Preparation and Characterization of Sulfonated Magnetic SiO2 Microspheres as the Solid Acid Catalysts for Esterification

Ping Ke 1, Danlin Zeng 1,*, Jie Wu 1, Jiawei Cui 1, Xin Li 1, Guanghui Wang 1
PMCID: PMC6933779  PMID: 31891093

Abstract

graphic file with name ao9b03262_0001.jpg

The sulfonated magnetic SiO2 microsphere solid acid catalysts were prepared by the impregnation and grafting methods with iron oxide magnetic nanoparticles (Fe3O4 MNPs) as the magnetic cores. The catalytic properties of the magnetic SiO2 solid acid catalyst were studied in detail. The characterization results showed that the SiO2 was successfully coated on the Fe3O4 MNPs. Compared with the grafting method, impregnated solid acid exhibits higher catalytic performance, which reached an esterification rate of up to 99.00% when the reaction temperature was 105 °C, the molar ratio of n-butanol/adipic acid was 3:1, and the ratio of the catalyst (the mass of magnetic solid acid) to liquids (the total volume of n-butanol and adipic acid) was 2.95%. The magnetic solid acid exhibited great separation ability and reusability. After six times of recycle, the conversion of the grafted magnetic solid acid still attained 85.61% compared with that of the impregnated magnetic solid acid, which reduced to 81.35%, holding great potential for green chemical processes.

Introduction

The liquid acid catalyst is by far the greatly important area of catalysis in all sectors of chemical manufacturing1−3 due to its mild reaction conditions and simple processes. However, with the advancement of science and technology, people’s awareness of environmental protection has gradually improved, finding that the high toxicity and corrosive properties from liquid acid lead to a huge waste of energy and production of large amounts of waste products,4 which make it no longer adapt to the development of green chemistry. Recently, solid acid that is nontoxic,5 noncorrosive,6 high activity,7 and stable8 has attracted great interest among researchers, which make it possible to replace the liquid acids.9,10 Consequently, lots of experiments have been introduced for generating a variety of solid acid catalysts such as based on Ps-AlCl3,11 SO42–/SnO2,12 Sn-MFI,13 and clay,14 which have been widely used in many fields such as chemical synthesis, biomass conversion, adsorption, catalysis, and so forth. Moreno et al.12 synthesized the SO42–/SnO2 solid acid catalyst for catalyzing the production of biodiesel from oleic acid and methanol. The characterization results showed that the SO42–/SnO2 catalyst had a high specific surface area (87 m2/g), which enhanced its catalytic activity. However, the conventional supported solid acid catalysts were usually recovered by centrifugation or physical sedimentation, resulting in a low yield and failing to meet the needs of industrial continuous production. Compared with these catalysts, magnetic solid acids can be easily separated in the presence of an external magnetic field, particularly in viscous reaction solution.15 Recently, a series of magnetic solid acids were synthesized by the sulfonation method with various shell materials.16−18 However, many of the reported magnetic solid acids are unsatisfactory in acid-catalyzed reactions.15,19

One way to overcome this problem of the magnetic solid catalyst is to use relatively stable SiO2 nanoparticle as the carrier, which can protect the iron oxide magnetic core in the presence of the acidic solution. In this type of magnetic SiO2 solid acid, the reactive centers are highly mobile, similar to the nonmagnetic catalyst, and at the same time, it has the advantage of recyclability.20 Generally, impregnation and grafting methods are often used for the solid acid preparation. For the former, the solid acid has a good catalytic effect, high utilization rate, and low cost, while for the latter, the acid radical is connected to the surface of the silicon-based material in the form of a covalent bond, which makes the acidic group more stable.21−23 Both impregnation and grafting are effective methods for improving the catalytic activity in which solid acid’s high recyclability can be represented.

