Enhancement of Rhodamine B Degradation by Ag Nanoclusters-Loaded g-C3N4 Nanosheets

Thi Mai Oanh Le 1, Thi Hang Lam 1,2, Thi Nhung Pham 1, Tuan Cuong Ngo 3, Ngoc Diep Lai 4, Danh Bich Do 1,*, Van Minh Nguyen 1
PMCID: PMC6403959  PMID: 30966667

Abstract

In this paper, silver (Ag) nanoclusters-loaded graphitic carbon nitride (g-C3N4) nanosheets are synthesized and their physical properties as well as photocatalytic activities are systematically investigated by different techniques. The existence of Ag atoms in the form of nanoclusters (NCs) rather than well-crystallized nanoparticles are evidenced by X-ray diffraction patterns, SEM images, and XPS spectra. The deposition of Ag nanoclusters on the surface of g-C3N4 nanosheets affect the crystal structure and slightly reduce the band gap energy of g-C3N4. The sharp decrease of photoluminescence intensity indicates that g-C3N4/Ag heterojunctions successfully prevent the recombination of photo-generated electrons and holes. The photocatalytic activities of as-synthesized photocatalysts are demonstrated through the degradation of rhodamine B (RhB) solutions under Xenon lamp irradiation. It is demonstrated that the photocatalytic activity depends strongly on the molar concentration of Ag+ in the starting solution. The g-C3N4/Ag heterojunctions prepared from 0.01 M of Ag+ starting solution exhibit the highest photocatalytic efficiency and allow 100% degradation of RhB after being exposed for 60 min under a Xenon lamp irradiation, which is four times faster than that of pure g-C3N4 nanosheets.

Keywords: photocatalyst, g-C3N4 nanosheet, Ag nanoclusters, degradation

1. Introduction

Graphitic carbon nitride (g-C3N4), an emerging graphene-like material, has received much attention for its use in numerous applications such as photocatalytic degradation of organic pollutants, conversion of carbon dioxide into hydrocarbons, production of hydrogen and oxygen, etc. The widespread use of the material is owed to its suitable characteristics in crystal structure, surface morphology, and band gap energy as well as its high thermal and chemical stability [1,2]. The band gap of 2.7 eV makes g-C3N4 an excellent candidate for high conversion efficiency under visible light, particularly in the wavelength range of 400–460 nm [3]. Moreover, g-C3N4 is inexpensive, abundant, and eco-friendly, making it the most attractive photocatalyst in the field of environmental protection and energy conservation [4]. Nevertheless, photocatalytic performance of pure g-C3N4 can still be further enhanced in several ways, such as increasing surface area, reducing electron-hole recombination rate, and broadening visible light absorption region to a longer wavelength [5,6].

Various studies have been carried out to improve photocatalytic activities of g-C3N4 via the above approaches [7,8,9,10,11,12]. Among them, producing heterojunctions between g-C3N4 and other semiconductors or metal nanoparticles (NPs) has been proven to be an effective solution to separate photo-generated electron-hole pairs and prevent their recombination [9,13,14,15]. Lately, loading noble metal NPs such as Pt [15,16], Au [17,18], Pd [19,20], and Ag [21,22] on the surface of g-C3N4 nanosheets have been reported as an efficient routine to enhance photocatalytic performance of g-C3N4. This is because noble metal NPs can act as excellent electron acceptors [23], thus reducing the recombination rate of electron-hole pairs in g-C3N4 nanosheets and also improving visible-light absorbance [13]. It is important to note that the photocatalytic ability depends strongly on the size of metal NPs. Previous reports have shown that small NPs exhibit strong photocatalytic performance [24,25] due to the high reactivity of unsaturated atoms on the surface of small particles. In particular, when the particle size decreases to subnanometer scale, the NPs are just nanoclusters (NCs) of metal atoms, not crystalline, and they can exhibit interesting photocatalytic abilities [24,26].

In this paper, we report a simple and environmental-friendly approach to synthesize g-C3N4/Ag heterojunctions in which the surface of g-C3N4 nanosheets are decorated with Ag NCs to demonstrate the use of the material as an excellent candidate for photodegradation of rhodamine B (RhB). To avoid the leakage of Ag metal into the environment and to determine the optimum loading concentration of Ag NCs on the surface of g-C3N4 nanosheets, we investigate the dependence of photocatalytic activity of Ag cluster-loaded g-C3N4 on the concentration of Ag+ in the starting solution.

2. Experiments

2.1. Materials

Urea (NH2CONH2, >98%) purchased from Sigma-Aldrich Co. (St. Louis, MO, USA) was used in the polymerization process of g-C3N4 nanosheets. To synthesize Ag nanoclusters, the precursors were prepared from silver nitrate (AgNO3, >99%), a product of Sigma-Aldrich Co. (St. Louis, MO, USA). Ethanol (CH3CH2OH), a product of Merck (Darmstadt, Germany), was used as a supporting solvent for washing the residual chemical substance contained in the as-synthesized materials. The water used was double distilled to remove unwanted contaminants. All chemical reagents were used as received without further purification.

