Abstract
Objectives
Enamel erosion caused by high consumption of acidic drinks poses a significant public health concern. This study was aimed to determine the protective effect of eggshell-titanium dioxide composite (EB@TiO2) against erosive acids on tooth enamel.
Methods
Twenty prepared bovine tooth enamel specimens were randomly assigned to 5 sample groups (n=4): (1) unexposed tooth enamel; (2) exposed tooth enamel + HCI; (3) exposed tooth enamel + HCI + Colgate toothpaste; (4) exposed tooth enamel + HCI + Sensodyne toothpaste; and (5) exposed tooth enamel + HCI + EB@TiO2. The mean roughness value (Rrms) of the exposed and unexposed tooth was measured with atomic force microscope (AFM). Scanning electron microscope (SEM) and Raman spectroscopy techniques were used to evaluate the surface morphology and changes. ANOVA was used to analyze the mean square roughness (Rrms) values for all specimens. Bonferonni correction was used to identify the mean differences among the 5 groups (α=0.05). The Rrms values measured for the unexposed and exposed specimens in HCI alone were statistically significant (P < 0.05).
Results
No significant differences were found for the unexposed and exposed specimens in HCI + toothpaste and EB@TiO2. The tooth enamel specimens exposed to HCI + Sensodyne had the highest Rrms values, while specimens exposed to HCI + EB@TiO2 had the lowest Rrms values.
Conclusions
This study confirms that the investigated toothpaste provides protection against acidic substances. The study results further suggests that EB@TiO2 could be used to provide enhanced protection for tooth enamel.
1. Introduction
Enamel erosion has become a topical issue in recent years among clinicians and oral health-care providers due to the increase in the consumption of acidic drinks such as soft drinks, energy drinks, and fruit drinks [1]. Previous studies [2, 3] reported that these drinks have a pH [2–4] value that facilitates the dissolution of the tooth and the destruction of the mineral composition of the enamel. Several other authors [4, 5] have demonstrated that as a result of consumption of acidic drinks, the onset of caries and enamel erosion correlate positively together.
Whilst the tooth enamel is mainly composed of hydroxyapatite in the form of phosphate ions (PO43−) and calcium ions (Ca2+), Shellis et al. [6], and Lussi and Carvalho [7] argued that there exists an equilibrium between the tooth enamel crystals and the surrounding oral environment. The destabilization of these equilibrium, particularly when the oral environment pH drops below a critical level (5.5 for enamel and 6.2 for dentin), may result in the dissolution of tooth mineral composition [8]. Moreover, the loss of enamel material by erosion is a dynamic process occasioned with periods of demineralization and remineralization (Figure 1); hence, preventive measures against enamel dissolution from acid and potentially permanent damage should be a priority for oral health-care providers [2, 3].
Traditionally, toothpastes have been considered effective and accessible vehicles to improve enamel resistant against erosive oral environment [9]. In recent years, different ingredients have been added to the toothpastes composition to enhance their protective effect against erosive substances. Amongst these ingredients, the use of topical fluoride to modify the effects of erosion at the tooth surface is well documented [10–13]. However, Moron et al. [14] stressed that conventional fluoride-containing toothpastes lack the capacity to protect sufficiently well against erosive substance. Furthermore, Larsen and Richards [15] revealed that at pH below 3, the protective effect of fluoride is diminished. Consequently, it has been suggested that the beneficial health effects against erosive attacks can be improved with the addition of calcium or calcium containing material into toothpaste [16].
Significantly, studies by King'Ori [17] and Onwubu et al. [18] suggest that the calcium of eggshell can be used as an abrasive cleaner for dental plaque in toothpaste. Lin et al. [19] and Tao et al. [20] equally demonstrated that the mechanical modification of calcium carbonates together with titanium dioxide improved the acid resistance properties when used in paper making industry. However, there is a limited research on the protective effect of a modified eggshell-titanium dioxide composite (EB@TiO2) on tooth enamel. This in vitro study aimed to determine the protective effect of a modified eggshell-titanium dioxide composite EB@TiO2 against erosive acids. The protective level of EB@TiO2 against erosive acids was compared against Colgate® and Sensodyne® toothpaste. It was hypothesized that EB@TiO2 will offer more protection against erosive challenge than the commercial toothpastes.