In this paper, iron oxide magnetic nanoparticles (Fe3O4 MNPs) were prepared by the hydrothermal method, and then the magnetic SiO2 was prepared by using the former Fe3O4 as the magnetic core. The magnetic SiO2 was used as the carrier to prepare the sulfonated magnetic SiO2 solid acid by impregnation and grafting methods. The catalytic activity of the magnetic SiO2 solid acid was investigated by the esterification of acetic acid and ethanol. The catalytic effect and cyclic stability of the impregnation and grafting modification methods were also compared, aiming to achieve the high activity and recyclability of magnetic solid acids by comparing to the previously reported nonmagnetic solid catalysts.

Results and Discussion

Morphological Analysis

The SEM and TEM images of Fe3O4 MNPs and magnetic SiO2 samples are shown in Figure 1. Spherical Fe3O4 with uniform particle size and uniform distribution can be seen in Figure 1. It could be inferred that the Fe3O4 microspheres were composed of finer microspheres from the fine particles on the spherical surface. Compared with Fe3O4 microspheres, the magnetic SiO2 particles exhibited a smooth surface, and the outer surface was coated with the SiO2 microspheres.

Figure 1.

Figure 1

Open in a new tab

SEM and TEM images of (a,c) Fe3O4 and (b,d) magnetic SiO2.

Continuously reunited and growing Fe3O4 grains can be seen in Figure 1c, which formed the big nanoparticles on the Fe3O4 surface. At the same time, it can be clearly seen from Figure 1d that the SiO2 particles were coated on the Fe3O4 particles. Additionally, the SiO2 particles were uniformly distributed, which made the surface of the magnetic SiO2 particles relatively smooth.

X-ray Diffraction

The XRD patterns of all as-prepared samples are shown in Figure 2. As shown in Figure 2, the characteristic peaks of Fe3O4 at 2θ = 18.5, 30.1, 35.5, 37.2, 43.2, 53.7, 57.1, 62.7, and 74.1° can be indexed as the diffractions of (111), (220), (311), (222), (400), (422), (511), (440), and (533), respectively, which are almost consistent with the diffraction peaks of the PDF standard powder diffraction card Fe3O4 (JCPDS 79-0419), indicating that the phase structure of Fe3O4 was the inverse spinel structure. Moreover, no obvious impurity peaks in the XRD pattern confirmed that the Fe3O4 showed a higher purity. It was interesting that the average size of Fe3O4 was calculated to be 17.9 nm,24 which inferred that Fe3O4 microspheres were composed of nanosized particles.

Figure 2.

Figure 2

Open in a new tab

XRD patterns of (a) Fe3O4, (b) magnetic SiO2, (c) impregnated solid acid, and (d) grafted solid acid.

Comparative analysis found that magnetic SiO2 and sulfonated magnetic SiO2 solid acid showed a broad diffraction peak at 2θ = 23° besides the characteristic diffraction peak of Fe3O4, which belongs to the characteristic peaks of the amorphous structure of SiO2, indicating that SiO2 was successfully coated on the Fe3O4 MNPs. Meanwhile, it can be seen from the XRD pattern of the solid acid that the intensity of the diffraction peak of Fe3O4 in the impregnated solid acid was slightly weakened, which indicated that Fe3O4 may be reacted during the sulfonation process, resulting in the relatively lower content.

Magnetic Analysis

The hysteresis loops of all samples are shown in Figure 3. As can be seen, all of the samples showed no hysteresis loops, and the coercive force was almost zero, indicating that they were superparamagnetic, which was consistent with the previous conclusions of XRD analysis. Compared with the high saturation magnetization (67.02 emu/g) of Fe3O4, the saturation magnetization (15.36 emu/g) of magnetic SiO2 was greatly reduced, which was caused by the thick layer of SiO2 wrapped on the surface of Fe3O4. The saturation magnetization of the impregnated magnetic SiO2 solid acid was 19.06 emu/g, slightly higher than that of the magnetic SiO2, which may be caused by a slight drop of the SiO2 shell during the sulfonation process.

Figure 3.

Figure 3

Open in a new tab

Hysteresis loops of (a) magnetic SiO2, (b) impregnated solid acid, (c) grafted solid acid, and (d) Fe3O4.

