Solvent and Intermediate Phase as Boosters for the Perovskite Transformation and Solar Cell Performance

Jinhyun Kim 1, Taehyun Hwang 1, Sangheon Lee 1, Byungho Lee 1, Jaewon Kim 1, Gil Su Jang 1, Seunghoon Nam 2, Byungwoo Park 1,a
PMCID: PMC4860713  PMID: 27156481

Abstract

High power conversion efficiency and device stabilization are two major challenges for CH3NH3PbI3 (MAPbI3) perovskite solar cells to be commercialized. Herein, we demonstrate a diffusion-engineered perovskite synthesis method using MAI/ethanol dipping, and compared it to the conventional synthesis method from MAI/iso-propanol. Diffusion of MAI/C2H5OH into the PbCl2 film was observed to be more favorable than that of MAI/C3H7OH. Facile perovskite conversion from ethanol and highly-crystalline MAPbI3 with minimized impurities boosted the efficiency from 5.86% to 9.51%. Additionally, we further identified the intermediates and thereby the reaction mechanisms of PbCl2 converting into MAPbI3. Through straightforward engineering to enhance the surface morphology as well as the crystallinity of the perovskite with even faster conversion, an initial power conversion efficiency of 11.23% was obtained, in addition to superior stability after 30 days under an ambient condition.

The feasible challenges in solar cell commercialization are enhancement in power conversion efficiency (PCE) and cost reduction to support the world-wide electricity consumption1,2,3,4,5. Alternatively, organometallic perovskite solar cells were first demonstrated by Miyasaka’s group in 2009 with a PCE of 3.8%6, and an enormous growth has been achieved over the last 6 years with the highest efficiency of 22.10%7. Perovskite (CH3NH3PbI3) solar cells are settled as the most attractive topic in photovoltaic research areas due to the low fabrication cost and high efficiencies, followed by inherent advantages of the perovskite material which include an appropriate and direct bandgap, small exciton binding energy, balanced ambipolar charge transport properties, etc.8,9,10,11,12. Furthermore, the synthesis of CH3NH3PbI3 (MAPbI3) goes through a simple process, by mixing PbI2 and MAI precursors6. In 2012, the superior performance via MAPbI3 synthesis with PbCl2 and MAI precursors was introduced by Snaith’s group, and property analyses were carried out by many groups13,14,15,16. Since then, researchers widely studied the chlorine effect, and concluded that chlorine enhances the morphology of perovskite films16,17,18,19,20. Even though the chlorine effect is suggested by many research groups, understanding the mechanisms on the synthesis is still required to be elucidated.

Architectural challenges are widely studied due to the ambipolar behavior21,22,23 of perovskites. Among them, the highest efficiency of 22.10%7 has been achieved with mesoporous structure, and mesoporous layer allows the additional light trapping effect24,25. In the mesoscopic structure, there are two major MAPbI3 deposition methods. The one-step solution deposition generally uses a mixture solution of PbI2 and MAI16, and the sequential deposition is carried out by pre-depositing the PbI2 film, followed by dipping it into an MAI-dissolved iso-propanol solution to form the MAPbI3 film26. Among them, the one-step solution deposition is highly beneficial in that this process is quite simple and time-saving. However, the sequential deposition is reported with a higher PCE than that of the one-step deposition27,28,29 due to the enhanced pore filling through the mesoporous TiO2 (mp-TiO2). Although the sequential deposition guarantees a high PCE, a comparative disadvantage in the sequential deposition is that it is a long-time process, since it goes through multiple steps to fabricate the perovskite film26.

In this article, we have demonstrated a straightforward diffusion-controlled synthesis approach by replacing the conventional MAI-dissolved iso-propanol solution with a MAI-dissolved ethanol solution, which enhanced the crystallinity, boosted the perovskite transformation, and minimized impurities. Moreover, we have detected intermediate phases when the PbCl2 precursor transforms into MAPbI3, and engineered the MAPbI3 deposition procedure by artificially mixing those intermediates as deposition precursors. This novel approach allowed superior surface morphology and crystallinity with enhanced conversion kinetics of MAPbI3, yielding an initial PCE of 11.23% and notable stability exhibiting 10.14% PCE after 30 days under ambient conditions.

