Second Generation Needling Techniques for the Treatment of Chondral Defects in Animal Model

Abstract

Purpose  To compare the macroscopic, histological, and immunohistochemical characteristics of the repair tissue of chondral defects treated with microfracture and nanofracture in an ovine model.

Methods  Full-thickness chondral lesions were created in the medial femoral condyle of both knees in four adult sheep and were treated with microfracture on one side and with nanofracture on the contralateral side. Chondral repair was assessed after 12 months by macroscopic, histological, and immunohistochemical analyses.

Results  Histological cartilage repair significantly improved in the samples treated with nanofracture for cellular morphological characteristics and cartilage architecture. The immunohistochemical analysis showed a significantly higher immunoreactivity to type II collagen in the defects treated with nanofracture.

Conclusion  Nanofracture provided better repair tissue than microfracture, with a more satisfactory cartilage architecture renovation and tissue having greater type II collagen content.

Clinical Relevance  Mesenchymal stem cell stimulation is the most frequently used primary cartilage repair procedure. Nanofracture represents a novel technique to stimulate bone marrow that results into a successful repair of chondral defects.

Introduction

Although almost 60 years have passed since the description of the first bone marrow stimulation technique by Smillie, 1 the treatment of chondral lesions so far represents a relevant and challenging issue. Despite the fact that along the years and especially in the recent past several treatments and novel biomaterials have been proposed, none of the different methods available has been able to renovate the joint surface from both the biological and biomechanical standpoint. 2 The microfracture technique developed by Steadman still represents the most frequently used procedure. 3 Approximately 80,000 microfracture procedures are performed every year in the United States. 4 5 The biological rationale of bone marrow stimulation is attributed to the role of mesenchymal stem cells (MSCs) recruited from the bone marrow. 6 7 8 9 10 11 The advantages of this technique include its minimal invasiveness, favorable cost-effectiveness ratio, and low technical demands. Satisfactory results are being achieved especially in young patients with defects of limited size. 8 12 13 However, the quality and characteristics of the newly formed fibrocartilaginous tissue have been widely discussed in the literature 14 15 due to the limited biomechanical properties of the tissue rich in type I collagen and due to its tendency to degenerate.

In recent years, improved knowledge and understanding of the structural and functional architecture of subchondral bone has led to an increased focus on the need to preserve its integrity during chondral defect treatment.

The limited penetration and the broad diameter of the awl 16 are currently thought to play a key role in repairing fibrocartilaginous tissue, as well as in subchondral bone compaction around the perforation 9 16 17 and in intralesional osteophytes formation. 9 18 To overcome the mechanical limitations of microfracture, the nanofracture technique was recently introduced using smaller diameter and deeper subchondral bone needle perforations (Arthrosurface Inc., Franklin, Massachusetts, United States). 9

The aim of this study was to assess macroscopic, histological, and immunohistochemical characteristics of repair tissue of chondral defects treated with microfractures or nanofractures in an ovine model. The hypothesis of the study was that nanofracture provides better repair tissue than microfracture.

Methods

The local ethic committee approved this study, and all procedures were conducted according to the Institutional Animal Care regulations, which conformed to the National Institutes of Health Guidelines on the Care of Laboratory Animals.

Four adult Sardinian ewes, aged 5.5 years, weighing approximately 45 kg, were used in the study. All animals were examined and found to be in good health.

Surgery was performed under sterile conditions and with sheep under general anesthesia. All sheep were intubated after the administration of thiopentone (25 mg/kg) and ventilated with O ₂ in N ₂ O by volume control. Anesthesia was maintained with 1.5 to 2% of isoflurane; a bolus dose of 0.1 mg of fentanyl was given before surgery.

A medial parapatellar arthrotomy was performed on the right and left stifle of all animals. Incision was performed to expose the medial femoral condyle in both hind legs. An 8-mm-diameter (area: 50.3 mm ² ), full-thickness chondral lesion in the load-bearing area of each medial femoral condyle was created using an arthroscopic burr. The calcified cartilage layer was removed; vertical walls were created at the periphery of the cartilage lesion. The defects were then treated with microfracture on one side and nanofracture on the contralateral side. Each cartilage lesion was treated with five bone channels. The distance between each channel was 3 mm according to previous recommendations. 7 Microfracture sites were treated using an awl manufactured by a curved Steadman awl. The perforation depth was user-controlled with visual feedback from the awl tip. Nanofracture sites were treated using a cannulated awl and a 1-mm-thick Nitinol needle (NanoFx, Arthrosurface Inc). The 9-mm perforation depth of the needle was controlled by the awl ( Fig. 1 ). The surgical technique was previously described. 9

Fig. 1.

( A ) Treatment of the defect with microfracture. ( B ) Treatment of the defect with nanofracture.

