Abstract
The coupling between spin, charge, and lattice degrees of freedom plays an important role in a wide range of fundamental phenomena. Monolayer semiconducting transitional metal dichalcogenides have emerged as an outstanding platform for studying these coupling effects. Here, we report the observation of multiple valley phonons – phonons with momentum vectors pointing to the corners of the hexagonal Brillouin zone – and the resulting exciton complexes in the monolayer semiconductor WSe2. We find that these valley phonons lead to efficient intervalley scattering of quasi particles in both exciton formation and relaxation. This leads to a series of photoluminescence peaks as valley phonon replicas of dark trions. Using identified valley phonons, we also uncover an intervalley exciton near charge neutrality. Our work not only identifies a number of previously unknown 2D excitonic species, but also shows that monolayer WSe2 is a prime candidate for studying interactions between spin, pseudospin, and zone-edge phonons.
Subject terms: Two-dimensional materials, Two-dimensional materials
In monolayer semiconductors phonons with momentum vectors pointing to the corners of the hexagonal Brillouin zone couple strongly to carriers’ spin and valley degree of freedom. Here, the authors report the observation of multiple valley phonons and the resulting exciton complexes in the monolayer semiconductor WSe2.
Introduction
Electron–phonon interaction is a ubiquitous process in solids. In monolayer semiconducting transition metal dichalcogenides (TMDs), the broken inversion symmetry and strong spin–orbit coupling leads to the well-known spin–valley coupling of band edge electrons1–6. The emergent valley-contrasting properties not only impact quasiparticles, but also are expected to give rise to new physics involving zone edge phonons, or valley phonons, which are collective lattice oscillations at the corners of hexagonal Brillouin zone (±K points). These phonons have been predicted to play an important role in spin and valley pseudospin relaxation through phonon-assisted intervalley scattering7,8. Additionally, valley phonons can possess chirality with intrinsic pseudo-angular momentum9, which has recently attracted wide attention10–13. Such chiral phonons have nontrivial Berry curvature and are predicted to give rise to valley phonon Hall effect, a counterpart of valley Hall effect of electrons in 2D semiconductors14–16. Despite the importance of valley phonons, experimental progress in understanding their properties has been limited, since it is challenging to probe phonons with large momentum vectors.
Here, we identify the signatures of multiple valley phonons in monolayer WSe2. The monolayer WSe2 hosts stable and long-lived dark exciton and trion as ground states17–22. The resulting accumulated exciton and trion populations are highly desirable for studying their interactions with phonons. We found that three valley phonons facilitate efficient spin-conserving intervalley scattering, which results in a series of dark exciton and dark trion phonon-replicas in the low-temperature photoluminescence (PL) spectrum. The sign and magnitude of Landé effective g-factors of the various replicas, together with their PL helicity under optical pumping, reveals that the spin-preserving intervalley scattering of the electron is more efficient than its intravalley spin-flip during the dark exciton/trion formation process. This results in a surprising finding: the single electron in both the positive dark trion and intervalley exciton resides in the valley opposite to that which the optical pump is coupled to. Moreover, the identified intervalley exciton resonance enables us to infer a short-range electron–hole exchange interaction of ~10 meV by extracting the energy splitting between intervalley and dark (intravalley) excitons.
Results
Gate-dependent PL spectrum of monolayer WSe2
The samples are exfoliated monolayer WSe2 encapsulated between thin flakes of hexagonal boron nitride (hBN). Few-layered graphene serves as a local bottom gate for electrostatic control of the monolayer carrier density (see the “Methods” section). Figure 1a, b are an optical microscope image and schematic of a representative device, respectively. Figure 1c shows the PL intensity plot as a function of gate voltage (V) and photon energy, at a temperature of 1.6 K. The laser energy is 1.775 eV with right circularly polarized (σ+) excitation and unpolarized detection. The full helicity-resolved gate-dependent spectra are shown in Supplementary Fig. 1. Monolayer WSe2 hosts a rich spectrum of excitonic species23–28. Several previously identified excitonic states are indicated in the figure, including the neutral bright exciton, bright trions29–33, the intravalley spin-forbidden dark exciton17–20,34 and dark trions18,35. The recently identified zone-center Γ5—or E''—phonon replicas below both neutral12,13 and charged dark excitons12 are also resolved, as indicated by black arrows.