Results

Ethanol Conversion

Sequential deposition is one of the most preferable methods for perovskite fabrication due to the high PCE. One major problem, however, is the long fabrication time by multiple fabrication steps26. To reduce the fabrication time in the sequential deposition process, boosting the formation kinetics of MAPbI3 using MAI with PbCl2 precursors is required. Therefore, a low viscous solvent and larger concentration of MAI are necessary for effective diffusion of MAI into the PbCl2 layer. In general, conventional dipping solution uses 10 mg mL−1 of MAI in iso-propanol26, and a high concentration of MAI in solvent reduces both cuboid sizes and PCEs30. Thus, finding an alternative solvent is necessary for the viscosity and diffusion aspects. Figure 1 schematically illustrates the movements of ionized MAI into the PbCl2 film with ethanol (20 mg mL−1) and iso-propanol (10 mg mL−1), where the conversion kinetics of PbCl2 into MAPbI3 for each solvent is quite different even with the optical images (Supplementary Fig. 1, fast conversion kinetics with MAI/ethanol). The extent of the reaction was easily estimated by color changes (Eg of MAPbI3 ≈ 1.55 eV). However, less viscous methanol was not effective due to the dissolution of MAPbI3 (Supplementary Fig. 2)26. The fabricated perovskite film with the same concentration (20 mg mL−1) for the iso-propanol solution results in rather small cuboid sizes (~80 nm) with a low PCE of 2.08% in the solar cell performance, as shown in Supplementary Fig. 3. The cuboid size of MAPbI3 with an ethanol solution is also distinguishable from that with iso-propanol, as shown in the scanning electron microscopy (SEM) (Fig. 2a,b). The PbCl2-deposited film and cuboid-size distributions are plotted in Fig. 2c, and the synthesized perovskite with twice-large cuboid sizes (~1180 nm) through an ethanol conversion is expected to produce higher carrier mobilities31.

Figure 1. Schematic illustration of the MAI in ethanol or iso-propanol diffusing into the PbCl2-wetted mesoporous-TiO2 (mp-TiO2).

Figure 1

Open in a new tab

The blocking-layer is coated on SnO2:F (FTO).

Figure 2. Solvent effects on MAPbI3 using ethanol or isoporpanol.

Figure 2

Open in a new tab

(a) SEM images of MAPbI3 using ethanol, (b) MAPbI3 using iso-propanol, and (c) PbCl2 on mp-TiO2. The average cuboid size is shown for MAPbI3 by ethanol or iso-propanol.

Figure 3 illustrates qualitative analysis of the perovskite formation with ethanol or iso-propano. The energy disperse x-ray spectroscopy (EDS) was conducted to identify the chlorine concentration (Fig. 3a). MAPbI3 converted from an ethanol solution contains lower Cl than that of iso-propanol-synthesized MAPbI3 since unreacted PbCl2 or partially-reacted MAPbCl3 remains in the film. Still, ethanol-based MAPbI3 shows some chlorine content, and we believe that this is caused by MACl which is a co-product during the MAPbI3 synthesis16,17,18. Actually, there is a possibility that chlorine is doped in the perovskite structure (MAPbI3-xClx) as reported by several groups14,15,16. However, the small quantity of chlorine in the perovskite structure is difficult to be evaluated, and the remaining chlorine may form other products17,19. Cross-sectional SEM image of MAPbI3 perovskite solar cell by ethanol exhibits uniform film structures, as shown in Fig. 3b. For further understanding of impurities, X-ray diffraction (XRD) scans were compared, and an ethanol-based MAPbI3 shows clear (110), (220) and (330) peaks (Fig. 3c). On the contrary, the conversion with iso-propanol produced impurity peaks of PbI2 and MAPbCl3 (Fig. 3c), indicating incomplete reaction. To explain the effect of ethanol on the crystallinity, we have additionally confirmed that the longer dipping time increases the crystallinity of MAPbI3 (Supplementary Fig. 4) eVen when the reaction was completed. Together with the optical observation in Supplementary Fig. 1, it can be said that MAI/ethanol-converted MAPbI3 completes the reaction faster with better crystallinity, compared to that of iso-propanol for the same dipping time. Furthermore, the light absorption from the synthesized perovskite is clearly different between ethanol and iso-propanol (Fig. 3d). The enhanced absorption at approximately 800 nm by ethanol is due to the superior purity of MAPbI3 (Eg ≈ 1.55 eV), while partially-reacted MAPbI3 by iso-propanol contains high-bandgap impurities, such as PbI2 (Eg ≈ 2.36 eV)32 and MAPbCl3 (Eg ≈ 3.17 eV)33. Therefore, the overall PCE is greatly improved from 5.86% to 9.51% (Fig. 3e) with much better stability (Fig. 3f), and both methods performed high reproducibility (Supplementary Fig. 5 and Supplementary Table 1). After 30 days, the PCE decreased from 9.51% to 8.53% and 5.86% to 3.75%, respectively, for the ethanol and iso-propanol solution (Table 1). The improved crystallinity and enlarged grain of MAPbI3 by ethanol surely prevents possible air penetration through various grain boundaries, leading to stability enhancement. The half-lifetime of the MAPbI3 perovskite solar cell (degradation details in Supplementary Fig. 6) was estimated to be ~150 and ~40 days, respectively, for ethanol and iso-propanol.

