Abstract
Gold nanoparticles (Au NPs) were prepared by reducing HAuCl4 with NaBH4. Their average particle sizes could be tuned in the range of 1.7 and 8.2 nm, by adjusting the amount of NaBH4 used during synthesis. The obtained Au NPs (colloids) were then loaded onto a commercial Al2O3 support to prepare Au/Al2O3 catalysts with tunable Au particle sizes. An optimal pH value (5.9) of the Au colloid solution was found to be essential for loading Au NPs onto Al2O3 while avoiding the growth of Au NPs. Au NPs and Au/Al2O3 catalysts were tested in the reduction of p-nitrophenol with NaBH4. Interestingly, the catalytic activity depended on the size of Au NPs, being the highest when the average size was 3.4 nm. Relevant characterization by UV-Vis, TEM, and XRD was conducted.
Keywords: gold catalysts, alumina, p-nitrophenol, nanoparticles, size effect
1. Introduction
Since Haruta and co-workers discovered that small gold nanoparticles (Au NPs) supported on some reducible oxides can be highly active catalysts for CO oxidation [1,2,3], heterogeneous catalysis by gold has attracted much attention [4,5,6]. Gold catalysts have found many applications in inorganic reactions (e.g., the water-gas shift reaction, ozone decomposition, selective oxidation of H2 to H2O2) and organic reactions (e.g., selective oxidation/reduction of organic compounds, carbon-carbon coupling) [5]. In particular, the application of gold catalysts in the synthesis of organic chemicals has been the subject of active research recently [7,8,9,10,11].
Supported gold catalysts were usually prepared by a deposition-precipitation method. Although the size of Au NPs can be kept small via that method, it is still difficult to control the size. Alternatively, Au NPs (colloids) with controllable sizes can be synthesized in a liquid phase, and then deposited onto a solid support [12,13,14,15]. That way, the influence of Au NP sizes on catalytic activity can be studied more conveniently.
In many cases, the catalytic activity increases as the average size of the Au NPs becomes smaller and smaller [16,17,18,19]. However, sometimes there exists an optimal particle size for a catalytic system. For instance, Valden et al. [20] dispersed Au NPs ranging from 1 to 6 nm in size on single-crystalline TiO2 surfaces, and found that the highest activity in CO oxidation was achieved when the Au particle size was between 2 and 4 nm. Laoufi et al. [21] investigated the catalytic activity of Au/TiO2 for CO oxidation, and found that the optimum Au particle size was 2.1 ± 0.3 nm.
Herein, Au NPs with tunable average particle sizes (1.7, 3.4, 5.7, 8.2 nm) were synthesized by reducing HAuCl4 with NaBH4, and then loaded onto a commercial Al2O3 support. The catalytic activities of unsupported Au NPs and Au/Al2O3 catalysts with different Au particle sizes were studied for the reduction of p-nitrophenol with NaBH4. An optimal Au particle size of 3.4 nm was identified.
2. Results and Discussion
2.1. Au NPs with Various Sizes
Au NPs (colloids) were prepared by reducing HAuCl4 (0.06 mmol) with NaBH4 (0.4, 0.5, 1.0, or 1.1 mmol). Figure 1 shows the TEM images of Au NPs synthesized with different amounts of NaBH4. The figure shows that the sizes of Au NPs can be tuned by adjusting the amount of NaBH4 added. For example, Au NPs with an average size of 1.7 nm were obtained when 0.06 mmol HAuCl4 and 0.4 mmol NaBH4 were mixed. On the other hand, the average size of Au NPs increased to 8.2 nm when 0.06 mmol HAuCl4 and 1.1 mmol NaBH4 were mixed. The average size and standard deviation were calculated based on 100 particles for each sample. The particle size distributions are shown in the Supplementary Materials. The size distribution of big Au NPs (8.2 ± 1.0 nm) is relatively wide. We attempted to synthesize the big Au NPs later, and also obtained a relatively wide size distribution (7.5 ± 1.8 nm, see Supplementary Materials).
The growth of gold nanoparticles as the amount of NaBH4 increases is also evident from UV-Vis data. When the amount of NaBH4 was 0.4 mmol, a shoulder band corresponding to small Au NPs appears, as shown in Figure 2a. The size of small Au NPs was estimated by TEM as 1.7 ± 0.3 nm (Figure 1a), and the size distribution was actually 1.1-2.4 nm (Supplementary Information). In the literature, Esumi et al. reported a similar shoulder band for 1.5 nm Au NPs [22]. In contrast, the Au NPs prepared with 1.0 mmol NaNH4 shows a distinctive absorption band centered at 525 nm (Figure 2b), corresponding to relatively bigger Au NPs [23].
