Exceptional CO₂ working capacity in a heterodiamine-grafted metal–organic framework

The amine functionalized material 1-dmen shows a record high working capacity for CO₂ capture at low regeneration temperatures compared with other MOFs. Furthermore, this performance is maintained upon exposure to humidity.

Abstract

An amine-functionalized metal–organic framework (MOF), dmen-Mg₂(dobpdc) (dmen = N,N-dimethylethylenediamine), which contains a heterodiamine with both primary and tertiary amines, was prepared via a post-synthetic method. This material exhibits a significant selectivity factor for CO₂ over N₂ that is commensurate with top-performing MOFs. It is remarkable that the solid is fully regenerated under vacuum or flowing Ar at low desorption temperatures, and following this can take up CO₂ at more than 13 wt%. An exceptionally high working capacity is achieved at low regeneration temperatures and after exposure to humid conditions, which are important parameters for a real post-combustion CO₂ capture process.

Introduction

Carbon capture and sequestration (CCS) has been investigated to mitigate atmospheric CO₂ concentrations and to address global environmental concerns. ^1–5 To capture CO₂ selectively from power plant flue gas, aqueous alkanolamine solutions have been intensively investigated. However, these amine solutions require an enormous energy input (∼30% of the produced power) to regenerate the solvents.⁶ This energy penalty that arises from heating the water of the amine solutions makes solid adsorbents with low heat capacities, and other prospective alternatives, advantageous.⁷ Thus, one of the current research topics in the field of developing innovative materials for post-combustion CO₂ capture is the reduction of the regeneration energy of the capture media.

To evaluate the actual amount of CO₂ captured during adsorption and desorption cycles in a practical post-combustion process, it is critically important to determine the working, rather than the absolute, CO₂ capacity. The estimated working capacity of porous materials such as porous polymer networks (PPNs) ^8–11 and monoethanolamine (MEA) ^1,12 gradually decreases with lower desorption temperatures, based on a simplified model using CO₂ isotherms (the difference between the adsorbed quantities at 0.15 bar CO₂ and 40 °C, and at 1 bar CO₂ and different desorption temperatures). ^9,13 The working capacities of the aforementioned materials become negligible at lower desorption temperatures; however, the regeneration temperature of the capture materials should be minimized to improve upon the high energy penalty of the current amine scrubbers.

Metal–organic frameworks (MOFs) with tunable pore shapes and other properties have been investigated for CO₂ capture. ^14–23 Of these MOFs, the MOF-74 series exhibits a high density of exposed Lewis acidic metal sites aligned along the pore walls. ^24–27 The coordinatively unsaturated sites cause strong interactions with CO₂ due to their large quadrupole moments and their polarizability.²⁸ For instance, an exceptionally high CO₂ capacity of 20.6 wt% under relevant post-combustion flue gas conditions was observed for Mg–MOF-74.¹³ However, in a breakthrough experiment, after exposure to 70% relative humidity (RH) and subsequent regeneration at high temperature, Mg–MOF-74 showed only about 16% recovery of its initial amount of CO₂.²⁹

Improving CO₂ capacities at lower CO₂ partial pressures has also been achieved by decorating the open metal sites of MOFs with diamines. ^1,30–35 In this case, homodiamines were selected to modify the interior of the pores of the MOF such that one amine was grafted onto an open metal site while the other remained uncoordinated. Amine-functionalized MOFs reveal outstanding CO₂ capacities at low CO₂ concentrations because the free amine groups located toward the pore centers can strongly couple to CO₂. ^36–40 In particular, Mg₂(dobpdc) (H₄dobpdc = 4,4′-dihydroxy-(1,1′-biphenyl)-3,3′-dicarboxylic acid) grafted with primary en (= ethylenediamine) and secondary mmen (= N,N′-dimethylethylenediamine) ligands, an extended version of Mg–MOF-74, showed a better CO₂ capacity, even upon exposure to water vapor when reactivated under a flow of pure Ar.⁴¹ In general, amine functionalization allows for the chemisorption of CO₂ onto the free amine groups when primary or secondary diamines are introduced. Therefore, the working capacity of amine-grafted MOFs with chemisorbed CO₂ is expected to be low if the regeneration temperature is not sufficiently high. This presents a substantial challenge to identify a promising adsorbent that can maintain a high working capacity even at low desorption temperatures.

