Abstract
Graphene/hBN heterostructures are promising active materials for devices in the THz domain, such as emitters and photodetectors based on interband transitions. Their performance requires long carrier lifetimes. However, carrier recombination processes in graphene possess sub-picosecond characteristic times for large non-equilibrium carrier densities at high energy. An additional channel has been recently demonstrated in graphene/hBN heterostructures by emission of hBN hyperbolic phonon polaritons (HPhP) with picosecond decay time. Here, we report on carrier lifetimes in graphene/hBN Zener-Klein transistors of ~30 ps for photoexcited carriers at low density and energy, using mid-infrared photoconductivity measurements. We further demonstrate the switching of carrier lifetime from ~30 ps (attributed to interband Auger) down to a few picoseconds upon ignition of HPhP relaxation at finite bias and/or with infrared excitation power. Our study opens interesting perspectives to exploit graphene/hBN heterostructures for THz lasing and highly sensitive THz photodetection as well as for phonon polariton optics.
Subject terms: Optical properties and devices; Electronics, photonics and device physics; Terahertz optics
Long carrier lifetimes are beneficial for graphene-based optoelectronics, but carrier recombination processes in graphene possess sub-picosecond characteristic times. Here, the authors report carrier lifetimes ~30 ps at low energy in graphene/hBN Zener-Klein transistors, attributed to interband Auger processes.
Introduction
Graphene/hBN heterostructures uniquely combine high-quality graphene owing to the use of encapsulating layers1 with the coupling of graphene carriers with the hyperbolic phonons in the hBN layers. Importantly, for applications they keep their valuable performance up to room temperature. Graphene/hBN heterostructures are very attractive for the development of interband semiconductor laser schemes at THz frequencies owing to the gap-less electronic band structure of graphene2,3 and the fine low-doping control. For the realization of a THz laser, carrier lifetimes of a few tens of picoseconds are needed to reach long-lived optical gain. In addition, sensitive THz photodetectors are achievable in graphene/hBN heterostructures owing to the high carrier mobility in encapsulated graphene and its broad absorption spectrum4,5. For a compromise between sensitivity and speed in such THz photoconductors, carrier lifetimes of a few tens of picoseconds are also required. More generally, the recombination dynamics of non-equilibrium carriers close to the Dirac point in the encapsulated graphene layer plays a crucial role in the performance of interband optoelectronic THz devices and recombination times of at least a few tens of picoseconds are often highly desirable5–8.
The recombination dynamics of non-equilibrium carriers in graphene has been widely investigated9–12. Mostly, femtosecond visible or near infrared pulses are used to generate hot non-equilibrium carriers of large density at high energies. After photoexcitation, the electron/hole populations are both redistributed (by energy-conserving intraband carrier–carrier scattering) and relaxed (by intraband electron–optical phonon scattering) within ∼50 fs. It results in two independent lower-energy broad electron and hole distributions, for which efficient interband Auger recombination processes leads to a single Fermi–Dirac distribution for conduction and valence populations within 100–200 fs. A subsequent cooling process occurs mediated by interband optical phonon emissions within 1–2 ps and by less efficient intraband acoustical phonon scattering10,13. Very recently, an additional recombination channel with picosecond decay time has been demonstrated in hBN encapsulated graphene relying on the coupling of hot carriers in graphene with hyperbolic phonon polaritons (HPhPs) in the hBN layers14,15. Few studies have used optical pump with energies lower than optical phonon energy and reported significant slowing of the carrier relaxation16. However, owing to the excitation of a large density of hot carriers, optical phonon emission remained the predominant relaxation channel11,17. In spite of intensive work, the investigation of recombination dynamic for carriers at low photon energy and fluence remains elusive in graphene, notably under dc bias control.
Here we use continuous mid-infrared laser excitation (ℏω = 117 meV) and set graphene at charge neutrality point (CNP) where transport is dominated by interband Zener tunneling18,19. This provides weak incident photon density and corresponds to a photon energy between the Fermi-level fluctuations (typically ~20 meV in graphene/hBN heterostructures) and the optical phonons of graphene and hBN (ℏΩ ≈ 170–200 meV). Focusing on this low-energy domain, we unveil on a strong photoconductive regime involving a remarkably long Auger recombination time (~30 ps) and a switching to a short HPhP emission time at a finite dc bias or mid-infrared optical power. It also allows to investigate the interplay between optical and electrical pumping.
