Localized Surface Plasmon Resonance Dependence on Misaligned Truncated Ag Nanoprism Dimer

Hanning Yang 1,2,3, Edgar Oduor Owiti 1,2,3, Xiangqian Jiang 1,2,3, Siren Li 1,2,3, Peng Liu 1,2,3, Xiudong Sun 1,2,3,4,✉
PMCID: PMC5493601  PMID: 28673049

Abstract

Misaligned edge-to-edge dimers are the common products during the preparation of Ag nanoprism dimers using self-assembly method. However, in the self-assembly method, Ag nanoprisms are easily truncated because they are easy to oxidize in an acidic environment. In this work, modeling a truncated Ag nanoprism on a misaligned edge-to-edge dimer provides a better understanding of the effects of the truncation and misalignment on localized surface plasmon resonance (LSPR) of the dimer. The resonant wavelength and intensity of the dimer are flexibly modulated by changing the misalignment length of the dimer. As the misalignment length increases, a stronger peak at the shorter wavelength and a weaker one at the longer wavelength are observed. The resonant wavelengths and intensities of the two peaks are also flexibly tuned by adjusting the truncated length of the Ag nanoprism in the dimer. The results are numerically demonstrated based on the finite element method (FEM) and show promising potential for nanoswitch, multi-channel tunable biosensor and other nanodevice applications.

Keywords: LSPR, Misalignment, Truncation, Ag Nanoprism dimer

Background

Silver and gold nanoparticles have attracted extensive attentions due to their unique optical properties which originate from their localized surface plasmon resonance (LSPR) effects. The conduction electrons in these nanoparticles collectively oscillate with the incident light causing an enhanced electric field that is localized around the surface of the nanoparticle [1, 2]. The LSPR effect of nanoparticles can be modulated by changing the nanoparticle’s size, shape, material, and the surrounding environment [3–5]. Among the numerous nanoparticles, nanoprisms (NPs) have attracted the most attention due to their anisotropic geometrical properties and tunable LSPR properties [6–8]. Because of the anisotropic geometrical properties, oscillating charges on the surface tend to accumulate around the NP’s tips making the localized electric field around NP more enhanced than in isotropic nanoparticles [9]. The LSPR properties of NP are usually divided into in-plane dipolar resonance, in-plane quadrupolar resonance, and out-of-plane dipolar resonance. The in-plane dipolar resonance shows a redshift effect with increasing the edge length of NP [10, 11].

As two nanoparticles are brought close to each other, the enhanced electric field concentrates in the gap of the dimer. This phenomenon is known as hot spot effect which originates from the LSPR coupling effect between the nanoparticles. The dimers with remarkable hot spot effects can be easily prepared by e-beam lithography [12], nanosphere lithography [13], and self-assembly method [14, 15]. For the self-assembly method, metal nanoparticles with specific geometries are linked through the molecules with particular groups. Therefore, the gap in the dimer is as narrow as the molecular chain length. This further reduces the gap between two nanoparticles and causes a more remarkable hot spot effect [16–18].

The hot spot effect of the NP dimer as a typical dimer has been extensively studied, but most studies about the NP dimers concentrate on the tip-to-tip geometry [19–23]. However, during preparation process of the tip-to-tip dimer through the self-assembly method, there is a wide existence of NP dimers with edge-to-edge geometries [15]. The self-assembly method often causes a randomly misaligned effect for the NP dimers. The randomly misaligned edge-to-edge Au NP dimers with the broken symmetry can induce a novel optical property [24]. This result indicates that the double resonances can be switched by modulating the misalignment length of the dimer. The resonant positions can be tuned by changing the gap length and the thickness of Au NP. Due to the sensitivity of optical properties on the structural parameters, this finding paves a promising way for developing nanoswitches, nanomotors, nanorulers, and dual-channel biosensors. However, because of the inertia of the gold atom, the structural parameters of Au NP dimers are usually fixed once they are prepared.