2.2. Au/Al2O3 Catalysts
Au/Al2O3 catalysts were prepared by adsorbing Au NPs onto Al2O3 at room temperature. The pH value of the colloid solution has to be adjusted by aqueous HCl below the isoelectric point of Al2O3 (~7.5), to allow for the complete adsorption of Au NPs. We recorded UV-Vis spectra of the supernatant collected after adsorbing Au NPs (5.7 nm) onto the Al2O3 support. The supernatant still exhibited an absorption band centered at 516 nm when the pH value was 8.2 (Figure 2c), indicating the incomplete adsorption of Au NPs onto Al2O3. On the other hand, there was no absorption band corresponding to Au NPs in the supernatant when the pH value was 5.9 (Figure 2d), suggesting the complete loading of Au NPs onto Al2O3. This conclusion was also confirmed by ICP analysis.
The effect of pH adjustment on the size of Au NPs was also investigated. As shown by the UV-Vis data in Figure 3, the absorption band corresponding to Au NPs became sharper and red-shifted as the pH value of the Au colloid solution decreased from 8.2 to 1.9, indicating the growth of Au NPs under very acidic conditions [24].
The particle growth was further confirmed by TEM (Figure 4). The average particle size of Au NPs before the pH adjustment was 5.7 nm. The average particle size was still 5.7 nm when the pH value was adjusted to 5.9 and Au NPs were adsorbed onto Al2O3. In contrast, the average particle size became 8.7 nm when the pH value was 1.9. Therefore, pH 5.9 was chosen to load Au NPs onto Al2O3 in the following preparation. That way, we can load Au NPs onto Al2O3 completely, while keeping their original size.
Au NPs with different average sizes were used to prepare Au/Al2O3 catalysts. The pH value of Au colloid solutions was adjusted to 5.9 in the preparation. As shown in Figure 5, the average sizes of gold nanoparticles supported onto Al2O3 were 2.0, 3.4, 5.7, and 8.7 nm, respectively. Therefore, the Au particle sizes were basically maintained after loading Au NPs onto the Al2O3 support.
Figure 6 illustrates the XRD patterns of Au/Al2O3 catalysts. The peaks corresponding to metallic Au overlapped with the peaks of Al2O3. When the average Au particle size increased from 2.0 nm in Figure 6b to 8.7 nm in Figure 6e, the Au peak at 2θ = 38.26° became visible.
2.3. Catalytic Reduction of p-Nitrophenol
The reduction of p-nitrophenol (4-NP) with NaBH4 was used to evaluate the catalytic activity of Au colloids and supported Au/Al2O3 catalysts. The reduction process was monitored by UV-Vis. In the UV-Vis spectra, the absorption at 384 nm corresponds to 4-NP (the reactant), whereas the absorption at 296 nm corresponds to p-aminophenol (4-AP), the product. No reaction happened in the absence of catalyst (data not shown). Figure 7 illustrate the absorbance changes at 384 and 296 nm in the presence of Au NPs (colloids). The Au NPs were active, evident from the faster drop of the absorbance at 384 nm. Since the amount of NaBH4 was 100 times higher than that required by the stoichiometry, the reaction was pseudo first-order to 4-NP.
Table 1 summarizes the turnover frequency (TOF) of Au NPs with different Au particle sizes. The TOF was defined as in [25,26]. For TOF calculation, the reaction time was 60 seconds. In an earlier report, TOF increased as the particle size decreased [25]. In our current study, the TOF value was the highest when the particle size was 3.4 nm.
Table 1.
