Abstract
Silicon photonics would strongly benefit from monolithically integrated low-threshold silicon-based laser operating at room temperature, representing today the main challenge toward low-cost and power-efficient electronic–photonic integrated circuits. Here we demonstrate low-threshold lasing from fully transparent nanostructured porous silicon (PSi) monolithic microcavities (MCs) infiltrated with a polyfluorene derivative, namely, poly(9,9-di-n-octylfluorenyl-2,7-diyl) (PFO). The PFO-infiltrated PSiMCs support single-mode blue lasing at the resonance wavelength of 466 nm, with a line width of ∼1.3 nm and lasing threshold of 5 nJ (15 μJ/cm2), a value that is at the state of the art of PFO lasers. Furthermore, time-resolved photoluminescence shows a significant shortening (∼57%) of PFO emission lifetime in the PSiMCs, with respect to nonresonant PSi reference structures, confirming a dramatic variation of the radiative decay rate due to a Purcell effect. Our results, given also that blue lasing is a worst case for silicon photonics, are highly appealing for the development of low-cost, low-threshold silicon-based lasers with wavelengths tunable from visible to the near-infrared region by simple infiltration of suitable emitting polymers in monolithically integrated nanostructured PSiMCs.
Keywords: silicon lasing, organic laser, porous silicon, resonant cavity, organic semiconductor, polyfluorene
Since the first report of room-temperature photoluminescence from nanostructured porous silicon (PSi),1 scientists have fantasized about PSi-based lasers,2 enabling the realization of integrated silicon photonic circuits.3 Although some trials on the fabrication of a Si nanocrystal-based laser have been attempted after the discovery of Si nanocrystal optical gain, a PSi-based laser has not been reported yet.4 In the following two decades, PSi has been more successfully used in optical biosensing5,6 and nanomedicine,7,8 owing to its vast surface-to-volume ratio (up to 1000 m2/cm3)9 and unusually long emission lifetime (5–13 μs).
Porous silicon is easily prepared via controlled electrochemical dissolution of crystalline silicon at room temperature.10 Interestingly, the mass of silicon removed for unit volume (i.e., the porosity) is proportional to the etching current density value. This provides a powerful tool to finely set PSi porosity value and profile and, in turn, to accurately tune the refractive index of PSi by simply controlling the current density value and waveform over time.11−13 In this way, a variety of mesoporous photonic structures (e.g., Bragg reflectors (DBRs),14,15 resonant microcavities (MCs),16,17 rugate filters,18,19 waveguides20) operating in both the visible and near-infrared regions were prepared in PSi through controlled modulation of the refractive index.
In the past few years, leveraging a cheap and robust material preparation technique coupled with a high flexibility and high quality in optical structure fabrication, PSi has gained renewed interest in integrated optics and photonics. Gradient refractive index (GRIN) optical elements,21 either 2D or 3D, capable of finely controlling light propagation, and resonant microcavities,22,23 either monolithic or transfer-printed, able to achieve strong light emission modification of emitter compounds have been reported. However, the presence of silicon, which has a strong absorption in the visible spectrum, has restricted the applicability of these PSi optical structures to the (near) infrared region.
In this scenario, there is nowadays an increasing effort put into the preparation of nonabsorbing PSi optical structures suitable for the UV–vis applications. Recently, Braun etal. reported on the fabrication of transparent porous silicon dioxide (PSiO2) and PSiO2/titanium dioxide (TiO2) optical elements, by either thermal oxidation or using a combination of thermal oxidation and atomic layer deposition infilling of PSi.24,25
In spite of such an intense effort, to the best of our knowledge, the original dream of a PSi-based laser with room-temperature operation, either in the visible or in the near-infrared region, has not been demonstrated yet.
In this work, we report on room-temperature lasing from monolithically integrated PSi microcavities. The laser structure consists of a high-quality, asymmetric and fully transparent PSiMC that is able to support blue lasing action from a conjugated polymer, e.g., poly(9,9)-dioctylfluorene (PFO), infiltrated inside it. The PFO-infiltrated PSiMC features single-mode blue lasing at the resonance wavelength of 466 nm, with a line width of ∼1.3 nm and lasing threshold as low as 5 nJ (i.e., fluence of 15 μJ/cm2), which is among the lowest values of state-of-the-art PFO-based lasers.26−28 Time-resolved photoluminescence further highlights a substantial modification of the emission lifetime in the PSiMC, which is shortened by 57% within the cavity mode, thus confirming a dramatic variation of the radiative decay rate due to a Purcell effect.
Results and Discussion
Fabrication of Hybrid PSi/PFO Laser
The preparation method of the hybrid PSi/PFO laser is sketched in Figure 1(a). First, we prepared a monolithic asymmetric PSi microcavity operating in the visible region and consisting of a half-wavelength defect sandwiched between two quarter-wavelength DBRs featuring a different number of bilayers (Figure 1a-1). The PSiMC is fabricated by a single-step electrochemical etching, in a HF/H2O electrolyte, of a highly doped p-type crystalline silicon. A square-wave etching current density profile with values of 20 and 400 mA cm–2 is used to produce a stack of alternating PSi layers with porosity values of 59% (i.e., 1.55 refractive index unit (RIU) at 550 nm) and 77% (1.28 RIU), respectively. These values represent a trade-off among achieving a porosity variation that maximizes the refractive index contrast, avoiding the collapse of the PSi at higher porosity due to mechanical instability, and eluding reduced penetration of polymer in the PSiMC due to the small diameter of the pores at lower porosity. Interestingly, a linear relationship is found between the central wavelength of the DBR stop-band, and, in turn, the resonance wavelength of the cavity, and the temporal period of the etching current density square-wave (Supporting Information Section 1). In fact, by increasing (decreasing) the temporal period of the etching current square-wave it is possible to increase (decrease) the optical thickness of high and low porosity layers in the PSiMC, which leads to a red(blue)-shift of the DBR stop-band and enables, in turn, the fine-tuning of the resonance wavelength of the cavity over the whole visible range (Supporting Information Section 1).
