loss. However, for CoFe2O4@C, we can hardly observe any obvious resonance peaks. This can be explained in that CoFe2O4 is the spinel structure and Co2+ occupies an A site while Fe3+ remains in the B site. The electron will transfer from the A to the B and increase polarization43. This type of polarization is weak and occurs in the interior of a single spindle structure. As a result, the CoFe2O4 core is not sensitive to the carbon shell and thus impairs the interface polarization.

Conclusions

In summary, we took advantage of the high chemical stability and dielectric loss feature of carbon to coat magnetic metals and prevent oxidation. In this context, the high Ms of CoxFey (CoFe2, CoFe5, and CoFe11) as the core increases the integral magnetic loss ability. The electromagnetic absorption between CoxFey@C and CoFe2O4@C demonstrates that the CoxFey@C is superior in microwave absorption at the RLmin with effective frequency. The enhanced microwave absorption can be attributed to the exchange resonance, interface and dipole polarization. The as-prepared sample has excellent stability after long-term air exposure.

Method

Ammonium hydroxide (NH4OH), glucose, formaldehyde, ferric chloride (FeCl3), cobalt acetate (Co(Ac)2), urea and ethylene glycol (EG), ethanol and resorcinol were purchased from the Sinopharm Chemical Reagent Co. All chemical regents were analytically pure and used without further purification.

CoxFe3−xO4 sphere-like nanoparticles preparation

The CoxFe3−xO4 sphere-like nanoparticles were synthesized by a simple solvthermal approach. The Co(Ac)2 and FeCl3 were mixed into a 30 mL EG solution for magnetic string 30 min. Then, before the mixed solution was transferred to 50 mL autoclave, 15 mmol urea was added into the solution. The autoclave was heated at 200 oC for 12 h. After the temperature cooled to room temperature, the precipitate was collected by magnetic separation. The representative CoFe2O4 was prepared when x was set to 1.

Synthesis of CoxFey@C

Initially, the 0.8 g of as-prepared CoxFe3−xO4 (X was set as 1, 0.5 and 0.25 and marked as S1, S2, and S3) were dispersed into a solution that contains 80 mL distilled water, 20 mL ethanol solution and 1 mL NH3.H2O with ultrasonic mixing for 1 h. Next, 0.5 g resorcinol and 3 mL formaldehyde were added to the above mixture for polymerization for 1 day. The generated CoxFe3−xO4@phenolic resin was reduced by hydrogen gas (VH2/VN2 = 10:90) at 500 °C for 2 h. The heating ramp ratio was controlled at 1 °C/min. For comparison, the most representative CoFe2O4@C (named as S0) was obtained in N2 atmosphere only and identical conditions.

Characterization

Phase analysis was conducted depending on the powder X-ray diffraction (XRD) patterns (Bruker D8 ADVANCE X-ray diffractometer) with Cu Kα radiation (λ = 0.154178 nm with 40 kV scanning voltage, 40 mA scanning current and scanning range from 20 to 80°). The core-shell features of these composites were detected with transmission electron microscope (TEM, JEM JEOL 2100). The magnetic properties of coercive force (Hc) and magnetization date were acquired by a vibrating sample magnetometer (VSM, Lakeshore, Model 7400 series) at room temperature (298 K). The atomic ratio of Fe and Co was measured with inductively coupled plasma (ICP, Optimal 5300DV).

Electromagnetic parameters tests

The S parameters including S11, S12, S21, and S22 were measured with an Agilent PNA N5224A vector network analyzer using the coaxial-line method. The samples were prepared by homogeneously mixing the paraffin wax and sample (mass ratio: 50:50) and then pressing into toroidal-shaped samples (Φout:7.0 mm, Φin:3.04 mm). Subsequently, the Agilent PNA software can process the ε′, ε″, μ′, μ″ values. Finally, the RL value with 2–3.5 mm can be determined by the following formulas44,45.

graphic file with name srep18249-m6.jpg
graphic file with name srep18249-m7.jpg

Here, Zin is the input impedance of the absorber, f is the frequency of the electromagnetic wave, d is the coating thickness of the absorber and c is the velocity of electromagnetic wave in free space. Terms εr (εr = ε′-jε″) and μr (μr = μ′-jμ″) are the complex permittivity and permeability of the absorber.