Particle size (nm) | Reaction time (s) | Conversion (%) | TOF (moles·g−1·s−1) |
---|---|---|---|
1.7 | 60 | 73.0 | 1.83 × 10−2 |
3.4 | 60 | 82.5 | 2.06 × 10−2 |
5.7 | 60 | 71.3 | 1.78 × 10−2 |
8.2 | 60 | 62.3 | 1.56 × 10−2 |
Figure 8 shows the plots of the Ln (Ct/C0) versus reaction time of 4-NP reduction reaction catalyzed by Au colloids and Au/Al2O3. The linear coefficients were all above 0.99, suggesting that the catalytic reduction of 4-NP follows pseudo first-order kinetics. Figure 9 demonstrates the correlation between the rate constant (obtained from the slopes in Figure 8) and the particle size of Au nanocatalysts. The highest rate constants were observed when the Au particle size was around 3.4 nm. The presence of an optimum Au particle size was also observed in Au/TiO2 catalysts for low temperature CO oxidation [20,21]. The reason why Au NPs smaller than 2 nm were less active is probably due to the deviation of metallic nature of such small Au NPs [20,21]. The reduction of p-nitrophenol requires metallic gold nanoparticles. Alternatively, this could be due to the different structures of the Au NPs as their sizes decrease. This aspect can be studied in more details in the future.
3. Experimental
3.1. Chemicals
All chemicals were used as received. HAuCl4·4H2O (99.999%), NaBH4 (AR), and p-nitrophenol (AR) were purchased from Aladdin Co (Shanghai, China). Polyvinylpyrrolidone (PVP, MW-58000) and aqueous HCl was purchased from Sinopharm Chemical Reagent Co (Shanghai, China). Al2O3 (surface area 350 m2/g, pore volume 0.8 ml/g) was purchased from Shandong Zibo Chemical Co (Shandong, China).
3.2. Catalyst Preparation
3.2.1. Preparation of Au NPs
Au NPs with different sizes were prepared by a reported method [27]. HAuCl4·4H2O (0.06 mmol) and PVP (10.0 mg) were dissolved in deionized water (95.0 g) in a round-bottom flask, followed by stirring for 30 min. Aqueous NaBH4 (5 mL) containing 1.0 mmol NaBH4 was then injected. The color of solution turned to dark red instantly. The solution was further stirred for 1 h to obtain 5.7 nm Au NPs. Au NPs with average sizes of 1.7, 3.4, and 8.2 nm were obtained by adding 0.4, 0.5, and 1.1 mmol NaBH4, respectively.
3.2.2. Preparation of 1.0 wt% Au/Al2O3 Catalysts
Typically, Au NPs (30.0 g) containing 0.018 mmol Au were transferred into a 3-neck round-bottom flask, and then a certain amount of HCl (10%) was added to adjust the pH value of the colloid solution. After that, Al2O3 (0.355 g) was added. The slurry was stirred for 1 h. Au/Al2O3 catalysts were collected by repeated centrifugation and washing.
3.3. Characterization
XRD patterns were collected on a Bruker AXS D8 Advance diffractometer using Cu Kα radiation. TEM and HRTEM images were obtained by a JEOL 2100 transmission electron microscope operated at 200 kV. Before imaging, the samples were dispersed in ethanol by sonication, and a few drops of the dispersion were dropped onto a carbon-coated Cu grid followed by solvent evaporation in air at room temperature. UV-Vis absorption spectra were recorded on a UV-3300 spectrophotometer.
3.4. Catalytic Reduction of p-Nitrophenol with NaBH4
Typically, aqueous p-nitrophenol (50.0 mL, 0.15 mmol p-nitrophenol) and aqueous NaBH4 (50.0 mL, 15.0 mmol NaBH4) were transferred into a 3-neck round-bottom flask. After stirring for several minutes, Au colloids (1.0 mL, 0.10 mg Au NPs) or 1.0 wt% Au/Al2O3 (10.0 mg) was transferred into the flask. The mixture was continuously stirred. Solution (1.0 mL) was sampled at certain intervals, diluted immediately with cold deionized water (9.0 mL, below 5 °C), and measured immediately by an ultraviolet spectrophotometer in the range of 250–500 nm. The absorption of p-nitrophenol was observed at 384 nm, and the absorption of the product p-aminophenol was observed at 296 nm.
4. Conclusions
Au NPs ranging in size from 1.7 to 8.2 nm were synthesized by reducing HAuCl4 with different amounts of NaNH4. The pH value of the colloid solutions was adjusted to 5.9 in order to allow for complete adsorption of Au NPs onto Al2O3 support while keeping the Au particle size intact. Au NPs and Au/Al2O3 catalysts with an average Au particle size of 3.4 nm showed the highest activities in reduction of 4-nitrophenol by NaBH4.
