The degradation potential of PET bottles in the marine environment: An ATR-FTIR based approach

C Ioakeimidis 1,2, K N Fotopoulou 3, H K Karapanagioti 3,a, M Geraga 1, C Zeri 2, E Papathanassiou 2, F Galgani 4, G Papatheodorou 1
PMCID: PMC4802224  PMID: 27000994

Abstract

The dominance and persistence of plastic debris in the marine environment are well documented. No information exists in respect to their lifespan in the marine environment. Nevertheless, the degradation potential of plastic litter items remains a critical issue for marine litter research. In the present study, polyethylene terephthalate bottles (PETs) collected from the submarine environment were characterized using ATR-FTIR in respect to their degradation potential attributed to environmental conditions. A temporal indication was used as indicative to the years of presence of the PETs in the environment as debris. PETs seem to remain robust for approximately fifteen years. Afterwards, a significant decrease of the native functional groups was recorded; some even disappear; or new-not typical for PETs-are created. At a later stage, using the PET time series collected from the Saronikos Gulf (Aegean Sea–E. Mediterranean), it was possible to date bottles that were collected from the bottom of the Ionian Sea (W. Greece). It is the first time that such a study has been conducted with samples that were actually degraded in the marine environment.

Whether we already traversing the “plastic era” that Yarsley and Couzens1 aptly described, remains to be seen. It is certain that plastics are ubiquitous in the marine environment, in vast quantities2, consisting the major pollutant component of the world’s seas and oceans3, present even on the most remote areas of the planet4. The boom in the global plastic production, reaching up to 280 million tons in 20125 and the imprudent use of plastics in our everyday life6 elevated plastics into a major environmental threat. The generated plastic waste in 192 coastal countries in 2010, has been estimated at approximately 275 million metric tons (MT), from which 4.8–12.7 million MT have entered the oceans7.

For the synthetic polymers, the degradation process starts once they are deposited into the oceans, mainly due to the synergistic effect of environmental variables and the inherent material instability8. Nonetheless, the degradation rate of the polymers is significantly slow, which makes them extremely persistent9. Thus, plastics can last in the marine environment for decades10 or even hundreds of years when in surface11; likely far longer when in deep sea12. Most synthetic polymers (polyethylene, polypropylene) are buoyant in waters while other (high-density polyethylene, polyethylene terephthalate) may sink13. The torpid degradation of the large plastic items, will result in the formation of small fragments (<5 mm); microplastics14. Both plastics15,16,17 and microplastics18,19,20,21 have adverse effects on the marine biota. They may collocate with microorganisms, invertebrates and microbial communities22, and even form plastiglomerates23.

Microplastics are certainly the most numerically abundant24 floating marine litter items, while the larger plastic items (>4.76 mm) seem to prevail in tonnage, roughly estimated weighting approximately 233,500 T (0.33–4.75 mm: 35,000 T)25. Especially for the Mediterranean Sea the ranges of floating plastic concentrations are of the same order of magnitude to those recorded in the five subtropical gyres26. When it comes to seafloor marine litter, several studies have highlighted them as an important stock deposited on the world’s seafloors27,28,29,30. Their behavior and interaction with the deep marine environment is yet unidentified.

Benthic litter tends to become trapped in areas of low circulation and high sediment accumulation. Litter that reaches the seabed may already have been transported considerable distance, only sinking when weighed down by entanglement and fouling. The consequence is the accumulation of litter on specific seabed locations in response to local sources and oceanographic conditions31,32,33,34. This is the case of the Saronikos Gulf in Greece, where significant amounts of marine litter tend to accumulate on the deeper zones (200–350 m), reaching densities up to 3,428 items km−2 (average: 1211 ± 594 items km−2). The vast majority (95%) are plastics, of which the 36.5% counts for plastic bags, 31% for plastic sheets, and 10% for plastic bottles.

Here, we investigate the degradation potential of plastic bottles of different age that were found at the bottom of the Saronikos Gulf (Aegean Sea–E. Mediterranean). The surface properties of plastic PET bottles were investigated in order to gain an insight that may give rise to a hypothesis about the degradation process of plastics in the environment (including the marine).

