. 2019 Aug 19;10:1716–1725. doi: 10.3762/bjnano.10.167

Novel hollow titanium dioxide nanospheres with antimicrobial activity against resistant bacteria

Carol López de Dicastillo 1,2,✉, Cristian Patiño 1,2, María José Galotto 1,2, Yesseny Vásquez-Martínez 3,4, Claudia Torrent 4, Daniela Alburquenque 5, Alejandro Pereira 2,6, Juan Escrig 2,5
Editor: Jörg J Schneider
PMCID: PMC6720579  PMID: 31501743

Abstract

The search for and synthesis of new antimicrobial nanostructures is important to reduce microbial incidence that induces infectious diseases and to aid in the antibiotic resistance crisis, which are two of the most pressing issues in global public health. In this work, novel, hollow, calcined titanium dioxide nanospheres (CSTiO2) were successfully synthesized for the first time through the combination of electrospinning and atomic layer deposition techniques. Poly(vinylpyrrolidone) (PVP) electrosprayed spherical particles were double-coated with alumina and titanium dioxide, and after a calcination process, hollow nanospheres were obtained with a radius of approximately 345 nm and shell thickness of 17 nm. The structural characterization was performed using electron microscopy, and X-ray diffraction and small-angle X-ray diffraction evidenced an anatase titanium dioxide crystalline structure. Thermogravimetric analysis and Fourier-transform infrared spectroscopy studies demonstrated the absence of polymer residue after the calcination process. The antimicrobial properties of the developed CSTiO2 hollow nanospheres were evaluated against different bacteria, including resistant E. coli and S. aureus strains, and when compared to commercial TiO2 nanoparticles, CSTiO2 nanospheres exhibited superior performance. In addition, the positive effect of UV irradiation on the antimicrobial activity was demonstrated.

Keywords: antimicrobial nanoparticles, atomic layer deposition, electrospinning, hollow nanospheres, titanium dioxide

Introduction

Microbial contamination and the increase of multidrug bacterial resistance have become two major current concerns for food safety and human health due to the number of food-borne diseases and nosocomial infections both in developed and developing countries worldwide [1]. Thus, the search for new alternatives against microbial incidence has become an important challenge. In this context, nanoparticles (NPs) have become of great interest to researchers because of their high reactivity against both Gram-positive and Gram-negative bacteria [2]. In recent years, metal and metal oxide NPs, such as silver, gold, titanium and zinc oxide NPs, have been extensively studied due to their interesting antimicrobial character [3–5]. Titanium dioxide (TiO2) NPs have also attracted significant attention due to their high stability, low cost, reusability, and high photocatalytic activity [6–8]. These excellent properties have been applied in many products such as foods, catalyst support, air purification, water disinfection, antibacterial, cosmetics and solar cells [9–10]. Photocatalytic TiO2 favors the inactivation of microorganisms due to its strong oxidizing power by free radical generation, such as hydroxyl and superoxide anion radicals [11–12].

Metal oxide NPs have been commonly synthesized by chemical and physical methods, which can produce a high size variability, defects and agglomeration and can reduce the effectiveness of their properties [7,13–14]. The use of chemical reducing agents causes the production of larger particles with extra energy consumption and commonly low stability. Thus, the use of controlled technologies to obtain NPs with improved properties has attracted great interest [10,15]. In this work, the combination of electrospinning and atomic layer deposition (ALD) technologies are presented as an innovative strategy to develop titanium dioxide hollow nanospheres with controlled and homogeneous dimensions. Electrospinning is a technique able to produce different nanostructures, such as fibers and spherical particles, through the application of a high voltage that breaks the surface tension of the droplet of a polymeric solution located at the tip of a needle [16–17]. The morphology of the resulting nanostructures is influenced by the properties of the polymeric solution and the type of polymer. On the other hand, ALD is a novel metal oxide deposition process with excellent thickness control due to its low temperature processing and separated superficial reactions between precursor materials. Precursors are pulsed one by one over a substrate in the chamber and likewise purged to eliminate the unreacted substances and the by-product [18–20].

This is the first report on the development of metal oxide nanospheres synthesized using both electrospinning and ALD techniques. The resulting nanospheres were fully characterized by measuring the morphological, structural and thermal properties. In addition, the antimicrobial activity against common and multidrug-resistant bacteria were also studied. Crucial factors, such as the size, surface morphology and crystal structure of the NPs, were found to affect their antibacterial mechanism. Thus, the comparison of the antimicrobial activity of the developed hollow TiO2 nanospheres with commercial TiO2 NPs was also performed.

