Morphology controlling method for amorphous silica nanoparticles and jellyfish-like nanowires and their luminescence properties

Haitao Liu 1, Zhaohui Huang 1,a, Juntong Huang 2, Song Xu 3, Minghao Fang 1, Yan-gai Liu 1, Xiaowen Wu 1,4, Shaowei Zhang 2
PMCID: PMC4778036  PMID: 26940294

Abstract

Uniform silica nanoparticles and jellyfish-like nanowires were synthesized by a chemical vapour deposition method on Si substrates treated without and with Ni(NO3)2, using silicon powder as the source material. Composition and structural characterization using field emission scanning electron microscopy, transmission electron microscopy, energy dispersive X-ray spectroscopy and fourier-transform infrared spectroscopy showed that the as-prepared products were silica nanoparticles and nanowires which have amorphous structures. The form of nanoparticles should be related to gas-phase nucleation procedure. The growth of the nanowires was in accordance with vapour-liquid-solid mechanism, followed by Ostwald ripening to form the jellyfish-like morphology. Photoluminescence and cathodoluminescence measurements showed that the silica products excited by different light sources show different luminescence properties. The emission spectra of both silica nanoparticles and nanowires are due to the neutral oxygen vacancies (≡Si-Si≡). The as-synthesized silica with controlled morphology can find potential applications in future nanodevices with tailorable photoelectric properties.

Nanomaterials, such as nanoparticles (NPs)1,2,3, nanowires (NWs)4,5,6 and nanofilms (NFs)7,8,9, have been received steadily growing attention as a result of their peculiar and fascination properties. They offer great application prospects in various fields, including biomedical, electrical and optical fields, etc.10,11 The morphologies of nanomaterials are of vital importance to their potential applications in different scopes. Efforts should be focused on the search for controlling synthesis of multifarious morphologies of one certain material by low cost and simple routes. In the past few years, researchers have witnessed significant advances in the morphology control synthesis of diverse nanomaterials including NPs, NWs, NFs, nanoporous materials, etc.12,13,14,15,16

As one type of the most important luminescence materials, silica nanomaterials have tremendous promise as indicators and photon sources for a number of biotechnological and information technology applications such as biological imaging, sensor technology, microarrays, and optical computing17,18,19,20,21. The morphology and size controlled products can be specifically designed to satisfy different specifications for their applications. For instance, many researches focused on the biomedical applications of silica NPs as a result of their biocompatibility, low toxicity and scalable availability17,20. Silica NWs have potential application in high-resolution optical heads of scanning near-field optical microscopes and low dimensional wave-guides in future integrated optical devices for their intense and stable blue light emission at room temperature22,23,24.

Here we report a simple process which could control synthesis of silica NPs and NWs. Silicon powder and p(111) Si substrate was used as the starting materials. The use of a catalyst is the key factor in the morphology control. The detailed growth mechanism for the jellyfish-like NWs morphology was discussed. Photoluminescence (PL) and Cathodoluminescence (CL) were used to characterize optical properties of the as-prepared NPs and NWs products, which are of benefit to understanding not only the relationship between morphology and luminescence properties of silica nanostructures, but also their optical properties in different excitation source. We think these researches could provide a facile method for the synthesis of silica NPs and NWs, and are a great help for the application of silica nanostructures in fluorescence labeling medicine or new generation nanodevices with tunable photoelectric properties.

Results and Discussion

In this research, without using templates, relatively uniform silica nanoparticles can be synthesized on Si wafer when the Si substrate was untreated by Ni(NO3)2 solution. Analysis by FESEM showed that in the absence of template, silica could form on silicon substrate as preferentially loose particles (Fig. 1a–c) with a nanosized diameter concentrated within the range of ~250–400 nm (Fig. 1d). The nanoparticles were composed of 32.1% Si and 67.9% O as revealed by EDS (inset in Fig. 1c), corresponding to the stoichiometric composition of SiO2.

Figure 1.

Figure 1

Open in a new tab

Typical low magnification FESEM image (a and b) and high magnification FESEM image (c) of the as-prepared products. The inset in (b) is EDS spectrum of the NPs. (d) Size distribution of as-synthesized silica NPs.