Herein, we report the synthesis and sorption properties of N,N-dimethylethylenediamine (dmen)-functionalized Mg₂(dobpdc) (1-dmen), constructed by grafting the open metal sites of Mg₂(dobpdc) (1) with dmen, composed of primary and tertiary amines. In addition to having an exceptionally high selectivity for CO₂ over N₂, this framework exhibits a record high working capacity at low regeneration temperatures among MOFs; this is a critical metric in determining the practical application in a post-combustion CO₂ capture process. This working capacity is retained after several temperature-swing adsorption (TSA) cycles, and even after exposure to humidity.

Results and discussion

Synthesis and structure

Mg₂(dobpdc)–DMF was prepared by reacting MgBr₂·6H₂O and H₄dobpdc in N,N′-dimethylformamide (DMF)–EtOH under microwave irradiation, and then evacuation at 390 °C to produce the activated sample (1). 1 was immersed in anhydrous hexane in the presence of 20 equiv. of dmen to yield the diamine-grafted sample. The amine-functionalized sample was treated at 130 °C under vacuum for 30 min to remove trace hexane from the pores. The dried sample (1-dmen) was exposed to a stream of CO₂ for 30 min to give the CO₂-captured material (1-dmen-CO₂ ). The CO₂-adsorbed sample was evacuated at 130 °C for 30 min to give the regenerated sample (1-dmen-re). The structural variations of these samples were examined by collecting synchrotron powder X-ray diffraction (PXRD) data (Fig. 1 and S1–S3†). The PXRD profiles were analyzed using Pawley refinement. The cell volume of V = 2789.8 ų for 1-dmen is reduced to V = 2650.2 ų for 1-dmen-CO₂ , a 5% reduction, indicating that CO₂ adsorption on 1-dmen causes a shrinkage of the framework. The cell reduction (5%) of this system is substantially smaller than that of en-Mg₂(dobpdc) with the primary diamine en (which gave a 13.5% cell reduction), and may be a result of the bulkier dmen in the pores.⁴¹ The remaining CO₂ is completely desorbed by heating 1-dmen-CO₂ under vacuum at 130 °C, as confirmed by the synchrotron PXRD data in which the cell volume (V = 2805.7 ų) of 1-dmen-re is close to the original volume of 1-dmen.

Fig. 1. (a) Synchrotron PXRD profiles of 1-dmen, 1-dmen-CO₂ , and 1-dmen-re. (b) Enlargement of the low-angle region of the PXRD data. (c) Framework structure of 1 with open metal sites, grafting modes of dmen onto the open metal sites, and subsequent CO₂ adsorption. The schematic diagram (bottom) indicates the arrangement of ammonium carbamates running along the c-axis.

IR spectroscopy

We utilized in situ infrared (IR) spectroscopy to probe the CO₂ adsorption mechanism. The IR cell and the interior of the instrument were thoroughly purged with N₂ to remove CO₂ prior to the IR measurements. We used an airtight IR cell (with KBr windows) and an oil bubbler to isolate the cell atmosphere from air. 1-dmen was put into the IR cell to record the IR data under an Ar atmosphere. The distinct peaks centered at 3330 and 3246 cm^–1 for 1-dmen can be assigned to the N–H stretching vibrations of the primary amine of dmen (Fig. S4†). ^41–43 When 15% CO₂ flowed into the cell for 3 min, the primary amine peaks weakened but still remained due to the presence of anchoring primary amines, while a new peak appeared at 3397 cm^–1. This new peak in 1-dmen is associated with the N–H stretching frequency of a carbamate, as can also be observed in the IR spectra of amine-functionalized silica ^44–47 and the secondary diamine-functionalized mmen-Mg₂(dobpdc).³⁸

