. 2016 Mar 10;7:10990. doi: 10.1038/ncomms10990

Making the hydrogen evolution reaction in polymer electrolyte membrane electrolysers even faster

Jakub Tymoczko 1,2, Federico Calle-Vallejo 3, Wolfgang Schuhmann 1,2, Aliaksandr S Bandarenka 1,4,5,a
PMCID: PMC4792955  PMID: 26960565

Abstract

Although the hydrogen evolution reaction (HER) is one of the fastest electrocatalytic reactions, modern polymer electrolyte membrane (PEM) electrolysers require larger platinum loadings (∼0.5–1.0 mg cm−2) than those in PEM fuel cell anodes and cathodes altogether (∼0.5 mg cm−2). Thus, catalyst optimization would help in substantially reducing the costs for hydrogen production using this technology. Here we show that the activity of platinum(111) electrodes towards HER is significantly enhanced with just monolayer amounts of copper. Positioning copper atoms into the subsurface layer of platinum weakens the surface binding of adsorbed H-intermediates and provides a twofold activity increase, surpassing the highest specific HER activities reported for acidic media under similar conditions, to the best of our knowledge. These improvements are rationalized using a simple model based on structure-sensitive hydrogen adsorption at platinum and copper-modified platinum surfaces. This model also solves a long-lasting puzzle in electrocatalysis, namely why polycrystalline platinum electrodes are more active than platinum(111) for the HER.

Inline graphicThere is substantial research into minimizing platinum use in polymer electrolyte membrane electrolyzers. Here, the authors report that the hydrogen evolution activity of platinum(111) electrodes can be significantly enhanced by monolayer amounts of copper, which weaken the binding of hydrogen intermediates.

Heterogeneous redox reactions at electrified interfaces are of growing importance in contemporary science and technology1,2,3, as they determine the performance of several electrochemical devices for future sustainable provision, storage and redistribution of renewable energy4,5,6,7. In particular, the efficiency of electrolysers and fuel cells largely depends on their electrode/electrolyte interfaces and catalytic properties8,9,10,11.

In this context, hydrogen (H2) production from water is an important electrocatalytic process due to its dual impact: it is a good model catalytic system12,13,14,15 for the evaluation of new material design methodologies and it is significant for future energy provision and storage16,17,18,19. In spite of numerous achievements18, only ∼4% of H2 produced comes from water electrolysis20. The main impediments to a wider utilization of water electrolysis are the high energy losses in electrolysers due to the insufficient activity of state-of-the-art electrodes. Considering the global hydrogen production of ∼15 trillion moles per year (2011)21 and average prices (2016) in the United States and Europe of ∼0.1 Euro per kWh (refs 22, 23), the electricity costs to produce just 4% of H2 using polymer electrolyte membrane (PEM) electrolysers would exceed ∼6 billion Euros. Compared with these expenses for electricity, the material costs (noble-metal catalysts, supports and so on) are relatively small. For instance, decreasing the operating voltage of PEM electrolysers from presently ∼2.0 (ref. 18) by 0.1 V using improved hydrogen and oxygen evolution electrocatalysts could decrease the electricity expenses for electrolysis by ∼0.3 billion Euros. Assuming a current density in state-of-the-art PEM electrolysers of 1 A cm−2 (ref. 18) and catalyst loadings of 1 mg cm−2 for anodes and cathodes18, only the reduction in electricity expenses exceeds ∼10 times the whole price of platinum (with the amounts, which are equivalent to ∼0.5% of its annual production) or iridium (∼30% of its annual production, correspondingly) catalysts necessary to electrochemically produce the above-mentioned amount of hydrogen annually. In other words, a ∼20 mV decrease in the operating voltage of PEM electrolysers corresponds to the price of noble-metal catalysts needed to produce 4% of H2 electrochemically. Although the long-term goal is to replace scarce electrocatalysts with more abundant and similarly active analogues, fundamental and application-related issues require further optimization of state-of-the-art hydrogen evolution reaction (HER) and oxygen evolution reaction electrocatalysts18.

