Molecules logoLink to Molecules
. 2014 Jun 18;19(6):8276–8288. doi: 10.3390/molecules19068276

Magnetic Pycnoporus sanguineus-Loaded Alginate Composite Beads for Removing Dye from Aqueous Solutions

Chih-Hui Yang 1, Ming-Cheng Shih 1, Han-Chen Chiu 1,2, Keng-Shiang Huang 2,*
PMCID: PMC6271236  PMID: 24945580

Abstract

Dye pollution in wastewater is a severe environmental problem because treating water containing dyes using conventional physical, chemical, and biological treatments is difficult. A conventional process is used to adsorb dyes and filter wastewater. Magnetic filtration is an emerging technology. In this study, magnetic Pycnoporus sanguineus-loaded alginate composite beads were employed to remove a dye solution. A white rot fungus, P. sanguineus, immobilized in alginate beads were used as a biosorbent to remove the dye solution. An alginate polymer could protect P. sanguineus in acidic environments. Superparamagnetic nanomaterials, iron oxide nanoparticles, were combined with alginate gels to form magnetic alginate composites. The magnetic guidability of alginate composites and biocompatibility of iron oxide nanoparticles facilitated the magnetic filtration and separation processes. The fungus cells were immobilized in loaded alginate composites to study the influence of the initial dye concentration and pH on the biosorption capacity. The composite beads could be removed easily post-adsorption by using a magnetic filtration process. When the amount of composite beads was varied, the results of kinetic studies of malachite green adsorption by immobilized cells of P. sanguineus fitted well with the pseudo-second-order model. The results indicated that the magnetic composite beads effectively adsorbed the dye solution from wastewater and were environmentally friendly.

Keywords: Pycnoporus sanguineus, malachite green, dye, alginate, iron oxide nanoparticles

1. Introduction

Water pollution caused by the discharge of industrial wastewater that contains dyes and heavy metal effluents has become a critical environmental problem [1,2]. Most developing countries have experienced severe water shortages that are attributable to water pollution caused by rapid industrialization [3,4]. From ecological and economical perspectives, removing dyes from textile effluents is crucial. Several dye removal processes, including coagulation, flocculation, biodegradation, adsorption on activated carbon, membrane separation, ion exchange, oxidation, advance oxidation, and selective bioadsorption, have been developed. Adsorption is a simple method for removing dyes. Adsorption processes often involve passive uptake and physicochemical binding of chemical species or ions to a solid surface.

Adsorbing pollutants by using environmentally friendly materials is generally considered superior to traditional methods [5]. Numerous studies have examined magnetic polymer beads [6,7,8,9,10,11]. Magnetic separation is widely used in the fields of medicine, diagnostics, molecular biology bioinorganic chemistry, and catalysis [12,13,14]. Magnetic separation is a promising novel environmental purification technique because it produces no contaminants such as flocculants. Therefore, using magnetic beads in filtration and separation is an emerging method for treating wastewater [15,16]. Magnetic separation was proved to be an effective technique for removing dyes from manufacturing effluents [17]. Adsorption using fungus is an alternative method for treating wastewater [18,19,20,21,22,23,24]. Researchers have reported that white rot fungus (e.g., Pycnoporus sanguineus, P. sanguineus) can be used to decolorize bromophenol blue and malachite green dyes [25]. However, the immobilized fungus has limitations, such as poor mechanical strength, instability at a low pH, and cell leakage.

According to a review of relevant research, few studies have examined using a combination of P. sanguineus, magnetic beads, and pH-sensitive alginate polymers to treat wastewater. In this study, magnetic P. sanguineus-loaded alginate composite beads were used as adsorbents to treat an aqueous solution containing malachite green (Figure 1). In addition to adsorption capacity, batch kinetics, the effect of contact time, the effect of the initial malachite green concentration, and magnetic separation were investigated.

Figure 1.

Figure 1

Open in a new tab

Schematic diagram of the adsorption and magnetic separation processes.

