. 2016 Jul 1;5(7):e16120. doi: 10.1038/lsa.2016.120

Supra-(carbon nanodots) with a strong visible to near-infrared absorption band and efficient photothermal conversion

Di Li 1, Dong Han 1, Song-Nan Qu 1,*, Lei Liu 1, Peng-Tao Jing 1, Ding Zhou 1, Wen-Yu Ji 1, Xiao-Yun Wang 2, Tong-Fei Zhang 2, De-Zhen Shen 1
PMCID: PMC6059947  PMID: 30167175

Abstract

A novel concept and approach to engineering carbon nanodots (CNDs) were explored to overcome the limited light absorption of CNDs in low-energy spectral regions. In this work, we constructed a novel type of supra-CND by the assembly of surface charge-confined CNDs through possible electrostatic interactions and hydrogen bonding. The resulting supra-CNDs are the first to feature a strong, well-defined absorption band in the visible to near-infrared (NIR) range and to exhibit effective NIR photothermal conversion performance with high photothermal conversion efficiency in excess of 50%.

Keywords: assembly, carbon nanodots, NIR photothermal conversion, supra-(carbon nanodots), visible to NIR absorption band

Introduction

As an emerging branch of carbon-based nanomaterials, carbon nanodots (CNDs) have inspired intensive research efforts because of their attractive merits1, 2, 3. Their outstanding optical properties (optical brightness, resistance to photobleaching and excitation/size-dependent emission), dispersibility in water, low toxicity, excellent biocompatibility and low cost make CNDs promising candidates for the advancement of biological applications4, 5, 6, 7, 8, 9. Recently, even more attractive photophysical properties have been exploited using CNDs/inorganic nanomaterials or CNDs/organic molecule composites rather than single-particle CNDs. For example, Tang et al. reported efficient solar-driven interfacial charge transfer between nitrogen-doped CNDs and TiO2 in the ultraviolet (UV) to blue regions10; Liu et al. used CNDs as photosensitizers and catalysts in CND–carbon nitride (C3N4) nanocomposites for visible overall water splitting11. Strauss et al. constructed self-assembling electron donor–acceptor hybrids from CNDs and perylenediimides derivates12. Recently, our group developed smart supra-CNDs from amphipathic CNDs through amphipathic interactions with on/off luminescence induced by the dissociation/formation of a self-assembled system. This strategy opens up a new pathway for CNDs engineering using nanoparticle interactions and assembly13. We believe that the construction of supra-CNDs from CND assemblies through interparticle interactions represents a new method to achieve novel photophysical properties.

The main absorption bands of CNDs are typically located in the UV, blue or green regions14, 15, 16, 17, which limit their applications in longer wavelength regions. To the best of our knowledge, the previous methods used to modulate CNDs’ absorbance mainly relied on surface passivation, heteroatom doping and dimensional modification15, 18, 19, 20, 21, 22, which are ineffective in the red and near-infrared (NIR) spectral regions. Therefore, exploring new concepts for CNDs engineering is of great scientific interest to tailor their features for desirable light-absorbing applications. In the present work, a novel type of supra-CND with a strong visible to NIR absorption band and efficient NIR photothermal conversion (up to 50%) were constructed by the assembly of hydrothermally produced CNDs through possible electrostatic interactions and hydrogen bonding. The inhomogeneous surface-confined charges and surface functional groups of the CNDs contribute to the formation and optical properties of the supra-CNDs, and as a result, an intense and well-defined absorption band was realized in the visible–NIR range, which has not been reported in CND systems previously. The good photothermal properties, high dispersibility in water and low toxicity make this type of supra-CND potential candidates for future biomedical applications.

Materials and methods

General information

Citric acid and urea were purchased from Beijing Chemical Corp, Beijing, China. Graphene oxides (GOs) were purchased from XF NANO, INC, Nanjing, Jiangsu province, China. All chemicals were used as received without further purification. The water used in all experiments was purified with a Milli-Q system (Millipore Corporation, Billerica, MA, USA). High-resolution transmission electron microscopy (HRTEM) was performed on a FEI Tecnai-G2-F20 TEM at 200 kV. Atomic force microscopy (AFM) images were captured on a Multimode 8 (Bruker Corporation, Santa Barbara, CA, USA) in tapping mode under ambient conditions. Fluorescence emission spectra were collected on a Shimadzu F7000 spectrophotometer (Shimadzu Corporation, Kyoto, Japan). Photoluminescence quantum yields were obtained in a calibrated integrating sphere using a FLS920 spectrometer (Edinburgh Instruments, UK). Optical absorption spectra were recorded on a Shimadzu UV-3101PC spectrophotometer. Raman spectra were measured with a Renishaw Raman system model 1000 spectrometer at 633 nm. Infrared (IR) spectra of the samples in pressed KBr pellets were recorded with a Bruker IFS66v Fourier-transform infrared (FT-IR) spectrometer equipped with a deuterated triglycine sulfate detector (32 scans) at a resolution of 4 cm−1. X-ray photoelectron spectroscopy (XPS) was performed with an ESCALAB MK II X-ray photoelectron spectrometer using Mg as the excitation source.