Besides, the grafted magnetic SiO2 solid acid exhibited a saturation magnetization of 37.83 emu/g, which was stronger than the saturation magnetization of the impregnated magnetic SiO2 solid acid. This was caused by the apparent shedding of the SiO2 shell on the surface of Fe3O4 during the grafting process, resulting in an increase in the relative content of Fe3O4.

Figure 4 shows the magnetic separation ability of the magnetic solid acid. It was found that the magnetic solid acid exhibited good separation ability regardless whether it was impregnated or grafted, which provided a strong basis for its high recyclability in the green industry.

Figure 4.

Figure 4

Open in a new tab

Magnetic separation of magnetic SiO2 solid acids: (a) impregnation and (b) grafting

FT-IR Spectra

The FT-IR spectra of all samples are shown in Figure 5. As shown in Figure 5, the broad bands at 3450 and 1640 cm–1 were attributed to the stretching vibration peaks and bending vibration peaks of O–H,25 respectively. The characteristic band observed in the FT-IR spectrum of Fe–O–Fe at 580 cm–1 was ascribed to the fundamental vibrational modes of Fe3O4. The characteristic bands around 470 and 953 cm–1 were the vibrational band of the Si–O–Si bond and Si–OH bond, respectively, indicating that the outer surface of Fe3O4 was coated with SiO2, which was caused by the large amount of hydroxyl groups on the surface of the silicon shell of Fe3O4. Furthermore, the band of 650 cm–1 in the solid acid was assigned to the S–O stretching vibration, showing that −SO3H were immobilized onto the surface of the magnetic SiO2 after acid modification, which can also be confirmed by the initial acidity of the impregnated magnetic solid acid being 4.127 mmol/L and that of the grafted ones being 1.584 mmol/L.

Figure 5.

Figure 5

Open in a new tab

FT-IR spectra of (a) magnetic SiO2, (b) grafted solid acid, (c) impregnated solid acid, and (d) Fe3O4.

Catalytic Activity and Cyclic Stability

The effects of reaction temperature, molar ratio of n-butanol/adipic acid, and catalyst (the mass of magnetic solid acid)/liquids (the total volume of n-butanol and adipic acid) on the esterification reaction are shown in Figure 6. It was found that different reaction factors showed a great influence on the esterification reaction. Figure 7 shows the conversion of grafted solid acid and impregnated solid acid as catalysts in six cycles.

Figure 6.

Figure 6

Open in a new tab

Effects of different conditions on esterification reaction of solid acid: (a) impregnation and (b) grafting.

Figure 7.

Figure 7

Open in a new tab

Effects of catalyst cycle times on conversion.

As shown in Figure 6, in the initial 0.5 h of the reaction, the esterification rate increased significantly with the increase of reaction time. As the reaction time prolonged, the esterification rate gradually increased to a steady state at a slower rate. This was because the reactants established a contact equilibrium with the catalyst during the reaction progress, achieving a higher esterification rate. While the reaction continued, this led to adsorption or even side effects of the product on the catalyst surface, inhibiting the progress of the esterification reaction.

The molar ratio had a significant effect on the esterification of solid acid compared with other factors in this paper. As shown from Figure 6II, the esterification rate of solid acid in this paper first increased then gradually became flat, with the increase of the molar ratio of n-butanol/adipic acid. The amount of n-butanol was less as the molar ratio was low, resulting in a lower conversion rate. As the molar ratio increases, the amount of n-butanol increased correspondingly, which was beneficial to the positive movement of the esterification reaction, and thus, the conversion rate was increased; however, the reaction reached equilibrium as there was an excessive increase of the molar ratio, resulting in a constant conversion rate and flat reaction curve.