Upon completion of the cartilage repair procedures, all incisions were closed in layers according to standard surgical practice. Postoperatively, the animals were kept in stalls with limited movement and weight-bearing. Animals were then left free to roam in their fencings without any immobilization of the operated limb. Full weight-bearing was allowed as tolerated, and no specific exercise regimen was adopted. General health and weight-bearing status were monitored by a veterinary during recovery.

Immediately after euthanasia, the defects were photographed to allow assessment by two blinded observers. Macroscopic evaluation was assessed based on the International Cartilage Repair Society (ICRS) evaluation score ( Table 1 ).

Table 1. International Cartilage Repair Society macroscopic evaluation of cartilage repair.

Categories	Score
Degree of defect repair
In level with surrounding cartilage	4
75% repair of defect depth	3
50% repair of defect depth	2
25% repair of defect depth	1
0% repair of defect depth	0
Integration to border zone
Complete integration with surrounding cartilage	4
Demarcating border < 1 mm	3
¾ of graft integrated, ¼ with a notable border > 1 mm width	2
½ of graft integrated with surrounding cartilage, ½ with a notable border > 1 mm	1
From no contact to ¼ of graft integrated with surrounding cartilage	0
Macroscopic appearance
Intact smooth surface	4
Fibrillated surface	3
Small, scattered fissures or cracs	2
Several, small or few but large fissures	1
Total degeneration of grafted area	0
Overall repair assessment
Grade I: normal	12
Grade II: nearly normal	11–8
Grade III: abnormal	7–4
Grade IV: severely abnormal	3–1

Condylar articular defects containing regenerated tissue, adjacent host cartilage, and subchondral bone were harvested using a water-cooled circular saw. The tissue blocks were fixed in 10% neutral-buffered formalin for 4 days and then placed in a decalcification solution for 4 to 10 days. After washing in running tap water for 4 to 8 hours to remove all traces of decalcification solution, the osteochondral specimens were paraffin-embedded and 4-μ sections were stained with safranin orange/fast green (Safranin O) and hematoxylin and eosin as previously described. 19

For the immunohistochemical analysis, we used the avidin–biotin complex and peroxidase. The immunohistochemical determination of type I and type II collagen contents was conducted on paraffin-embedded sections using an automatic immunostainer (Ventana BenchMark ULTRA, Roche Diagnostics, Basel, Switzerland), with a ready-to-use dilution of a monoclonal mouse antitype I or antitype II collagen immunoglobulin (ThermoFisher Scientific, Waltham, Massachusetts, United States). The reaction was displayed by the Ultraview DAB kit (Ventana Medical System, Roche Diagnostics), a revelation system kit including the secondary antimouse antibody biotinylated, the enzymatic substrate, and the chromogen DAB.

Immunoreactivity to type I collagen in the repair tissue was compared with that of the adjacent subchondral bone, serving as positive internal control (0 = no immunoreactivity; 1 = significantly weaker; 2 = moderately weaker; 3 = similar; 4 = stronger immunoreactivity).

Results

Macroscopic Evaluation

Macroscopic evaluations conducted according to the ICRS evaluation score on chondral defects treated with microfracture technique showed a partial filling of the defect by a thin healing tissue; the latter showed characteristics similar to the healthy cartilage almost exclusively on the peripheral areas of the lesion ( Fig. 2 ). Conversely, macroscopic evaluations performed on condyles treated by using the nanofracture technique showed an almost complete covering of the defect by a newly formed tissue, resulting more similar to the native cartilage in the whole chondral defect. Furthermore, the repair tissue showed a higher integration with the surrounding cartilage and lack of fibrillation and fissures on the majority of the surface ( Fig. 3 ).

Fig. 2.

Macroscopic appearance of a defect treated with microfracture technique 12 months after surgery. Partial filling of the defect by a thin healing tissue can be observed.

Fig. 3.

Macroscopic appearance of a defect treated with nanofracture technique 12 months after surgery. The defect is almost completely covered by a newly formed tissue that is similar to the native cartilage. Furthermore, the repair tissue shows a good integration with the surrounding cartilage and lack of fibrillation and fissures on the majority of the surface.

Histological and Immunohistochemical Evaluation

Histological evaluation on samples treated using the microfracture technique showed a partial filling of the defect by fibrocartilaginous tissue formed by rounded cells similar to chondrocytes submerged into a fibrous extracellular matrix. The repair tissue did not show the normal structure consisting of cartilage layers and was characterized by an almost complete lack of tidemark and a severe alteration of the subchondral bone architecture ( Fig. 4 ).

Fig. 4.

Histological evaluation of a defect treated with microfracture technique 12 months after surgery. Repair tissue does not show the normal structure consisting of cartilage layers and is characterized by an almost complete lack of tidemark and a severe alteration of the subchondral bone architecture.