Results and Discussion

Material characterization

Titanium dioxide nanospheres were successfully obtained following the three-step procedure shown in Figure 1. First, electrosprayed spherical poly(vinylpyrrolidone) (SPVP) particles were obtained using a vertical electrospinning system. Subsequently, coated electrosprayed SPVP particles were obtained through the ALD process of Al2O3 (SPVP_Al2O3) and TiO2 (SPVP_Al2O3_TiO2) layers. Prior to the deposition of titanium dioxide, a very thin deposition of Al2O3 (alumina) was necessary with the role of fixing the SPVP particles to avoid their detachment during the TiO2 ALD step. Finally, the calcination process, carried out at 600 °C under an air atmosphere, was applied to remove the PVP polymer from the structures, resulting in hollow titanium dioxide nanospheres (calcined TiO2 spheres, CSTiO2).

Figure 1.

Figure 1

Open in a new tab

Three-step scheme to synthesize titanium dioxide nanospheres from electrosprayed SPVP spherical particles, resulting in hollow spheres after calcination, CSTiO2.

Figure 2 shows photographs and scanning electronic microscopy (SEM) images of structures obtained through the three-step scheme displayed in Figure 1. As Figure 2e shows, SPVP particles were successfully obtained through a stable electrospraying process by using a 20% (w/w) PVP polymeric solution. Unlike the common electrospinning process, which results in fibers by the continuous stretching of the Taylor cone through the application of a voltage to a polymeric solution with high viscosity, this case was considered an “electrospraying” process, which resulted in spherical particles due to the low-viscosity-based solution. In this process, the electric field generated monodisperse drops that contracted due to the fast evaporation of the solvent induced by Columbic explosion [21–22].

Figure 2.

Figure 2

Open in a new tab

Photographs of: (a) electrosprayed spherical PVP particles (SPVP); (b) deposition of Al2O3 on SPVP by ALD (SPVP_ Al2O3); (c) deposition of TiO2 on the SPVP_ Al2O3 material by ALD (SPVP_ Al2O3_ TiO2); (d) calcined samples (CSTiO2); Scanning electronic microscopy (SEM) images of: (e) SPVP; (f) SPVP_ Al2O3, (g) SPVP_Al2O3_TiO2; (h) CSTiO2.

Figure 2a–c shows photographs of the three steps of the process: electrosprayed, alumina coated and alumina–titania double-coated particles. The alumina deposition maintained the initial white color of the collected electrosprayed spheres, while the TiO2 deposition acquired a dark bluish color. This change may be related to the number of deposition cycles that produced an optical interference due to the amount of deposited material [18,23]. SEM images presented in Figure 2e–g revealed that the morphology of the spheres was maintained after the depositions, ensuring uniformity and homogeneity.

Subsequently, TiO2-coated nanospheres underwent a calcination process at 600 °C, resulting in the final, hollow nanostructures. This thermal treatment produced a change of color to white (Figure 2d), which was associated with the change of the TiO2 crystalline structure. Furthermore, as Figure 2h and Figure 3a–d show, SEM and transmission electronic microscopy (TEM) images confirmed that the spherical morphology was maintained after the calcination treatment.

Figure 3.

Figure 3

Open in a new tab

TEM images of calcined nanospheres, CSTiO2, at: (a) 2000×; (b) 5000×; (c) 10000× and (d) further details of the image in (c).

Specifically, TEM images of CSTiO2 also evidenced the presence of holes in the walls of some nanostructures, which were likely produced due to the thermal degradation and release of the PVP polymeric backbone. In general, the thermal treatment at 600 °C did not generate enough pressure to break the nanosphere wall because of the double protection offered by the internal layer with Al2O3 and external layer with TiO2. TEM analysis also revealed that the total thickness obtained was approximately 16.8 nm after both ALD processes were performed (Figure 3c).

Energy dispersive X-ray (EDX) analysis was performed to determine the elemental composition of CSTiO2 and to confirm the presence of both Al2O3 and TiO2 layers. The EDX mapping results are shown in Figure 4a, where red, green and yellow colors correspond to oxygen, aluminum and titanium, respectively. The image did not present both layers separately, probably because the alumina layer was very thin and covered by the TiO2 layer. The peak corresponding to elemental titanium (Figure 4b) comprised the principal composition (38.8%) of the sample. Additional analysis regarding the chemical composition was also performed by Fourier-transform infrared spectroscopy (FTIR) in order to study the main functional groups of the sample (data found in Supporting Information File 1).

Figure 4.

Figure 4

Open in a new tab

(a) EDX mapping marked with red (oxygen), green (aluminum) and yellow (titanium), (b) EDX spectrum of a CSTiO2 SEM image; and (c) TGA curves of the developed structures.