Compared with the optimal reaction conditions (Figure 6) and cyclic stability (Figure 7) of two different magnetic solid acids, it can be found that the highest esterification rate of the grafted magnetic solid acid was 89.12%, while the esterification rate of the impregnation magnetic solid acid was up to 99.00% when the reaction temperature was 105 °C, the molar ratio of n-butanol/adipic acid was 3:1, and the ratio of the catalyst /liquids was 2.95%, which was increased by 11.09%, indicating that the catalytic activity of the impregnated magnetic solid acid was higher than that of the grafted magnetic solid acid. It also can be seen that the impregnated magnetic solid acid decreased remarkably with the increase in the cycle times, and the conversion decreased to 81.35% after six cycle times, which can be attributed to the leaching of the −SO3H absorbed on the outer surface during the reaction. It was confirmed by acidity detection of the impregnated catalyst after six cycle times, which showed that the amount of acid was greatly reduced from 4.127 to 1.856 mmol/g, which reduced by 55.03%. Meanwhile, the conversion of the grafted magnetic solid acid after the first cycle was 88.49%, and a small decline was observed for the next five cycles, which is mainly due to higher stability of the acid sites of the grafted catalysts. After six times of recycle, the conversion of the grafted solid acid still attained 85.61% with better stability, which can be confirmed by acidity detection of the grafted catalyst after six cycle times, showing that the amount of acid was slightly reduced from 1.584 to 1.203 mmol/g. Furthermore, the better thermal stability of the grafted catalyst from the thermogravimetric analysis (Figure 8), compared with the impregnated catalyst, also further supported the results of both conversion rates in Figure 7. The stability of both was comparable to those of the reported solid acid catalytic systems,26,27 especially the grafted magnetic solid acid.

Figure 8.

Figure 8

Open in a new tab

Comparison of TG analysis of catalysts.

Additionally, the catalytic properties of conventional solid acids were also studied,28−30 and a comparison with other solid acid catalysts under the same above conditions was analyzed as shown in Table 1. As can be seen, the solid acids exhibited high catalytic activity in the esterification reaction but still lower than those of the impregnated and grafted solid acids in this case, and the activity of the impregnated solid acid can be comparable to that of concentrated sulfuric acid. Combining Figures 4 and 7, it can be found that the solid acid prepared herein is not only easy to separate but also exhibits high catalytic activity and cyclic stability, thus showing a potential industrial application.

Table 1. Catalytic Performances of the Various Catalysts.

catalysts acidity (mmol/g) conversion (%) TOF (h–1)
impregnated solid acid 4.127 99.00 67
grafted solid acid 1.584 89.12 59
SO42–/ZrO2 3.643 70.82 42
HZSM-5 1.216 57.18 34
sulfuric acid   99.86 135
Open in a new tab

Conclusions

The Fe3O4 MNPs were prepared as the magnetic core of the magnetic SiO2 solid acid. The characterization results showed that the SiO2 was successfully coated on Fe3O4 particles. The −SO3H was also loaded on the catalysts after acid modification. The catalytic properties indicated that the impregnated magnetic solid acid showed a better catalytic activity (an esterification rate of up to 99.00%), while the grafted magnetic solid acid showed a better cyclic stability (the conversion attained 85.61%) after six times of recycle. Compared to the previously reported nonmagnetic solid catalysts, the magnetic solid acid prepared in this paper had a simple magnetic recovery process, higher catalytic activity, and cyclic stability, which can be a highly effective solid acid catalyst for green chemical processes.

Experimental Section

Materials

All chemicals including trisodium citrate, ferric chloride, urea, polyacrylamide, polyethylene glycol, ethanol, ammonia, tetraethyl orthosilicate(TEOS), sulfuric acid(98 wt %), 3-mercaptopropyl trimethoxysilane (MPTMS), toluene, methanol, hydrogen peroxide(H2O2, 30 wt %), adipic acid, n-butanol, cyclohexane, saturated saline were purchased from Sinopharm Chemical Reagent Co., Ltd. All other unlabeled chemicals were of analytical grade, and no further purification was required.

Preparation of Sulfonated Magnetic SiO2 Solid Acid

The steps for preparing the sulfonated magnetic SiO2 solid acid are as follows. 8 mmol of trisodium citrate, 4 mmol of FeCl3, and 12 mmol of urea were first dissolved in 80 mL of deionized water. Then 8 mmol of polyacrylamide and 0.4 mmol of polyethylene glycol were stirred and dissolved in deionized water. Next, the mixture was continuously reacted at 200 °C in a hydrothermal reaction kettle for 6 h, subsequently separated by an external magnet attraction, thoroughly washed with deionized water, and dried in a vacuum oven at 60 °C. Finally, the Fe3O4 MNPs were obtained by cooling and grinding.

