Abstract
Self-propelled micro/nanomotors possess tremendous exciting promise in diverse fields. We describe an asymmetric, fuel-free and near-infrared light-powered torpedo micromotor, which is constructed by using a porous membrane-assisted layer-by-layer sol-gel method to form silica multilayer inside the pores, following by the deposition of gold nanoparticles on one end of the pores. In the absence of chemical fuels, the high propulsion of microtorpedoes under illumination of near-infrared light is owing to the photo-thermal effect of gold clusters, generating a thermal gradient inside the microtorpedoes. The speed of microtorpedoes is dependent on the laser powers and media. More interestingly, such fuel free-powered microtorpedoes could explode triggered by higher laser power at the predefined site and thus provide a new platform for future biomedical applications.
Introduction
The development of artificial micro/nanomotors launched a new horizon in the field of nanotechnology as their potential promises for environmental remediation, dynamic assembly of intelligent materials, precise disease treatment, and lab-on-chip devices1–14. By mimicking autonomous movement of chemically-powered natural biomolecular motors, various artificial micro/nanomotors have been brought to the foreground over past decade, leading to the development of chemical fuels or other physically actuated motors15–21. Various chemicals, such as hydrogen peroxide22–26, hydrazine27, acid/based28, 29, and bromine/iodide30 provide chemical energy for the self-propulsion of synthetic motors. Despite considerable progress in chemically-powered micro/nanomotors has been achieved, one must be taken into attention that most of chemical fuels are not segmental environment friendly and their relative toxicity is biologically incompatible. To avoid the toxicity of chemical fuels, physical stimulus-powered micro/nanomotors are under intense research recently. Ultrasonic, magnetic field, electric field, and light illumination had been successfully developed to propel micro/nanomotors in the absence of chemical fuels31–36. Among various physical triggers to actuate the propulsion of synthetic motors, near infra-red light (NIR) attracts considerable attention owing to its optimal penetration and minimum absorption in biological tissues, showing promising potential applications in the field of biomedicines37. Previously we reported the NIR laser-triggered propulsion of the polymer multilayer microrocket through thermophesis10. Due to the limited illuminating area and ununiform density of NIR laser, the movement behavior of such polymer rocket is not stable and not easy to achieve the for the long term.
Here we demonstrate the successful construction of gold-functionalized torpedo micromotors based on a porous membrane-assisted layer-by-layer sol-gel method, following the assembly of gold clusters in the big opening (tail) of the microtorpedoes. Under the irradiation of NIR light, the microtorpedoes swim along a rather straight trajectory under the propulsion of self-thermophoretic force as physically simulated38, 39. Compared with the previous polymer multilayer rocket, the torpedo micromotors possess gold nanoparticles layer which are mainly located around the large opening of torpedo micromotors. Addtionally, the two-photon confocal laser scanning microscope provide an advanced light source which sustains with an equally photon-distributed and average-powered focus plane. The combination of torpedo design and improved light setup accomplished the NIR light-triggered high movement with stable behaviour. The movement of the microtorpedo can be modulated by varying the power of NIR light, and also the torpedoes displays efficient movement in various fluids such as pure water, salt solution, PBS, and cell cultured medium. More interestingly, these microtorpedoes could instantaneously explode to several pieces upon a high NIR power. The computational simulation reveals that the NIR irradiation onto the torpedo rapidly increase the temperature, leading to intensive evaporation inside the torpedo micromotor and the following explosion of the torpedo. Such a light-driven microtorpedo with an explosive capability offers a new possibility for the application of fuel-free micro/nanomachines in biomedical field.