The focus of this paper is to understand the valley phonon origin of several previously unidentified PL peaks. In particular, we focus on the triplet and quadruplet PL peaks outlined by dashed black boxes, and those pointed at by the white arrows in Fig. 1c. We have measured multiple samples that exhibit similar spectrum (Supplementary Fig. 2), and the nearly identical power dependence of the peaks of interest across several samples rules out the possibility of them arising due to defect states (Supplementary Fig. 3). As we explain below, all these peaks arise from the coupling of optically dark states to the bright ones via emitting valley phonons, which results in a series Stokes-shifted valley phonon-replicas of the dark exciton and dark trions in the PL spectrum.
Valley phonon replicas of positively charged dark trion
We first consider the quadruplet PL peaks in the hole doping regime. Figure 2a shows the circular polarization resolved PL with σ+ polarized excitation. The photon energy is relative to the positive dark trion (D+), and the intensity of the quadruplets is multiplied by a factor of 4 to emphasize these weak spectral features. We ascribe the four peaks to bright replicas of the dark trion, mediated by interactions with phonons. The quadruplets are labeled as , , , , which correspond to their origin from coupling of D+ with valley phonons K3, K1, and K2, and the zone-center phonon Γ5. This nomenclature has its origin in the Koster notation of the K-point irreducible representations of the C3h point double-group corresponding to the symmetry of the monolayer semiconductors (Supplementary Table 3, character table).
The valley phonon replicas are 26, 18, and 13 meV below D+, respectively. The association with zone-edge phonons K3, K1, and K2 is two-fold. The first reason is that the energy differences between D+ and its replicas match the energies of the associated phonon modes (Supplementary Fig. 5, phonon spectrum). The second reason is rooted in the selection rules of electron–phonon coupling;7 intervalley transitions of electrons and holes are mediated only by specific phonons (see discussions in Supplementary Notes 3 and 4). Finally, we note that appears 22 meV below D+, which is consistent with the recently reported Γ5 phonon replica of D+12.
To further examine these assignments, we performed magneto-PL to extract the effective Landé g-factors of the various states, which are then used to identify the spin and valley indices of the constituent electrons and holes in the excitonic states36–40. The extracted g-factors of the states of interest are listed in Table 1. The g-factors of other states are listed in Supplementary Table 1, and a detailed analysis can be found in Supplementary Note 2. Briefly, for intravalley electron–hole recombination, the magnitude of the g-factor is about 4 for parallel electron and hole spins36,37,39,40, and about 9 when the two spins are anti-parallel12,13,21. Meanwhile, if the recombination involves electron and hole from opposite valleys but with parallel spins, a value about 13 is expected.
Table 1.
Dark state | K2 replica | K1 replica | Γ5 replica | K3 replica | |
---|---|---|---|---|---|
Neutral regime: I0 | −12.5 | – | 12.0 | – | −12.6 |
Neutral regime: D0 | −9.1 | – | – | −9.8 | – |
Hole doped: D+ | −8.6 | −13.0 | 12.2 | −9.7 | −13.4 |
Electron doped: D− | −9.5 | −13.6 | 12.2 | −9.9 | −12.5 |
Figure 2b shows the circular polarization resolved PL intensity as a function of out-of-plane magnetic field. The energy scale is relative to the position of D+ at zero applied magnetic field. Both the cross pattern of D+ in Fig. 2b and its unpolarized light emission (see Fig. 2a) result from the underlying out-of-plane dipole orientation12, and are hallmarks of direct intravalley recombination of dark trions. Following the convention of valley Zeeman splitting as Δ = E(σ+)−E(σ−), where E(σ+) and E(σ−) are the peak energies of the σ+ and σ− polarized PL components, we obtained g(D+) = −8.6. The obtained g-factor of D+ is therefore consistent with expectations for the direct recombination through the intravalley spin–flip transition.