Additional Information

How to cite this article: Lv, H. et al. CoxFey@C Composites with Tunable Atomic Ratios for Excellent Electromagnetic Absorption Properties. Sci. Rep. 5, 18249; doi: 10.1038/srep18249 (2015).

Supplementary Material

Supplementary Information
srep18249-s1.doc (64.3KB, doc)

Acknowledgments

Financial support from the National Natural Science Foundation of China (No.: 11575085), the Aeronautics Science Foundation of China (No.:2014ZF52072), the Funding for Outstanding Doctoral Dissertation in NUAA(No.: BCXJ15-09), and the Priority Academic Program Development of Jiangsu Higher Education Institutions is gratefully acknowledged.

Footnotes

Author Contributions G.J. designed the material structure. H.L. performed the experiment. M.L., Z.Z. and Y.Z. collected the experimental data. B.Z. and D.T. measured the electromagnetic parameters. Y.D. analysed the VSM data. H.Z. provided insightful discussions for the dielectric loss. H.L. organized the manuscript. All authors contributed to preparing the manuscript.

References

  1. Zhao T. K. et al. Electromagnetic Wave Absorbing Properties of Amorphous Carbon Nanotubes. Sci. Rep. 4, 5619–5624 (2014). [DOI] [PMC free article] [PubMed] [Google Scholar]
  2. Lv H. L., Ji G. B., Zhang H. Q. & Du Y. W. Facile synthesis of a CNT@Fe@SiO2 ternary composite with enhanced microwave absorption performance. RSC. Adv. 5, 76836–76843 (2015). [Google Scholar]
  3. Wang L. et al. Hierarchical graphene@Fe3O4 nanocluster@carbon@MnO2 nanosheet array composites: synthesis and microwave absorption performance. Phys. Chem. Chem. Phys. 17, 5878–5886 (2015). [DOI] [PubMed] [Google Scholar]
  4. Tejendra K. G. et al. MnO2 decorated graphene nanoribbons with superior permittivity and excellent microwave shielding properties. J. Mater. Chem. A. 2, 4256–4263 (2014). [Google Scholar]
  5. Liu Y., Liu X. X., Li R., Wen W. & Wang X. J. Design and fabrication of carbon fiber/carbonyl iron core–shell structure composites as high performance microwave absorbers. RSC Adv. 5, 8713–8720 (2015). [Google Scholar]
  6. Lv H. L. et al. Facile synthesis of porous coin-like iron and its excellent electromagnetic absorption performance. RSC Adv. 5, 25936–25941 (2015). [Google Scholar]
  7. Ji R. L., Cao C. B., Chen Z., Zhai H. Z. & Ju B. Solvothermal synthesis of CoxFe3−xO4 spheres and their microwave absorption properties. J. Mater. Chem. C. 2, 5944–5953 (2014). [Google Scholar]
  8. Tong G. X. et al. Flower-like Co superstructures: Morphology and phase evolution mechanism and novel microwave electromagnetic characteristics. CrystEngComm. 14, 2071–2079 (2012). [Google Scholar]
  9. Zhang S. L. et al. Preparation of rugby-shaped CoFe2O4 particles and their microwave absorbing properties. J. Mater. Chem. A. 2, 18033–18039 (2014). [Google Scholar]
  10. Li G. M., Wang L. C., Li W. X., Ding R. M. & Xu Y. CoFe2O4 and/or Co3Fe7 loaded porous activated carbon balls as a lightweight microwave absorbent. Phys. Chem. Chem. Phys. 16, 12385–12392 (2014). [DOI] [PubMed] [Google Scholar]
  11. Lu B. et al. Influence of alloy components on electromagnetic characteristics of core/shell-type Fe–Ni nanoparticles. J. Appl. Phys. 104, 114313–114318 (2008). [Google Scholar]
  12. Yang Z. H., Li Z. W., Yu L. H., Yang Y. H. & Xu Z. C. Achieving high performance electromagnetic wave attenuation: a rational design of silica coated mesoporous iron microcubes. J. Mater. Chem. C. 2, 7583–7588 (2014). [Google Scholar]