2. Results and Discussion

2.1. Characterization of Magnetic P. sanguineus-Loaded Alginate Composite Beads

Figure 2 shows the morphologies of the prepared alginate beads, P. sanguineus-loaded alginate beads, and P. sanguineus-loaded alginate beads with magnetic iron oxide nanoparticles. The alginate beads were transparent particles with a mean diameter of 700 μm (Figure 2b). The P. sanguineus-loaded alginate beads exhibited transparent particles containing brown spots indicating the aggregation of P. sanguineus. The results shown in Figure 2c revealed that all alginate beads contained brown spots, suggesting that P. sanguineus was dispersed within the beads. The P. sanguineus-loaded alginate beads with magnetic iron oxide nanoparticles (Figure 2d) exhibited opaque brown and black surfaces, preventing P. sanguineus from being observed. The mean diameter of each bead was 800 μm. The results indicated that the relative standard deviation of composite beads shown in Figure 2d was >10%, and the beads were elliptical in shape. We attribute the elliptical shape to the lower concentration of the Na-alginate solution (0.9 wt %) used in the P. sanguineus-loaded alginate beads with magnetic iron oxide nanoparticles relative to that used in the alginate beads (2 wt %). The beads were hydrogels. When the concentration of the Na-alginate solution was below 1 wt %, the polymer beads exhibited a loose structure and became nonspherical. In addition, the prepared magnetic nanoparticles were shown in Figure 2e. The magnetic properties and aggregation status of magnetite nanoparticles have been described in the literature [26]. It provide clues for optimal the prepared magnetite nanoparticles.

Figure 2.

Figure 2

Open in a new tab

Optical microscopy images of (a) P. sanguineus in a dish, (b) alginate beads, (c) P. sanguineus-loaded alginate beads, (d) P. sanguineus-loaded alginate beads with magnetic iron oxide nanoparticles (e.g., magnetic P. sanguineus-loaded alginate composite beads), and (e) the SEM image of the prepared superparamagnetic nanoparticles (scale bar is 20 nm, 80 kV, 500,000×).

2.2. Removal of Dye from an Aqueous Solution

The prepared magnetic P. sanguineus-loaded alginate composite beads (0.05 mg) were added to 16.65 mL of a 10 mg/L malachite green solution at room temperature (approximately 298 K) to evaluate the efficiency of dye adsorption. To observe the color change of the solution in a vial, a magnet was used to concentrate the composite beads. Figure 3a,b show the initial picture. When the composite beads were aggregated using a magnet, the solution was deep blue in color. The purified solution and postadsorption composite beads could be separated easily when the iron oxide nanoparticles were used. The magnet was removed to enable adsorption to proceed for 100 min. The composite beads were aggregated using the magnet again, revealing that the composite beads caused the deep blue color of the solution to fade, and a light blue color was observed (Figure 3b). The magnet was then removed to enable 1,440 min of adsorption to proceed. Subsequently, the composite beads were aggregated using the magnet, and the solution became nearly colorless (Figure 3c). The results revealed that the prepared magnetic P. sanguineus-loaded alginate composite beads adsorbed malachite green gradually over time. We speculate that the mechanism of biosorption is based on the biosorption of dyes by P. sanguineus [27].

Figure 3.

Figure 3

Open in a new tab

Photographs of malachite green dye treatment using magnetic P. sanguineus-loaded alginate composite beads: (a) original solution (b) baseline, (c) after 100 min of adsorption, and (d) after 1440 min adsorption.

2.3. Effect of Initial Dye Concentration and Contact Time

To evaluate the adsorption effect, three concentrations of malachite green solutions were tested at room temperature (approximately 298 K), as shown in Figure 4.

Figure 4.

Figure 4

Open in a new tab

Effects of initial dye concentration on the biosorption of the malachite green dye by immobilized cells of P. sanguineus (temperature: approximately 25 °C).