In addition, there are other strong peaks associated with the combination bands (ν ₃ + ν ₁ at 3728 and 3704 cm^–1; ν ₃ + 2ν ₂ at 3625 and 3599 cm^–1) and the asymmetric stretching mode (ν ₃ at around 2377 cm^–1) of CO₂. ^48,49 To remove free CO₂ from the cell, it was purged with a N₂ flow for 1 min. The characteristic N–H stretching bands are retained even after purging with N₂ for 10 min. For the CO₂-captured sample, a broad peak centered at 2200 cm^–1 is visible together with multiple peaks in the range of 1700–1630 cm^–1 (Fig. S5†). The broad peak is assignable to a combination band from the ammonium cations, and the multiple peaks are related to the C O stretching of the amide group and the asymmetric deformation of the ammonium cation. ^45,47 These peaks simultaneously disappear as the N–H stretching peak at 3397 cm^–1 vanishes, suggesting the formation of a carbamate group during CO₂ adsorption, although there is also the possibility of concomitant carbamic acid formation, as observed in amine-modified silica and as supported by DFT calculations on mmen-Mg₂(dobpdc). ^35,45 The presence of the N–H stretching band of carbamate indicates that the tertiary amines of dmen are grafted onto the open metal sites, while the primary amines that protrude in the pore direction react with CO₂ to produce the carbamate species with the assistance of neighboring amine groups. ^41,45–47 To understand the CO₂ adsorption behavior of 1-dmen as a function of temperature, we measured the in situ IR data at several temperatures (Fig. S6†). At 25 °C, the N–H stretch (3397 cm^–1) for the chemisorbed species is present together with the primary N–H stretching bands (3330 and 3246 cm^–1). In addition, there is a characteristic band around 2200 cm^–1, assigned to ammonium cations. As the temperature increases, the N–H and ammonium bands weaken while the primary N–H stretching peaks increase. From this result, it appears that the chemisorbed species is disrupted and the free primary amine groups reform. At 130 °C, almost no CO₂ is adsorbed on 1-dmen.

Adsorption isotherm and mechanism

From the N₂ uptake for 1-dmen at 77 K (Fig. S7†), it is observed that the BET surface area of 675 m² g^–1 is between those of en-Mg₂(dobpdc) (1253 m² g^–1) and mmen-Mg₂(dobpdc) (70 m² g^–1), ^38,41 which is related to the bulkiness of the appended heterodiamines on the unsaturated metal sites. From the analysis of the pore size distributions, the average pore size of 1-dmen is smaller than those of both en-Mg₂(dobpdc) and mmen-Mg₂(dobpdc) (Fig. S8†). The CO₂ adsorption isotherms for 1-dmen were collected at several temperatures after the samples had been activated at 75 °C for 4 h prior to each measurement (Fig. 2a). The isotherm curves show steps at certain pressures, depending on the adsorption temperature. The shift of the step pressure may be associated with the greater thermal motion of the grafted dmen and CO₂ molecules at elevated temperatures. Similar behavior was also observed in Mg₂(dobpdc) functionalized with primary and secondary diamines. ^38,41 At 1 bar, the adsorbed quantity is 4.34 mmol g^–1 at 40 °C, comparable to those at 50 and 60 °C. Remarkably, however, almost no CO₂ is adsorbed on 1-dmen at 75 °C and 1 bar, which is comparable with the adsorption behaviors of en-Mg₂(dobpdc) and mmen-Mg₂(dobpdc), which both show non-adsorption at temperatures above 120 °C.

Fig. 2. (a) Adsorption isotherms of CO₂ for 1-dmen at the indicated temperatures. The solid lines are eye-guides. (b) CO₂ and N₂ isotherms at 25 °C.