2.2. Synthesis of g-C3N4

Unlike previous reports [11], in this study, g-C3N4 was synthesized through urea polymerization in air. In a typical process, 5 g of urea (≥98%, Sigma-Aldrich) was stored in an alumina crucible, which was then covered with an aluminum foil. The crucible was heated to 550 °C in a furnace for 2 h in air. An amount of 0.5 g of bright yellow obtained powder was added into 50 mL of distilled water. The solution was then ultrasonically vibrated for 1 h at room temperature to homogenously disperse g-C3N4 nanosheets in water.

2.3. Synthesis of Ag Nanoclusters-Loaded g-C3N4

The deposition of Ag NCs on the surface of g-C3N4 nanosheets was carried out through a simple process without the support of light irradiation. In order to create Ag+ starting solution with different Ag+ molar concentrations of 0.005 M, 0.007 M, 0.01 M, 0.03 M, 0.05 M, and 0.1 M, respectively, various amounts of AgNO3 were added to 50 mL of distilled water. This solution was then poured into the as-prepared, well-dispersed g-C3N4 nanosheets solution. The suspension was magnetically stirred in the dark for 9 h at a temperature of 90 °C. The grey precipitates were washed three times with distilled water and once with ethanol using an ultrasound vibration and a centrifuge machine at the speed of 4000 rpm. Finally, the obtained powder was dried under vacuum at 60 °C for 10 h before any characterization.

Ag nanocluster-loaded g-C3N4 nanosheets synthesized in starting solutions with various Ag+ molar concentrations were labeled as gCN/Ag xM, where x refers to the Ag+ molar concentrations (x = 0.005, 0.007, 0.01, 0.03, 0.05, 0.1, respectively).

2.4. Characterizations

X-ray diffraction (XRD) patterns of Ag cluster-loaded g-C3N4 nanosheets were recorded by a D8 Advance diffractometer (Bruker, Billerica, MA, USA) using Cu-Kα radiation. UnitCell software was used to calculate the lattice parameters of sample from the XRD data. The morphology of as-synthesized samples was carried out by scanning electron microscopy (SEM) technique (S-4800 NIHE microscope, Hitachi, Tokyo, Japan) and transmission electron spectroscopy (TEM) (FEI Tecnai G2 20 TEM). X-ray photoelectron spectroscopy (XPS) was carried out on the Multilab-2000 spectrometer with an Al Kα monochromatized source. Ultraviolet-visible (UV-vis) absorption spectra of the samples were recorded using a Jasco V670 UV-vis spectrophotometer. Fourier transform infrared spectra (FT-IR) were collected on an IR Prestige-21 FT-IR/NIR spectrometer (Shimadzu, Kyoto, Japan). Photoluminescence (PL) spectra were also performed on a fluorescence spectrophotometer (Nanolog iHR 320, Horiba, Kyoto, Japan) using an excitation wavelength of 350 nm.

2.5. Investigation of Photocatalytic Activity

In order to assess the photocatalytic performance of as-synthesized g-C3N4/Ag heterojunctions, the degradation of RhB solution was carried out under the presence of g-C3N4/Ag heterojunctions using the irradiation of Xenon lamp. In a typical experiment, 0.06 g of Ag cluster-loaded g-C3N4 nanosheets were dispersed in 30 mL of distilled water using ultrasonic vibrating for 1 h. An amount of 30 mL of RhB 20 ppm aqueous solution was poured into the as-prepared dispersion under magnetic stirring to achieve a final solution of RhB 10 ppm. Before irradiation, the whole solution was magnetically stirred in a dark chamber for 30 min to reach an adsorption-desorption equilibrium state between RhB molecules and Ag cluster-loaded g-C3N4 nanosheets. An amount of 3 mL of suspension was taken from the reactor every 10 min and centrifuged to remove g-C3N4. The relative concentration of RhB in the solution as a function of time was evaluated by measuring the intensity of the absorption peak at 554 nm using UV-vis spectrophotometer.

3. Results and Discussion

The XRD patterns of the as-prepared samples are shown in Figure 1a. It is obvious that pure g-C3N4 and Ag cluster-loaded g-C3N4 nanosheets synthesized with different Ag+ concentrations exhibited similar X-ray diffraction patterns. As can be seen, pure g-C3N4 sample exhibited three peaks at around 13.00, 24.93, and 27.65° which were attributed to (100), (101), and (002) diffraction planes, respectively, of the hexagonal phase of graphitic carbon nitride (JCPDS card no. 87-1526). It was found that XRD intensity of Ag cluster-loaded g-C3N4 samples decreased gradually with increasing Ag+ concentrations in the starting solutions. Additionally, the position of (002) peak shifted slightly toward smaller value of 2θ angle. In order to clearly observe the shift of peak position, (002) peaks were normalized to the same intensity and fitted using Gaussian function. Figure 1b shows fitting curves of (002) peak of the as-prepared samples, and the peak position shift is clearly seen. These observations indicate that Ag nanoclusters have a certain influence on the crystal structure of g-C3N4. However, it is noted that no diffraction peak corresponding to Ag crystal was observed in any of the Ag cluster-loaded g-C3N4 samples. This may be ascribed to the low concentration of Ag on the surface of g-C3N4 as well as the amorphous nature of Ag NCs/NPs.