Results and Discussion
The fabrication strategy is schematically illustrated in Fig. 1. Three layers of silica as a framework were firstly deposited by applying a porous membrane-assisted layer-by-layer sol-gel method (SSG). Briefly, the SiCl4 as a silica precursor was deposited into the pores of a polycarbonate membrane (pore size: 3 μm) with a thickness of 8 ± 2 μm, and then the SiCl4 was hydrated to one layer of silica inside the pores by immersing the membrane into water. After 3 layers of silica were deposited, the citrate-stabilized gold nanoparticles (AuNPs) were integrated into the pores. It should be noted that the AuNPs were aggregated into gold clusters around the big opening of silica torpedoes by using a repeated wet-dry process40, 41. To improve the connetion of the silica layers between the pores and the surface of the template, a polishing step onto the surface of the template was conducted with wet cotton containing alumina powder (average mech size of 30 μm). Finally, the torpedo motors with gold clusters were collected by dissolving the membrane with CH2Cl2.
The scanning electron microscopy (SEM) image in Fig. 2a shows the asymmetric tubular geometry of a bare silica torpedo without AuNPs. The silica framework is smoother than our previous polymer multilayer tubes22. The length is roughly 8 ± 2 μm in accordance of thickness of the template, and the size of wide opening and narrow opening are 3 ± 0.5 μm and 1.5 ± 0.5 μm. The top view SEM image in Supplementary Fig. S1 illustrates that the thickness of the bare torpedo is about 105 ± 15 nm, representing a 35 ± 5 nm per layer. This bare torpedo is thicker than the previously reported silica tubes with same number of layers42. It should be attributed to the prolonged adsorption and hydrolysis time of SiCl4. Compared with the bare silica torpedoes, the AuNPs-functionalized torpedoes reserve the geometry and size of bare torpedo well, and the bright region is ascribed to the integration of gold clusters (Fig. 2b). An energy dispersive X-ray (EDX) mapping analysis was carried out to investigate the gold distribution of the microtorpedoes (Fig. 2c,d). Thebright yellow region in Fig. 2d displays the distribution of AuNPs clusters mainly located in the wide opening of the torpedo. The transmission electron microscopy (TEM) image in Fig. 2e further confirms the distribution of AuNPs clusters in the big opening. More interestingly, the UV-vis-NIR spectrum in Fig. 2f indicates the maximum adsorption peak of the AuNPs-functionalized torpedoes is approximately 850 nm, which is essential for the NIR light-triggered propulsion.
In order to illuminate the torpedoes, NIR laser beam was vertically guided onto the sample plane through an objective lens of a two-photon confocal laser scanning microscope. The time-lapse images in Fig. 3a captured from Supplementary Video 1, illustrate a nearly linear trajectory of the torpedoes under the NIR irradiation with a power of 5.5 J cm−2 as indicated by the red line. The direction of motion is along the body axis from the wide opening to the narrow opening. Similar with previous reports32, the motion of microtorpedoes should also be ascribed that the torpedo motors convert the adsorbed photons to heat owing to the plasma resonance adsorption of AuNPs clusters in the NIR region. The AuNPs clusters covering the wide opening and asymmetric tubular geometry of the torpedoes under NIR irradiation result in an asymmetric thermal gradient, generating athermophoreticforce along the body axis. Figure 3b records the speed distribution of the torpedo in Fig. 3a. The microtorpedo motor displays a straight movement with a stable speed of 0.8 μm/s during 90 s. Unlike our previous researches, a fixed, focused laser dot made the velocity of torpedo motors increasing firstly and subsequently decreasing22, 23. We here used the two-photon confocal laser scanning microscope (TP-CLSM) combined with the temporal concentration femtosecond ultrafast pulses laser. It is an equally photon-distributed and average-powered focus plane, like a defocus laser irradiation. The real-time monitoring technology in TP-CLSM also enhances system reliability by providing excellent beam stability and minimal power fluctuations during the irradiation duration. The velocity of the torpedo could be easily controlled by modulating NIR laser power as shown in Fig. 3c. The maximum velocity at a laser power of 28.2 J cm−2 is 19.5 ± 1.5 μm s−1. A linear relationship between the NIR laser power and velocity offers a convenient and quantitative control upon the torpedo motor, including the on-demand deceleration, acceleration, and controlled velocity.