The results indicated that the maximal uptake capacities were 0.4, 1.35 and 1.8 mg/g for the 10, 30, and 70 mg/L malachite green solutions, respectively. The time required to reach equilibrium differed according to the concentration of the malachite green solution; specifically, equilibrium was reached after the 10 mg/L malachite green solution was adsorbed for 180 min, after the 30-mg/L malachite green solution was adsorbed for 180 min, and after the 70 mg/L malachite green solution was adsorbed for 90 min. The results revealed that each adsorption rate increased before the maximal uptake capacity was reached. We infer that the prepared composite beads feature high adsorption and a high adsorption rate at high concentrations.

2.4. Effect of pH on Adsorption

The effect of pH values ranging from 3 to 8 on dye adsorption (Figure 5) was investigated using 16.65 mL of a 10 mg/L malachite green solution, 0.05 mg of composite beads, and a reaction temperature of 298 K. The results indicated that pH variations did not influence the dye adsorption capacity. No significant differences were observed among pH values. The results indicated that, in an acidic environment, the alginate polymer beads adequately protected P. sanguineus. The results evidenced that the magnetic P. sanguineus-loaded alginate composite beads effectively adsorbed dye pollutants.

Figure 5.

Figure 5

Open in a new tab

Effects of pH values on the biosorption of the malachite green dye (50-mL centrifugal tube, agitation speed = 125 ppm).

2.5. Kinetics Studies

Kinetics experiments of malachite green biosorption by immobilized cells of P. sanguineus were conducted, and the experimental data were fitted to the pseudo-first-order and pseudo-second-order kinetic models. The best-fit model was selected based on the values of the linear regression correlation coefficient R2. The adsorption of malachite green was plotted according to Equation (4) and is shown in Figure 6. The pseudo-first-order constants and correlation coefficient R2 were calculated based on Figure 6 and are listed in Table 1. The high R2 values confirm that the pseudo-first-order kinetics model suitably represented all adsorption data. Furthermore, the calculated values of adsorption capacity qe obtained from the pseudo-first-order model were reasonably close to the experimental qe values in the case of pseudo-first-order kinetics. The rate of a pseudo-second-order reaction depends on the amount of solute adsorbed on the surface of the adsorbent and the amount adsorbed at equilibrium [28]. When pseudo-second-order kinetics is applicable, the plot of t/qt against t for Equation (5) shows a linear relationship from which qe and k2 can be determined based on the slope and the intercept, respectively. As shown in Table 2, the results indicated that the experimental data were not consistent with the pseudo-second-order kinetic model.

Figure 6.

Figure 6

Open in a new tab

Linearized pseudo-first-order kinetics plot of the biosorption of the malachite green dye onto immobilized cells of P. sanguineus at various concentrations of composite beads.

Table 1.

Kinetic pseudo-first-order model parameters of the biosorption at various concentrations of composite beads.

Co mg/L T (K) Pseudo-First-Order
K1 qe R2
70 298 0.080 1.40 0.981
30 298 0.045 0.26 0.912
10 298 0.024 0.68 0.991
Open in a new tab

Table 2.

Kinetic pseudo-second-order model parameters of the biosorption at various concentrations of composite beads.

Co mg/L T (K) Pseudo-Second-Order
K2 qe R2
70 298 0.004 2.214 0.984
30 298 0.242 0.275 0.760
10 298 0.023 0.420 0.928
Open in a new tab

Figure 6 and Figure 7 show a comparison of pseudo-first-order and pseudo-second-order kinetic models of malachite green adsorption onto magnetic P. sanguineus-loaded alginate composite beads at various initial dye concentrations. All experimental data on malachite green adsorption onto magnetic P. sanguineus-loaded alginate composite beads were consistent with the pseudo-first-order model and exhibited high correlation coefficients. Theoretically, the Lagergren pseudo-first-order equation indicates that the logarithm of the difference between the equilibrium and the monitored adsorbed amount should be a linear function of time. This equation is closely associated with the model of one-site occupancy adsorption kinetics governed by the rate of the surface reaction. The results shown in Figure 6 indicated that the adsorption process observed in this study was consistent with this model. The Lagergren pseudo-first-order equation was recently generalized to two-site-occupancy adsorption and called the pseudo-second-order kinetic equation. The main assumption of the pseudo-second-order kinetic model is that the sorption capacity is proportional to the number of active sites occupied on the sorbent. According to relevant literature, pseudo-second-order kinetics is more applicable to dye adsorption than other kinetic models because the effects of transport phenomena and chemical reactions are often experimentally inseparable. Figure 7 shows that the adsorption process was not two-site-occupancy adsorption.