Figure 1.

Figure 1

Open in a new tab

(a) XRD diffraction patterns of the as-prepared samples, (b) the fitting curves of (002) peak of the as-prepared samples.

Figure 2 depicts TEM images of the as-prepared samples. As shown in Figure 2a,b, the morphology of pure g-C3N4 nanosheets is composed of thin layer structures like silk pieces, which is consistent with previous reported results [27,28]. Figure 2c,d demonstrate the presence of dense and homogenous distribution of Ag NCs and Ag NPs decorated on the surface of g-C3N4 nanosheets in the g-C3N4/Ag 0.01 M and g-C3N4/Ag 0.1 M samples. This observation suggests that Ag NPs can act as electron storage tanks, preventing the recombination of photogenerated electron-hole pairs. Inset of Figure 2c displays the histogram of Ag NCs diameters which shows the size of the particles is between 3 and 5 nm (average diameter of 4 nm). This small size means that Ag NPs are more like Ag atom nanoclusters than well-crystallized particles. Figure 2d shows that as the concentration of Ag+ increases, the Ag-nanoclusters become nanoparticles with an average size of 30 nm. Additionally, no crystallite formation was found (inset of Figure 2d), which reflects the amorphous nature of NPs. These TEM, HRTEM results partly explain the absence of diffraction peaks of Ag crystal in XRD results.

Figure 2.

Figure 2

Open in a new tab

TEM images of the as-prepared (a,b) pure g-C3N4 sample, (c) g-C3N4/Ag 0.01 M sample, and (d) g-C3N4/Ag 0.1 M sample. Inset of figure (c) shows a histogram of Ag NCs diameters. Inset of figure (d) shows the HRTEM image of a single Ag nanoparticle at the magnification of 285000X.

Since the XPS technique can elucidate the chemical compositions and chemical status of different elements on the surface of materials, XPS spectra were carried out to further demonstrate the deposition of Ag nanoclusters on the surface of g-C3N4 (Figure 3). XPS survey spectra of both pure g-C3N4 (upper curve) and gCN/Ag 0.01 M (lower curve) samples (Figure 3a) exhibited three peaks at about 287 (C1s), 400 (N1s), and 534 eV (O1s) which were assigned to the presence of C, N, and O elements, respectively, while Ag element was detected in gCN/Ag 0.01 M sample at a binding energy of about 368 eV. Figure 3b shows a zoom-in of the XPS spectra of the C1s peaks for pure g-C3N4 nanosheets where four secondary peaks with binding energy of 285.5, 287.1, 288.7, and 289.5 eV could be ascribed to: (1) the sp2 graphitic carbon (C-C), (2) C=N resulting from defect-containing C atoms, (3) the sp2-hybridized C atoms bonded with N atoms in the s-triazine units (N-C=N), and (4) the sp3-hybridized carbon atoms (C-(N)3) in the g-C3N4 lattice, respectively [15,29,30]. The high resolution XPS spectra of the N1s peak for pure g-C3N4 are shown in Figure 3c. This peak was also mainly decomposed into three component peaks centered at about 398.3, 399.7, and 401.7 eV, which corresponded to: (1) pyridinic N, (2) pyrrolic N, and (3) graphitic (quaternary) N, respectively [31,32,33]. In particular, it can be noted that all component peaks for the C1s and N1s peaks shifted to lower energy binding value when Ag NCs deposited on the surface of g-C3N4, suggesting an electronic interaction between g-C3N4 and Ag NCs. This observation is similar to those reported by some previous studies [15,34]. Finally, the high resolution XPS spectrum of the Ag3d peak displayed in Figure 3d exhibited two typical peaks at about 368.1 and 374.1 eV, which represented the Ag3d3/2 and Ag3d5/2 binding energy of the metallic Ago [35]. The results observed in both XRD patterns and XPS analysis suggest that Ag cluster-loaded g-C3N4 nanosheets were well synthesized, and the deposition of Ag NCs caused a certain influence on the crystal structure as well as the electronic state of the elements on the surface of g-C3N4 nanosheets. In other words, there was a certain interaction—or even a good cohesion—between Ag NCs and g-C3N4 nanosheets, which may become a good channel for photogenerated electron-hole pairs transferring.

Figure 3.