2. Materials and Methods
2.1. Preparation of Eggshell-Titanium Dioxide Composite (EB@TiO2)
Modification of eggshell with titanium dioxide was achieved in two steps. In the first step, eggshells were prepared according to the procedure described by Onwubu et al. [21]. Eggshells were disinfected by storing them in a diluted solution of household sodium hypochlorite for six hours. Subsequently, eggshells were vacuum-dried for ± 6–9 min at 250°C. Thereafter, 30 g of the dried eggshell was placed in a 500 ml stainless jar (inner diameter of 100 mm), together with 50 stainless steel balls of 10 mm diameter, and dry-milled in a planetary ball mill (Retsch® PM 100) at 400 rpm for 20 minutes. The collected powder was sieved to a particle size of ≤ 25 µm using a mechanical sieving shaker (Retsch AS 200, Germany). In the next step, 20 g of the fine eggshell powder obtained in step 1 was modified by adding 5 g of anatase titanium dioxide (≤15 µm). The mixture was subsequently ball-milled for 200 min to obtain eggshell-titanium dioxide composite (EB@TiO2). The particle size distribution of the composite measured using high-resolution transmission microscope (TEM-Philips CM 120 model) at 120 kV and image J software (National Institute of Health USA, http://imagej.nih.gov./ij) was found to be 14 nm (Figure 2).
2.2. pH Measurement
The pH and buffering characteristics of the EB@TiO2 (tested samples) and the respective toothpastes, brand names, and manufacturers are given in Table 1. The pH of each of the samples in deionized water as well as in 0.01 mol·L−1 hydrochloric acid (HCI) were measured by placing 1.5 g of each samples in a beaker containing 50 mL deionized and HCI, respectively. The solution was constantly agitated at low speed of 600 rpm for 30 min. A pH meter (Starter 300, Ohaus Incorporation USA) equipped with temperature sensor was used to record changes in the pH reading. Before testing the samples, the pH was calibrated using tested buffer of known pH solutions.
Table 1.
Toothpastes | Brand name | Manufacturer | pH in deionized water | Buffering capacity Β (mmol 2−1 pH−1) |
---|---|---|---|---|
Colgate | CALCITM—SEAL protection | Colgate-Palmolive Co | 9.61 | 6.6 ± 02.9 |
Sensodyne | Rapid relief | GlaxoSmithKline | 7.41 | 2.3 ± 0.02 |
EB@TiO2 | N/A | Researcher | 9.31 | 7.3 ± 0.11 |
2.3. Preparation of Tooth Enamel Specimens
Twenty freshly collected bovine enamel anterior teeth were used to evaluate the acid resistant properties of EB@TiO2. The collected teeth were subsequently cleaned and disinfected in 10% chloroxylenol solution. Enamel specimens measuring 5 mm × 5 mm × 3 mm was prepared after cutting off the roots using a low-speed diamond saw under water cooling conditions. Before subjecting the specimens to acidic condition, the specimens were embedded in a resin (FT 160; AMT composite), and a silicone mold (Blue mold; Agar scientific) was used to make a mounting base. The embedded specimens were randomly assigned into five groups (n=4) and were then exposed to 0.01 mol·L−1 HCI (pH = 2) for 30 min as follows: Group 1: unexposed tooth enamel; Group 2: exposed tooth enamel + HCI; Group 3: exposed tooth enamel + HCI + Colgate; Group 4: exposed tooth enamel + HCI + Sensodyne; and Group 5: exposed tooth enamel + HCI + EB@TiO2.
After 30 min of acid exposure, the specimens were rinsed in deionized water for 30 s and blot-dried.
2.4. Atomic Force Microscopy (AFM) Analysis
AFM (Nanoscope; Bruker) was used to analyze the mean square roughness (Rrms) values of the specimens. The instrument was set in contact mode with a scanning size of 10 µm and a scan rate of 2.394 Hz. For each specimen, 5 different measurements of the Rrms values were made. The average measured Rrms values were then used for the statistical analysis.
2.5. Field-Scanning Electron Microscope Evaluation of the Specimens
The surface of the exposed and unexposed specimens was characterized using scanning electron microscope (FESEM; Carl Zeiss). As a proxy measure, a specimen from each group was analyzed microscopically.
2.6. Raman Spectroscopy Analysis of Specimens
The changes in the mineral content of the specimens were observed using a Raman (Perkin Elmer precisely Raman-station 400). The Raman analysis was done on the all the samples with the laser power set at 70 mW, exposure every 10 seconds for 3 seconds at a time. Five different measurements were done for each samples and the average was used for statistical analysis.