Figure 2a is a typical low magnification TEM image, showing the typical ball-like geometry of silica with diameter range from 200 nm–300 nm. High-resolution TEM analysis (Fig. 2b) of silica particles provided an evidence for their amorphous structure. The corresponding SAED pattern of the ball-like particle is shown in Fig. 2c, which proofed their amorphous structure. The EDS analysis reveals that the NP was composed of 39.34% Si and 60.66% O. Together with HRTEM, SAED and the EDS results measured in SEM and TEM, we roughly considered the as-prepared ball-like products were amorphous silica NPs.

Figure 2.

Figure 2

Open in a new tab

(a) TEM image, (b) HRTEM image and (c) SAED pattern of the nanospheres. (d) EDS spectrum taken from a single nanoparticle.

As Fig. 3a shows, jellyfish-like structured products were prepared when Si wafer was treated by aqueous Ni(NO3)2 solution before the CVD reaction. High magnification FESEM images (Fig. 3b,c) show that the jellyfish-like structures were composed of numerous NWs. EDS spectrum inset in Fig. 3b reveals the NWs composition mainly contain Si and O elements. Furthermore, FT-IR spectroscopy was also used to confirm the composition of the jellyfish products. As shown in Fig. 3d, the peaks at 479 cm−1 and 812 cm−1 were correspond to Si-O-Si stretching vibration of amorphous SiOx. The peak at around 1119 cm−1 was attributed to Si-O stretching vibration. Therefore, the jellyfish-like nanostructures were also silica products.

Figure 3.

Figure 3

Open in a new tab

(a) Low magnification FESEM image and (b,c) high magnification FESEM images of the jellyfish-like NWs product synthesized on a silicon wafer. The inset in (b) is EDS spectrum taken from the NWs area in (b). (d) FT-IR absorption spectrum of the jellyfish-like product.

Furthermore, the jellyfish-like products were further characterized using TEM equipped with EDS. Figure 4a shows the typical TEM image of the silica NWs, where the spherical catalyst particle attached to the tip of the “jellyfish head” (NWs) had a diameter ~1.5 μm. The diameter of the NWs as shown in Fig. 4b was 35–50 nm and very uniform. The HRTEM image of the NWs is shown in Fig. 4c, which were similar to the NPs, combined with the SAED image inset in Fig. 4c, revealed the NWs an amorphous phase. The EDS spectrum (Fig. 4d) of the “head of the jellyfish” recorded from the marked area in Fig. 4a depicts the area was composed of Ni, Si, O, which implied that Ni provided a site for the initial nucleation and successive growth of amorphous silica NWs.

Figure 4. Conventional TEM image of the jellyfish-like NWs, where the metal catalyst can be easily distinguished from the nanowires.

Figure 4

Open in a new tab

(b) A typical TEM image of the NWs under low magnification. (c) A typical HRTEM image of a single NW and the inset is the corresponding SAED pattern. (d) EDS spectrum taken from the marked area in (a).

In the growth mechanisms of silica NPs and NWs prepared by thermal CVD procedure, the involvement of vapour phase and Ni-catalyst played important roles in their formation process. In this work, before argon was introduced into the experimental setup, the vapour was difficult to expel fully from the system by the rotary pump. When the sample was heated to 1200 °C, the residual oxygen (O2 and H2O) in the furnace and the oxygen released from the refractory lining can react with the silicon powder following reaction (1)25,26.

graphic file with name srep22459-m1.jpg

Furthermore, SiO gas can also be formed according to the following reaction (2) on account of the SiO2 thin film existed on the surface of Si substrate.

graphic file with name srep22459-m2.jpg

The as-formed SiO gas was transported to the substrate position by the carrier gas. As it is known, SiO is metastable and can be decomposed into SiO2 and Si. As we previously mentioned, a certain amount of oxygen remained in the furnace, which reacted with Si vapour to further generate SiOx23.

In conventional CVD procedure, the vapors were transported and condensed on to a solid substrate surface which was placed in a lower temperature zone27. Different from this classical growth mechanism, a few studies have previously been reported in which nanoparticles was formed through gas-phase nucleation procedure. Gas-phase nucleation procedure is also an important process for the synthesis of nanoparticles28,29,30. By using both approaches, the morphology of the silica products in this research can be controlled effectively.

For the generating of silica nanoparticles, a gas-phase nucleation dominated mechanism was proposed. When the as-generated SiO gas diffused to the lower temperature zone, SiOx clusters were generated and fell down on the substrate surface. No 1D silica structures were observed on the substrate without catalyst (as shown in Fig. 1a,b). It indicates that the silica NPs cannot grown anisotropy on the surface of the substrate. Correlative researches indicated that the partial pressure of precursor gaseous has an important role in determining the diameters of the nanoparticles. Nevertheless, the exact growth mechanism of silica NPs still needs to be further investigated.