Theoretical simulation was conducted to investigate the photo-thermal effect and the propulsion mechanism of torpedo motors under NIR irradiation. The tail of the asymmetric torpedo is covered by cylindrical AuNPs clusters. The AuNPs clusters convert the absorbed photons to heat, acting as a heating source. Accordingly, the kinetic energy of water molecules around the AuNPs clusters-functionalized tail is improved greatly. This thermophoretic force is proportional to the local temperature gradient around the AuNPs clusters-functionalized tail43–45,
1 |
Here the coefficient:
2 |
The computed temperature around AuNPs clusters by the heat diffusion equation is shown in Fig. 4a. The thermophoretic force is proportional to the square of the steam gas viscosity η, the radius of torpedo tail, and the ratio of the thermal conductivity of steam gas Ka to the thermal conductivity of gold kp. When the torpedo finally reaches a steady motion, the thermophoretic force is fully counterbalanced by the viscous resistant force. Figure 4b suggests that the strongest thermophoretic force vectors indicating by black arrows fall on the AuNPs clusters and point upward. Some weak force vectors generated by the hot steam gas layer inside the torpedo point to the opposite direction. The resultant vector of all of these independent force vectors point upward to push the torpedo forward. We further simplify the geometry of the torpedo motor as a cylinder-shell by neglecting the small difference of the radius between the small opening and big opening. The viscous resistant force due to viscous interaction in aqueous environment is computed by equation46,
3 |
Given that the aqueous media near the interface of gold film exist a hot steam in the scope of laser, and the speed of the torpedo maintains the stable speed of 0.8 μm/s. The steam dynamic viscosity η here is η = 1.29779*10−5 kg/ms. The length of torpedo (L) is 7 μm. The radius of the torpedo (R) is 2.25 μm. The computed viscous force with these parameters is 1.39 nN (Fviscous in Fig. 4d). Since the torpedo possesses a narrow opening on one end and a wide opening on the other end, this asymmetric geometry ensured a well-defined directional motion as demonstrated in Fig. 3a. To better understand the motion mechanism, the fluid dynamic simulation was used to Fig. out the velocity field distribution of fluid for a tilted torpedo (Fig. 4c). It can be seen that the flow passing through the central line of the torpedo enhances the robustness of directional motion. When the tail of the torpedo tilted to the right hand side, the flows on the right hand side point to the left hand side to exert a stronger impulse on the torpedo. This impulse force pushes the wide opening of the torpedo to the vertical axis.
To accomplish complex tasks for future biomedical application, the motion of torpedoes was examined in diverse media. Figure 5a, captured from Supplementary Videos 2–4, shows the time-lapse images with track lines for the NIR-powered movement in 30 s, indicating that the NIR-activated torpedoes could efficiently move in pure water, PBS, seawater, and cell culture media. Also, the track lines with different distances under the same windows reflect the increased environmental viscosity of these fluids. The average speed during 30 s is roughly 0.8 μm/s, 0.5 μm/s, 0.4 μm/s and 0.3 μm/s, respectively (Fig. 5b). The decrease of velocity is owing to the increasing viscosity33. On the other hand, salts or proteins in close proximity to the AuNPs clusters could absorb thermal energy, resulting in lower velocity in complex media47. Note that the AuNPs-functionalized silica torpedo displays red fluorescence from AuNPs upon the irradiation of NIR laser owing to the surface plasmon resonance as shown in Fig. 5a 48.