Here we show that incorporating (sub)monolayer amounts of copper (Cu) to platinum (Pt) enhances the catalytic activity ∼2 times at low overpotentials, surpassing the highest HER-specific activities reported under similar conditions. These results are rationalized in terms of a structure-sensitive analysis of hydrogen adsorption on Pt- and Cu-modified Pt surfaces that also explains why polycrystalline Pt is more active than Pt(111) towards the HER.

Results

General considerations

According to the current understanding, the HER (as well as hydrogen oxidation reaction, HOR) mechanisms involve adsorbed hydrogen (denoted *H) at the electrode surface. As stated by the Sabatier principle24, the optimal catalytic surface should bind reaction intermediates neither too weak nor too strong. This qualitative rule can be converted to a quantitative tool using calculated or measured adsorption energies for the relevant reaction intermediates at specific active sites on the surface. Figure 1 shows theoretical adsorption energies and experimental activity data for HER at pure metal surfaces25. As can be seen from Fig. 1, the trends in the measured HER can be fairly explained using the hydrogen binding energy as a ‘descriptor', ΔEH, estimated via density functional theory (DFT) calculations, as reported by Nørskov et al.25

Figure 1. Trends in hydrogen evolution reaction activity.

Figure 1

Open in a new tab

Experimental HER activity expressed as the exchange current density, log(i0), for different metal surfaces as a function of the calculated *H chemisorption energy, ΔEH. The result of a simple theoretical kinetic model is also shown as a dotted line. Original data are taken from ref. 25.

Although exact ΔEH values depend on the surface coverage of hydrogen12, a straightforward outcome of this approach is that the optimum electrocatalytic sites for the HER should bind *H slightly weaker (∼0.09 eV) than Pd, Rh or Pt. In principle, the electronic properties of metal surfaces can be modulated by different means. One of the common ways to do this is to prepare bulk alloys, where the bulk crystal composition and structure influence the properties of the surfaces and, hence, their catalytic activity through strain and ligand effects26,27,28. An alternative way is to modify the properties of the topmost layer at the surface by selectively positioning atomic layers of solute metals directly at the surface to form either overlayers29, surface or subsurface alloys. An example of the latter approach is shown in Fig. 2.

Figure 2. Cyclic voltammetry in Ar-saturated 0.1 M HClO4.

Figure 2

Open in a new tab

The CVs of the Pt(111), Cu overlayer on Pt(111), Cu-Pt(111) SA and NSA (1 ML Cu initially deposited) demonstrate how the relative position of the Cu atomic layer governs the adsorption/desorption of hydrogen (grey area) at the electrode surface. dE/dt=50 mV s−1.

Electrochemical performance

Figure 2 shows cyclic voltammograms (CVs) taken in Ar-saturated 0.1 M HClO4 electrolytes for the unmodified Pt(111), the Cu overlayer on Pt(111), the Cu-Pt(111) near-surface alloys (NSAs) and surface alloys (SAs) within the regions of their electrochemical stability. In the CVs, the potential region between ∼0.4 and 0.07 V corresponds to hydrogen adsorption/desorption before the formation of H2 at more negative potentials. Notably, the position of the Cu atomic layer significantly changes the hydrogen binding energy. For example, the SA apparently binds *H stronger than Pt(111), as revealed by the corresponding CVs between ∼0.2 and ∼0.4 V (Fig. 2). In contrast, positioning the Cu atoms into the second layer (1 ML Cu initially deposited) weakens *H binding compared with unmodified Pt(111). In addition, the Cu pseudomorphic overlayer (POL) does not adsorb hydrogen species at these potentials (Fig. 2).

Experimentally observable changes in ΔEH are mainly due to ligand effects, as Cu and Pt have dissimilar valence configurations (s1d10 versus s1d9) and the differences in the lattice constants are not negligible (3.61 versus 3.92 Å). These differences have a direct impact on the kinetics of reactions that involve adsorbed hydrogen species as reaction intermediates, in particular for the HER. For example, the SA, which binds hydrogen species stronger than Pt(111), would also probably be less active for both HER and HOR: this corresponds to the left part of the volcano plot in Fig. 1 and more negative ΔEH values, relative to Pt. On the other hand, the Cu overlayer is ‘too noble' for the hydrogen species to be active towards HER. This corresponds to the right part of the volcano in Fig. 1, far from the optimum towards more positive ΔEH values. In contrast, one can expect that the NSA would probably be more active than Pt(111): its surface binds hydrogen species slightly weaker than Pt, which corresponds to the direction towards the theoretical maximum in Fig. 1. In Fig. 3, we confirm all these expectations.