Synthesis of supra-CNDs

The supra-CNDs were prepared by post-treatment of CNDs synthesized via a hydrothermal procedure, as previously reported17, 23. Specifically, citric acid (3 g) and urea (6 g) were reacted at 160 °C for 4 h under hydrothermal conditions. The freshly obtained solution was freeze-dried, and the resulting yellow CND solids were further washed in ethanol to remove the unreacted materials for purification. The CNDs were stable in dry atmosphere but unstable in solution and humid air. The yellow CNDs were placed in humid air (60% humidity), and their color gradually changed from yellow to entirely black within several days (7 days at 60% humidity). The black powders could be dispersed in water, and further purification via dialysis and freeze-drying gave the dark-blue supra-CNDs. Supra-CNDs also formed spontaneously with time from concentrated aqueous solutions of CNDs (300 mg ml−1 for 12 h) at room temperature, and the conversion of CNDs to supra-CNDs was less efficient than that in the solid state in humid air.

Results and discussion

Because of the observed color changes, optical absorption and fluorescence spectra were collected first. Figure 1d shows that in addition to the absorption peak centered at 356 nm, supra-CNDs exhibited a well-defined strong absorption band at 700 nm, covering the visible to NIR spectral range of 470–1000 nm (full width at half maximum=201 nm). Because of the influence of scattering effects on the extinction determination, we performed synchronous scanning in an integrating sphere to examine the absolute absorption of an aqueous dispersion of supra-CNDs. As shown in Supplementary Fig. S1, two characteristic absorption bands in the UV and visible–NIR regions were observed, consistent with those in the absorption spectrum, indicating that scattering effects were insignificant in the extinction determination. In contrast, CNDs exhibited a single absorption band in the UV region centered at 340 nm. The change in absorption corresponded to the color change from CNDs to supra-CNDs. Optical images of the CNDs and supra-CNDs in the solid state and in solution are presented in Figure 1a and 1b. In the optical images and fluorescence spectra (Figure 1c and 1e), CNDs showed intense blue emission (λem=443 nm) with a quantum efficiency of 35.56% excited at 340 nm, whereas supra-CNDs were hardly emissive. To the best of our knowledge, this is the first report of supra-CNDs exhibiting a significant absorption band in the visible to NIR spectral range. These attractive optical properties inspired us to study the structural and photophysical properties of supra-CNDs.

Figure 1.

Figure 1

Open in a new tab

Optical images of CNDs (left) and supra-CNDs (right), (a) in the solid state, (b) in solution and (c) under UV irradiation; (d) the absorption spectra (normalized at the absorption maxima in the UV region) of CND and supra-CND, and (e) the fluorescence spectra of CND and supra-CND (0.28 mg ml−1) excited at 340 nm.

To gain insight into the structural features of supra-CNDs, microscopy was conducted, and the results obtained for supra-CNDs and CNDs were compared. In the AFM images (Figure 2a–2f), the heights of the CNDs were homogeneously distributed in the range of 1–5 nm, whereas supra-CNDs exhibited increased heights in the range of 5–25 nm. The mean heights were 2.76 nm for CNDs and 12.34 nm for supra-CNDs. The larger sizes and inhomogeneous structures (Supplementary Fig. S2) of supra-CNDs indicated that assembly of smaller CNDs might occur during the color-changing process. HRTEM revealed the presence of a crystalline graphite phase in both CNDs and supra-CNDs (Figure 2g and 2h, Supplementary Fig. S3). Notably, the crystalline CNDs possessed well-resolved uniform lattice fringes (d100=0.21 nm)22, 24 throughout the particles, whereas in the circled parts of Figure 2h, supra-CNDs showed non-uniform lattice fringes (d100=0.21 nm) that were adjacently located. Therefore, the supra-CNDs were composed of CND assemblies. Overall, the AFM and HRTEM characterizations confirmed that single CNDs assembled to form supra-CNDs.

Figure 2.

Figure 2

Open in a new tab

(a) AFM image, (b) height profile along the line in the AFM image, (c) height distribution and (g) HRTEM image of CNDs; (d) AFM image, (e) height profile along the line in the AFM image, (f) height distribution and (h) HRTEM image of supra-CNDs.