Results

The attenuated total reflectance (ATR)-Fourier transform infrared (FTIR) comparative spectra of the outer surface of the degraded PETs were plotted in a comparative way (Fig. 1). For the PET V, five main peaks are identified at wavenumbers 1715, 1245, 1100, 870, and 730 cm−1, corresponding in ketones (C = O), ether aromatic (C-O), ether aliphatic (C-O), aromatic (C-H) and aromatic (C-H) bond. For PET ER, the same peaks are observed. Among the native groups of the polymer (PET), there are various that are decreasing or even disappearing and are attributed to the environmental degradation.

Figure 1. ATR-FTIR comparative spectra of the outer (OUT) surface of the degraded PETs (1997(a,b), 1998, 1999, 2001, 2008, 2011, 2014) compared with a virgin sample (2015). For better visualization, enlarged excerpts of the ATR-FTIR comparative spectra are given at wavenumbers (a) 400–1000, (b) 1000–1200, (c) 1200–1600, (d) 1600–1800 cm−1.

Figure 1

Open in a new tab

At 1715 cm−1 (C = O), there is a decrease; same for 1245 cm−1; at 1100 cm−1, there is a decrease and in some extent the peak disappears (Fig. 1b); at 870 cm−1, the aromatic (C-H) is disappearing, while at 730 cm−1, there is a decrease and the peak almost disappears. The outer PET surface also demonstrates new groups, which are not typical for PET. These groups were observed in the samples (1997(a,b), 1998 and 1999) as follows: (a) at 620 cm−1 (Fig. 1a) a new alkyne bond (C-H) is created and (b) at 1435 cm−1 (Fig. 1c) a new alkane (C-H) bond is created as well.

A similar ATR-FTIR comparative spectra was plotted for the inner PET surface (Fig. S1), with results similar to the ones provided for the outer surface. Thus, the degradation process of PETs seems to happen concurrently for both PET sides i.e. inner and outer surface.

Following the investigation of the polymer degradation through the ATR-FTIR comparative spectra, the surface topography and roughness of the polymers were also investigated through SEM visualizations in order to see whether the visualizations give us a similar trend as the ATR-FTIR comparative spectra. The surface topography and roughness of PETs, which are estimated, to be present in the environment for more and less than fifteen years are presented in Figs 2 and 3, respectively. It is obvious that the surface of the newer PETs is smooth whereas the surface of the older PETs is highly cracked and uneven. This is in agreement with the general trend observed by ATR-FTIR that suggests that the surface of the older PETs is altered.

Figure 2. SEM visualizations of the surface topography and roughness of the polymers which are estimated to be present in the environment for more than fifteen years:

Figure 2

Open in a new tab

(a) PET_1997a, (b) PET_1997b, (c) PET_1998.

Figure 3. SEM visualizations of the surface topography and roughness of the polymers which are estimated to be present in the environment for less than fifteen years:

Figure 3

Open in a new tab

(a) PET_2001, (b) PET_2008, (c) PET_2011.

Discussion

The ATR-FTIR spectroscopy is a common technique that can be used to investigate the environmental degradation of PETs through the determination of any possible changes in the functional groups35. While applying this technique to compare materials, special precaution should be taken in respect to the production of false results i.e. decrease in band intensity. In this study, multiple (×5) spectra have been taken for the same spot of each of the three PET bottles (i.e. 1997, 2008, 2015) (Fig. S2). Also, spectra for different spots (×5) of the same PET bottle for each of the three PET bottles (i.e. 1997, 2008, 2015) are shown in Fig. S3. In all these cases, no significant differences between the recorded band intensities have been found compared to spectra differences among PET bottles with different expiration dates. Thus, the presented technique can be reliably used for comparing materials.