Figure 3

Open in a new tab

(a) XPS survey spectra. XPS spectra of (b) C1s, (c) N1s and (d) Ag3d of pure g-C3N4 and g-C3N4/Ag 0.01M samples.

The optical properties of as-synthesized samples were investigated using UV-vis diffused reflectance spectroscopy and photoluminescence (PL) spectroscopy. As can be seen in Figure 4a, pure g-C3N4 nanosheets exhibited an absorption edge at about 430 nm and the absorption edges of the Ag cluster-loaded g-C3N4 samples shifted slightly to a longer wavelength, indicating a gradually narrowing band gap. Accordingly, the band gap energy, which was estimated using the Tauc’s plot (the inset of Figure 4a) for indirect semiconductor, decreased from 2.88 eV for pure g-C3N4 nanosheet to 2.82 eV for gCN/Ag 0.01 M sample. Moreover, Figure 4a also presents an increase of absorbance around 400 nm (the upward solid arrow) for Ag NCs-loaded g-C3N4 samples, which can be ascribed to absorption due to the surface plasmon resonance (SPR) of Ag NPs [36,37]. These hot SPR electrons in turn can be injected inversely from Ag NPs to g-C3N4 nanosheets, which is called charge transfer due to SPR effect (CTSPR in Figure 5), enhancing the number of active •O2− radicals on the g-C3N4 surface, while the h+ remaining in Ag NPs promotes the production of active •OH radicals on Ag NPs surface [38,39]. On the other hand, SPR electrons can also transfer their energy to stimulate the production of electron-hole pairs in g-C3N4 nanosheets. Therefore, the high absorbance in Ag cluster-loaded samples due to SPR effect promises a contribution to the degradation of RhB.

Figure 4.

Figure 4

Open in a new tab

(a) UV-vis diffuse reflectance and (b) photoluminescence (PL) spectra of as-synthesized samples with different Ag+ concentrations.

Figure 5.

Figure 5

Open in a new tab

Charge transfer pathways through g-C3N4/Ag heterojunctions and the generation of active •O2- and •OH radicals on g-C3N4/Ag heterojunctions.

Room temperature PL spectra of as-synthesized samples were carried out to investigate the separation behavior of electron-hole pairs through heterojunctions between Ag NPs and g-C3N4 nanosheets (Figure 4b). It is obvious that pure g-C3N4 nanosheets presented strong PL intensity, indicating a high recombination rate of electron and hole pairs. By contrast, PL intensity of Ag nanoclusters-loaded g-C3N4 samples decreased distinctly with increasing Ag+ concentration; the lowest PL intensity was obtained by the g-C3N4/Ag sample having a concentration of 0.01 M. This behavior has been interpreted as the consequence of charge transfer from g-C3N4 to Ag NCs/NPs due to the energy difference between conduction band (CB) bottom level of g-C3N4 and Fermi level of Ag NCs/NPs [38]. Therefore, Ag NCs/NPs can act as the “trap” of photogenerated electrons, effectively preventing the recombination of electron-hole pairs in g-C3N4 nanosheets. For the Ag-NCs of small sizes, the excited energy levels (LUMO) is high and reach the conduction band of the g-C3N4, therefore facilitating the charge transfers from the g-C3N4 substrate to the Ag-NCs and quenching the photoluminescence. From the gCN/Ag-0.005 M sample to the gCN/Ag-0.01 M sample, the amount of Ag-NCs increase and we see the decrease in PL intensity, as shown in Figure 4b. As the concentration of Ag+ increases, the formed Ag-NCs become larger as shown in Figure 2d. This will result in a reduction in the LUMO level of the Ag-quantum dots, being lower than CB of the g-C3N4 substrate. The electron transfer from CB of g-C3N4 to the LUMO level of Ag-NCs will be less supported, as seen in Figure 4b, and the PL intensities of the gCN/Ag-0.03 M, gCN/Ag-0.05 M and gCN/Ag-0.1 M samples are stronger than that of the gCN/Ag-0.01 M sample [40]. The charge transfer due to these “trap” (CTtrap in Figure 5) can also make an important contribution to the enhancement of photocatalytic activity.