Besides the NIR-triggered movement, the torpedoes also allow for the on demand explosion upon high power of NIR irradiation. Once the output power of NIR laser was beyond 32.3 J cm−2, one can see that an intact torpedo (Fig. 6a captured from Suppplementary Video 5) instantaneously exploded into two big pieces (Fig. 6b captured from Supplementary Video 5). The SEM image of the corresponding broken torpedo displays that the breakage was mainly occurred in the junction of AuNPs clusters-functionalized tail and silica framework (Fig. 6c). The torpedo possesses a complex structure of three layers of tubular silica and an inner layer of loosely combined AuNPs clusters which mainly covers the wide opening end. Upon the irradiation of NIR laser, the temperature of the AuNPs clusters rapidly arises owing to photo-thermal effect, while the temperature of the uncovered remains a relative low temperature. In this case, a heated area expands its volume since the water brings the heat away through the convective flow (Fig. 6d, right scheme). Given that the torpedo motors have the same physical property as the conventional glass tube within tolerable fluctuations. To give a rough estimation on the explosion of torpedo, the Young’s modulus of the torpedoes was taken as the same as glass, E = 7.3*1010 Pa, and the linear thermal expansion coefficient is β = 7*10−6/°C. Therefore, the thermal stress that breaks the torpedoes can be roughly computed by a linear approximation equation49, 50,
4 |
Here ΔT is the temperature difference between the hot centre and the cold edge. Figure 6d shows the distribution of thermal stress along the torpedo body. The temperature difference induces the thermal stress on the interface between the cold area and hot area. Once this thermal stress exceeds the critical maximal strength of the torpedo, it would break into pieces. In other words, the explosion of torpedo motor is caused by the highly inhomogeneous thermal stress distribution across the torpedo body. Note that a low thermal stress only causes single crack in the beginning and leads to a few broken pieces, while a high thermal stress would result in more pieces.
Finally, the AuNPs distribution inside the torpedoes could be roughly controlled by modulating the repeated wet-dry process. Figure 7a, captured from Supplementary Video 6, shows a longitudinally AuNPs clusters-functionalized torpedo, and under exposure of NIR laser, the torpedo exploded into scattered strip along the boundary of the AuNPs clusters. There exists an obviously inhomogeneous thermal stress along the boundary. Figure 7b further shows the computed thermal stress distribution on the torpedo by using the above thermal stress equation. The thermal stress suddenly jumps along the boundary line between the Au coated part and uncovered part. The SEM image of the exploded torpedo fragments reveals the highly inhomogeneous distribution of AuNPs clusters on the inner wall of torpedo (Fig. 7b). It means that the explosive position of the torpedoes could be tuned by assembling AuNPs in a controlled manner.
In summary, we produced a fuel-free torpedo motor which performs stable movement in a straight line in various media, such as pure water, salt solution, PBS, and cell cultured media. The velocity of torpedo motors can be controlled by operating the power of the NIR laser, and the driving mechanism of the NIR-activated torpedo motors is self-thermophoresis. The asymmetric geometry ensured its stable trajectory in a straight line, which is also confirmed by fluid dynamic simulation. Compared with previously NIR-powered synthetic motors propelled by the focused laser, the equally photons-distributed NIR laser in TP-CLSM provide a more controllable and stable velocity. The explosion of torpedoes can be controlled by different deposited spot. Such free-fuel torpedoes provide a path to develop a biocompatible synthetic motor for biomedical application.
Methods
Materials
Commercial porous polycarbonate membranes with the cone-shaped pore wide diameter of 3 μm were purchased from Whatman Corp. The SiCl4 was purchased from Acros. CCl4, CH2Cl2, HAuCl4·4H2O, citric acid monohydrate, methanol and ethanol were used without further purification. The water used in all experiments was prepared in a Milli-Q purification system with the resistivity higher than 18.2 MΩ cm−1.
Preparation of gold nanoparticles (AuNPs)
Citrate-stabilized gold nanoparticles were synthesized according to previous reports32. 50 mL of a citric acid (2.2 mM) solution was placed in a three-neck round bottom flask and heated to 100 °C. Subsequently, 1 mL of 25 mM HAuCl4 solution was added and the reaction mixture was heated to 100 °C for 3.5 min before it was allowed to cool to room temperature.
