. 2019 Jul 23;9:10664. doi: 10.1038/s41598-019-46993-0

Effects of carbon concentration on high-hardness plasma-polymer-fluorocarbon film deposited by mid-range frequency sputtering

Sung Hyun Kim 1, Mac Kim 1, Min Seop Um 1, Woo Jin Choi 1, Jae Heung Lee 1, Yong Suk Yang 2,✉, Sang-Jin Lee 1,✉
PMCID: PMC6650446  PMID: 31337795

Abstract

We propose a method for fabricating high-hardness plasma-polymer-fluorocarbon (PPFC) thin films with controllable optical and surface properties via manipulation of the target composition design and sputtering power density. The carbon/polytetrafluoroethylene (PTFE) composite polymeric material targets with the low electrical resistance were prepared by press-molding using a mechanically mixed powder of PTFE, carbon nanotubes, and graphite. The composite targets showed electrical sheet resistances of 0.1–100 Ω/sq. PPFC thin films were deposited by mid-range frequency (MF) sputtering at power densities within 0.62~4.92 W/cm2. The maximum surface hardness of the PPFC thin film was 4.75 GPa, which was 21.6 times higher than that of fluorocarbon thin film sputtered from PTFE under the same conditions. With the increase of the carbon concentration in the target, the carbon cross-linking density of the PPFC thin film increased but the fluorine concentration decreased. The concentration of fluorine in the PPFC thin films grew with increasing sputtering power density. The MF sputtered carbon-rich PPFC thin films are controllable with physical properties of optical transmittance, surface hardness and surface water repellency which could be applied as protective layers for transparent flexible devices.

Subject terms: Surfaces, interfaces and thin films; Structural properties

Introduction

Plasma-polymer-fluorocarbons (PPFC) are fluorinated polymers such as polytetrafluoroethylene (PTFE) or fluorinated organic gases like CF4 or C2F6 that are formed through glow discharge1. The Biederman group2,3, the Faupel group4,5 and the Iwamori group6,7 have extensively studied sputtered PPFC thin films and reported optical and mechanical properties of PPFC thin films. Sputtered PPFC thin films can exhibit attractive properties such as high transparency7, electrical insulation8, superhydrophobicity9–11, oleophobicity12, and high surface hardness13,14; they are suitable for use in display panels, automobiles, and textile fibers.

In foldable and rollable flexible displays, transparent layers capable of protecting display surfaces are indispensable15,16; plasma polymer thin films are suitable candidates for such layers. Amorphous carbon, or diamond like carbon (DLC), is a representative plasma polymer material with excellent surface protection properties, having the surface hardness of 20 GPa. As the density of carbon cross-linking, constituting the backbone matrix of the plasma polymer, is increased, the thin film increases in surface hardness1,17. However, DLC is high in brittleness and difficult to apply as a flexible protective layer with a small radius of curvature, as well as having low optical transmittance; these properties limit its applicability in transparent flexible devices. In order to overcome these problems, DLC films doped with fluorine and boron have been reported with improved surface characteristics18,19. PPFC thin films prepared by sputtering using a fluorine-containing polymer such as PTFE are among the candidates for flexible protective layers to overcome the disadvantages of DLC. PPFC thin films have high optical transmittance and can resist surface contamination by self-cleaning effects20. However, the surface hardness of PPFC thin films is low as 0.5–1.0 GPa, similar to that of human fingernails (~0.4 GPa)21.

In a previous work, we presented a novel method for PPFC thin film fabrication using carbon nanotube (CNT)/PTFE composite targets, which could use a mid-range frequency (MF) power source, whereas conventional polymer targets can only be sputtered with 13.56 MHz radio frequency power sources, with reflected noise 104–105 times higher than that with a 40 kHz MF power system22. In this study, the effect of carbon content on PPFC thin films was researched by increasing the composition ratio of carbon in the sputtering target. The influence of the sputtering power density was also investigated. For a CNT/PTFE composite target using CNT powder with more than 20 wt% CNT, powder dispersion hardly occurs. Therefore, graphite was used as the carbon material. However, the graphite/PTFE composite targets with 5 and 10 wt% graphite showed sheet resistances of 5.98 × 1014 Ω/sq and 1.71 × 1010 Ω/sq, respectively, unsuitable for MF sputtering. Because of the limited mixing characteristics of CNTs and graphite powder, composite targets with different composition ratios were fabricated. The composite targets were used for MF sputtering at power densities of 2.46–4.92 W/cm2 to fabricate carbon-rich PPFC thin films. The structural, surface, and optical properties of the thin films were compared and analyzed according to the carbon concentration of the target and the sputtering power density.