Despite their color changes in solution and the solid state, CNDs are stable when frozen and when the surrounding H2O molecules exist in the form of ice. These results suggest that liquid water or H2O molecules in humid air can increase the motion and rotational freedom of single CNDs in the solution or condensed state, thereby inducing the assembly of CNDs into supra-CNDs. Therefore, the key effect of water or humid air is making the ‘frozen’ CNDs ‘free’ to assemble into supra-CNDs. In other words, water molecules function as the medium for CND assembly.

The Raman spectrum of the supra-CNDs (Figure 3a) exhibited two broad peaks of the D band (disordered, sp3) and G band (graphitized, sp2) at approximately 1338 and 1555 cm−1, respectively, and the relative intensity of the D band and G band (ID/IG=0.87) indicated that supra-CNDs possessed a relatively high carbon-lattice-structure content25. In the XPS spectra (Figure 3c–3f), carbon, nitrogen and oxygen elements were detected as C=C (284.6 eV), C−N/C−O (285.6 eV), C=N/C=O (287.2 eV) and O−C=O (288.8 eV) for carbon; C−N−C (399.8 eV), N−(C)3 (400.1 eV) and N−H (401.6 eV) for nitrogen; and C=O (531.6 eV) and C−OH/C−O−C (533.0 eV) for oxygen20, 24, 26. The FT-IR spectrum of supra-CNDs (Figure 3b) exhibited the characteristic absorption bands of ν(O−H)/ν(N−H) (3100−3500 cm−1), ν(C=O)/δ(N−H)/ν(C=N) (1550−1750 cm−1) and δ(C−H)/ν(C−N) (1330−1480 cm−1)25, 26, 27. Combining the XPS and FT-IR spectra, we inferred the existence of functional groups, such as amino, carboxyl and aromatic CN heterocycles, in the supra-CNDs that originated from the CNDs.

Figure 3.

Figure 3

Open in a new tab

(a) Raman, (b) IR, (c) XPS survey, (d) C1s, (e) N1s and (f) O1s spectra of supra-CND solids.

To further explore the driving force of CND assembly and the origin of the strong visible to NIR absorption band of supra-CNDs, luminescence quenching experiments with both electron acceptors and donors were conducted with the CNDs to probe their electronic nature. For the oxidative/reductive quenching experiments, the luminescence intensity of a CND dispersion was quantitatively quenched by adding increasing amounts of either the electron acceptor (2,4-dinitrotoluene) or the electron donor (p-phenylenediamine), and the Stern-Volmer constants were calculated to be 283.3 M−1 for 2,4-dinitrotoluene and 177.6 M−1 for p-phenylenediamine (Supplementary Fig. S4). Therefore, the CNDs were excellent electron donors and electron acceptors because of the presence of surface-confined electrons and holes. The CNDs exhibited inhomogeneous surface-confined charges because of inhomogeneous particle surface sites, as demonstrated above and in the literatures12, 28, 29, 30, which might lead to electronic instability, induce assembly via possible electrostatic interactions and quench their luminescence. The assembly was further confirmed by the time-dependent absorption spectra of aqueous dispersions of CNDs. We measured the optical absorbance of aqueous dispersions of CNDs at four concentrations (10, 50, 100 and 300 mg ml−1; Figure 4a and Supplementary Fig. S5) and observed the gradual emergence of a visible–NIR absorption band (500−900 nm) after the CNDs were dispersed in water. In Figure 4b, the mass-extinction coefficient at the visible–NIR absorption maximum is shown to increase with time and the CND concentration of the dispersion; as the concentration increased, the mass-extinction coefficient of the red-shifted absorption peaks grew more rapidly. The concentration-dependent visible–NIR absorbance indicated that long-wavelength photon-induced electron transition could only occur in CND assemblies.

Figure 4.

Figure 4

Open in a new tab

(a) Time-dependent absorption spectra of CNDs at a concentration of 300 mg ml−1 in a 1-mm quartz cell and (b) time-dependent mass-extinction coefficients of aqueous dispersions of CNDs with increasing concentrations measured at the absorption maxima of 593 nm for 10 mg ml−1, 605 nm for 50 mg ml−1, 630 nm for 100 mg ml−1 and 653 nm for 300 mg ml−1.