Figure 3. The dependence of MAPbI3 perovsktie solar cells using the MAI in an ethanol or iso-propanol solution.

Figure 3

Open in a new tab

(a) EDS mapping for iodine and chlorine in the synthesized MAPbI3 with an ethanol (top) or iso-propanol (bottom) solution. (b) Cross-sectional SEM image of a MAPbI3 perovskite solar cell from the MAI/ethanol solution. (c) X-ray diffraction of MAPbI3. (d) Absorption spectra for the synthesized MAPbI3. (e) J-V characteristics of the MAPbI3 perovskite solar cells. (f) Degradation of solar cells synthesized by ethanol or iso-propanol for the as-fabricated cells and cells after 30 days.

Table 1. Photovoltaic performance of MAPbI3 perovskite solar cells using an ethanol or iso-propanol solution (as-fabricated cells and cells after 30 days).

Reaction Condition Voc(V) Jsc(mA/cm2) FF η(%)
Initial Ethanol 0.87 17.3 0.63 9.51
Iso-propanol 0.83 14.4 0.49 5.86
30 Days Ethanol 0.84 16.4 0.63 8.53
Iso-propanol 0.79 10.1 0.47 3.75
Open in a new tab

To identify the reaction mechanisms, intermediate phases during the perovskite formation were investigated by the concentration variations of MAI in ethanol. With a low concentration of MAI/ethanol (Fig. 4a), PbCl2 partially reacts into PbI2 (5 mg mL−1). The chlorine in PbCl2 ion-exchanges with iodine in MAI to form PbI2, and the dissociated MA+ and Cl− from outer PbCl2 intercalate into the inner PbCl2 layer, transforming to the MAPbCl3 phase (15 mg mL−1 of MAI/ethanol). The intermediate PbI2 reacts with MAI directly to form MAPbI3 by intercalating MAI in the layered PbI2, while MAPbCl3 will ion-exchange with I− and reconstructs to the final MAPbI3, as schemed in Fig. 4b (20 mg mL−1 of MAI/ethanol). The whole reaction occurs through the following steps:

Figure 4. Reaction intermediates and mechanism analysis by X-ray diffraction measurements.

Figure 4

Open in a new tab

(a) Reaction 1 (left), reaction 4 (middle), and PbI2 precursor (right) with various concentrations of MAI in an ethanol solution. (b) Mechanisms of reaction 1 (PbCl2 + 3 MAI → MAPbI3 + 2 MACl). The MAI and ethanol diffuse into the outer PbCl2 layer, which converts PbCl2 into PbI2 and MACl. Additional MAI from the solution converts the synthesized outer PbI2 into MAPbI3, and MACl reacts with the inner PbCl2 transforming into MAPbCl3. The synthesized MAPbCl3 ion-exchanges with I− for the full MAPbI3 and MACl to complete the reaction.

graphic file with name srep25648-m1.jpg
graphic file with name srep25648-m2.jpg
graphic file with name srep25648-m3.jpg
graphic file with name srep25648-m4.jpg
graphic file with name srep25648-m5.jpg