As for one dimensional (1D) nanostructures, the vapour-liquid-solid (VLS) growth mechanism is most widely employed27. The mechanism uses foreign element catalytic agent to medicate the growth31. VLS methods are used to prepare various kinds of 1D materials such as Si, Ge, GaN, GaAs, ZnO, ZnS, MgO, SiO2, etc.27

In this research, on account of Ni-catalyst (as revealed in Fig. 4a), VLS procedure dominated the growth of silica NWs. However, a small number of silica NPs were also observed in this process as shown in Figure S1. This phenomenon is results of two mechanisms (gas-phase nucleation and VLS). Due to the addition of Ni-catalyst, the nucleation barrier on the substrate surface was reduced. Ni-Si-O eutectic alloy was formed when SiO gas diffused onto the surface of the substrate. With the diffusion of SiO, when the alloy reached supersaturation condition, the SiOx nuclei were generated and grew anisotropy. In addition, a type of jellyfish-like 1D nanostructure is produced in the present work rather than conventional single NWs. The Ostwald ripening process is considered (the detailed descriptions can be found in Supporting Informations). Figure 3a and b clearly revealed that the primary nanowires grown in the “head” of the “jellyfish” aggregate along the lateral direction to form nanowire bundles. Therefore, by using the aforementioned procedures, the morphology of the silica products can be controlled.

In order to characterize the difference of optical properties between NPs and NWs, their PL and CL spectra were recorded at room temperature. Figure 5 presents the PL spectra of the as-prepared NPs and NWs using a Xe lamp (254 nm) as the excitation source. Both the NPs and NWs show a blue emission band at 415 nm (2.99 eV). Furthermore, the peak intensity of the NPs is much higher than that of the nanowires. This suggests that the stimulated area of the NPs is much larger than the NWs.

Figure 5. The emission spectra of the as-obtained silica NPs and jellyfish-like NWs.

Figure 5

Open in a new tab

Figure 6 shows together NPs and NWs SEM images (Fig. 6a,c) and homologous CL images. From the CL images, the contrast from the nanostructures (NPs and NWs) displayed clear bright variations.

Figure 6.

Figure 6

Open in a new tab

SEM images (a and c) and their corresponding CL images (b and d) of the as-obtained silica NPs and NWs. The images were obtained with a focused electron beam at an accelerating voltage of 30 kV.

To investigate the luminescence properties of these two types of nanostructures in detail, CL spectra (as shown in Fig. 7) were also collected at an accelerating voltage of 30 kV. However, different emission spectra were obtained compared with their PL spectra. All of the silica nanostructures demonstrated a blue emission centered at ~470 nm (2.64 eV). The NWs’ spectra show an emission shoulder at ~396 nm (3.13 eV). Up to now, a number of researches have been carried out to investigate the luminescence of SiOx NPs32 and NWs33. Blue/green emissions ranged from 380 nm (3.26 eV) to 530 nm (2.34 eV) wavelengths have been reported for silica nanostructures23,24,33,34. As previously reported, the luminescence peaks at around 410 nm (3.02 eV) ~470 nm (2.64 eV) were attributed to the neutral oxygen vacancy (≡Si-Si≡) arising from such oxygen deficiency35,36,37. The peak positions including PL and CL spectra in our silica NPs and NWs are in general agreement with the previously reported values. Hence, both the PL spectra and CL spectra are caused by the emission of the excited oxygen vacancies. In CL measurements, under an accelerating voltage of 30 kV, the electrons could inject into a hundred of nanometers even several micrometers in depth into the samples. This may cause the different emission peaks between these two kinds of tests, even measured the same products. As previous reports demonstrated, silica nanostructures showed a varying degree of oxygen deficiency, but the emission peaks around 410 nm (3.02 eV) ~470 nm (2.64 eV) are all attributed to the neutral oxygen vacancy (≡Si-Si≡)33. In this research, under an accelerating voltage of 30 kV, the electrons could inject into a hundred of nanometres even several micrometers in depth into the samples. This may cause a different dominated luminescence mechanism between PL and CL measurements. Based on the above analysis, we roughly considered that the number and depth of the neutral oxygen vacancies which are excited in silica nanostructures may affect the emission peak position. Compared the CL spectra between NPs and NWs, the appearance of the 396 nm shoulder in NWs CL spectrum may due to the intrinsic diamagnetic defect center38 or the 1D structure. From the PL and CL results, it can be concluded that the luminescence property of the silica nanostructures can be changed along with the excitation light sources. The changeable emission properties of the silica nanostructures are of significant interest for their potential application in new photoelectric nanodevices. Especially the luminescence properties of the NPs make it is possible to apply in fluorescence labeling medicine field.