As shown in Supplementary Fig. S6, the existence of C=C (284.6 eV), C−N/C−O (285.6 eV), C=N/C=O (287.2 eV) and O−C=O (288.5 eV) for carbon; C−N−C (399.2 eV), N−(C)3 (399.8 eV) and N−H (401.1 eV) for nitrogen; and C=O (531.5 eV) and C−OH/C−O−C (533.0 eV) for oxygen in the CNDs was confirmed by XPS. Given that the IR spectrum (Supplementary Fig. S8) featured the characteristic absorption bands of ν(O−H)/ν(N−H) (3100−3500 cm−1), ν(C=O)/δ(N−H)/ν(C=N) (1550−1750 cm−1) and δ(C−H)/ν(C−N) (1330−1480 cm−1), we proposed the existence of amino, carboxyl and pyridinic nitrogen groups in the CNDs. Considering the electropositive nature of amino groups and the electronegative nature of carboxyl and pyridinic nitrogen groups, the electropositive and negative centers were located on the amino groups and carboxyl/pyridinic nitrogen groups, respectively, at different surface sites on the CNDs. To illustrate the possible electronic structure of the CNDs and their assembly process, an arbitrarily defined single-sheet CND geometry was proposed based on the probable incorporation mode of urea with amino groups on one side and carboxyl/pyridinic nitrogen on the other side of the sheet, as shown in Supplementary Fig. S7. Adjacent CNDs are supposed to assemble via possible interparticle electrostatic interactions and hydrogen bonding between the amino groups as positive charge centers and the carboxyl/pyridinic groups as negative charge centers. The IR spectra reveal that the characteristic absorption peaks of C=N, C=O and amino groups shifted to smaller wavenumbers in the supra-CNDs relative to the CNDs, indicating the formation of interparticle hydrogen bonds (Supplementary Fig. S8)31. These possible interparticle electrostatic interactions and hydrogen bonding could stabilize the assemblies and support the formation of supra-CNDs.

Density functional theory calculations were performed based on the proposed CND geometry, as illustrated in Figure 5a–5c32,33,34,35. Compared with the undoped sp2 carbon segments (highest occupied molecular orbital (HOMO) at 0 eV and lowest unoccupied molecular orbital (LUMO) at 2.82 eV), the incorporation of positive/negative surface groups barely changed the energy gap between the HOMO and LUMO of the CNDs (HOMO at −0.11 eV and LUMO at 2.68 eV) but evoked additional trap-state energy levels on the surface defined as the a level at 0.31 eV above the HOMO and d level at 0.44 eV below the LUMO in a single CND sheet. However, electron transition from the a level to the d level is almost forbidden because of the spatial separation of their charge density distributions. This might explain the non-absorbance of CNDs in the visible to NIR regions. In the assembly of CNDs, the respective a and d energy levels of different CNDs can overlap spatially. Therefore, the electron transitions from the a level to the d level are permitted in the CND assemblies and correspond to the visible–NIR absorption of the CND assemblies. Nevertheless, the spatial arrangement of adjacent sheets in a single CND is restricted and might make the electron transitions from the a to d levels in adjacent sheets in the same CND unfavorable and ineffective compared with those between different CNDs, which can assemble in favorable spatial conformations. Thus, electron transitions might occur from the a to d energy levels in adjacent sheets of the same CND, but their proportion might be not sufficient to influence the NIR absorption. Based on the above discussion, a possible model was established to elucidate the assembly and NIR absorption principle of supra-CNDs and is presented in Figure 6. Driven by possible electrostatic interactions and hydrogen bonding between the charge-confined surfaces, CNDs tend to assemble to form supra-CNDs in any possible three-dimensional spatial arrangement. Characteristic visible–NIR absorption originates from the electron transitions through the coupled energy levels in the CND assemblies, which could be enhanced by increased assembly degrees in highly concentrated systems. Herein, we processed CNDs in the solid state in humid air and found that the H2O molecules in air enable CNDs to assemble in highly concentrated systems, which is important to achieve the strong visible–NIR absorption in supra-CNDs. However, we cannot confirm whether H2O molecules are absorbed in the as-produced supra-CNDs because of the uncertainty of the exact CND composition. Considering the trap-state energy levels on the CND surfaces before assembly, energy level coupling and electron transition should be dominated by the intrinsic electronic properties of the CNDs and the assembled structures; therefore, we ignore the incorporation of H2O molecules in the theoretical calculation.

Figure 5.

Figure 5

Open in a new tab

(a) The calculated energy levels of a single CND sheet and a single CND sheet with surface groups. The surface group-related levels are indicated by blue and red lines, respectively. (b) The charge density distributions of the HOMO and LUMO levels in the CND sheet. (c) The charge density distributions of the HOMO, LUMO and surface group-related levels in the CND sheet with surface groups. The energy of the HOMO level of the CND sheet is defined as 0 eV. The colored isosurface of the charge density is 0.001e Å−3.