Results

We mixed CNT powder and PTFE powder in weight ratios of 5:85, 10:90, and 15:85. Graphite powder and PTFE powder were also mixed at weight ratios of 5:85, 10:90, 15:85, and 30:70. Then, the conductive CNT/PTFE and graphite/PTFE targets were shaped into radius 5.3 mm and thickness 6 mm disk. The polymer composite targets were named CNT 5, CNT 10, CNT 15, Graphite 5, Graphite 10, Graphite 15, and Graphite 30. The sheet resistance of the composite targets are reported in Fig. S1. For comparison, pure PTFE without any carbon material was also press-molded to produce a target named Pristine PTFE. The sputtered fluorocarbon films using the fabricated composite targets are named PPFC C5 (CNT 5), PPFC C10 (CNT 10), PPFC C15 (CNT 15), PPFC G15 (Graphite 15), and PPFC G30 (Graphite 30). Figure 1 is a schematic of the composite target production process and the MF sputtering system used for PPFC thin film deposition. The pristine PTFE target was sputtered using an RF power source because of the excessively high sheet resistance of 9.49 × 1014 Ω/sq; plasma was not generated for lower frequencies. The sputtered pristine fluorocarbon film was named PPFC 0. We prepared the vacuum chamber with a rotatable substrate size of 200 × 200 mm2 and target-to-substrate distance of 240 mm. Base pressure of vacuum system was 6 × 10−4 Pa and the processing atmosphere was 0.93 Pa. CNT 5, CNT 10, CNT 15, Graphite 15 and Graphite 30 composite targets were sputtered with a 40 kHz MF power source with dual magnetron cathodes. Pristine PTFE was sputtered with a 13.56 MHz RF power. PPFC thin films were deposited at power densities within 0.62~4.92 W/cm2 on polyethylene terephthalate (PET) films and a silicon substrates.

Figure 1.

Figure 1

Open in a new tab

Schematic of CNT/PTFE and Graphite/PTFE composite target production process and the MF sputtering system used for PPFC film deposition.

Figure 2 shows the optical transmittances, b* values indicating yellowness, and the water contact angles of the PPFC thin films according to the carbon concentration in the targets and sputtering power densities. The optical and surface properties of the PPFC G15 thin films were similar to those of PPFC C15 (Fig. S2). Based on these results, the PPFC 0, PPFC C5, PPFC C10, PPFC G15, and PPFC G30 thin films were used to study the physical properties of the PPFC thin films as functions of the carbon composition. Figure 2(a) shows the 550-nm optical transmittance and b* yellowness parameters of the sputtered PPFC thin films according to the carbon concentrations in the targets. The Carbon/PTFE and Pristine PTFE composite targets were sputtered at the same power density of 2.46 W/cm2. PPFC 0, PPFC C5, PPFC C10, and PPFC G15 films show high light transmittances >90%, while the PPFC G30 films have the relatively low light transmittance of 75.70%. The b* values of the PPFC C5 and PPFC C10 films are similar to that of PPFC 0, but they are 3.48 and 6.99 for the PPFC G15 and PPFC G30 films, respectively, up to 5 times higher than that of the PPFC 0 film, due to the composition ratio of CNT and graphite in composite target increased, the amount of sputtered carbon atoms increased relatively. Previous studies have reported that the optical band gap of hydrocarbon materials, including DLC and fluorocarbon, decreases as the pi-states bonding of the sp2 hybrid configuration increases23,24. The decrease in optical transmittance and the increase in b* values mean an increase in the carbon composition ratio of PPFC thin films. Figure 2(b) shows the water contact angles of the sputtered fluorocarbon film surfaces according to the carbon concentration in the targets and the surface energies calculated by GGFY (Girifalco–Good–Fowkes–Young) method. The surface energy of PPFC C5 is 12.34 × 10−3 N/m; that of PPFC C10 was 10.73 × 10−3 N/m, similar to that of 9.73 × 10−3 N/m shown by PPFC 0. The surface energy increases from 10.0 × 10−3 N/m in PPFC 0 to 38.5 × 10−3 N/m in PPFC G30. This property change is also attributed to the increase in carbon concentration of the PPFC thin film as the carbon ratio of the composite target is increased. Figure 2(c) shows the 550-nm optical transmittance and b* yellowness parameters of the sputtered fluorocarbon films at different sputtering power densities. The PPFC C5 and PPFC C10 thin films show no significant changes in properties with different sputtering power densities; however, for carbon contents exceeding 15 wt%, the PPFC G15 and PPFC G30 films increase in transparency and hydrophobicity. As the sputtering power density is increased, the light transmittance increases from 87.80% to 91.95% for the PPFC G15 thin film and from 75.70% to 91.32% for the PPFC G30 thin film; b* decreases from 4.40 to 2.60 for PPFC G15 and from 6.99 to 3.38 for PPFC G30. Previous studies of polymer materials using mass spectroscopy analysis have revealed that heavier fragments are sputtered at higher sputtering power densities25,26. A previous work also reported that in PTFE decomposition by glow discharge, C, C2F4, C2F6, C3F6, C3F8, and additional heavier substances are generated27. Other researchers have reported that the partial sputter yield of fluorine increases as the impact energy of argon ions is increased28. Figure 2(d) shows the water contact angles according to sputtering power density. The changes in the water contact angle of the PPFC thin films almost coincide with the tendency of the changes in light transmittance shown in Fig. 2(c). As the sputtering power density is increased, the PPFC G15 thin film contact angle increases from 76° to 100° and that of the PPFC G30 thin film increases from 72° to 101°. In order to investigate the compositional changes of the thin films with respect to the sputtering power density in this study, the binding energies between carbon and fluorine in the thin films were analyzed by XPS and the quantitative fluorine–carbon ratios were calculated.