Figure 1b shows scanning electron microscopy (SEM) cross-section images highlighting the architecture of an as-prepared asymmetric PSiMC with a half-wavelength defect layer sandwiched between two DBRs with 30 (top) and 10 (bottom) bilayers. The square-wave modulation of the porosity along the direction perpendicular to the wafer surface can be clearly appreciated, with darker/brighter alternating layers indicating high/low porosity (low/high refractive index) regions. The defect layer of the cavity can be better appreciated in the inset, also highlighting the columnar structure of the pores running perpendicularly to the wafer surface. The detailed morphology of both low- and high-porosity layers of the PSiMC is shown in the top-view SEM images in Figure 1(c,d), from which pore sizes in the range of 10–20 and 100–120 nm, respectively, are apparent.
After the PSiMC is fully etched, the etching current density value is abruptly increased to produce pseudo-electropolishing (porosity about 98%) of the silicon underneath the cavity, which facilitates its eventual transfer-printing to a different substrate, though ensuring that enough silicon is left to mechanically hold the cavity in place during the next high-temperature thermal oxidation. The latter is necessary to fully convert silicon into silicon dioxide, and eliminate, in turn, any silicon-induced absorption in the UV–vis region. Pictures of asymmetric PSiMCs both as-prepared and oxidized are given in Supporting Information Section 2.
We then transfer-printed the oxidized PSiMC onto a transparent material by directly peeling the cavity off the silicon substrate using an elastomeric film, namely, polydimethylsiloxane (PDMS), to enable transmittance operation (Figure 1a-2). The high chemical affinity between silicon dioxide and PDMS ensures an easy and effective transfer of the PSiMC from the silicon chip to the PDMS film, with a damage-free and up-scalable approach (Figure 1a-3). Figure 1e shows a picture of an asymmetric PSiMC, with resonance wavelength at 460 nm, transfer-printed onto a PDMS slab. The uniformity of the blue color reflected from the cavity is an indication of the good reliability of the whole preparation process, in terms of etching, oxidation, and transfer-printing steps.
Eventually, infiltration of a blue-emitting polymer, namely, PFO, inside the cavity is carried out via drop-casting of the polymer solution into the transfer-printed PSiMC (Figure 1a-4). The polymer solution uniformly infiltrates the PSi structure for its full depth, resulting in a hybrid (i.e. inorganic–organic) PSi/PFO resonant cavity after solvent evaporation (Figure 1a-5). Fluorescence microscope images of the PSiMC after PFO infiltration highlight a good uniformity of the infiltration process, both in the in-plane and in the out-of-plane directions of the cavity (Supporting Information Section 2).
Spectroscopic Characterization of PSi/PFO Microcavity
Typical reflectance and transmittance experimental spectra collected at each preparation step of the PSi/PFO hybrid microcavity are shown in Figure 2a. Figure 2a-1 shows the reflectance spectrum at normal incidence of the as-prepared PSiMC (step 1). The photonic stop-band is centered at 520 nm, with a full-width at half-maximum (fwhm) of 85 nm and reflectance above 90%. Reflectance fringes above 575 nm are due to Fabry–Perot interference in the PSi layer. Notice that the reflectance notch corresponding to the resonance wavelength of the cavity (defect mode), which should occur at 525 nm by design, is not visible in the reflectance spectrum (blue solid line). This is due to the uneven number of bilayers of DBRs at each side of the cavity. In fact, the asymmetric architecture consists of an actual resonant cavity with two DBRs with 10 bilayers on each side of the defect layer plus an additional DBR with 20 bilayers on top of the MC. The latter dominates the reflectance spectrum of the on-chip asymmetric PSiMC, hindering the actual resonant cavity underneath, as confirmed by the theoretical reflectance spectrum calculated using the transfer matrix method (TMM) (light blue dotted line).
After the oxidation process, the photonic stop-band blue-shifts about 90 nm due to a lowering of the refractive indices of both high- and low-porosity layers (Figure 2a-2, red line).29 The fwhm of the photonic stop-band reduces to 45 nm, in agreement with the lowered refractive index contrast, though a high reflectance (>90%) is maintained. The theoretical spectrum (dark red dotted line) confirms that more than the 99% of the silicon is converted into silicon dioxide. This is also confirmed by Fabry–Perot interference fringes visible at wavelengths below 450 nm in the oxidized PSiMC, where silicon absorption dominated for as-prepared PSiMCs.
Both reflectance and transmittance spectra of the oxidized PSiMC after transfer-printing on a PDMS slab are reported in Figure 2a-3 (green and light green solid lines). In this case, the reflectance spectrum is collected on the opposite side of the PSiMC compared to the previous cases, with the reflectance probe facing the DBR with 10 bilayers. As expected, the reflectance spectrum (dark green line) now shows a sharp notch at 420 nm (fwhm = 4.1 nm) with a quality factor Q = λ/fwhm of 102.5, and the transmittance spectrum (light green line) of the PSiMC shows a dip in correspondence of the photonic stop-band. The cavity mode does not show up in the transmittance spectrum, as validated by theoretical calculations (green and dark green dotted lines). We argue that light traveling through the cavity at the resonance wavelength is reflected back by the DBR with 20 bilayers, though scattered traveling back and forth in the cavity. The cavity shows a transmittance higher than 75% over the entire visible range outside the photonic band gap, which further confirms PSi full oxidation.