The Zeeman shifts of the quadruplet PL peaks underpin their origin as phonon replicas of the dark positive trion D+. The extracted g-factors of −13.4, 12.2, and −13.0 for , , , respectively, are consistent with intervalley recombination of electron and hole. Note that the g factor sign of is opposite to others, which will be discussed later. While the intervalley recombination is naturally forbidden for delocalized exciton complexes, because of the large momentum mismatch, emission of a valley phonon can supply the required momentum, resulting in phonon-assisted luminescence of the otherwise dark states. Combined with the concurrence of similar valley phonon energies and energy difference between the peaks and , we conclude that , , are K3, K1, and K2 valley phonon replicas of D+.
The polarization of the peak highlights the importance of valley phonons in the formation process of D+. From Fig. 2a, we observe that is cross-circularly polarized. The valley optical selection rules dictate that σ+ excitation creates an electron and hole in the +K valley, while σ− polarized emission can only happen through spin-conserved electron–hole recombination in the −K valley. In addition, = −9.7 indicates the intravalley electron–hole recombination nature of the peak. The cross-polarized emission of therefore leads to the surprising conclusion that σ+ excitation results in D+ with the single electron located in the −K valley: i.e. D+(−K).
The cross polarization of D+ can be understood by considering the impact of phonons on the electron relaxation pathways following photoexcitation. The D+ population is created by optical pumping of the spin-conserved interband transition (Fig. 2c), followed by the relaxation of the electron from the higher energy spin-valley locked sub-band to the lower energy one. The latter step requires either a spin–flip or a valley–flip. From symmetry analysis, the Γ5 phonon can lead to the intravalley spin–flip relaxation of electron from upper to lower conduction band7, but it cannot cause intervalley scattering. On the other hand, spin-conserving intervalley scattering of the electron with K3 phonon is a symmetry-allowed zeroth-order channel8. Figure 2c illustrates the intervalley electron–phonon relaxation process that leads to the formation of D+ (−K). First, σ+ excitation creates electron in the spin up conduction band in the K valley. Assisted by the K3 valley phonon (Fig. 2d), this spin up electron is then scattered into the spin up band in the −K valley, forming D+(−K) with two holes separately located at the top of ±K valleys. D+(−K) then couples to σ− polarized photon by emitting Γ5 phonon, as shown in Fig. 2e. Evidently, the observed cross-polarized emission implies that the valley–flip rate exceeds the spin–flip one in the relaxation of electron.
Having established that σ+ polarized excitation results in D+(−K), the understanding of both and is straightforward. As indicated in Fig. 2f, the spin up electron in the lower −K sub-band is virtually scattered to the higher +K sub-band by emitting either a K3 or K2 valley phonon (see Supplementary Note 5 for further analysis of K2). The spin-conserving intervalley scatter then allows for recombination with the hole in the +K valley, emitting σ+ polarized photon with energy either 26 meV (K3) or 13 meV (K2) below D+. The g-factors of and are nearly equal, about −13.4 and −13.0, respectively, and correspond to expected values for the intervalley spin-conserving electron–hole recombination.
Moreover, the measured amplitude of , which is several times stronger than that of , is also consistent with group-theory selection rules. In particular, the selection rules dictate that, in pristine monolayer WSe2, only the K3 phonon mode can induce intervalley electron transitions between conduction band edges at the high symmetry K and −K points7. Meanwhile, intervalley electron transitions that are mediated by other K-point phonon modes are higher-order processes with correspondingly smaller amplitudes that involve electron states in the neighborhood of ±K. Such relatively weak processes can be amplified by several possible sources, such as localization next to defects, breaking WSe2 mirror inversion symmetry by hBN encapsulation, or WSe2/hBN moire superlattice providing in plane momentum.
The positive g-factor of is a signature of the interaction of the hole and K1 valley phonon. According to the group-theory selection rules, K1 is the only phonon mode that enables the spin-conserving intervalley transition between valence-band states at K and −K points (i.e., it is a zeroth-order process)7. As shown in Fig. 2g, the hole in the higher valence band of K valley is virtually scattered to the lower valence band of the −K valley with the same spin orientation via emission of a K1 valley phonon, forming an intermediate virtual B trion. The recombination of the electron with this scattered hole in the −K valley results in , with energy 18 meV below D+. While the initial and final states have the same spin-valley configuration as in and , the emission from is σ− polarized. Therefore, the g-factor of is expected to have similar magnitude, but opposite sign, compared to the g-factors of and , as we have observed. Note that although the interaction between the hole and valley phonon K1 is relatively strong, the coupling of D+(−K) (or A trion) with the virtual B trion state is ~400 meV detuned, which is much larger than in the case of K3 intervalley electron scattering. Therefore, the PL intensity of is expected to be several times weaker than that of , which is in agreement with our observation (see Supplementary Note 4).