Thermogravimetric analysis (TGA) curves representing the mass loss with respect to temperature of SPVP, coated electrosprayed spheres (SPVP_Al2O3 and SPVP_Al2O3_TiO2), and CSTiO2 structures are shown in Figure 4c. Except for the CSTiO2 sample, the uncoated and coated samples presented mass loss between 5 to 10% below 100 °C, corresponding to the dehydration process of the polymeric material in these structures. As expected, the TGA curves of structures containing PVP clearly evidenced both typical PVP degradation processes: i) the carbonic backbone decomposition around 200 °C; and ii) pyrrolidone group decomposition between 350 and 470 °C [24–26]. TGA was used to verify two important facts: i) The calcination process effectively removed the PVP polymer, since CSTiO2 presented the same TGA curve as the commercial TiO2 NPs. TGA curves of CSTiO2 did not show any PVP degradation process thereby demonstrating that CSTiO2 was PVP-free. ii) The aluminum oxide and titanium dioxide deposited during the ALD processes were (0.16 ± 0.02)% and (23.41 ± 0.47)% with respect to the polymer weight, respectively. The deposition of titania, when compared to our previous work, confirmed that the deposition onto the PVP polymer and polyvinyl alcohol presented a similar rate and it was mainly dependent on the number of cycles that determine the growth of thickness in the sample [18,27–28]. A small weigh loss of approximately 2% was found in CSTiO2, probably associated with the decomposition of hydroxyl groups on the titanium dioxide surface [29].

X-ray power diffraction (XRD) analysis of the structures is shown in Figure 5. SPVP diffraction patterns showed a broad band with peak at 2θ equal to 20.3° (solid line) corresponding to the amorphous nature of the PVP polymer [30–33]. Because they were independent of the samples, the peaks at approximately 11.2, 30 and 40° corresponded to the noise baseline due to the nature of the samples. XRD diffractograms revealed that the calcination was an aggressive thermal treatment that resulted in an anatase TiO2 crystalline structure in the CSTiO2 sample [34–36]. Although previous works have mentioned that the anatase structure of TiO2 is a metastable structure, and can be irreversibly transformed into a stable rutile structure by heating, this process did not occur during calcination. The anatase–rutile transition occurs between 400 to 1000 °C, and it is dependent on several parameters, such as the size of the nanocrystals, impurity content, microstructure and surface area. The necessary activation energy is high and the process is slow. In addition, some works have also confirmed that the anatase phase can be stable up to 600 °C, and the rutile phase can be delayed to higher temperatures [36–38]. The anatase crystalline structure was confirmed by the presence of peaks at 25.28, 37.8, 48.05, 53.89, 55.06, 62.69, 68.76, 70.31 and 74.03º (dashed lines). This crystalline structure can present promising antimicrobial activity due to the fact that several studies have declared that this structure presents the highest antimicrobial activity owing to its higher photocatalytic nature than rutile or brookite structures [39–41].

Figure 5.

Figure 5

Open in a new tab

XRD diffraction patterns of: PVP electrosprayed spheres (SPVP), double coated spheres (SPVP_Al2O3_TiO2) and hollow TiO2 nanospheres (CSTiO2).

The small-angle X-ray scattering (SAXS) technique is a powerful technique that is based on the spatial fluctuations of the electronic density of the material that allows for the measurement of polymers, alloys, and amorphous materials, whose size varies between 1 nm and several hundreds of nanometers [42]. Figure 6 shows the I(q)–q plot (SAXS curve) of the CSTiO2 structures. Additionally, the q in the Figure 6 is the scattering vector and I(q) is the intensity of scattering, respectively. The SAXS data were analyzed using the DIFFRAC.SAXS program that can fit and evaluate the size of the structures assuming different geometries. In this work, a core/shell particle was obtained with a particle radius of 345 nm and a shell thickness of approximately 17 nm. These results revealed an excellent agreement with the data obtained from TEM images shown in Figure 3.

Figure 6.

Figure 6

Open in a new tab

The I(q)–q plot of CSTiO2 structures obtained by SAXS.