Up to our knowledge, this is the first time that plastic items, deposited in the marine environment with a temporal indication, are examined in respect to degradation. The expiration dates on the plastic bottles give an initial estimation regarding the bottles residence time in the environment. Surely, their deposition cannot be safely specified; nonetheless a magnitude regarding the years of presence in the marine environment can be estimated. The age of the bottles was estimated by the marked expiration date. However, we don’t know when exactly the examined bottles ended up in the marine environment; how long were floating in the sea surface or stranded on beach. A conservative estimate regarding the old samples (1997(a,b), 1998, 1999) is that they are exposed in the environment, including the marine environment, for more than fifteen years. When compared to the newer samples (2001, 2008, 2011, 2014), PET surface seems to stay robust for more than fifteen years in the environment. This is corroborated by the additional groups that were created only on the surface of the older samples (1997(a,b), 1998, 1999) at wavenumbers 620 cm−1 (C-H) (Fig. 1a) and 1435 cm−1 (C-H2) (Fig. 1c). It is the first time that such groups are recorded on PETs.

What is really interesting in the finding of the present study is that there is a clear separation of the ATR-FTIR spectra between the two groups i.e. the 90s and the millennium bottles. Thus, giving a distinct sign for the degradation process of PETs. Even for the extreme situation of the 1999 and the 2001 bottles, where there is only a two years interval, still the separation of the ATR-FTIR spectra is very clear.

At the same time, no or scarce information exists regarding the life-time of the synthetic polymers in the environment or under laboratory conditions which could be used as a reference towards the comparison of the present findings. In laboratory experiments studying PET degradation, a life expectancy of PET bottles was predicted under 100% humidity of 2736 and 9337 years. Whereas Muller et al.38 in his review paper based on the above-mentioned studies predicted the general life time of PET ranging from 16 to 48 years.

In laboratory studies at low temperatures, hydrolysis appears to be the most important degradation process. The findings of the present study show that plastics seem to follow a different pattern when stranded on the sea floor. Hence, the degradation of plastics is very subjective to the local environmental conditions that are difficult to be simulated in laboratory conditions. It is possible that the initial stage for degradation is the absorption of UV radiation (photolysis). UV light has sufficient energy to break the chemical bonds in the main polymer chain39. Then, PETs with altered surface properties sink to the bottom of the sea and hydrolytic degradation starts. Esters are the key functional groups that interact with water40. In the old samples, the progress of the degradation becomes slower since the ester functional groups disappear. The creation of new functional groups consisting only of carbon and hydrogen represents a totally new surface that its degradation path is not known.

In order to confirm whether the severe deterioration of the native functional groups of the PET surface, together with the formation of new ones are denotative of the aged (>fifteen years) PETs and thus could be further used for dating PETs found on the seafloor, the findings of the present study were compared with other PET spectra found in another sea basin. PETs (1995i, 1998i, 2010i, 2011i) from the Ionian Sea (Western Greece) (Fig. S4) were examined in respect to environmental degradation (ATR-FTIR analysis; same rational) and were compared with the ATR-FTIR time-series derived from the Saronikos Gulf (Fig. 4, S5). When the environmental degradation of PETs from the Ionian Sea was compared with that observed in the Saronikos Gulf, the results were very encouraging and confirmed the points discussed above. The two old bottles i.e. 1995i, 1998i from the Ionian Sea gave similar patterns of deterioration for the main five PET peaks at wavenumbers: 1715, 1245, 1100, 870 and 730 cm−1 (Fig. 4). Same for the formation of the new functional groups at wavenumbers 620 and 1435 cm−1. Especially, the 1998 PET bottle from the Ionian Sea (1998i) gave a similar ATR-FTIR spectrum with that of the 1998 PET from the Saronikos Gulf. Moreover, the ATR-FTIR spectrum of the 1995 PET from the Ionian Sea (1995i) gave even higher deterioration when compared to the oldest PET from the Saronikos Gulf (1997), with the deterioration being significant. The newer samples from the Ionian Sea (2010i, 2011i) followed the same pattern as the corresponding ones from Saronikos Gulf (Fig. S5). Thus by comparing the ATR-FTIR spectra of PET samples, one could date PET litter bottles from different marine environments.