Magnetic SiO2 microspheres were prepared by a procedure previously reported.31 1 mmol of Fe3O4 MNPs, 0.4 mol of ethanol, and 0.08 mol of deionized water were added into a three-neck flask. The solution was stirred until it was dispersed homogeneously. Then 0.08 mol of ammonia and 0.02 mol of TEOS were added dropwise, with subsequent stirring at 35 °C for 3 h. Next, the mixture was magnetically separated, thoroughly washed with deionized water, and dried in a vacuum oven at 60 °C to obtain the magnetic SiO2 microspheres.

The sulfonated magnetic SiO2 solid acid was prepared by impregnation and grafting methods as follows. For the former, SiO2 microspheres and sulfuric acid(m(SiO2):m(sulfuric acid) = 1:10) were heated at 200 °C for 4 h, and then the mixture was separated by a magnet attraction after cooling to room temperature, washed to the neutral filtrate, and finally dried. For the latter, 1 g of SiO2 microspheres, 0.3 mL of MPTMS, and 10 mL of toluene were refluxed at 110 °C for 12 h and subsequently dried after washing with toluene and ethanol, and then 30 mL of H2O2, 10 mL methanol, and 0.25 mL of sulfuric acid were added into the mixture. Finally, the solid acid sample was obtained by stirring and drying.

Characterization of the Samples

Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were performed by a PHILIPS XL30 instrument with a working voltage of 15 kV and a JEOL 2100F instrument with a working voltage of 200 kV, respectively. The X-ray diffraction (XRD) patterns were recorded on a Phillips Xpert Pro powder diffraction system using Cu Kα radiation with a Ni filter over the range of 10° ≤ 2θ ≤ 80°. Magnetic properties were measured using a BHV-55 vibrating sample magnetometer (VSM) from Riken Electronics Co. Ltd., Japan. FT-IR spectra (4000–500 cm–1) were recorded at room temperature on a Bruker VERTEX 70 FT-IR spectrometer using KBr in a ratio of 1:200.

Catalyst Properties

The catalyst properties are shown by the esterification rate and cyclic stability. The loading amounts (mmol/g) of total acids in the catalyst were determined using the modified acid–base titration referred to the literature.32−34 The 0.6 mL saturated saline was added into a mixed solution of 0.2 g of sulfonated magnetic SiO2 solid acid, 3.65 g of adipic acid, 4.6 mL of n-butanol, and 5 mL of cyclohexane in a 100 mL three-neck flask, subsequently stirred, and dissolved. Phenolphthalein was used as an indicator and titrated with 0.1 mol/L NaOH solution to determine the initial acid value and the reaction acid value, in which the calculation method was based on the Chinese national standard (GB/T1668-2008). The esterification rate was measured as follows

graphic file with name ao9b03262_m001.jpg 1
graphic file with name ao9b03262_m002.jpg 2

where X is the acid value, mg/g; Y is the esterification rate, %; c is the concentration of the standard NaOH solution, mol/L; V1 and V2 are the volumes of the NaOH solution consumed before and after the reaction, respectively, mL; X1 and X2 are the acid values before and after the reaction, mg/g; m is the mass of the reaction solution, g; and 56.11 is the conversion factor.

TOF (turn over frequency) was calculated by the data of the moles of converted reactant, the moles of acid sites, and the reaction equilibrium time, which reflected the intrinsic activity of the catalyst, and usually was measured as follows35

graphic file with name ao9b03262_m003.jpg 3

The steps for catalyst recycling experiment are as follows: the catalyst sulfonated magnetic solid acid was recovered by magnetic separation when the reaction was completed. The recovered catalyst was washed with methanol and dried at 105 °C in a vacuum oven. The recovered catalyst was reused for the next cycle, and other steps were the same.

Acknowledgments

We are very grateful to the financial support from the National Natural Science Foundation of China (Grant No. 21473126).

The authors declare no competing financial interest.