Figure 2.

Figure 2

Open in a new tab

(a) 550 nm-optical transmittances and b* yellowness parameters and (b) water contact angles and surface energies of PPFC thin films according to carbon concentration in composite polymer target. (c) 550-nm optical transmittance and b* yellowness parameters and (d) water contact angles of PPFC thin films according to sputtering power density.

Figure 3(a) shows the XPS spectra of the C 1s binding energy regions for the PPFC thin films. In order to remove surface impurities, each sample was subjected to an argon plasma etching treatment for 5s. In some samples, hydrocarbon (C–H) peaks at 285.0 eV remain due to the surface adsorption of organic materials. In this energy region, a binding energy shift occurs by the fluorine atom screening effect near the observed carbon atoms. As reported in previous studies, the peaks at 294.0 eV, 292.0 eV, 239.8 eV, and 286–288 eV represent –CF3, –CF2-, C-F, and C-CFn carbon crosslinked bonding, respectively22,25,26,29. Figure 3(b) shows the fluorine–carbon bond ratios (abbreviated F/C ratios) and F atomic concentrations calculated by the decomposition of the XPS C 1s peaks according to the carbon concentrations in the targets. The F/C ratios are calculated by the deconvoluted areas of the –CF3, -CF2-, and –CF peaks relative to the total area of C 1s region6,30. The fluorine atomic concentration is quantitatively calculated from the C 1s photoelectron in the 284.8 eV region and the F 1s photoelectron in the 689.2 eV region, considering atomic scattering factors. The fluorine composition ratio of the PPFC G30 thin film is 8.85%, while that in the PPFC 0 thin film is greatly reduced by 55.17%, because the carbon sputtering yield is two times higher than that of PTFE28,31. The C–CFn peak shown in Fig. 4(a) shifts to a lower bonding energy according to the decreasing fluorine atom concentration, also attributed to the decrease of fluorine atoms around carbon atoms. Figure 3(c) shows the XPS spectra of the PPFC G30 films formed with different sputtering power densities; Fig. 3(d) shows the F/C ratio and fluorine atomic concentration calculated by the decomposition of the XPS C 1s peak. The atomic concentration of fluorine in the PPFC G30 thin films is increased with sputtering power density, consistent with the optical and surface properties of the PPFC G30 thin films shown in Fig. 2.

Figure 3.