Results
Graphene/hBN Zener–Klein phototransistor
We investigate a transistor (Fig. 1a) fabricated in an hBN-encapsulated exfoliated single-layer graphene (Fig. 1b). The hBN/graphene heterostructure, of dimensions L × W = 20 µm × 10.4 µm, is deposited on a Ni bottom gate electrode and equipped with Cr/Au edge contacts (see details in the ‘Methods’ section). The bottom hBN layer, of thickness 67 nm, limits electrostatic doping to the range ±0.15 × 1012 cm−2. The thickness of the Ni layer is set to 12 nm to be semi-transparent to mid-infrared light with a measured transmission of T = 10.9%. From low-bias resistance measurements at 4 K reported in Fig. 1d, we extract a carrier mobility of 3.2 m2/Vs, a residual carrier density of n0 = 4 × 1010 cm−2 ascribed to residual charge puddles due to disordered potential likely created by air gaps at the Ni–hBN interface, and a contact resistance Rc = 650 Ω. As discussed in Supplementary Note 1, the extraction of carrier mobility from gate-dependent resistance measurement is valid at energy close to the carrier photoexcitation energy of 58.5 meV since the fluctuations of the Fermi-level energy induced by residual carrier density are lower than = 23.3 meV20.
The dark-current bias characteristics were initially investigated. As discussed below, it is essential in this experiment to keep a low (constant) doping; to this end, we compensate for drain doping by a careful calibration of the gate voltage at the CNP as function of VDS (which follows VCNP = Const. + 0.56 VDS)19. The dark current, Idark, at the CNP and at 4 K follows a superlinear bias dependence (see Fig. 1c, black square symbols), as reported in earlier experiments18. The main contribution to the current in the graphene channel is ascribed to interband Zener–Klein tunneling. Indeed, Zener–Klein current, which is due to the tunneling of electron carriers from the valence to conduction bands19,21, follows a power law, with 1 < α ≤ 1.5 that fits well our data for α = 1.3 (red dashed curve in Fig. 1c). A low bias and a slight deviation are observed that we attribute to finite charge puddle doping. Note that the Zener–Klein tunneling current is equivalent to an electrical pumping of non-equilibrium electron–hole pairs within the energy window ε < ±20 meV, as measured by noise thermometry19. Our optoelectronic experiment, which combines dc electric field and mid-infrared excitation, uniquely benchmarks the electrical and optical pumping of hBN/graphene heterostructures and provides unique insight of their interplay.
Using carrier transport measurements under mid-infrared continuous light excitation (CO2 laser of wavelength λ = 10.6 µm, i.e. photon energy of 117 meV), we investigated the photoresponse of the graphene/hBN transistor at energies below the in-plane optical phonon energy branch (170–200 meV) of both graphene and hBN. The laser spot diameter is focused on the device with a waist of 21.2 µm quasi-matching the sample length. Figure 1e shows the spatial distribution of the photocurrent along the channel length at the CNP for (blue curve) and (black curve) with . At zero source-drain voltage, the photocurrent is antisymmetric with respect to the sample length with extrema in the immediate vicinity of the leads and a node at the center. It can be assigned to photocarriers generated at the contact junctions that are accelerated by built-in electric fields at the contact as a result of the work function mismatch between graphene and the contact metal. Indeed, the regions close to the metallic leads (over typically 1 µm) become photoactive owing to band-bending. Both photovoltaic and thermoelectric effects likely play role in this regime22. By contrast, the photocurrent at finite source-drain bias is symmetric with a maximum at the sample center. It has the same polarity as the dark current and its maximum value is seven times larger than the maxima in the unbiased condition. The spatial profile of the photocurrent is well described by the convolution of a constant photoresponse along the channel with the Gaussian profile of the laser beam (see Supplementary Note 2).
Let us discuss the competing mechanisms responsible for this photocurrent at finite source-drain bias in graphene5. When a source-drain bias is applied, the uniform doping can be rendered asymmetric with a gradually effective doping along the graphene channel leading to the existence of thermoelectric effects in graphene. However, since only a weak gradient of temperature is induced by the large laser spot, the photocurrent contribution due to thermoelectric effect is expected to be very weak and opposite in sign to the dark current. Similarly, bolometric current, which results in the transport change produced by heating associated with the incident electromagnetic radiation, shows a vanishing contribution at low electrostatic doping and is also opposite in sign to the dark current due to decreasing mobility with increasing temperature (Fig. 1f at |VGATE| > 0.24 V). As a result, the photoconductive effect, where photoexcited electrons and holes are accelerated in opposite directions by an electric field, dominates over alternative photocurrent mechanisms at the CNP and at finite source-drain bias. As mentioned above, the photocurrent that relies on photoconductive effect is strongly sensitive to electrostatic doping. This is illustrated in Fig. 1f, which shows the gate voltage dependence of the photocurrent for an illumination at the channel center. We show a sharp peak at charge neutrality (half-width ~33 meV), narrower than the resistance peak itself (Fig. 1d). This dominates the photoresponse in the full doping range, in particular the negative photothermal response at large doping. It constitutes the signal of interest of this work. Although observed in previous photo-transport experiments23–25, these were in a regime of high-photon energy (>0.7 eV).
