. 2016 Sep 12;6:32896. doi: 10.1038/srep32896

Quenched Magnon excitations by oxygen sublattice reconstruction in (SrCuO2)n/(SrTiO3)2 superlattices

M Dantz 1,a, J Pelliciari 1, D Samal 2,*, V Bisogni 1,†, Y Huang 1, P Olalde-Velasco 1,‡, V N Strocov 1, G Koster 2, T Schmitt 1,b
PMCID: PMC5018731  PMID: 27616448

Abstract

The recently discovered structural reconstruction in the cuprate superlattice (SrCuO2)n/(SrTiO3)2 has been investigated across the critical value of n = 5 using resonant inelastic x-ray scattering (RIXS). We find that at the critical value of n, the cuprate layer remains largely in the bulk-like two-dimensional structure with a minority of Cu plaquettes being reconstructed. The partial reconstruction leads to quenching of the magnons starting at the Γ-point due to the minority plaquettes acting as scattering points. Although comparable in relative abundance, the doped charge impurities in electron-doped cuprate superconductors do not show this quenching of magnetic excitations.

Despite the great focus high-Tc cuprates have received in the past 25 years, a comprehensive explanation for superconductivity is still lacking. Since conventional BCS-like phonon mediation has been ruled out, it has been widely accepted that magnetic fluctuations play a significant role. However, their role is still controversial in light of the discovery of competing charge-ordering phenomena1,2,3,4,5,6,7. Therefore, huge effort has recently been put in the investigation of the interplay between structural modifications and magnetic excitations8,9.

It is thus desirable to investigate the impact of structural changes on the microscopic magnetism of cuprates. Complex oxide thin films and heterostructures in particular provide a multitude of possibilities for artificially tailoring the microscopic interactions at the atomic level since their structure is easily controllable by choice of substrate (i.e. strain) and dimensionality. Recently, developments in the field of epitaxial film growth and lattice engineering have sprouted a manifold of novel materials with interesting properties10,11,12.

Infinite layer SrCuO2 (SCO) in (SrCuO2)n/(SrTiO3)2 superlattices (SL) has been reported to be susceptible to structural changes in the very thin limit due to its polar nature13,14,15. Starting from the infinite layer bulk structure of connected copper-oxygen plaquettes hosting long-range ordered antiferromagnetism, it develops a quasi one-dimensional conformation by re-arranging the oxygen sublattice below a critical thickness of about 5 unit cells (uc), that is caused by a relaxation of the polar electrostatic energy10,14. The oxygen sublattice rearrangement effectively causes the copper-oxygen plaquettes to flip out of the a-b plane (Fig. 1(a)) into either the b-c plane (Fig. 1(b)) or the a-c plane (Fig. 1(c)) resulting in a quasi 1D structure when the SCO thickness is confined below the critical value.

Figure 1.

Figure 1

Open in a new tab

Sketches of the structure with respect to the scattering plane (green plane), for (a) the bulk like infinite layer, (b) the Π sheet orientation, (c) the Σ-sheet orientation. Red (blue) balls depict oxygen (copper). Strontium atoms are omitted for clarity.

The effect of chemical doping on the magnetic excitations in the cuprates has been studied intensively16,17,18. However, studies on modifying the collective magnetism by structural modifications, while leaving the stoichiometry intact, are missing so far. In this article, we report on direct measurements of the influence of a structural reconstruction on collective magnetic excitations in cuprate 2D layers. While being completely reoriented below the reconstruction threshold thickness, the SLs around the critical thickness exhibit an instability towards flipping, i.e. while the majority of plaquettes are still in bulk like configuration, a minority of plaquettes is already flipped, forming impurities in the 2D layers. These impurities act as scattering points for magnons, quenching them around the Γ-point. This allows us to compare the present case of dimensionality-induced defect scattering to the known effects of chemical doping in the cuprates.

We employ resonant inelastic x-ray scattering (RIXS), which has been established as a powerful tool for the simultaneous investigation of structural, electronic and magnetic properties especially for cuprates9,19,20,21. RIXS is sensitive to orbital and ligand-field excitations22,23,24, as well as to elementary magnetic excitations, such as the evolution from magnon to paramagnon character upon doping16,25,26,27. The experiment was performed with the RIXS spectrometer of the ADRESS beamline of the Swiss Light Source at the Paul Scherrer Institut28,29, which allows for a combined energy resolution better than 130 meV. A complete description of the experimental conditions can be found in the Supplementary Information.