The PbI2 phase converts into MAPbI3 earlier than the formation of MAPbCl3, as shown by the X-ray diffraction of MAPbI3 vs. MAPbCl3 phases for MAI concentrations of 10 and 15 mg mL−1 (Fig. 4a). We have also compared the perovskite formation from MAPbCl3 (MAPbCl3 + 3 MAI → MAPbI3 + 3 MACl) with PbI2 (PbI2 + MAI → MAPbI3) (respectively, in the middle and right of Fig. 4a), and found that both have resulted in no intermediate phases. Synthesizing fully-converted MAPbI3 from PbCl2 requires both intercalation and reconstruction steps, while the idea of reconstruction from MAPbCl3 to MAPbI3 was investigated in the previous report34. Therefore, we intuitively conclude that the recrystallization of intermediates both inside and on top of the mp-TiO2 film can enhance the coverage morphology, nanostructures, and crystallinity16,17,18 of MAPbI3 by multiple crystal-alignment steps. Moreover, ethanol conversion increases the kinetics of the reaction steps, and produces improved MAPbI3 film, compared to the conversion with iso-propanol.

Reaction Mechanism Engineering

To understand the phase-formation paths of MAPbI3 from PbCl2, we came up with an idea to further optimize MAPbI3 by utilizing the identified intermediate phases. While the direct conversion of MAPbCl3 to MAPbI3 can drastically reduce the reaction time, the repetition of crystallization from PbCl2 to MAPbI3 will enhance the surface morphology. Even though PbI2 appears during the transformation of the PbCl2 precursor to MAPbI3, and increases the reaction kinetics, the MAPbCl3 precursor is more reactive than the PbI2 precursor to synthesize MAPbI3 (middle and right graphs in Fig. 4a) where the MAPbCl3 precursor is likely to transform with lower MAI concentration than that of the PbI2 precursor. Also, the chlorine-based precursor should be preferred considering the positive effects of chlorine on the MAPbI3 perovskite solar cells16,17,18,19,20. Therefore, a straightforward direction is rendered by mixing PbCl2 and MAPbCl3 in several different ratios of 3:0 (reaction 1), 2:1 (reaction 2), 1:2 (reaction 3), and 0:3 (reaction 4), to optimize the reaction time with smooth surface morphology (Table 2 and Fig. 5).

Table 2. Precursor ratio of PbCl2: MAPbCl3 for the reactions 1, 2, 3, and 4.

  Reaction Mechanism Precursor Ratio (PbCl2: MAPbCl3)
RXN 1 PbCl2 + 3 MAI → MAPbI3 + 2 MACl 3:0
RXN 2 2 PbCl2 + MAPbCl3 + 9 MAI → 3 MAPbI3 + 7 MACl 2:1
RXN 3 PbCl2 + 2 MAPbCl3 + 9 MAI → 3 MAPbI3 + 8 MACl 1:2
RXN 4 MAPbCl3 + 3 MAI → MAPbI3 + 3 MACl 0:3
Open in a new tab

Figure 5. Schematic illustration of the experimental procedure.

Figure 5

Open in a new tab

Various ratios of PbCl2: MAPbCl3 were initially deposited on the substrate, and then the MAI-dissolved ethanol solution was utilized to synthesize MAPbI3.

As expected, we observed the morphology changes by synthesizing MAPbI3 films from precursors with different ratios of PbCl2 and MAPbCl3 through SEM, as shown in Fig. 6a. Perovskite films synthesized by reaction 2 exhibits clearly improved coverage with ~2320-nm-sized cuboids. Furthermore, addition of MAPbCl3 (reaction 3 and 4) deteriorates the coverage, but increases the cuboid size. When a larger amount of the MAPbCl3 precursor is added through reactions, the crystallinity of MAPbI3 is enhanced significantly, as shown by XRD (Fig. 6b,c). The enhanced crystallinity can be explained by the extent of reaction, and the facilely-transformed perovskite is likely to have high crystallinity even with the same dipping time (Supplementary Fig. 4). These observations are also consistent with the optical variations during the MAPbI3 formation (Supplementary Fig. 7). It should be noted that the coverages for the reactions 1, 2, 3, and 4 are different. However, conversions at ~10 s are distinct between reactions 1 (PbCl2 precursor) and 4 (MAPbCl3 precursor). The light absorption in Fig. 6d indicates that the absorption is more influenced by the coverage rather than the crystallinity and cuboid size of MAPbI3. The maximum coverage in reaction 2 reached the highest absorption, and the minimum coverage with reaction 4 yielded the lowest absorption. As a material perspective, MAPbI3 synthesis by reaction 4 is supposed to show excellent properties due to the high crystallinity and cuboid sizes, as plotted in Fig. 7a. Moreover, EDS was additionally measured to identify the comparative chlorine contents with iodine, which is plotted in Fig. 7b for each reaction, indicating that reaction 1 obtained the highest, and reaction 4 occupied the lowest concentration of chlorine. This chlorine tendency suggests that a co-product of MACl is minimized through the addition of MAPbCl3. (It should be noted that the EDS technique may not reflect the accurate chlorine concentration due to the coverage difference of each reaction.) It is possible that the detected chlorine through EDS is from the MACl phase or other products16,17,18. Moreover, excessive chlorine may lead to impurities, and deteriorate the device performance. Therefore, high crystallinity and low impurity of MAPbI3 are highly beneficial in the carrier mobilities, but recombination of carriers arising from poor coverage31 is another factor that we should be aware of.