Figure 7.

Figure 7

Open in a new tab

Linearized pseudo-second-order kinetics plot of the biosorption of malachite green onto immobilized cells of P. sanguineus at various concentrations of composite beads.

3. Experimental

3.1. Microorganism and Production Medium

P. sanguineus was obtained from the Bioresource Collection and Research Center, Food Industry Research and Development Institute, Taiwan. The fungus was maintained through weekly transfer on malt extract agar slants incubated at 308 K for 7 d and was subsequently stored at 277 K until required. A 500-mL production medium consisting of 0.15 g/mL of glucose, 0.3 g/mL of peptone, and 24 g/mL of malt extract was autoclaved at 394 K (150 kN/m2) for 20 min.

3.2. Preparation of Iron Oxide Nanoparticles

Ferrous chloride 4-hydrate (FeCl2•4H2O, 98%), iron (III) chloride hexahydrate (FeCl3•6H2O, 99%), and sodium hydroxide (NaOH) were purchased from Sigma (Uni-onward, Taiwan), J. T. Baker (Uni-onward, Taiwan), and Alfa Aesar (Uni-onward, Taiwan), respectively. A 2 N FeCl2•4H2O ferro solution (1 mL) and a 2 N FeCl3•6H2O ferric solution (4 mL) were mixed. After 15 min of constant stirring, a ferro-ferric solution was obtained. Subsequently, 5 mL of glycine was added to the ferro-ferric solution, and the solution was stirred for 15 min. A 20% NaOH solution (9 mL) was added dropwise to the ferro-ferric-glycine solution, and the solution was stirred at room temperature (approximately 298 K). After 5 min, black iron oxide nanoparticles were observed based on the coprecipitation of both ferrous cations and ferric cations. The particles were then collected by conducting centrifugation and washed several times with 30 mL of distilled deionized water to remove any alkali. Similar synthetic methods have been described [29,30,31].

3.3. Preparation of Calcium-Alginate Beads

Ca-alginate beads were prepared by dropping 3 mL of a 2 wt % Na-alginate solution (Na-alginate powder from a brown algae source, 300–400 cps, purchased from Sigma (Uni-onward, Taiwan)) into 50 mL of a 20% CaCl2 solution at room temperature (approximately 298 K). The beads were stirred slowly for 30 min, collected through filtration, and washed with sterile deionized water. The washed beads were collected and stored at room temperature (approximately 298 K). Similar synthetic methods have been described [32,33,34,35].

3.4. Preparation of Magnetic P. sanguineus-Loaded Alginate Composite Beads

A cell suspension was prepared by inoculating a stock culture of P. sanguineus onto malt extract agar plates. The mycelium mat that formed was scraped from the plate by using a sterile blade and mixed with 50 mL of a sterile Tween 20 (purchased from Sigma (Uni-onward, Taiwan)) solution before placing it in a sterile sampling bottle (100 mL). The sampling bottle was vortexed for 5 min to distribute the mycelium evenly in the liquid. Subsequently, 15 mL of the cell suspension was inoculated into an Erlenmeyer flask containing 135 mL of the production medium. The flask was incubated on a rotary shaker operating at 150 rpm at 303 K for 66 h. The harvested culture broth was centrifuged at 4,500 rpm and 298 K for 4 min.

The magnetic P. sanguineus-loaded alginate composite beads were prepared by dropping a mixture comprising 2 mL of the 2 wt % Na-alginate solution, 1 mL of iron oxide nanoparticles, and 2 mL of a 2% P. sanguineus solution into a 50-mL 20% CaCl2 solution at room temperature (approximately 298 K). The beads were stirred slowly for 30 min, collected through filtration, and washed with sterile deionized water. The washed beads were collected and stored at room temperature (approximately 298 K).