Results

Structure

In Fig. 1 we show the different structural orientations possible in these superlattices. Figure 1(a) depicts the bulk-like structure with the copper-oxygen plaquettes oriented in the a-b plane forming a quasi 2D checkerboard-like structure, i.e parallel to the sample surface, thus being perpendicular to the growth direction. When reducing the thickness below the reorientation threshold of 5 uc, the orientation of the oxygen sublattice changes by repositioning some of the oxygen ions from the CuO2 plane to the Sr plane (i.e. the b-c plane), thus effectively flipping the copper-oxygen plaquettes along one axis perpendicular to the c axis. Since the a and b crystal directions are twinned, the flipping occurs with equal probability along both directions, creating domains of the two different orientations (see Fig. S1 in the Supplementary Information), as depicted in Fig. 1(b,c). As the copper plaquettes are now oriented either in the a-c or b-c plane, they are not continuous along c-direction due to the limited thickness of SCO layer, effectively reducing them to a quasi one-dimensional structure of width n. Note that structurally, these two orientations are equivalent, but our scattering geometry introduces a distinction between them as one of the two possible orientations is lying in the scattering plane (Fig. 1(b)) and one is oriented perpendicular to it (Fig. 1(c)). Therefore, we introduce the nomenclature of calling the former Π sheets and the latter Σ sheets, following the notation of light polarisation in the respective direction.

In bulk single crystals, SrCuO2 forms quasi one-dimensional chains. However, it has also been reported that if grown under pressure and high temperature, a 2D planar structure can also be realised30,31,32. In particular, if grown on SrTiO3, SrCuO2 grows in a two-dimensional structure, as can be inferred from the structural data in ref. 14, as well as from a polarization analysis of the XAS data in Fig. 2(a), in which we show Cu L3 x-ray absorption spectra (XAS), taken at an incidence angle of 5 degrees for 3, 5, and 8 uc SL. The XAS data shows a vanishing excitonic peak at 931 eV for π polarization, whereas for σ polarization, this feature is dominating the spectrum. This is incompatible with the 1D crystal structure as found in bulk crystalline SrCuO2 as it proves that the unoccupied Inline graphic orbital lies parallel to the surface of the sample. In the 1D bulk crystalline SrCuO2, the unoccupied orbital lies perpendicular to the surface33, which would produce either no dichroism (in the case of the chains running perpendicular to the scattering plane), or it would give a strong excitonic peak in the π polarization and a vanishing signal in the σ polarization otherwise. When tuning the thickness of the films measured in this work, we see the footprint of the change in crystal structure in the evolution of the XAS in Fig. 2(a), exactly as expected from this geometrical argument. The disappearance of the dichroism upon crossing the structural reorientation threshold can be explained by the copper-oxygen plaquette sheet reorientation, shown in Fig. 1(b,c), assuming an equal distribution of sheet orientations between Π and Σ sheets and an average domain size much smaller than the x-ray beam spot (in this case ca. 4 × 50 μm2). As local tetragonal symmetry is preserved, both sheet orientations have the hole in the Inline graphic orbital lying in the sheet plane, thus being only accessible with σ polarised light for the Σ sheets, and π polarised light for the Π sheet. This dichroism emphasises that above the reorientation thickness threshold, this compound indeed forms a 2D structure, similar to CaCuO2 investigated in ref. 34. Furthermore, this results in the vanishing dichroism observed when crossing the reorientation threshold.

Figure 2.

Figure 2

Open in a new tab

(a) Cu L3 X-ray absorption spectra for the different superlattices measured, showing the successively vanishing linear dichroism. The XAS of the 80 uc thick film is virtually identical to the 8 uc SL and therefore left out. (b) Exemplary fit of the magnetic part. The remaining spectral weight between the elastic line (A) and the magnon (B) can be attributed to phonons including higher order harmonics21. The Multi Magnon part (C) has been fitted with a Gaussian line, as the higher order contributions are negligible for the position of the single magnon peak. (c) Cu L3 RIXS data for the superlattices. Note the remaining Inline graphic peak at 2.7 eV, which is persisting across the atomic reorientation threshold (see text). Both (b,c) are taken at 10 K with σ polarization at q = 0.45(r.l.u.).