2.7. Statistical Analysis
The mean roughness (Rrms) value of the specimens was evaluated with 1-way analysis of variance (ANOVA) by means of statistical software (IBM SPSS Statistics v25; IBM Corp.), followed by Bonferonni correction and the significance level was set at α=0.05. For Raman analysis, the base line correction was estimated by the polynomial fitting method, and the peak area and height were determined from the Gaussian plot using Origin Pro software (OriginLab Corporation v 8).
3. Results
3.1. Atomic Force Microscopy (AFM)
The 1-way ANOVA, mean, standard deviation, and standard error results are shown in Table 2. A notable statistical difference was observed in the mean surface roughness (Rrms) for the unexposed and exposed specimens (P < 0.05).
Table 2.
Groups | N | Mean ± SD | Std. error | 95% confidence interval for mean | P | Post hoc bonferroni test | |
---|---|---|---|---|---|---|---|
Lower bound | Upper bound | P | |||||
Unexposed tooth | 4 | 32.6 ± 16.3 nm | 8.1 | 6.7077 | 58.5478 | 0.021 | 0.021,2 |
Exposed tooth + HCI | 4 | 101.9 ± 18.0 nm | 9.0 | 73.1958 | 130.5232 | 0.2951,5 | |
Exposed tooth + HCI + Colgate | 4 | 65.2 ± 29.0 nm | 14.5 | 19.0787 | 111.4123 | 0.9921,3 | |
Exposed tooth + HCI + Senosdyne | 4 | 83.1 ± 33.7 nm | 16.8 | 29.4663 | 136.6767 | 0.1591,4 | |
Exposed tooth + EB@TiO2 | 4 | 57.2 ± 29.6 nm | 14.8 | 10.0747 | 104.3583 | 1.001,5 |
Superscript numbers indicate significant differences between the sample groups (ANOVA, P < 0.05).
Comparing the unexposed specimens (group 1) with specimens exposed to HCI alone (group 2), a significant difference were measured (P < 0.05). The unexposed specimens had the lowest mean Rrms (32.6 ± 16.3 nm) values while specimens exposed to HCI alone had the highest value (101.9 ± 18.0 nm). No significant differences were measured for the unexposed specimens and the specimens exposed in groups 3, 4, and 5, respectively (P > 0.05). AFM micrograph shown in Figure 3 further illustrates the surface profile of the specimens. The surface roughness appeared more pronounced for Figures 3(b)–3(d) when compared against Figures 3(a) and 3(e).
3.2. Field-Scanning Electron Microscope Observation of Specimens
The FESEM images of the specimens are shown in Figure 4. The images revealed surface differences between the unexposed specimens, exposed tooth alone, and the test groups (EB@TiO2 and commercial toothpastes). While using the unexposed specimen to benchmark the demineralization of the exposed sample groups, the images in Figures 4(b) and 3(d) visibly showed evidence of the prismatic destruction of the hydroxyapatites which suggest erosion of tooth specimens exposed to acid alone and the Sensodyne toothpaste. In contrast, the tooth specimen exposed to acid in the presence of both EB@TiO2 and Colgate showed less evidence of the prismatic destruction of the enamel (Figures 4(c) and 3(e)).
3.3. Raman Spectroscopy
Furthermore, the changes in the position of phosphates (V3 (PO43−)) peaks for the unexposed and exposed specimens are given in Figure 4. In the unexposed specimens, the peak was only slightly prominent (Figure 5). On the other hand, the peaks for the specimen exposed in HCI alone (Figure 5) were distinctly prominent to a considerable height (Table 3). Moreover, only slight changes were noticed in the peaks of the specimens exposed to sample groups 3 (Figure 5), 4 (Figure 5), and 5 (Figure 5), respectively.
Table 3.
Sample groups | Peak parameters | |
---|---|---|
Height | Area | |
Unexposed tooth | 2454.2 | 32769.3 |
Tooth exposed to HCI | 18853.3 | 345765.1 |
Tooth exposed to HCI + Colgate toothpaste | 3956.9 | 52589.4 |
Tooth exposed to HCI + Sensodyne | 4270.3 | 73357.7 |
Tooth exposed to HCI + EB@TiO2 | 2965.9 | 49185.4 |
4. Discussion
The purpose of this study was to examine the protective effect of a modified eggshell-titanium dioxide composite (EB@TiO2) in comparison with some commercial toothpastes against erosive acids. In line with suggested techniques in the literature [22–24], AFM was used to characterize and measure the changes in the surface roughness pre- and postexposure to HCI. The average mean square roughness values (Rrms) measured were used for statistical analysis. The Rrms is the standard deviation height obtained from the AFM images (Figure 3) in areas of 30 × 30 µm2 with a resolution of 256 × 256 pixels. The Rrms data demonstrated that exposure of tooth enamel to HCI significantly affected the surface roughness (P < 0.05).
