Abstract
The impact of vertical electrical field on the electron related linear and 3rd order nonlinear optical properties are evaluated numerically for pyramidal GeSn quantum dots with different sizes. The electric field induced electron confining potential profile’s modification is found to alter the transition energies and the transition dipole moment, particularly for larger dot sizes. These variations strongly influence the intersubband photoabsorption coefficients and changes in the refractive index with an increasing tendency of the 3rd order nonlinear component with increasing both quantum dot (QD) size and applied electric field. The results show that intersubband optical properties of GeSn quantum dots can be successively tuned by external polarization.
Keywords: GeSn, quantum dot, electric field, intersubband nonlinear optics, absorption coefficients, refractive index changes
1. Introduction
Self-assembled quantum dots have received an increasing interest during the past decades owing to their potentiality for novel optoelectronic devices [1,2]. Indeed, the strong carriers’ confinement in these nanostructures has encouraged exploring the light emission and detection in the IR [3,4,5,6] and THz regime [7,8,9] using intersubband optical transitions. A particular interest has been devoted to the study of linear and nonlinear QD intersubband optical properties [7,9,10,11,12,13,14,15,16,17] for their importance in integrated quantum photonic technologies [18]. Despite the achieved progress, efficient light source integrable with Silicon technology has, so far, represented a challenge for Si-photonic integrated circuits [19]. Recent achievement in direct band gap GeSn material has accentuated its suitability towards comparable properties to III-V materials while being compatible with complementary metal-oxide semiconductor (CMOS) technology [20,21,22,23,24,25]. Accordingly, several reports have already demonstrated the aptness of this material for optoelectronic applications, such as light emitters [25,26,27,28] and detectors [29,30,31]. Furthermore, growing experimental and theoretical research activities have been developed to explore GeSn based low dimensional structures such as quantum dots [32,33,34,35,36,37,38,39]. Indeed, different synthesis roots have been reported including, colloidal QD [33], thermal diffusion [32] and self-organization [34]. Furthermore, high Tin content GeSn QD with direct band gap transition energy has recently been reported [40]. Despite the experimental and theoretical achievement, GeSn QD are still immature and a lot of works have still to be done. Recently, we have reported on the evolution of the intersubband photoabsorption coefficients (AC) and Refractive index changes (RIC) as a function of GeSn dots size and incident radiation intensity [16]. The present work treats the effect of vertical electric field on intersubband related optical properties of pyramidal GeSn QD with different sizes for CMOS compatible nonlinear optical devices.
2. Theoretical Consideration
The self-assembled GeSn QD has been considered to have a pyramidal shape with 1nm thick wetting layer (WL) embedded in Ge matrix which is one of the frequently observed shapes for semiconducting self-assembled QD [41] as illustrated by Figure 1a. Throughout this work, we set the tin composition at 30% and a QD height to base side length’s (L) ratio of 1/3 (Figure 1b,c).
To evaluate the QD s- and p- like electrons’ energy levels and associated wave functions in Γ-valley, single band 3D-Schrodinger equation (Equation (1)) is solved in Cartesian coordinates within the effective mass approximation by finite elements method offered by COMSOL multiphysics software (version 5.0, COMSOL Inc., Stockholm, Sweden) [42] for the strained pyramidal GeSn QD under vertical applied electric field (Figure 1).
(1) |
where , , and m* represent the electron energy level, envelop wave function, potential barrier and effective mass, respectively. is the external electric field and e the elementary charge. Further details can be found elsewhere [42,43]. The calculation of the transition angular frequency associated dipole moment is mandatory to evaluate the AC and RIC. Indeed, the angular frequency dependent total intersubband optical AC () and RIC () are given by [10,11]:
(2) |
(3) |
where and , denote the linear AC and RIC (Equations (4) and (6)). and represent the 3rd order nonlinear AC and RIC expressed respectively by Equations (5) and (7):
(4) |
(5) |
(6) |
(7) |
I is the incident in-plane polarized light intensity, σ denotes the electron density (one electron per QD) [12]. is the relaxation rate and the GeSn material’s refractive index deduced by linear interpolation [16]. is the p-to-s transition frequency and denotes the corresponding dipole moment for in-plane X polarized incident radiation. The subscript f and i refer to the final and initial states (QD p- and s electron states in this study). The p states are doubly degenerated (identified as px and py). A selection rule making the allowed transition to arise only from px state can be done by considering the incident radiation to be polarized along X direction [7,16,44].