Figure 3. RDE voltammetry in Ar-saturated 0.1 M HClO4.

Figure 3

Open in a new tab

The RDE voltammograms for Cu overlayer, Pt(111), SA and NSA (1 ML Cu initially deposited) electrodes show the correlation between the HER activity of the electrodes and the position of the Cu atomic layers relative to the topmost Pt layer. The negative currents start before 0.0 V RHE, because the electrolyte is saturated with the inert gas. dE/dt=10 mV s−1.

At low overpotentials, a Cu-Pt(111) POL does not show noticeable HER activities (Fig. 3). The SA is less active than Pt(111), as expected. Finally, the voltammogram for the NSA (1 ML Cu initially deposited) in Fig. 3 reveals a substantially higher hydrogen evolution activity as compared with that for Pt(111). It is noteworthy that the results presented in Fig. 3 correspond to measurements in Ar-saturated electrolytes, as these are the simplest tests to derive activity trends with minimal influence of complex experimental factors (those are especially important for overlayers, when the electrolyte is saturated with electroactive species such as H2 or CO)30. In the following, we focus on a more detailed electrochemical characterization of the active NSA electrodes.

Figure 4 shows typical rotating disk electrodes (RDE) voltammograms recorded in H2-saturated 0.1 M HClO4 for Pt(111) and NSA electrodes. The NSA surface is more active than unmodified Pt for both HER and HOR. As those reactions involve the same intermediates, the same ΔEH descriptor can be used to explain this fact. Although we do not use iR correction to avoid additional errors in this particular case (see ref. 30) and rather compare the model surfaces under the same conditions, it is still possible to approximately estimate the ‘apparent' exchange current density, i0, at very low overpotentials close to 0.0 V reversible hydrogen electrode (RHE)15. This value reflects the intrinsic activity of materials and can be used to compare different electrocatalysts reported by different research groups. The estimated i0 values are at least ∼1.5 mA cm−2 for Pt(111) and ∼3.0 mA cm−2 for the NSA. Notably, the apparent exchange current density for Pt(111) is higher than that reported in a very detailed investigation performed by Markovic et al.15 for low-index Pt(hkl) single-crystal surfaces measured in H2SO4 at the same pH value. We hypothesize that this is due to a difference in the exact experimental protocols, as discussed recently in detail in ref. 30. Nevertheless, this fact additionally prevents misinterpretation of the NSA activity results, as those are compared with already very active reference Pt surfaces.

Figure 4. RDE voltammetry in H2-saturated HClO4.

Figure 4

Open in a new tab

(a) RDE voltammograms of the Cu-Pt(111) NSA (1 ML Cu initially deposited) compared with the unmodified Pt(111) electrode. dE/dt=10 mV s−1. (b) Logarithmic plot of the currents related to hydrogen evolution for the NSA and Pt(111).

If the so-called Tafel plot is used (Fig. 4b), the slopes of the curves for the NSA and Pt(111) samples at each electrode potential are rather similar, suggesting that there are no significant changes in the HER mechanism among these two surfaces.

Table 1 compares the activities for the HER/HOR at room temperature for active model surfaces, as summarized in refs 15, 18, 31 and measured in this work. In addition, as can be seen from Table 1, typical values for the apparent exchange current densities of Pt nanoparticles (averaged among values used by different groups), even at elevated temperatures and in real devices, are approximately three times lower than that for the NSA sample.

Table 1. Activities for the HER/HOR at room temperature.

Electrode i0,apparent (mA cm−2)* Source
Pt(111) ∼0.45 ref. 15
Pt(100) ∼0.6  
Pt(110) ∼0.98  
PdOL/PtRu(111) ∼2.0 refs 29,31
PdOL/Pt(111) ∼2.0  
Pt(111) ∼1.5 This work
Cu-Pt(111) NSA (1 ML Cu initially deposited) ∼3.0 This work
Pt (nanoparticles) ∼1.0 (at 80 °C) ref. 18
Open in a new tab

HER, hydrogen evolution reaction; HOR, hydrogen oxidation reaction.