This notable feature indicates a weaker interaction between CO₂ and the amine groups in 1-dmen than that between CO₂ and the amines in en-Mg₂(dobpdc) and mmen-Mg₂(dobpdc).

The isosteric heat of adsorption (Q _st), which represents the mean binding energy of a gas molecule at a specific site of an adsorbent, was estimated by employing a dual-site Langmuir–Freundlich model to fit the CO₂ isotherms. The precise pressures corresponding to the adsorbed CO₂ amounts were introduced as input parameters to the Clausius–Clapeyron equation to calculate the adsorption enthalpy (Fig. S9†). Using this calculation, the estimated heat of adsorption (–Q _st) increases to 75 kJ mol^–1 at a loading of 0.25 mmol g^–1, and remains almost invariant in the range of 71–75 kJ mol^–1 below loadings of 2.6 mmol g^–1. This overall feature of the adsorption enthalpy for 1-dmen resembles that observed for the other Mg₂(dobpdc) moieties functionalized with diamines. ^38,41 The initial low Q _st values at ultradilute CO₂ concentrations are unusual for chemisorbents. To investigate the adsorption behavior at the CO₂ pressures before and after the step in the isotherm, we measured the IR in situ at 40 °C by flowing simulated air (0.39 ppm CO₂ balanced with N₂) or pure CO₂ into the cell (Fig. S10†). There is no evidence of chemisorption at the CO₂ pressure before the step, while the peak at 3397 cm^–1 appears after the step pressure, indicating the formation of the chemisorbed species. To understand the CO₂ adsorption mechanism, we performed DFT calculations on the binding energy of each possible Mg–amine pair. From the results, the primary amine–Mg pair has a binding energy of –174.3 kJ mol^–1, which is thermodynamically more stable than that of the tertiary amine–Mg pair (–135.6 kJ mol^–1) (Fig. 1 and S11†). This result suggests that the open metal site is primarily occupied by the primary amine end of 1-dmen, although some tertiary amine ends are probably grafted onto the exposed metal site as well. On the basis of the in situ IR data and DFT calculations, one possible CO₂ adsorption mechanism is as follows: the low-affinity adsorption at low pressures is highly uncommon for chemisorbents, and cannot be rationalized in the absence of sorbent restructuring under CO₂ dosing conditions. At a certain partial pressure, the amine is reorganized so that it is now available to bind CO₂ via chemisorption causing a jump in the binding energy. Therefore, we speculate that under CO₂ conditions, deprotonation of the coordinate amine group takes place with the assistance of the basic tertiary amine group of the dangling dmen molecule. Concomitant nucleophilic attack of CO₂ forms an alkylammonium carbamate. The generated ion-pair interacts to weaken the Mg–N bond strength of the neighboring dmen and in turn accelerates cooperative CO₂ insertion, which can explain the abrupt rise in the CO₂ isotherm (Fig. 2a). The carbamate species is rearranged at a critical temperature and pressure (Fig. 1c), as recently reported for mmen-Mg₂(dobpdc).⁵⁰ In this scenario, the carbamates are aligned along the c-direction, which may account for the structural shrinkage upon CO₂ adsorption (Fig. 1c).⁵⁰