Orbital structure

It has been observed that the Cu L3 XAS data resembled an orbital reconstruction, but a clear interpretation was still lacking14. An equal occupation of the Inline graphic and the Inline graphic orbitals was assumed from vanishing linear dichroism observed in XAS. This would, however, be incompatible with local tetragonal symmetry as these two orbitals would have to be degenerate. Therefore, direct access to the energy levels of the different d-orbitals is desirable. In Fig. 2c, we show Cu L3 RIXS spectra for 3, 5 and 8 uc superlattices containing the spectral footprint of the different dd-excitations, i.e. transitions of the electron vacancy from the Inline graphic orbital to other d-orbitals. The persistence of the Inline graphic peak upon crossing the reorientation threshold is a fingerprint of the persistence of local tetragonal symmetry, discouraging the picture of orbital reconstruction. From the RIXS data, we can immediately extract the crystal field splitting parameters for the bulk-like cases. Using the method presented in ref. 23, we obtain values of Ds = 0.429 ± 0.005 eV, Dt = 0.197 ± 0.005 eV and 10Dq = 1.486 ± 0.003 eV, which are similar to the values obtained for bulk CaCuO223. Details are shown in the Supplementary Information.

Magnetic excitations

Next, we investigate the magnetic excitations in these superlattices. RIXS is an ideal tool for investigating magnetic excitations in thin films as it is sensitive even to layers of one unit cell thickness9,34. A sketch of the experimental setup can be found in the Supplementary Materials, Fig. S3. In Fig. 3, we show momentum dependent RIXS measurements with incident polarization chosen in order to enhance single magnon excitations35, i.e. σ polarisation in grazing incidence geometry (corresponding to negative q-transfer values) and π polarisation in grazing exit geometry (corresponding to positive q-transfer values) for the 80 unit cell thick film (Fig. 3(a)), the 8 and 5 uc SL (Fig. 3(b,c), respectively). For the 3 uc SL however, due to the change in geometry, we restrict ourselves to π polarisation in order to selectively excite the Π sheets. This choice was made because the Σ sheets are continous only perpendicular to the scattering plane. In order to obtain the exact positions of the magnetic excitations, we performed a multi peak fit as shown in Fig. 2(c). Note that single magnon excitations (Peak B) is close to the resolution limit as it is very similar in width to the elastic scattering line (Peak A) and can thus be identified as a coherent magnon excitation. Peak C is an excitation of multiple magnons at once with highest contribution of a bigmanon. Note that a Bimagnon peak does not necessarily have twice the energy of a single magnon excitation36. The higher order contributions have been neglected as can be seen from the small high energy tail as they do not play a role for the exact location of the single magnon excitation. For the 80 uc thick film as well as the 8 uc and 5 uc SL, we observe a clear magnon dispersion with a periodicity of the lower bound of π. Note that we use the convention commonly used in RIXS of defining the momentum transfer so that the antiferromagnetic ordering vector is at (h, k, l) = (1, 1, 0)π. For a 1D compound such as bulk single crystal SrCuO2, a spinon dispersion with a lower bound periodicity of 0.5π would be expected, as has been observed by some of us in the related compound Sr2CuO3 in ref. 22 and by inelastic neutron scattering in both SrCuO2 and Sr2CuO330,31. We observe that the magnetic spectral weight of both the 80 uc thick film and the 8 uc SL have a markedly different behaviour compared to the magnetic excitation in the aforementioned references. This is further evidenced by the magnon behaviour of the magnetic excitations in the Γ − M direction of the 8 uc sample shown in the Supplementary Information, Fig. S4. Both the 80 uc and the 8 uc cases are reasonably similar, while for the 5 uc SL, we observe a reduction of the spectral weight of the magnetic excitation starting around the Γ point. For the 3 uc sample, the magnetic excitations seem to be quenched completely. This can also be seen in the constant momentum cuts shown in Fig. 4(a). For the 5 uc SL, the spin excitations show a more sophisticated behaviour. While virtually absent in the lowest momentum cut, the spin excitations close to the AF zone boundary are almost as strong as for the bulk sample. We also observe that multi-magnon excitations are unusually strong compared to other undoped cuprates37. The relative strength of multi-magnon excitations has been linked to increased quantum fluctuations9, which might be caused by strain induced by the substrate or due to the reduced dimensionality.

Figure 3.