Figure 4. ATR-FTIR comparative spectra of the outer (OUT) surface of the degraded PETs from the Saronikos Gulf (1997(a,b), 1998, 1999, 2001, 2008, 2011, 2014) and the old samples from the Ionian Sea (1995i, 1998i) compared with a virgin sample (2015).

Figure 4

Open in a new tab

For better visualization, enlarged excerpts of the ATR-FTIR comparative spectra are given at wavenumbers (a) 400–1000, (b) 1000–1200, (c) 1200–1600, (d) 1600–1800 cm−1.

Additionally, by comparing each peak from the Ionian Sea (Fig. 4, S5) with the corresponding peaks (native and new) from the Saronikos Gulf, a first date prediction is attempted for each of the PETs from the Ionian Sea. In Table 1, the date prediction of PETs from the Ionian Sea can be found based on each peak. Based on Table 1, the comparison of all peaks gave a quite accurate prediction for the expiration date of the PET samples from the Ionian Sea. The variation observed is within ± 3 years. Sample 1995i was out of the timeline recorded from Saronikos Gulf, yet the peak comparison suggested that the sample was older than the oldest PET sample from Saronikos Gulf (1997). For sample 1998i, most of the peaks suggested that the sample had an expiration date of 1998 or 1999. For samples 2010i and 2011i, the native peaks predicted their expiration date ± 3 years and the lack of new peaks (620, 1435 cm−1) suggested that the samples had an expiration date later than 2001.

Table 1. Date predictions for the PET samples from the Ionian Sea based on the comparison with individual peaks recorded for the various PET samples from Saronikos Gulf.

  Ionian Sea PETs
1995i 1998i 2010i 2011i
Native Peaks (cm−1)
1715 1997 1998 2010 2011
1245 <1997 1999 2010 2011
1100 <1997 1999 2008 2011
870 <1997 1999 2010 2008
730 <1997 1999 2008 2011
New peaks (cm)
1435 <1997 1998 >2001 >2001
620 <1997 1998 >2001 >2001
Expiration date 1995 1998 2010 2011
Open in a new tab

The degradation potential of plastics in the marine environment is of crucial importance. Being able to estimate the age of plastics (i.e. PETs) found in the marine environment is critical as it would further help us understand whether plastics have just entered the marine environment or whether they accumulate into the marine environment for decades. Such a finding would further enhance the introduction of management schemes through the understanding of whether the plastic pollution is new or old and tackle the problem accordingly. In addition, such a tool would benefit other scientists involved in studying the effects of marine litter i.e. identification of the age of plastics that have been colonized by organisms or of microplastics that do not have an expiration date written on them. The authors are planning to keep updating the existing database and thus, extending the PET time series along with the introduction of new comparative analytical techniques and methods (such as loss of mass, AFM, TEM, etc.).

Methods

On the basis of the assessment of marine litter on the seafloor of the Saronikos Gulf (Greece) from January 2013 to April 2014, plastic marine litter items were collected from its deepest part (150–350 m), from 70 hauls conducted by commercial trawl fisheries (Fig. 5). Plastic bottles made of polyethylene terephthalate (PET) were collected on condition that the expiration date was discernible. From a total of 509 plastic bottles, only in eight8 colorless plastic bottles (PETs) the expiration date could be clearly viewable; corresponding in the following years: 1997 (two bottles from the same year; indicated as: a,b), 1998, 1999, 2001, 2008, 2011, 2014 (Fig. S6). The plastic bottles were sorted and coded according to their expiration date, in two categories: the ‘90s bottles (1997(a,b), 1998, 1999) and the millennium bottles (2001, 2008, 2011, 2014). The expiration date-usually two years after production-was used as denotative to the time-period that the samples were present in the environment, including the marine.

Figure 5. Study map of the Saronikos Gulf (Greece), where the PET bottles were trawled from the submarine environment (ArcMap, ArcGIS 9, V. 9.3; www.esri.com).

Figure 5

Open in a new tab

All collected samples (PETs) were analyzed in respect to environmental degradation through the estimation of the ATR-FTIR, in order to determine any possible functional groups on the surface of PETs which could be further attributed to environmental degradation. The degraded samples were compared to a similar virgin sample obtained from a supermarket, coded as 2015. Furthermore, the surface topography and roughness as well as the organisms inhabiting on the surface of PETs, were investigated and visualized under SEM.