Figure 3

Open in a new tab

XPS spectra of (a) PPFC 0, PPFC C5, PPFC C10, PPFC G15, and PPFC G30 and (b) F/C ratio and fluorine atomic concentration calculated by decomposition of XPS C 1s peak. XPS spectra of (c) PPFC G30 thin films according to sputtering power density and (d) F/C ratio and fluorine atomic concentration of PPFC G30 films calculated by decomposition of XPS C 1s peak.

Figure 4.

Figure 4

Open in a new tab

Nanoindentation curves of (a) PPFC thin films and (b) calculated surface hardness and modulus according to the carbon content of the targets. Nanoindentation curves of (c) PPFC G30 thin films according to sputtering power density and (d) calculated surface hardness and modulus.

The surface hardness values of the thin films were analyzed by the nanoindentation method in order to examine the influence of the composition of the composite target and the sputtering power density on the hardness of the PPFC thin films. Figure 4(a) shows the nanoindentation curve of the PPFC thin films fabricated with varied composite targets. As the carbon composition ratio of the target is increased, the indentation depth of the deposited PPFC thin film decreases, which means that the surface hardness of the PPFC thin film increases. The general formula for calculating the surface hardness through the nanoindentation method is as follows32.

HIT=Pmax/Ac 1
Ac=24.5hc2(Berkovichtip) 2

Here, HIT is the indentation hardness, Pmax is the peak indentation load, and Ac is the projected area of the hardness impression. The Ac for the geometry of the Berkovich tip is given in Eq. (2) from32; hc is the contact height, excluding elastic recovery, at the maximum displacement of the Berkovich tip. Figure 4(b) shows the surface hardness and modulus calculated from the indentation curve. The surface hardness values of the PPFC thin films increase by 17.5 times from 0.22 GPa for PPFC 0 to 3.85 GPa for PPFC G30. This result means that the cross-linking density of the carbon in the PPFC thin films increases, which is consistent with the XPS analysis results. The modulus of the PPFC thin films increases from 4.30 GPa of PPFC 0 to 113.00 GPa of PPFC G15 and then decrease to 64.09 GPa in PPFC G30. This change in modulus indicates that the PPFC G30 thin film is more resilient to external energy, as visually demonstrated by the differences in strain energy dissipation, represented by the areas of the indentation curves for the different films. Figure 4(c) shows the nanoindentation curves of the PPFC G30 thin films according to the sputtering power density; the calculated surface hardness and modulus are shown in Fig. 4(d). The PPFC G30 thin film shows the surface hardness of 4.75 GPa at 3.08 W/cm2, which is 22.6 times higher than the 0.22 GPa hardness of PPFC 0; both surface hardness and modulus decrease with increasing power density. This is due to the increase of the fluorine concentration in the PPFC thin films as the sputtering power density is increased and the carbon cross-linking density of the PPFC thin film is decreased, as confirmed by the C-CFn peak shown in Fig. 3(c).

Figure 5 shows the results of Raman spectroscopy to further analyze the changes in carbon bonding structures of the PPFC films according to the changing carbon composition ratios of the targets. Figure 5(a) shows the Raman spectra of the PPFC 0, PPFC C5, PPFC C10, PPFC G15, and PPFC G30 thin films. At 1380 cm−1, the D peak corresponding to disorder in carbon is detected by the A1g symmetric mode of amorphous carbon; at 1590 cm−1, the G peak indicating graphitic carbon is detected by the zone-center E2g symmetric vibration mode of carbon. In the PPFC 0 film, neither D nor G peak is detected. This is the fluorine atom in fluorocarbon films that disrupts the symmetry of the carbon bond and A1g and E2g symmetry, which means that thin films arrangement is changed from a diamond-like to a polymer-like one33–35. In the PPFC 5 C thin film, only the G peak is weak at 1612 cm−1. Raman curves of PPFC C10, PPFC G15, and PPFC G30 films show equivalent D peaks at 1373 cm−1. The G peaks of the PPFC C10, PPFC G15, and PPFC G30 thin films are at 1597 cm−1, 1595 cm−1, and 1573 cm−1, respectively. As the carbon concentration of the PPFC thin films is increased, the intensities of the D peak and G peak tend to increase. This result is consistent with the increasingly intense C-CFn peaks in the XPS analysis shown in Fig. 3(a). Figure 5(b) shows the relationship between the deconvoluted D peak and G peak fitted to the Raman spectra. The ratio of the D/G peak intensity decreases as the carbon concentration in the PPFC is increased, suggesting that PPFC thin films with higher carbon cross-linking densities are formed23. The increases in the carbon cross-linking densities in the thin films cause increases in the thin film hardness values. PPFC G30 thin films fabricated at high sputtering power densities show decreases in D and G peak intensity; at the power higher than 3.69 W/cm2, the D and G peaks are not detected, because the A1g and E2g symmetry are collapsed by the increased fluorine content. The XPS and Raman spectral analyses show that the number of bonds between carbons increases as the carbon concentration in the target is increased, and that carbon cross-linking density becomes high in the PPFC thin films.