Figure 3

Open in a new tab

Contour plots of the RIXS data for (a) the 80 uc thick film, (b) the 8 uc superlattice, (c) the 5 uc superlattice and (d) the Π sheet in the 3 uc superlattice. The solid lines in (a,b) are the fits to linear spin wave theory. Note for the 8 and 5 uc superlattices the increasing leakage of spectral weight from the coherent magnon excitation to the incoherent region at higher energies. See text for detailed experimental conditons.

Figure 4.

Figure 4

Open in a new tab

(a) Constant momentum cuts for the 3, 5 and 8 uc cases, showing the quenching of the magnetic spectral weight. The arrows denote the maximum intensity of the low energy magnetic excitation. (b,c) Integrated spectral weight of the magnetic excitations, for (b) the low energy part (up to 0.6 eV), (c) the whole magnetic regime up to 0.9 eV. Note that for the 80 uc, 8 uc and 3 uc the ratio of spectral weight remains constant in (b,c), while the integrated signal of the 5 uc cases increases significantly (Note that all spectra are for σ polarisation, i.e probing the Σ sheet for the 3 uc film). It should be noted that due to the different structual conformation, the 3 uc can only act as a rough reference.

Although quenched for low q, the magnetic excitations in the 5 uc SL are located at similar energies as the 8 uc SL for higher q, see Fig. 3. Spectral weight is transferred from the low energy part at about 300 meV to higher energies, as can be seen in Fig. 3(c). For the 3 uc SL, the low energy part of the magnetic spectral weight is quenched across the entire BZ, see Fig. 3(d). In Fig. 4(a), we show cuts of the contour plots for different q and different SCO thicknesses. We observe that the difference in spectral weight between the 5 uc and 8 uc cases is largest around the Γ point and is reduced towards the X point. Furthermore, for low q transfer, we see a pronounced high energy tail between 0.4 eV and 0.9 eV, which can also be observed in Fig. 3(c). However, the spectral weight of the low energy part of the magnetic excitation in the 5 uc case is almost matching that of the bulk-like 8 uc one for large q, see Fig. 4(a). We interpret the low energy part as a coherent magnon excitation and the higher energy part as an incoherent excitation. In order to investigate this shift of spectral weight, we sum up the coherent part of the magnetic excitations (0.1 eV to 0.6 eV), shown in Fig. 4(b), and both the coherent and incoherent part (0.1 eV to 0.9 eV) in Fig. 4(c). We can see that the 8 uc and 5 uc films are castly different when taking only the coherent part into account, while being almsot identical when taking the whole range of magnetic excitations into account. However, we can observe slight differences between the different samples, even between the 8 uc and the reference thick film of 80 uc. We attribute this to small interface effects, as have been demonstrated in refs 9 and 34. For the 3 uc sample, we see still some amount of spectral wight, which can be explained by spin excitations of incoherent nature throughout the Brillouin zone.

From the dispersion of the magnon excitations of the 8 uc and 80 uc cases it is possible to extract the superexchange constant J by using a linear spin wave approach34,38,39. For thinner SCO layers (5 and 3 uc SLs), the quenching of the magnetic spectral weight around the Γ point prohibits such an analysis. As a starting point for our fitting, we used ref. 39 which employed INS to measure the magnetic dispersion of a La2CuO4 bulk crystal, and extracted J = 143 meV, Jc = −58 meV and Inline graphic meV. Taking into account our resolution of 130 meV, we assume the latter two to be equal to 0. The measurements were carried out in the Γ − X direction, therefore ky = 0. The linear spin wave equation used here is given as Eq. 1 in the Methods section. The linear spin wave fit results are shown in Fig. 3(a,b) on top of the contour plots as solid lines. The difference between the 80 uc film and 8 uc SL are within error bars, confirming that the 8 uc case is also a good representative of the unperturbed bulk-like system in terms of the superexchange J. The fitted parameters for the 8 uc heterostructure are J8 = 163 ± 6 meV, Jc8 = −52 ± 6 meV and for the 80 uc thick film we obtain J80 = 162 ± 6 meV, Jc80 = −52 ± 6 meV. This is in reasonable agreement with the values for CCO (which shares a similar structure), for which J = 157 meV and Jc = −49 meV were extracted34.

