. 2017 May 30;4(6):1506–1514. doi: 10.1021/acsphotonics.7b00285

High Photocurrent in Gated Graphene–Silicon Hybrid Photodiodes

Sarah Riazimehr †,§, Satender Kataria †,§,*, Rainer Bornemann , Peter Haring Bolívar , Francisco Javier Garcia Ruiz , Olof Engström , Andres Godoy , Max C Lemme †,§,*
PMCID: PMC5526651  PMID: 28781983

Abstract

graphic file with name ph-2017-002857_0006.jpg

Graphene/silicon (G/Si) heterojunction based devices have been demonstrated as high responsivity photodetectors that are potentially compatible with semiconductor technology. Such G/Si Schottky junction diodes are typically in parallel with gated G/silicon dioxide (SiO2)/Si areas, where the graphene is contacted. Here, we utilize scanning photocurrent measurements to investigate the spatial distribution and explain the physical origin of photocurrent generation in these devices. We observe distinctly higher photocurrents underneath the isolating region of graphene on SiO2 adjacent to the Schottky junction of G/Si. A certain threshold voltage (VT) is required before this can be observed, and its origins are similar to that of the threshold voltage in metal oxide semiconductor field effect transistors. A physical model serves to explain the large photocurrents underneath SiO2 by the formation of an inversion layer in Si. Our findings contribute to a basic understanding of graphene/semiconductor hybrid devices which, in turn, can help in designing efficient optoelectronic devices and systems based on such 2D/3D heterojunctions.

Keywords: graphene, heterojunction, Schottky diode, photocurrent, inversion layer


Graphene-based optoelectronic devices and photodetectors have recently attracted scientific attention for their ultrafast response time and broadband spectral range.111 Graphene is largely compatible with the well-established silicon (Si) process technology, which makes it a promising candidate for large-scale integration and cost-effective applications.1214 Although pure graphene-based photodetectors are extremely attractive for ultrafast optical communications, they suffer from low light absorption and, hence, low photoresponsivity. During the past few years, there have been many studies to understand the fundamentals of light–matter interaction in graphene1520 and to improve the photoresponsivity using complex architectures.3,2126 Nevertheless, practical applications may require hybrid technologies, that is, cointegration of graphene and conventional semiconductors, as demonstrated for high-speed communications,27 solar cells,28 chemical and biological sensing,29 and photodetectors.3033 Graphene/Si (G/Si) Schottky junctions are among the simplest possible hybrid structures, and substantial experimental and theoretical work has been published on such heterojunctions for photodetection.31,3339 Here, the photogeneration of charge carriers mainly occurs in Si due to low absolute light absorption in graphene (2.3%).7 Nevertheless, graphene forms a transparent Schottky junction with Si that enables the extraction of photoexcited carriers and, thus, allows exposing the entire active area to the incident photons. Most of the studies to date have focused on improving the performance of G/Si Schottky diodes in terms of photoresponse and on the nature of the Schottky barrier. Less attention has been paid to the exact location of photocurrent generation in G/Si Schottky diodes. Liu et al.40 investigated the role of different substrates on the photoresponse of graphene using scanning photocurrent measurements, and they observed that photocurrent in graphene on insulating SiO2 substrates is larger than photocurrents obtained in graphene on Si substrates. This observation was attributed to the likelihood of carriers excited from the trap states in SiO2 and their much longer lifetimes as compared to those excited in Si. Recently, Srisonphan et al.37 have reported extremely high quantum efficiencies in hybrid graphene/Si-based devices where graphene is placed across SiO2 over a Si trench to form a device consisting of a graphene–Si heterojunction and a graphene/SiO2/Si field effect structure. They propose photoinduced carrier multiplication in the 2DEG region near SiO2/Si interface to explain the observed high photocurrents in their devices. Despite considerable work carried out on graphene/Si heterojunction-based devices, the main mechanisms of the observable high photocurrents in these devices have been only recently investigated in depth.41,42 In this work, we thoroughly investigate graphene/n-Si Schottky photodiodes using the scanning photocurrent measurement technique. We clearly show where charge carriers are photogenerated and injected from the Si substrate to graphene. Counterintuitively, we find that higher photocurrent is generated in the graphene/SiO2/Si (G/SiO2/Si or GIS) region compared to the graphene/Si (G/Si) region at reverse biases above a threshold voltage (VT). This observation is found to be independent of excitation laser power, and it is explained through simulations by the formation of an inversion layer in n-Si under G/SiO2, corroborating the experimental data and the model proposed in.41,42

The G/Si Schottky diodes were fabricated using chemical vapor deposited graphene, transferred onto prepatterned n-Si substrates, similar to the process in ref (33). Figure 1a,b shows a schematic and a scanning electron micrograph of a G/n-Si photodiode, respectively. One end of the structured graphene film is in contact with the Si substrate, forming the Schottky junction. The other end is contacted with a gold pad on SiO2.

Figure 1.

Figure 1

(a) Schematic, (b) scanning electron micrograph, and (c) JV plot of a graphene–n-Si (G-Si) photodiode in the dark and under illumination. Schematic band diagram of the graphene–n-Si interface (d) in the dark at zero bias voltage and (e) under illumination in reverse biased condition. EC, EV, EFSi, EFg, Øg, XSi, Vbi, ØB, Va, and VR indicate conduction band, valence band, Fermi level of Si, Fermi level of graphene, graphene work function, Si electron affinity, built-in potential, Schottky barrier height (SBH), applied voltage, and reverse bias voltage of the diode, respectively. (f) Abs SR vs wavelength (lower x-axis) and energy (upper x-axis) of the graphene–n-Si photodiode for wavelengths ranging from 360 nm (3.44 eV) to 2200 nm (0.56 eV) and the inset shows zoom-in from 1200 nm (1.03 eV) to 2000 nm (0.62 eV) at zero bias and reverse biases of −1 and −2 V.