Figure 5.

Figure 5

Open in a new tab

(a) Raman spectra of PPFC 0, PPFC C5, PPFC C10, PPFC G15, and PPFC G30 thin films and (b) deconvoluted D and G peak positions and relative intensities determined by fitting of the Raman spectra.

The PPFC G30 thin film deposited at 3.08 W/cm2 showed a high surface hardness of 4.75 GPa, but the fluorine atomic fraction was lower than PPFC 0, as reflected by the optical transmittance of 85.83% (5.77% lower than that of PPFC 0) and the surface energy (water contact angle) of 30.95 × 10−3 N/m (80°), which is 21.22 × 10−3 N/m higher than that of PPFC 0. The PPFC G30 film with a power density of 4.92 W/cm2 showed a twofold increase in the fluorine composition ratio relative to that of the film formed at 3.08 W/cm2, a light transmittance of 91.32%, and a surface energy (water contact angle) of 15.99 × 10−3 N/m (100°). On the other hand, the surface hardness of the highest power density sputtered PPFC G30 thin film 4.92 W/cm2 was 0.91 GPa, which is one-fifth of PPFC deposited at G30 3.08 W/cm2, but four times higher than the 0.22 GPa hardness measured from PPFC 0. The PPFC thin films prepared by the MF sputtering of composite polymer targets, as proposed in this study, show controllable physical properties of optical transmittance, surface hardness and surface water repellency with manipulation of the composition of the target and the sputtering power density.

Conclusion

In this study, CNT/PTFE and Graphite/PTFE composite targets were fabricated and PPFC thin films were deposited by MF sputtering using the targets. The PPFC 0, PPFC C5, and PPFC C10 thin films with lower carbon concentrations in the film matrix backbones showed high optical transmittances and surface water repellency irrespective of sputtering power, while the PPFC G15 and PPFC G30 films with higher carbon concentrations showed lower optical transmittance and surface water repellency at the sputtering power density of 2.46 W/cm2. The XPS and Raman spectroscopic analyses of the PPFC thin films revealed that, as the carbon concentration in target was increased, the carbon cross-linking density of the PPFC thin films increased, yielding a hardness value 21.6 times that of the PPFC 0 thin films. As the sputtering power density was increased, the fluorine concentration of the PPFC thin film increased, as indicated by XPS analysis. As the fluorine concentration increased, the optical transmittances and water repellency of the thin films increased and the carbon cross-linking densities decreased. In this study, high-hardness PPFC thin films were successfully fabricated by using polymer composite targets, and it was confirmed that the composition and carbon cross-linking density of the thin films could be controlled by changing the sputtering power density.

Methods

Preparation of carbon/PTFE composite target

To investigate the effect of carbon contents on PPFC thin films, we designed polymeric composite target mixed with carbon materials. Multiwall CNT powder (HANOS CM-280, Hanwha Chemical) and PTFE powder (A7-J, Dupont Mitsui) were mixed in weight ratios of 5:85, 10:90, and 15:85 to fabricate relatively low carbon contents target. Graphite powder (TIMREX® KS44, Timcal) and PTFE powder were also mixed at weight ratios of 15:85, and 30:70 to fabricate composite targets having a higher carbon contents than CNT/PTFE. Each pre-mixed powder was press-molded with heat treatment and then milled to form a disk type target of 10 cm in radius and 6 mm in height. Pressure of compression was 200 kgf/cm2 and heat treatment temperature was 370 °C. The CNT/PTFE composite targets are named CNT 5, CNT 10 and CNT 15. The Graphite/PTFE composite targets are named Graphite 15, and Graphite 30.