The infiltration of PFO in the transfer-printed PSiMC results in a red-shift (about 50 nm) of the photonic stop-band, due to the increase in the effective refractive index of the structure induced by the presence of a polymer with a refractive index greater than that of air,30 with a concomitant increase of the fwhm (about 7 nm) of the defect mode at 466 nm (Q = 67), due to the lowered refractive index contrast (Figure 2a-4, orange and light orange solid lines). The stop-band remains well-defined with no additional shoulders, indirect indication that the cavity is uniformly infiltrated with PFO. The transmittance value is still higher than 55% at wavelengths above 500 nm, though a broad absorption band emerges below 400 nm that further confirms the presence of the PFO. Theoretical spectra (orange and light orange dotted lines) point out that the fraction of the polymer infiltrated in the PSiMC is 4% of the air volume.
The good agreement between experimental and calculated spectra after each preparation step confirms good accuracy between design and fabrication of PSi/PFO microcavities, for both morphological (i.e., layer thickness, porosity, period) and optical (i.e., refractive index value, profile) parameters. A more detailed description of the calculated spectra is reported in the Supporting Information Section 2.
Figure 2b compares peak-normalized emission spectra under continuous wave (CW) laser excitation (λ = 405 nm) of PFO when infiltrated into the transfer-printed PSiMC (blue line) and into an oxidized PSi layer with constant porosity of 66% transfer-printed on a PDMS slab (red line, used as reference nonresonant structure). The reflectance spectrum (black line) of the PFO-infiltrated PSiMC is also reported in Figure 2b superposed to the emission spectra. The PSi reference acts as a simple interferometer (reflectance spectrum in Supporting Information Section 3), and it does not provide any optical feedback that might induce modification of the density of state of PFO. The PL spectrum of PFO infiltrated inside the PSi reference exhibits the characteristic vibronic progression of the emission peaks at 438, 466, and 497 nm. This is fully consistent with the photoluminescence spectrum of a PFO thin film drop-cast onto a PDMS slab (Supporting Information Section 3) and in perfect agreement with the one reported in the literature for the β-phase of the polymer.31
On the other hand, when PFO is embedded inside the PSiMC, which was designed to have the cavity mode perfectly overlapping the amplified spontaneous emission (ASE) of PFO,26 there is a redistribution of the oscillator strength17 that strongly modifies the PL spectrum. Specifically, the PL emission is significantly enhanced (50%) and narrowed (fwhm = 2.9 nm) in correspondence with the cavity mode wavelength (λem = 466 nm, in the reflectance spectrum) due to a rearrangement of the photonic density of states (DOS) (Supporting Information Section 4).32 This is confirmed by time-resolved PL (TRPL) measurements carried out using a pulsed laser source (λexcitation = 400 nm) with low excitation power (10–50 nW) at room temperature. Figure 2c shows typical PL radiative decays of PFO infiltrated in the cavity at wavelengths corresponding to the cavity mode (λ = 450–480 nm); PL decay time constants and intensities are reported in the table. TRPL shows a faster decay time of PFO emission when infiltrated inside the PSiMC (blue line) than when infiltrated inside the PSi reference (red line). It is worth restating that the reference PSi structure consists of a simple porous silicon layer with constant porosity (i.e., constant refractive index) that does not provide any photonic effect on the emitting material and its DOS.
Interestingly, the PL temporal decay curve is best fit by a biexponential function (I(t) = I0 + I1e–t/τ1 + I2e–t/τ2). The need for a biexponential fitting is not surprising for the infiltrated polymer, given the large surface/volume ratio of the regions in which the polymer is embedded, which can strongly influence the physical properties of the emitter.33 This is in agreement with the physical model of the luminescence of conjugated polymers originating from both strongly bound intramolecular excitons (primary exponential) and more weakly bound interchain states (secondary exponential, with a longer decay time).34−39 In our system the longer decay time can be assigned either to the polymer interaction with the SiO2 nanostructure or to the formation of polymer aggregates inside the pores. The time-constant values of PL reported in Figure 2 provide clear evidence of the modification of the decay rates induced by the photonic feedback structure. Specifically, we observe a significant reduction (∼57% for τ1) of the primary exponential decay time, which can be ascribed to a modified exciton recombination time when the polymer is infiltrated in the PSiMC and confirms the rearrangement of the DOS inside the cavity at the resonance wavelength. Calculation of the ratio between spontaneous emission lifetime of a dipole embedded in a nonresonant medium and of a dipole located inside the microcavity at the lasing/resonance wavelength yields τ1Ref/τ1MC ≈ 1.83 (obtained from experimental data in Figure 2c, table), from which a Purcell factor Fp ≈ 1.9 is estimated according to the literature.40−42 A value of Fp > 1 supports the enhancing of spontaneous emission rate in resonant microcavities32,43 through a Purcell effect.44,45
The redistribution of the DOS induced by the PSiMC is further corroborated by the observation of slower decay time of the PL at wavelengths outside the cavity mode in correspondence with the photonic stop-band, compared to that on the PSi reference (Supporting Information Section 4).
Modification of the density of states of the PFO host in PSiMCs and the relatively high Q of PSiMCs is a clear indication that porous silicon microcavities represent a suitable feedback structure for an organic laser.
Lasing Action from PSi/PFO Microcavity
Lasing of PFO-infiltrated PSiMC is investigated using a Ti-sapphire laser (λex = 400 nm, 150 fs, 2 kHz, spot diameter 100 μm) as a pumping source and collecting the emission spectra as a function of pump power at normal incidence. A sketch of the experimental setup used is shown in Supporting Information Section 5. Specifically, the PFO-infiltrated PSiMC was placed with the 30-bilayer DBR facing the laser pump and the 10-bilayer DBR facing the collection lens. This configuration permits maximizing the emission of PFO inside the cavity in the collection direction. In fact, light emitted from PFO inside the cavity at the resonant wavelength in the direction of the laser pump is reflected back to the collection direction from the uneven 20-bilayer of the DBR.