Valley phonon replicas of negatively charged dark trion
The valley phonon replicas of the negative dark trion D− can be understood using similar analysis as above. Figure 3a shows the helicity-resolved PL under σ+ polarized excitation. The lower energy spectral features, denoted as T1, , and show appreciable co-circular polarization. Figure 3b shows the PL intensity as a function of magnetic field and photon energy, with σ−/σ− polarized excitation/detection (the σ+/σ+ results are shown in Supplementary Fig. 7). The extracted g-factor of is −12.5, indicating intervalley recombination, and the energy is 26 meV below D−. As such, we can identify that originates from the interaction of −K valley electron with K3 phonon, as depicted in the inset of Fig. 3a. The g-factor of (−9.9) is nearly the same as that of D− (−9.5), and as expected, the peak appears 22 meV below D−.
The observation of triplet peak pattern in the PL spectrum under electron doping is slightly different from the quadruplet one observed under hole doping. Since T1 is more intense than D−, and its g-factor is about −4.5, it is not likely to be a phonon replica of D−. Its origin is unknown, but T1 is near the spectral range of the K2 and K1 valley phonon replicas, and thus obscures them entirely. Nevertheless, the large difference in g-factor of T1 from that of D− allows us to identify in magneto-PL, since the states shift away from one another. We note that there is a faint line in Fig. 3b, appearing on the high energy shoulder of T1 at high magnetic field. We ascribe this peak to based on its g-factor of about −13.6, and its energy difference from D− of 13 meV, both of which are in good agreement with expectations for K2 phonon replica.
Meanwhile, becomes evident when the excitation laser is resonant with the bright neutral exciton (X0). Figure 3c presents the PL intensity as a function of gate voltage and photon energy, with σ+ polarized excitation laser in resonance with X0 (1.733 eV) and σ− polarized detection. For V = 0.2 V, arrow on side of Fig. 3c, becomes apparent at 18 meV below D−. Figure 3d shows magneto-PL with the same cross-polarized polarization (σ+/σ−) (see Supplementary Fig. 8 for complete data set). We find that has a positive g-factor of 12.2, which is identical to that of . Therefore, despite the initial appearance, the four phonon replica states observed under hole-doping also appear under electron-doping conditions. Moreover, we observe similar magnitude and sign of g-factors, as well as energy separation from the parent dark trion state.
Identification of intervalley dark excitons and its valley phonon replica
The valley phonon-assisted momentum relaxation mechanism also produces phonon replicas for neutral dark excitons. Figure 4a shows the helicity-resolved PL spectra near charge neutrality (V = −0.2 V). The energy axis is offset from I0, which is the sharp line 32 meV below the bright neutral exciton in Fig. 1c. We also observe strong direct recombination from the neutral intravalley dark exciton D0, at 42 meV below X0. We confirm that D0 has negligible circular polarization, resulting from its out-of-plane dipole orientation, and the extracted g-factor (−9.1) is in good agreement with previously reported values12,13,21. Magneto-PL measurements with linear excitation (V) and σ+/σ− collection are shown in the top/bottom panel of Fig. 4b, respectively. The observed PL peak at 22 meV below D0, with a g-factor of −9.8 is consistent with the reported Γ5 phonon replica 12,13. We further note that shows a zero-field splitting of 0.6 meV, which arises from the fine structure of D0 (Supplementary Fig. 9)8,21. We note that there are two replicas of D0 that are apparent in the magneto-PL (cross-patterns at 3 and 13 meV below D0). The peak position of the latter one matches that of positive dark trion thus is precursor of D+, while the former one cannot be unambiguously identified at this time.