*At pH 1, without iR correction, as reported in the literature.

To further evaluate the activity of the Cu-Pt(111) NSA with respect to the best known catalysts and additionally account for possible artefacts caused by the formation of the non-conducting H2 gas phase at the electrode surface during the cathodic/anodic scans, we compare chronoamperograms (current versus time curves taken at a certain potential) for the most active surfaces reported up to date in Fig. 5.

Figure 5. Hydrogen evolution activity as a function of time.

Figure 5

Open in a new tab

The figure contains the current–time curves for hydrogen evolution reaction under potentiostatic conditions (E=−0.06 V) for the Cu-Pt(111) NSA, polycrystalline Pt, PdOL-modified Pt and unmodified Pt(111) electrodes (RDE measurements at 1,600 r.p.m.).

Figure 5 compares the activity of the Cu-Pt(111) NSA (1 ML Cu initially deposited) with polycrystalline Pt and PdOL deposited on Pt(111). First, the activity for all samples remains practically unchanged, as well as their basic CVs, indicating that the differences in activities are not due to artefacts caused by generation of the non-conducting gas phase. Notably, the activity of the Cu-Pt(111) NSA (1 ML Cu initially deposited) is reproducibly better than any other reported state-of-the-art electrocatalysts including polycrystalline Pt32, which has been suggested as one of the most active surface towards HER.

We performed additional benchmark measurements using polycrystalline Pt samples including iR correction. The activity results show that our polycrystalline samples possess exactly the same activity towards HER/HOR as reported by Sheng et al.32 in their detailed study of the activities of polycrystalline Pt30,33.

Furthermore, the influence of the subsurface concentration of Cu in Cu-Pt(111) and Cu-Pt(pc) NSAs has been tested by varying the amount of Cu initially deposited (Fig. 6a). Interestingly, the activity of the Cu-Pt(111) NSA sample with 1 ML Cu deposited initially remains the most active one. Attempts to introduce even more Cu into the subsurface region through a two-stage deposition/annealing procedure leads to a decrease in the activity (marked with ‘*' in Fig. 6a). All active samples evaluated in this work are compared in Fig. 6b.

Figure 6. Effect of Cu and Pd addition on the hydrogen evolution reaction activity.

Figure 6

Open in a new tab

(a) Effect of the Cu subsurface concentration on the HER activity measured at a potential of −0.06 V versus RHE for Pt(111) and polycrystalline Pt electrodes (Pt(pc), RDE measurements at 1,600 r.p.m., scan rate: 50 mV s−1), given with corresponding error bars (standard deviation) estimated using the results of at least five independent measurements. Open symbol with ‘*' represents the situation when more than 1 ML of copper was introduced intentionally. (b) Current densities measured at −0.06 V versus RHE for Pt(111), Pt(pc), Pd overlayer on Pt(111) (PdOL/Pt(111), Pd overlayer on Pt(pc) (PdOL/Pt(pc)), Cu/Pt(pc) NSA and Cu/Pt(111) NSA with corresponding error bars (standard deviation) estimated using the results of at least five independent measurements. The values are displayed without iR correction.

Notably, the Cu-Pt(111) NSA samples demonstrated good stabilities towards H-induced segregation and anodic corrosion after 5,000 cycles between 0.05 and 1.0 V (versus RHE), as reported recently34. This additionally suggests that modification of just the subsurface region of HER electrocatalysts is a promising approach to enhance not only their catalytic activity but also their stability.

Computational

Finally, we rationalize our most important experimental findings based on the computational results as shown in Fig. 7. Figure 7a contains the trends in hydrogen adsorption for pure Pt(111) and CuPt(111) NSAs and SAs. Clearly, subsurface Cu at all concentrations has the same net effect of weakening the adsorption energies of atomic hydrogen, whereas surface Cu has the opposite effect in line with previous results35. DFT calculations confirm that hydrogen atoms are indeed bound more weakly at NSAs and more strongly at SAs.