Acknowledgments
D.Y. Hua thanks National Natural Science Foundation (Grant No. 11375091) and Natural Science Foundation of Ningbo (Grant No. 2011A610171) for financial support. S.H. Zhou thanks China Zhejiang Provincial Natural Science Foundation (Grant No. Y4110116) and the Ministry of Science and Technology of China (Grant No. 2012DFA40550) for financial support. Z. Ma acknowledges the financial support by National Natural Science Foundation of China (Grant Nos. 21007011 and 21177028), the Ph.D. Programs Foundation of the Ministry of Education in China (Grant No. 20100071120012), and the Overseas Returnees Start-Up Research Fund of the Ministry of Education in China.
Supplementary Materials
Supplementary materials can be accessed at: http://www.mdpi.com/1420-3049/18/10/12609/s1.
Conflicts of Interest
The authors declare no conflict of interest.
Footnotes
Sample Availability: Samples of the compounds are available from the authors.
References
- 1.Haruta M., Kobayashi T., Sano H., Yamada N. Novel gold catalysts for the oxidation of carbon-monoxide at a temperature far below 0 °C. Chem. Lett. 1987:405–408. [Google Scholar]
- 2.Haruta M., Yamada N., Kobayashi T., Iijima S. Gold catalysts prepared by coprecipitation for low-temperature oxidation of hydrogen and of carbon monoxide. J. Catal. 1989;115:301–309. doi: 10.1016/0021-9517(89)90034-1. [DOI] [Google Scholar]
- 3.Haruta M., Tsubota S., Kobayashi T., Kageyama H., Genet M.J., Delmon B. Low-temperature oxidation of CO over gold supported on TiO2, α-Fe2O3, and Co3O4. J. Catal. 1993;144:175–192. doi: 10.1006/jcat.1993.1322. [DOI] [Google Scholar]
- 4.Hashmi A.S.K. The catalysis gold rush: New claims. Angew. Chem. Int. Ed. 2005;44:6990–6993. doi: 10.1002/anie.200502735. [DOI] [PubMed] [Google Scholar]
- 5.Bond G.C., Louis C., Thompson D.T. Catalysis by Gold. Imperial College Press; London, UK: 2006. [Google Scholar]
- 6.Takei T., Akita K., Nakamura I., Fujitani T., Okumura M., Okazaki K., Huang J.H., Ishida T., Haruta M. Heterogeneous catalysis by gold. Adv. Catal. 2012;55:1–126. doi: 10.1016/B978-0-12-385516-9.00001-6. [DOI] [Google Scholar]
- 7.Della Pina C., Falletta E., Prati L., Rossi M. Selective oxidation using gold. Chem. Soc. Rev. 2008;37:2077–2095. doi: 10.1039/b707319b. [DOI] [PubMed] [Google Scholar]
- 8.Corma A., Garcia H. Supported gold nanoparticles for organic reactions. Chem. Soc. Rev. 2008;37:2096–2126. doi: 10.1039/b707314n. [DOI] [PubMed] [Google Scholar]
- 9.Zhang Y., Cui X.J., Shi F., Deng Y.Q. Nano-gold catalysis in fine chemical synthesis. Chem. Rev. 2012;112:2467–2505. doi: 10.1021/cr200260m. [DOI] [PubMed] [Google Scholar]
- 10.Stratakis M., Garcia H. Catalysis by supported gold nanoparticles: Beyond aerobic oxidative processes. Chem. Rev. 2012;112:4469–4506. doi: 10.1021/cr3000785. [DOI] [PubMed] [Google Scholar]
- 11.Davis S.E., Ide M.S., Davis R.J. Selective oxidation of alcohols and aldehydes over supported metal nanoparticles. Green Chem. 2013;15:17–45. doi: 10.1039/c2gc36441g. [DOI] [Google Scholar]
- 12.Tsubota S., Nakamura T., Tanaka K., Haruta M. Effect of calcination temperature on the catalytic activity of Au colloids mechanically mixed with TiO2 powder for CO oxidation. Catal. Lett. 1998;56:131–135. doi: 10.1023/A:1019069315071. [DOI] [Google Scholar]
- 13.Grunwaldt J.D., Kiener C., Wogerbauer C., Baiker A. Preparation of supported gold catalysts for low-temperature CO oxidation via “size-controlled” gold colloids. J. Catal. 1999;181:223–232. doi: 10.1006/jcat.1998.2298. [DOI] [Google Scholar]