CO₂ selectivity

The isotherms of CO₂ and N₂ at 25 °C were measured to evaluate the adsorption selectivity for CO₂ over N₂ (Fig. 2b). This selectivity is required for post-combustion CO₂ capture to effectively separate CO₂ from the flue gas where CO₂ and N₂ coexist at partial pressures of 0.15 and 0.75 bar, respectively. At 25 °C and 0.15 bar, 1-dmen takes up 3.77 mmol g^–1 of CO₂, an adsorption capacity larger than those of en-Mg₂(dobpdc) (3.62 mmol g^–1) and mmen-Mg₂(dobpdc) (3.13 mmol g^–1). ^38,41 Using single-component isotherms, the selectivity factor, which is normalized to the composition of the gases, is defined as S = (q _CO2 /q _other)/(p _CO2 /p _other), where q _n and p _n are the adsorption capacity and the pressure of the component n, respectively. The purity of the adsorbed gas, a practical and meaningful value for the transport and sequestration of captured CO₂, is calculated using 100q _CO2 /(q _CO2 + q _other). For the practical purity of the adsorbed gas, it is not only the adsorbed species that must be considered, but also the composition of the residual gas in the column that is not adsorbed; the bulk density of the adsorbent is very important. The calculations done here assume that all non-adsorbed gas is removed by vacuum from the column before desorption, which is not feasible for flue gas capture. The selectivity of 1-dmen for CO₂ over N₂ and the purity of CO₂ are estimated to be 554 and 99%, respectively. The selectivity of 1-dmen is comparable to those of the top-performing MOFs, mmen-Mg₂(dobpdc) (S = 200), en-Mg₂(dobpdc) (S = 230), mmen-Cu-BTTri (S = 327), and PEI-MIL-101 (S = 600), at pressures and temperatures relevant to practical post-combustion CO₂ capture. ^1,13,36,51

To further explore the relative selectivity of 1-dmen, we examined the competitive sorption kinetics of different gas compositions, including pure CO₂, CH₄/CO₂ = 50/50, H₂/CO₂ = 70/30, and N₂/CO₂ = 85/15, at 40 °C. The gas uptake is equivalent to 18.8 wt% for pure CO₂, 16.6 wt% for CH₄/CO₂ = 50/50, 15.0 wt% for H₂/CO₂ = 70/30, and 14.1 wt% for N₂/CO₂ = 85/15, while no obvious adsorption was observed for pure CH₄, H₂, or N₂ (Fig. S12†). Each CO₂ adsorption amount is similar to that at the corresponding CO₂ partial pressure in the isotherm at 40 °C (Fig. 2a). These results suggest that CO₂ adsorbs more strongly than CH₄, H₂, and N₂, thus favorably taking up the available adsorption sites and pores while the other gases are excluded. The observed sorption kinetics of the gas mixtures indicate a relatively high CO₂ selectivity over the other gases.

Facile regeneration and recyclability

Adsorbed CO₂ can be removed from the solid at 30 °C, lower than the uptake temperature of 40 °C, followed by a degree of CO₂ adsorption with a capacity identical to the first cycle's (Fig. 3a). Fig. 3b presents the cycling behavior for the adsorption (40 °C)-activation (40 °C) protocols, showing a significant adsorption capacity as well as a facile desorption of the CO₂ adsorbed at low temperature (Fig. S13†); this is supported by in situ IR spectroscopy (Fig. S14†). A recyclability test using a TSA procedure was also run (Fig. 3c). CO₂ was adsorbed at 40 °C for 1 h and desorbed at 75 °C for 1 h under Ar. After 24 cycles, no capacity loss was observed, suggesting that the material is thermally stable under these experimental conditions. Thus, 1-dmen could be potentially applicable for capturing CO₂ from coal-fired power plant emissions, because its regeneration requires very low desorption temperatures, and it has a high adsorption capability and no capacity decay even after many TSA cycles. This finding is valuable in that our material requires a lower energy input to regenerate the capture material, which is one of the most essential objectives for current CCS technologies.

Fig. 3. (a) Adsorption–desorption cycling of CO₂ for 1-dmen, showing reversible uptake from simulated flue gas (0.15 bar CO₂ balanced with N₂). Adsorption temperature was 40 °C and desorption temperatures were 130 °C, 60 °C, 50 °C, 40 °C, and 30 °C under Ar. (b) Adsorption–desorption cycling of CO₂ at 40 °C by switching atmospheres between simulated flue gas and Ar. (c) Adsorption–desorption cycling of CO₂ at adsorption (40 °C) and desorption (75 °C) under Ar. (d) Vacuum-swing adsorption at 25 °C using a Micromeritics ASAP2020 instrument.