Current density–voltage (JV) characteristics of the G/n-Si Schottky photodiode are shown in Figure 1c in semilogarithmic scale. The black and red plots (Figure 1c) are representative of JV characteristics of the diode in the dark and under illumination, respectively. The photodiode clearly exhibits rectifying behavior in the dark. The forward JV characteristic of the diode can be described by the Shockley diode equation.43 For this diode, an ideality factor of 1.16, a Schottky barrier height (SBH) of 0.76 eV, and a series resistance of 4 kΩ have been extracted (the method is described in detail in ref (44)). The ideality factor of 1.16 indicates how closely the diode follows an ideal diode behavior with an ideality factor of 1. A detailed discussion on interpretation of these parameters can be found in ref (39). The corresponding energy band diagrams for the G/n-Si diode at zero bias voltage in the dark are shown in Figure 1d. The photoresponsivity of the G/n-Si diodes has been probed under white-light illumination with an intensity of 0.5 mW·cm–2. When the G/n-Si junction is illuminated, the incident photons generate electron–hole pairs in the n-Si substrate. Under the application of a reverse bias, the photogenerated holes in n-Si are accelerated into graphene, leading to a significant photocurrent. As a result, the diode in the off-state under reverse bias exhibits a dark current density of 38 μA·cm–2, while under illumination, a noticeable photocurrent density of 2 mA·cm–2 was measured at −2 V. The energy band diagram of the photodiode in reverse bias under illumination is shown in Figure 1e.

The absolute spectral response (SR) was measured using a lock-in technique by a LabVIEW controlled setup. Figure 1f shows the SR measurements over a broad spectrum (from 360 to 1800 nm) at various applied reverse bias voltages (VR) on the G/n-Si photodiode. The plot shows an increase of the absolute SR value with the applied reverse bias due to the increased electric field (Figure 1f). The maximum responsivity is 270 mA·W–1 at a reverse dc bias of −2 V. This maximum is observed at an energy of approximately 1.30 eV (λ = 950 nm) and can be attributed to absorption in the n-Si. In fact, the photodiode shows a SR very similar to Si p-n photodiodes in shape and magnitude, even though one doped Si region has been replaced by single layer graphene. In contrast to Si p–n diodes, a low and flat SR can be observed over a broad spectrum for energies below the Si bandgap, where there is no contribution from the underlying n-Si. In this region, the SR drops to values below 0.19 mA·W–1. This part of the SR can be attributed to light absorption of 2.3% in the single layer graphene, as reported in our previous work.33

These data establish that the fabricated devices behave as photodiodes, similar to our previously published devices.33 Next, we performed scanning photocurrent (SPC) measurements to map out the regions of photocurrent generation in the devices. It should be remembered here that JV characteristics or SR of a diode are generally measured by shining light on the whole device area; therefore, it provides an overall picture of the diode behavior and does not distinguish the regions (of photocurrent generation) constituting the device structure. However, SPC measurements can provide a detailed spatial distribution of photocurrent in localized regions by scanning a laser of desired wavelength over a selected area. Figure 2a shows an optical micrograph of the device under study. The red rectangle indicates the scanned area, and the black dashed line represents the area where graphene is present. The device was imaged over an area of 0.65 mm × 1.3 mm with a scan speed of 0.256 s/line and integration time of 1 ms. We used a 10× objective (numerical aperture 0.25) for obtaining the large area scans. The diffraction limited laser spot size was approximately 2.4 μm. Figure 2b, c, and d show the photocurrent maps of the scanned area at VR = −1, −1.5, and −2 V, respectively, at a low laser power of 2 μW. At a reverse bias of −1 V, higher photocurrents were recorded in the G/Si region compared to the G/SiO2 region (Figure 2b). This situation was reversed for increased VR, where much higher photocurrents were obtained in the G/SiO2 regions (Figure 2c,d). Comparing the absolute increase of photocurrent with VR, we observe an 8-fold rise in current for G/SiO2 and a 2-fold rise in G/Si region at −2 V compared to −1 V (Figure 2e). This result is quite counterintuitive to the initial perception that photocurrents are generated predominantly in the G/Si region, that is, at the Schottky junction, and will be explained below. We confirmed these measurements on another device, which also exhibited good rectification behavior, with similar results for the photocurrent (Figure S1). We also note a decaying photocurrent near the graphene edge in G/SiO2 and G/Si region (Figure S2). This can be attributed to the rapid separation of photogenerated charge carriers in Si near these junctions.

Figure 2.

Figure 2

Scanning photocurrent (SPC) measurements of the diode at various reverse biases. (a) Optical micrograph of the diode. The area inside the red rectangle was scanned for photocurrent measurements. The graphene region is represented by the black dashed rectangle. The horizontal yellow dashed lines inside the scanned area depict the SiO2 region and the same is valid for all the images. Photocurrent maps of the scanned area at a laser power of 2 μW and a reverse bias of (b) −1, (c) −1.5, and (d) −2 V. (e) Evolution of the photocurrent (shown as absolute values) with increase in reverse voltage in G/Si (circle symbol) and G/SiO2 (rectangle symbol) regions at a laser power of 2 μW. A higher current is observed in G/SiO2 region compared to G/Si region at reverse biases slightly above 1 V.

Next, we varied the incident laser power (by 2 orders of magnitude) and performed the SPC measurements on the same area at a constant VR. This was done in order to exclude any dependency, if any, of the present findings on the incident laser power. We selected VR to be −1 and −2 V, at which photocurrent was higher in the G/Si and in the G/SiO2 region, respectively. The photocurrent maps of the photodiode at VR = −1 V with laser powers of 0.5, 5, and 50 μW are shown in Figure 3a–c. A slight increase in photocurrent with laser power is noted, but higher photocurrents were consistently measured in the G/Si region. The current maps obtained at VR = −2 V for different laser powers again show a different picture (Figure 3d–f). Here, the photocurrent was consistently higher in G/SiO2 region than in G/Si region. The average values of the so obtained photocurrents at different laser powers are plotted in Figure 3g. The maps show a substantially sharper rise in the photocurrent in the G/SiO2 region compared to the G/Si one when VR was varied from −1 to −2 V at a defined laser power. We can conclude that the region that produces the higher photocurrent is independent of the incident laser power; instead, it depends on the applied bias voltage.