Figure 7. Trends in H2 adsorption and evolution.

Figure 7

Open in a new tab

(a) *H adsorption energies with surface Cu (SAs, red) and subsurface Cu (NSAs, orange) on Pt(111). *H binds more strongly to SAs compared with Pt(111), whereas the opposite is observed for the NSAs. The inset shows *H at a NSA with 0.67 ML Cu (grey balls, Pt; red, Cu atoms; white, adsorbed *H). (b) Adsorption energies of *H on Pt and NSAs with 1ML Cu as a function of the generalized coordination numbers of the active sites. In all cases, *H adsorption energies are weaker on the NSAs than on the corresponding sites on Pt. Moreover, more coordinated sites than in the case of (111) terraces bind *H weaker, whereas the less coordinated ones bind it stronger. (c) Volcano plot showing the individual HER activity, coordination and composition of all studied sites. Sites at Cu-Pt(111) NSAs and overcoordinated Pt sites possess the highest activities, whereas SAs and undercoordinated sites are not active.

To assess the structural sensitivity of the HER, we have tested the adsorption of *H at various sites apart from the hollow sites at (111) terraces usually considered in computational models25. Figure 7b shows the differences in adsorption energies of *H with respect to Pt(111) on numerous sites at Pt surfaces and NSAs with 1 ML Cu in the subsurface. The trends are described as a function of the generalized coordination numbers (Inline graphic) of the active sites36,37. In simple terms, generalized coordination numbers are a weighted average of the conventional coordination numbers. The weights are the coordination numbers of the nearest neighbours of the active sites. The various sites considered in this study and the way of estimating their generalized coordination numbers are provided in Supplementary Table 1.

Two noteworthy features of hydrogen atom adsorption on Pt and Cu-Pt NSAs are captured in Fig. 7b. First, sites with coordination lower than Pt(111) bind *H more strongly, whereas those with larger coordination bind more weakly. Second, *H adsorption on Cu-Pt NSAs is systematically weaker than on their counterparts at pure Pt, regardless of surface coordination.

Figure 7c contains the HER volcano-type activity plot built following the model by Nørskov et al.25 (see also Fig. 1 and Supplementary Methods). The plot reflects simultaneously the effect of geometric coordination and Cu content on the HER activity. First of all, highly coordinated defects on pure Pt are substantially more active than sites at Pt(111), which justifies the fact that polycrystalline Pt is more active than Pt(111) for the HER (see Supplementary Methods for further experimental evidence). Undercoordinated defects, however, are less active than (111) terraces. On the other hand, Cu-Pt(111) NSAs are highly active and both overcoordinated and undercoordinated defects decrease their activity, which explains why (111) NSAs are more active than the polycrystalline ones. Finally, SAs are not active in view of their strong *H adsorption energies. Therefore, structure- and composition-sensitive experimental trends for the HER in acidic media are well captured by the trends in *H adsorption energies. In turn, these energies are substantially influenced by the surface coordination of the active sites and the presence of Cu.

Discussion

We have provided experimental and theoretical evidence to claim that selective positioning of Cu atomic layers modifies the adsorption properties of platinum electrodes for the electrochemical hydrogen evolution, accelerating one of the fastest electrocatalytic reactions known to date. Using predominantly the ligand effect, submonolayer amounts of Cu atoms in the second atomic layer induce a twofold increase in the electrocatalytic activity of Pt(111). This makes them the most active electrocatalysts ever reported for the HER in acidic media under comparable conditions, to the best of our knowledge. Further efforts to improve the performance of nanoparticle materials for the cathodes in PEM electrolysers may use this rationale based on the purposeful and delicate location of submonolayer amounts of foreign metals at surfaces.