When comparing the absorption measurements (Fig. 2(a)), we find that in the 5 uc SL there is a remanent linear dichroism, although smaller than that of the 8 uc SL. We attribute this to a structure of largely unperturbed Cu-O plaquettes, which is interrupted by a minority of flipped plaquettes. These minority plaquettes act as scattering points for magnons, breaking the antiferromagnetic long-range order, creating finite size effects. This allows us to estimate the average distance between two flipped plaquettes. We take the q-value for which the coherent magnetic peak is about half as intense as for the bulk-like sample, which is about q = 0.26(r.l.u.) = 2π/λ, where λ is the wavelength of the magnon which we take as the minimum coherence length needed. This yields λ = a/0.26 ≈ 4a, i.e. an average distance between flipped plaquettes of 4 lattice constants.

Discussion

The linear dichroism observed in the XAS spectra as well as the magnetic dispersion are clear indications that the bulk-like SLs and the thick film are indeed in a 2D structure. For the thinner films, a contribution of reoriented plaquettes make the structure less obvious. The quenching of spectral weight for the 5 uc film near the Γ point and the overall disappearance of a coherent magnetic excitation for the 3 uc film show that the reorientation is gradual over several thicknesses, which is consistent with the evolution of the c-axis parameter measured in ref. 14.

Our conclusion is that in the 5 uc SL the majority of copper-oxygen plaquettes are still in the bulk-like planar configuration while the minority of the plaquettes are creating scattering points for magnons. Therefore, we conclude that the transfer of spectral weight to higher loss energies for low and intermediate q (which corresponds to long wavelength magnons) is the result of local spin-flip excitations that cannot form coherent magnons, while for large q (i.e. short-wavelength magnons) the finite size effect induced by the flipped plaquettes is less influential. In order to estimate the amount of flipped plaquettes in the 5 uc film, we can estimate an upper boundary by integrating the coherent magnetic spectral weight. We compare the magnetic spectral weight of the 5 uc and 8 uc samles at highest q. Therefore, we can assume that even in the 5 uc sample no incoherent scattering takes place. Under this assumption, the difference in spectral weight is only due to the flipped plaquettes in the 5 uc film and we calculate an upper limit of 8 ± 2% of flipped plaquettes.

This loss of magnetic coherence due to finite size effects is of considerable interest in the context of high-temperature superconductors. For hole-doped cuprates, the doped positive charge has dominantly Zhang-Rice exciton character and is thus mainly located on the oxygen atoms surrounding the Cu ion19,40, while for electron doped cuprates the doped charge is donated by the donor ion directly to the Cu ion, leading to a Cu d10 (i.e. S = 0) impurity41. In a simple approximation, the doped charge in electron-doped cuprates can be seen as an impurity in the otherwise antiferromagnetically correlated Cu ions, comparable to the impurity represented in the present case by the flipped plaquettes.

Previous RIXS experiments on electron cuprates, e.g. Nd2−xCexCuO4 (NCCO) were carried out up to a doping level of x = 0.1842,43. This corresponds to an average distance of impurities of 2/0.18 ≈ 11 Cu sites, which corresponds to a q-value of 0.09(r.l.u.). While this distance is larger by a factor of 2–3 compared to the average distance of impurities in the SCO/STO superlattices investigated here, the paramagnos should be quenched at the corresponding q-value of q = 0.09(r.l.u.) in the electron doped cuprates. However, Fig. 3 of ref. 43 clearly shows they are not. Therefore, we conclude that the scattering mechanism responsible for the quenching of the spectral weight in the present case is inherently different from that found in the superconducting cuprates and implies that the breaking of antiferromagnetic order found in the latter is not static.

In conclusion, we have performed RIXS and XAS at the Copper L3 edge in order to unravel the interplay between local structure and magnetic excitations of SCO layers at the unit cell level in the (SrCuO2)n/(SrTiO3)2 superlattices. We found an antiferromagnetic nearest neighbour superexchange constant of 162 ± 6 meV for the 80 uc film and 163 ± 6 meV for the 8 uc superlattice, very close to the value obtained for infinite layer CCO. We further observed that around the structural reconstruction threshold of 5 uc the majority of plaquettes are still in the bulk like planar structure while a minority is already reoriented. These reoriented plaquettes form scattering points for magnons, due to which magnon spectral weight around the Γ point is significantly reduced. For the 3 uc case, no coherent magnons have been observed. This mechanism of impurity scattering is not present in the comparable case of electron-overdoped cuprate superconductors, thus pointing towards an influence of itinerancy on the interplay of magnetic and electronic properties in the cuprate superconductors. Our findings further emphasise the ability of this class of superlattices to act as an easily modifiable model system of 2-dimensional layered cuprates.