In another experiment, the desorption behavior of 1-dmen was further investigated via the vacuum-swing adsorption (VSA) method ^52,53 using an ASAP2020 analyzer (Fig. 3d). At 25 °C, 1-dmen was saturated with CO₂ at 1.2 bar and then placed under high vacuum. The removal of adsorbed CO₂ from the solid was performed repeatedly by applying a vacuum to the adsorbent; this CO₂ desorption under vacuum was confirmed by IR data in which the peaks relating to CO₂ adsorption progressively vanish upon the application of a high vacuum (Fig. S15†). Thus, notably, even such a large amount of CO₂ as is adsorbed onto 1-dmen at 1.2 bar (∼4.5 mmol g^–1) can be completely desorbed only under vacuum, without heating. Such facile desorption of captured CO₂ under evacuation supports the hypothesis that the alkylammonium carbamate species is weakly bound, as was also found in amine-grafted SBA-15.⁴⁷

CO₂ working capacity

The working capacity that corresponds to the true amount of CO₂ adsorbed during an adsorption–desorption process is a decisive metric to evaluate the material performance of CO₂ capture in real-world post-combustion applications, and is a far more important parameter than the absolute CO₂ uptake under flue gas conditions. As previously shown for sorbents, ^9,13 an estimation of the working capacity can be made on the basis of the difference between the quantities adsorbed at the adsorption and desorption temperatures (WC_q = q _ads – q _des) when the operation temperature is fixed at T _ads = 40 °C.

In this case, the adsorption amounts were obtained from CO₂ isotherms at disparate loading conditions (q _ads at P _ads = 0.15 bar CO₂, T _ads = 40 °C; q _des at P _des = 1 bar CO₂, T _des = corresponding desorption state temperature). The obtained working capacity is significant: 11.6 wt%, even at T _des = 75 °C (Fig. S16†). Notably, the working capacity of this material, with its significantly lower desorption temperature, can be compared to those of MOFs such as Mg–MOF-74 and MOF-177, functionalized PPN-6, zeolite NaX, and MEA, in which almost zero or negative values of working capacities were recorded at the identical temperature. ^9,13 In particular, the increased temperature does not improve the working capacity of 1-dmen because CO₂ is hardly adsorbed onto the sample at temperatures higher than 75 °C. On the other hand, we performed thermogravimetric (TG) experiments to monitor the mass change upon regeneration and CO₂ adsorption using TSA processes, which can give valuable information about the working capacity for practical CO₂ capture applications. 1-dmen was activated at 130 °C under a pure CO₂ atmosphere for 90 min, and then 15% CO₂ in N₂ was flowed over the sample at 40 °C for 60 min (Fig. 4a and S17†). A CO₂ adsorption capacity of 13.3 wt% was observed, and was maintained after 7 cycles. We examined the working capacities (WC_TGA) of 1-dmen at different desorption temperatures and compared them to those of other solid adsorbents such as zeolite 13X and MOFs with open metal sites or grafted amines (Fig. 4b). The working capacities of 1-dmen were exceptionally high, mostly in the range of 11.7–13.5 wt%, even though the desorption temperature changed from 130 °C to 90 °C; these mark the highest values among MOFs at relatively low temperatures. In other words, the obtained capacity of 1-dmen at a desorption temperature of 130 °C is substantially superior to those of some top performing MOFs such as Mg–MOF-74 (3.7 wt%), Mg₂(dobpdc) (4.5 wt%), en-Mg₂(dobpdc) (2.9 wt%), mmen-Mg₂(dobpdc) (2.1 wt%), and tmen-Mg₂(dobpdc) (3.9 wt%) (tmen = N,N,N′,N′-tetramethylethylenediamine), and to that of zeolite 13X (7.0 wt%). As the desorption temperature decreased below 90 °C, the working capacity of 1-dmen sharply reduced to almost zero at 70 °C. The primary en-Mg₂(dobpdc) and secondary mmen-Mg₂(dobpdc) show lower working capacities than the tertiary diamine-grafted solid tmen-Mg₂(dobpdc), even though the actual CO₂ adsorptions of en-Mg₂(dobpdc) and mmen-Mg₂(dobpdc) are larger than that of tmen-Mg₂(dobpdc) upon activation in pure Ar. This implies that successful regeneration under pure CO₂ contributes to the enhanced working capacity of tmen-Mg₂(dobpdc). On the other hand, the working capacity of 1-dmen exceeds that of tmen-Mg₂(dobpdc) because it exhibits high CO₂ uptake as well as facile regeneration. Therefore, both a large CO₂ uptake and easy regeneration under pure CO₂ are responsible for a high working capacity.