Figure 3.

Figure 3

Laser power dependence of photocurrent. Photocurrent maps of the diode at a reverse bias of −1 V with a laser power of (a) 0.5, (b) 5, and (c) 50 μW. Photocurrent maps of the diode at a reverse bias of −2 V with a laser power of (d) 0.5, (e) 5, and (f) 50 μW. The graphene region is represented by the black dashed rectangle. The horizontal yellow dotted lines depict the SiO2 region. (g) Evolution of the photocurrent at different laser powers of 0.5, 5, and 50 μW and at reverse biases of −1 and −2 V in G/Si (circle symbols) and G/SiO2 (rectangle symbols) regions. A significant photocurrent is observed at the Au contact periphery at a bias of −2 V, which increases for higher laser power. Also, it is found that region of higher current is independent of laser power, rather it depends on the applied bias. (h) Current–voltage (IV) curves obtained for G/SiO2 and G/Si regions of the diode under dark and laser illumination at two different laser powers, that is, 5 and 150 μW. A kink is clearly observed at an applied reverse bias of around 1.2–1.3 V. The inset in (h) shows the magnified curves in the bias range from −0.7 to −1.8 V to emphasize the kink formation at a particular bias. The vertical dashed lines mark the position of the threshold voltage at which the current starts rising sharply.

IV curves of G/SiO2 and G/Si were recorded while shining the laser (used for SPC measurements) locally in these regions one after the other (Figure 3h). Unlike, the measurements where the whole diode is illuminated with white light to obtain IV curves, these local measurements yield more detailed information by isolating the photocurrent generation and contribution from the different regions. A kink in IV curves is observed in the G/SiO2 regions at VR of 1.2 to 1.3 V, irrespective of the incident laser power, after which the current rises sharply. We deliberately used two laser powers in order to cover the regimes of low (5 μW) and high laser power (150 μW), respectively. These observations clearly demonstrate that G/SiO2 regions play a significant role in PC generation and that there appears to be a threshold voltage where these areas become more efficient. Our device structure can clearly be considered as a combination of two heterostructures, namely, graphene on n-Si (G/Si) and graphene-SiO2-n-Si (GIS). The first one acts as a Schottky junction, and the second one behaves as conductor–insulator–semiconductor.

To further elucidate the physical origin of the observed high photocurrent in the G/SiO2 regions of the photodiodes, we have assessed the evolution of the energy bands as a function of the applied bias, highlighting the different behavior in each region. In the dark, the surface potential in the Schottky diode is equal to VbiVa, where built-in potential Vbi = (ϕg – ϕSi)/e. e, ϕg, ϕSi, and Va refer to the electron’s charge, graphene’s work function, Si work function, and the diode’s applied bias voltage, respectively. So that, surface potential increases continuously with Va and the depletion width of the n-Si under graphene widens continuously as the reverse bias increases. However, for the second heterojunction (GIS), the surface potential shows a lower curvature than in the Schottky diode due to the voltage drop through the insulator. Moreover, when a negative bias is applied to the graphene, as in the present case, the energy bands along the whole n-Si substrate bends upward.

The GIS system behaves as a normal MOS structure, and holes are attracted to the SiO2/Si interface when a negative bias is applied. This in turn can lead to the inversion of the n-Si underneath the oxide.

The condition for the creation of the inversion layer is that the number of minority carriers (holes in this case) at the surface is larger than that of the majority carriers in the bulk (electrons).43 When this condition is fulfilled, a considerable difference in the band alignment between the GIS and G/Si junctions along the n-Si substrate is produced. An additional aspect to consider is that the depletion width in the GIS region becomes almost pinned once the inversion layer is created, as the substrate depletion charge is screened by the holes located at the interface.43,41 The calculations of electron and hole concentrations at the SiO2/Si interface, for two devices with 40 and 85 nm oxide thickness, clearly show a rise in hole concentration with increasing VR (Figure S4). Furthermore, the thinner insulator results in a lower threshold voltage and consequently in a higher hole density in the inversion layer for the same VR value. The calculated threshold voltage for 85 nm thick oxide is around −1.2 V, which is in excellent agreement with the bias where a kink is observed in the IV curves measured in the G/SiO2 region only (Figure 3h).

All these physical phenomena have been thoroughly studied and represented in Figure 4. Figure 4a,b shows the cross-section of the G/n-Si heterojunction diode with the corresponding simulated plot of the valence band (EV) along the n-Si substrate, exactly at the interface with graphene and SiO2 at VR = −1 V and VR = −2 V, respectively, with −2 V ≤ VT < −1 V, where VT is the threshold voltage of the G-SiO2-n-Si junction. Below the G/Si junction, EV is shifted upward an amount equal to the applied reverse bias. However, this is not the case for the GIS junction, where EV shows a much modest growth due to the creation of the inversion layer for |VR| > |VT| (Figure 4c). This different behavior gives rise to a high lateral energy gradient that favors hole collection from GIS to G/Si junction.

Figure 4.

Figure 4

Cross-section of the graphene–n-Si heterojunction diode with corresponding simulated plot of the valence band (EV) along the n-silicon, just at the top interface with graphene and SiO2 in reverse biased condition of (a) VR = −1 V (|VR| < |VT|) and (b) VR = −2 V (|VR| ≥ |VT|) in the dark. The conduction band (EC) will be parallel to the EV and shifted by the Si bandgap. Schematics, which show (c) formation of depletion layer in n-Si under graphene and G/SiO2 at |VR| < |VT| and (d) widening of depletion width in n-Si under graphene and formation of inversion layer in n-Si under SiO2 at |VR| ≥ |VT| in the dark and (e) and (f) under illumination. VR, VT, EC(Si), and EV(Si) indicate reverse voltage, threshold voltage, conduction band, and valence band of n-Si, respectively. Plotted dashed lines in n-Si region are representative of depletion layer. The formation of an inversion layer in Si, underneath G/SiO2 region, above a threshold reverse voltage results in a higher photocurrent in that region. The holes in the inversion layer may fill the trap states at the SiO2/Si interface, therefore, allowing more efficient collection of photogenerated holes. This results in a higher photocurrent with increasing reverse bias.