The I0 emission is distinct from that of D0 and exhibits all the expected behavior of the momentum indirect, or intervalley dark exciton, which has not been previously identified in this system. This emission peak is strongly co-circularly polarized, with near unity polarization. Its g-factor of about −12.5 corresponds to the recombination of electron and hole residing in opposite valleys, implying that I0 is the direct recombination of intervalley exciton. The formation of I0 is a consequence of the fast valley-flip of electrons via scattering with K3 phonon in the dark exciton formation, as illustrated in Fig. 4c. This is consistent with formation of D+(−K) discussed above (Fig. 2c). The 10 meV energy splitting between D0 and I0 is then a direct measure of the short-range electron–hole exchange interactions41. We note that the direct photon emission from the momentum indirect I0 is weak in intensity, even when compared to the spin-forbidden dark state D0. However, weak PL from indirect states is not unprecedented. Similar to the case of indirect band-gap semiconductors such as silicon, recombination of intervalley excitons without phonons can be mediated by localization next to defects42, which alleviates the need to conserve crystal momentum due to translation symmetry.
The assignment of I0 is corroborated by the identifications of its K1 and K3 phonon replicas, made evident by examining the energy, polarization, and g-factors of the spectral features. The feature indicated as in Fig. 4a, is located 18 meV below I0, is cross-circularly polarized, and has a positive g-factor of 12.0. These values are nearly identical to those found for both and , and consistent with expectations for the K1 valley phonon replica of I0. The recombination process via intervalley hole scattering is illustrated in Fig. 4d. In addition, the peak is about 26 meV below I0 and has a g-factor of −12.6, which is the same as I0 and supports its origin as K3 valley phonon replica of I0 (Fig. 4e).
Discussion
In conclusion, we unravel the role of valley phonons in exciton and trion formation and their recombination in semiconducting monolayer WSe2. Our work settles questions of the origin of nearly all of the observed peaks in the complex excitonic spectrum of monolayer WSe2. Another important result is that the relaxation of optically generated electrons from the upper conduction band to the lower conduction band is dominated by K3 phonon-assisted spin-conserving intervalley scattering, rather than the Γ5 phonon-assisted spin–flip intravalley scattering. Such a relaxation pathway gives rise to the unexpected initial state for the positively charged dark trion, and efficient formation of intervalley exciton I0. This understanding is important for correct interpretation of excitonic spectral features, and may allow for new schemes to control the electron/exciton spin-valley state via optical pumping, e.g. coherent control of D0 and I0 populations via stimulated Raman adiabatic passage. Our work further motivates detailed studies of the electron-valley phonon coupling matrix elements by the first principle calculations, which should provide insights for theoretical models to gain a complete understanding of the complex monolayer WSe2 spectrum.
Methods
Sample fabrication
Monolayers of WSe2 were mechanically exfoliated from bulk crystals and identified by optical contrast, which was later confirmed by their low-temperature PL spectrum. Thickness of hBN flakes used for encapsulation was typically 10–20 nm, while the thickness of graphite back gate electrodes was typically around 5 nm. Heterostructures of hBN/WSe2/hBN/Graphite are made with dry-transfer technique using polycarbonate films43. The surface of every flake in the heterostructure was confirmed clean with atomic force microscopy prior to fabrication. Finally, the V/Au contact are patterned with standard electron beam lithography and evaporation.
PL spectroscopy
PL measurements were performed with a confocal microscope in reflection geometry, with sample mounted in an exchange gas cooled cryostat (AttoDry 2100). The cryostat is equipped with a superconducting magnet in Faraday geometry (magnetic field B perpendicular to sample plane). All measurements were performed at 1.6 K unless otherwise specified. A He–Ne laser (632.8 nm) or a frequency tunable continuous-wave Ti:sapphire laser were used to excite the sample. Polarization resolved PL measurements were performed with a set of broad-band half-wave plates, quarter wave plates and linear polarizers. PL signal was collected by a spectrometer with a silicon charge-coupled device.