Additional Information

How to cite this article: Ioakeimidis, C. et al. The degradation potential of PET bottles in the marine environment: An ATR-FTIR based approach. Sci. Rep. 6, 23501; doi: 10.1038/srep23501 (2016).

Supplementary Material

Supplementary Information
srep23501-s1.pdf (1.8MB, pdf)

Acknowledgments

The present study was conducted within the framework of the European IP Project FP7-PERSEUS EC Grant Agreement No 287600. C.I. has received a Ph.D. grant. Sampling in the Ionian waters was conducted within the framework of the ‘DeFishGear’ project IPA-Adriatic Cross Border Cooperation 2007–2013′.

Footnotes

Author Contributions C.I.: Designing the experimental setup, Experimental Work and Data Analysis, Wrote the Paper. K.N.F.: Designing the experimental setup, Experimental Work and Data Analysis. H.K.K.: Designing the experimental setup, Wrote the Paper. M.G.: Data Analysis. C.Z.: Data Analysis, Reviewed the Manuscript. E.P.: Designing the experimental setup, Reviewed the Manuscript. F.G.: Reviewed the Manuscript. G.P.: Experimental Work and Data Analysis, Wrote the Paper.

References

  1. Yarsley V. E. & Couzens E. G. Plastics (Middlesex: Penguin Books Limited, 1945). [Google Scholar]
  2. Zaikab G. D. Marine microbes digest plastic. Nature, Published online 28 March, doi: 10.1038/news.2011.191 (2011).
  3. Law K. L. et al. Plastic accumulation in the North Atlantic subtropical gyre. Science 329, 1185–1188, doi: 10.1126/science.1192321 (2010). [DOI] [PubMed] [Google Scholar]
  4. Cózar A. et al. Plastic debris in the open ocean. PNAS 111, 10239–10244, doi: 10.1073/pnas.1314705111 (2014). [DOI] [PMC free article] [PubMed] [Google Scholar]
  5. Rochman C. M. et al. Policy: Classify plastic waste as hazardous. Nature 494, 169–171, doi: 10.1038/494169a (2013). [DOI] [PubMed] [Google Scholar]
  6. Bakir A., Rowland S. J. & Thompson R. C. Competitive sorption of persistent organic pollutants onto microplastics in the marine environment. Mar Pollut Bull 64, 2782–2789, doi: 10.1016/j.marpolbul.2012.09.010 (2012). [DOI] [PubMed] [Google Scholar]
  7. Jambeck J. R. et al. Plastic waste inputs from land into the ocean. Science 347, 768–771, doi: 10.1126/science.1260352 (2015). [DOI] [PubMed] [Google Scholar]
  8. Pastorelli G. et al. Environmentally induced colour change during natural degradation of selected polymers. Polym Degrad Stab 107, 198–209, doi: 10.1016/j.polymdegradstab.2013.11.007 (2014). [DOI] [Google Scholar]
  9. Sudhakar M. et al. Biofouling and biodegradation of polyolefins in ocean waters. Polym Degrad Stab 92, 1743–1752, doi: 10.1016/j.polymdegradstab.2007.03.029 (2007). [DOI] [Google Scholar]
  10. Shaw D. & Day R. Colour- and form-dependent loss of plastic micro-debris from the North Pacific Ocean. Mar Pollut Bull 28, 39–43, doi: 10.1016/0025-326X(94)90184-8 (1994). [DOI] [Google Scholar]
  11. Gregory M. R. & Andrady A. L. Plastics in the marine environment. Plastics and the Environment (eds Andrady A. L.) 379–401 (Wiley & Sons, New Jersey 2003). [Google Scholar]
  12. Barnes D. K., Galgani F., Thompson R. C. & Barlaz M. Accumulation and fragmentation of plastic debris in global environments. Philos T Roy Soc B 364, 1985–1998, doi: 10.1098/rstb.2008.0205 (2009). [DOI] [PMC free article] [PubMed] [Google Scholar]