When our device is illuminated, incident light is absorbed in the Si substrate and electron–hole pairs are generated as a result. It should be noted that graphene has a low absorption coefficient and that the photogenerated carriers have a very short lifetime (in the range of picoseconds45). Besides that, SiO2 is transparent for the energy range of the photons we used for the measurements, that is, 532 nm wavelength laser. Considering these two factors, we can say that graphene and SiO2 do not act as main absorbers in our study, and the same has been observed through SR measurements where the maximum absorption is seen in Si in the visible range (Figure 1f). Therefore, the photons absorbed in the depletion width of G/Si region or at a distance below the diffusion length of its border produce charge-carriers that are rapidly separated (this is also apparent from Figure S2, where we observe an increasing photocurrent near the G/Si region). The schematic cross-section shown in Figure 4e,f and the band diagram in Figure 1e depict that the photogenerated holes are attracted to the surface and electrons go to the Si substrate. The holes that reach the G/Si interface are free to move into the graphene contact. However, in the case of the GIS structure, a thick barrier (here, 85 nm thick SiO2) exists that prevents the tunneling and the transit of the photogenerated holes to the contacts. Therefore, the photogenerated holes will start accumulating below the SiO2 as they have to reach the G/Si interface before they can be extracted to the contact. For |VR| < |VT|, we observed a lower photocurrent for the laser spot located in the GIS region compared to the G/Si region (see Figure 2b). For these low voltages, the GIS structure is either in the depletion or in the weak inversion region (Figure 4c,e). In either case, photogenerated holes have to travel a long distance close to the Si/SiO2 interface, where the probability of recombination is quite high due to the presence of interface states. If we continue to increase the reverse bias, we finally reach |VT|, and the GIS junction achieves the strong inversion condition. In that case, a high concentration of holes is located at the SiO2/Si interface generating a quasi p–n junction. Therefore, for biases higher than |VT|, the photocurrent measured at GIS increases rapidly, as it is shown in Figure 2e. For a constant laser power and a fixed depletion width in the GIS region, we do not expect a rise in the generation rate of charge carriers.

Therefore, to explain the increase in the measured photocurrent, we need to consider other factors. First, the larger band bending (surface potential) along the n-Si substrate, as shown in Figure 4b,d, enhances the lateral drift of photogenerated holes in the n-Si substrate from the GIS to the G/Si region following the top of the valence band. The second factor is the formation of the inversion layer, which produces an effective passivation layer for the surface states located at the Si/SiO2 interface.4648 As a consequence, a noticeable reduction of surface recombination is achieved, and the inversion layer provides a highly conductive path for the minority charge carriers (holes in the present case).46 Green et al.,46,47 in their pioneering studies of MIS-type photovoltaic cells, have shown that when an inversion layer is formed in Si underneath the oxide, it results in an enhanced solar cell efficiency. Moreover, in our case, the difference in the band alignment between both junctions assists the lateral drift of the accumulated holes in the inversion layer into the G/Si junction and their extraction to the external contacts (Figure 4d,f). Also, the formation of a native oxide layer at the G/Si junction cannot be avoided completely during the fabrication. This may further suppress the photocurrent due to increased recombination processes at the G/Si junction. All these factors result in a higher photocurrent in the GIS region of the photodetector, compared to the G/Si junction, as observed in the present study.

The creation of this type of quasi p–n junction is a process usually employed to improve the performance of photosensitive devices, as it was shown in the case of organic/Si heterojunctions.49,50 Yu et al.50 observed the formation of a strong inversion layer near the Si surface in organic-Si nanowire hybrid solar cells, which converts the Schottky contact into a p–n junction resulting in a highly efficient cell. The same effect has recently been proposed for graphene/silicon photodiodes.41,42 However, in the present case, we not only induce an inversion layer in Si underneath thick SiO2 at reverse biases as low as −2 V, using atomically thin graphene, but also visualize it in present SPC measurements in graphene based photodiodes. This can be attributed to the atomic thinness and transparency of graphene acting as a contact material, which enables the observation of photocurrent generation underneath it.

As is well-known from metal oxide semiconductor field effect transistors, the formation of the inversion layer is a bias dependent phenomenon and a stronger inversion layer is formed when thinner insulators are employed.43 In order to confirm this experimentally, we fabricated G/n-Si photodiodes with two different SiO2 thicknesses of 85 and 40 nm. Figure 5a and b show JV characteristics under white light illumination of both photodiodes in semilogarithmic and linear scale, respectively. We note a slight saturation in dark current and a notable photocurrent in these diodes in the forward direction. These discrepancies may have their origins in the low contact quality, as revealed by the IV characteristics of the metal-Si contacts (Figure S3). Nevertheless, below the threshold, the two photodetectors are dominated by the (identical) G/n-Si Schottky diode regions and behave very similarly. However, a distinctively larger photocurrent is observed for the diode with 40 nm thick oxide once the threshold voltage for the inversion layer is reached, because the carrier density in the gated region of this diode is higher for a given VR (compare simulation results in Figure S4). The present findings clearly demonstrate that the gated region of G/Si photodiodes contribute significantly to measured photocurrents in such hybrid photodiodes.

Figure 5.

Figure 5

JV comparison of graphene/n-Si photodiode with two different SiO2 thicknesses of 85 and 40 nm on (a) semilogarithmic and (b) linear scale in the dark and under illumination. The inset shows zoom-in for reverse bias voltage.