Carbon-rich PPFC thin film fabrication

We designed the vacuum chamber (Cluster Sputter system, Charmtron) with a rotatable substrate size of 200 × 200 mm2. The sputter guns on the opposite side of the substrate were composed of two sputtering cathodes apparatus. Target-to-substrate distance was fixed at 240 mm. The sputtering chamber was evacuated by a rotary vane pump and cryogenic pump. Refrigerated surfaces at 10 K in cryogenic pump trapped residual gas to a level of 6 × 10−4 Pa. The processing atmosphere was 0.93 Pa argon gas controlled by a mass flow controller using throttle valve system. CNT 5, CNT 10, CNT 15, Graphite 15 and Graphite 30 composite targets were sputtered with a 40 kHz MF power source (PE II, Advanced Energy). In sputtering process, dual magnetron cathodes was used to improve sputtering efficiency. Thin films were deposited at power densities within 0.62~4.92 W/cm2. The 100 nm carbon-rich PPFC films were deposited on a 188 μm thick of PET film (Kimoto) and a silicon substrate (silicon (100) wafer, iTASCO).

Characterizations of carbon-rich PPFC thin films

The optical properties of the PPFC thin films were analyzed using a spectrophotometer (U-4100, Hitachi) in the wavelength range 300–2400 nm and compared in terms of transmittance at 550 nm and the b* parameter of yellowness. Surface properties of the PPFC thin film were measured by a contact angle analyzer (Phoenix 300 Touch, Surface Electro Optics). 2 μL of water was used as the contact angle measurement liquid, and its surface tension was 72 × 10−3 N/m. The surface energies were calculated by the Girifalco–Good–Fowkes–Young method. The chemical structures were analyzed using Raman spectroscopy (inVia Raman Microscope, Renishaw) and X-ray photoelectron spectroscopy (XPS, AXIS NOVA, Kratos). The surface hardness and modulus values were measured using the nanoindentation method (Nanoindentation, Anton Paar). The hardness measurements at an indentation force of 50 μN were analyzed.

Supplementary information

Supplementary Information (369.5KB, doc)

Acknowledgements

This study was supported by the Core Research Project at Korea Research Institute of Chemical Technology (KRICT) (KK-1953-20) funded by the Ministry of Science and ICT and was also supported by the Industrial Technology Innovation Program (no. 10079601) funded by the Ministry of Trade, Industry & Energy (MOTIE, Korea).

Author Contributions

S.-J.L. and Y.S.Y. and designed the study and the experiments. S.H.K. fabricated the fluorocarbon thin films using the sputter system. S.H.K., M.K., M.S.U., W.J.C. and J.H.L. analyzed the properties of the fluorocarbon thin films. Y.S.Y. and S.-J.L. wrote the manuscript. S.H.K. drew schematic design of target production process and the sputtering system. All of the authors discussed the results and commented on the manuscript.

Competing Interests

The authors declare no competing interests.

Footnotes

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Contributor Information

Yong Suk Yang, Email: ysyang@pusan.ac.kr.

Sang-Jin Lee, Email: leesj@krict.re.kr.

Supplementary information

Supplementary information accompanies this paper at 10.1038/s41598-019-46993-0.