Figure 7. Room temperature CL spectra of the as-synthesized silica nanostructures.

Figure 7

Open in a new tab

(a) NPs; (b) NWs.

Conclusions

In conclusion, morphology control synthesis of uniform silica nanoparticles (NPs) and jellyfish-like nanowires (NWs) has been achieved using a chemical vapour deposition (CVD) method. Structural characterization indicates that both the NPs and NWs have an amorphous structure. The form of NPs may be related to gas-phase nucleation procedure, and the growth of the nanowires are in accordance with vapour-liquid-solid (VLS) mechanism. And the jellyfish morphology of the as-prepared silica nanowires is related to Ostwald ripening effect. PL and CL measurements indicate that the emission spectra of both silica NPs and NWs are due to the neutral oxygen vacancy (≡Si-Si≡) existed in these nanostructures. Interestingly, the luminescence property of the silica nanostructures can be changed along with the excitation light sources. This research provides a simple method in morphology control synthesis of silica NPs and NWs. The outstanding optical properties make them possess considerable potential application prospect in fluorescence labeling medicine field, photoelectric nanodevices etc.

Methods

The experimental setup consists of a horizontal high-temperature tube furnace, an alumina tube, a rotary pump system, and a gas controlling system. Silica NPs and jellyfish-like NWs were synthesized directly on silicon substrate by a simple CVD procedure, using high-purity argon as carrier gas. A p-type Si (111) substrate of size 2 cm × 2 cm was ultrasonically cleaned by acetone and ethanol for 10 minutes each, then dried in air condition. In a typical synthesis reaction, 1 g silicon powder was placed in one end of an alumina boat, and Si substrates (treated without or with several drops of aqueous 0.1 m Ni(NO3)2 solution, the solution was dispersed and air dried) were placed on the opposite end. After that, the fixed alumina boat was placed in the center of a tube furnace, it is worth noted that the silicon powder end was placed in the air inlet end. The experimental setup was evacuated to 10 Pa by a rotary pump and argon (purity 99.999% (v/v)) was introduced until the furnace pressure reached 0.14 MPa. Then the setup was heated in a programmed way, from room temperature to 1000 °C at 10 °C/min, from 1000 °C to 1200 °C at 3 °C/min and maintained there for 3 h.

The as-prepared products were characterized by field emission scanning electron microscopy (FESEM, Hitach S4800, Japan) and transmission electron microscopy (TEM/HRTEM, FEI-Tecnai-G2-F30, America) equipped with energy dispersive X-ray spectroscopy (EDS). Fourier-transform infrared spectroscopy (FT-IR) data were collected with a Nicolet IR100/200 spectrophotometer over the wavenumber range of 450–1500 cm−1. After the phase and structure examinations, PL spectra of the as-prepared nanostructures were collected with a fluorescence spectrophotometer (Hitachi F-4600, Japan) using a Xe lamp excitation. CL images and spectra were determined by using an ultrahigh vacuum scanning electron microscope (UHV-SEM) equipped with a Gemini electron gun (Omicron, Germany) and a CL detector (Gatan mono 3 plus) at an accelerating voltage of 30 kV. All PL and CL images and spectra were collected at room temperature under the same conditions to ensure convictive comparsion.

Additional Information

How to cite this article: Liu, H. et al. Morphology controlling method for amorphous silica nanoparticles and jellyfish-like nanowires and their luminescence properties. Sci. Rep. 6, 22459; doi: 10.1038/srep22459 (2016).

Supplementary Material

Supplementary Information
srep22459-s1.doc (4.6MB, doc)

Acknowledgments

This work was supported by the National Natural Science Foundation of China (grant no. 51032007, 51272241, 51472222 and 51372232).

Footnotes

Author Contributions H.T.L. and Z.H.H. conceived and designed the experiments. H.T.L. carried out the experiments. H.T.L., J.T.H., S.X., M.H.F., Y.G.L., X.W.W. and S.W.Z. analyzed the data. All authors discussed the results. All authors have given approval to the final version of the manuscript.