In conclusion, we have revealed through scanning photocurrent measurements that the photocurrent in graphene-based hybrid photodiodes is generated not only in the G-Si Schottky barrier region, but also very efficiently in the adjacent G-SiO2–Si (GIS) region, where it strongly depends on the applied reverse bias voltage. It is found that the photocurrent rises sharply by about 1 order of magnitude in the GIS region above a certain threshold bias voltage, regardless of the incident laser power. We also investigated the effect of oxide thickness on the photocurrent and observed a larger photocurrent for the device with thinner oxide. The observations are explained through simulations by the formation of an inversion layer in Si under the SiO2. This inversion layer not only provides a low resistance path for the minority charge carries, but also acts as a passivation for the surface states in SiO2, thereby enhancing the photocurrent by efficient collection of the charge carriers. The present findings establish the fundamental mechanisms of photocurrent generation in graphene based hybrid optoelectronic devices and may also provide guidelines for designing hybrid photodetectors based on the combination of two- and three-dimensional materials.

Methods

Device Fabrication

A lightly doped n-Si wafer with a thermally grown silicon dioxide (SiO2) layer of 85 nm was used as a substrate. The n-Si wafers were phosphorus-doped with a doping concentration of 2 × 1015 cm–3. For chip fabrication, the wafer was diced into 13 × 13 mm2 samples. Eight photodiodes were fabricated on each chip. The oxide was etched with buffered oxide etchant (BOE) after a first standard UV-photolithography step in order to expose the n-Si substrate. The contact metal electrodes were defined by a second photolithography step followed by sputtering of 20 nm of chromium (Cr) and 80 nm of gold (Au) and liftoff process. The metal electrodes were deposited immediately after the native oxide removal ensuring to form good ohmic contacts. Large-area graphene was grown on a copper foil in a NanoCVD (Moorfield, U.K.) rapid thermal processing tool. To transfer graphene films onto prepatterned substrates, ∼ 1 cm2 pieces of graphene-coated Cu foil were spin-coated with Poly methyl methacrylate (PMMA) and baked on a hot plate at 85 °C for 5 min. Electrochemical delamination has been used to remove the polymer-supported graphene films from the copper surface.14 In order to make a good electrical contact between graphene and n-Si substrate, the native silicon oxide on the n-Si substrates was removed by BOE prior to the graphene transfer. Afterward, the devices were thoroughly immersed into acetone for 3 h, followed by cleaning them with isopropanol and DI water and drying. At the end, a last photolithography step was performed followed by oxygen plasma etching of graphene in order to define graphene junction areas.

Electrical Characterization

Electrical measurements on the diodes were made with a Karl Süss probe station connected to a Keithley semiconductor analyzer (SCS4200) under ambient condition. The voltage for all devices was swept from 0 to +3 V for forward (VF) and from 0 to −3 V for reverse (VR) biasing. A white light source (50 W halogen lamp) with a dimmer to control the light intensity was used to quickly check that the fabricated diodes are working properly and that they are generally sensitive to light. The intensity of the light source was measured by a CA 2 laboratory thermopile.

Optical Characterization

The spectral response (SR) of the photodetectors was measured using a lock-in technique by comparing it to the calibrated reference detectors. A tungsten-halogen lamp (wavelength ranging between 300 and 2200 nm) was used as a light source. Specific wavelengths were selected by a monochromator. The intensity of the light beam was modulated by a chopper with a frequency of 17 Hz. Calibrated Si and indium–gallium arsenide (InGaAs) diodes were used as reference detectors. The photodetectors’ currents were measured by preamplifiers (FEMTO) and lock-in amplifiers at chopper frequency of 17 Hz for detection of ultralow currents down to 10 pA. For the responsivity calculation, the measurement principle allows to establish a wavelength dependent correction factor. This correction factor takes into account variations of the preamplifiers, varying photo flux densities caused by the monochromator as well as the area difference between the reference detector and the sample.

Scanning Photocurrent Measurements

Scanning photocurrent measurements were performed using a Witec Alpha300 R confocal microscope equipped with a piezoelectric scanning stage. The microscope was coupled to a 532 nm wavelength to generate spatially resolved photocurrent, which is converted into a voltage signal using a current preamplifier and is recorded by a lock-in amplifier. The samples to be investigated were mounted on a custom-made sample holder on a PCB.

Simulations

For the simulation of the G/Si Schottky diode and the GIS junction we have solved the 1-D Poisson equation considering a Si substrate with an n-type doping of 2 × 1015 cm–3 and a 85 nm thermally grown SiO2 layer on top of it. The use of a 1D model is justified by the dimensions of the device under study, which is of the order of hundreds of μm. In the case of the G/Si junction, the extension of the depletion region is below 2 μm for VR = −2 V and even smaller for the G/SiO2/Si junction. For MIS structures, the gradual-channel approximation is typically employed,43 and the 1D-Poisson equation provides a good description of its electrostatic behavior. We have considered that the initial graphene is p-type with an estimated carrier concentration of p0 = 3.5 × 1012 cm–2. The origin of this charge is thought to be due to charge puddles produced during the graphene transfer onto SiO2.51 This intrinsic doping shifts the Fermi level (EF) below the Dirac point (ED) a value

graphic file with name ph-2017-002857_m001.jpg

where ℏ is the reduced Planck’s constant and vF = 1.1 × 106 m/s is the Fermi velocity of graphene. The values obtained from this calculation provide a good agreement with the experimental ones, such as the Schottky barrier height. The charges located in the semiconductor, both depletion and inversion, are positive as it corresponds to ionized donor impurities and holes, respectively. For the case of the G/Si Schottky diode, we consider only the depletion charge, and for the GIS junction, we also include the inversion charge.

An equal and opposite charge is induced in the graphene layer, causing an additional Fermi level shift relative to the Dirac point as a function of the applied reverse bias. This additional shift will be opposite to the one produced by the intrinsic charge in the graphene and it can be calculated once the charge in the semiconductor is estimated as a function of the potential in the substrate. Thus, a self-consistent calculation52 is mandatory and it will provide us information about the depletion width, surface potential, depletion and inversion charge, and conduction and valence band values as a function of the applied bias.