Supplementary information
Acknowledgements
This work was mainly supported by the Department of Energy, Basic Energy Sciences, Materials Sciences and Engineering Division (DE-SC0018171). Part of understanding of the valley phonon physics is supported by DoE BES DE-SC0014349. Device fabrication and part of magneto optical spectroscopy work are supported by Army Research Office (ARO) Multidisciplinary University Research Initiative (MURI) program, Grant no. W911NF-18-1-0431and NSF MRSEC 1719797. W.Y. and H.Y. were supported by Research Grants Council of Hong Kong (17312916), and Seed Funding for Strategic Interdisciplinary Research Scheme of HKU. D.G.M. and J.Y. were supported by the US Department of Energy, Office of Science, Basic Energy Sciences, Materials Sciences and Engineering Division. K.W. and T.T. were supported by the Elemental Strategy Initiative conducted by the MEXT, Japan and and the CREST (JPMJCR15F3), JST. X.X. acknowledges the support from the State of Washington funded Clean Energy Institute and from the Boeing Distinguished Professorship in Physics.
Author contributions
M.H. and P.R. fabricated the devices and performed the measurements, assisted by N.P.W. and supervised by X.X. and W.Y. H.D., W.Y., D.V.T., M.Y., H.Y., M.H., P.R. and X.X. analyzed and interpreted the results. J.Y. and D.G.M. synthesized and characterized the bulk WSe2 crystals. K.W. and T.T. provided the bulk hBN crystals. M.H., P.R., X.X., H.D. and W.Y. wrote the paper with inputs from all authors. All authors discussed the results.
Data availability
The data that support the findings of this study are available from the corresponding authors upon reasonable request.
Competing interests
The authors declare no competing interests.
Footnotes
Peer review information Nature Communications thanks the anonymous reviewer(s) for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
These authors contributed equally: Minhao He, Pasqual Rivera.
Contributor Information
Hanan Dery, Email: hanan.dery@rochester.edu.
Wang Yao, Email: wangyao@hku.hk.
Xiaodong Xu, Email: xuxd@uw.edu.
Supplementary information
Supplementary information is available for this paper at 10.1038/s41467-020-14472-0.
References
- 1.Xu XD, Yao W, Xiao D, Heinz TF. Spin and pseudospins in layered transition metal dichalcogenides. Nat. Phys. 2014;10:343–350. doi: 10.1038/nphys2942. [DOI] [Google Scholar]
- 2.Xiao D, Liu G-B, Feng W, Xu X, Yao W. Coupled spin and valley physics in monolayers of MoS2 and other group-VI dichalcogenides. Phys. Rev. Lett. 2012;108:196802. doi: 10.1103/PhysRevLett.108.196802. [DOI] [PubMed] [Google Scholar]
- 3.Wang G, et al. Colloquium: excitons in atomically thin transition metal dichalcogenides. Rev. Mod. Phys. 2018;90:021001. doi: 10.1103/RevModPhys.90.021001. [DOI] [Google Scholar]
- 4.Mak KF, Xiao D, Shan J. Light–valley interactions in 2D semiconductors. Nat. Photon. 2018;12:451–460. doi: 10.1038/s41566-018-0204-6. [DOI] [Google Scholar]
- 5.Cao T, et al. Valley-selective circular dichroism of monolayer molybdenum disulphide. Nat. Commun. 2012;3:887. doi: 10.1038/ncomms1882. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 6.Manzeli S, Ovchinnikov D, Pasquier D, Yazyev OV, Kis A. 2D transition metal dichalcogenides. Nat. Rev. Mater. 2017;2:17033. doi: 10.1038/natrevmats.2017.33. [DOI] [Google Scholar]
- 7.Song Y, Dery H. Transport theory of monolayer transition-metal dichalcogenides through symmetry. Phys. Rev. Lett. 2013;111:026601. doi: 10.1103/PhysRevLett.111.026601. [DOI] [PubMed] [Google Scholar]
- 8.Dery H, Song Y. Polarization analysis of excitons in monolayer and bilayer transition-metal dichalcogenides. Phys. Rev. B. 2015;92:125431. doi: 10.1103/PhysRevB.92.125431. [DOI] [Google Scholar]
- 9.Zhang L, Niu Q. Chiral phonons at high-symmetry points in monolayer hexagonal lattices. Phys. Rev. Lett. 2015;115:115502. doi: 10.1103/PhysRevLett.115.115502. [DOI] [PubMed] [Google Scholar]
- 10.Zhu H, et al. Observation of chiral phonons. Science. 2018;359:579–582. doi: 10.1126/science.aar2711. [DOI] [PubMed] [Google Scholar]
- 11.Chen X, et al. Entanglement of single-photons and chiral phonons in atomically thin WSe2. Nat. Phys. 2019;15:221–227. doi: 10.1038/s41567-018-0366-7. [DOI] [Google Scholar]
- 12.Liu, E. et al. Valley-selective chiral phonon replicas of dark excitons and trions in monolayer WSe2. Phys. Rev. Research 1, 032007(R) (2019).