Figure 3a shows the experimental PL spectra of an asymmetric PFO-infiltrated PSiMC for pump energies per pulse from 0.55 to 30 nJ. At low excitation energies (below 2 nJ, inset in Figure 3a) the PL spectrum shows a sharp peak at 466 nm with fwhm = 2.4 nm, which corresponds to the defect mode wavelength of the PFO-infiltrated PSiMC, in good agreement with the PL spectrum under CW excitation of Figure 2(e). A broader PL band is observed at 475 nm, which corresponds to the unmodified emission of PFO, with intensity comparable to that of the cavity mode at 466 nm. Above a pump energy of 5 nJ (corresponding to a fluence of ∼15 μJ/cm2) the peak at 466 nm narrows (fwhm = 1.35 nm at 5 nJ) and its intensity increases nonlinearly with the excitation energy. This is apparent in Figure 3(b), which shows both output power and mode width (fwhm) of the laser line (466 nm) of the PFO-infiltrated PSiMC as a function of the input pump energy. The PL emission at 466 nm is best fit with two Gaussian curves, both centered at 466 nm, with the higher intensity, sharper component assigned to the single mode laser emission of PFO infiltrated into the PSiMC and the lower intensity, broader component (fwhm ∼6–8 nm) assigned to unmodified PL collected by the collimation lens in our experimental setup.
We claim that the strong nonlinear increase of the PL intensity at 466 nm, together with the perfect matching of the sharp PL emission line and cavity resonant mode (both at 466 nm), is a clear indication of lasing action from PFO infiltrated inside the PSiMC. Accordingly, we identify the excitation energy per pulse of 5 nJ (∼15 μJ/cm2) as the lasing threshold of our PFO-infiltrated PSiMC. This is in good agreement with the theoretical value calculated in Supporting Information Section 6. Interestingly, this value is comparable to that of best state-of-the-art PFO lasers,26−28 thus confirming the high quality of the photonic feedback structure achieved using porous silicon.
Note that the PL intensity at 475 nm (green line and square, Figure 3(b)) always increases linearly with the pump energy, thus confirming that no stimulated emission (i.e., only spontaneous emission) occurs outside the resonant mode of the cavity. The ratio between PL intensity of resonant and nonresonant modes43,46 (i.e., between stimulated and spontaneous emission, Supporting Information Section 6) further confirms the lasing threshold of about 5 nJ (15 μJ/cm2).
At high input energies, we observe that the width of the laser line slightly increases upon increasing the excitation fluence (Figure 3(b)), which is a fingerprint for pulsed pumped organic lasers operating in the gain switching regime.47,48
To evaluate the operating stability of the hybrid PFO/PSi laser with time, the PFO-infiltrated PSiMC was irradiated with a laser energy of 50 nJ, which is 10 times higher than the lasing threshold, yielding only a ∼40% decay of the PL intensity at the lasing wavelength after 6 min of irradiation (i.e., 7.2 × 105 pulses). These values are in good agreement with organic semiconductor and solid-state dye lasers, whose operating lifetimes are typically on the order of 105 to 107 pulses49 (Supporting Information Section 7).
To rule out that the observed effect on the PFO-infiltrated PSiMC is related to ASE, PL spectra are also collected at the output of the PFO-infiltrated PSi reference for excitation energy per pulse from 50 to 1600 nJ using the same experimental setup. Figure 3c shows that the PL spectra of PFO when infiltrated in the PSi reference with constant porosity have a line shape similar to that measured under CW excitation (shown in Figure 2b), regardless of the excitation energy (Supporting Information Section 8). Furthermore, PL intensity increases linearly with the pump energy, and no line narrowing occurs for the PSi reference (Figure 3d).
Furthermore, lasing from PFO-infiltrated PSiMC is also observed for a microcavity designed to have a resonance wavelength red-shifted (591 nm) with respect to PFO emission (Supporting Information Section 9). In this case, the PSiMC was properly rotated by 50° to blue-shift the stop-band thanks to angular dispersion of photonic crystal structures so as to overlap the emission spectrum of the PFO (Supporting Information Section 9). This result further corroborates high quality in fabrication and good flexibility in operation of the proposed PSi-based laser.
Conclusion
In this work we reported on a ground-breaking approach for the fabrication of a monolithic low-threshold silicon-based hybrid laser via drop-casting infiltration of transparent nanostructured porous silicon resonant cavities with a polymer emitter.
As a proof-of-concept, fabrication of a blue-emitting hybrid laser by infiltration of PFO within a PSiMC is successfully reported. The laser features a single mode laser line at 466 nm (mode width ∼1.3 nm) with an exceptionally low threshold (input energy per pulse ∼5 nJ, fluence ∼15 μJ/cm2). Furthermore, a significant modification of the density of states of PFO when infiltrated in the PSiMC indicates that a Purcell effect also takes place.
The laser fabrication is low-cost, highly reliable, and up-scalable. It is based on the preparation of a monolithic PSiMC by one-step electrochemical etching, subsequent thermal oxidation, transfer-printing to a PDMS slab, and final drop-casting of PFO into the microcavity. The laser fabrication is also very flexible. In fact, it is possible to effectively tune the laser wavelength by simply shifting the PSiMC resonant wavelength and infiltrating a suitable polymer with emission matching the resonant mode of the PSiMC. Moreover, patterning of the microcavity down to a few micrometers in size can be carried out by standard photolithography.