  13. Zhao B., Shao G., Fan B. B., Zhao W. Y. & Zhang R. Investigation of the electromagnetic absorption properties of Ni@TiO2 and Ni@SiO2 composite microspheres with core–shell structure. Phys. Chem. Chem. Phys. 17, 2531–2539 (2015). [DOI] [PubMed] [Google Scholar]
  14. Ren Y. L. et al. Three-dimensional SiO2@Fe3O4 core/shell nanorod array/graphene architecture: synthesis and electromagnetic absorption properties. Nanoscale. 5, 12296–12303 (2013). [DOI] [PubMed] [Google Scholar]
  15. Liu J. W. et al. Microwave Absorption Enhancement of Multifunctional Composite Microspheres with Spinel Fe3O4 Cores and Anatase TiO2 Shells. Small. 8, 1214–1221 (2012). [DOI] [PubMed] [Google Scholar]
  16. Yu M. et al. Yolk–shell Fe3O4@ZrO2 prepared by a tunable polymer surfactant assisted sol–gel method for high temperature stable microwave absorption. J. Mater. Chem. C. 2, 7275–7283 (2014). [Google Scholar]
  17. Liu J. W. et al. Hierarchical Fe3O4@TiO2 Yolk–Shell Microspheres with Enhanced Microwave-Absorption Properties. Chem. Eur. J. 19, 6746–6752 (2013). [DOI] [PubMed] [Google Scholar]
  18. Chen Y. J. et al. Porous Fe3O4/SnO2 Core/Shell Nanorods: Synthesis and Electromagnetic Properties. J. Phys. Chem. C. 117, 10061–10064 (2009). [Google Scholar]
  19. Liu J. W. et al. Synthesis and Microwave Absorption Properties of Yolk−Shell Microspheres with Magnetic Iron Oxide Cores and Hierarchical Copper Silicate Shells. ACS Appl. Mater. Interfaces. 5, 2503−2509 (2013). [DOI] [PubMed] [Google Scholar]
  20. Qi X. S. et al. Controllable and Large-Scale Synthesis of Carbon Nanofibers, Bamboo-Like Nanotubes, and Chains of Nanospheres over Fe/SnO2 and Their Microwave-Absorption Properties. J. Phys. Chem. C. 114, 808–814 (2010). [Google Scholar]
  21. Wei T., Ji C. Q., Zhong W. & Liu J. M. High permittivity polymer embedded with Co/ZnO core/shell nanoparticles modified by organophosphorus acid. Appl. Phys. Lett. 91, 222907–222910 (2007). [Google Scholar]
  22. Lv H. L. et al. Hexagonal-cone like of Fe50Co50 with broad frequency microwave absorption: Effect of ultrasonic irradiation time. J. Alloys. Compds. 615, 1037–1042 (2014). [Google Scholar]
  23. Sirvent P. et al. Effective high-energy ball milling in air of Fe65Co35 alloys. J. Appl. Phys. 115, 17B505–17B507 (2014). [Google Scholar]
  24. Xi L., Wang Z., Zuo Y. L. & Shi X. N. The enhanced microwave absorption property of CoFe2O4 nanoparticles coated with a Co3Fe7–Co nanoshell by thermal reduction. Nanotechnology. 22, 045707–045712 (2011). [DOI] [PubMed] [Google Scholar]
  25. Lv H. L. et al. Coin-like α-Fe2O3@CoFe2O4 Core−Shell Composites with Excellent Electromagnetic Absorption Performance. ACS Appl. Mater. Interfaces. 7, 4744−4750 (2015). [DOI] [PubMed] [Google Scholar]
  26. Feng C. et al. Enhanced microwave absorption of flower-like FeNi@C nanocomposites by dual dielectric relaxation and multiple magnetic resonance. RSC Adv. 4, 22710–22715(2014). [Google Scholar]
  27. Li W. X. et al. Fabrication of Fe3O4@C core–shell nanotubes and their application as a lightweight microwave absorbent. RSC Adv. 4, 55738–55744 (2014). [Google Scholar]
  28. Zhang X. F. et al. Microstructure and microwave absorption properties of carbon-coated iron nanocapsules. J. Phys. D: Appl. Phys. 40, 5383–5387(2007). [Google Scholar]
  29. Zhang X. F. et al. Microwave absorption properties of the carbon-coated nickel nanocapsules. Appl. Phys. Lett. 89, 053115–053117 (2006). [Google Scholar]