Figure 6. The film quality dependence of MAPbI3 for the reactions 1, 2, 3, and 4.

Figure 6

Open in a new tab

(a) SEM images of the precursor and MAPbI3, (b,c) X-ray diffraction for the precursor and MAPbI3, and (d) absorption spectra of MAPbI3 by reactions 1, 2, 3, and 4.

Figure 7. The purity and deivce performance analysis for the reactions 1, 2, 3, and 4.

Figure 7

Open in a new tab

(a) Average cuboid size, (b) EDS for the comparative chlorine contents with iodine contents, (c) J-V curves, and (d) the efficiency degradation for the as-fabricated cells and cells after 30 days.

To understand the effects of crystallinity and coverage on the photovoltaic performance and stability, J-V curves are measured for 30 days under ambient conditions (Supplementary Fig. 6, and Table 3). In Fig. 7c, J-V curves were shown for the performance of the solar cells from each reaction, and the highly covered perovskite film from reaction 2 achieved the highest PCE of 11.23%. The lowest PCE of 4.03% was obtained by reaction 4, and these results indicate that the initial PCE is highly dependent on the perovskite coverage, which plays crucial roles in the carrier recombination. In contrast, MAPbI3 synthesized by reaction 4 was distinctively stable after 30 days. The stability is well correlated with the crystallinity and grain size, apparent from the normalized PCE in Fig. 7d, confirming the reduced decomposition behavior from the low-defect perovskite. All of the solar cells with different experimental conditions performed high reproducibility (Supplementary Fig. 5 and Supplementary Table 1). From the reactions 1, 2, 3, and 4, the half-lifetimes of MAPbI3 perovskite solar cells (degradation details in Supplementary Fig. 6) are estimated to be ~150, ~160, ~270, and ~300 days.

Table 3. Solar cell performance from the reactions 1, 2, 3, and 4 (as-fabricated cells and cells after 30 days).

Reaction Conditions Voc(V) Jsc (mA cm−2) FF η(%)
Initial RXN 1 0.87 17.3 0.63 9.51
RXN 2 0.90 19.8 0.63 11.23
RXN 3 0.76 16.3 0.56 6.94
RXN 4 0.61 11.7 0.57 4.03
30 Days RXN 1 0.84 16.4 0.62 8.53
RXN 2 0.89 17.8 0.64 10.14
RXN 3 0.73 15.2 0.59 6.55
RXN 4 0.61 11.7 0.52 3.83
Open in a new tab

Discussion

Fast conversion can have positive influences on the device performance and stability by producing highly-crystalline MAPbI3 perovskite. Therefore, we have controlled the diffusion reaction of MAI and PbCl2 with ethanol to boost the perovskite transformations, leading to phase-pure and highly-crystalline perovskite films. Since PbCl2 goes through several intermediate phases during the formation of MAPbI3, we utilized the intermediates by mixing them with a conventional PbCl2 precursor to boost the conversion kinetics and performance of the resulting solar cell. Thereby, the optimized crystallinity and coverage yielded a PCE of 11.23% with PbCl2: MAPbCl3 = 2:1 (reaction 2). Although the precursor with 100% MAPbCl3 (reaction 4) resulted in the fastest transformations of MAPbI3 and the most stable solar cell performance, poor coverage lowered the PCE of the device. Therefore, compact coverage of the perovskite with super-sized cuboids expects to achieve further enhanced performance and stability of the MAPbI3 perovskite solar cell. At this point, investigation of hysteresis still remains as a future work.

