Table 3.
Capacitance comparison of PANI/CNTs composites obtained from different experimental methods.
| Material | Specific Capacitance/F g−1 | Capacity Retention (Cycle Number) |
Ref. |
|---|---|---|---|
| 3D PANI/CNT arrays | 359 F g−1 at 1.56 mA cm−2 | 80.02% (5000) | [69] |
| PANI/GO/MWCNTs | 696 F g−1 at 20 mV s−1 | 89% (3000) | [70] |
| PANI/CNTs/Graphene | 0.79 F cm−2 at 1.5 mA cm−2 | 76% (3000) | [71] |
| RGO/CNTs/PANI | 359 F g−1 at 1 A g−1 | 80.5% (2000) | [72] |
| CNF/CNTs/PANI | 0.067 F cm−2 at 0.5 mA cm−2 | 90% (5000) | [73] |
| MWCNTs/PANI | 809.6 F g−1 at 25 mV s−1 | 78% (2000) | [74] |
| CNT/PANI | 0.016 F cm−2 at 0.25 mA cm−2 | 63% (500) | [75] |
| CNT/PANI network | 632 F g−1 at 1 A g−1 | / | [76] |
| CNF-CNTs/PANI | 5.6 F cm−2 at 2 mA cm−2 | 85% (5000) | [77] |
| Polylactic acid/PANI/CNTs | 510 F g−1 at 1 A g−1 | 99.5% (2000) | [78] |