3.5. Preparation of Dye Solutions

The stock solution of a malachite green dye (chemical formula: C23H25N2•0.5C2H2O4; λmax = 620; purchased from Sigma (Uni-onward, Taiwan)) were prepared by dissolving 1 g of the dye in 1 L of sterile deionized water. The stock solution was then successively diluted to the desired initial concentrations, namely 10 mg/L, 30 mg/L, and 70 mg/L.

3.6. Kinetic Studies

Predicting batch kinetics can facilitate the design of adsorption systems because kinetics describes the uptake rate of adsorbents, thereby enabling the adsorption mechanism to be predicted [36,37,38,39,40].

3.6.1. Pseudo-First-Order Kinetic Model

The pseudo-first-order kinetic model has been used extensively to predict sorption kinetics. The model proposed by Langergren [41] is expressed as follows:

graphic file with name molecules-19-08276-i001.jpg (1)

After definite integration is established by applying the boundary conditions t = 0 to t = t and qt = 0 to qt = qt, the integrated form of Equation (1) can be expressed as follows [40]:

graphic file with name molecules-19-08276-i002.jpg (2)

where qe and qt are the amounts of adsorbate adsorbed (mg/g) at equilibrium and time t (min), respectively, and k1 is the adsorption rate constant of the pseudo-first-order equation (min−1). The values of log(qe − qt) were linearly correlated with t. The plot of log(qe − qt) versus t shows a linear relationship from which K1 and qe can be determined based on the slope and intercept of the plot, respectively.

3.6.2. Pseudo-Second-Order Kinetic Model

The pseudo-second-order equation is expressed as follows [28]:

graphic file with name molecules-19-08276-i003.jpg (3)

Integrating Equation (4) for the boundary conditions t = 0 to t = t and qt = 0 to qt = qt yields

graphic file with name molecules-19-08276-i004.jpg (4)

which is the integrated rate law for a pseudo-second-order reaction. Equation (4) can be rearranged to obtain Equation (5), which has a linear form:

graphic file with name molecules-19-08276-i005.jpg (5)

where k2 is the rate constant of the pseudo-second-order equation (g/mg min). The linear plot of t/qt versus t indicates that 1/qe is the slope and Inline graphic is the intercept.

4. Conclusions

In this study, alginate composite beads containing magnetic iron oxide and activated P. sanguineus were prepared to selectively remove a dye from synthetic wastewater. The results indicated that the immobilized cells of P. sanguineus can be used as an adsorbent to remove malachite green. In addition, no significant difference was observed between the adsorption capacity of malachite green and pH variations. This high pH range tolerance advance the application of the prepared composite beads in acidic conditions. The magnetic properties of the composite beads enabled them to be separated from the effluent by using a simple magnetic field, thus facilitating the development of a simple process for remediating water polluted with dyes.

Acknowledgments

This work was financially supported by a grant from I-Shou University and the Ministry of Science and Technology of Taiwan.

Author Contributions

C-H Yang designed the designed research; M-C Shih analyzed data; H-C Chiu performed the experiments; K-S Huang wrote the paper. All authors read and approved the final manuscript.

Conflicts of Interest

The authors declare no conflict of interest.

Footnotes

Sample Availability: Not available.