Preparation of gold film-functionalized torpedoes
The silica tubes were synthesized according to the previous reports42. Commercially available porous polycarbonate membranes with the cone-shaped pore wide diameter of 3 μm were used. A membrane was immersed in a SiCl4 solution for 3 min and quickly washed with CCl4 to remove the reagent from the faces. The membrane was then placed in a beaker with a fresh portion of CCl4 for 20 min to remove the free SiCl4 from the pores. Finally, the membrane was soaked in a CCl4/MeOH 1:1 (2 min) and EtOH (5 min) to displace CCl4, and dried in a vacuum jar with a residual pressure of 10−7 mbar at 100 °C. Then the membrane was immersed in deionized water for 6 min, washed in a beaker with MeOH (2 min), and dried in a vacuum jar (10−7 mbar) at 100 °C for 30 min. After each adsorption and hydrolysis step, a SiO2 layer was developed. When 3 SiO2 layers were obtained, several drops (rougly 50 μl) of Au nanoparticles drip on the wide-opening surface of membranes. Then the Au nanoparticle solution-caped membrane dried in a vacuum at 100 °C for 30 min, repeating the procedure for 3 times. The top and bottom surface of membrane template were polished using a wet cotton swab with alumina powder (average mech size of 30 μm) to obtain the single tubular microtorpedoes. Subsequently, the template were dissolved in CH2Cl2, the resulting solution was washed with CH2Cl2 for 5 times. The resulting torpedoes were collected by centrifugation at 3000 rpm for 5 min. followed by dispersing in ethanol and water. The torpedoes solution was then stored at 4 °C for further experiment.
Motion experiments
A drop of a gold film-functionalized silica torpedoes solution was placed on a glass slide. A cover slide was then put on it and sealed with nail oil. Then two-photon confocal laser scanning microscopy (TP-CLSM, Olympus FV1000) was employed to record the movement of gold film-functionalized silica torpedoes. A self-coded software based on MAT-LAB 2012 was utilized to analysis and track the motorial behaviour of Au-caped silica torpedoes.
Characterization
SEM and EDX images were collected by a Quanta 200FEG instrument at an operating voltage of 20 k eV. A drop of Au-caped silica torpedoes solution was dripped on a silicon wafer for the test. TEM analysis was performed on a JEOL 2100 microscope operated at 100 kV. The samples were prepared on a carbon-coated copper grid.
Electronic supplementary material
Acknowledgements
This work was financially supported by the National Science Foundation of China (21573053, 21674029, and 21603047), State Key Laboratory of Advanced technology for Materials Synthesis and Processing, and China Postdoctoral Science Foundation funded project (2016M590286).
Author Contributions
Q.H. and Z.W. conceived the project and conducted the experiments. Q.R. and M.X. carried out synthesis of the torpedo motors, characterization of motion studies, and explosion studies. T.S. conducted theoretical simulation. Q.R., Z.W. and T.S. interpreted data and wrote the paper. All author reviewed the manuscript.
Competing Interests
The authors declare that they have no competing interests.
Footnotes
Electronic supplementary material
Supplementary information accompanies this paper at doi:10.1038/s41598-017-04908-x
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Contributor Information
Zhiguang Wu, Email: zhiguangwu@hit.edu.cn.
Qiang He, Email: qianghe@hit.edu.cn.
References
- 1.Wang, J. Nanomachines: fundamentals and applications. John Wiley & Sons (2013).
