Correction for Li et al., Pressure-induced phase transitions and superconductivity in a black phosphorus single crystal

PHYSICS Correction for “Pressure-induced phase transitions and superconductivity in a black phosphorus single crystal,” by Xiang Li, Jianping Sun, Prashant Shahi, Miao Gao, Allan H. MacDonald, Yoshiya Uwatoko, Tao Xiang, John B. Goodenough, Jinguang Cheng, and Jianshi Zhou, which was first published September 14, 2018; 10.1073/pnas.1810726115 (Proc Natl Acad Sci USA 115:9935–9940).

The authors note that on page 9937, right column, first paragraph, line 2, “1.3 × 10⁴ cm²·V^–1·s^–1” should instead appear as “1.3 × 10⁵ cm²·V^–1·s^–1”; and, on page 9939, left column, first paragraph, lines 8–9, “4.4 nm^–2 at 1 GPa, ∼26.8 nm^–2 at 2 GPa, and ∼65.8 nm^–2 at 3 GPa” should instead appear as “∼0.044 nm^–2 at 1 GPa, ∼0.268 nm^–2 at 2 GPa, and ∼0.658 nm^–2 at 3 GPa.”

The authors also note that, on page 9937, right column, first paragraph, line 4, “(16)” should instead appear as “(21).”

Lastly, the authors note that Fig. 3 appeared incorrectly. The corrected figure and its legend appear below.

Fig. 3.

(A–G) The fitting parameters from the transport properties and superconducting transition temperature as a function of pressure across A17, A7, and C phases. Error bars are smaller than symbols.