References

  1. Brust M., Walker M., Bethell D., Schiffrin D. J. & Whyman R. Synthesis of thiol-derivatised gold nanoparticles in a two-phase liquid–liquid system. J. Chem. Soc., Chem. Commun. 7, 801–802 (1994). [Google Scholar]
  2. Bastús N. G., Merkoçi F., Piella J. & Puntes V. Synthesis of highly monodisperse citrate-stabilized silver nanoparticles of up to 200 nm: kinetic control and catalytic properties. Chem. Mater. 26, 2836–2846 (2014). [Google Scholar]
  3. Popczun E. J., Read C. G., Roske C. W., Lewis N. S. & Schaak R. E. Highly active electrocatalysis of the hydrogen evolution reaction by cobalt phosphide nanoparticles. Angew. Chem. 126, 5531–5534 (2014). [DOI] [PubMed] [Google Scholar]
  4. Cui Y. & Lieber C. M. Functional nanoscale electronic devices assembled using silicon nanowire building blocks. Science 291, 851–853 (2001). [DOI] [PubMed] [Google Scholar]
  5. Elnathan R., Kwiat M., Patolsky F. & Voelcker N. H. Engineering vertically aligned semiconductor nanowire arrays for applications in the life sciences. Nano Today 9, 172–196 (2014). [Google Scholar]
  6. Kim S.-K. et al. Design of nanowire optical cavities as efficient photon absorbers. ACS nano 8, 3707–3714 (2014). [DOI] [PubMed] [Google Scholar]
  7. Malvadkar N. A., Hancock M. J., Sekeroglu K., Dressick W. J. & Demirel M. C. An engineered anisotropic nanofilm with unidirectional wetting properties. Nature materials 9, 1023–1028 (2010). [DOI] [PubMed] [Google Scholar]
  8. Horiuchi S. et al. Single graphene sheet detected in a carbon nanofilm. Appl. Phys. Lett. 84, 2403–2405 (2004). [Google Scholar]
  9. Wang X. et al. Recent advances in solution-processed inorganic nanofilm photodetectors. Chem. Soc. Rev. 43, 1400–1422 (2014). [DOI] [PubMed] [Google Scholar]
  10. Dasgupta N. P. et al. 25th anniversary article: semiconductor nanowires–synthesis, characterization, and applications. Adv. Mater. 26, 2137–2184 (2014). [DOI] [PubMed] [Google Scholar]
  11. Liu J.-W. et al. Macroscopic-scale assembled nanowire thin films and their functionalities. Chem. Rev. 112, 4770–4799 (2012). [DOI] [PubMed] [Google Scholar]
  12. Albanese A., Tang P. S. & Chan W. C. The effect of nanoparticle size, shape, and surface chemistry on biological systems. Annu. Rev. Biomed. Eng. 14, 1–16 (2012). [DOI] [PubMed] [Google Scholar]
  13. Huang J. et al. β-Sialon nanowires, nanobelts and hierarchical nanostructures: morphology control, growth mechanism and cathodoluminescence properties. Nanoscale 6, 424–432 (2014). [DOI] [PubMed] [Google Scholar]
  14. Portehault D., Cassaignon S., Baudrin E. & Jolivet J.-P. Morphology control of cryptomelane type MnO2 nanowires by soft chemistry. Growth mechanisms in aqueous medium. Chem. Mater. 19, 5410–5417 (2007). [Google Scholar]
  15. Cardoso V., Minas G., Costa C. M., Tavares C. & Lanceros-Mendez S. Micro and nanofilms of poly (vinylidene fluoride) with controlled thickness, morphology and electroactive crystalline phase for sensor and actuator applications. Smart Mater. Struct. 20, 087002 (2011). [Google Scholar]
  16. Park S.-E. et al. Supramolecular interactions and morphology control in microwave synthesis of nanoporous materials. Catal. Surv. Asia 8, 91–110 (2004). [Google Scholar]
  17. Slowing I. I., Vivero-Escoto J. L., Wu C.-W. & Lin V. S.-Y. Mesoporous silica nanoparticles as controlled release drug delivery and gene transfection carriers. Adv. Drug Del. Rev. 60, 1278–1288 (2008). [DOI] [PubMed] [Google Scholar]
  18. Lou J. et al. Modeling of silica nanowires for optical sensing. Opt. Express 13, 2135–2140 (2005). [DOI] [PubMed] [Google Scholar]
  19. Wang Z. L. et al. Silica nanotubes and nanofiber arrays. Adv. Mater. 12, 1938–1940 (2000). [Google Scholar]