These results are significant for the development of low-cost, low-threshold silicon-based lasers operating from the visible to the near-infrared range, which could be exploited in many applications, including silicon photonics, ultrasensitive biosensors, and personalized nanomedicine. Electrical pumping, for which the majority of the aforementioned applications would benefit from, remains a challenging goal to be achieved with hybrid lasers though, due to both low carrier mobility and triplet generation in organic optical-gain materials. Nevertheless, the proposed PSi/organic hybrid laser could represent an effective proof-of-concept platform for the development of indirect electrically-pumped lasers, where an efficient electrically-driven light source is used to optically pump the PSi/organic laser, leveraging the high quality of the PSi feedback structure and, in turn, the low-energy lasing threshold exhibited by this class of lasers.
Methods
Preparation of PSiMC and PSi Reference
Porous silicon microcavities and PSi reference interferometers were prepared by anodic etching of highly doped p-type crystalline silicon (boron-doped, ⟨100⟩-oriented, resistivity of 0.8–1.2 mΩcm, Siltronix, Inc.). The electrochemical etching was carried out in a homemade Teflon cell using a two-electrode configuration, with the silicon substrate (area of 2.835 cm2) placed onto an aluminum flat anode and a platinum coil immersed in the solution of HF (48%)/EtOH (3:1 v/v) and acting as cathode. A source measure unit (SMU) (Keithley 2610), configured as current source and voltage meter, was used to set the etching current density, both value and profile, and simultaneously monitor the voltage drop between silicon and platinum electrodes.
First, a PSi sacrificial layer was etched at a constant current density of 400 mA/cm2 for 15 s and immediately dissolved by dissolution in a NaOH (1 M in deionized (DI) water)/EtOH (9:1 v/v) solution. This step is necessary to avoid the presence of a top parasitic porous silicon layer, with pores smaller than 10 nm due to chemical contamination of the silicon surface, which could strongly impact the preparation of PSi optical structures. After removal of the PSi sacrificial layer, the silicon samples were rinsed with deionized water and ethanol, gently dried under nitrogen flow, then used for the etching of a second PSi optical structure, either the PSiMC or the PSi reference interferometer.
For the etching of the PSiMC we set a square-wave current density profile with values of 400 and 20 mA/cm2 to obtain a periodic modulation of the PSi porosity between 77% and 59%, respectively, and, in turn, of the PSi refractive index varying between n400 = 1.28 RIU and n20 = 1.55 RIU (at 550 nm), yielding a contrast of 0.27 RIU. The porosity values and, in turn, the refractive index values of the PSi layers prepared with the aforementioned current densities were extracted from reflectance spectra collected from PSi homogeneous layers etched at constant current density and, in turn, with constant porosity.50
The PSiMC was designed with a half-wavelength defect sandwiched between quarter-wavelength DBRs with 30 (top) and 10 (bottom) bilayers. The PSiMC with stop-band at 525 nm as-prepared was etched using a square-wave etching current profile with a period of 4.5 s and duty cycle of 0.9 (i.e., t400 = 4.95 s, t20 = 0.55 s), to take into account the different etching speeds at different etching current densities. The etching time of the two current density values is tuned to ensure that the optical thickness of both high- and low-porosity layers is one-quarter of the central wavelength of the photonic stop-band of the DBRs. Notice that, the etching time is doubled during the etching of the defect layer of the cavity to obtain an optical thickness that is half the stop-band central wavelength. The defect layer is etched at 20 mA/cm2 to have a low porosity value and, in turn, a high refractive index value that allows the electromagnetic field to be concentrated inside the cavity. The overall etching process gives rise to a PSiMC with a total thickness of ∼15 μm.
The PSi reference interferometer was prepared at a constant etching current of 100 mA/cm2 for 350 s to obtain a homogeneous PSi layer with constant porosity of 66% and thickness of ∼15 μm, comparable to average porosity and total thickness of the PSiMC.
After preparation of the PSi optical structures, we applied a constant current density of 800 mA/cm2 for 0.6 s to produce a pseudo-electropolishing of the silicon underneath the cavity, though leaving the microcavities still anchored to bulk silicon. The as-prepared samples are then rinsed with 2-propanol and pentane and gently dried under nitrogen flow to obtain a crack-free PSi layer.
Eventually, samples are thermally oxidized in a muffle furnace (ZB 1, ASAL) at 750 °C for 1:30 h, with a ramp rate of 12 °C/min, in ambient conditions.
Transfer-Printing of PSiMC onto PDMS
PDMS slabs (Sylgard 184, Dow Corning, Midland, MI, USA) were prepared by mixing base and curing agent in a ratio 10:1 by weight. The resulting mix was cast onto a Petri dish and degassed under vacuum for 30 min to avoid the presence of air bubbles trapped inside it. The Petri dish containing the mix was then placed into an oven at 110 °C for 1 h to achieve polymer cross-linking. Eventually, the PDMS disks were properly cut into slabs, which were placed onto the silicon chips containing either the oxidized PSiMC or the PSi reference and used to gently peel the PSi structures off the silicon substrate and transfer them onto the PDMS slab.
Infiltration of PFO into PSiMC
Poly(9,9)-dioctylfluorene (20 kDa. Aldrich) was used as received, without further purification. A PFO solution was prepared by dissolving 1% wt in toluene at room temperature. The infiltration was performed by dropping 20 μL of the polymer solution onto the PSiMC, then allowing the solvent to evaporate in ambient conditions.
Morphological and Optical Characterization of PSi/PFO Microcavities
Reflectance and transmittance spectra were collected with an Ocean Optics H4000+ES spectrometer in combination with a fiber-coupled Ocean Optics DH-2000 deuterium-halogen source. CW photoluminescence measurements were carried out with the same spectrometer by using a 405 nm CW laser diode (Thorlabs). The porosity of the PSi layers was computationally evaluated by fitting experimental reflectance spectra of as-prepared PSi samples with a homemade software developed in Matlab (MathWorks, USA). Time-resolved PL measurements were carried out using a femtosecond laser source coupled to a streak camera detection system (Hamamatsu C5680). A Ti:sapphire laser (Coherent Chameleon Ultra II, pulse bandwidths of ∼100 fs, repetition rate of 80 MHz, and power of 10–50 nW) was used to pump a second-harmonic crystal (barium borate) to tune the pump wavelength to 400 nm.