References

  • 1.Kabir M., Daly E., Maggi F. A review of ion and metal pollutants in urban green water infrastructures. Sci. Total Environ. 2014;470:695–706. doi: 10.1016/j.scitotenv.2013.10.010. [DOI] [PubMed] [Google Scholar]
  • 2.Yang H., Flower R.J., Thompson J.R. Pollution: China’s new leaders offer green hope. Nature. 2013;493:163–163. doi: 10.1038/493163d. [DOI] [PubMed] [Google Scholar]
  • 3.Maurya N.S., Mittal A.K., Cornel P., Rother E. Biosorption of dyes using dead macro fungi: Effect of dye structure, ionic strength and pH. Bioresour. Technol. 2006;97:512–521. doi: 10.1016/j.biortech.2005.02.045. [DOI] [PubMed] [Google Scholar]
  • 4.Rodríguez Couto S. Dye removal by immobilised fungi. Biotechnol. Adv. 2009;27:227–235. doi: 10.1016/j.biotechadv.2008.12.001. [DOI] [PubMed] [Google Scholar]
  • 5.Mahmoodi N.M. Magnetic ferrite nanoparticle–alginate composite: Synthesis, characterization and binary system dye removal. J. Taiwan Inst. Chem. Eng. 2013;44:322–330. doi: 10.1016/j.jtice.2012.11.014. [DOI] [Google Scholar]
  • 6.Rocher V., Siaugue J.M., Cabuil V., Bee A. Removal of organic dyes by magnetic alginate beads. Water Res. 2008;42:1290–1298. doi: 10.1016/j.watres.2007.09.024. [DOI] [PubMed] [Google Scholar]
  • 7.Alexandru M.G., Bogdan S.V., Alina M.H. Eugenol functionalized magnetite nanostructures used in anti-infectious therapy. Lett. Appl. Nanobiosci. 2013;2:120–123. [Google Scholar]
  • 8.Cotar A.I., Grumezescu A.M., Huang K.S., Voicu G., Chifiriuc C.M., Radulescu R. Magnetite nanoparticles influence the efficacy of antibiotics against biofilm embedded Staphylococcus aureus cells. Biointerface Res. Appl. Chem. 2013;3:559–565. [Google Scholar]
  • 9.Grumezescu A.M., Andronescu E., Ficai A., Ficai D., Huang K.S., Gheorghe I., Chifiriuc C.M. Water soluble magnetic biocomposite with potential applications for the antimicrobial therapy. Biointerface Res. Appl. Chem. 2012;2:469–475. [Google Scholar]
  • 10.Mihaiescu D.E., Hoeja M., Gheorghe I., Fical A., Grumezescu A.M., Bleotu C., Chifiriuc C.M. Water soluble magnetite nanoparticles for antimicrobial drugs delivery. Lett. Appl. Nanobiosci. 2012;1:45–49. [Google Scholar]
  • 11.Andronescu E., Grumezescu A.M., Ficai A., Gheorghe I., Chifiriuc M., Mihaiescu D.E., Lazar V. In vitro efficacy of antibiotic magnetic dextran microspheres complexes against staphylococcus aures and pseudomonas aeruginosa strains. Biointerface Res. Appl. Chem. 2012;2:332–338. [Google Scholar]
  • 12.LeSage D., Arai K., Glenn D.R., DeVience S.J., Pham L.M., Rahn L.L., Lukin M.D., Yacoby A., Komeili A., Walsworth R.L. Optical magnetic imaging of living cells. Nature. 2013;496:486–489. doi: 10.1038/nature12072. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 13.Mura S., Nicolas J., Couvreur P. Stimuli-responsive nanocarriers for drug delivery. Nat. Mater. 2013;12:991–1003. doi: 10.1038/nmat3776. [DOI] [PubMed] [Google Scholar]
  • 14.Ahrens E.T., Bulte J.W. Tracking immune cells in vivo using magnetic resonance imaging. Nat. Rev. Immunol. 2013;13:755–763. doi: 10.1038/nri3531. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 15.Deans J.R., Dixon B.G. Uptake of Pb2+ and Cu2+ by novel biopolymers. Water Res. 1992;26:469–472. doi: 10.1016/0043-1354(92)90047-8. [DOI] [Google Scholar]