References

  1. Lotero E.; Liu Y.; Lopez D. E.; Suwannakarn K.; Bruce D. A.; Goodwin J. G. Synthesis of Biodiesel via Acid Catalysis. Ind. Eng. Chem. Res. 2005, 44, 5353–5363. 10.1021/ie049157g. [DOI] [Google Scholar]
  2. Olivier-Bourbigou H.; Magna L.; Morvan D. Ionic liquids and catalysis: Recent progress from knowledge to applications. Appl. Catal., A 2010, 373, 1–56. 10.1016/j.apcata.2009.10.008. [DOI] [Google Scholar]
  3. Andrijanto E.; Dawson E. A.; Brown D. R. Hypercrosslinked polystyrene sulphonic acid catalysts for the esterification of free fatty acids in biodiesel synthesis. Appl. Catal., B 2012, 115-116, 261–268. 10.1016/j.apcatb.2011.12.040. [DOI] [Google Scholar]
  4. Papatryfon X. L.; Heliopoulos N. S.; Molchan I. S.; Zubeir L. F.; Bezemer N. D.; Arfanis M. K.; Kontos A. G.; Likodimos V.; Iliev B.; Romanos G. E.; Falaras P.; Stamatakis K.; Beltsios K. G.; Kroon M. C.; Thompson G. E.; Klöckner J.; Schubert T. J. S. CO2 Capture Efficiency, Corrosion Properties, and Ecotoxicity Evaluation of Amine Solutions Involving Newly Synthesized Ionic Liquids. Ind. Eng. Chem. Res. 2014, 53, 12083–12102. 10.1021/ie501897d. [DOI] [Google Scholar]
  5. Zolfagharinia S.; Kolvari E.; Koukabi N. A practical heteropolyacid nanocatalyst supported on nano-sized ceramic for the chemoselective oxidation of sulfides to sulfoxides through an experimental design approach. Chem. Pap. 2017, 71, 2505–2520. 10.1007/s11696-017-0246-0. [DOI] [Google Scholar]
  6. Jing H.; Wang X.; Liu Y.; Wang A. Preparation of magnetic nanocomposites of solid acid catalysts and their applicability in esterification. Chin. J. Catal. 2015, 36, 244–251. 10.1016/S1872-2067(14)60221-7. [DOI] [Google Scholar]
  7. Tyufekchiev M.; Duan P.; Rohr-Schmidt K.; Granados Focil S.; Timko M. T.; Emmert M. H. Cellulase-Inspired Solid Acids for Cellulose Hydrolysis: Structural Explanations for High Catalytic Activity. ACS Catal. 2018, 8, 1464–1468. 10.1021/acscatal.7b04117. [DOI] [Google Scholar]
  8. Zeng D.; Liu S.; Gong W.; Wang G.; Qiu J.; Chen H. Synthesis, characterization and acid catalysis of solid acid from peanut shell. Appl. Catal., A 2014, 469, 284–289. 10.1016/j.apcata.2013.09.038. [DOI] [Google Scholar]
  9. Gupta P.; Paul S. Solid acids: Green alternatives for acid catalysis. Catal. Today 2014, 236, 153–170. 10.1016/j.cattod.2014.04.010. [DOI] [Google Scholar]
  10. Li Y.; Zeng D. Synthesis and characterization of flower-like carbon spheres solid acid from glucose for esterification. Mater. Lett. 2017, 193, 172–175. 10.1016/j.matlet.2017.01.071. [DOI] [Google Scholar]
  11. Tamami B.; Borujeny K. P. Chemoselective tetrahydropyranylation of alcohols and phenols using polystyrene supported aluminium chloride as a catalyst. Tetrahedron Lett. 2004, 45, 715–718. 10.1016/j.tetlet.2003.11.056. [DOI] [Google Scholar]
  12. Moreno J. I.; Jaimes R.; Gómez R.; Nióo-Gómez M. E. Evaluation of sulfated tin oxides in the esterification reaction of free fatty acids. Catal. Today 2011, 172, 34–40. 10.1016/j.cattod.2011.03.052. [DOI] [Google Scholar]