In the following, we investigate successively three relevant photoconductive regimes: (i) the linear regime where both bias and optical power are low, (ii) the non-linear regimes where either power or bias exceed the linear photoconductive limit, and finally (iii) the full photoconductive response including all regimes.
Linear photoresponse
Figure 2a presents the photocurrent–bias characteristics at low-bias and low-incident mid-infrared power. The polarization of the incident light is linear, parallel to the graphene channel (and the dc electric field). It shows the linear dependence of the photocurrent with bias over a broad optical power range, as expected for a photoconduction process23. The photocurrent reaches the µA range. From these measurements and electrical characterization, we extract the photoexcited carrier density in this stationary regime at the CNP using JPC = with µ = 3.2 m2/V/s and . The photoexcited carrier density reported in Fig. 2b as a function of the incident optical power evolves from <0.1 × 109 to ~0.7 × 109 cm−2. Note that the photoinduced electron and hole densities given by are significantly higher than the thermal electron and hole densities (1.4 × 107 cm−2) in ideal intrinsic graphene at T = 4 K. However, it remains relatively weak compared to the residual carrier density. To attain insight into the efficiency of the recombination processes, we can estimate the photoexcited carrier recombination time from the photocarrier densities and light excitation conditions23. The carrier diffusion is disregarded since the illumination and electric field are nearly uniform and the diffusion time is in the nanosecond range, i.e. much longer than recombination times. From a rate-equation approach, it follows that the total number of photoexcited carriers, with average density , is given by , where α0 is the light absorption, Slaser the area of the laser spot, ℏω is the photon energy, τ is a phenomenological carrier lifetime, M is a carrier multiplication factor (resulting from impact ionization effect that can lead to the creation of additional carriers contributing to the photocurrent26) and Po the laser power incident on the sample. Po is lower than the incident optical power Pinc by a factor 0.63 due the larger size of the optical Gaussian beam with respect to the sample dimension. The light absorption α0 by the graphene layer is calculated using the transfer matrix method considering the layered geometry of our device (the hBN dielectric film of ~67 nm thickness and the Ni back gate of 12 nm thickness). We calculate the ratio of the electric fields at the graphene plane Et and of the incident light E0 (see Supplementary Note 3). Then the graphene absorption is given by α0 = A(Et/E0)2 = 0.11% where A = 2.3% is the interband absorption in free space of monolayer graphene (in the absence of Pauli blocking at the CNP). We verify that the transmitted light through the device and the semi-transparent Ni electrode is proportional to the incident optical power, indicating no absorption saturation effect. In our experimental conditions, M is predicted to be close to unity. Indeed Jago et al. have calculated that M is typically <1.2 when photocarriers, with initial energy of 0.65 eV, evolve in a dc electric field27. Moreover, Tomadin et al. have predicted that M tends to unity when pump photon energy is lowered below 0.5 eV in undoped graphene sample28. Figure 2b shows the carrier recombination time (denoted carrier lifetime) extracted from this analysis, assuming negligible carrier multiplication effect (M = 1). We report on an unprecedented carrier lifetime of >30 ps (~35 ps in Fig. 2b), at low incident optical power and low bias, which is the main result of our work. This value is consistent with the slowing down of relaxation processes observed for low-energy carriers in graphene using pump–probe experiments, attributed to inefficient scattering via optical phonon emission11,29. In contrast to pump–probe experiments, which directly measure the dynamics of photoexcited carriers but with no direct distinction between relaxation and recombination processes, our experiment provides an estimation but singles out the recombination times of the photoexcited carriers. Indeed, only interband processes where electron and hole recombine are involved in the carrier lifetime τ since the intraband processes that relax the photocarriers within their respective band do not suppress the photocurrent.
Note that the carrier recombination times reported in Fig. 2b are underestimated if inhomogeneities of the Fermi level within the sample area due to charge puddles are considered since Pauli blocking reduces the effective absorbing area. Further, even if some carriers in the puddle region are taken into account in the calculation, the carrier lifetime still remains underestimated, as the mobility in the puddle region is lower than that in the linear region30.