Figure 6.

Figure 6

Open in a new tab

Schematic representations of the structure, energy alignment, absorption principle and photothermal effect in supra-CNDs. The blue horizontal bars, yellow horizontal bars, red jagged lines and red wavy lines represent the a level, d level, NIR laser irradiation and heat origins from the nonradiative deactivation of the NIR-induced electrons on the d level, respectively.

The NIR photothermal effects of nanomaterials with photon-to-thermal energy conversion under skin-penetrating NIR irradiation have become a research focus because of their potential applications in cancer therapy and photoacoustic imaging36, 37. Carbon nanomaterials have wide spectral absorption because of their zero or narrow bandgap properties. Given the requirements of practical applications, abundant and varied surface modifications have been performed on carbon nanomaterials to improve their solubility and NIR absorption. The as-prepared supra-CNDs are composed of surface charge-confined CNDs, and their strong visible–NIR absorptions are attributed to the interparticle electron transitions between the trap-state energy levels on the surface. The photophysical mechanism of the enhanced visible–NIR absorption in supra-CNDs differs from those of carbon nanotubes or C60. Their small particle sizes and efficient NIR photothermal conversion allow supra-CNDs to be directly used as photothermal agents without further modification. Very recently, Ge et al. reported red luminescent CNDs with a photothermal conversion efficiency of 38.5% under 671-nm laser irradiation at a power density of 2 W cm−2, indicating the applicability of CNDs in thermal theranostics24. However, these CNDs exhibit a weak absorption tail in the NIR region. Because of supra-CNDs’ strong absorption in the NIR region, it was easy for us to investigate their NIR photothermal properties. In marked contrast to pure water, the aqueous dispersion of supra-CNDs showed a clear concentration- and laser power density-dependent temperature increase under irradiation with a 732-nm laser. As shown in Figure 7a and 7b and Supplementary Table S1, the temperature of the supra-CND aqueous dispersions increased by 19.8 to 35.2 °C in 10 min under 1- W cm−2 irradiation with a 732-nm laser as the concentration increased from 25 to 200 ppm and by 16.1 to 55.5 °C in 10 min when 100-ppm dispersions were irradiated with a 732-nm laser as the power density increased from 0.5 to 2 W cm−2. The temperature elevation of the supra-CNDs dispersion surpassed that of GOs and CNDs measured under the same conditions because of their high mass-extinction coefficients in the NIR region (18.6 l g−1 cm−1 for supra-CND, 1.4 l g−1 cm−1 for GO and 0 l g−1 cm−1 for CND) at 732 nm (Figure 7c). The photothermal conversion efficiency of supra-CNDs was calculated to be 52% (100-ppm supra-CNDs dispersion under 0.5-W cm−2 irradiation with 732 nm), which is among the highest values reported for NIR nanoheaters38. Although the absorbance at 808 nm was not as high as that at 732 nm, supra-CNDs exhibited effective photothermal conversion under 808-nm laser irradiation, which can achieve deeper optical penetration depths in biological tissues39. The temperature elevations were 9.6 to 35.2 °C for the supra-CD-NIR aqueous dispersions with concentrations of 25−200 ppm (Supplementary Table S1), and the photothermal conversion efficiency was 53.2% (100 ppm, 1-W cm−2 irradiation at 808 nm, Figure 7d and Supplementary Fig. S9)40, 41. At this stage, the mechanism of the high NIR photothermal conversion in supra-CNDs was not clear. Based on the above results, we propose that the good NIR photothermal performance of supra-CNDs originated from the nonradiative deactivation of the NIR-induced electrons on the d level by recombination with the holes on the a level, as illustrated in Figure 6 and Supplementary Fig. S10. For most carbon-based nanomaterials, enhancing the NIR absorbance improves the photothermal conversion performance by increasing the harvesting of the NIR photons. For example, Su et al. and Robinson et al. reported that porphyrin-functionalized GO and ultrasmall reduced GO exhibited enhanced NIR absorbance relative to GO and proved that high NIR absorbance contributes to efficient photothermal conversion42, 43. Thus, we propose that this mechanism should also work in supra-CNDs based on their carbonaceous composition, strong NIR absorption and high photothermal conversion efficiency. In contrast to the reported carbon nanomaterials, the enhanced visible–NIR absorption in supra-CNDs is attributable to the interparticle electron transitions between the trap-state energy levels on the surfaces and provides a new strategy for carbon nanomaterial engineering. Considering the potential biomedical applications of supra-CNDs in photothermal therapy and photoacoustic imaging, their cytotoxicity was assessed in HeLa cells using the 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay and various concentrations of supra-CNDs. The cellular viability exceeded 85% after 24 h of incubation in the presence of supra-CNDs at concentrations as high as 400 ppm, which confirmed that the supra-CNDs possess low cytotoxicity (Supplementary Fig. S11) and can be applied in biological systems.