Because Ag is easily oxidized, the tips of the Ag NP can be easily etched in the process of its preparation. This results to Ag NP transforming into an Ag truncated nanoprism (TNP). The change of the structural symmetry originating from the truncation effect induces some novel optical properties [8, 25]. The truncation effect can be introduced in the misaligned edge-to-edge Ag NP dimer to obtain a tunable device with novel optical properties. Here, effects of the truncation and misalignment on the LSPR edge-to-edge Ag TNP dimers are studied using FEM.

Methods

Structural Model of Misaligned Truncated Ag Nanoprism Dimer

The structural model used in the calculations is shown in Fig. 1. Ag NPs used in the self-assembly method are usually prepared by the seed-induced growth method: its edge length is flexibly modulated by controlling the reaction conditions and keeping the thickness constant [26]. In this paper, the thickness of Ag NP is kept constant at T = 8 nm. The Ag NP edge-to-edge dimers are assumed to be prepared by the self-assembly method; therefore, the gap length in this dimer (G) has a specific molecular length G = 2 nm.

Fig. 1.

Fig. 1

Open in a new tab

Schematic diagram of the Ag TNP dimer showing a specific misalignment length l 1

The misaligned edge-to-edge dimer consists of two identical Ag TNPs with the following dimensions, edge length (L), misalignment length (l 1), and truncated length (l 2). The tips of Ag NP are cut off along a straight line with the initial edge length L = 130 nm and truncated length l 2 = 10 nm. To study the effect of the misalignment, a misalignment ratio R = l 1/L of Ag TNP dimer is varied from 0 to 1.5. As R approached 0 or 1, the Ag TNP dimers with the increased truncated length were modeled to study the influence of the truncation effect. Ag TNP transforms to a hexagonal nanoplate (HNP), as the edge length of Ag HNP (L 1) is equal to the truncated length l 2 = L/3. To further investigate the effect of the truncation and misalignment, Ag HNP dimers with the misalignment ratio R 1 = l 1/L 1, ranging from 0 to 3, were simulated.

Finite Element Method for Misaligned Truncated Ag Nanoprism Dimer

FEM method using COMSOL Multiphysics is used to investigate the effect of misalignment length on the LSPR edge-to-edge Ag TNP dimer. The relative permittivity for Ag was obtained from the Drude model, ε(ω) = ε ∞ − ω p 2/[ω(ω + iγ)], where ε ∞ = 3.7 is the infinite frequency, ω p = 1.38 × 1016 is the bulk plasma frequency, and γ = 3.72 × 1013 is the oscillation damping of electrons [27].

The Ag TNP dimer was modeled on the x-y plane at z = 0 with air (n = 1) surrounding it. Using air around the dimer was done to simplify the computation process. The incident light, polarized along the y-axis, was directed normally along z-axis on the Ag TNP surface. Tuning of the wavelength was done between λ = 600 nm to λ = 1100 nm with a step of 4 nm.

Results and Discussion

The extinction cross-section (ECS) intensity distribution map of the Ag TNP dimer showing variation between the wavelength and R was firstly calculated to investigate effect of the misalignment length on the LSPR. Figure 2 shows the ECS intensity distribution color map of the Ag TNP dimer. As shown in Fig. 2, the Ag TNP dimer with R = 0 displays two peaks with equal intensities. When R is equal to 1, the shorter wavelength peak, labeled as peak 1, is strong and shows a blueshift effect. For the longer wavelength, labeled as peak 2, the intensity decreases and shows a blueshift effect. As R is increased from 0 to 1, the resonant wavelength of peak 1 initially decreases and then slightly stabilizes. Meanwhile, its intensity gradually increases. It is worth noting that peak 1 decreases abruptly when R changes from 0 to 1/8. This is because the disappearance of the higher-order LSPR mode. The resonant wavelength of peak 2 first increases and then decreases, but its intensity decreases throughout.

Fig. 2.