Antimicrobial activity

The improved bioactivity of nanometer-sized TiO2 particles is due to the area of contact and/or volume that is increased by reducing the particle size, specifically in this case the thickness (<100 nm), which allows greater interaction with molecules and proteins of the cellular membrane and a lower amount of substance [2,43–44]. In this work, the evaluation of the antibacterial activity of CSTiO2 with a spherical morphology and nanoscale-thickness of approximately 17 nm was evaluated and compared with traditional TiO2 NPs. The reduction of thickness of these nanostructures was obtained by reducing the cycles of deposition during the ALD process [18,45–46]. The antibacterial activity of CSTiO2 and TiO2 NPs was evaluated by the inhibition of growth of Staphylococcus aureus (control strain ATCC®6538TM and resistant strain MRSA 97-7 and MRSA 622-4) and Escherichia coli (control strain ATCC®25922TM and resistant strain E. coli 33.1). When the analysis was done using control strains, the results in Table 1 indicate that CSTiO2 presented an improved antibacterial activity against S. aureus and a similar activity against E. coli in comparison with commercial TiO2 NPs. Nevertheless, when assays were carried out with resistant bacteria, only CSTiO2 presented promising antibacterial activity against E. coli MRSA 33.1. This low performance could be due to the increased multidrug resistance evidenced by some bacteria due to different mechanisms, such as reduced cell permeability, target overproduction and protection [47]. As Table 1 shows, the concentration of the strongest antibiotics commonly used against these bacteria were in the range of 25–150 µg mL−1.

Table 1.

Percent inhibition of nanostructures against resistant and control bacterial strains.

Antimicrobial compound Percent inhibition of bacterial growth at 100 µg mL−1
S. aureus ATCC6538 S. aureus MRSA 97-7 S. aureus MRSA 622-4 E. coli ATCC25922 E. coli MRSA 33.1
CSTiO2 20% 0% 0% 40% 7%
TiO2 NPs 0% 0% 0% 35% 11%
Vancomycin (25 µg mL−1) 100% 100% 100% – –
Ampicillin (150 µg mL−1) – – – 100% 100%
Open in a new tab

In general, CSTiO2 exhibited higher antibacterial capacity against Gram-negative bacteria, such as control and resistant E. coli strains, than Gram-positive bacteria, such as S. aureus ATCC 6538, MRSA 97-7 and MRSA 622-4. Different mechanisms of antimicrobial activity can be exerted by NPs. Specifically, in the case of TiO2 NPs, previous works have declared bactericidal activity via reactive oxygen species (ROS) generation and disruption of bacteria cell walls in the case of E. coli, and release and reactions of ions with thiol groups belonging to proteins of the bacterial membrane of S. aureus [48–49].

Probably, CSTiO2 presented better affinity and greater contact area with Gram-negative bacteria cells due to their cell wall structure, allowing a greater ROS formation. This tendency was already observed with TiO2 dioxide nanotubes developed in a previous work [18].

Due to the photocatalytic nature of titanium dioxide, different UV-A irradiation exposure times were studied in order to understand their effect on the antimicrobial activity of TiO2 nanostructures against S. aureus MRSA 97-7. The results shown in Table 2 validated that the antibacterial effect of CSTiO2 can be greatly increased due to the photocatalytic activity of these NPs in suspension. The antimicrobial performance of CSTiO2, induced by exposure to UV-A light (<390 nm), occurred generally through the generation of ROS and specifically from hydroxyl radicals (OH•) (through electron abstraction from water) and superoxide anion radicals O2• (generated by the reduction of O2). ROS incidence can attack microbial cells through various processes, such as lipid peroxidation of cell membrane, damaging DNA and/or amino acid- and protein-based cell oxidation [50–51]. This analysis also evidenced that, although an important enhancement of CSTiO2 antimicrobial activity occurred within 60 min of UV irradiation, no further improvements in activity were observed with extended irradiation time. On the other hand, commercial TiO2 NPs did not present any antimicrobial activity against this resistant bacteria, even after a UV-irradiation time of 120 min. This fact can be due to the high resistance of this microorganism to these antimicrobial NPs at this concentration. Thus, a series of TiO2 NPs suspensions at increasing concentrations were examined over 60 min UV-irradiation. Assays revealed that commercial TiO2 NPs presented 28% reduction of S. aureus MRSA 97-7 strain at 300 µg mL−1.

Table 2.

Effect of UV irradiation on the antimicrobial activity of nanoparticles at 100 µg mL−1. The percent inhibition of the S. aureus MRSA 97-7 strain against 100 µg/mL of CSTiO2 and TiO2 NPs as a function of irradiation time is given.

Nanoparticles 0 min irradiation 20 min irradiation 60 min irradiation 120 min irradiation
CSTiO2 0% 5% 37% 36%
TiO2 NPs 0% 0% 0% 0%
Open in a new tab

Conclusion

This is the first report on the development of metal oxide nanospheres from the combination of electrospinning and atomic layer deposition processes. Although the purpose was the development of antimicrobial nanostructures based on titanium dioxide (due to its high photocatalytic nature), it was necessary to deposit a thin layer of alumina prior to the titania deposition to physically stabilize these low weight particles. Although previous works have demonstrated the successful deposition of metal oxides on nanofibers, the morphological change to spherical particles entailed a more difficult deposition process that was nevertheless successfully employed. Thus, hollow, spherical, antimicrobial nanostructures with a shell of 17 nm thickness were successfully obtained and antimicrobial results evidenced better performance than commercial TiO2 nanoparticles, principally against multidrug resistant bacteria such as the S. aureus strain. Antimicrobial tests also revealed that hollow TiO2 nanospheres present promising activity when irradiated with UV light. In addition to the antibacterial properties, these hollow nanospheres could be used for photocatalytic purposes. This represents a first work that opens up possibilities for the development of further nanostructures with different morphologies based on different metal oxides.