Figure 7.

Figure 7

Open in a new tab

Photothermal profile of supra-CNDs. Temperature elevations of (a) supra-CND aqueous dispersions with different concentrations under 732-nm laser irradiation (1 W cm−2) compared with pure water, (b) supra-CND aqueous dispersions (100 ppm) under 732-nm irradiation with increasing laser power densities, (c) supra-CND, GO and CND aqueous dispersions (100 ppm) under 732-nm laser irradiation (1 W cm−2) and (d) supra-CND aqueous dispersions with different concentrations under 808-nm laser irradiation (1 W cm−2) compared with pure water. All experiments were conducted at room temperature.

Conclusions

In conclusion, supra-CNDs possessing remarkable absorption in the visible–NIR spectral range (470–1000 nm) were constructed by assembling CNDs. The inhomogeneous surface-confined charges and surface functional groups on the CNDs were proposed to be responsible for the assembly driving force, including possible electrostatic interactions and hydrogen bonds, which facilitated the generation of supra-CNDs and gave rise to strong visible–NIR absorption. The supra-CNDs exhibited good NIR photothermal performance with high photothermal conversion efficiency, and thus, they are promising photothermal agents for biomedical applications. Our present work is important because it not only resulted in a new type of carbon-based NIR-absorbing nanoheater but it is also a novel concept and route for CND photophysical engineering. Further research on the photophysical mechanism and biomedical applications of supra-CNDs is in progress.

Acknowledgments

This work was supported by the National Science Foundation of China (No. 11204298, 61205025, 61274126 and 61306081), the Jilin Province Science and Technology Research Project (No. 20140101060JC, 20150519003JH and 20130522142JH), and the Outstanding Young Scientist Program of CAS. SQ and DS conceived and designed the materials and experiments. DL performed the material synthesis and characterizations. DH and LL conducted the theoretical calculations. PJ, WJ and DZ participated in the photophysical characterization. XW and TZ evaluated the cytotoxicity. All authors contributed to the manuscript.

Footnotes

Note: Supplementary Information for this article can be found on the Light: Science & Applications' website(http://www.nature.com/lsa).

The authors declare no conflict of interest.

Supplementary Material

Supplementary Information
Click here for additional data file. (6.8MB, doc)