  20. Jaiswal J. K., Mattoussi H., Mauro J. M. & Simon S. M. Long-term multiple color imaging of live cells using quantum dot bioconjugates. Nat. Biotechnol. 21, 47–51 (2003). [DOI] [PubMed] [Google Scholar]
  21. Ow H. et al. Bright and stable core-shell fluorescent silica nanoparticles. Nano Lett. 5, 113–117 (2005). [DOI] [PubMed] [Google Scholar]
  22. Davis S. A., Burkett S. L., Mendelson N. H. & Mann S. Bacterial templating of ordered macrostructures in silica and silica-surfactant mesophases. Nature 385, 420–423 (1997). [Google Scholar]
  23. Pang C. et al. Synthesis and photoluminescence of ultralong amorphous SiO2 nanowires catalysed by germanium. CrystEngComm 13, 4082–4085 (2011). [Google Scholar]
  24. Peng X. et al. Blue-light emission from amorphous SiOx nanoropes. Appl. Phys. A 74, 831–833 (2002). [Google Scholar]
  25. Khongwong W., Imai M., Yoshida K. & Yano T. Synthesis of. β-SiC/SiO2 core-shell nanowires by simple thermal evaporation. J. Ceram. Soc. Jpn. 117, 194–197 (2009). [Google Scholar]
  26. Niu J. J. et al. A simple route to synthesize scales of aligned single-crystalline SiC nanowires arrays with very small diameter and optical properties. J. Phys. Chem. B 111, 4368–4373 (2007). [DOI] [PubMed] [Google Scholar]
  27. Xia Y. et al. One-dimensional nanostructures: synthesis, characterization, and applications. Adv. Mater. 15, 353–389 (2003). [Google Scholar]
  28. Frenklach M. et al. Homogeneous nucleation of diamond powder in the gas phase. J. Appl. Phys. 66, 395 (1989). [Google Scholar]
  29. Girshick S. L. et al. Numerical modeling of gas-phase nucleation and particle growth during chemical vapor deposition of silicon. J. Electrochem. Soc. 147, 2303 (2000). [Google Scholar]
  30. Vorob’ev A. N. et al. A. Effect of gas-phase nucleation on chemical vapor deposition of silicon carbide. J. Cryst. Growth 211, 343–346 (2000). [Google Scholar]
  31. Mohammad S. N. Analysis of the vapor–liquid–solid mechanism for nanowire growth and a model for this mechanism. Nano Lett. 8, 1532–1538 (2008). [DOI] [PubMed] [Google Scholar]
  32. Wang D., Xing G., Peng H. & Wu T. Chlorine-assisted size-controlled synthesis and tunable photoluminescence in Cr-doped silica nanospheres. J. Phys. Chem. C 113, 7065–7068 (2009). [Google Scholar]
  33. Kim J. H. & Yoon C. S. Amorphous silicon dioxide nanowire array synthesized via carbonization of polyimide thin film. J. Phys. Chem. C 112, 4463–4468 (2008). [Google Scholar]
  34. Meng G. et al. Synthesis and photoluminescence of aligned SiOx nanowire arrays. Appl. Phys. A 76, 119–121 (2003). [Google Scholar]
  35. Nishikawa H., Shiroyama T., Nakamura R., Ohki Y., Nagasawa K. & Hama Y. Photoluminescence from defect centers in high-purity silica glasses observed under 7.9-eV excitation. Physical Review B 45, 586 (1992). [DOI] [PubMed] [Google Scholar]
  36. Liao L. S. et al. Blue luminescence from Si+-implanted SiO2 films thermally grown on crystalline silicon. Appl. Phys. Lett. 68, 850–852 (1996). [Google Scholar]
  37. Zhai T. et al. Synthesis and cathodoluminescence of morphology-tunable SiO2 nanotubes and ZnS/SiO2 core-shell structures using CdSe nanocrystals as the seeds. J. Phys. Chem. C 111, 11604–11611 (2007). [Google Scholar]
  38. Tohmon R. et al. Correlation of the 5.0- and 7.6-eV absorption bands in SiO2 with oxygen vacancy. Phys. Rev. B 39, 1337–1345 (1989). [DOI] [PubMed] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Supplementary Materials

Supplementary Information
srep22459-s1.doc (4.6MB, doc)

Articles from Scientific Reports are provided here courtesy of Nature Publishing Group

RESOURCES