  30. Jiang J. J. et al. Disorder-modulated microwave absorption properties of carbon-coated FeCo nanocapsules. J.Appl. Phys. 114, 17A514–17A516 (2014). [Google Scholar]
  31. Liu P., Zhou P. H., Xie J. L. & Deng L. J. Electromagnetic and absorption properties of urchinlike Ni composites at microwave frequencies. J. Appl. Phys. 111, 093905–093909 (2012). [Google Scholar]
  32. Duan Y. P., Liu Z., Jing H., Zhang Y. H. & Li S. Q. Novel microwave dielectric response of Ni/Co-doped manganese dioxides and their microwave absorbing properties. J. Mater.Chem. 22, 18291–18299 (2012). [Google Scholar]
  33. Du Y. C. et al. Shell Thickness-Dependent Microwave Absorption of Core−Shell Fe3O4@C Composites. ACS Appl. Mater. Interfaces. 6, 12997–13006 (2014). [DOI] [PubMed] [Google Scholar]
  34. Huang H. et al. Manipulated electromagnetic losses by integrating chemically heterogeneous components in Fe-based core/shell architecture. J. Appl. Phys. 113, 084312–084318 (2013). [Google Scholar]
  35. Wang G. S., Nie L. Z. & Yu S. H. Tunable wave absorption properties of β-MnO2 nanorods and their application in dielectric composites. RSC Advances. 2, 6216–6221(2012). [Google Scholar]
  36. He C. H. et al. Facile synthesis of hollow porous cobalt spheres and their enhanced electromagnetic properties. J. Mater. Chem. 22, 22160–22166 (2012). [Google Scholar]
  37. Yang Y., Yang Y., Xiao W. & Ding J. Microwave electromagnetic and absorption properties of magnetite hollow nanostructures. J. Appl. Phys. 115, 17A512–17A514 (2014). [Google Scholar]
  38. Fu L. S., Jiang J. T., Xu C. Y. & Zhen L. Synthesis of hexagonal Fe microflakes with excellent microwave absorption performance. CrystEngComm. 14, 6827–6832 (2012). [Google Scholar]
  39. Wen S. L., Liu Y., Zhang X. C., Cheng J. W. & Li H. Synthesis dual-nonlinear magnetic resonance and microwave absorption properties of nanosheet hierarchical cobalt particles. Phys. Chem. Chem. Phys. 16, 18333–18340 (2014). [DOI] [PubMed] [Google Scholar]
  40. Lv H. L., Ji G. B., Liu W., Zhang H. Q. & Du Y. W. Achieving hierarchical hollow carbon@Fe@Fe3O4 nanospheres with superior microwave absorption properties and lightweight features. J. Mater. Chem. C. 3, 10232–10241 (2015). [Google Scholar]
  41. Lv H. L. et al. Porous Three-Dimensional Flower-like Co/CoO and Its Excellent Electromagnetic Absorption Properties. ACS Appl. Mater. Interfaces. 7, 9776–9783 (2015). [DOI] [PubMed] [Google Scholar]
  42. Lv H. L., Ji G. B., Liang X. H., Zhang H. Q. & Du Y. W. A novel rod-like MnO2@Fe loading on graphene giving excellent electromagnetic absorption properties. J. Mater. Chem. C. 3, 5056–5064 (2015). [Google Scholar]
  43. Yang Z. H. et al. Optimization of ZnxFe3−xO4 Hollow Spheres for Enhanced Microwave Attenuation. ACS Appl. Mater. Interfaces. 6, 21911–21915 (2014). [DOI] [PubMed] [Google Scholar]
  44. Zhang L. L. et al. Facile synthesis of iron oxides/reduced graphene oxide composites: application for electromagnetic wave absorption at high temperature. Sci. Rep. 5, 9298–9295 (2015). [DOI] [PMC free article] [PubMed] [Google Scholar]
  45. Zhao X. C. et al. Excellent microwave absorption property of Graphene-coated Fe nanocomposites. Sci. Rep. 3, 3421–3425(2013). [DOI] [PMC free article] [PubMed] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Supplementary Materials

Supplementary Information
srep18249-s1.doc (64.3KB, doc)

Articles from Scientific Reports are provided here courtesy of Nature Publishing Group

RESOURCES