3. Results and Discussion
The calculation of Γ-s and -p electron energy states and associated envelop wave functions allows to evaluate the and required to study the electric field’s impact on intersubband optical properties as a function of the QD size. The transition energy is shown Figure 2 as a function of the QD size (pyramid base side) for F = 100 kV/cm, 0 kV/cm and −100kV/cm. The dot size range is delimited to L between 25 nm to 40 nm [38] warranting efficient contribution of Γ-electrons to the intersubband transition energy.
In absence of electric field (F = 0 kV/cm), the intraband transition decreases from 74 meV (L = 25 nm) down to 38 meV (L = 40 nm). Applying positive electric field of 100 kV/cm enhances the transition from 6 meV for the smallest QD size up to 10 meV for the largest one. Meanwhile, the energy spacing between p and s states get rather shrank by approximately 6 meV for an external electric field of −100 kV/cm. This behavior is a direct impact of the electric field driven modification of the electron confining potential’s profile. To explain this trend, the electron probability density from s and p states (ZX plane) under an electric field of 100 kV/cm, 0 kV/cm and −100 kV/cm are shown by Figure 3 where a simplified band profile has also been provided for details. Indeed, the electric field has been found to induce a vertical shift of the electron probability density along z-axis. Its maximum gets vertically displaced towards the dot’s tip for negative electric field and towards its base for positive one [15]. Indeed, for a QD with base side length of 40 nm and a height of 13.3 nm, the maximum ground state electron probability density is located at z = 4.5 nm for unbiased QD. Under vertical electric field, the maximum is shifted upward by approximately 2.5 nm for F = −100 kV/cm and a downward vertical shift by approximately 2 nm for F = 100 kV/cm. Consequently, in the first case, the potential minimum is created near the dot tip limiting the allowed space for electron confinement (comparable environment to a QD size reduction) enhancing the separation energy between s and p states leading to the observed blueshift (Figure 2). On the other hand, the positive electric field produces a confining potential minimum at the QD base giving rise to a lowering of the confined energy states and consequent reduction of the p-to-s transition energies.
Further information can be gained through studying the evolution of the dipole moment as a function of the dot size and electric field (Figure 4). The transition dipole moment shows an increasing trend with increasing the unbiased QD size. However, it gets progressively enhanced (decreased) with increasing the QD size upon applying 100 kV/cm (−100 kV/cm) electric field. The observed relative variation traduces a high sensitivity of larger QD sizes to the applied electric field. The obtained results show that the QD intersubband optical properties can be successively adjusted by electric polarization allowing tuning not only the intersubband emission energy but also the transition dipole moment without need for QD size variation.
Accordingly, the impact of the dot size and electric field on the AC, RIC and the corresponding linear and third order nonlinear components are shown by Figure 5, as a function of the incident photon energy, for F = 0 kV/cm, 100 kV/cm and −100 kV/cm. The results are given for the smallest and the largest dot size to illustrate the simultaneous effect of electric field and dot size. For a given applied electric field value, the observed curves shift following the decreased transition energy with the increase of the dot size. Similarly, for a given QD size, and compared to the case where no electric field is applied, the curves get blueshifted for an electric field oriented in the negative Z direction and redshifted in the opposite case following the electric field induced intersubband transition energies shift.
The resonance peak of the linear AC (Figure 5a–c) considerably quenches with increasing the dot size while no noticeable change is shown to occur upon the variation of the applied electric field. In the meantime, the peak’s intensity of the third-order nonlinear AC shows an increasing trend in absolute value with increasing the applied electric field for larger QD size. Consequently, the resultant total AC exhibits strong dependence on the applied electric field. When the nonlinear part of the AC becomes comparable in magnitude to the linear one, the effect of bleaching occurs inducing a splitting of the total AC into two peaks. This saturation effect observed for the unbiased larger QD size is smoothed for F = −100 kV/cm and accentuated for F = 100 kV/cm. This behavior is analogous to that perceived upon increasing the QD size and consequent variation of the absorption threshold energy [16].