- 2.Paxton WF, et al. Catalytic nanomotors: autonomous movement of striped nanorods. J. Am. Chem. Soc. 2004;126:13424–13431. doi: 10.1021/ja047697z. [DOI] [PubMed] [Google Scholar]
- 3.Mallouk TE, Sen A. Powering nanorobots. Sci. Am. 2009;300:72–77. doi: 10.1038/scientificamerican0509-72. [DOI] [PubMed] [Google Scholar]
- 4.Ozin GA, Manners I, Fournier-Bidoz S, Arsenault A. Dream nanomachines. Adv. Mater. 2015;17:3011–3018. doi: 10.1002/adma.200501767. [DOI] [Google Scholar]
- 5.Mei Y, Solovev AA, Sanchez S, Schmidt OG. Rolled-up nanotech on polymers: from basic perception to self-propelled catalytic microengines. Chem. Soc. Rev. 2011;40:2109–2119. doi: 10.1039/c0cs00078g. [DOI] [PubMed] [Google Scholar]
- 6.Sánchez S, Soler L, Katuri J. Chemically powered micro- and nanomotors. Angew. Chem. Int. Ed. 2015;54:1414–1444. doi: 10.1002/anie.201406096. [DOI] [PubMed] [Google Scholar]
- 7.Li J, Rozen I, Wang J. Rocket science at the nanoscale. ACS Nano. 2016;10:5619–5634. doi: 10.1021/acsnano.6b02518. [DOI] [PubMed] [Google Scholar]
- 8.Qiu T, et al. Swimming by reciprocal motion at low reynolds number. Nat. Commun. 2014;5:5119. doi: 10.1038/ncomms6119. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 9.Wilson DA, Nolte RJ, van Hest JC. Autonomous movement of platinum-loaded stomatocytes. Nat. Chem. 2012;4:268–274. doi: 10.1038/nchem.1281. [DOI] [PubMed] [Google Scholar]
- 10.Wu Z, et al. Superfast near-infrared light-driven polymer multilayer rockets. Small. 2016;12:577–582. doi: 10.1002/smll.201502605. [DOI] [PubMed] [Google Scholar]
- 11.Li T, et al. Magnetically propelled fish-like nanoswimmers. Small. 2016;12:6098–6105. doi: 10.1002/smll.201601846. [DOI] [PubMed] [Google Scholar]
- 12.Tu Y, et al. Mimicking the cell: bio-inspired functions of supramolecular sssemblies. Chem. Rev. 2015;116:2023–2078. doi: 10.1021/acs.chemrev.5b00344. [DOI] [PubMed] [Google Scholar]
- 13.Lin X, et al. Self-propelled micro-/nanomotors based on controlled assembled architectures. Adv. Mater. 2016;28:1060–1072. doi: 10.1002/adma.201502583. [DOI] [PubMed] [Google Scholar]
- 14.Xu T, et al. Ultrasound-modulated bubble propulsion of chemically powered microengines. J. Am. Chem. Soc. 2014;136:8552–8555. doi: 10.1021/ja504150e. [DOI] [PubMed] [Google Scholar]
- 15.Xu X, et al. Near-field enhanced plasmonic-magnetic bifunctional nanotubes for single cell bioanalysis. Adv. Funct. Mater. 2013;23:4332–4338. doi: 10.1002/adfm.201203822. [DOI] [Google Scholar]
- 16.Van Rhee PG, et al. Polymersome magneto-valves for reversible capture and release of nanoparticles. Nat. Comm. 2014;5:5010. doi: 10.1038/ncomms6010. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 17.Song M, et al. Converting chemical energy into electricity through a functionally cooperating device with diving–surfacing cycles. Adv. Mater. 2014;26:7059–7063. doi: 10.1002/adma.201402237. [DOI] [PubMed] [Google Scholar]
- 18.Mou F, et al. Self-propelled micromotors driven by the magnesium-water reaction and their hemolytic properties. Angew. Chem. Int. Ed. 2013;52:7208–7212. doi: 10.1002/anie.201300913. [DOI] [PubMed] [Google Scholar]
- 19.Pumera M, et al. Graphene for electrochemical sensing and biosensing. Trends Anal. Chem. 2010;29:954–965. doi: 10.1016/j.trac.2010.05.011. [DOI] [Google Scholar]