  13. Yuan E.; Dai W.; Wu G.; Guan N.; Hunger M.; Li L. Facile synthesis of Sn-containing MFI zeolites as versatile solid acid catalysts. Microporous Mesoporous Mater. 2018, 270, 265–273. 10.1016/j.micromeso.2018.05.032. [DOI] [Google Scholar]
  14. Muraleedharan L.; Bellundagere; Chandrashekara M.; Bangalore; Prakash S. J.; Bhat S. Clay-Based Solid Acid Catalyst for the Alkylation of p -Cresol with tert -Butyl Alcohol. ChemistrySelect 2018, 3, 801–808. 10.1002/slct.201702098. [DOI] [Google Scholar]
  15. Liu W.-J.; Tian K.; Jiang H.; Yu H.-Q. Facile synthesis of highly efficient and recyclable magnetic solid acid from biomass waste. Sci. Rep. 2013, 2419. 10.1038/srep02419. [DOI] [PMC free article] [PubMed] [Google Scholar]
  16. Liu N.; Zheng R. Y.; Liu W. Y.; Ma J. X.; Zheng X.; Li B.; Wang Z. Preparation and Characterization of Magenetically Core-Shell Structure Carbon Based Solid Sulfonic Acid. Adv. Mater. Res. 2012, 599, 86–90. 10.4028/www.scientific.net/AMR.599.86. [DOI] [Google Scholar]
  17. Liang X. Novel magnetic carbon based solid acid for alkylation of benzene and dodecene. Chem. Eng. J. 2015, 264, 251–257. 10.1016/j.cej.2014.11.105. [DOI] [Google Scholar]
  18. Shahamat Z.; Nemati F.; Elhampour A. Facile template-free route to fabricate core-shell Fe3O4@PANI-SO3H urchin-like nanoparticles as reusable catalyst for Hantzsch reaction: change morphology upon sulfonation. Res. Chem. Intermed. 2018, 44, 6649–6666. 10.1007/s11164-018-3514-x. [DOI] [Google Scholar]
  19. Zheng F. C.; Chen Q. W.; Hu L.; Yan N.; Kong X. K. Synthesis of sulfonic acid-functionalized Fe3O4@C nanoparticles as magnetically recyclable solid acid catalysts for acetalization reaction. Dalton Trans. 2014, 43, 1220–1227. 10.1039/C3DT52098F. [DOI] [PubMed] [Google Scholar]
  20. Karimi B.; Khalkhali M. Solid silica-based sulfonic acid as an efficient and recoverable interphase catalyst for selective tetrahydropyranylation of alcohols and phenols. J. Mol. Catal. A: Chem. 2005, 232, 113–117. 10.1016/j.molcata.2005.01.028. [DOI] [Google Scholar]
  21. Gholamzadeh P.; Ziarani G. M.; Lashgari N.; Badiei A.; Asadiatouei P. Silica functionalized propyl sulfonic acid (SiO2-Pr-SO3H): An efficient catalyst in organic reactions. J. Mol. Catal. A: Chem. 2014, 391, 208–222. 10.1016/j.molcata.2014.04.025. [DOI] [Google Scholar]
  22. Ziarani G. M.; Badiei A.; Hassanzadeh M.; Mousavi S. Synthesis of 1,8-dioxo-decahydroacridine derivatives using sulfonic acid functionalized silica (SiO2-Pr-SO3H) under solvent free conditions. Arab. J. Chem. 2014, 7, 335–339. 10.1016/j.arabjc.2011.01.037. [DOI] [Google Scholar]
  23. Ziarani Z. M.; Lashgari N.; Badiei A. Sulfonic acid-functionalized mesoporous silica (SBA-Pr-SO3H) as solid acid catalyst in organic reactions. J. Mol. Catal. A: Chem. 2015, 397, 166–191. 10.1016/j.molcata.2014.10.009. [DOI] [Google Scholar]
  24. Yan H.; Zhang J.; You C.; Song Z.; Yu B.; Shen Y. Influences of different synthesis conditions on properties of Fe3O4 nanoparticles. Mater. Chem. Phys. 2009, 113, 46–52. 10.1016/j.matchemphys.2008.06.036. [DOI] [Google Scholar]