Furthermore, the linear RIC (Figure 5 d–f) shows an overall increase with increasing the applied electric field with a pronounced sensitivity for larger dot size. Meanwhile, a similar and more accentuated variation is found to occur for the third-order nonlinear RIC affecting the total changes in the refractive index curve. The observed behavior is mainly due to the simultaneous increase of the dipole moment and decrease of the intersubband transition energy.
Our calculations clearly reveal that the intersubband optical nonlinearity can be conveniently tuned by applying an external electric field for a given QD size and incident light intensity. Accordingly, the nonlinear effects can be tuned. This investigation has been conducted on GeSn QD with the available materials parameters remain a subject to experimental validation. Nonetheless, this comprehensive study could also be useful to understand the impact of the applied electric field on the intersubband optical properties of similar QD.
4. Conclusions
We have evaluated the effect of applied electric field on the intersubband optical transition, dipole moment, AC, and RIC for various GeSn QD size. The transition energy and dipole moment are found to be strongly affected by the electric field-induced confining potential profile changes. Larger size QD are found to be more sensitive to the effects of applied electric field. The intersubband-related AC and RIC can be widely tuned by employing external electric field. This comprehensive study could help future realization of CMOS compatible nonlinear optical devices.
Acknowledgments
The authors would like to thank the Deanship of Scientific Research at King Saud University for funding this work through the Research Group No: RG-1436-014.
Author Contributions
Conceptualization and Formal analysis M.B. and B.I.; Writing-original draft M.B., Investigation M.B. and B.I. Validation B.S. and N.A.M.; Supervision B.I.; Writing-review & editing B.S., N.A.M., B.I.
Funding
This research received no external funding.
Conflicts of Interest
The authors declare no conflict of interest.
References
- 1.Horiuchi N. Strain-tunable dots. Nat. Photon. 2019;13:72. doi: 10.1038/s41566-019-0353-2. [DOI] [Google Scholar]
- 2.Su X., Wang Y., Zhang B., Zhang H., Yang K., Wang R., He J. Bismuth quantum dots as an optical saturable absorber for a 1.3 μm Q-switched solid-state laser. Appl. Opt. 2019;58:1621–1625. doi: 10.1364/AO.58.001621. [DOI] [PubMed] [Google Scholar]
- 3.Phillips J., Bhattacharya P., Kennerly S.W., Beekman D.W., Dutta M. Self-assembled InAs-GaAs quantum-dot intersubband detectors. IEEE J. Quantum Electron. 1999;35:936–943. doi: 10.1109/3.766837. [DOI] [Google Scholar]
- 4.Chen W., Deng Z., Guo D., Chen Y., Mazur Y.I., Maidaniuk Y., Benamara M., Salamo G.J., Liu H., Wu J., et al. Demonstration of InAs/InGaAs/GaAs quantum dots-in-a-well mid-wave infrared photodetectors grown on silicon substrate. J. Lightwave Technol. 2018;13:2572–2581. doi: 10.1109/JLT.2018.2811388. [DOI] [Google Scholar]
- 5.Wu J., Jiang Q., Chen S., Tang M., Mazur Y.I., Maidaniuk Y., Benamara M., Semtsiv M.P., Masselink W.T., Sablon K.A., et al. Monolithically integrated InAs/GaAs quantum dot mid-infrared photodetectors on silicon substrates. ACS Photon. 2016;3:749–753. doi: 10.1021/acsphotonics.6b00076. [DOI] [Google Scholar]