Fig. 4. (a) Adsorption–desorption cycling of CO₂ for 1-dmen. The adsorption of simulated flue gas (0.15 bar CO₂ balanced with N₂) was recorded at 40 °C and desorption was performed at 130 °C under flowing pure CO₂. The symbol C represents the influx of pure CO₂ to regenerate the sample. The working capacity is determined as the difference between A and B. (b) The working capacities of 1-dmen and the other porous solids obtained under the same conditions. (c) CO₂ adsorption of 1-dmen in flue gas using the sequence (adsorption at 40 °C – desorption at 130 °C under pure CO₂ – 10 min exposure to 100% RH). (d) Working capacities of the CO₂ uptake in the first and second cycles for 1-dmen, mmen-Mg₂(dobpdc), en-Mg₂(dobpdc), Mg₂(dobpdc), and Mg–MOF-74 using TG experiments. The first cycle was measured with fully activated samples in flue gas, and the second cycle was measured by following the sequence.

CO₂ uptake capacity under humid conditions

The reusability of a solid adsorbent in the presence of water vapor is also essential to be relevant for CO₂ capture applications.⁵⁴ We assessed the material's performance by repeated exposure to humid environments. The solid sample can be fully saturated with CO₂ within the exposure time (10 min), because its initial rate of adsorption is estimated to be roughly 1.7 wt% min^–1 (Fig. S18†). In this experiment, 1-dmen was exposed to 100% RH for 10 min. The humidified sample was then reactivated under a pure CO₂ flow at 130 °C for 4 h, followed by CO₂ adsorption at 40 °C. After 5 cycles run in this sequence (adsorption at 15% CO₂ and 40 °C, humidification at 100% RH, activation at 130 °C under pure CO₂), a capacity loss of 5% is observed (Fig. 4c). To compare the CO₂ working capacity of 1-dmen upon exposure to humidity with those of other adsorbents, we applied the same experimental protocols to the amine-grafted MOFs, en-Mg₂(dobpdc) and mmen-Mg₂(dobpdc), and the MOFs with open metal sites, Mg–MOF-74 and Mg₂(dobpdc) (Fig. 4d). The capacity of 1-dmen retains significantly high values in subsequent cycles, while in comparison, the working capacities of the other MOFs during the first cycle are below 4.5 wt% and are reduced even further in the second cycle. From these results, the CO₂ working capacity of 1-dmen outperforms those of the other tested materials that have primary and secondary diamines or open metal sites.

To examine the CO₂ adsorption capability under humid conditions, we performed time-dependent in situ IR spectroscopy at 40 °C upon simultaneous exposure to 15% CO₂ and 100% RH (Fig. S19†). The N–H stretching band (3397 cm^–1) of the chemisorbed species appears under humid CO₂ flowing conditions. The characteristic peak still survives after purging the cell with pure N₂ for 1 min, while the free CO₂ peaks disappear. This observation definitely supports the conclusion that CO₂ is preferably adsorbed onto the grafted amine groups even under humid conditions.