  13. Ivar do Sul J. A. & Costa M. F. The present and future of microplastic pollution in the marine environment. Env Pollut 185, 352–364, doi: 10.1016/j.envpol.2013.10.036 (2013). [DOI] [PubMed] [Google Scholar]
  14. Thompson R. C. et al. Lost at sea: where is all the plastic? Science 304, 838, doi: 10.1126/science.1094559 (2004). [DOI] [PubMed] [Google Scholar]
  15. Elliott J. E. & Elliott K. H. Tracking Marine Pollution. Science 340, 556–558, doi: 10.1126/science.1235197 (2013). [DOI] [PubMed] [Google Scholar]
  16. Rochman C. M. et al. Polybrominated diphenyl ethers (PBDEs) in fish tissue may be an indicator of plastic contamination in marine habitats. Sci Total Environ 476–477, 622–633, doi: 10.1016/j.scitotenv.2014.01.058 (2014). [DOI] [PubMed] [Google Scholar]
  17. Madeira Di Beneditto A. P. & Arruda Ramos R. M. Marine debris ingestion by coastal dolphins: What drives differences between sympatric species? Mar Pollut Bull 83, 298–301, doi: 10.1016/j.marpolbul.2014.03.057 (2014). [DOI] [PubMed] [Google Scholar]
  18. Fossi M. C. et al. Large filter feeding marine organisms as indicators of microplastic in the pelagic environment: The case studies of the Mediterranean basking shark (Cetorhinus maximus) and fin whale (Balaenoptera physalus). Mar Env Res 100, 17–24, doi: 10.1016/j.marenvres.2014.02.002 (2014). [DOI] [PubMed] [Google Scholar]
  19. Watts A. J. R. et al. Uptake and Retention of Microplastics by the Shore Crab Carcinus maenas. Environ Sci Technol 48, 8823–8830, doi: 10.1021/es501090e (2014). [DOI] [PubMed] [Google Scholar]
  20. Rossi G., Barnoud J. & Monticelli L. Polystyrene Nanoparticles Perturb Lipid Membranes J Phys Chem Lett 5, 241–246, doi: 10.1021/jz402234c (2014). [DOI] [PubMed] [Google Scholar]
  21. Van Cauwenberghe L. & Janssen C. R. Microplastics in bivalves cultured for human consumption. Env Pollut 193, 65–70, doi: 10.1016/j.envpol.2014.06.010 (2014). [DOI] [PubMed] [Google Scholar]
  22. Wright S. L., Thompson R. C. & Galloway T. S. The physical impacts of microplastics on marine organisms: A review. Environ Pollut 178, 483–492, doi: 10.1016/j.envpol.2013.02.031 (2013). [DOI] [PubMed] [Google Scholar]
  23. Corcoran P. L., Moore C. J. & Jazvac K. An anthropogenic marker horizon in the future rock record. GSA Today 24, doi: 10.1130/GSAT-G198A.1 (2014). [DOI] [Google Scholar]
  24. Law K. L. & Thompson R. C. Microplastics in the seas. Science 345, 144–145, doi: 10.1126/science.1254065 (2004). [DOI] [PubMed] [Google Scholar]
  25. Eriksen M. et al. Plastic pollution in the world’s oceans: more than 5 trillion plastic pieces weighing over 250,000 Tons afloat at sea. PLoS ONE 9(12), e111913, doi: 10.1371/journal.pone.0111913 (2015). [DOI] [PMC free article] [PubMed] [Google Scholar]
  26. Cózar A. et al. Plastic accumulation in the Mediterranean Sea. PLoS ONE 10(4), e0121762, doi: 10.1371/ journal.pone.0121762 (2015). [DOI] [PMC free article] [PubMed] [Google Scholar]
  27. Galgani F. et al. Litter on the sea floor along European coasts: Mar Pollut Bull 40, 516–527, doi: 10.1016/S0025-326X(99)00234-9 (2000). [DOI] [Google Scholar]