The photocatalytic performances of g-C3N4 and gCN/Ag samples were estimated through the degradation of RhB under irradiation of a Xenon lamp. The degradation rate of RhB was quantified indirectly through the variation of 554 nm absorption peak intensity of RhB solution using a standard curve relating RhB concentration to absorbance. Figure 6a displays the dependence of concentration ratio C/Co on time. The role of adsorption and photocatalysis was assessed separately by stirring 30 min in dark and then 120 min exposed under Xenon lamp irradiation. Obviously, the adsorption process of all samples mostly took place after 10 min of stirring in dark, ensuring that the adsorption-desorption equilibrium state of suspension can be completely achieved after 30 min. Figure 6a shows all Ag NCs/NPs-loaded g-C3N4 samples displayed a remarkable enhancement of both adsorption and photocatalytic efficiency. While about 25% of RhB still existed after 120 min of irradiation using pure g-C3N4 nanosheets, some loaded samples such as gCN/Ag 0.01 M, gCN/Ag 0.03 M, and gCN/Ag 0.1 M degraded almost 100% of RhB after just 60 min. The gCN/Ag 0.01 M sample presented strongest photocatalytic activity in RhB decomposing which was evidenced by the largest slope of C/Co curve. The order of samples in which photocatalytic efficiency is increasing is g-C3N4, gCN/Ag 0.005 M, gCN/Ag 0.007 M, gCN/Ag 0.05 M, gCN/Ag 0.1 M, gCN/Ag 0.03 M, gCN/Ag 0.01 M, and gCN/Ag 0.01 M. Figure 6b exhibits the obvious change of RhB concentration in UV-vis absorption spectra of gCN/Ag 0.01 M heterojunction as a function of time. After 50 min exposure to Xenon lamp irradiation, the 554 nm absorption peak of RhB not only disappeared completely but also shifted from 554 nm to 530 nm, demonstrating the decomposition of conjugated structure of RhB [41]. This enhancement of photocatalytic activity in loaded samples can be adequately explained by the assumption that photogenerated electrons on g-C3N4 nanosheets effectively transferred to Ag nanoclusters, which reduces the recombination rate of electrons and holes as evidenced by the obvious reduction in PL spectra. In addition, the interpretation of CTSPR as discussed in UV-vis analysis may also contribute to this sharp increase of photocatalytic performance.

Figure 6.

Figure 6

Open in a new tab

(a) Photocatalytic activities of the g-C3N4 nanosheets and g-C3N4/Ag heterojunctions with different Ag+ concentrations for degradation of RhB under xenon lamp irradiation and (b) the sharp decrease of RhB concentration in UV-vis absorption spectrum of gCN/Ag 0.01M sample as a function of time (Dx refers to stirring in dark for x minutes and Ex refers to exposing under Xenon lamp irradiation for x minutes).

4. Conclusions

It was demonstrated that g-C3N4/Ag heterojunctions, in the form of Ag nanoclusters decorated on the surface of g-C3N4 nanosheets, are an excellent candidate for degradation of the rhodamine B. The Ag NCs/NPs-loaded g-C3N4 nanosheets were successfully synthesized via a simple approach based mainly on annealing method. Ag NCs/NPs with different size were demonstrated to disperse well on the surface of g-C3N4 nanosheets and to create bonds with the atoms on the surface of g-C3N4. The photocatalytic experiment shows that the as-synthesized Ag nanoclusters-loaded g-C3N4 exhibit much better photocatalytic activity than pure g-C3N4 nanosheets. It is evident that the photocatalytic efficiency for RhB degradation strongly depends on Ag+ concentration in the starting solution and the best photocatalytic efficiency is obtained with 0.01 M of Ag+ concentration. The photocatalytic enhancement was demonstrated by the increase of photo-induced electron-hole pairs as well as the effective separation of electrons and holes via g-C3N4/Ag heterojunctions. These results also provide empirical evidence for the mechanism of quenching the photoluminescence and photocatalysis of the g-C3N4/Ag-NCs or g-C3N4/Ag-NPs composite that has been proposed in previous studies but has not really been confirmed yet.

Acknowledgments

This research is funded by Vietnam National Foundation for Science and Technology Development (NAFOSTED) under grant number 103.02-2016.46.

Author Contributions

Conceptualization by T.M.O.L., T.H.L., D.B.D., and V.M.N.; Data curation by T.H.L. and T.N.P.; Formal analysis by T.M.O.L., T.H.L., T.C.N., N.D.L., D.B.D., and V.M.N.; Investigation by T.M.O.L., T.H.L., T.N.P., and D.B.D.; Methodology by T.M.O.L., T.H.L., T.N.P., and D.B.D.; Project administration by D.B.D.; Writing—review & editing by T.M.O.L., T.H.L., T.N.P., T.C.N., N.D.L., D.B.D., and V.M.N.

Conflicts of Interest

The authors declare no conflict of interest.