Fig. 2

Open in a new tab

ECS spectra of Ag TNP dimers. a ECS intensity distribution map as functions of R and wavelength. b ECS resonant wavelength (the dark scatter line) and intensity (the red short dotted line) spectra versus R. The square and triangle lines show peak 1 and peak 2, respectively

Peak 1 in Fig. 2a strengthens further as R increases from 1 to 1.5 and its resonant wavelength is kept unchanged. Moreover, peak 2 continuously decreases until it disappears while its resonant wavelength decreases throughout. As R reaches 1.5, the double peaks degenerate into a single peak with a resonant wavelength equal to that of the Ag TNP monomer. When R is large than 1, the LSPR coupling interaction between Ag TNPs is extremely weak. In Fig. 2b, peak 2 plays the dominant role in ECS spectrum when R < 0.5 (the blue region) whereas peak 1 dominates when R > 0.5 (the yellow region). Therefore, the two peaks can be switched on or off by modulating the misalignment length of the dimer.

The electric field distributions of Ag TNP dimers for different values of R are shown in Fig. 3. The geometrical configuration of the Ag TNP dimer changes as R varies from 0 to 1.5. When R is equal to 0, the Ag TNP dimer possesses the edge-to-edge geometry. As R reaches to 1, the configuration changes into the tip-to-tip geometry, and as R increases further, the configuration turns an abnormal tip-to-tip geometry. In Fig. 3a, the enhanced electric fields are localized at the center and two ends of the gap, so for R = 0, peak 1 is a higher-order LSPR mode. When R is larger than 0, the higher-order LSPR mode disappears and the structural symmetry of the dimer is broken. Then peak 1 can be attributed to the antisymmetric mode from the LSPR coupling interaction between Ag truncated nanoprisms in the dimer shown in Fig. 3b–d. The electric fields mainly distribute around the lateral tips away from the gap in the Ag TNP dimer. When R is large enough, the electric field distributions of Ag TNPs in the dimer are similar to that of the Ag TNP monomer as shown in Fig. 3h. Figure 3e–g show that peak 2 can be attributed to the symmetric mode from the LSPR coupling interaction between Ag truncated nanoprisms in the dimer. The enhanced electric fields are mainly localized in the gaps. The results show that the two peaks can be turned on or off by modulating the LSPR coupling interaction between Ag TNPs in the dimer. When R is equal to 0, Ag TNP dimers for the two peaks possess huge enhanced electric fields (above 900 V/m) in the gap. The enhancement effect of the surrounding electric field of the Ag TNP dimers weakens as R increases. This means that the misalignment effect will weaken the hot spot effect of Ag TNP dimer, if R increases and the enhanced electric field distribution will shift from the gap to the lateral tips of Ag TNP in the dimer.

Fig. 3.

Fig. 3

Open in a new tab

Calculated electric field distributions of Ag TNP dimers and monomer. Images are taken as the cross-section of the Ag TNP dimer at z = 0 on the x-y plane. Panels a–g correspond to the points A–G marked in Fig. 2a. Peak 1: a R = 0; b R = 0.5, B; c R = 1; d R = 1.5. Peak 2: e R =0, f R = 0.5, g R = 1. h Monomer

To investigate the effect of the truncation on the switching, the truncated length-dependent ECS resonant wavelength and intensity spectra of the Ag TNP dimers are simulated and shown in Fig. 4 (for R = 0, 1). When the truncated length l 2 is 43.3 nm and L = 130 nm, Ag TNP turns into Ag HNP. As shown in Fig. 4a, peak 1 abruptly decreases from the initial strong state and then stabilizes in a weak state as l 2 is increased when R = 0. This is because the higher-order LSPR mode corresponding to peak 1 at the same R value no longer exists in the gap as the gap length decreases (i.e., as l 2 increases). The origin of peak 1 changes from the higher-order LSPR mode to the antisymmetric mode of the LSPR coupling interaction as the truncated length increases. When R equals to 0 or 1 as shown in Fig. 4, the resonant wavelengths of the two peaks decrease throughout. As shown in Fig. 4b, peak 2 gradually fades as l 2 increases to a specific value, the double peaks degenerate to a single peak. Similarly, this is due to the symmetric mode from the LSPR coupling interaction weakening as the interval between the two Ag TNPs increases (i.e., as l 2 increases). This means that the switching effect of the Ag TNP dimer can be flexibly modulated by changing the truncated length originating from the easy-to-oxidize features of Ag.

Fig. 4.