- 20.Bregulla AP, Yang H, Cichos F. Stochastic localization of microswimmers by photon nudging. ACS Nano. 2014;8:6542–6550. doi: 10.1021/nn501568e. [DOI] [PubMed] [Google Scholar]
- 21.Gao W, Uygun A, Wang J. Hydrogen-bubble-propelled zinc-based microrockets in strongly acidic media. J. Am. Chem. Soc. 2011;134:897–900. doi: 10.1021/ja210874s. [DOI] [PubMed] [Google Scholar]
- 22.Wu Z, et al. Self-propelled polymer-based multilayer nanorockets for transportation and drug release. Angew. Chem. Int. Ed. 2013;52:7000–7003. doi: 10.1002/anie.201301643. [DOI] [PubMed] [Google Scholar]
- 23.Qin W, et al. Catalysis-driven self-thermophoresis of Janus plasmonic nanomotors. Angew. Chem. Int. Ed. 2017;56:515–518. doi: 10.1002/anie.201609121. [DOI] [PubMed] [Google Scholar]
- 24.Kagan D, et al. Functionalized micromachines for selective and rapid isolation of nucleic acid targets from complex samples. Nano Lett. 2011;11:2083–2087. doi: 10.1021/nl2005687. [DOI] [PubMed] [Google Scholar]
- 25.Wang H, Zhao GJ, Pumera M. Bubble-propelled micromotors based on Ag and MnO2 catalysts. J. Am. Chem. Soc. 2014;136:2719–2722. doi: 10.1021/ja411705d. [DOI] [PubMed] [Google Scholar]
- 26.Ebbens SJ, Howse JR. Direct observation of the direction of motion for spherical catalytic swimmers. Langmuir. 2011;27:12293–12296. doi: 10.1021/la2033127. [DOI] [PubMed] [Google Scholar]
- 27.Kline TR, Paxton WF, Mallouk TE, Sen A. Catalytic nanomotors: remote-controlled autonomous movement of striped metallic nanorods. Angew. Chem. Int. Ed. 2005;117:754–756. doi: 10.1002/ange.200461890. [DOI] [PubMed] [Google Scholar]
- 28.Dey KK, et al. The pH taxis of an intelligent catalytic microbot. Small. 2013;9:1916–1920. doi: 10.1002/smll.201202312. [DOI] [PubMed] [Google Scholar]
- 29.Gao W, et al. Multi-fuel driven Janus micromotors. Small. 2013;9:467–471. doi: 10.1002/smll.201201864. [DOI] [PubMed] [Google Scholar]
- 30.Liu R, Sen A. Autonomous nanomotor based on copper–platinum segmented nanobattery. J. Am. Chem. Soc. 2011;133:20064–20067. doi: 10.1021/ja2082735. [DOI] [PubMed] [Google Scholar]
- 31.Loget G, Kuhn A. Electric field-induced chemical locomotion of conducting objects. Nat. Commun. 2011;2:535. doi: 10.1038/ncomms1550. [DOI] [PubMed] [Google Scholar]
- 32.Wu Z, et al. Near-infrared light-triggered “on/off” motion of polymer multilayer rockets. ACS Nano. 2014;8:6097–6105. doi: 10.1021/nn501407r. [DOI] [PubMed] [Google Scholar]
- 33.Shao J, et al. Near-infrared-activated nanocalorifiers in microcapsules: vapor bubble generation for in vivo enhanced cancer therapy. Angew. Chem. Int. Ed. 2015;54:12782–12787. doi: 10.1002/anie.201506115. [DOI] [PubMed] [Google Scholar]
- 34.Xu T, et al. Reversible swarming and separation of self-propelled chemically powered nanomotors under acoustic fields. J. Am. Chem. Soc. 2015;137:2163–2166. doi: 10.1021/ja511012v. [DOI] [PubMed] [Google Scholar]
- 35.Ariga K, et al. Enzyme nanoarchitectonics: organization and device application. Chem. Soc. Rev. 2013;42:6322–6345. doi: 10.1039/c2cs35475f. [DOI] [PubMed] [Google Scholar]
