Table 1.

Primary diameter, length aspect ratio and source of cellulose nanofibrils and nanocrystals.

Sample	Diameter (nm)	Length (nm) *	Aspect Ratio	Source
CNF 6.7 μm	38.7 ± 33.4	6.7×103 ± 3.2×103	158.9 ± 95.8	Consortium
CNF 6.1 μm	72.6 ± 63.6	6.1×103±2.7×103	83.9 ± 37.6	Consortium
CNC 280 nm	22.4 ± 7.2	279.1 ± 116.3	12.5 ± 5.2	Consortium
CNC 100 nm	15.4 ± 4.3	93.1 ± 45.0	6.0 ± 2.9	Maine
CNC 3.6 μm	23.8 ± 29.2	3.6×103±4.1×103	151.8 ± 171.7	Acid hydrolysis
CNC 1.1 μm	23.3 ± 21.8	1.1×103± 1.0×103	49.4 ± 44.7	Acid hydrolysis
CNC 210 nm	18.6 ± 5.7	210.9 ± 164.5	11.4 ± 8.9	Acid hydrolysis
CNC 150 nm	18.2 ± 5.1	153.4 ± 59.5	8.4 ± 3.3	Acid hydrolysis
CNC 110 nm	17.8 ± 5.8	112.4 ± 53.2	6.3 ± 3.0	Acid hydrolysis

^*P<0.001 between groups analyzed by ANOVA.