More so, the Rrms values measured for the enamel tooth specimens exposed to HCI alone group were significantly higher than the unexposed tooth enamel (P < 0.05). This strongly confirmed that the exposure of enamel to acidic substances leads to enamel demineralization. Whilst tooth enamel comprises mostly of calcium (Ca2+), phosphates (PO43+), and hydroxide (OH−), the enamel is constantly in equilibrium with the surrounding saliva and enamel crystals. In support of Shellis et al. [6], the exposure of the tooth enamel to HCI alone may cause enamel to release more ions to the environment to attain a new state of equilibrium. Consequently, and consistent with Lussi and Carvalho [7], the acidic condition exacerbated the process leading to enamel demineralization (Figure 4(b)).
This notwithstanding, the Rrms values measured for the enamel tooth specimen exposed to Colgate, Sensodyne, and EB@TiO2 were not different from the unexposed tooth (P > 0.05). In light of these, it can be inferred that the toothpastes (Colgate and Sensodyne) and test group (EB@TiO2) were protective against enamel demineralization. This supports the notion that the sampled toothpastes are effective and accessible vehicles to improve enamel resistant against erosive oral environment [9]. In comparing the protective effect of the sampled toothpastes samples against EB@TiO2, the Rrms values with the highest mean was for Sensodyne and the lowest for EB@TiO2 (Table 2). This could have been attributed to the presence of Ca and or titanium ions in the exposed tooth in the presence of EB@TiO2. More so, and given the differences in the mean Rrms values between EB@TiO2 and Colgate toothpaste, the observed differences appear to reflect the buffering capacities of the 2 groups (Table 1). This strongly supports Caneppele et al. [25] that the buffering capacity of acidic concentration is critical in erosive potential of acidic substance, which may influence the dissolution rate of the enamel. Equally, the differences in the Rrms values between EB@TiO2 and Colgate toothpastes may also be associated with the modification of the calcium carbonate constituents of eggshell with titanium dioxide. Hence, the tested hypothesis is partially accepted as the EB@TiO2 composite effectively protected the tooth enamel against erosion.
Furthermore, the Raman spectrum of the exposed and unexposed tooth enamel observed at a peak of 960 cm−1 could be attributed to the symmetrical stretching of the tetrahedron oxygen atoms that surrounds the phosphorus atoms [26, 27]. This result is consistent with Ionita [28] that Raman spectrum of healthy enamel and demineralized tooth is observed at a well-defined peak at 959 cm−1 vibrations. Moreover, the highest-Raman spectrum demineralization intensity observed for the exposed tooth alone in HCI was nearly 5-times greater than the intensity measured for the unexposed tooth (Figure 5). In addition, He et al. [29] and Targino et al. [30] theorize that the mineral intensity measured in Raman could be a factor that determines the rate of demineralization of tooth enamel. Significantly, the Raman intensity measured for EB@TiO2 was comparable to those measured for Colgate toothpaste; however, it was lower than the sampled Sensodyne toothpaste (Figure 5). This observation is consistent with the results of Joiner et al. [16] which show that the addition of calcium and or calcium containing materials into toothpaste improves its resistant against acidic erosion on tooth enamel.
In light of the above findings, the researchers plan to further examine the remineralization potential of EB@TiO2, particularly in the repair of damaged tooth (enamel and dentine). These studies would help establish the suitability of EB@TiO2 in the maintenance of oral health particularly as a desensitising toothpaste.
5. Conclusion
In conclusion, this study has demonstrated that toothpastes provide protection to the tooth enamel against erosive substance. Notably, the study has shown that EB@TiO2 offer better protective covering to the enamel against acid attack.
Acknowledgments
The authors acknowledge the financial support from the National Research Foundation of South Africa (no. 104824).
Data Availability
The data used to support the findings of this study are included within the article.
Conflicts of Interest
No conflicts of interest declared.