On the other hand, the histological evaluation of samples treated with the nanofracture technique highlighted a more satisfactory defect filling and a better structural cartilage architecture into the lesion. The newly formed tissue showed the same features as a fibrohyaline repair tissue in which small groups of rounded cellular elements clustered and diffusely distributed could be observed ( Fig. 5 ).

Fig. 5.

Histological evaluation of a defect treated with nanofracture technique 12 months after surgery. Satisfactory defect filling and restoration of the structural cartilage architecture can be observed.

Immunofluorescence showed a scarce positivity for type II collagen in defects treated with microfractures ( Fig. 6 ) compared with defects treated by with nanofractures. In the latter group, the repair tissue presented a strong positivity for type II collagen, visible especially around the perforations ( Fig. 7 ).

Fig. 6.

Immunohistochemical evaluation of a defect treated with microfracture technique 12 months after surgery. The defect is filled with fibrocartilage tissue, with poor immunofluorescence positivity for type II collagen.

Fig. 7.

Immunohistochemical evaluation of a defect treated with nanofracture technique 12 months after surgery. ( A ) The defect is completely filled by fibrohyaline repair tissue strongly positive to immunohistochemistry for type II collagen. ( B ) Strong positivity in correspondence of the channels can be observed. ( C ) Clones of regenerating chondrocytes are present around the area that correspond to increased collagen type II synthesis.

Discussion

The main finding of this study is that small-diameter needle perforation into full-thickness chondral defects significantly improves repair in a preclinical animal model at 12 months postoperatively compared with large drill holes.

Since the first use proposed by Steadman in the 1980s, microfracture has become the treatment of choice for the management of chondral lesions. 3 The technique is based on direct stimulation of MSCs of the subchondral bone, which have a high potential for differentiation into various connective tissues, including cartilage, bone, tendon, and ligaments. 20 21 The regenerative effects of MSCs achieve their objective in promoting tissue repair and the resolution of inflammation through direct cell-to-cell interaction or by secretion of bioactive components. 22 23 Several studies confirmed the efficacy of the microfracture technique, with improved clinical outcomes in 70 to 90% of patients. 7 8 13 24 25 26 However, the formation of fibrocartilage tissue and the deterioration of clinical results over time represent important limitations, 27 28 29 30 and alternative procedures for the management of chondral lesions have been advocated. 14 15

The use of standard microfracture awls is no longer supported by recent basic science evidence. 17 31 32

Eldracher et al conducted a study on an animal model aiming at evaluating through macroscopic, histological, immunohistochemical, and microcomputed tomography analysis the repair of chondral defects treated by a perforation diameter of either 1 or 1.8 m. Results were definitely better in defects treated with smaller diameter holes, repair tissue having greater content in type II collagen and showing an architecture more similar to normal. 33

Orth et al recently published their comparative results treating 8 × 4-mm full-thickness defects in the weight-bearing area of ovine knees. The study used two custom-made awls with a diameter of either 1 or 1.2 mm. The perforation depth was stop controlled at 5 mm; the distal tips were trihedral. The authors reported a significant improvement in the overall histological score using small diameter awls. In addition, the histological surface regularity was significantly improved by smaller instruments. 32

Chen et al published several studies evaluating the histological characteristics of the newly formed tissue after treatment of chondral defects with different reparative techniques and various degrees of penetration into the subchondral bone. 17 31 34 Histological and histomorphometric evaluations showed that the best access to bone marrow was observed when drilling to greater depths, thereby improving defect fill and production of cartilage with a higher hyaline content. 25 A further study by the same group showed that treatment with microfracture is associated with fragmentation and compaction around the trabecular canals. 17

Our study confirmed previous results, showing beneficial subchondral effects using small diameter needle perforation. While Orth et al 32 chose a 5-mm perforation depth using custom instruments, we used clinically available instrumentation for nanofracture involving the use of a 1-mm-thick needle inserted into a cannulated awl that creates stop-controlled 9-mm-deep perforations. This technique was compared with microfracture using the standard conically shaped tip.

In accordance with different studies published in the literature, our work highlights how chondral defects repair obtained with reduced diameter perforations and with a higher penetration into the subchondral bone is associated with the formation of tissue having histological and immunohistological characteristics more similar to the native cartilage compared with standard microfracture. Better results obtained with nanofracture might be explained by a lower fragmentation and trabecular compaction around the perforations, leading to a better communication between those and the surrounding trabecular channels. These canals allow for the immediate on-site formation of a superclot, resulting in improved recruitment of multipotent MSCs.

Overall, inference of an animal study is limited because functional status cannot be assessed at baseline and follow-up evaluations. However, the animal model used in this study is considered suitable for cartilage defect testing. Limitations due to small cohort size should also be considered.

Finally, no biomechanical analysis of the newly formed tissue was performed.

In conclusion, nanofracture represents a novel technique for bone marrow stimulation based on smaller diameter and deeper perforations, resulting into a more satisfactory chondral repair compared with methods based on perforation of larger diameter and lower depth.