References

  • 1.Biederman, H. Plasma Polymer Films 13–24 (World Scientific, 2004).
  • 2.Biederman H. RF sputtering of polymers and its potential application. Vacuum. 2000;59:594–599. doi: 10.1016/S0042-207X(00)00321-3. [DOI] [Google Scholar]
  • 3.Biederman H, et al. RF magnetron sputtering of polytetrafluoroethylene under various conditions. Thin Solid Films. 2001;392:208–213. doi: 10.1016/S0040-6090(01)01029-X. [DOI] [Google Scholar]
  • 4.Zaporojtchenko V, Podschun R, Schürmann U, Kulkarni A, Faupel F. Physico-chemical and antimicrobial properties of cosputtered Ag-Au/PTFE nanocomposite coatings. Nanotechnology. 2006;17:4904–4908. doi: 10.1088/0957-4484/17/19/020. [DOI] [Google Scholar]
  • 5.Schürmann U, Hartung W, Takele H, Zaporojtchenko V, Faupel F. Controlled syntheses of Ag-polytetrafluoroethylene nanocomposite thin films by co-sputtering from two magnetron sources. Nanotechnology. 2005;16:1078–1082. doi: 10.1088/0957-4484/16/8/014. [DOI] [Google Scholar]
  • 6.Iwamori S. Adhesion and tribological properties of sputtered polymer thin films with thermally stable polymer targets. J. Vac. Soc. Jpn. 2007;50:619–624. doi: 10.3131/jvsj.50.619. [DOI] [Google Scholar]
  • 7.Iwamori S, Noda K. Optical property of fluorocarbon thin films deposited onto polyester film substrate by an RF sputtering. Mater. Lett. 2012;66:349–352. doi: 10.1016/j.matlet.2011.08.041. [DOI] [Google Scholar]
  • 8.Gonon P, Sylvestre A. Dielectric properties of fluorocarbon thin films deposited by radio frequency sputtering of polytetrafluoroethylene. J. Appl. Phys. 2002;92:4584–4589. doi: 10.1063/1.1505983. [DOI] [Google Scholar]
  • 9.Sarkar DK, Farzaneh M, Paynter RW. Superhydrophobic properties of ultrathin RF-sputtered Teflon films coated etched aluminum surfaces. Mater. Lett. 2008;62:1225–1229. doi: 10.1016/j.matlet.2007.08.051. [DOI] [Google Scholar]
  • 10.Kamegawa T, Shimizu Y, Yamashita H. Superhydrophobic surfaces with photocatalytic self-cleaning properties by nanocomposite coating of TiO2 and polytetrafluoroethylene. Adv. Mater. 2012;24:3697–3700. doi: 10.1002/adma.201201037. [DOI] [PubMed] [Google Scholar]
  • 11.Takashi K, Koichi I, Hiromi Y. Multifunctional surface designed by nanocomposite coating of polytetrafluoroethylene and TiO2 photocatalyst self-cleaning and superhydrophobicity. Sci. Rep. 2017;7:13628. doi: 10.1038/s41598-017-14058-9. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 12.Huang C, Pan C-H, Tsai C-Y, Tseng I-Y. Fabrication of oleophobic fluorocarbon film by 13.56 MHz CH2F2/Ar plasma chemical vapor deposition. Surf. Coat. Tech. 2013;231:47–52. doi: 10.1016/j.surfcoat.2012.05.060. [DOI] [Google Scholar]
  • 13.Tang G, Ma X, Sun M, Li X. Mechanical characterization of ultra-thin fluorocarbon films deposited by RF magnetron sputtering. Carbon. 2005;43:345–350. doi: 10.1016/j.carbon.2004.09.022. [DOI] [Google Scholar]
  • 14.Jiang X, et al. Improvement of adhesion strength and scratch resistance of fluorocarbon thin films by cryogenic treatment. Appl. Surf. Sci. 2014;288:44–50. doi: 10.1016/j.apsusc.2013.09.103. [DOI] [Google Scholar]
  • 15.Jin JH, Ko J-H, Yang SC, Bae B-S. Rollable transparent glass-fabric reinforced composite substrate for flexible devices. Adv. Mater. 2010;22:4510–4515. doi: 10.1002/adma.201002198. [DOI] [PubMed] [Google Scholar]
  • 16.Gustafsson G, et al. Flexible light-emitting diodes made from soluble conducting polymers. Nature. 1992;357:477–479. doi: 10.1038/357477a0. [DOI] [Google Scholar]
  • 17.Li L, Jones PM, Hsia Y-T. Characterization of a nanometer-thick sputtered polytetrafluoroethylene film. Appl. Surf. Sci. 2011;257:4478–4485. doi: 10.1016/j.apsusc.2010.12.104. [DOI] [Google Scholar]
  • 18.He X-M, Hakovirta M, Nastasi M. Hardness, hydrophobic and optical properties of fluorine and boron co-alloyed diamond-like carbon films. Mater. lett. 2005;59:1417–1421. doi: 10.1016/j.matlet.2004.11.059. [DOI] [Google Scholar]