Methods

Perovskite Solar Cell Fabrication

Fluorine-doped tin oxide substrate (FTO, TEC 8: Pilkington) was cleaned by sonication in Mucasol (Aldrich), ethanol (DEAJUNG), and DI water for 30 min sequentially. 50 nm of compact the TiO2 blocking layer was deposited by spin-coating the mixture solution of 0.15 mM titanium diisopropoxide bis(acetylacetonate) (Aldrich) and 1-butanol (75.0 wt. % in iso-propanol, Aldrich) in 2500 rpm for 20 s followed by heating at 125 °C for 5 min in an air oven. The same step was repeated with 0.3 mM concentration and the substrate was annealed at 500 °C for 30 min. After the TiO2 blocking layer was ready, TiO2 pastes (ENB Korea) with 20 nm-sized nanoparticles were mixed with terpineol (Aldrich) in 1:2 ratio, followed by spin-coating at 4000 rpm for 30 s, yielding a ~350 nm thickness of the mp-TiO2 layer. For the perovskite synthesis, MAI was first synthesized by following literature method26. 1.5 M PbCl2 (Aldrich) was diluted in dimethyl sulfoxide (DMSO, Aldrich), and then MACl (Aldrich) was added with different concentrations (0, 0.5, 1.0, and 1.5 M) to synthesize the reaction 1, 2, 3, and 4 precursors where the reaction 1, 2, and 3 precursors contain both MAPbCl3 and PbCl2 phases, whereas the reaction 4 precursor contains only MAPbCl3 (MAPbCl3 forms by 1:1 molar stoichiometric ratios of MACl and PbCl2). After the preparation of precursor mixture solutions, the solution was preheated at 100 °C and the substrate was preheated at 150 °C, then the solution was spin-coated at 2000 rpm for 5 s, followed by 6000 rpm for 5 s. The film was annealed at 150 °C for 30 min, and cooled down in an ambient condition. After the film was cooled down, it was dipped into 20 mg mL−1 of MAI in an anhydrous ethanol solution (Daejung) for 20 min under ambient conditions (25 °C and 55% humidity) and annealed at 100 °C for 30 min. The hole transport solution was prepared by mixing 72.3 mg mL−1 of spiro-OMeTAD (Merck) in chlorobenzene (Aldrich) with 28.8 μL of tert-butylpyridine (Aldrich) and a 17.5 μL solution of 520 mg of lithium bis(trifluoromethylsyfonyl)imide salt (Aldrich) in 1 mL acetonitrile (Aldrich) was spin-coated at 3000 rpm for 45 s. Finally, 100 nm thickness of an Au electrode was then thermally evaporated.

Device Characterizations

The morphologies of MAPbI3 perovskite films were analyzed using scanning electron microscope (Normal-SEM, JSM-6360: Hitachi). The chlorine compositions and distribution were examined using energy-dispersive X-ray spectroscopy (EDS, ISIS-300: Oxford Instruments). The phases of the synthesized samples were characterized by X-ray diffraction (XRD, D8 Advance: Bruker). The photocurrent-voltage (J–V) curves of MAPbI3 perovskite solar cells were obtained with a potentiostat (CHI 608C: CH Instrumental Inc.) under AM 1.5 illumination at 100 mW cm−2 (K3000: McScience) with an active cell area of 0.09 cm2. The field-emission scanning electron microscope (FE-SEM, Merlin-Compact: Carl Zeiss) was used to observe the plan and cross-sectional views. The absorption spectra of the MAPbI3-deposited films were recorded on a UV-Vis spectrophotometer (Lambda 20: Perkin Elmer). Stability was measured every 5 days, and stored at 25 °C with 55% of humidity under dark conditions.

Additional Information

How to cite this article: Kim, J. et al. Solvent and Intermediate Phase as Boosters for the Perovskite Transformation and Solar Cell Performance. Sci. Rep. 6, 25648; doi: 10.1038/srep25648 (2016).

Supplementary Material

Supplementary Information
srep25648-s1.pdf (568.2KB, pdf)

Acknowledgments

This work was supported by the National Research Foundation of Korea (NRF): 2013R1A1A2065793, 2010-0029065 and 2015K2A1A2070386.