Fig. 4

Open in a new tab

ECS spectra of Ag TNP dimers with l 2 changing from 0 to 43.3 nm. a R = 0; b R = 1. The dark scatter and red short dot lines show the resonant wavelength and intensity spectra, respectively. The square and triangle lines show peak 1 and peak 2, respectively

When the truncated length increases to a critical value, Ag TNP in the dimer transforms into Ag HNP. The edge length of Ag HNP L 1 is 43.3 nm. Figure 5 shows the ECS intensity distribution map of Ag HNP dimers versus R 1 and wavelength. Here, the wavelength of the incident light ranges from 500 to 900 nm. For the Ag HNP edge-to-edge dimer, a change of the misalignment length (l 1) also causes the variations of two peaks in its ECS spectrum. With increasing the misalignment ratio R 1 = l 1/L 1, the switching effect of the Ag HNP edge-to-edge dimer is more remarkable than the Ag TNP dimer. Peak 2 originating from the symmetric mode of the LSPR coupling interaction quickly fades in the ECS spectrum with the two Ag HNPs moving away from each other (R 1 > 1) as shown in Fig. 5. Peak 1 originates from the antisymmetric mode from the LSPR coupling interaction between Ag HNPs and gradually occupies the dominant role. The intensity ratio of peak 2 to peak 1 for the Ag HNP dimer is obviously larger than that of the Ag TNP dimer. Compared with the ECS spectrum of the Ag TNP dimer, the Ag HNP dimer possesses a single peak configuration which also can be switched by changing the misalignment length. This is further evidence that Ag NP edge-to-edge dimers with different truncated length possess a misalignment-related switching effect.

Fig. 5.

Fig. 5

Open in a new tab

ECS spectra of the Ag HNP dimer. a ECS intensity distribution map versus R 1 and wavelength. b Resonant wavelength spectra of the two peaks

Conclusions

In summary, the LSPR effects of Ag TNP misaligned edge-to-edge dimers have been studied using FEM. The ECS spectrum of Ag TNP dimer possesses two peaks, which can be switched on or off by modulating the misalignment length. When R is less than 0.5, the longer wavelength peak plays the prominent role in the ECS spectrum. As R grows larger than 0.5, the shorter wavelength peak occupies the dominant role. Due to the truncation effect, the resonant wavelengths of the two peaks can be flexibly modulated by changing the truncated length. When the truncated length increases to a specific value, Ag TNP transforms into Ag HNP. The double peaks degenerate to a single peak, and the peaks of the Ag HNP dimer also can be switched by changing the misalignment length. The calculated results indicate that Ag TNP misaligned edge-to-edge dimers pave the way for a promising surface-enhanced Raman spectrum, nanoswitch, multi-channel tunable biosensor, other nanodevices, etc.

Acknowledgments

Funding

This study is financially supported by the National Natural Science Foundation of China (No. 11374074, 61308069) and the National Basic Research Program of China (No. 2013CB328702).

Authors’ Contributions

HYA, XJ, and XS conceived the idea. HYA, EO, PL, and XS calculated the results and made the conclusions. HYA, EO, and SL contributed to the preparation and revision of the manuscript. All the authors read and approved the final manuscript.

Competing Interests

The authors declare that they have no competing interests.

Publisher’s Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Abbreviations

ECS

Extinction cross-section

FEM

Finite element method

G

Gap length

HNP

Hexagonal nanoplate

L

Edge length

l1

Misalignment length

l2

Truncated length

LSPR

Localized surface plasmon resonance

NP

Nanoprism

R

Misalignment ratio

T

Thickness

TNP

Truncated nanoprism

Contributor Information

Hanning Yang, Email: hnyang@hit.edu.cn.

Edgar Oduor Owiti, Email: eowiti@hit.edu.cn.

Xiangqian Jiang, Email: xqjiang@hit.edu.cn.

Siren Li, Email: sirenli@hit.edu.cn.

Peng Liu, Email: 420945069@qq.com.

Xiudong Sun, Email: xdsun@hit.edu.cn.