References

  • 1.Zhang Y., Pan Q., Chai G., Liang M., Dong G., Zhang Q., Qiu J. Synthesis and Luminescence Mechanism of Multicolor-Emitting g-C3N4 Nanopowders by Low Temperature Thermal Condensation of Melamine. Sci. Rep. 2013;3:1943. doi: 10.1038/srep01943. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 2.Ye S., Wang R., Wu M.Z., Yuan Y.P. A Review on g-C3N4 for Photocatalytic Water Splitting and CO2 Reduction. Appl. Surf. Sci. 2015;358:15–27. doi: 10.1016/j.apsusc.2015.08.173. [DOI] [Google Scholar]
  • 3.Le S., Jiang T., Zhao Q., Liu X., Li Y., Fang B., Gong A.M. Cu-Doped Mesoporous Graphitic Carbon Nitride for Enhanced Visible-Light Driven Photocatalysis. RSC Adv. 2016;6:38811–38819. doi: 10.1039/C6RA03982K. [DOI] [Google Scholar]
  • 4.Yuan Y., Zhang L., Xing J., Utama M.I.B., Lu X., Du K., Li Y., Hu X., Wang S., Genc A., et al. High-Yield Synthesis and Optical Properties of g-C3N4. Nanoscale. 2015;7:12343–12350. doi: 10.1039/C5NR02905H. [DOI] [PubMed] [Google Scholar]
  • 5.Zhang Y., Schnepp Z., Cao J., Ouyang S., Li Y., Ye J., Liu S. Biopolymer-Activated Graphitic Carbon Nitride Towards a Sustainable Photocathode Material. Sci. Rep. 2013;3:2163. doi: 10.1038/srep02163. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 6.Pawar R.C., Kang S., Park J.H., Kim J.H., Ahn S., Lee C.S. Room-Temperature Synthesis of Nanoporous 1D Microrods of Graphitic Carbon Nitride (g-C3N4) with Highly Enhanced Photocatalytic Activity and Stability. Sci. Rep. 2016;6:31147. doi: 10.1038/srep31147. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 7.Yan H., Tian X., Pang Y., Feng B., Duan K., Zhou Z., Weng J., Wang J. Heterostructured g-C3N4/Ag/TiO2 Nanocomposites for Enhancing the Photoelectric Conversion Efficiency of Spiro-Ometad-Based Solid-State Dye-Sensitized Solar Cells. RSC Adv. 2016;6:102444–102452. doi: 10.1039/C6RA18758G. [DOI] [Google Scholar]
  • 8.Zhang S., Hang N.T., Zhang Z., Yue H., Yang W. Preparation of G-C3n4/Graphene Composite for Detecting NO2 at Room Temperature. Nanomaterials. 2017;7:12. doi: 10.3390/nano7010012. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 9.Jin J., Liang Q., Ding C., Li Z., Xu S. Simultaneous Synthesis-Immobilization of Ag Nanoparticles Functionalized 2D g-C3N4 Nanosheets with Improved Photocatalytic Activity. J. Alloys Compd. 2017;691:763–771. doi: 10.1016/j.jallcom.2016.08.302. [DOI] [Google Scholar]
  • 10.Fagan R., McCormack D.E., Hinder S.J., Pillai S.C. Photocatalytic Properties of G-C3N4–TiO2 Heterojunctions under UV and Visible Light Conditions. Mater. Lett. 2016;9:286. doi: 10.3390/ma9040286. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 11.Oanh L.T.M., Do D.B., Hang L.T., Lai N.D., Phuong N.T., Thang D.V., Hung N.M., Minh N.V. Influence of Annealing Temperature on Physical Properties and Photocatalytic Ability of g-C3N4 Nanosheets Synthesized through Urea Polymerization in Ar Atmostphere. Phys. B Condens. Matter. 2018;532:48–53. doi: 10.1016/j.physb.2017.05.026. [DOI] [Google Scholar]
  • 12.Li Q., Xu D., Ou X., Yan F. Nitrogen-Doped Graphitic Porous Carbon Nanosheets Derived from in Situ Formed g-C3N4 Templates for the Oxygen Reduction Reaction. Chem. Asian J. 2017;12:1816–1823. doi: 10.1002/asia.201700586. [DOI] [PubMed] [Google Scholar]
  • 13.Liu Y., Zhang H., Lu Y., Wu J., Xin B. A Simple Method to Prepare g-C3N4/Ag-Polypyrrole Composites with Enhanced Visible-Light Photocatalytic Activity. Catal. Commun. 2016;87:41–44. doi: 10.1016/j.catcom.2016.09.002. [DOI] [Google Scholar]
  • 14.Xu J., Wang G., Fan J., Liu B., Cao S., Yu J. g-C3N4 Modified TiO2 Nanosheets with Enhanced Photoelectric Conversion Efficiency in Dye-Sensitized Solar Cells. J. Power. Sources. 2015;274:77–84. doi: 10.1016/j.jpowsour.2014.10.033. [DOI] [Google Scholar]