Experimental

Chemicals and microorganisms

Poly(vinylpyrrolidone) (PVP) (molecular weight 40.000), trimethylaluminium (TMA), tetrakis(dimethylamide)titanium (TDMAT) (99.99% trace metals basis) and ethanol were obtained from Sigma Aldrich (Santiago, Chile). Texas Industrial Solutions Advanced (Santiago, Chile) supplied commercial titanium dioxide nanoparticles commonly used in industrial applications, named TiO2 NPs.

Two clinical isolates of methicillin resistant Staphylococcus aureus 622-4 and 97-7, and one clinical isolate of Escherichia coli 33.1 were kindly donated by Dr. Marcela Wilkens from Universidad de Santiago de Chile (Chile). Control strains, S. aureus ATCC6538 and E. coli ATCC25922, were also used and provided from the same source.

A UV-A lamp bulb with 15 W from Philips (model Actinic BL TL TL-D 15W/10 1SL/25) was used.

Development of hollow TiO2 nanospheres

Electrosprayed SPVP materials were obtained using a vertical electrospinning system (Spraybase® power supply unit, Ireland). A 20% (w/v) PVP solution was prepared in 50% ethanol solution and stirred at room temperature until the polymer was completely dissolved. The solution was transferred to 5 mL plastic syringes and connected through a PTFE tube to a 20-gauge blunt (0.9 mm diameter) stainless steel needle charged by a high voltage power supply in the range of 0–20 kV. The parameters were previously optimized in order to obtain homogeneous spherical particles and the following values were used: flow rate 0.5 mL h−1, distance 12 cm and voltage 12.9 kV.

Coated electrosprayed SPVP particles were obtained through the deposition of Al2O3 and TiO2 layers using a Savannah S100 ALD device from Ultratech (San Jose, CA, USA) following the provider’s recipes from Cambridge NanoTech. 50 cycles of Al2O3 deposition was carried out at 80 °C using TMA and ultrapure water as precursors. Both TMA and H2O were unheated. The pulse times of TMA and water in the TMA/water cycle were kept at 0.015 s, while the exposure times in each half-cycle were 30 s and 60 s, respectively. Subsequently, the TiO2 deposition process was performed using the combination of the TDMAT precursor agent and ultrapure water for 300 cycles. These precursors were alternatively introduced into the ALD chamber at 200 °C with a pulse time of 0.1 and 0.015 s, respectively, while the exposure times were 10 s in both cases. The temperature of the TDMAT and H2O solutions were set at 75 °C and room temperature, respectively.

The calcination process was carried out at 600 °C for 1 h under air atmosphere.

Characterization of structures: from SPVP to CSTiO2

The morphology of each structure obtained through the entire process for the development of CSTiO2 was observed using SEM (Zeiss EVO MA10 SEM) at 20 kV. Electrosprayed SPVP particles, before and after the ALD processes, and hollow CSTiO2, obtained after the polymer template removal, were studied. CSTiO2 particles were also observed through TEM (Hitachi HT7700 high resolution TEM) at 100 kV. Additionally, the elemental composition of CSTiO2 was analyzed by SEM (Vega3 Tescan SEM) with an in-column EDX detector at 15 kV.

TGA was carried out using a Mettler Toledo Gas Controller GC20 Stare System TGA/DCS. The samples (≈6 mg) were heated from 25 to 800 °C at 10 °C min−1 under nitrogen atmosphere (flow rate 50 mL min−1).

XRD patterns were measured using a Siemens diffractometer D5000 (30 mA and 40 kV) using Cu Ka (λ = 1.54 Å) radiation at room temperature. All scans were performed in a 2θ range of 2–80° at 0.02° s−1.

SAXS measurements were performed using a Bruker N8 Horizon SAXS system equipped with a Cu Kα radiation (λ = 1.54 Å) source and 2D VÅNTEC-500 and MONTEL optics. The data were acquired in the q-range from 0.012–0.37 Å−1 with a measurement time of 14.400 s in vacuum (2 mbar) at room temperature. The generator was operated at a power of 1 kW. The data processing and analysis were performed using a Bruker DIFFRAC.SAXS program.