- 6.Zhuo N., Zhang J.C., Wang F.J., Liu Y.H., Zhai S.Q., Zhao Y., Wang D.B., Jia Z.W., Zhou Y.H., Wang L.J., et al. Room temperature continuous wave quantum dot cascade laser emitting at 7.2 μm. Opt. Expr. 2017;25:13807–13815. doi: 10.1364/OE.25.013807. [DOI] [PubMed] [Google Scholar]
- 7.Sabaeian M., Riyahi M. Truncated pyramidal-shaped InAs/GaAs quantum dots in the presence of a vertical magnetic field: An investigation of THz wave emission and absorption. Phys. E Low-Dimensional Syst. Nanostruct. 2017;89:105–114. doi: 10.1016/j.physe.2017.02.008. [DOI] [Google Scholar]
- 8.Zibik E.A., Grange T., Carpenter B.A., Porter N.E., Ferreira R., Bastard G., Stehr D., Winnerl S., Helm M., Liu H.Y., et al. Long lifetimes of quantum-dot intersublevel transitions in the terahertz range. Nat. Mater. 2009;8:803–807. doi: 10.1038/nmat2511. [DOI] [PubMed] [Google Scholar]
- 9.Burnett B.A., Williams B.S. Density matrix model for polarons in a terahertz quantum dot cascade laser. Phys. Rev. B. 2014;90:15530. doi: 10.1103/PhysRevB.90.155309. [DOI] [Google Scholar]
- 10.Ünlü S., Karabulut İ., Şafak H. Linear and nonlinear intersubband optical absorption coefficients and refractive index changes in a quantum box with finite confining potential. Phys. E Low-Dimensional Syst. Nanostruct. 2006;33:319–324. doi: 10.1016/j.physe.2006.03.163. [DOI] [Google Scholar]
- 11.Vahdani M.R.K., Rezaei G. Linear and nonlinear optical properties of a hydrogenic donor in lens-shaped quantum dots. Phys. Lett. A. 2009;373:3079–3084. doi: 10.1016/j.physleta.2009.06.042. [DOI] [Google Scholar]
- 12.Şahin M. Third-order nonlinear optical properties of a one- and two-electron spherical quantum dot with and without a hydrogenic impurity. J. App. Phys. 2009;106:063710. doi: 10.1063/1.3225100. [DOI] [Google Scholar]
- 13.Karabulut İ., Baskoutas S. Linear and nonlinear optical absorption coefficients and refractive index changes in spherical quantum dots: Effects of impurities, electric field, size, and optical intensity. J. Appl. Phys. 2008;103:073512. doi: 10.1063/1.2904860. [DOI] [Google Scholar]
- 14.Sabaeian M., Khaledi-Nasab A. Size-dependent intersubband optical properties of dome-shaped InAs/GaAs quantum dots with wetting layer. Appl. Opt. 2012;51:4176–4185. doi: 10.1364/AO.51.004176. [DOI] [PubMed] [Google Scholar]
- 15.Sabaeian M., Shahzadeh M., Farbod M. Electric field-induced nonlinearity enhancement in strained semi-spheroid-shaped quantum dots coupled to wetting layer. AIP Adv. 2014;4:127105. doi: 10.1063/1.4903368. [DOI] [Google Scholar]
- 16.Baira M., Salem B., Madhar N.A., Ilahi B. Linear and nonlinear intersubband optical properties of direct band gap GeSn quantum dots. Nanomaterials. 2019;9:124. doi: 10.3390/nano9010124. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 17.Tian S.-C., Lu H.-Y., Zhang H., Wang L.-J., Shu S.-L., Zhang X., Hou G.-Y., Wang Z.-Y., Tong C.-Z., Wang L.-J. Enhancing third- and fifth-order nonlinearity via tunneling in multiple quantum dots. Nanomaterials. 2019;9:423. doi: 10.3390/nano9030423. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 18.Androvitsaneas P., Young A.B., Lennon J.M., Schneider C., Maier S., Hinchliff J.J., Atkinson G.S., Harbord E., Kamp M., Hofling S., et al. Efficient quantum photonic phase shift in a low Q-factor regime. ACS Photon. 2019;6:429–435. doi: 10.1021/acsphotonics.8b01380. [DOI] [Google Scholar]