- 14.Comotti M., Li W.C., Spliethoff B., Schüth F. Support effect in high activity gold catalysts for CO oxidation. J. Am. Chem. Soc. 2006;128:917–924. doi: 10.1021/ja0561441. [DOI] [PubMed] [Google Scholar]
- 15.Yin H.F., Ma Z., Chi M.F., Dai S. Activation of dodecanethiol-capped gold catalysts for CO oxidation by treatment with KMnO4 or K2MnO4. Catal. Lett. 2010;136:209–221. doi: 10.1007/s10562-010-0316-1. [DOI] [Google Scholar]
- 16.Schwartz V., Mullins D.R., Yan W.F., Chen B., Dai S., Overbury S.H. XAS study of Au supported on TiO2: Influence of oxidation state and particle size on catalytic activity. J. Phys. Chem. B. 2004;108:15782–15790. doi: 10.1021/jp048076v. [DOI] [Google Scholar]
- 17.Kundu S., Wang K., Liang H. Size-selective synthesis and catalytic application of polyelectrolyte encapsulated gold nanoparticles using microwave irridation. J. Phys. Chem. C. 2009;113:5157–5163. doi: 10.1021/jp9003104. [DOI] [Google Scholar]
- 18.Shimizu K., Miyamoto Y., Kawasaki T., Tanji T., Tai Y., Satsuma A. Chemoselective hydrogenation of nitroaromatics by supported gold catalysts: Mechanistic reasons for size- and support-dependent activity and selectivity. J. Phys. Chem. C. 2009;113:17803–17810. [Google Scholar]
- 19.Shekhar M., Wang J., Lee W.-S., Williams W.D., Kim S.M., Stach E.A., Miller J.T., Delgass W.N., Riberio F.H. Size and support effects for the water-gas shift catalysis over gold nanoparticles supported on model Al2O3 and TiO2. J. Am. Chem. Soc. 2012;134:4700–4708. doi: 10.1021/ja210083d. [DOI] [PubMed] [Google Scholar]
- 20.Valden M., Pak S., Lai X., Goodman D.W. Structure sensitivity of CO oxidation over model Au/TiO2 catalysts. Catal. Lett. 1998;56:7–10. doi: 10.1023/A:1019028205985. [DOI] [Google Scholar]
- 21.Laoufi I., Saint-Lager M.-C., Lazzari R., Jupille J., Robach O., Garaudée S., Cabailh G., Dolle P., Cruguel H., Bailly A. Size and catalytic activity of supported gold nanoparticles: An in Operando study during CO oxidation. J. Phys. Chem. C. 2011;115:4673–4679. [Google Scholar]
- 22.Esumi K., Satoh K., Torigoe K. Interactions between alkanethiols and gold-dendrimer nanocomposite. Langmuir. 2001;17:6860–6864. doi: 10.1021/la010632e. [DOI] [Google Scholar]
- 23.Yazid H., Adnan R., Farrukh M.A., Hanid S.A. Synthesis of Au/Al2O3 nanocrystal and its application in the reduction of p-nitrophenol. J. Chin. Chem. Soc. 2011;58:593–601. doi: 10.1002/jccs.201190093. [DOI] [Google Scholar]
- 24.Jana N.R., Gearheart L., Murphy C.J. Seeding growth for size control of 5—40 nm diameter gold nanoparticles. Langmuir. 2001;17:6282–6786. doi: 10.1021/la010757j. [DOI] [Google Scholar]
- 25.Panigrahi S., Basu S., Praharaj S., Pande S., Jana S., Pal A., Ghosh S.K., Pal T. Synthesis and size-selective catalysis by supported gold nanoparticles: Study on heterogeneous and homogeneous catalytic processes. J. Phys. Chem. C. 2007;111:4596–4605. [Google Scholar]
- 26.Saha S., Pal A., Kundu S., Basu S., Pal T. Photochemical green synthesis of calcium-alginate-stabilized Ag and Au nanoparticles and their catalytic application to 4-nitrophenol reduction. Langmuir. 2009;26:2885–2893. doi: 10.1021/la902950x. [DOI] [PubMed] [Google Scholar]
- 27.Liu L.C., Wei T., Guan X., Zi X.H., He H., Dai H.X. Size and morphology adjustment of PVP-stabilized silver and gold nanocrystals synthesized by hydrodynamic assisted self-assembly. J. Phys. Chem. C. 2009;113:8595–8600. doi: 10.1021/jp810668x. [DOI] [Google Scholar]
Associated Data
This section collects any data citations, data availability statements, or supplementary materials included in this article.