Methods

Electrode preparation

Details relating to the electrode surface preparation and characterization are given in Supplementary Figs 1–13. The relative position of Cu atomic layers at the surface was controlled as described elsewhere35,38,39. Briefly, to form a copper POL or deposit submonolayer amounts of it, underpotential deposition was performed from a solution containing 2 mM Cu2+ in 0.1 M HClO4. The Cu-Pt(111) NSAs, where Cu atoms are preferentially located in the subsurface layer, were obtained by short annealing of the overlayer (∼2 min) at 400 °C in Ar/H2 atmosphere containing 5% of H2 in Ar (6.0, AirLiquide, Germany). Cu-Pt(111) SAs, where Cu atoms are located in the first atomic layer of the Pt host, were subsequently obtained by annealing the NSAs in Ar/CO atmosphere (0.1% CO in Ar, ∼2 min at 400 °C). The preparation procedures result in single-crystalline samples of Pt(111), Cu-Pt(111) NSAs and SAs, which were atomically smooth.

Activity measurements

Electrolytes containing 0.1 M HClO4 (Merck Suprapur, Germany) were used for activity measurements. A mercury–mercury sulfate reference electrode was kept in a separate compartment and separated from the working electrolyte with an ionically conducting ceramic insert. A polycrystalline Pt wire was used as counter electrode. All potentials are referred to the RHE scale. A SP-300 potentiostat (Bio-Logic, France) was used to control the electrochemical measurements. Electrochemical experiments including the activity measurements were performed using a specifically designed electrochemical cell for the preparation and in-situ electrochemical characterization of single-crystal alloy electrodes, previously described in ref. 40. Measurements with RDE were performed using a Pine RDE 710 instrument (USA).

DFT calculations

Full details of the DFT calculations, the assessment of adsorption energies, the model for estimating the current densities and the computation of generalized coordination numbers are provided in Supplementary Methods section with additional explanations illustrated in Supplementary Fig. 14 and Supplementary Table 1.

Additional information

How to cite this article: Tymoczko, J. et al. Making the hydrogen evolution reaction in polymer electrolyte membrane electrolyzers even faster. Nat. Commun. 7:10990 doi: 10.1038/ncomms10990 (2016).

Supplementary Material

Supplementary Information

Supplementary Figures 1-14, Supplementary Table 1, Supplementary Methods and Supplementary References

ncomms10990-s1.pdf (2MB, pdf)

Acknowledgments

Financial support from SFB 749, the cluster of excellence Nanosystems Initiative Munich (NIM), Cluster of Excellence RESOLV (EXC 1069) funded by the DFG (Deutsche Forschungsgemeinschaft) and in the framework of Helmholtz-Energie-Allianz ‘Stationäre elektrochemische Speicher und Wandler' (HA-E-0002) is gratefully acknowledged. F.C.V. acknowledges funding by the Netherlands Organization for Scientific Research (NWO), Veni project number 722.014.009. The Stichting Nationale Computerfaciliteiten (NCF) is acknowledged for the use of their supercomputer facilities, with financial support from NWO.

Footnotes

Author contributions A.B. and W.S. conceived and supervised the experiments, which were carried out by J.T. F.C.V. made the DFT calculations and the theoretical modelling. The manuscript was written through contributions of all authors. All authors have given approval to the final version of the manuscript.