  28. Schlining K. et al. Debris in the deep: Using a 22-year video annotation database to survey marine litter in Monterey Canyon, central California, USA. Deep-Sea Res PT I 79, 96–105, doi: 10.1016/j.dsr.2013.05.006 (2013). [DOI] [Google Scholar]
  29. Pham C. K. et al. Marine Litter Distribution and Density in European Seas, from the Shelves to Deep Basins. PLoS ONE 9, e95839, doi: 10.1371/journal.pone.0095839 (2014). [DOI] [PMC free article] [PubMed] [Google Scholar]
  30. Ioakeimidis C. et al. A comparative study of marine litter on the seafloor of coastal areas in the Eastern Mediterranean and Black Seas. Mar Pollut Bull 89, 296–304, doi: 10.1016/j.marpolbul.2014.09.044 (2014). [DOI] [PubMed] [Google Scholar]
  31. Keller A. A., Fruh E. L., Johnson M. M., Simon V. & McGourty C. Distribution and abundance of anthropogenic marine debris along the shelf and slope of the US West Coast. Mar. Pollut. Bull. 60, 692–700, doi: 10.1016/j.marpolbul.2009.12.006 (2010). [DOI] [PubMed] [Google Scholar]
  32. Watters D. L., Yoklavich M. M., Love M. S. & Schroeder D. M. Assessing marine debris in deep seafloor habitats off California. Mar Pollut Bull 60, 131–138, doi: 10.1016/j.marpolbul.2009.08.019 (2010). [DOI] [PubMed] [Google Scholar]
  33. Ramirez-Llodra E., De Mol B., Company J. B., Coll M. & Sardà F. Effects of natural and anthropogenic processes in the distribution of marine litter in the deep Mediterranean Sea. Prog Oceanogr 118, 273–287, doi: 10.1016/j.pocean.2013.07.027 (2013). [DOI] [Google Scholar]
  34. Pham C. K., Gomes-Pereira J. N., Isidro E. J., Santos R. S. & Morato T. Abundance of litter on Condor seamount (Azores, Portugal, Northeast Atlantic). Deep-Sea Res PT II 98, 204–208, doi: 10.1016/j.dsr2.2013.01.011 (2013). [DOI] [Google Scholar]
  35. Fotopoulou K. N. & Karapanagioti H. K. Surface properties of beached plastics. Environ Sci Pollut Res 22, 11022–11032, doi: 10.1007/s11356-015-4332-y (2015). [DOI] [PubMed] [Google Scholar]
  36. Edge M., Hayes M., Mohammadian M., Allen N. S. & Jewitt T. S. Aspects of poly (ethylene terephthalate) degradation for archival life and environmental degradation. Polym Degrad Stab 32, 131–153, doi: 10.1016/0141-3910(91)90047-U (1991). [DOI] [Google Scholar]
  37. Allen N. S., Edge M. & Mohammadian M. Physicochemical aspects of the environmental degradation of poly(ethylene terephthalate). Polym Degrad Stab 43, 229–237, doi: 10.1016/0141-3910(94)90074-4 (1994). [DOI] [Google Scholar]
  38. Müller R. J., Kleeberg I. & Deckwer W. D. Biodegradation of polyesters containing aromatic constituents. J Biotechnol 86, 87–95, doi: 10.1016/S0168-1656(00)00407-7 (2001). [DOI] [PubMed] [Google Scholar]
  39. Venkatachalam S. et al. Degradation and Recyclability of Poly (Ethylene Terephthalate). Polyester (eds Hosam El-Din M. Saleh), Chapter 4, 75–98 (InTech Publishers), doi: 10.5772/2748 (2012). [DOI] [Google Scholar]
  40. Li X. K. et al. Reaction Kinetics and Mechanism of Catalyzed Hydrolysis of Waste PET Using Solid Acid Catalyst in Supercritical CO2. AIChE 61, 200–214, doi: 10.1002/aic (2014). [DOI] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Supplementary Materials

Supplementary Information
srep23501-s1.pdf (1.8MB, pdf)

Articles from Scientific Reports are provided here courtesy of Nature Publishing Group

RESOURCES