Methods

Experiment

RIXS spetra were taken at the maximum of the Cu L3 edge (931.1 eV), i.e. at the 2p3/2 to 3d resonance. A scattering angle of 130 degree was used for all spectra with incidence angles varying between 5 and 125 degrees with respect to the sample surface. The samples were oriented ex-situ and measured at a pressure of 5 ⋅ 10−10 mbar at a temperature of 10 K. The acquisition time for each spectrum varied between 60 and 180 minutes for different sample geometries. The data was normalized to the full spectral weight of the crystal field excitations. The momentum transfer q is calculated by the projection of the absolute momentum transfer in the two-dimensional or quasi one-dimensional sample orientation, see the sketch in the Supplementary Information Fig. S3.

Linear Spin wave theory

For the extraction of the magnetic exchange parameter J, we used a linear spin wave approach in line with previous work39. The full equation for the linear spin wave theory is

graphic file with name srep32896-m8.jpg

with Aq = J − Jc/2 − (J′ − Jc/4)(1 − νhνk) − J″[1 − (ν2h + ν2k)/2], Bq = (J − Jc/2)(νk + νh)/2 and νx = cos(2πx). Since we are only looking at Γ − X direction, it follows that νh = 1 and since we set J′ = J″ = 0, Eq. 1 reduces to

graphic file with name srep32896-m9.jpg

Zc has been determined to be 1.1838.

Additional Information

How to cite this article: Dantz, M. et al. Quenched Magnon excitations by oxygen sublattice reconstruction in (SrCuO2)n/(SrTiO3)2 superlattices. Sci. Rep. 6, 32896; doi: 10.1038/srep32896 (2016).

Supplementary Material

Supplementary Information
srep32896-s1.pdf (1.9MB, pdf)

Acknowledgments

This research is funded by the Swiss National Science Foundation and its Sinergia network Mott Physics Beyond the Heisenberg (MPBH) model. Experiments have been performed at the ADRESS beamline of the Swiss Light Source at the Paul Scherrer Institut. J.P. and T.S. acknowledge financial support through the Dysenos AG by Kabelwerke Brugg AG Holding, Fachhochschule Nordwestschweiz, and the Paul Scherrer Institut. This research has been partially funded by the Swiss National Science Foundation within the D-A-CH programme (SNSF Research Grant 200021L 141325). V.B. and P.O. acknowledge financial support from the European Communitys Seventh Framework Programme (FP7/2007-2013) under Grant Agreement No. 290605 (PSIFELLOW/COFUND).

Footnotes

Author Contributions M.D., J.P., V.B., Y.H., P.O.V., V.N.S and T.S. carried out the measurements, D.S. and G.K. produced the samples, T.S. and G.K. conceived the project and M.D. and T.S. wrote the paper; all authors were involved in the discussion and preparation of the manuscript.