References
- 1.Gambon D., Brand H., Veerman E. Dental erosion in the 21st century: what is happening to nutritional habits and lifestyle in our society? British Dental Journal. 2012;213(2):55–57. doi: 10.1038/sj.bdj.2012.613. [DOI] [PubMed] [Google Scholar]
- 2.Lombardini M., Ceci M., Colombo M., Bianchi S., Poggio C. Preventive effect of different toothpastes on enamel erosion: AFM and SEM studies. Scanning. 2014;36(4):401–410. doi: 10.1002/sca.21132. [DOI] [PubMed] [Google Scholar]
- 3.West N., Seong J., Hellin N., Eynon H., Barker M., He T. A clinical study to measure anti-erosion properties of a stabilized stannous fluoride dentifrice relative to a sodium fluoride/triclosan dentifrice. International Journal of Dental Hygiene. 2017;15(2):113–119. doi: 10.1111/idh.12159. [DOI] [PubMed] [Google Scholar]
- 4.Harding M., Whelton H., O’Mullane D., Cronin M. Dental erosion in 5-year-old Irish school children and associated factors: a pilot study. Community Dental Health. 2003;20(3):165–170. [PubMed] [Google Scholar]
- 5.Luo Y., Zeng X., Du M., Bedi R. The prevalence of dental erosion in preschool children in China. Journal of Dentistry. 2005;33(2):115–121. doi: 10.1016/j.jdent.2004.08.007. [DOI] [PubMed] [Google Scholar]
- 6.Shellis R. P., Featherstone J. D., Lussi A. Erosive Tooth Wear. Basel, Switzerland: Karger Publishers; 2014. Understanding the chemistry of dental erosion; pp. 163–179. [DOI] [PubMed] [Google Scholar]
- 7.Lussi A., Carvalho T. S. Analyses of the erosive effect of dietary substances and medications on deciduous teeth. PLoS One. 2015;10(12) doi: 10.1371/journal.pone.0143957.e0143957 [DOI] [PMC free article] [PubMed] [Google Scholar]
- 8.Lussi A., Jaeggi T. Erosion—diagnosis and risk factors. Clinical Oral Investigations. 2008;12(S1):5–13. doi: 10.1007/s00784-007-0179-z. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 9.Kato M., Lancia M., Sales-Peres S., Buzalaf M. Preventive effect of commercial desensitizing toothpastes on bovine enamel erosion in vitro. Caries Research. 2010;44(2):85–89. doi: 10.1159/000282668. [DOI] [PubMed] [Google Scholar]
- 10.Ganss C., Schulze K., Schlueter N. Toothpastes. Basel, Switzerland: Karger Publishers; 2013. Toothpaste and erosion. [Google Scholar]
- 11.Almosa N. A., Lundgren T., Aldrees A. M., Birkhed D., Kjellberg H. Diagnosing the severity of buccal caries lesions in governmental and private orthodontic patients at debonding, using the ICDAS-II and the DIAGNOdent Pen. The Angle Orthodontist. 2013;84(3):430–436. doi: 10.2319/051313-371.1. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 12.Krithikadatta J., Fredrick C., Abarajithan M., Kandaswamy D. Remineralisation of occlusal white spot lesion with a combination of 10% CPP-ACP and 0.2% sodium fluoride evaluated using diagnodent: a pilot study. Oral Health & Preventive Dentistry. 2013;11(2):191–196. doi: 10.3290/j.ohpd.a29736. [DOI] [PubMed] [Google Scholar]
- 13.Barbour M., Finke M., Parker D., Hughes J., Allen G., Addy M. The relationship between enamel softening and erosion caused by soft drinks at a range of temperatures. Journal of Dentistry. 2006;34(3):207–213. doi: 10.1016/j.jdent.2005.06.002. [DOI] [PubMed] [Google Scholar]
- 14.Moron B. M., Miyazaki S., Ito N., et al. Impact of different fluoride concentrations and pH of dentifrices on tooth erosion/abrasion in vitro. Australian Dental Journal. 2013;58(1):106–111. doi: 10.1111/adj.12016. [DOI] [PubMed] [Google Scholar]
- 15.Larsen M., Richards A. Fluoride is unable to reduce dental erosion from soft drinks. Caries Research. 2002;36(1):75–80. doi: 10.1159/000057595. [DOI] [PubMed] [Google Scholar]
- 16.Joiner A., Schäfer F., Hornby K., et al. Enhanced enamel benefits from a novel fluoride toothpaste. International Dental Journal. 2009;59(S4):244–253. [Google Scholar]
- 17.King’Ori A. A review of the uses of poultry eggshells and shell membranes. International Journal of Poultry Science. 2011;10(11):908–912. [Google Scholar]