Lasing experiments were performed using an amplified Ti:sapphire laser with 2 mJ output energy and 2 kHz repetition rate at 400 nm. The laser power was set using a tunable optical density. The samples were placed with the 30-bilayer stack facing the focused laser pump and the 10-bilayer stack facing the collection lens. The emitted light was collected through a spherical collimation lens connected to a fiber-coupled spectrometer (Avantes AvaSpec-ULS2048XL-EVO).
SEM images were taken using a Zeiss ULTRA55 microscope.
Acknowledgments
This work was supported by the EU H2020 ETN SYNCHRONICS under grant agreement 643238. We thank Dr. F. F. R. Toia (STMicroelectronics, Milan) for technical assistance with SEM images.
Supporting Information Available
The Supporting Information is available free of charge on the ACS Publications website at DOI: 10.1021/acsnano.8b00875.
Additional experiments, figures, and data on morphological characterization of PSi layers and PSiMCs; spectroscopic investigation of PSiMCs and PSi reference structure before and after infiltration of PFO; spectroscopic characterization of PFO solution and thin film; Fermi’s golden rule and radiative decay rate; lasing experiment setup; theoretical estimation of lasing threshold and coherence length; operating stability of PFO/PSiMC laser; spectroscopic characterization of the red-shifted PSiMC (PDF)
The authors declare no competing financial interest.
Supplementary Material
References
- Cullis A. G.; Canham L. T. Visible Light Emission Due to Quantum Size Effects in Highly Porous Crystalline Silicon. Nature 1991, 353, 335. 10.1038/353335a0. [DOI] [Google Scholar]
- Canham L. Gaining Light From Silicon. Nature 2000, 408, 411–412. 10.1038/35044156. [DOI] [PubMed] [Google Scholar]
- Liang D.; Bowers J. E. Recent Progress in Lasers on Silicon. Nat. Photonics 2010, 4, 511. 10.1038/nphoton.2010.167. [DOI] [Google Scholar]
- Priolo F.; Gregorkiewicz T.; Galli M.; Krauss T. F. Silicon Nanostructures for Photonics and Photovoltaics. Nat. Nanotechnol. 2014, 9, 19. 10.1038/nnano.2013.271. [DOI] [PubMed] [Google Scholar]
- Lin V. S.; Motesharei K.; Dancil K. P.; Sailor M. J.; Ghadiri M. R. A Porous Silicon-Based Optical Interferometric Biosensor. Science 1997, 278, 840–843. 10.1126/science.278.5339.840. [DOI] [PubMed] [Google Scholar]
- Mariani S.; Pino L.; Strambini L. M.; Tedeschi L.; Barillaro G. 10 000-Fold Improvement in Protein Detection Using Nanostructured Porous Silicon Interferometric Aptasensors. ACS Sens 2016, 1, 1471–1479. 10.1021/acssensors.6b00634. [DOI] [Google Scholar]
- Gu L.; Hall D. J.; Qin Z.; Anglin E.; Joo J.; Mooney D. J.; Howell S. B.; Sailor M. J. In Vivo Time-Gated Fluorescence Imaging With Biodegradable Luminescent Porous Silicon Nanoparticles. Nat. Commun. 2013, 4, 2326. 10.1038/ncomms3326. [DOI] [PMC free article] [PubMed] [Google Scholar]
- Park J.-H.; von Maltzahn G.; Ong L. L.; Centrone A.; Hatton T. A.; Ruoslahti E.; Bhatia S. N.; Sailor M. J. Cooperative Nanoparticles for Tumor Detection And Photothermally Triggered Drug Delivery. Adv. Mater. 2010, 22, 880–885. 10.1002/adma.200902895. [DOI] [PMC free article] [PubMed] [Google Scholar]
- Jane A.; Dronov R.; Hodges A.; Voelcker N. H. Porous Silicon Biosensors on the Advance. Trends Biotechnol. 2009, 27, 230–239. 10.1016/j.tibtech.2008.12.004. [DOI] [PubMed] [Google Scholar]
- Sailor M. J.Porous Silicon in Practice: Preparation, Characterization and Applications; John Wiley & Sons: Weinheim, 2012. [Google Scholar]
- Föll H.; Christophersen M.; Carstensen J.; Hasse G. Formation and Application of Porous Silicon. Mater. Sci. Eng., R 2002, 39, 93–141. 10.1016/S0927-796X(02)00090-6. [DOI] [Google Scholar]
- Janshoff A.; Dancil K.-P. S.; Steinem C.; Greiner D. P.; Lin V. S. Y.; Gurtner C.; Motesharei K.; Sailor M. J.; Ghadiri M. R. Macroporous p-type Silicon Fabry–Perot Layers. Fabrication, Characterization, and Applications in Biosensing. J. Am. Chem. Soc. 1998, 120, 12108–12116. 10.1021/ja9826237. [DOI] [Google Scholar]
- Ruminski A. M.; Barillaro G.; Secret E.; Huang W. D.; Potocny A.; Carion U.; Wertans C.; Sailor M. J. Topological Control of Porous Silicon Photonic Crystals by Microcontact Printing. Adv. Opt. Mater. 2013, 1, 510–516. 10.1002/adom.201300014. [DOI] [Google Scholar]