  • 16.Davis T.A., Volesky B., Mucci A. A review of the biochemistry of heavy metal biosorption by brown algae. Water Res. 2003;37:4311–4330. doi: 10.1016/S0043-1354(03)00293-8. [DOI] [PubMed] [Google Scholar]
  • 17.Idris A., Ismail N.S.M., Hassan N., Misran E., Ngomsik A.-F. Synthesis of magnetic alginate beads based on maghemite nanoparticles for Pb(II) removal in aqueous solution. J. Ind. Eng. Chem. 2012;18:1582–1589. doi: 10.1016/j.jiec.2012.02.018. [DOI] [Google Scholar]
  • 18.Yahaya Y.A., Don M.M., Bhatia S. Biosorption of copper (II) onto immobilized cells of pycnoporus sanguineus from aqueous solution: Equilibrium and kinetic studies. J. Hazard. Mater. 2009;161:189–195. doi: 10.1016/j.jhazmat.2008.03.104. [DOI] [PubMed] [Google Scholar]
  • 19.Pointing S., Vrijmoed L. Decolorization of azo and triphenylmethane dyes by pycnoporus sanguineus producing laccase as the sole phenoloxidase. World. J. Microbiol. Biotechnol. 2000;16:317–318. doi: 10.1023/A:1008959600680. [DOI] [Google Scholar]
  • 20.Bayramoğlu G., Bektaş S., Arıca M.Y. Biosorption of heavy metal ions on immobilized white-rot fungus trametes versicolor. J. Hazard. Mater. 2003;101:285–300. doi: 10.1016/S0304-3894(03)00178-X. [DOI] [PubMed] [Google Scholar]
  • 21.Ting Y.P., Sun G. Use of polyvinyl alcohol as a cell immobilization matrix for copper biosorption by yeast cells. J. Chem. Technol. Biotechnol. 2000;75:541–546. doi: 10.1002/1097-4660(200007)75:7<541::AID-JCTB247>3.0.CO;2-9. [DOI] [Google Scholar]
  • 22.Aksu Z., Gönen F. Biosorption of phenol by immobilized activated sludge in a continuous packed bed: Prediction of breakthrough curves. Process Biochem. 2004;39:599–613. doi: 10.1016/S0032-9592(03)00132-8. [DOI] [Google Scholar]
  • 23.Bauer A., Layh N., Syldatk C., Willetts A. Polyvinyl alcohol-immobilized whole-cell preparations for the biotransformation of nitriles. Biotechnol. Lett. 1996;18:343–348. [Google Scholar]
  • 24.Yesilada O., Asma D., Cing S. Decolorization of textile dyes by fungal pellets. Process Biochem. 2003;38:933–938. doi: 10.1016/S0032-9592(02)00197-8. [DOI] [Google Scholar]
  • 25.Annuar M., Adnan S., Vikineswary S., Chisti Y. Kinetics and energetics of azo dye decolorization by pycnoporus sanguineus. Water Air Soil Pollut. 2009;202:179–188. doi: 10.1007/s11270-008-9968-5. [DOI] [Google Scholar]
  • 26.Tiberto P., Barrera G., Celegato F., Coïsson M., Chiolerio A., Martino P., Pandolfi P., Allia P. Magnetic properties of jet-printer inks containing dispersed magnetite nanoparticles. Eur. Phys. J. B. 2013;86 doi: 10.1140/epjb/e2013-3098. [DOI] [Google Scholar]
  • 27.Arica M.Y., Kaçar Y., Genç Ö. Entrapment of white-rot fungus trametes versicolor in Ca-alginate Beads: Preparation and biosorption kinetic analysis for cadmium removal from an aqueous solution. Bioresour. Technol. 2001;80:121–129. doi: 10.1016/S0960-8524(01)00084-0. [DOI] [PubMed] [Google Scholar]
  • 28.Ho Y.S., McKay G. Pseudo-second order model for sorption processes. Process Biochem. 1999;34:451–465. doi: 10.1016/S0032-9592(98)00112-5. [DOI] [Google Scholar]
  • 29.Chih H.Y., Chih Y.W., Keng S.H., Chao P.K., Yi C.C., Jei F.S. Microfluidic one-step synthesis of Fe3O4-chitosan composite particles and their applications. Int. J. Pharm. 2014;463:155–160. doi: 10.1016/j.ijpharm.2013.08.020. [DOI] [PubMed] [Google Scholar]