Acknowledgments

We would like to thank Dr. Chanyoung Yim (University of Siegen) for fruitful discussions. Funding from the European Research Council (ERC, InteGraDe, 3017311), the German Research Foundation (DFG LE 2440/1-2 and GRK 1564), European regional funds (HEA2D, EFRE-0800149), and the Spanish Ministry of Education, Culture and Sport (Salvador de Madariaga Program, PRX16/00205) are gratefully acknowledged.

Supporting Information Available

The Supporting Information is available free of charge on the ACS Publications website at DOI: 10.1021/acsphotonics.7b00285.

  • Figures S1–S4 (PDF).

The authors declare no competing financial interest.

Supplementary Material

ph7b00285_si_001.pdf (429.1KB, pdf)

References

  1. Bonaccorso F.; Sun Z.; Hasan T.; Ferrari A. C. Graphene Photonics and Optoelectronics. Nat. Photonics 2010, 4, 611–622. 10.1038/nphoton.2010.186. [DOI] [Google Scholar]
  2. Ferrari A. C.; Bonaccorso F.; Fal’ko V.; Novoselov K. S.; Roche S.; Bøggild P.; Borini S.; Koppens F. H. L.; Palermo V.; Pugno N.; et al. Science and Technology Roadmap for Graphene, Related Two-Dimensional Crystals, and Hybrid Systems. Nanoscale 2015, 7, 4598–4810. 10.1039/C4NR01600A. [DOI] [PubMed] [Google Scholar]
  3. Koppens F. H. L.; Chang D. E.; García de Abajo F. J. Graphene Plasmonics: A Platform for Strong Light–Matter Interactions. Nano Lett. 2011, 11, 3370–3377. 10.1021/nl201771h. [DOI] [PubMed] [Google Scholar]
  4. Grigorenko A. N.; Polini M.; Novoselov K. S. Graphene Plasmonics. Nat. Photonics 2012, 6, 749–758. 10.1038/nphoton.2012.262. [DOI] [Google Scholar]
  5. Koppens F. H. L.; Mueller T.; Avouris P.; Ferrari A. C.; Vitiello M. S.; Polini M. Photodetectors Based on Graphene, Other Two-Dimensional Materials and Hybrid Systems. Nat. Nanotechnol. 2014, 9, 780–793. 10.1038/nnano.2014.215. [DOI] [PubMed] [Google Scholar]
  6. Dawlaty J. M.; Shivaraman S.; Strait J.; George P.; Chandrashekhar M.; Rana F.; Spencer M. G.; Veksler D.; Chen Y. Measurement of the Optical Absorption Spectra of Epitaxial Graphene from Terahertz to Visible. Appl. Phys. Lett. 2008, 93, 131905. 10.1063/1.2990753. [DOI] [Google Scholar]
  7. Nair R. R.; Blake P.; Grigorenko A. N.; Novoselov K. S.; Booth T. J.; Stauber T.; Peres N. M. R.; Geim A. K. Fine Structure Constant Defines Visual Transparency of Graphene. Science 2008, 320, 1308–1308. 10.1126/science.1156965. [DOI] [PubMed] [Google Scholar]
  8. Kuzmenko A. B.; van Heumen E.; Carbone F.; van der Marel D. Universal Optical Conductance of Graphite. Phys. Rev. Lett. 2008, 100, 117401. 10.1103/PhysRevLett.100.117401. [DOI] [PubMed] [Google Scholar]
  9. Mueller T.; Xia F.; Avouris P. Graphene Photodetectors for High-Speed Optical Communications. Nat. Photonics 2010, 4, 297–301. 10.1038/nphoton.2010.40. [DOI] [Google Scholar]
  10. Xia F.; Mueller T.; Lin Y.; Valdes-Garcia A.; Avouris P. Ultrafast Graphene Photodetector. Nat. Nanotechnol. 2009, 4, 839–843. 10.1038/nnano.2009.292. [DOI] [PubMed] [Google Scholar]
  11. Sun Z.; Hasan T.; Torrisi F.; Popa D.; Privitera G.; Wang F.; Bonaccorso F.; Basko D. M.; Ferrari A. C. Graphene Mode-Locked Ultrafast Laser. ACS Nano 2010, 4, 803–810. 10.1021/nn901703e. [DOI] [PubMed] [Google Scholar]
  12. Gan X.; Shiue R.-J.; Gao Y.; Meric I.; Heinz T. F.; Shepard K.; Hone J.; Assefa S.; Englund D. Chip-Integrated Ultrafast Graphene Photodetector with High Responsivity. Nat. Photonics 2013, 7, 883–887. 10.1038/nphoton.2013.253. [DOI] [Google Scholar]
  13. Pospischil A.; Humer M.; Furchi M. M.; Bachmann D.; Guider R.; Fromherz T.; Mueller T. CMOS-Compatible Graphene Photodetector Covering All Optical Communication Bands. Nat. Photonics 2013, 7, 892–896. 10.1038/nphoton.2013.240. [DOI] [Google Scholar]
  14. Kataria S.; Wagner S.; Ruhkopf J.; Gahoi A.; Pandey H.; Bornemann R.; Vaziri S.; Smith A. D.; Ostling M.; Lemme M. C. Chemical Vapor Deposited Graphene: From Synthesis to Applications. Phys. Status Solidi A 2014, 211, 2439–2449. 10.1002/pssa.201400049. [DOI] [Google Scholar]
  15. Xu X.; Gabor N. M.; Alden J. S.; van der Zande A. M.; McEuen P. L. Photo-Thermoelectric Effect at a Graphene Interface Junction. Nano Lett. 2010, 10, 562–566. 10.1021/nl903451y. [DOI] [PubMed] [Google Scholar]