- 13.Li Z, et al. Emerging photoluminescence from the dark-exciton phonon replica in monolayer WSe2. Nat. Commun. 2019;10:2469. doi: 10.1038/s41467-019-10477-6. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 14.Xiao D, Yao W, Niu Q. Valley-contrasting physics in graphene: magnetic moment and topological transport. Phys. Rev. Lett. 2007;99:236809. doi: 10.1103/PhysRevLett.99.236809. [DOI] [PubMed] [Google Scholar]
- 15.Mak KF, McGill KL, Park J, McEuen PL. The valley Hall effect in MoS2 transistors. Science. 2014;344:1489–1492. doi: 10.1126/science.1250140. [DOI] [PubMed] [Google Scholar]
- 16.Gorbachev RV, et al. Detecting topological currents in graphene superlattices. Science. 2014;346:448–451. doi: 10.1126/science.1254966. [DOI] [PubMed] [Google Scholar]
- 17.Zhang X-X, You Y, Zhao SYF, Heinz TF. Experimental evidence for dark excitons in monolayer WSe2. Phys. Rev. Lett. 2015;115:257403. doi: 10.1103/PhysRevLett.115.257403. [DOI] [PubMed] [Google Scholar]
- 18.Zhang X-X, et al. Magnetic brightening and control of dark excitons in monolayer WSe2. Nat. Nanotech. 2017;12:883. doi: 10.1038/nnano.2017.105. [DOI] [PubMed] [Google Scholar]
- 19.Zhou Y, et al. Probing dark excitons in atomically thin semiconductors via near-field coupling to surface plasmon polaritons. Nat. Nanotech. 2017;12:856. doi: 10.1038/nnano.2017.106. [DOI] [PubMed] [Google Scholar]
- 20.Wang G, et al. In-plane propagation of light in transition metal dichalcogenide monolayers: optical selection rules. Phys. Rev. Lett. 2017;119:047401. doi: 10.1103/PhysRevLett.119.047401. [DOI] [PubMed] [Google Scholar]
- 21.Robert C, et al. Fine structure and lifetime of dark excitons in transition metal dichalcogenide monolayers. Phys. Rev. B. 2017;96:155423. doi: 10.1103/PhysRevB.96.155423. [DOI] [Google Scholar]
- 22.Tang, Y., Mak, K. F. & Shan, J. Long valley lifetime of dark excitons in single-layer WSe2. Nat. Commun. 10, 4047 (2019). [DOI] [PMC free article] [PubMed]
- 23.You Y, et al. Observation of biexcitons in monolayer WSe2. Nat. Phys. 2015;11:477. doi: 10.1038/nphys3324. [DOI] [Google Scholar]
- 24.Stier AV, et al. Magnetooptics of exciton Rydberg states in a monolayer semiconductor. Phys. Rev. Lett. 2018;120:057405. doi: 10.1103/PhysRevLett.120.057405. [DOI] [PubMed] [Google Scholar]
- 25.Barbone M, et al. Charge-tuneable biexciton complexes in monolayer WSe2. Nat. Commun. 2018;9:3721. doi: 10.1038/s41467-018-05632-4. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 26.Li Z, et al. Revealing the biexciton and trion–exciton complexes in BN encapsulated WSe2. Nat. Commun. 2018;9:3719. doi: 10.1038/s41467-018-05863-5. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 27.Chen S-Y, Goldstein T, Taniguchi T, Watanabe K, Yan J. Coulomb-bound four- and five-particle intervalley states in an atomically-thin semiconductor. Nat. Commun. 2018;9:3717. doi: 10.1038/s41467-018-05558-x. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 28.Ye Z, et al. Efficient generation of neutral and charged biexcitons in encapsulated WSe2 monolayers. Nat. Commun. 2018;9:3718. doi: 10.1038/s41467-018-05917-8. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 29.Jones AM, et al. Optical generation of excitonic valley coherence in monolayer WSe2. Nat. Nanotech. 2013;8:634–638. doi: 10.1038/nnano.2013.151. [DOI] [PubMed] [Google Scholar]