- 18.Onwubu S., Vahed A., Singh S., Kanny K. Physicochemical characterization of a dental eggshell powder abrasive material. Journal of Applied Biomaterials and Functional Materials. 2017;15(4) doi: 10.5301/jabfm.5000361. [DOI] [PubMed] [Google Scholar]
- 19.Lin H., Dong Y.-b., Jiang L.-y. Preparation of calcium carbonate particles coated with titanium dioxide. International Journal of Minerals, Metallurgy and Materials. 2009;16(5):592–597. doi: 10.1016/s1674-4799(09)60102-3. [DOI] [Google Scholar]
- 20.Tao H., He Y., Zhao X. Preparation and characterization of calcium carbonate–titanium dioxide core–shell (CaCO3@TiO2) nanoparticles and application in the papermaking industry. Powder Technology. 2015;283:308–314. doi: 10.1016/j.powtec.2015.05.039. [DOI] [Google Scholar]
- 21.Onwubu S. C., Vahed A., Singh S., Kanny K. M. Reducing the surface roughness of dental acrylic resins by using an eggshell abrasive material. Journal of Prosthetic Dentistry. 2017;117(2):310–314. doi: 10.1016/j.prosdent.2016.06.024. [DOI] [PubMed] [Google Scholar]
- 22.Shellis R., Barbour M., Jones S., Addy M. Effects of pH and acid concentration on erosive dissolution of enamel, dentine, and compressed hydroxyapatite. European Journal of Oral Sciences. 2010;118(5):475–482. doi: 10.1111/j.1600-0722.2010.00763.x. [DOI] [PubMed] [Google Scholar]
- 23.Kim I.-H., Son J. S., Min B. K., Kim Y. K., Kim K.-H., Kwon T.-Y. A simple, sensitive and non-destructive technique for characterizing bovine dental enamel erosion: attenuated total reflection Fourier transform infrared spectroscopy. International Journal of Oral Sciences. 2016;8(1):54–60. doi: 10.1038/ijos.2015.58. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 24.Pereira D. L., Freitas A. Z., Bachmann L., Benetti C., Zezell D. M., Ana P. A. Variation on molecular structure, crystallinity, and optical properties of dentin due to Nd: YAG laser and fluoride aimed at tooth erosion prevention. International Journal of Molecular Sciences. 2018;19(2):p. 433. doi: 10.3390/ijms19020433. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 25.Caneppele T. M. F., Jeronymo R. D. I., Di Nicoló R., de Araújo M. A. M., Soares L. E. S. In Vitro assessment of dentin erosion after immersion in acidic beverages: surface profile analysis and energy-dispersive X-ray fluorescence spectrometry study. Brazilian Dental Journal. 2012;23(4):373–378. doi: 10.1590/s0103-64402012000400011. [DOI] [PubMed] [Google Scholar]
- 26.Ramakrishnaiah R., Gu R., Basavarajappa S., et al. Applications of Raman spectroscopy in dentistry: analysis of tooth structure. Applied Spectroscopy Reviews. 2015;50(4):332–350. doi: 10.1080/05704928.2014.986734. [DOI] [Google Scholar]
- 27.Silveira J., Coutinho S., Marques D., et al. Raman spectroscopy analysis of dental enamel treated with whitening product–Influence of saliva in the remineralization. Spectrochimica Acta Part A: Molecular and Biomolecular Spectroscopy. 2018;198:145–149. doi: 10.1016/j.saa.2018.03.007. [DOI] [PubMed] [Google Scholar]
- 28.Ionita I. Diagnosis of tooth decay using polarized micro-Raman confocal spectroscopy. Romanian Reports in Physics. 2009;61:567–574. [Google Scholar]
- 29.He B., Huang S., Zhang C., Jing J., Hao Y., Xiao L. Mineral densities and elemental content in different layers of healthy human enamel with varying teeth age. Archives of Oral Biology. 2011;56(10):997–1004. doi: 10.1016/j.archoralbio.2011.02.015. [DOI] [PubMed] [Google Scholar]
- 30.Targino A. G., Rosenblatt A., Oliveira A. F., Chaves A. M., Santos V. E. The relationship of enamel defects and caries: a cohort study. Oral Diseases. 2011;17(4):420–426. doi: 10.1111/j.1601-0825.2010.01770.x. [DOI] [PubMed] [Google Scholar]
Associated Data
This section collects any data citations, data availability statements, or supplementary materials included in this article.
Data Availability Statement
The data used to support the findings of this study are included within the article.