- Maniya N. H.; Patel S. R.; Murthy Z. V. P. Simulation and Fabrication Study of Porous Silicon Photonic Crystal. Optik 2014, 125, 828–831. 10.1016/j.ijleo.2013.07.062. [DOI] [Google Scholar]
- Pavesi L.; Dubos P. Random Porous Silicon Multilayers: Application to Distributed Bragg Reflectors and Interferential Fabry - Pérot Filters. Semicond. Sci. Technol. 1997, 12, 570. 10.1088/0268-1242/12/5/009. [DOI] [Google Scholar]
- Thuy Chi D.; Huy B.; Thuy Van N.; The Anh N.; Thanh Hai N.; Van Hoi P. A. Microcavity Based on a Porous Silicon Multilayer. Adv. Nat. Sci.: Nanosci. Nanotechnol. 2011, 2, 035001. 10.1088/2043-6262/2/3/035001. [DOI] [Google Scholar]
- Pavesi L.; Panzarini G.; Andreani L. C. All-Porous Silicon-Coupled Microcavities: Experiment Versus Theory. Phys. Rev. B: Condens. Matter Mater. Phys. 1998, 58, 15794–15800. 10.1103/PhysRevB.58.15794. [DOI] [Google Scholar]
- Salem M. S.; Sailor M. J.; Sakka T.; Ogata Y. H. Electrochemical Preparation of a Rugate Filter in Silicon and its Deviation from the Ideal Structure. J. Appl. Phys. 2007, 101, 063503. 10.1063/1.2710339. [DOI] [Google Scholar]
- Robbiano V.; Di Stasio F.; Surdo S.; Mian S.; Barillaro G.; Cacialli F.. Hybrid-Organic Photonic Structures for Light Emission Modification. In Organic and Hybrid Photonic Crystals; Comoretto D., Ed.; Springer International Publishing: Cham, 2015; pp 339–358. [Google Scholar]
- Rong G.; Najmaie A.; Sipe J. E.; Weiss S. M. Nanoscale Porous Silicon Waveguide for Label-Free DNA Sensing. Biosens. Biosens. Bioelectron. 2008, 23, 1572–1576. 10.1016/j.bios.2008.01.017. [DOI] [PubMed] [Google Scholar]
- Krueger N. A.; Holsteen A. L.; Kang S. K.; Ocier C. R.; Zhou W.; Mensing G.; Rogers J. A.; Brongersma M. L.; Braun P. V. Porous Silicon Gradient Refractive Index Micro-Optics. Nano Lett. 2016, 16, 7402–7407. 10.1021/acs.nanolett.6b02939. [DOI] [PubMed] [Google Scholar]
- Jenie S. N. A.; Pace S.; Sciacca B.; Brooks R. D.; Plush S. E.; Voelcker N. H. Lanthanide Luminescence Enhancements in Porous Silicon Resonant Microcavities. ACS Appl. Mater. Interfaces 2014, 6, 12012–12021. 10.1021/am500983r. [DOI] [PubMed] [Google Scholar]
- Ning H.; Krueger N. A.; Sheng X.; Keurn H.; Zhang C.; Choquette K. D.; Li X. L.; Kim S.; Rogers J. A.; Braun P. V. Transfer-Printing of Tunable Porous Silicon Microcavities with Embedded Emitters. ACS Photonics 2014, 1, 1144–1150. 10.1021/ph500230j. [DOI] [Google Scholar]
- Wan Y.; Krueger N. A.; Ocier C. R.; Su P.; Braun P. V.; Cunningham B. T. Resonant Mode Engineering of Photonic Crystal Sensors Clad with Ultralow Refractive Index Porous Silicon Dioxide. Adv. Opt. Mater. 2017, 5, 1700605. 10.1002/adom.201700605. [DOI] [Google Scholar]
- Ocier C. R.; Krueger N. A.; Zhou W. J.; Braun P. V. Tunable Visibly Transparent Optics Derived from Porous Silicon. ACS Photonics 2017, 4, 909–914. 10.1021/acsphotonics.6b01001. [DOI] [Google Scholar]
- Ryu G.; Xia R.; Bradley D. D. C. Optical Gain Characteristics of β-phase Poly(9,9-dioctylfluorene). J. Phys.: Condens. Matter 2007, 19, 056205. 10.1088/0953-8984/19/5/056205. [DOI] [Google Scholar]
- Heliotis G.; Xia R.; Turnbull G. A.; Andrew P.; Barnes W. L.; Samuel D. W.; Bradley D. D. C. Emission Characteristics and Performance Comparison of Polyfluorene Lasers with One- And Two-Dimensional Distributed Feedback. Adv. Funct. Mater. 2004, 14, 91–97. 10.1002/adfm.200305504. [DOI] [Google Scholar]
- O’Carroll D.; Lieberwirth I.; Redmond G. Microcavity Effects and Optically Pumped Lasing in Single Conjugated Polymer Nanowires. Nat. Nanotechnol. 2007, 2, 180–184. 10.1038/nnano.2007.35. [DOI] [PubMed] [Google Scholar]
- Edward P. D.; Holm R. T.. Handbook of Optical Constants of Solids; Academic Press: New York, 1998. [Google Scholar]
- Stavrinou P. N.; Ryu G.; Campoy-Quiles M.; Bradley D. D. C. The Change in refractive Index of poly(9,9-dioctylfluorene) Due to the Adoption of the β-phase Chain Conformation. J. Phys.: Condens. Matter 2007, 19, 056205. 10.1088/0953-8984/19/46/466107. [DOI] [Google Scholar]
- Chen S. H.; Su A. C.; Su C. H.; Chen S. A. Crystalline Forms and Emission Behavior of Poly(9,9-di-n-octyl-2,7-fluorene). Macromolecules 2005, 38, 379–385. 10.1021/ma048162t. [DOI] [Google Scholar]