Footnotes

Author Contributions J.K. fabricated the solar cell devices, designed the whole experiments, and participated in writing the paper. T.H. supported the optimization process on the solar cell fabrication, and participated in writing the paper. S.L. carried out the electrochemical analyses, and participated in writing the paper. B.L. supported the optimization process of MAPbI3 perovskite synthesis, and participated in writing the paper with vital comments. J.K. analyzed electrochemical properties of the MAPbI3 perovskite, and participated in writing the paper. G.S.J. supported the optimization steps in thermal evaporation of an Au electrode. S.N. helped writing the paper, and gave constructive scientific comments. B.P. advised on the overall experiments with vital comments, and finalized the manuscript.

References

  1. Shin B. et al. Thin film solar cell with 8.4% power conversion efficiency using an earth‐abundant Cu2ZnSnS4 absorber. Prog. Photovolt.: Res. Appl. 21, 72–76 (2013). [Google Scholar]
  2. Choi H. et al. The role of ZnO-coating-layer thickness on the recombination in CdS quantum-dot-sensitized solar cells. Nano Energy 2, 1218–1224 (2013). [Google Scholar]
  3. Kim D. et al. Backcontact CdSe/CdTE windowless solar cells. Sol. Energ. Mat. Sol. C. 109, 246–253 (2013). [Google Scholar]
  4. Kim J. et al. The role of a TiCl4 treatment on the performance of CdS quantum-dot-sensitized solar cells. J. Power Sources 220, 108–113 (2012). [Google Scholar]
  5. Choi H. et al. The construction of tandem dye-sensitized solar cells from chemically-derived nanoporous photoelectrodes. J. Power Sources 274, 937–942 (2015). [Google Scholar]
  6. Kojima A., Teshima K., Shirai Y. & Miyasaka T. Organometal halide perovskites as visible-light sensitizers for photovoltaic cells. J. Am. Chem. Soc. 131, 6050–6051 (2009). [DOI] [PubMed] [Google Scholar]
  7. National Renewable Energy Laboratory (NREL), Best Research-Cell Efficiencies, http://www.nrel.gov/ncpv/images/efficiency_chart.jpg (Accessed: 30th March, 2016).
  8. Kazim S., Nazerruddin M. K., Gratzel M. & Ahmad S. Perovskite as Light Harvester: A Game Charger in Photovoltaics. Angew. Chem. Int. Ed. 53, 2812–2824 (2014). [DOI] [PubMed] [Google Scholar]
  9. McGehee M. D. Materials science: fast-track solar cells. Nature 501, 323–325 (2013). [DOI] [PubMed] [Google Scholar]
  10. Hodes G. Perovskite-based solar cells. Science 342, 317–318 (2013). [DOI] [PubMed] [Google Scholar]
  11. Ponseca C. S. et al. Organometal halide perovskite solar cell materials rationalized: ultrafast charge generation, high and microsecond-long balanced mobilities, and slow recombination. J. Am. Chem. Soc. 136, 5189–5192 (2014). [DOI] [PubMed] [Google Scholar]
  12. Frost J. M. et al. Atomistic origins of high-performance in hybrid halide perovskite solar cells. Nano Lett. 14, 2584–2590 (2014). [DOI] [PMC free article] [PubMed] [Google Scholar]
  13. Lee M. M., Teuscher J., Miyasaka T., Murakami T. N. & Snaith H. J. Efficient hybrid solar cells based on meso-superstructured organometal halide perovskites. Science 338, 643–647 (2012). [DOI] [PubMed] [Google Scholar]
  14. Colella S. et al. MAPbI3−xClx mixed halide perovskite for hybrid solar cells: the role of chloride as dopant on the transport and structural properties. Chem. Mater. 25, 4613–4618 (2013). [Google Scholar]
  15. Wehrenfennig C., Eperon G. E., Johnston M. B., Snaith H. J. & Herz L. M. High charge carrier mobilities and lifetimes in organolead trihalide perovskites. Adv. Mater. 26, 1584–1589 (2014). [DOI] [PMC free article] [PubMed] [Google Scholar]
  16. Williams S. T. et al. Role of chloride in the morphological evolution of organo-lead halide perovskite thin films. ACS Nano 8, 10640–10654 (2014). [DOI] [PubMed] [Google Scholar]