Moreover, to probe the true effect of water vapor on CO₂ uptake, we performed humid adsorption–desorption cycles, exposing 1-dmen to 15% CO₂ and 3.75% H₂O balanced with He. The sample was placed in an automated chemisorption analyzer (Autochem II 2920) to test its adsorption of CO₂ at 40 °C for 30 min, followed by CO₂ desorption at 130 °C for 1 h. The reversible adsorption–desorption events occurred while a CO₂ uptake of around 14.6 wt% was maintained (Fig. 5a), similar to the CO₂ adsorption amount under dry conditions. The framework structure of 1-dmen remains intact after the cycling experiment in humid conditions, as shown by the PXRD data (Fig. S20†). To explore the dynamic separation capability, we ran breakthrough tests for a gas mixture containing 15% CO₂ in an N₂ gas stream. The sample bed was preheated at 130 °C for 4 h in a He atmosphere. The gas mixture was introduced to the solid packed in a column, and the effluent was detected by a gas chromatograph (Agilent 7890A). Under dry conditions, the solid held CO₂ for up to 14.7 min g^–1 relative to the N₂ breakthrough time (Fig. 5b). To identify dynamic CO₂ separation in the presence of moisture, we carried out humid breakthrough experiments. While 5% water vapor was flowed into the adsorbent bed prior to the breakthrough runs, a gas mixture of 15% CO₂ and 80% N₂ was infused into the fixed bed. The breakthrough time for CO₂ was equivalent to 21.1 min g^–1, which is greater than that of the dry CO₂ capacity. The shorter retention time of CO₂ in dry conditions can be understood by the facile desorption of CO₂ from 1-dmen under flowing dry inert gas, as shown in Fig. 3b. From the breakthrough data, it is evident that this material exhibits effective CO₂ separation from the gas mixture, due to the more enhanced interaction of CO₂ with the amine groups than N₂, which will be beneficial for practical CO₂ capture applications.

Fig. 5. (a) CO₂ adsorption–desorption cycling curve for 1-dmen in humid conditions. (b) Breakthrough curves for 1-dmen under dry (N₂, red circle; CO₂, orange circle) and humid conditions (N₂, green triangle; CO₂, blue triangle).

Conclusions

The presented results show that the structure of 1-dmen undergoes shrinkage upon CO₂ adsorption, and that the original structure is recovered when CO₂ is released from the solid. The selectivity factor for CO₂ over N₂ for this solid is on a par with those of the foremost CO₂-capturing MOFs. Remarkably, the regeneration of the adsorbent is completed under vacuum or flowing Ar even at very low desorption temperatures, while the material maintains a high CO₂ adsorption capacity (above 13 wt%). Notably, the working capacity of 1-dmen, relevant to post-combustion CO₂ capture applications, is exceptionally high at low desorption temperatures and upon exposure to humidity; its capacity exceeds those of the tested MOFs with amine grafting and with open metal sites in identical conditions. Overall, this material, with a record high working capacity at low regeneration temperatures, will be a promising adsorbent for a real post-combustion CO₂ capture process. To establish its use for other practical applications, it will be necessary to determine how this material will perform in the presence of not only humidity but also NO _x and SO₂.

Experimental

All chemicals and solvents in the synthesis were reagent grade and used as received. H₄dobpdc and 1-DMF were prepared according to the literature.³⁸

[Mg₂(dobpdc)(dmen)_1.8(H₂O)_0.2] (1-dmen)

A sample of fully activated 1 (100 mg, 0.31 mmol) was loaded in a Schlenk flask in a glove box. A solution of dry hexane (100 mL) with 20 equiv. of N,N-dimethylethylenediamine (dmen, 0.68 mL, 6.27 mmol) was transferred to the flask using a cannula. The suspension was stirred for 18 h at room temperature. The solid was separated by filtration and washed with dry hexane several times. The resulting residue was immersed in dry hexane for 72 h and then evacuated at 130 °C for 4 h to obtain an off-white powder. Yield: 150 mg (99.5%). Anal. calcd for C_21.2H_28.6Mg₂N_3.6O_6.4 [1-dmen-(H₂O)_0.3]: C, 52.34; H, 5.87; N, 10.24. Found: C, 52.34; H, 5.93; N 10.37.