- 36.Schiffrin DJ. Nanoparticles and self-organisation: the emergence of hierarchical properties from the nanoparticle soup (ie, the small is getting bigger). Concluding remarks for Faraday Discussion: nanoparticle synthesis and assembly. Faraday Discuss. 2015;181:481–487. doi: 10.1039/C5FD00094G. [DOI] [PubMed] [Google Scholar]
- 37.Wang F, et al. Doxorubicin-tethered responsive gold nanoparticles facilitate intracellular drug delivery for overcoming multidrug resistance in cancer cells. ACS Nano. 2011;5:3679–3692. doi: 10.1021/nn200007z. [DOI] [PubMed] [Google Scholar]
- 38.Sun R, et al. Light-driven linear helical supramolecular polymer formed by molecular-recognition-directed self-assembly of bis (p-sulfonatocalix [4] arene) and pseudorotaxane. J. Am. Chem. Soc. 2013;135:5990–5993. doi: 10.1021/ja4016952. [DOI] [PubMed] [Google Scholar]
- 39.Link S, El-Sayed MA. Optical properties and ultrafast dynamics of metallic nanocrystals. Annu. Rev. Phys. Chem. 2003;54:331–366. doi: 10.1146/annurev.physchem.54.011002.103759. [DOI] [PubMed] [Google Scholar]
- 40.Son SJ, Lee SB. Controlled gold nanoparticle diffusion in nanotubes: platform of partial functionalization and gold capping. J. Am. Chem. Soc. 2006;128:15974–15975. doi: 10.1021/ja0663632. [DOI] [PubMed] [Google Scholar]
- 41.Cong VT, et al. Gold nanoparticle silica nanopeapods. J. Am. Chem. Soc. 2014;136:3833–3841. doi: 10.1021/ja411034q. [DOI] [PubMed] [Google Scholar]
- 42.Kovtyukhova NI, Mallouk TE, Mayer TS. Templated surface sol–gel synthesis of SiO2 nanotubes and SiO2-insulated metal nanowires. Adv. Mater. 2003;15:780–785. doi: 10.1002/adma.200304701. [DOI] [Google Scholar]
- 43.Hinds, W. C. Aerosol technology: properties, behavior, and measurement of airborne particles. John Wiley & Sons. (2012).
- 44.Happel, J. and Brenner, H. Low Reynolds number hydrodynamics: with special applications to particulate media. Springer Science & Business Media (2012).
- 45.Jiang HR, Yoshinaga N, Sano M. Active motion of a Janus particle by self-thermophoresis in a defocused laser beam. Appl. Phys. Lett. 2010;105:268302. doi: 10.1103/PhysRevLett.105.268302. [DOI] [PubMed] [Google Scholar]
- 46.Buttinoni I, et al. Active Brownian motion tunable by light. J. Phys.: Condens. Matter. 2012;24:284129. doi: 10.1088/0953-8984/24/28/284129. [DOI] [PubMed] [Google Scholar]
- 47.Simoncelli S, et al. Combined optical and chemical control of a microsized photofueled janus particle. Small. 2016;12:2854–2858. doi: 10.1002/smll.201503712. [DOI] [PubMed] [Google Scholar]
- 48.Chen L, et al. Photoresponsive monodisperse cholesteric liquid crystalline microshells for tunable omnidirectional lasing enabled by a visible light-riven chiral molecular switch. Adv. Opt. Mater. 2014;2:845–848. doi: 10.1002/adom.201400166. [DOI] [Google Scholar]
- 49.Kang K. Assessment of a model development for window glass breakage due to fire exposure in a field model. Fire Saf. J. 2009;44:415–424. doi: 10.1016/j.firesaf.2008.09.002. [DOI] [Google Scholar]
- 50.Wang Q, et al. A stochastic analysis of glass crack initiation under thermal loading. Appl. Therm. Eng. 2014;67:447–457. doi: 10.1016/j.applthermaleng.2014.01.075. [DOI] [Google Scholar]
Associated Data
This section collects any data citations, data availability statements, or supplementary materials included in this article.