References

  • 1.Nien L-W, Lin S-C, Chao B-K, Chen M-J, Li J-H, Hsueh C-H. Giant electric field enhancement and localized surface plasmon resonance by optimizing contour bowtie nanoantennas. J Phys Chem C. 2013;117(47):25004–25011. doi: 10.1021/jp408610q. [DOI] [Google Scholar]
  • 2.Liu Y, Huang CZ. Screening sensitive nanosensors via the investigation of shape-dependent localized surface plasmon resonance of single Ag nanoparticles. Nanoscale. 2013;5(16):7458–7466. doi: 10.1039/c3nr01952g. [DOI] [PubMed] [Google Scholar]
  • 3.Liu Y, Song F, Zhang J, Lv Z, Liu J, Yu Y, Zhao H, Wang H. Tunable local surface plasmon resonance in liquid-crystal-coated Ag nanoparticles. Phys Lett A. 2013;377(16–17):1199–1204. doi: 10.1016/j.physleta.2013.03.017. [DOI] [Google Scholar]
  • 4.Le Thi Ngoc L, Jin M, Wiedemair J, van den Berg A, Carlen ET. Large area metal nanowire arrays with tunable sub-20 nm nanogaps. ACS Nano. 2013;7(6):5223–5234. doi: 10.1021/nn4009559. [DOI] [PubMed] [Google Scholar]
  • 5.Personick ML, Langille MR, Zhang J, Wu J, Li S, Mirkin CA. Plasmon-mediated synthesis of silver cubes with unusual twinning structures using short wavelength excitation. Small. 2013;9(11):1947–1953. doi: 10.1002/smll.201202451. [DOI] [PubMed] [Google Scholar]
  • 6.Millstone JE, Hurst SJ, Metraux GS, Cutler JI, Mirkin CA. Colloidal gold and silver triangular nanoprisms. Small. 2009;5(6):646–664. doi: 10.1002/smll.200801480. [DOI] [PubMed] [Google Scholar]
  • 7.Shuford KL, Ratner MA, Schatz GC. Multipolar excitation in triangular nanoprisms. J Chem Phys. 2005;123(11):114713. doi: 10.1063/1.2046633. [DOI] [PubMed] [Google Scholar]
  • 8.Jin R, Cao Y, Mirkin CA, Kelly KL, Schatz GC, Zheng JG. Photoinduced conversion of silver nanospheres to nanoprisms. Science. 2001;294:1091–1093. doi: 10.1126/science.1064539. [DOI] [PubMed] [Google Scholar]
  • 9.Aherne D, Ledwith DM, Gara M, Kelly JM. Optical properties and growth aspects of silver nanoprisms produced by a highly reproducible and rapid synthesis at room temperature. Adv Funct Mater. 2008;18(14):2005–2016. doi: 10.1002/adfm.200800233. [DOI] [Google Scholar]
  • 10.Yang P, Portalès H, Pileni M-P. Identification of multipolar surface plasmon resonances in triangular silver nanoprisms with very high aspect ratios ysing the DDA method. J Phys Chem C. 2009;113(27):11597–11604. doi: 10.1021/jp901248e. [DOI] [Google Scholar]
  • 11.Hermoso W, Alves TV, de Oliveira CCS, Moriya EG, Ornellas FR, Camargo PHC. Triangular metal nanoprisms of Ag, Au, and Cu: modeling the influence of size, composition, and excitation wavelength on the optical properties. Chem Phys. 2013;423:142–150. doi: 10.1016/j.chemphys.2013.07.008. [DOI] [Google Scholar]
  • 12.Kim S, Jin J, Kim YJ, Park IY, Kim Y, Kim SW. High-harmonic generation by resonant plasmon field enhancement. Nature. 2008;453(7196):757–760. doi: 10.1038/nature07012. [DOI] [PubMed] [Google Scholar]
  • 13.Haynes CL, Van Duyne RP. Nanosphere lithography: a versatile nanofabrication tool for studies of size-dependent nanoparticle optics. J Phys Chem B. 2001;105(24):5599–5611. doi: 10.1021/jp010657m. [DOI] [Google Scholar]