References

  1. Li XM, Rui MC, Song JZ, Shen ZH, Zeng HB. Carbon and graphene quantum dots for optoelectronic and energy devices: a review. Adv Funct Mater 2015; 25: 4929–4947. [Google Scholar]
  2. Baker SN, Baker GA. Luminescent carbon nanodots: emergent nanolights. Angew Chem Int Ed Engl 2010; 49: 6726–6744. [DOI] [PubMed] [Google Scholar]
  3. Hola K, Zhang Y, Wang Y, Giannelis EP, Zboril R et al. Carbon dots—emerging light emitters for bioimaging, cancer therapy and optoelectronics. Nano Today 2014; 9: 590–603. [Google Scholar]
  4. Ding CQ, Zhu AW, Tian Y. Functional surface engineering of C-dots for fluorescent biosensing and in vivo bioimaging. Acc Chem Res 2014; 47: 20–30. [DOI] [PubMed] [Google Scholar]
  5. Kong B, Zhu AW, Ding CQ, Zhao XM, Li B et al. Carbon dot-based inorganic–organic nanosystem for two-photon imaging and biosensing of pH variation in living cells and tissues. Adv Mater 2012; 24: 5844–5848. [DOI] [PubMed] [Google Scholar]
  6. Huang P, Lin J, Wang XS, Wang Z, Zhang CL et al. Light-triggered theranostics based on photosensitizer-conjugated carbon dots for simultaneous enhanced-fluorescence imaging and photodynamic therapy. Adv Mater 2012; 24: 5104–5110. [DOI] [PMC free article] [PubMed] [Google Scholar]
  7. Zheng M, Liu S, Li J, Qu D, Zhao HF et al. Integrating oxaliplatin with highly luminescent carbon dots: an unprecedented theranostic agent for personalized medicine. Adv Mater 2014; 26: 3554–3560. [DOI] [PubMed] [Google Scholar]
  8. Tang J, Kong B, Wu H, Xu M, Wang YC et al. Carbon nanodots featuring efficient FRET for real-time monitoring of drug delivery and two-photon imaging. Adv Mater 2013; 25: 6569–6574. [DOI] [PubMed] [Google Scholar]
  9. Qu D, Zheng M, Li J, Xie ZG, Sun ZC. Tailoring color emissions from N-doped graphene quantum dots for bioimaging applications. Light Sci Appl 2015; 4: e364, doi:10.1038/lsa.2015.137. [Google Scholar]
  10. Tang J, Zhang YY, Kong B, Wang YC, Da PM et al. Solar-driven photoelectrochemical probing of nanodot/nanowire/cell interface. Nano Lett 2014; 14: 2702–2708. [DOI] [PubMed] [Google Scholar]
  11. Liu J, Liu Y, Liu NY, Han YZ, Zhang X et al. Metal-free efficient photocatalyst for stable visible water splitting via a two-electron pathway. Science 2015; 347: 970–974. [DOI] [PubMed] [Google Scholar]
  12. Strauss V, Margraf JT, Dirian K, Syrgiannis Z, Prato M et al. Carbon nanodots: supramolecular electron donor–acceptor hybrids featuring perylenediimides. Angew Chem Int Ed Engl 2015; 54: 8292–8297. [DOI] [PubMed] [Google Scholar]
  13. Lou Q, Qu SN, Jing PT, Ji WY, Li D et al. Water-triggered luminescent “nano-bombs” based on supra-(carbon nanodots). Adv Mater 2015; 27: 1389–1394. [DOI] [PubMed] [Google Scholar]
  14. Sun MY, Qu SN, Ji WY, Jing PT, Li D et al. Towards efficient photoinduced charge separation in carbon nanodots and TiO2 composites in the visible region. Phys Chem Chem Phys 2015; 17: 7966–7971. [DOI] [PubMed] [Google Scholar]
  15. Wang X, Cao L, Yang ST, Lu FS, Meziani MJ et al. Bandgap-like strong fluorescence in functionalized carbon nanoparticles. Angew Chem Int Ed Engl 2010; 122: 5438–5442. [DOI] [PMC free article] [PubMed] [Google Scholar]
  16. Anilkumar P, Cao L, Yu JJ, Tackett KN, Wang P et al. Crosslinked carbon dots as ultra-bright fluorescence probes. Small 2013; 9: 545–551. [DOI] [PubMed] [Google Scholar]
  17. Li XM, Zhang SL, Kulinich SA, Liu YL, Zeng HB. Engineering surface states of carbon dots to achieve controllable luminescence for solid-luminescent composites and sensitive Be2+ detection. Sci Rep 2014; 4: 4976. [Google Scholar]
  18. Tang LB, Ji RB, Li XM, Bai GX, Liu CP et al. Deep ultraviolet to near-infrared emission and photoresponse in layered N-doped graphene quantum dots. ACS Nano 2014; 8: 6312–6320. [DOI] [PubMed] [Google Scholar]
  19. Ge JC, Lan MH, Zhou BJ, Liu WM, Guo L et al. A graphene quantum dot photodynamic therapy agent with high singlet oxygen generation. Nat Commun 2014; 5: 4596. [DOI] [PMC free article] [PubMed] [Google Scholar]
  20. Qu SN, Liu XY, Guo XY, Chu MH, Zhang LG et al. Amplified spontaneous green emission and lasing emission from carbon nanoparticles. Adv Funct Mater 2014; 24: 2689–2695. [Google Scholar]
  21. Peng H, Travas-Sejdic J. Simple aqueous solution route to luminescent carbogenic dots from carbohydrates. Chem Mater 2009; 21: 5563–5565. [Google Scholar]