  • 15.Ong W.J., Tan L.L., Chai S.P., Yong S.T. Heterojunction Engineering of Graphitic Carbon Nitride (g-C3N4) Via Pt Loading with Improved Daylight-Induced Photocatalytic Reduction of Carbon Dioxide to Methane. Dalton Trans. 2015;44:1249–1257. doi: 10.1039/C4DT02940B. [DOI] [PubMed] [Google Scholar]
  • 16.Xue J., Ma S., Zhou Y., Zhang Z., He M. Facile Photochemical Synthesis of Au/Pt/g-C3N4 with Plasmon-Enhanced Photocatalytic Activity for Antibiotic Degradation. ACS Appl. Mater. Interfaces. 2015;7:9630–9637. doi: 10.1021/acsami.5b01212. [DOI] [PubMed] [Google Scholar]
  • 17.Zhuang J., Lai W., Xu M., Zhou Q., Tang D. Plasmonic Aunp/g-C3N4 Nanohybrid-Based Photoelectrochemical Sensing Platform for Ultrasensitive Monitoring of Polynucleotide Kinase Activity Accompanying Dnazyme-Catalyzed Precipitation Amplification. ACS Appl. Mater. Interfaces. 2015;7:8330–8338. doi: 10.1021/acsami.5b01923. [DOI] [PubMed] [Google Scholar]
  • 18.Wang J., Liu R., Zhang C., Han G., Zhao J., Liu B., Jiang C., Zhang Z. Synthesis of g-C3N4 Nanosheets/Au@Ag Nanoparticles Hybrids as Sers Probe for Cancer Cells Diagnostics. RSC Adv. 2015;5:86803–86810. doi: 10.1039/C5RA16558J. [DOI] [Google Scholar]
  • 19.Konda S.K., Amiri M., Chen A. Photoassisted Deposition of Palladium Nanoparticles on Carbon Nitride for Efficient Oxygen Reduction. J. Phys. Chem. C. 2016;120:14467–14473. doi: 10.1021/acs.jpcc.6b02080. [DOI] [Google Scholar]
  • 20.Wang H.-H., Zhang B., Li X.-H., Antonietti M., Chen J.-S. Activating Pd Nanoparticles on Sol–Gel Prepared Porous G-C3N4/SiO2 via Enlarging the Schottky Barrier for Efficient Dehydrogenation of Formic Acid. Inorg. Chem. Front. 2016;3:1124–1129. doi: 10.1039/C6QI00151C. [DOI] [Google Scholar]
  • 21.Tian K., Liu W.-J., Jiang H. Comparative Investigation on Photoreactivity and Mechanism of Biogenic and Chemosythetic Ag/C3N4 Composites under Visible Light Irradiation. ACS Sustain. Chem. Eng. 2015;3:269–276. doi: 10.1021/sc500646a. [DOI] [Google Scholar]
  • 22.Jiang D., Zhang Y., Chu H., Liu J., Wan J., Chen M. N-Doped Graphene Quantum Dots as an Effective Photocatalyst for the Photochemical Synthesis of Silver Deposited Porous Graphitic C3N4 Nanocomposites for Nonenzymatic Electrochemical H2O2 Sensing. RSC Adv. 2014;4:16163–16171. doi: 10.1039/C4RA00601A. [DOI] [Google Scholar]
  • 23.Bing W., Chen Z., Sun H., Shi P., Gao N., Ren J., Qu X. Visible-Light-Driven Enhanced Antibacterial and Biofilm Elimination Activity of Graphitic Carbon Nitride by Embedded Ag Nanoparticles. Nano Res. 2015;8:1648–1658. doi: 10.1007/s12274-014-0654-1. [DOI] [Google Scholar]
  • 24.Wang X., Zhao Z., Ou D., Tu B., Cui D., Wei X., Cheng M. Highly Active Ag Clusters Stabilized on TiO2 Nanocrystals for Catalytic Reduction of P-Nitrophenol. Appl. Surf. Sci. 2016;385:445–452. doi: 10.1016/j.apsusc.2016.05.147. [DOI] [Google Scholar]
  • 25.Panigrahi S., Basu S., Praharaj S., Pande S., Jana S., Pal A., Ghosh S.K., Pal T. Synthesis and Size-Selective Catalysis by Supported Gold Nanoparticles: Study on Heterogeneous and Homogeneous Catalytic Process. J. Phys. Chem. C. 2007;111:4596–4605. doi: 10.1021/jp067554u. [DOI] [Google Scholar]
  • 26.Valden M., Lai X., Goodman D.W. Onset of Catalytic Activity of Gold Clusters on Titania with the Appearance of Nonmetallic Properties. Science. 1998;281:1647–1650. doi: 10.1126/science.281.5383.1647. [DOI] [PubMed] [Google Scholar]
  • 27.Yi J., Liao K., Zhang C., Zhang T., Li F., Zhou H. Facile in Situ Preparation of Graphitic-C3N4@Carbon Paper as an Efficient Metal-Free Cathode for Nonaqueous Li-O2 Battery. ACS Appl. Mater. Inter. 2015;7:10823–10827. doi: 10.1021/acsami.5b01727. [DOI] [PubMed] [Google Scholar]