In vitro antibacterial activity assays using human pathogens

The antimicrobial activity of CSTiO2 against E. coli ATCC®25922TM, E. coli multiresistant 33.1, S. aureus ATCC®6538TM and methicillin-resistant S. aureus 97-7 and 622-4 were determined using the microdilution method established by Clinical and Laboratory Standards Institute with some modifications [52]. Briefly, stock solutions (5 mg mL−1) of nanoparticles in water were sonicated for 3 min and diluted in Mueller–Hinton broth (MHB) to the different two-fold assay concentrations. The obtained solution was then added to the MHB and serially two-fold diluted (in a 96-well microplate). 15 μL of inoculum at 5 × 106 colony-forming units (CFUs) per mL, prepared in MHB, was then added in a final volume of 150 μL.

The effect of UV irradiation on the antimicrobial activity was investigated by irradiating the 96-well microplate with a UV-A lamp located 25 cm above the samples for 0, 20, 60, and 120 min with 150 rpm stirring at room temperature. The plates were sealed with a tight-fitting plastic cover and incubated at 37 °C for 18 h. The assays were performed in triplicate. In wells containing MHB, 15 μL of inoculum served as a negative control. The antimicrobial activity of commercial TiO2 NPs was also evaluated in order to compare the effectiveness of both nanostructures.

Supporting Information

File 1

The study of structures through Fourier-transform infrared spectroscopy is described.

Acknowledgments

The authors acknowledge the financial support of CONICYT through the Project Fondecyt Regular 1170624, “Programa de Financiamiento Basal para Centros Científicos y Tecnológicos de Excelencia” (Project FB0807) and DICYT-USACH (grant No. 021601VM) and the Project Fondecyt 11171045.