  17. Unger E. L. et al. Chloride in lead chloride-derived organo-metal halides for perovskite-absorber solar cells. Chem. Mater. 26, 7158–7165 (2014). [Google Scholar]
  18. Deepa M., Ramos J. F., Shivaprasad M. S. & Ahmad S. Unravelling the Role of Monovalent Halides in Mixed-Halide Organic-Inorganic Perovskite. ChemPhysChem. 17, 913–920 (2016). [DOI] [PubMed] [Google Scholar]
  19. Yin W.-J., Chen H., Shi T., Wei S.-H. & Yan Y. Origin of high electronic quality in structurally disordered CH3NH3PbI3 and the passivation effect of Cl and O at grain boundaries. Adv. Electron. Mater. 1, 1500044 (2015). [Google Scholar]
  20. Mosconi E., Ronca E. & Angelis F. D. First-principles investigation of the TiO2/organohalide perovskites interface: the role of interfacial chlorine. J. Phys. Chem. Lett. 5, 2619–2625 (2014). [DOI] [PubMed] [Google Scholar]
  21. Chen Q. et al. Planar heterojunction perovskite solar cells via vapor-assisted solution process. J. Am. Chem. Soc. 136, 622–625 (2013). [DOI] [PubMed] [Google Scholar]
  22. Eperon G. E., Burlakov V. M., Docampo P., Goriely A. & Snaith H. J. Morphological control for high performance, solution-processed planar heterojunction perovskite solar cells. Adv. Funct. Mater. 24, 151–157 (2014). [Google Scholar]
  23. Liu M., Johnston M. B. & Snaith H. J. Efficient planar heterojunction perovskite solar cells by vapour deposition. Nature 501, 395–398 (2013). [DOI] [PubMed] [Google Scholar]
  24. Mihi A. Zhang C. & Braun P. V. Transfer of preformed three-dimensional photonic crystals onto dye-sensitized solar cells. Angew. Chem. Int. Ed. 50, 5712–5715 (2011). [DOI] [PubMed] [Google Scholar]
  25. Grandidier J., Callahan D. M., Munday J. N. & Atwater H. A. Light absorption enhancement in thin-film solar cells using whispering gallery modes in dielectric nanospheres. Adv. Mater. 23, 1272–1276 (2011). [DOI] [PubMed] [Google Scholar]
  26. Burschka J. et al. Sequential deposition route to high performance perovskite-sensitized solar cells. Nature 499, 316–320 (2013). [DOI] [PubMed] [Google Scholar]
  27. Im J.-H., Kim H.-S. & Park N.-G. Morphology-photovoltaic property correlation in perovskite solar cells: one-step versus two-step deposition of CH3NH3PbI3. APL Mater. 2, 081510 (2014). [Google Scholar]
  28. Ma Y. et al. A highly efficient mesoscopic solar cell based on CH3NH3PbI3−xClx fabricated via sequential solution deposition. Chem. Commun. 50, 12458–12461 (2014). [DOI] [PubMed] [Google Scholar]
  29. Yantara N. et al. Loading of mesoporous titania films by CH3NH3PbI3 perovskite, single step vs. sequential deposition. Chem. Commun. 51, 4603–4606 (2015). [DOI] [PubMed] [Google Scholar]
  30. Im J.-H., Jang I.-H., Pellet N., Gratzel M. & Park N.-G. Growth of CH3NH3PbI3 cuboids with controlled size for high-efficiency perovskite solar cells. Nat. Nanotechnol. 9, 927–932 (2014). [DOI] [PubMed] [Google Scholar]
  31. Nie W. et al. High-efficiency solution-processed perovskite solar cells with millimeter-scale grains. Science 347, 522–525 (2015). [DOI] [PubMed] [Google Scholar]
  32. Supasai T., Rujisamphan N., Ullrich K., Chemseddine A. & Dittrich T. Formation of a passivating CH3NH3PbI3/PbI2 interface during moderate heating of CH3NH3PbI3 layers. Appl. Phys. Lett. 103, 183906–1 (2013). [Google Scholar]
  33. Comin R. et al. Structural, optical, and electronic studies of wide-bandgap lead halide perovskites. J. Mater. Chem. C 3, 8839–8843 (2015). [Google Scholar]
  34. Zhou H. et al. Interface engineering of highly efficient perovskite solar cells. Science 345, 542–546 (2014). [DOI] [PubMed] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Supplementary Materials

Supplementary Information
srep25648-s1.pdf (568.2KB, pdf)