References

  1. Comin R. et al. Broken translational and rotational symmetry via charge stripe order in underdoped YBa2cu3o6+y. Science 347, 1335–1339 (2015). [DOI] [PubMed] [Google Scholar]
  2. Ghiringhelli G. et al. Long-Range Incommensurate Charge Fluctuations in (Y, Nd)Ba2cu3o6+x. Science 337, 821–825 (2012). [DOI] [PubMed] [Google Scholar]
  3. Abbamonte P. et al. Spatially modulated ‘Mottness’ in La2-xBaxCuO4. Nat Phys 1, 155–158 (2005). [Google Scholar]
  4. Parker C. V. et al. Fluctuating stripes at the onset of the pseudogap in the high-Tc superconductor Bi2sr2cacu2o8+x. Nature 468, 677–680 (2010). [DOI] [PubMed] [Google Scholar]
  5. Li Q., Hücker M., Gu G. D., Tsvelik A. M. & Tranquada J. M. Two-Dimensional Superconducting Fluctuations in Stripe-Ordered La1.875ba0.125cuo4. Phys. Rev. Lett. 99, 067001 (2007). [DOI] [PubMed] [Google Scholar]
  6. Chang J. et al. Direct observation of competition between superconductivity and charge density wave order in YBa2cu3o6.67. Nat Phys 8, 871–876 (2012). [Google Scholar]
  7. Campi G. et al. Inhomogeneity of charge-density-wave order and quenched disorder in a high-Tc superconductor. Nature 525, 359–362 (2015). [DOI] [PubMed] [Google Scholar]
  8. Dean M. P. M. et al. Magnetic excitations in stripe-ordered La1.875ba0.125cuo4 studied using resonant inelastic x-ray scattering. Phys. Rev. B 88, 020403 (2013). [Google Scholar]
  9. Dean M. P. M. et al. Spin excitations in a single La2cuo4 layer. Nat Mater 11, 850–854 (2012). [DOI] [PubMed] [Google Scholar]
  10. Samal D. & Koster G. Manipulating oxygen sublattice in ultrathin cuprates: A new direction to engineer oxides. Journal of Materials Research 30, 463–476 (2015). [Google Scholar]
  11. Mannhart J. & Schlom D. G. Oxide Interfaces? An Opportunity for Electronics. Science 327, 1607–1611 (2010). [DOI] [PubMed] [Google Scholar]
  12. Zubko P., Gariglio S., Gabay M., Ghosez P. & Triscone J.-M. Interface Physics in Complex Oxide Heterostructures. Annual Review of Condensed Matter Physics 2, 141–165 (2011). [Google Scholar]
  13. Zhong Z., Koster G. & Kelly P. J. Prediction of thickness limits of ideal polar ultrathin films. Phys. Rev. B 85, 121411 (2012). [Google Scholar]
  14. Samal D. et al. Experimental Evidence for Oxygen Sublattice Control in Polar Infinite Layer SrCuO2. Phys. Rev. Lett. 111, 096102 (2013). [DOI] [PubMed] [Google Scholar]
  15. Kuiper B. et al. Control of oxygen sublattice structure in ultra-thin SrCuO2 films studied by X-ray photoelectron diffraction. APL Materials 1, 042113 (2013). [Google Scholar]
  16. Le Tacon M. et al. Intense paramagnon excitations in a large family of high-temperature superconductors. Nat Phys 7, 725–730 (2011). [Google Scholar]
  17. Dean M. P. M. et al. Persistence of magnetic excitations in La2-xSrxCuO4 from the undoped insulator to the heavily overdoped non-superconducting metal. Nat Mater advance online publication (2013). [DOI] [PubMed] [Google Scholar]
  18. Lipscombe O. J., Hayden S. M., Vignolle B., McMorrow D. F. & Perring T. G. Persistence of high-frequency spin fluctuations in overdoped superconducting La2-xSrxCuO4 (x = 0.22). Phys. Rev. Lett. 99, 067002 (2007). [DOI] [PubMed] [Google Scholar]
  19. Monney C. et al. Determining the short-range spin correlations in the spin-chain Li2cuo2 and CuGeO3 compounds using resonant inelastic x-ray scattering. Phys. Rev. Lett. 110, 087403 (2013). [DOI] [PubMed] [Google Scholar]
  20. Schlappa J. et al. Collective Magnetic Excitations in the Spin Ladder Sr14cu24o41 Measured Using High-Resolution Resonant Inelastic X-Ray Scattering. Physical Review Letters 103 (2009). [DOI] [PubMed] [Google Scholar]
  21. Lee W. S. et al. Role of Lattice Coupling in Establishing Electronic and Magnetic Properties in Quasi-One-Dimensional Cuprates. Phys. Rev. Lett. 110, 265502 (2013). [DOI] [PubMed] [Google Scholar]
  22. Schlappa J. et al. Spin-orbital separation in the quasi-one-dimensional Mott insulator Sr2cuo3. Nature 485, 82–85 (2012). [DOI] [PubMed] [Google Scholar]
  23. Sala M. M. et al. Energy and symmetry of dd excitations in undoped layered cuprates measured by Cu L3 resonant inelastic x-ray scattering. New J. Phys. 13, 043026 (2011). [Google Scholar]