References

  • 1.Dakal T C, Kumar A, Majumdar R S, Yadav V. Front Microbiol. 2016;7:1831. doi: 10.3389/fmicb.2016.01831. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 2.Wang L, Hu C, Shao L. Int J Nanomed. 2017;12:1227–1249. doi: 10.2147/ijn.s121956. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 3.Rai M K, Deshmukh S D, Ingle A P, Gade A K. J Appl Microbiol. 2012;112:841–852. doi: 10.1111/j.1365-2672.2012.05253.x. [DOI] [PubMed] [Google Scholar]
  • 4.Kadiyala U, Turali-Emre E S, Bahng J H, Kotov N A, VanEpps J S. Nanoscale. 2018;10:4927–4939. doi: 10.1039/c7nr08499d. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 5.Siddiqi K S, ur Rahman A, Tajuddin, Husen A. Nanoscale Res Lett. 2018;13(1):141. doi: 10.1186/s11671-018-2532-3. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 6.Xu Z, Zhuang C, Zou Z, Wang J, Xu X, Peng T. Nano Res. 2017;10:2193–2209. doi: 10.1007/s12274-017-1453-2. [DOI] [Google Scholar]
  • 7.Zhao Z, Zhang X, Zhang G, Liu Z, Qu D, Miao X, Feng P, Sun Z. Nano Res. 2015;8:4061–4071. doi: 10.1007/s12274-015-0917-5. [DOI] [Google Scholar]
  • 8.Feng X, Pan F, Zhao H, Deng W, Zhang P, Zhou H-C, Li Y. Appl Catal, B. 2018;238:274–283. doi: 10.1016/j.apcatb.2018.07.027. [DOI] [Google Scholar]
  • 9.Qiu K, Durham P G, Anselmo A C. Nano Res. 2018;11:4936–4954. doi: 10.1007/s12274-018-2137-2. [DOI] [Google Scholar]
  • 10.Li H, Zhou Q, Gao Y, Gui X, Yang L, Du M, Shi E, Shi J, Cao A, Fang Y. Nano Res. 2015;8:900–906. doi: 10.1007/s12274-014-0571-3. [DOI] [Google Scholar]
  • 11.Dhanasekar M, Jenefer V, Nambiar R B, Babu S G, Selvam S P, Neppolian B, Bhat S V. Mater Res Bull. 2018;97:238–243. doi: 10.1016/j.materresbull.2017.08.056. [DOI] [Google Scholar]
  • 12.De Falco G, Porta A, Del Gaudio P, Commodo M, Minutolo P, D’Anna A. MRS Adv. 2017;2:1493–1498. doi: 10.1557/adv.2016.665. [DOI] [Google Scholar]
  • 13.Aytekin Aydın M T, Hoşgün H L, Dede A, Güven K. Spectrochim Acta, Part A. 2018;205:503–507. doi: 10.1016/j.saa.2018.07.063. [DOI] [PubMed] [Google Scholar]
  • 14.Xu Z, Kan Y, Liu C. Mater Res Bull. 2018;107:80–86. doi: 10.1016/j.materresbull.2018.07.012. [DOI] [Google Scholar]
  • 15.Pat-Espadas A M, Cervantes F J. J Chem Technol Biotechnol. 2018;93:3091–3112. doi: 10.1002/jctb.5681. [DOI] [Google Scholar]
  • 16.Liu D, Zhang C, Dong G, Xu C, Liu D, Lv Y, Zhong B, Wang B. Mater Res Express. 2018;6:015007. doi: 10.1088/2053-1591/aae467. [DOI] [Google Scholar]
  • 17.Liu X, Yang Y, Yu D-G, Zhu M-J, Zhao M, Williams G R. Chem Eng J. 2019;356:886–894. doi: 10.1016/j.cej.2018.09.096. [DOI] [Google Scholar]
  • 18.López de Dicastillo C, Patiño C, Galotto M, Palma J, Alburquenque D, Escrig J. Nanomaterials. 2018;8(2):128. doi: 10.3390/nano8020128. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 19.Porro S, Bejtka K, Jasmin A, Fontana M, Milano G, Chiolerio A, Pirri C F, Ricciardi C. Nanotechnology. 2018;29:495201. doi: 10.1088/1361-6528/aae2ff. [DOI] [PubMed] [Google Scholar]
  • 20.Ricci P C, Laidani N, Chiriu D, Salis M, Carbonaro C M, Corpino R. Appl Surf Sci. 2018;456:83–94. doi: 10.1016/j.apsusc.2018.06.021. [DOI] [Google Scholar]
  • 21.Cui L, Liu Z-P, Yu D-G, Zhang S-P, Bligh S W A, Zhao N. Colloid Polym Sci. 2014;292:2089–2096. doi: 10.1007/s00396-014-3226-8. [DOI] [Google Scholar]
  • 22.Munir M M, Suryamas A B, Iskandar F, Okuyama K. Polymer. 2009;50:4935–4943. doi: 10.1016/j.polymer.2009.08.011. [DOI] [Google Scholar]
  • 23.Edy R, Zhao Y, Huang G S, Shi J J, Zhang J, Solovev A A, Mei Y. Prog Nat Sci: Mater Int. 2016;26:493–497. doi: 10.1016/j.pnsc.2016.08.010. [DOI] [Google Scholar]
  • 24.Mallakpour S, Behranvand V. Prog Org Coat. 2015;86:18–24. doi: 10.1016/j.porgcoat.2015.03.004. [DOI] [Google Scholar]
  • 25.Mallakpour S, Jarang N. Polym Bull. 2018;75:1441–1456. doi: 10.1007/s00289-017-2100-5. [DOI] [Google Scholar]
  • 26.Hulsey S, Absar S, Sultana Q N, Sabet S M, Mahfuz H, Khan M. Polym Compos. 2018;39(Suppl 2):E1025–E1033. doi: 10.1002/pc.24444. [DOI] [Google Scholar]
  • 27.Kavre Piltaver I, Peter R, Šarić I, Salamon K, Jelovica Badovinac I, Koshmak K, Nannarone S, Delač Marion I, Petravić M. Appl Surf Sci. 2017;419:564–572. doi: 10.1016/j.apsusc.2017.04.146. [DOI] [Google Scholar]