  • 14.Gao B, Arya G, Tao AR. Self-orienting nanocubes for the assembly of plasmonic nanojunctions. Nat Nanotechnol. 2012;7(7):433–437. doi: 10.1038/nnano.2012.83. [DOI] [PubMed] [Google Scholar]
  • 15.Gao B, Alvi Y, Rosen D, Lav M, Tao AR. Designer nanojunctions: orienting shaped nanoparticles within polymer thin-film nanocomposites. Chem Commun. 2013;49(39):4382–4384. doi: 10.1039/C2CC37158H. [DOI] [PubMed] [Google Scholar]
  • 16.Li W, Camargo PH, Au L, Zhang Q, Rycenga M, Xia Y. Etching and dimerization: a simple and versatile route to dimers of silver nanospheres with a range of sizes. Angew Chem. 2010;49(1):164–168. doi: 10.1002/anie.200905245. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 17.Kessentini S, Barchiesi D, D’Andrea C, Toma A, Guillot N, Di Fabrizio E, Fazio B, Maragó OM, Gucciardi PG, Lamy de la Chapelle M. Gold dimer nanoantenna with slanted gap for tunable LSPR and improved SERS. J Phys Chem C. 2014;118(6):3209–3219. doi: 10.1021/jp409844y. [DOI] [Google Scholar]
  • 18.Ci X, Wu B, Song M, Liu Y, Chen G, Wu E, Zeng H. Tunable Fano resonances in heterogenous Al-Ag nanorod dimers. Appl Phys A. 2014;117(2):955–960. doi: 10.1007/s00339-014-8479-z. [DOI] [Google Scholar]
  • 19.Lin T-R, Chang S-W, Chuang SL, Zhang Z, Schuck PJ. Coating effect on optical resonance of plasmonic nanobowtie antenna. Appl Phys Lett. 2010;97(6):063106. doi: 10.1063/1.3478228. [DOI] [Google Scholar]
  • 20.Grzeskiewicz B, Ptaszynski K, Kotkowiak M. Near and far-field properties of nanoprisms with rounded edges. Plasmonics. 2014;9:607–614. doi: 10.1007/s11468-014-9671-x. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 21.Guo H, Meyrath TP, Zentgraf T, Liu N, Fu L, Schweizer H, Giessen H. Optical resonances of bowtie slot antennas and their geometry and material dependence. Opt Express. 2008;16(11):7756–7766. doi: 10.1364/OE.16.007756. [DOI] [PubMed] [Google Scholar]
  • 22.Hatab NA, Hsueh CH, Gaddis AL, Retterer ST, Li JH, Eres G, Zhang Z, Gu B. Free-standing optical gold bowtie nanoantenna with variable gap size for enhanced Raman spectroscopy. Nano Lett. 2010;10(12):4952–4955. doi: 10.1021/nl102963g. [DOI] [PubMed] [Google Scholar]
  • 23.Rosen DA, Tao AR. Modeling the optical properties of bowtie antenna generated by self-assembled Ag triangular nanoprisms. ACS Appl Mater Interfaces. 2014;6(6):4134–4142. doi: 10.1021/am4057612. [DOI] [PubMed] [Google Scholar]
  • 24.Zhang C-H, Zhu J, Li J-J, Zhao J-W. Misalign-dependent double plasmon modes “switch” of gold triangular nanoplate dimers. J Appl Phys. 2015;117(6):063102. doi: 10.1063/1.4907869. [DOI] [Google Scholar]
  • 25.Fischer H, Martin OJF. Engineering the optical response of plasmonic nanoantennas. Opt Express. 2008;16(12):9144–9154. doi: 10.1364/OE.16.009144. [DOI] [PubMed] [Google Scholar]
  • 26.Goebl J, Zhang Q, He L, Yin Y. Monitoring the shape evolution of silver nanoplates: a marker study. Angew Chem. 2012;51(2):552–555. doi: 10.1002/anie.201107240. [DOI] [PubMed] [Google Scholar]
  • 27.Park J, Kim H, Lee B. High order plasmonic Bragg reflection in the metal-insulator-metal waveguide Bragg grating. Opt Express. 2008;16(1):413–425. doi: 10.1364/OE.16.000413. [DOI] [PubMed] [Google Scholar]