  • 19.Butter RS, Waterman DR, Lettington AH, Ramos RT, Fordham EJ. Production and wetting properties of fluorinated diamond-like carbon coatings. Thin Solid Films. 1997;311:107–113. doi: 10.1016/S0040-6090(97)00337-4. [DOI] [Google Scholar]
  • 20.Kim SH, Kim M, Lee JH, Lee S-J. Self-cleaning transparent heat mirror with a plasma polymer fluorocarbon thin film fabricated by a continuous roll-to-roll sputtering process. ACS Appl. Mater. Interfaces. 2018;10:10454–10460. doi: 10.1021/acsami.8b00761. [DOI] [PubMed] [Google Scholar]
  • 21.Newman SB, Young RW. Indentation hardness of the fingernail. J. Invest. Dermatol. 1967;49:103–105. doi: 10.1038/jid.1967.110. [DOI] [PubMed] [Google Scholar]
  • 22.Kim SH, et al. Fluorocarbon thin films fabricated using carbon nanotube/polytetrafluoro ethylene composite polymer targets via mid-frequency sputtering. Sci. Rep. 2017;7:1451. doi: 10.1038/s41598-017-01472-2. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 23.Robertson J. Diamond like amorphous carbon. Mater. Sci. Eng. R. 2002;37:129–281. doi: 10.1016/S0927-796X(02)00005-0. [DOI] [Google Scholar]
  • 24.Li QY, Wang FM, Zhang L. Study of colors of diamond-like carbon films. Sci. China Phys. Mech. Astron. 2013;56:545–550. doi: 10.1007/s11433-013-5002-z. [DOI] [Google Scholar]
  • 25.Yamada Y, Kurobe T. X-ray photoelectron spectroscopy of fluorocarbon films deposited by RF sputtering. Jpn. J. Appl. Phys. 1993;32:5090–5094. doi: 10.1143/JJAP.32.5090. [DOI] [Google Scholar]
  • 26.Kousal J, et al. RF magnetron sputtering and evaporation of polyisobutylene and low density polyethylene. Surf. Coat. Technol. 2005;200:472–475. doi: 10.1016/j.surfcoat.2005.02.107. [DOI] [Google Scholar]
  • 27.Mathias E, Muller CH. The decomposition of polytetrafluoroethylene in a glow discharge. J. Phys. Chem. 1967;71:2671–2675. doi: 10.1021/j100867a602. [DOI] [Google Scholar]
  • 28.Rzeznik L, Fleming Y, Wirtz T, Philipp P. Experimental and simulation-based investigation of He, Ne and Ar irradiation of polymers for ion microscopy. Beilstein J. Nanotech. 2016;7:1113–1128. doi: 10.3762/bjnano.7.104. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 29.Ueda A, et al. Fabrication of electrochemically stable fluorinated nano-carbon film compared with other fluorinated carbon materials. Carbon. 2009;47:1943–1952. doi: 10.1016/j.carbon.2009.03.041. [DOI] [Google Scholar]
  • 30.Stelmashuk V, Biederman H, Slavínská D, Zemek J, Trchová M. Plasma polymer films RF sputtered from PTFE under various argon pressures. Vacuum. 2005;77:131–137. doi: 10.1016/j.vacuum.2004.08.011. [DOI] [Google Scholar]
  • 31.Kolasinski RD, Polk JE, Goebel D, Johnson LK. Carbon sputtering yield measurements at grazing incidence. Appl. Surf. Sci. 2008;254:2506–2515. doi: 10.1016/j.apsusc.2007.09.082. [DOI] [Google Scholar]
  • 32.Jee AY, Lee MY. Comparative analysis on the nanoindentation of polymers using atomic force microscopy. Polymer Testing. 2010;29:95–99. doi: 10.1016/j.polymertesting.2009.09.009. [DOI] [Google Scholar]
  • 33.Jacobsohn LG, Maia da Costa MEH, Trava-Airoldi VJ, Freire FL. Hard amorphous carbon–fluorine films deposited by PECVD using C2H2–CF4 gas mixtures as precursor atmospheres. Diam. Relat. Mater. 2003;12:2037–2041. doi: 10.1016/S0925-9635(03)00200-0. [DOI] [Google Scholar]
  • 34.d’Agostino R, Lamendola R, Favia P, Giquel A. Fluorinated diamond like carbon films deposited from radiofrequency glow discharge in a triode reactor. J. Vac. Sci. Technol. A. 1994;12:308–313. doi: 10.1116/1.578873. [DOI] [Google Scholar]
  • 35.Touhara H, Okino F. Property control of carbon materials by fluorination. Carbon. 2000;47:241–267. doi: 10.1016/S0008-6223(99)00140-2. [DOI] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Supplementary Materials

Supplementary Information (369.5KB, doc)

Articles from Scientific Reports are provided here courtesy of Nature Publishing Group

RESOURCES