  16. Lemme M. C.; Koppens F. H. L.; Falk A. L.; Rudner M. S.; Park H.; Levitov L. S.; Marcus C. M. Gate-Activated Photoresponse in a Graphene P–n Junction. Nano Lett. 2011, 11, 4134–4137. 10.1021/nl2019068. [DOI] [PubMed] [Google Scholar]
  17. Urich A.; Unterrainer K.; Mueller T. Intrinsic Response Time of Graphene Photodetectors. Nano Lett. 2011, 11, 2804–2808. 10.1021/nl2011388. [DOI] [PMC free article] [PubMed] [Google Scholar]
  18. Gabor N. M.; Song J. C. W.; Ma Q.; Nair N. L.; Taychatanapat T.; Watanabe K.; Taniguchi T.; Levitov L. S.; Jarillo-Herrero P. Hot Carrier–Assisted Intrinsic Photoresponse in Graphene. Science 2011, 334, 648–652. 10.1126/science.1211384. [DOI] [PubMed] [Google Scholar]
  19. Sun D.; Aivazian G.; Jones A. M.; Ross J. S.; Yao W.; Cobden D.; Xu X. Ultrafast Hot-Carrier-Dominated Photocurrent in Graphene. Nat. Nanotechnol. 2012, 7, 114–118. 10.1038/nnano.2011.243. [DOI] [PubMed] [Google Scholar]
  20. Liu C.-H.; Dissanayake N. M.; Lee S.; Lee K.; Zhong Z. Evidence for Extraction of Photoexcited Hot Carriers from Graphene. ACS Nano 2012, 6, 7172–7176. 10.1021/nn302227r. [DOI] [PubMed] [Google Scholar]
  21. Park J.; Ahn Y. H.; Ruiz-Vargas C. Imaging of Photocurrent Generation and Collection in Single-Layer Graphene. Nano Lett. 2009, 9, 1742–1746. 10.1021/nl8029493. [DOI] [PubMed] [Google Scholar]
  22. Echtermeyer T. J.; Britnell L.; Jasnos P. K.; Lombardo A.; Gorbachev R. V.; Grigorenko A. N.; Geim A. K.; Ferrari A. C.; Novoselov K. S. Strong Plasmonic Enhancement of Photovoltage in Graphene. Nat. Commun. 2011, 2, 458. 10.1038/ncomms1464. [DOI] [PubMed] [Google Scholar]
  23. Fang Z.; Liu Z.; Wang Y.; Ajayan P. M.; Nordlander P.; Halas N. J. Graphene-Antenna Sandwich Photodetector. Nano Lett. 2012, 12, 3808–3813. 10.1021/nl301774e. [DOI] [PubMed] [Google Scholar]
  24. Engel M.; Steiner M.; Lombardo A.; Ferrari A. C.; Löhneysen H. v; Avouris P.; Krupke R. Lightmatter Interaction in a Microcavity Controlled Graphene Transistor. Nat. Commun. 2012, 3, 906. 10.1038/ncomms1911. [DOI] [PMC free article] [PubMed] [Google Scholar]
  25. Furchi M.; Urich A.; Pospischil A.; Lilley G.; Unterrainer K.; Detz H.; Klang P.; Andrews A. M.; Schrenk W.; Strasser G.; et al. Microcavity-Integrated Graphene Photodetector. Nano Lett. 2012, 12, 2773–2777. 10.1021/nl204512x. [DOI] [PMC free article] [PubMed] [Google Scholar]
  26. Konstantatos G.; Badioli M.; Gaudreau L.; Osmond J.; Bernechea M.; de Arquer F. P. G.; Gatti F.; Koppens F. H. L. Hybrid Graphene-Quantum Dot Phototransistors with Ultrahigh Gain. Nat. Nanotechnol. 2012, 7, 363–368. 10.1038/nnano.2012.60. [DOI] [PubMed] [Google Scholar]
  27. Schall D.; Neumaier D.; Mohsin M.; Chmielak B.; Bolten J.; Porschatis C.; Prinzen A.; Matheisen C.; Kuebart W.; Junginger B.; et al. 50 GBit/s Photodetectors Based on Wafer-Scale Graphene for Integrated Silicon Photonic Communication Systems. ACS Photonics 2014, 1, 781–784. 10.1021/ph5001605. [DOI] [Google Scholar]
  28. Li X.; Zhu H.; Wang K.; Cao A.; Wei J.; Li C.; Jia Y.; Li Z.; Li X.; Wu D. Graphene-On-Silicon Schottky Junction Solar Cells. Adv. Mater. 2010, 22, 2743–2748. 10.1002/adma.200904383. [DOI] [PubMed] [Google Scholar]
  29. Kim H.-Y.; Lee K.; McEvoy N.; Yim C.; Duesberg G. S. Chemically Modulated Graphene Diodes. Nano Lett. 2013, 13, 2182–2188. 10.1021/nl400674k. [DOI] [PMC free article] [PubMed] [Google Scholar]
  30. Bablich A.; Kataria S.; Lemme M. C. Graphene and Two-Dimensional Materials for Optoelectronic Applications. Electronics 2016, 5, 13. 10.3390/electronics5010013. [DOI] [Google Scholar]
  31. An X.; Liu F.; Jung Y. J.; Kar S. Tunable Graphene–Silicon Heterojunctions for Ultrasensitive Photodetection. Nano Lett. 2013, 13, 909–916. 10.1021/nl303682j. [DOI] [PubMed] [Google Scholar]
  32. Li X.; Zhu M.; Du M.; Lv Z.; Zhang L.; Li Y.; Yang Y.; Yang T.; Li X.; Wang K. High Detectivity Graphene-Silicon Heterojunction Photodetector. Small 2016, 12, 595. 10.1002/smll.201502336. [DOI] [PubMed] [Google Scholar]
  33. Riazimehr S.; Bablich A.; Schneider D.; Kataria S.; Passi V.; Yim C.; Duesberg G. S.; Lemme M. C. Spectral Sensitivity of Graphene/silicon Heterojunction Photodetectors. Solid-State Electron. 2016, 115 (Part B), 207–212. 10.1016/j.sse.2015.08.023. [DOI] [Google Scholar]