- 19.Marris-Morini D., Vakarin V., Ramirez J.M., Liu Q., Ballabio A., Frigerio J., Montesinos M., Alonso-Ramos C., Le Roux X., Serna S., et al. Germanium-based integrated photonics from near- to mid-infrared applications. Nanophotonics. 2018;7:1781–1793. doi: 10.1515/nanoph-2018-0113. [DOI] [Google Scholar]
- 20.He G., Atwater H. Interband transitions in SnxGe1−x alloys. Phys. Rev. Lett. 1997;79:1937–1940. doi: 10.1103/PhysRevLett.79.1937. [DOI] [Google Scholar]
- 21.Chen R., Lin H., Huo Y., Hitzman C., Kamins T.I., Harris J.S. Increased photoluminescence of strain-reduced, high-Sn composition Ge1−xSnx alloys grown by molecular beam epitaxy. Appl. Phys. Lett. 2011;99:181125. doi: 10.1063/1.3658632. [DOI] [Google Scholar]
- 22.Jiang L., Gallagher J.D., Senaratne C.L., Aoki T., Mathews J., Kouvetakis J., Menéndez J. Compositional dependence of the direct and indirect band gaps in Ge1−ySny alloys from room temperature photoluminescence: implications for the indirect to direct gap crossover in intrinsic and n-type materials. Semicond. Sci. Technol. 2014;29:115028. doi: 10.1088/0268-1242/29/11/115028. [DOI] [Google Scholar]
- 23.Toko K., Oya N., Saitoh N., Yoshizawa N., Suemasu T. 70 °C synthesis of high-Sn content (25%) GeSn on insulator by Sn-induced crystallization of amorphous Ge. Appl. Phys. Lett. 2015;106:082109. doi: 10.1063/1.4913744. [DOI] [Google Scholar]
- 24.Taoka N., Capellini G., Schlykow V., Montanari M., Zaumseil P., Nakatsuka O., Zaima S., Schroeder T. Electrical and optical properties improvement of GeSn layers formed at high temperature under well-controlled Sn migration. Mater. Sci. Semiconduct. Proc. 2017;57:48–53. doi: 10.1016/j.mssp.2016.09.040. [DOI] [Google Scholar]
- 25.Chang C., Chang T.W., Li H., Cheng H.H., Soref R., Sun G., Hendrickson J.R. Room-temperature 2-μm GeSn PIN homojunction light-emitting diode for inplane coupling to group-IV waveguides. Appl. Phys. Lett. 2017;111:141105. doi: 10.1063/1.4999395. [DOI] [Google Scholar]
- 26.Wirths S., Geiger R., Von Den Driesch N., Mussler G., Stoica T., Mantl S., Ikonic Z., Luysberg M., Chiussi S., Hartmann J.M., et al. Lasing in direct-bandgap GeSn alloy grown on Si. Nat. Photon. 2015;9:88–92. doi: 10.1038/nphoton.2014.321. [DOI] [Google Scholar]
- 27.Dou W., Zhou Y., Margetis J., Ghetmiri S.A., Al-Kabi S., Du W., Liu J., Sun G., Soref R.A., Tolle J. Optically pumped lasing at 3 μm from compositionally graded GeSn with tin up to 22.3% Opt. Lett. 2018;43:4558–4561. doi: 10.1364/OL.43.004558. [DOI] [PubMed] [Google Scholar]
- 28.Stange D., Wirths S., Geiger R., Schulte-Braucks C., Marzban B., von den Driesch N., Mussler G., Zabel T., Stoica T., Hartmann J.M., et al. Optically pumped GeSn microdisk lasers on Si. ACS Photon. 2016;3:1279–1285. doi: 10.1021/acsphotonics.6b00258. [DOI] [Google Scholar]
- 29.Huang B.J., Lin J.H., Cheng H.H., Chang G.E. GeSn resonant-cavity-enhanced photodetectors on silicon-on-insulator platforms. Opt. Lett. 2018;43:1215–1218. doi: 10.1364/OL.43.001215. [DOI] [PubMed] [Google Scholar]
- 30.Pandey A.K., Basu R., Kumar H., Chang G.E. Comprehensive analysis and optimal design of Ge/GeSn/Ge PNP infrared heterojunction phototransistors. IEEE J. Electron Devices Soc. 2019;7:118–126. doi: 10.1109/JEDS.2018.2884253. [DOI] [Google Scholar]