- 30.He K, et al. Tightly bound excitons in monolayer WSe2. Phys. Rev. Lett. 2014;113:026803. doi: 10.1103/PhysRevLett.113.026803. [DOI] [PubMed] [Google Scholar]
- 31.Ross JS, et al. Electrically tunable excitonic light-emitting diodes based on monolayer WSe2 p–n junctions. Nat. Nanotech. 2014;9:268. doi: 10.1038/nnano.2014.26. [DOI] [PubMed] [Google Scholar]
- 32.Splendiani A, et al. Emerging photoluminescence in monolayer MoS2. Nano Lett. 2010;10:1271–1275. doi: 10.1021/nl903868w. [DOI] [PubMed] [Google Scholar]
- 33.Mak KF, Lee C, Hone J, Shan J, Heinz TF. Atomically thin MoS2: a new direct-gap semiconductor. Phys. Rev. Lett. 2010;105:136805. doi: 10.1103/PhysRevLett.105.136805. [DOI] [PubMed] [Google Scholar]
- 34.Park K-D, Jiang T, Clark G, Xu X, Raschke MB. Radiative control of dark excitons at room temperature by nano-optical antenna-tip Purcell effect. Nat. Nanotech. 2018;13:59–64. doi: 10.1038/s41565-017-0003-0. [DOI] [PubMed] [Google Scholar]
- 35.Liu E, et al. Gate tunable dark trions in monolayer WSe2. Phys. Rev. Lett. 2019;123:027401. doi: 10.1103/PhysRevLett.123.027401. [DOI] [PubMed] [Google Scholar]
- 36.Aivazian G, et al. Magnetic control of valley pseudospin in monolayer WSe2. Nat. Phys. 2015;11:148. doi: 10.1038/nphys3201. [DOI] [Google Scholar]
- 37.Srivastava A, et al. Valley Zeeman effect in elementary optical excitations of monolayer WSe2. Nat. Phys. 2015;11:141. doi: 10.1038/nphys3203. [DOI] [Google Scholar]
- 38.Lyons TP, et al. The valley Zeeman effect in inter- and intra-valley trions in monolayer WSe2. Nat. Commun. 2019;10:2330. doi: 10.1038/s41467-019-10228-7. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 39.Li Y, et al. Valley splitting and polarization by the Zeeman effect in monolayer MoSe2. Phys. Rev. Lett. 2014;113:266804. doi: 10.1103/PhysRevLett.113.266804. [DOI] [PubMed] [Google Scholar]
- 40.MacNeill D, et al. Breaking of valley degeneracy by magnetic field in monolayer MoSe2. Phys. Rev. Lett. 2015;114:037401. doi: 10.1103/PhysRevLett.114.037401. [DOI] [PubMed] [Google Scholar]
- 41.Yu H, Liu G-B, Gong P, Xu X, Yao W. Dirac cones and Dirac saddle points of bright excitons in monolayer transition metal dichalcogenides. Nat. Commun. 2014;5:3876. doi: 10.1038/ncomms4876. [DOI] [PubMed] [Google Scholar]
- 42.Karaiskaj D, et al. Photoluminescence of isotopically purified silicon: how sharp are bound exciton transitions? Phys. Rev. Lett. 2001;86:6010–6013. doi: 10.1103/PhysRevLett.86.6010. [DOI] [PubMed] [Google Scholar]
- 43.Wang L, et al. One-dimensional electrical contact to a two-dimensional material. Science. 2013;342:614–617. doi: 10.1126/science.1244358. [DOI] [PubMed] [Google Scholar]
Associated Data
This section collects any data citations, data availability statements, or supplementary materials included in this article.
Supplementary Materials
Data Availability Statement
The data that support the findings of this study are available from the corresponding authors upon reasonable request.