  34. Lv P.; Zhang X.; Zhang X.; Deng W.; Jie J. High-Sensitivity and Fast-Response Graphene/Crystalline Silicon Schottky Junction-Based Near-IR Photodetectors. IEEE Electron Device Lett. 2013, 34, 1337–1339. 10.1109/LED.2013.2275169. [DOI] [Google Scholar]
  35. Wang X.; Cheng Z.; Xu K.; Tsang H. K.; Xu J.-B. High-Responsivity Graphene/silicon-Heterostructure Waveguide Photodetectors. Nat. Photonics 2013, 7, 888–891. 10.1038/nphoton.2013.241. [DOI] [Google Scholar]
  36. Chen Z.; Cheng Z.; Wang J.; Wan X.; Shu C.; Tsang H. K.; Ho H. P.; Xu J.-B. High Responsivity, Broadband, and Fast Graphene/Silicon Photodetector in Photoconductor Mode. Adv. Opt. Mater. 2015, 3, 1207–1214. 10.1002/adom.201500127. [DOI] [Google Scholar]
  37. Srisonphan S. Hybrid Graphene–Si-Based Nanoscale Vacuum Field Effect Phototransistors. ACS Photonics 2016, 3, 1799–1808. 10.1021/acsphotonics.6b00610. [DOI] [Google Scholar]
  38. Di Bartolomeo A. Graphene Schottky Diodes: An Experimental Review of the Rectifying Graphene/semiconductor Heterojunction. Phys. Rep. 2016, 606, 1–58. 10.1016/j.physrep.2015.10.003. [DOI] [Google Scholar]
  39. Moench W. Explanation of the Barrier Heights of Graphene Schottky Contacts by the MIGS-and-Electronegativity Concept. J. Appl. Phys. 2016, 120, 104501. 10.1063/1.4962310. [DOI] [Google Scholar]
  40. Liu F.; Kar S. Quantum Carrier Reinvestment-Induced Ultrahigh and Broadband Photocurrent Responses in Graphene-Silicon Junctions. ACS Nano 2014, 8, 10270–10279. 10.1021/nn503484s. [DOI] [PubMed] [Google Scholar]
  41. Di Bartolomeo A.; Luongo G.; Giubileo F.; Funicello N.; Niu G.; Schroeder T.; Lisker M.; Lupina G.. Hybrid Graphene/Silicon Schottky Photodiode with Intrinsic Gating Effect. 2D Mater. 2017.4025075. 10.1088/2053-1583/aa6aa0 [DOI] [Google Scholar]
  42. Bartolomeo A. D.; Giubileo F.; Luongo G.; Iemmo L.; Martucciello N.; Niu G.; Fraschke Mirko; Skibitzki O.; Schroeder T.; Lupina G. Tunable Schottky Barrier and High Responsivity in graphene/Si-Nanotip Optoelectronic Device. 2D Mater. 2017, 4, 015024. 10.1088/2053-1583/4/1/015024. [DOI] [Google Scholar]
  43. Simon M. Sze; Kwok K. Ng.. Physics of Semiconductor Devices, 3rd ed.; Wiley, 2006. [Google Scholar]
  44. Cheung S. K.; Cheung N. W. Extraction of Schottky Diode Parameters from Forward Current-voltage Characteristics. Appl. Phys. Lett. 1986, 49, 85–87. 10.1063/1.97359. [DOI] [Google Scholar]
  45. Limmer T.; Feldmann J.; Da Como E. Carrier Lifetime in Exfoliated Few-Layer Graphene Determined from Intersubband Optical Transitions. Phys. Rev. Lett. 2013, 110, 217406. 10.1103/PhysRevLett.110.217406. [DOI] [PubMed] [Google Scholar]
  46. Green M. A.; Blakers A. W. Advantages of Metal-Insulator-Semiconductor Structures for Silicon Solar Cells. Sol. Cells 1983, 8, 3–16. 10.1016/0379-6787(83)90036-4. [DOI] [Google Scholar]
  47. Godfrey R. B.; Green M. A. A 15% Efficient Silicon MIS Solar Cell. Appl. Phys. Lett. 1978, 33, 637–639. 10.1063/1.90446. [DOI] [Google Scholar]
  48. Erickson A. S.; Kedem N. K.; Haj-Yahia A. E.; Cahen D. Aluminum Oxide–n-Si Field Effect Inversion Layer Solar Cells with Organic Top Contact. Appl. Phys. Lett. 2012, 101, 233901. 10.1063/1.4769041. [DOI] [Google Scholar]
  49. Liu Y.; Zhang Z.; Xia Z.; Zhang J.; Liu Y.; Liang F.; Li Y.; Song T.; Yu X.; Lee S.; et al. High Performance Nanostructured Silicon–Organic Quasi P–n Junction Solar Cells via Low-Temperature Deposited Hole and Electron Selective Layer. ACS Nano 2016, 10, 704–712. 10.1021/acsnano.5b05732. [DOI] [PubMed] [Google Scholar]
  50. Yu X.; Shen X.; Mu X.; Zhang J.; Sun B.; Zeng L.; Yang L.; Wu Y.; He H.; Yang D. High Efficiency Organic/Silicon-Nanowire Hybrid Solar Cells: Significance of Strong Inversion Layer. Sci. Rep. 2015, 5, 17371. 10.1038/srep17371. [DOI] [PMC free article] [PubMed] [Google Scholar]
  51. Deshpande A.; Bao W.; Miao F.; Lau C. N.; LeRoy B. J. Spatially Resolved Spectroscopy of Monolayer Graphene on SiO2. Phys. Rev. B: Condens. Matter Mater. Phys. 2009, 79, 205411. 10.1103/PhysRevB.79.205411. [DOI] [Google Scholar]
  52. An Y.; Behnam A.; Pop E.; Ural A. Metal-Semiconductor-Metal Photodetectors Based on Graphene/p-Type Silicon Schottky Junctions. Appl. Phys. Lett. 2013, 102, 013110. 10.1063/1.4773992. [DOI] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Supplementary Materials

ph7b00285_si_001.pdf (429.1KB, pdf)