References

  1. Nørskov J. K., Bligaard T., Rossmeisl J. & Christensen C. H. Towards the computational design of solid catalysts. Nat. Chem. 1, 37–46 (2009). [DOI] [PubMed] [Google Scholar]
  2. Koper M. T. M. Structure sensitivity and nanoscale effects in electrocatalysis. Nanoscale 3, 2054–2073 (2011). [DOI] [PubMed] [Google Scholar]
  3. Stephens I. E. L., Bondarenko A. S., Grønbjerg U., Rossmeisl J. & Chorkendorff I. Understanding the electrocatalysis of oxygen reduction on platinum and its alloys. Energy Environ. Sci. 5, 6744–6762 (2012). [Google Scholar]
  4. Bard A. J. Inner-sphere heterogeneous electrode reactions. Electrocatalysis and photocatalysis: the challenge. J. Am. Chem. Soc. 132, 7559–7567 (2010). [DOI] [PubMed] [Google Scholar]
  5. Gasteiger H. A. & Markovic N. M. Just a dream—or future reality? Science 324, 48–49 (2009). [DOI] [PubMed] [Google Scholar]
  6. Vesborg P. C. K. & Jaramillo T. F. Addressing the terawatt challenge: scalability in the supply of chemical elements for renewable energy. RSC Adv. 2, 7933–7947 (2012). [Google Scholar]
  7. Rabis A., Rodriguez P. & Schmidt T. J. Electrocatalysis for polymer electrolyte fuel cells: recent achievements and future challenges. ACS Catal. 2, 864–890 (2012). [Google Scholar]
  8. Symes M. D. & Cronin L. Decoupling hydrogen and oxygen evolution during electrolytic water splitting using an electron-coupled-proton buffer. Nat. Chem. 5, 403–409 (2013). [DOI] [PubMed] [Google Scholar]
  9. Bandarenka A. S. & Koper M. T. M. Structural and electronic effects in heterogeneous electrocatalysis: Toward a rational design of electrocatalysts. J. Catal. 308, 11–24 (2013). [Google Scholar]
  10. Holewinski A., Xin H., Nikolla E. & Linic S. Identifying optimal active sites for heterogeneous catalysis by metal alloys based on molecular descriptors and electronic structure engineering. Curr. Opin. Chem. Eng. 2, 312–319 (2013). [Google Scholar]
  11. Gasteiger H. A., Baker D. R. & Carter R. N. in Hydrogen Fuel Cells: Fundamentals and Applications Wiley-CPH (2010). [Google Scholar]
  12. Skulason E. et al. Modeling the electrochemical hydrogen oxidation and evolution reactions on the basis of density functional theory calculations. J. Phys. Chem. C 114, 18182–18197 (2010). [Google Scholar]
  13. Greeley J., Jaramillo T. F., Bonde J., Chorkendorff I. & Nørskov J. K. Computational high-throughput screening of electrocatalytic materials for hydrogen evolution. Nat. Mater. 5, 909–913 (2006). [DOI] [PubMed] [Google Scholar]
  14. Björketun M. E., Bondarenko A. S., Abrams B. L., Chorkendorff I. & Rossmeisl J. Screening of electrocatalytic materials for hydrogen evolution. Phys. Chem. Chem. Phys. 12, 10536–10541 (2010). [DOI] [PubMed] [Google Scholar]
  15. Markovic N. M., Grgur B. N. & Ross P. N. Temperature-dependent hydrogen electrochemistry on platinum low-index single-crystal surfaces in acid solutions. J. Phys. Chem. B 101, 5405–5413 (1997). [Google Scholar]
  16. Züttel A., Borgschulte A. & Schlapback L. Hydrogen as a Future Energy Carrier Wiley-VCH (2008). [Google Scholar]
  17. Wang M., Wang Z., Gong X. & Guo Z. The intensification technologies to water electrolysis for hydrogen production—a review. Renew. Sust. Energ. Rev. 29, 573–588 (2014). [Google Scholar]
  18. Carmo M., Fritz D. L., Mergel J. & Stolten D. A comprehensive review on PEM water electrolysis. Int. J. Hydrogen Energy 38, 4901–4934 (2013). [Google Scholar]
  19. Jaramillo T. F. et al. Identification of active edge sites for electrochemical H2 evolution from MoS2 nanocatalysts. Science 317, 100–102 (2007). [DOI] [PubMed] [Google Scholar]
  20. Bicakova O. & Straka P. Production of hydrogen from renewable resources and its effectiveness. Int. J. Hydrogen Energy 37, 11563–11578 (2012). [Google Scholar]
  21. US Department of Energy Hydrogen Analysis Resource Center, Hydrogen Production, Worldwide and US Total Hydrogen Production http://hydrogen.pnl.gov/cocoon/morf/hydrogen/article/706 (2012).