  • 28.Bishal A K, Sukotjo C, Takoudis C G. J Vac Sci Technol, A. 2017;35:01B134. doi: 10.1116/1.4972245. [DOI] [Google Scholar]
  • 29.Xiao Z, Guo P, Sun N. J Appl Polym Sci. 2017;134:44377. doi: 10.1002/app.44377. [DOI] [Google Scholar]
  • 30.Mangalam R, Thamilselvan M, Selvasekarapandian S, Jayakumar S, Manjuladevi R. Ionics. 2017;23:2837–2843. doi: 10.1007/s11581-016-1931-7. [DOI] [Google Scholar]
  • 31.Saroj A L, Singh R K, Chandra S. Mater Sci Eng, B. 2013;178:231–238. doi: 10.1016/j.mseb.2012.11.007. [DOI] [Google Scholar]
  • 32.Hong H-K, Park C-K, Gong M-S. Bull Korean Chem Soc. 2010;31:1252–1256. doi: 10.5012/bkcs.2010.31.5.1252. [DOI] [Google Scholar]
  • 33.Bai J, Li Y, Sun L, Zhang C, Yang Q. Bull Mater Sci. 2009;32:161–164. doi: 10.1007/s12034-009-0024-x. [DOI] [Google Scholar]
  • 34.López de Dicastillo C, Roa K, Garrido L, Pereira A, Galotto M. Polymers (Basel, Switz) 2017;9:117. doi: 10.3390/polym9040117. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 35.Kuchi C, Harish G S, Reddy P S. Ceram Int. 2018;44:5266–5272. doi: 10.1016/j.ceramint.2017.12.138. [DOI] [Google Scholar]
  • 36.Subhapriya S, Gomathipriya P. Microb Pathog. 2018;116:215–220. doi: 10.1016/j.micpath.2018.01.027. [DOI] [PubMed] [Google Scholar]
  • 37.Wang Z, Saxena S K, Pischedda V, Liermann H P, Zha C S. J Phys: Condens Matter. 2001;13:8317–8323. doi: 10.1088/0953-8984/13/36/307. [DOI] [Google Scholar]
  • 38.Mendoza-Anaya D, Salas P, Angeles-Chávez C, Pérez-Hernández R, Castaño V M. Rev Mex Fis. 2004;50(Suppl 1):12–16. [Google Scholar]
  • 39.Yoganarasimhan S R, Rao C N R. Trans Faraday Soc. 1962;58:1579–1589. doi: 10.1039/tf9625801579. [DOI] [Google Scholar]
  • 40.Nagalakshmi M, Karthikeyan C, Anusuya N, Brundha C, Basu M J, Karuppuchamy S. J Mater Sci: Mater Electron. 2017;28:15915–15920. doi: 10.1007/s10854-017-7487-0. [DOI] [Google Scholar]
  • 41.Purbia R, Borah R, Paria S. Inorg Chem. 2017;56:10107–10116. doi: 10.1021/acs.inorgchem.7b01864. [DOI] [PubMed] [Google Scholar]
  • 42.Shi W M, Dai X J, Yang G C, Xu Y, Liu Y. Mater Sci Forum. 2013;743–744:831–836. doi: 10.4028/www.scientific.net/msf.743-744.831. [DOI] [Google Scholar]
  • 43.Esfandiari N, Simchi A, Bagheri R. J Biomed Mater Res, Part A. 2014;102:2625–2635. doi: 10.1002/jbm.a.34934. [DOI] [PubMed] [Google Scholar]
  • 44.Cushing B L, Kolesnichenko V L, O'Connor C J. Chem Rev. 2004;104(9):3893–3946. doi: 10.1021/cr030027b. [DOI] [PubMed] [Google Scholar]
  • 45.Pessoa R S, dos Santos V P, Cardoso S B, Doria A C O C, Figueira F R, Rodrigues B V M, Testoni G E, Fraga M A, Marciano F R, Lobo A O, et al. Appl Surf Sci. 2017;422:73–84. doi: 10.1016/j.apsusc.2017.05.254. [DOI] [Google Scholar]
  • 46.Park J Y, Choi S-W, Kim S S. Nanotechnology. 2010;21:475601. doi: 10.1088/0957-4484/21/47/475601. [DOI] [PubMed] [Google Scholar]
  • 47.Baptista P V, McCusker M P, Carvalho A, Ferreira D A, Mohan N M, Martins M, Fernandes A R. Front Microbiol. 2018;9:1441. doi: 10.3389/fmicb.2018.01441. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 48.Li Y, Zhang W, Niu J, Chen Y. ACS Nano. 2012;6:5164–5173. doi: 10.1021/nn300934k. [DOI] [PubMed] [Google Scholar]
  • 49.Roy A S, Parveen A, Koppalkar A R, Ambika Prasad M V N. J Biomater Nanobiotechnol. 2010;1:37–41. doi: 10.4236/jbnb.2010.11005. [DOI] [Google Scholar]
  • 50.Brunet L, Lyon D Y, Hotze E M, Alvarez P J J, Wiesner M R. Environ Sci Technol. 2009;43:4355–4360. doi: 10.1021/es803093t. [DOI] [PubMed] [Google Scholar]
  • 51.Fu G, Vary P S, Lin C-T. J Phys Chem B. 2005;109(18):8889–8898. doi: 10.1021/jp0502196. [DOI] [PubMed] [Google Scholar]
  • 52.Barry A L, Craig W A, Nadler H, et al. Methods for Determining Bactericidal Activity of Antimicrobial Agents. 1999;19 [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Supplementary Materials

File 1

The study of structures through Fourier-transform infrared spectroscopy is described.

Beilstein_J_Nanotechnol-10-1716-s001.pdf (334.7KB, pdf)

Articles from Beilstein Journal of Nanotechnology are provided here courtesy of Beilstein-Institut

RESOURCES