- Kavokin A. V.; Baumberg J. J.; Malpuech G.; Laussy F. P.. Microcavities; Oxford University Press: Oxford, 2017. [Google Scholar]
- Di Stasio F.; Berti L.; McDonnell S. O.; Robbiano V.; Anderson H. L.; Comoretto D.; Cacialli F. Fluorescent Polystyrene Photonic Crystals Self-Assembled with Water-Soluble Conjugated Polyrotaxanes. APL Mater. 2013, 1, 042116. 10.1063/1.4826544. [DOI] [Google Scholar]
- Cornil J.; Beljonne D.; Calbert J. P.; Brédas J. L. Interchain Interactions in Organic π-Conjugated Materials: Impact on Electronic Structure, Optical Response, and Charge Transport. Adv. Mater. 2001, 13, 1053–1067. . [DOI] [Google Scholar]
- Spano F. C. The Spectral Signatures of Frenkel Polarons in H- and J-Aggregates. Acc. Chem. Res. 2010, 43, 429–439. 10.1021/ar900233v. [DOI] [PubMed] [Google Scholar]
- Cornil J.; dos Santos D. A.; Crispin X.; Silbey R.; Brédas J. L. Influence of Interchain Interactions on the Absorption and Luminescence of Conjugated Oligomers and Polymers: a Quantum-Chemical Characterization. J. Am. Chem. Soc. 1998, 120, 1289–1299. 10.1021/ja973761j. [DOI] [Google Scholar]
- Brédas J.-L.; Cornil J.; Heeger A. J. The Exciton Binding Energy in Luminescent Conjugated Polymers. Adv. Mater. 1996, 8, 447–452. 10.1002/adma.19960080517. [DOI] [Google Scholar]
- Gierschner J.; Ehni M.; Egelhaaf H.-J.; Milián Medina B.; Beljonne D.; Benmansour H.; Bazan G. C. Solid-State Optical Properties of Linear Polyconjugated Molecules: π-Stack Contra Herringbone. J. Chem. Phys. 2005, 123, 144914. 10.1063/1.2062028. [DOI] [PubMed] [Google Scholar]
- P Petrozza A.; Brovelli S.; Michels J. J.; Anderson H. L.; Friend R. H.; Silva C.; Cacialli F. Control of Rapid Formation of Interchain Excited States in Sugar-Threaded Supramolecular Wires. Adv. Mater. 2008, 20, 3218–3223. 10.1002/adma.200800007. [DOI] [Google Scholar]
- Gérard J. M.; Sermage B.; Gayral B.; Legrand B.; Costard E.; Thierry-Mieg V. Enhanced Spontaneous Emission by Quantum Boxes in a Monolithic Optical Microcavity. Phys. Rev. Lett. 1998, 81, 1110–1113. 10.1103/PhysRevLett.81.1110. [DOI] [Google Scholar]
- Adawi A. M.; Cadby A.; Connolly L. G.; Hung W. C.; Dean R.; Tahraoui A.; Fox A. M.; Cullis A. G.; Sanvitto D.; Skolnick M. S.; Lidzey D. G. Spontaneous Emission Control in Micropillar Cavities Containing a Fluorescent Molecular Dye. Adv. Mater. 2006, 18, 742–747. 10.1002/adma.200502099. [DOI] [Google Scholar]
- Wang J.; Cao R.; Da P.; Wang Y.; Hu T.; Wu L.; Lu J.; Shen X.; Xu F.; Zheng G.; Chen Z. Purcell Effect in an Organic-Inorganic Halide Perovskite Semiconductor Microcavity System. Appl. Phys. Lett. 2016, 108, 022103. 10.1063/1.4939724. [DOI] [Google Scholar]
- Yamamoto Y.; Machida S.; Björk G. Micro-Cavity Semiconductor Lasers with Controlled Spontaneous Emission. Opt. Quantum Electron. 1992, 24, S215–S243. 10.1007/BF00625826. [DOI] [Google Scholar]
- Noda S.; Fujita M.; Asano T. Spontaneous-Emission Control by Photonic Crystals and Nanocavities. Nat. Photonics 2007, 1, 449–458. 10.1038/nphoton.2007.141. [DOI] [Google Scholar]
- Purcell E. M. Spontaneous Emission Probabilities at Radio Frequencies. Phys. Rev. 1946, 69, 681. 10.1007/978-1-4615-1963-8_40. [DOI] [Google Scholar]
- Tessler N.; Denton G. J.; Friend R. H. Lasing from Conjugated-Polymer Microcavities. Nature 1996, 382, 695–697. 10.1038/382695a0. [DOI] [Google Scholar]
- Persano L.; Del Carro P.; Mele E.; Cingolani R.; Pisignano D.; Zavelani-Rossi M.; Longhi S.; Lanzani G. Monolithic Polymer Microcavity Lasers with On-Top Evaporated Dielectric Mirrors. Appl. Phys. Lett. 2006, 88, 121110. 10.1063/1.2179611. [DOI] [Google Scholar]
- Svelto O.; Hanna D. C.. Principles of Lasers; Springer: New York, 1998. [Google Scholar]
- Samuel I. D. W.; Turnbull G. A. Organic Semiconductor Lasers. Chem. Rev. 2007, 107, 1272–1295. 10.1021/cr050152i. [DOI] [PubMed] [Google Scholar]
- Ruminski A. M.; Barillaro G.; Chaffin C.; Sailor M. J. Internally Referenced Remote Sensors for HF and Cl2 Using Reactive Porous Silicon Photonic Crystals. Adv. Funct. Mater. 2011, 21, 1511–1525. 10.1002/adfm.201002037. [DOI] [Google Scholar]
Associated Data
This section collects any data citations, data availability statements, or supplementary materials included in this article.