  • 30.Chih Y.W., Chih H.Y., Keng S.H., Fang R.C., Andrew H.J.W., Chih H.C. Electrostatic droplets assisted in-situ synthesis of superparamagnetic chitosan microparticles for magnetic-responsive controlled drug release and copper ion removal. J. Mater. Chem. B. 2013;1:2205–2212. doi: 10.1039/c3tb00467h. [DOI] [PubMed] [Google Scholar]
  • 31.Chih H.Y., Chih Y.W., Keng S.H., Chen S.Y., Andrew H.J.W., Wei T.W., Ming Y.L. Facile synthesis of radial-like macroporous superparamagnetic chitosan spheres with in-situ co-precipitation and gelation of ferro-gels. PLoS One. 2012;7:e49329. doi: 10.1371/journal.pone.0049329. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 32.Keng S.H., Chih H.Y., Chao P.K., Ming D.K., Alexandru M.G., Yung S.L., Chih Y.W. Synthesis of uniform core-shell gelatin-alginate microparticles as intestine-released oral delivery drug carrier. Electrophoresis. 2014;35:330–336. doi: 10.1002/elps.201300194. [DOI] [PubMed] [Google Scholar]
  • 33.Keng S.H., Yung S.L., Wan R.C., Yi L.W., Chih H.Y. A facile fabrication of alginate microbubbles using a gas foaming reaction. Molecules. 2013;18:9594–9602. doi: 10.3390/molecules18089594. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 34.Keng S.H., Yang C.H., Lin Y.S., Wang C.Y., Lu K., Chang Y.F., Wang Y.L. Electrostatic droplets assisted synthesis of alginate microcapsules. Drug Deliv. Transl. Res. 2011;1:289–298. doi: 10.1007/s13346-011-0020-8. [DOI] [PubMed] [Google Scholar]
  • 35.Keng S.H., Yung S.L., Chih H.Y., Chia W.T., Ming Y.H. In situ synthesis of twin monodispersed alginate microparticles. Soft Matter. 2011;7:6713–6718. [Google Scholar]
  • 36.Won S.W., Han M.H., Yun Y.S. Different binding mechanisms in biosorption of reactive dyes according to their reactivity. Water Res. 2008;42:4847–4855. doi: 10.1016/j.watres.2008.09.003. [DOI] [PubMed] [Google Scholar]
  • 37.Yan H., Yang L., Yang Z., Yang H., Li A., Cheng R. Preparation of chitosan/poly(acrylic acid) magnetic composite microspheres and applications in the removal of copper(II) ions from aqueous solutions. J. Hazard. Mater. 2012 doi: 10.1016/j.jhazmat.2012.06.014. [DOI] [PubMed] [Google Scholar]
  • 38.Fan L., Luo C., Li X., Lu F., Qiu H., Sun M. Fabrication of novel magnetic chitosan grafted with graphene oxide to enhance adsorption properties for methyl blue. J. Hazard. Mater. . 2012 doi: 10.1016/j.jhazmat.2012.02.068. [DOI] [PubMed] [Google Scholar]
  • 39.Fan L., Zhang Y., Luo C., Lu F., Qiu H., Sun M. Synthesis and characterization of magnetic β-cyclodextrin–chitosan nanoparticles as nano-adsorbents for removal of methyl blue. Int. J. Biol. Macromol. 2012;50:444–450. doi: 10.1016/j.ijbiomac.2011.12.016. [DOI] [PubMed] [Google Scholar]
  • 40.Zhou L., Jin J., Liu Z., Liang X., Shang C. Adsorption of acid dyes from aqueous solutions by the ethylenediamine-modified magnetic chitosan nanoparticles. J. Hazard. Mater. 2011;185:1045–1052. doi: 10.1016/j.jhazmat.2010.10.012. [DOI] [PubMed] [Google Scholar]
  • 41.Huang Y.T., Shih M.C. Prediction of adsorption kinetics and isotherms by using linear regression method. Int. J. Sci. Commer. Hum. 2013;5:303–320. [Google Scholar]