  24. Bisogni V. et al. Orbital Control of Effective Dimensionality: From Spin-Orbital Fractionalization to Confinement in the Anisotropic Ladder System CaCu2o3. Phys. Rev. Lett. 114, 096402 (2015). [DOI] [PubMed] [Google Scholar]
  25. Dean M. P. M. et al. High-Energy Magnetic Excitations in the Cuprate Superconductor Bi2sr2cacu2o8+delta: Towards a Unified Description of Its Electronic and Magnetic Degrees of Freedom. Phys. Rev. Lett. 110, 147001 (2013). [DOI] [PubMed] [Google Scholar]
  26. Zhou K.-J. et al. Persistent high-energy spin excitations in iron-pnictide superconductors. Nat Commun 4, 1470 (2013). [DOI] [PubMed] [Google Scholar]
  27. Guarise M. et al. Anisotropic softening of magnetic excitations along the nodal direction in superconducting cuprates. Nat Commun 5 (2014). [DOI] [PubMed] [Google Scholar]
  28. Strocov V. N. et al. High-resolution soft X-ray beamline ADRESS at the Swiss Light Source for resonant inelastic X-ray scattering and angle-resolved photoelectron spectroscopies. J Synchrotron Radiat 17, 631–643 (2010). [DOI] [PMC free article] [PubMed] [Google Scholar]
  29. Ghiringhelli G. et al. SAXES, a high resolution spectrometer for resonant x-ray emission in the 400?1600ev energy range. Review of Scientific Instruments 77, 113108 (2006). [Google Scholar]
  30. Zaliznyak I. A. et al. Spinons in the Strongly Correlated Copper Oxide Chains in SrCuuO2. Phys. Rev. Lett. 93, 087202 (2004). [DOI] [PubMed] [Google Scholar]
  31. Walters A. C. et al. Effect of covalent bonding on magnetism and the missing neutron intensity in copper oxide compounds. Nat Phys 5, 867–872 (2009). [Google Scholar]
  32. Takano M., Takeda Y., Okada H., Miyamoto M. & Kusaka T. ACuO2 (A: alkaline earth) crystallizing in a layered structure. Physica C: Superconductivity 159, 375–378 (1989). [Google Scholar]
  33. Hyatt N. C., Gray L., Gameson I., Edwards P. P. & Hull S. High-pressure neutron diffraction study of the quasi-one-dimensional cuprate Sr2cuo3. Phys. Rev. B 70, 214101 (2004). [Google Scholar]
  34. Minola M. et al. Magnetic and ligand field properties of copper at the interfaces of (CaCuO2)n/(SrTiO3)n superlattices. Phys. Rev. B 85, 235138 (2012). [Google Scholar]
  35. Ament L. J. P., Ghiringhelli G., Sala M. M., Braicovich L. & van den Brink J. Theoretical Demonstration of How the Dispersion of Magnetic Excitations in Cuprate Compounds can be Determined Using Resonant Inelastic X-Ray Scattering. Phys. Rev. Lett. 103, 117003 (2009). [DOI] [PubMed] [Google Scholar]
  36. Braicovich L. et al. Magnetic Excitations and Phase Separation in the Underdoped La2-xSrCuO4 Superconductor Measured by Resonant Inelastic X-Ray Scattering. Physical Review Letters 104 (2010). [DOI] [PubMed] [Google Scholar]
  37. Braicovich L. et al. Dispersion of Magnetic Excitations in the Cuprate La2cuo4 and CaCuO2 Compounds Measured Using Resonant X-Ray Scattering. Phys. Rev. Lett. 102, 167401 (2009). [DOI] [PubMed] [Google Scholar]
  38. Coldea R. et al. Spin waves and electronic interactions in La2cuo4 (2001). [DOI] [PubMed]
  39. Headings N. S., Hayden S. M., Coldea R. & Perring T. G. Anomalous High-Energy Spin Excitations in the High-${T}_{c}$ Superconductor-Parent Antiferromagnet La2cuo4. Phys. Rev. Lett. 105, 247001 (2010). [DOI] [PubMed] [Google Scholar]
  40. Zhang F. & Rice T. Effective Hamiltonian for the superconducting Cu oxides. Physical Review B 37, 3759–3761 (1988). [DOI] [PubMed] [Google Scholar]
  41. Armitage N. P., Fournier P. & Greene R. L. Progress and perspectives on electron-doped cuprates. Rev. Mod. Phys. 82, 2421–2487 (2010). [Google Scholar]
  42. Lee W. S. et al. Asymmetry of collective excitations in electron- and hole-doped cuprate superconductors. Nat Phys 10, 883–889 (2014). [Google Scholar]
  43. Ishii K. et al. High-energy spin and charge excitations in electron-doped copper oxide superconductors. Nat Commun 5 (2014). [DOI] [PubMed] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Supplementary Materials

Supplementary Information
srep32896-s1.pdf (1.9MB, pdf)