- 31.Abdel-Rahman M., Alduraibi M., Hezam M., Ilahi B. Sputter deposited GeSn alloy: A candidate material for temperature sensing layers in uncooled microbolometers. Infrared Phys. Technol. 2019;97:376–380. doi: 10.1016/j.infrared.2019.01.023. [DOI] [Google Scholar]
- 32.Seifner M.S., Hernandez S., Bernardi J., Romano-Rodriguez A., Barth S. Pushing the composition limit of anisotropic Ge1−xSnx nanostructures and determination of their thermal stability. Chem. Mater. 2017;29:9802–9813. doi: 10.1021/acs.chemmater.7b03969. [DOI] [Google Scholar]
- 33.Esteves R.J.A., Ho M.Q., Arachchige I.U. Nanocrystalline group IV alloy semiconductors: Synthesis and characterization of Ge1−xSnx quantum dots for tunable bandgaps. Chem. Mater. 2015;27:1559–1568. doi: 10.1021/cm503983b. [DOI] [Google Scholar]
- 34.Lozovoy K.A., Kokhanenko A.P., Voitsekhovskii A.V. Critical thickness of transition from 2D to 3D growth and peculiarities of quantum dots formation in GexSi1−x/Sn/Si and Ge1−ySny/Si systems. Surf. Sci. 2018;669:45–49. doi: 10.1016/j.susc.2017.11.006. [DOI] [Google Scholar]
- 35.Nakamura Y., Masada A., Ichikawa M. Quantum-confinement effect in individual Ge1−xSnx quantum dots on Si(111) substrates covered with ultrathin SiO2 films using scanning tunneling spectroscopy. Appl. Phys. Lett. 2007;91:013109. doi: 10.1063/1.2753737. [DOI] [Google Scholar]
- 36.Moontragoon P., Vukmirović N., Ikonić Z., Harrison P. Electronic structure and optical properties of Sn and SnGe quantum dots. J. Appl. Phys. 2008;103:103712. doi: 10.1063/1.2932169. [DOI] [Google Scholar]
- 37.Ilahi B. Design of direct band gap type I GeSn/Ge quantum dots for mid-IR light emitters on Si substrate. Phys. Status Solidi RRL. 2017;11:1700047. doi: 10.1002/pssr.201700047. [DOI] [Google Scholar]
- 38.Baira M., Salem B., Madhar N.A., Ilahi B. Tuning direct bandgap GeSn/Ge quantum dots’ interband and intraband useful emission wavelength: towards CMOS compatible infrared optical devices. Superlattice. Microstruct. 2018;117:31–35. doi: 10.1016/j.spmi.2018.02.038. [DOI] [Google Scholar]
- 39.Ilahi B., Al-Saigh R., Salem B. Impact of the wetting layer thickness on the emission wavelength of direct band gap GeSn/Ge quantum dots. Mater. Res. Express. 2017;4:075026. doi: 10.1088/2053-1591/aa785b. [DOI] [Google Scholar]
- 40.Zhang L., Hong H., Li C., Chen S., Huang W., Wang J., Wang H. High-Sn fraction GeSn quantum dots for Si-based light source at 1.55 μm. Appl. Phys. Express. 2019 doi: 10.7567/1882-0786/ab0993. [DOI] [Google Scholar]
- 41.Berbezier I., Ronda A., Portavoce A. SiGe nanostructures: new insights into growth processes. J. Phys. Condens. Matter. 2002;14:8283. doi: 10.1088/0953-8984/14/35/306. [DOI] [Google Scholar]
- 42.Melnik R.V.N., Willatzen M. Bandstructures of conical quantum dots with wetting layers. Nanotechnology. 2014;15:1. doi: 10.1088/0957-4484/15/1/001. [DOI] [Google Scholar]
- 43.Souaf M., Baira M., Nasr O., Alouane M., Maaref H., Sfaxi L., Ilahi B. Investigation of the InAs/GaAs quantum dots’ size: dependence on the strain reducing layer’s position. Materials. 2015;8:4699–4709. doi: 10.3390/ma8084699. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 44.Narvaez G.A., Zunger A. Calculation of conduction-to-conduction and valence-to-valence transitions between bound states in InGaAs/GaAs quantum dots. Phys. Rev. B. 2007;75:085306. doi: 10.1103/PhysRevB.75.085306. [DOI] [Google Scholar]