  22. European Commission (Eurostat) Energy Price Statistics http://ec.europa.eu/eurostat/statistics-explained/index.php/Energy_price_statistics (accessed on December 2015).
  23. US Energy Information Administration http://www.eia.gov/electricity/data/browser/#/topic/7?agg=2,0,1&geo=g&freq=M (accessed on December 2015).
  24. Sabatier P. Hydrogentions et deshydrogenations par catalyse. Ber. Deut. Chem. Gesell. 44, 1984–2001 (1911). [Google Scholar]
  25. Nørskov J. K. et al. Trends in the exchange current for hydrogen evolution. J. Electrochem. Soc. 152, J23–J26 (2005). [Google Scholar]
  26. Mavrikakis M., Hammer B. & Nørskov J. K. Effect of strain on the reactivity of metal surfaces. Phys. Rev. Lett. 81, 2819–2822 (1998). [Google Scholar]
  27. Kitchin J. R., Nørskov J. K., Barteau M. A. & Chen J. G. Role of strain and ligand effects in the modification of the electronic and chemical properties of bimetallic surfaces. Phys. Rev. Lett. 93, 156801–156804 (2004). [DOI] [PubMed] [Google Scholar]
  28. Kitchin J. R., Nørskov J. K., Barteau M. A. & Chen J. G. Modification of the surface electronic and chemical properties of Pt(111) by subsurface 3d transition metals. J. Chem. Phys. 120, 10240–10246 (2004). [DOI] [PubMed] [Google Scholar]
  29. Greeley J., Nørskov J. K., Kibler L. A., El-Aziz A. M. & Kolb D. M. Hydrogen evolution over bimetallic systems: understanding the trends. ChemPhysChem 7, 1032–1035 (2006). [DOI] [PubMed] [Google Scholar]
  30. Čolić V. et al. Experimental aspects in benchmarking of the electrocatalytic activity. ChemElectroChem 2, 143–149 (2015). [Google Scholar]
  31. Kibler L. A. Hydrogen electrocatalysis. ChemPhysChem 7, 985–991 (2006). [DOI] [PubMed] [Google Scholar]
  32. Sheng W. C., Gasteiger H. A. & Shao-Horn Y. Hydrogen oxidation and evolution reaction kinetics on platinum: acid versus alkaline electrolytes. J. Electrochem. Soc. 157, B1529–B1536 (2010). [Google Scholar]
  33. Ganassin A., Colic V., Tymoczko J., Bandarenka A. S. & Schuhmann W. Non-covalent interactions in water electrolysis: influence on the activity of Pt(111) and iridium oxide catalysts in acidic media. Phys. Chem. Chem. Phys. 17, 8349–8355 (2015). [DOI] [PubMed] [Google Scholar]
  34. Tymoczko J., Calle-Vallejo F., Colic V., Schuhmann W. & Bandarenka A. S. Evaluation of the electrochemical stability of model Cu-Pt(111) near-surface alloy catalysts. Electrochim. Acta 179, 469–474 (2015). [Google Scholar]
  35. Bandarenka A. S. et al. Design of an active site towards optimal electrocatalysis: overlayers, surface alloys and near-surface alloys of Cu/Pt(111). Angew. Chem. Int. Ed. 51, 11845–11848 (2012). [DOI] [PubMed] [Google Scholar]
  36. Calle-Vallejo F., Martínez J. I., García-Lastra J. M., Sautet P. & Loffreda D. Angew. Chem. Int. Ed. 53, 8316–8319 (2014). [DOI] [PubMed] [Google Scholar]
  37. Calle-Vallejo F. et al. Finding optimal surface sites on heterogeneous catalysts by counting nearest neighbors. Science 350, 185–189 (2015). [DOI] [PubMed] [Google Scholar]
  38. Stephens I. E. L. et al. Tuning the activity of Pt(111) for oxygen electroreduction by subsurface alloying. J. Am. Chem. Soc. 133, 5485–5491 (2011). [DOI] [PubMed] [Google Scholar]
  39. Bondarenko A. S., Stephens I. E. L. & Chorkendorff I. A cell for the controllable thermal treatment and electrochemical characterisation of single crystal alloy electrodes. Electrochem. Commun. 23, 33–36 (2012). [Google Scholar]
  40. Tymoczko J., Schuhmann W. & Bandarenka A. S. A versatile electrochemical cell for the preparation and characterisation of model electrocatalytic systems. Phys. Chem. Chem. Phys. 15, 12998–13004 (2013). [DOI] [PubMed] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Supplementary Materials

Supplementary Information

Supplementary Figures 1-14, Supplementary Table 1, Supplementary Methods and Supplementary References

ncomms10990-s1.pdf (2MB, pdf)