  25. Wang W.; Yang X.; Fang Y.; Ding J. Preparation and performance of form-stable polyethylene glycol/silicon dioxide composites as solid-liquid phase change materials. Appl. Energy 2009, 86, 170–174. 10.1016/j.apenergy.2007.12.003. [DOI] [Google Scholar]
  26. Khder A. S.; El-Sharkawy E. A.; El-Hakam S. A.; Ahmed A. I. Surface characterization and catalytic activity of sulfated tin oxide catalyst. Catal. Commun. 2008, 9, 769–777. 10.1016/j.catcom.2007.08.022. [DOI] [Google Scholar]
  27. Ryoo H. I.; Hong L. Y.; Jung S. H.; Kim D. P. Direct syntheses of sulfonated mesoporous SiO2-TiO2-SO3H materials as solid acid catalysts. J. Mater. Chem. 2010, 6419. 10.1039/c0jm01174f. [DOI] [Google Scholar]
  28. Gowri Krishnan S.; Pua F. L.; Palanisamy K.; Nabihah S. Preparation of Oil Palm EFB Derived Solid Acid Catalyst for Esterification Reaction: Effect of Calcination Temperature. Key Eng. Mater. 2016, 701, 117–121. 10.4028/www.scientific.net/KEM.701.117. [DOI] [Google Scholar]
  29. Zeng D.; Zhang Q.; Chen S.; Liu S.; Wang G. Synthesis porous carbon-based solid acid from rice husk for esterification of fatty acids. Microporous Mesoporous Mater. 2016, 219, 54–58. 10.1016/j.micromeso.2015.07.028. [DOI] [Google Scholar]
  30. Wang H. H.; Liu L. J.; Gong S. W. Esterification of oleic acid to biodiesel over a 12-phosphotungstic acid-based solid catalyst. J. Fuel Chem. Technol. 2017, 45, 303–310. 10.1016/S1872-5813(17)30018-X. [DOI] [Google Scholar]
  31. Liu H.; Yang J.; Hua Z.; Zhang Y.; Yang L.; Xiao L.; Xie Z. The structure and magnetic properties of Cu-doped ZnO prepared by sol–gel method. Appl. Surf. Sci. 2010, 256, 4162–4165. 10.1016/j.apsusc.2010.01.118. [DOI] [Google Scholar]
  32. Zhu J.; Gan L.; Li B.; Yang X. Synthesis and characteristics of lignin-derived solid acid catalysts for microcrystalline cellulose hydrolysis. Korean J. Chem. Eng. 2017, 34, 110–117. 10.1007/s11814-016-0220-5. [DOI] [Google Scholar]
  33. Aronne A.; Di Serio M.; Vitiello R.; Clayden N. J.; Minieri L.; Imparato C.; Piccolo A.; Pernice P.; Carniti P.; Gervasini A. An Environmentally Friendly Nb–P–Si Solid Catalyst for Acid-Demanding Reactions. J. Phys. Chem. C 2017, 121, 17378–17389. 10.1021/acs.jpcc.7b05886. [DOI] [Google Scholar]
  34. Flores K. P.; Omega J. L. O.; Cabatingan L. K.; Go A. W.; Agapay R. C.; Ju Y. H. Simultaneously carbonized and sulfonated sugarcane bagasse as solid acid catalyst for the esterification of oleic acid with methanol. Renewable Energy 2019, 130, 510–523. 10.1016/j.renene.2018.06.093. [DOI] [Google Scholar]
  35. Huang X.; Li Y.; Li Y.; Zhou H.; Duan X.; Huang Y. Synthesis of PtPd Bimetal Nanocrystals with Controllable Shape, Composition, and Their Tunable Catalytic Properties. Nano Lett. 2012, 12, 4265–4270. 10.1021/nl301931m. [DOI] [PubMed] [Google Scholar]

Articles from ACS Omega are provided here courtesy of American Chemical Society

RESOURCES