  22. Dong YQ, Pang HC, Yang HB, Guo CX, Shao JW et al. Carbon-based dots co-doped with nitrogen and sulfur for high quantum yield and excitation-independent emission. Angew Chem Int Ed Engl 2013; 52: 7800–7804. [DOI] [PubMed] [Google Scholar]
  23. Qu D, Zheng M, Du P, Zhou Y, Zhang LG et al. Highly luminescent S, N co-doped graphene quantum dots with broad visible absorption bands for visible light photocatalysts. Nanoscale 2013; 5: 12272–12277. [DOI] [PubMed] [Google Scholar]
  24. Ge JC, Jia QY, Liu WM, Guo L, Liu QY et al. Red-emissive carbon dots for fluorescent, photoacoustic, and thermal theranostics in living mice. Adv Mater 2015; 27: 4169–4177. [DOI] [PubMed] [Google Scholar]
  25. Qu SN, Wang XY, Lu QP, Liu XY, Wang LJ. A biocompatible fluorescent ink based on water-soluble luminescent carbon nanodots. Angew Chem Int Ed Engl 2012; 51: 12215–12218. [DOI] [PubMed] [Google Scholar]
  26. Liu S, Tian JQ, Wang L, Zhang YW, Qin XY et al. Hydrothermal treatment of grass: a low-cost, green route to nitrogen-doped, carbon-rich, photoluminescent polymer nanodots as an effective fluorescent sensing platform for label-free detection of Cu(II) ions. Adv Mater 2012; 24: 2037–2041. [DOI] [PubMed] [Google Scholar]
  27. Zhu SJ, Meng QN, Wang L, Zhang JH, Song YB et al. Highly photoluminescent carbon dots for multicolor patterning, sensors, and bioimaging. Angew Chem Int Ed Engl 2013; 52: 3953–3957. [DOI] [PubMed] [Google Scholar]
  28. Wang X, Cao L, Lu FS, Meziani MJ, Li HT et al. Photoinduced electron transfers with carbon dots. Chem Commun 2009; 25: 3774–3776. [DOI] [PMC free article] [PubMed] [Google Scholar]
  29. Strauss V, Margraf JT, Dolle C, Butz B, Nacken TJ et al. Carbon nanodots: toward a comprehensive understanding of their photoluminescence. J Am Chem Soc 2014; 136: 17308–17316. [DOI] [PubMed] [Google Scholar]
  30. Cao L, Sahu S, Anilkumar P, Bunker CE, Xu J et al. Carbon nanoparticles as visible-light photocatalysts for efficient CO2 conversion and beyond. J Am Chem Soc 2011; 133: 4754–4757. [DOI] [PubMed] [Google Scholar]
  31. Joseph J, Jemmis ED. Red-, blue-, or no-shift in hydrogen bonds: a unified explanation. J Am Chem Soc 2007; 129: 4620–4632. [DOI] [PubMed] [Google Scholar]
  32. Kresse G, Furthmüller J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput Mater Sci 1996; 6: 15–50. [DOI] [PubMed] [Google Scholar]
  33. Perdew JP, Burke K, Ernzerhof M. Generalized gradient approximation made simple. Phys Rev Lett 1996; 77: 3865–3868. [DOI] [PubMed] [Google Scholar]
  34. Blöchl PE. Projector augmented-wave method. Phys Rev B 1994; 50: 17953–17979. [DOI] [PubMed] [Google Scholar]
  35. Eda G, Lin YY, Mattevi C, Yamaguchi H, Chen HA et al. Blue photoluminescence from chemically derived graphene oxide. Adv Mater 2010; 22: 505–509. [DOI] [PubMed] [Google Scholar]
  36. Vogel A, Venugopalan V. Mechanisms of pulsed laser ablation of biological tissues. Chem Rev 2003; 103: 577–644. [DOI] [PubMed] [Google Scholar]
  37. Cheng L, Wang C, Feng LZ, Yang K, Liu Z. Functional nanomaterials for phototherapies of cancer. Chem Rev 2014; 114: 10869–10939. [DOI] [PubMed] [Google Scholar]
  38. Li B, Wang Q, Zou RJ, Liu XJ, Xu KB et al. Cu7.2S4 nanocrystals: a novel photothermal agent with a 56.7% photothermal conversion efficiency for photothermal therapy of cancer cells. Nanoscale 2014; 6: 3274–3282. [DOI] [PubMed] [Google Scholar]
  39. Weissleder R. A clearer vision for in vivo imaging. Nat Biotechnol 2001; 19: 316–317. [DOI] [PubMed] [Google Scholar]
  40. Roper DK, Ahn W, Hoepfner M. Microscale heat transfer transduced by surface plasmon resonant gold nanoparticles. J Phys Chem C 2007; 111: 3636–3641. [DOI] [PMC free article] [PubMed] [Google Scholar]
  41. Chen HJ, Shao L, Ming T, Sun ZH, Zhao CM et al. Understanding the photothermal conversion efficiency of gold nanocrystals. Small 2010; 6: 2272–2280. [DOI] [PubMed] [Google Scholar]
  42. Su SH, Wang JL, Wei JH, Martínez-Zaguilán Raul, Qiu JJ et al. Efficient photothermal therapy of brain cancer through porphyrin functionalized graphene oxide. New J Chem 2015; 39: 5743–5749. [Google Scholar]
  43. Robinson JT, Tabakman SM, Liang YY, Wang HL, Casalongue HS et al. Ultrasmall reduced graphene oxide with high near-infrared absorbance for photothermal therapy. J Am Chem Soc 2011; 133: 6825–6831. [DOI] [PubMed] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Supplementary Materials

Supplementary Information
Click here for additional data file. (6.8MB, doc)