  • 28.Su F.Y., Zhang W.D. Carbonyl-Grafted g-C3N4 Porous Nanosheets for Efficient Photocatalytic Hydrogen Evolution. Chem. Asian J. 2017;12:515–523. doi: 10.1002/asia.201601518. [DOI] [PubMed] [Google Scholar]
  • 29.Ong W.J., Putri L.K., Tan L.L., Chai S.P., Yong S.T. Heterostructured AgX/G-C3N4 (X=Cl and Br) Nanocomposites via a Sonication-Assisted Deposition-Precipitation Approach: Emerging Role of Halide Ions in the Synergistic Photocatalytic Reduction of Carbon Dioxide. Appl. Catal. B Environ. 2016;180:530–543. doi: 10.1016/j.apcatb.2015.06.053. [DOI] [Google Scholar]
  • 30.Feng L., Yang L., Huang Z., Luo J., Li M., Wang D., Chen Y. Enhancing Electrocatalytic Oxygen Reduction on Nitrogen-Doped Graphene by Active Sites Implantation. Sci. Rep. 2013;3:3306. doi: 10.1038/srep03306. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 31.Kundu S., Nagaiah T.C., Xia W., Wang Y., Dommele S.V., Bitter J.H., Santa M., Grundmeier G., Bron M., Schuhmann W., et al. Electrocatalytic Activity and Stability of Nitrogen-Containing Carbon Nanotubes in the Oxygen Reduction Reaction. J. Phys. Chem. C. 2009;113:14302–14310. doi: 10.1021/jp811320d. [DOI] [Google Scholar]
  • 32.Shao Y., Zhang S., Engelhard M.H., Li G., Shao G., Wang Y., Liu J., Aksay I.A., Lin Y. Nitrogen-Doped Graphene and Its Electrochemical Applications. J. Mater. Chem. 2010;20:7491–7496. doi: 10.1039/c0jm00782j. [DOI] [Google Scholar]
  • 33.Wang Y., Shao Y., Matson D.W., Li J., Lin Y. Nitrogen-Doped Graphene and Its Application in Electrochemical Biosensing. ACS Nano. 2010;4:1790–1798. doi: 10.1021/nn100315s. [DOI] [PubMed] [Google Scholar]
  • 34.Lu M., Pei Z., Weng S., Feng W., Fang Z., Zheng Z., Huang M., Liu P. Constructing Atomic Layer g-C3N4–CdS Nanoheterojunctions with Efficiently Enhanced Visible Light Photocatalytic Activity. Phys. Chem. Chem. Phys. 2014;16:21280–21288. doi: 10.1039/C4CP02846E. [DOI] [PubMed] [Google Scholar]
  • 35.Chen Y., Huang W., He D., Situ Y., Huang H. Construction of Heterostructured g-C3N4/Ag/TiO2 Microspheres with Enhanced Photocatalysis Performance under Visible-Light Irradiation. ACS Appl. Mater. Interfaces. 2014;6:14405–14414. doi: 10.1021/am503674e. [DOI] [PubMed] [Google Scholar]
  • 36.Mott D., Thuy N.T., Aoki Y., Maenosono S. Aqueous Synthesis and Characterization of Ag and Ag-Au Nanoparticles: Addressing Challenges in Size, Monodispersity and Structure. Philos. Trans. Ser. A Math. Phys. Eng. Sci. 2010;368:4275–4292. doi: 10.1098/rsta.2010.0120. [DOI] [PubMed] [Google Scholar]
  • 37.Charle K.P., Konig L., Nepijko S., Rabin I., Schulze W. The Surface Plasmon Resonance of Free and Emberred Ag-Clusters in the Size Range of 1.5 < D < 30 nm. Cryst. Res. Technol. 1998;33:1085–1096. [Google Scholar]
  • 38.Zhang S., Zhang B.P., Li S., Huang Z., Yang C., Wang H. Enhanced Photocatalytic Activity in Ag-Nanoparticle-Dispersed BaTiO3 Composite Thin Films: Role of Charge Transfer. J. Adv. Ceram. 2017;6:1–10. doi: 10.1007/s40145-016-0209-x. [DOI] [Google Scholar]
  • 39.Kaur R., Pal B. Plasmonic Coinage Metal–TiO2 Hybrid Nanocatalysts for Highly Efficient Photocatalytic Oxidation under Sunlight Irradiation. New J. Chem. 2015;39:5966–5976. doi: 10.1039/C5NJ00450K. [DOI] [Google Scholar]
  • 40.Sridharan K., Jang E., Park J.H., Kim J.H., Lee J.H., Park T.J. Silver Quantum Cluster (Ag9)-Grafted Graphitic Carbon Nitride Nanosheets for Photocatalytic Hydrogen Generation and Dye Degradation. Chem. Eur. J. 2015;21:9126–9132. doi: 10.1002/chem.201500163. [DOI] [PubMed] [Google Scholar]
  • 41.Gao L., Li Z., Liu J. Facile Synthesis of Ag3VO4/B-AgVO3 Nanowires with Efficient Visible-Light Photocatalytic Activity. RSC Adv. 2017;7:27515–27521. doi: 10.1039/C7RA03955G. [DOI] [Google Scholar]

Articles from Polymers are provided here courtesy of Multidisciplinary Digital Publishing Institute (MDPI)

RESOURCES