This raises the question of the physical mechanism responsible for this very slow recombination of the photoexcited carriers. Recombination mechanisms of hot carriers in graphene usually involve the interplay between carrier–carrier and carrier–phonon scatterings. However, in this regime of low power, low bias and low temperature, scatterings via optical phonon in graphene and via coupling with hyperbolic phonon in hBN are strongly suppressed by Pauli blocking, as ℏω is well below their energy band 170–200 meV. With ℏω = 117 meV, one cannot rule out scattering by the lower 95–100 meV HPhP branch, a mechanism which is expected to be weak31. Acoustic phonon scattering cannot cause recombination because energy and momentum would not be conserved for interband transitions32. Indeed, the acoustic phonon mode, having an energy ωq = csq with cs smaller than the graphene band velocity vF, does not provide a possible channel for interband transitions, which requires an energy greater than vFq. Emission of acoustic phonons is therefore only possible through intraband transitions33. The momentum mismatch issue can be circumvented by impurity-assisted phonon supercollisions34,35; however, this mechanism is suppressed in high-mobility graphene. Radiative emission is very slow in graphene, typically at nanosecond timescale36. Consequently, at low-bias and low-photoexcited carrier density, interband Coulomb scattering (Auger recombination) is expected to be the remaining scattering mechanism involved in the recombination of non-equilibrium carriers (i.e. photoinduced carriers in excess to the dark ones) in hBN/graphene/hBN transistors (see Fig. 2e). It is consistent with previous theoretical works predicting that interband Coulomb scattering times for carriers close to the Dirac point in graphene fall within the few to few tens of picoseconds range36,37. We attribute the independence of the carrier lifetime to the incident optical power observed in Fig. 2b to Auger recombination processes assisted by the large density of charges (Zener–Klein and residual carriers), which exceed the photoexcited carrier density at low incident power. As a result, the total charge density involved in Auger recombination process remains essentially constant from 0.1 to 1 mW incident optical power.
The responsivity and internal quantum efficiency of the graphene/hBN heterostructure transistor are shown in Fig. 2c. Despite the high carrier mobility and the long carrier lifetime in the encapsulated graphene layer, the responsivity and internal quantum efficiency (IQE) are relatively low compared to other reported mid-infrared graphene detectors38. The main reason is the weak photoconductive gain due to the long carrier transit time, in the nanosecond range, compared to the carrier lifetime, which results from the large drain-source distance of 20 µm. This length was set here to match the large diffraction limited spot size for mid-infrared light. However, advanced design such as antenna-assisted graphene detector, where optical antennas are used as both light-harvesting components and electrodes, can be implemented to greatly enhance simultaneously light-absorption and carrier-collection efficiency39.
For further insight into many-body Coulomb scattering, we take advantage of both the asymmetry of the photocurrent induced by the dc electric field and the asymmetry of the initial distribution of photoexcited carriers in k-space induced by the polarization of the incident light. Indeed, illuminating graphene with linearly polarized radiation provides an initial anisotropic distribution of photoexcited carriers in k-space with two lobes in the direction perpendicular to the light polarization. Figure 2d shows the ratio between the photocurrent measured when light polarization is perpendicular to the dc electric field over the photocurrent when light polarization is parallel to the dc electric field, indicating that the anisotropy of the photoexcited carrier distribution is not fully relaxed in this steady-state regime. This anisotropy is consistent with expectations even when considering that Coulomb scattering is predominantly collinear in graphene. As a matter of fact, non-collinear Coulomb scattering has been reported with a characteristic time of 2 ps40. Being much smaller than our recombination time, the polarization effect at the few percent scale agrees with our observation. The photocurrent and therefore the carrier lifetime are larger for perpendicular polarization, i.e. when the lobes of the photoexcited carriers are parallel to the shift induced by the dc electric field with respect to the Dirac point. In this configuration, Auger recombination processes are expected to be less efficient due to Pauli blocking by dark carriers, whose density is maximized in the direction of the dc electric field. In the following, we mainly use light polarization parallel to the dc electric field to minimize the interaction of photoexcited carriers with the out-of-equilibrium electron–hole pairs created by Zener–Klein tunneling.
Non-linear photoresponse
We now turn to non-linear regimes to further explore the hBN/graphene heterostructure-based devices. At low-incident optical power, we observe in Fig. 3a strong deviations from the for leading even to a negative differential photoconductance for , independently of the optical power in the range Pinc = 0.1–1 mW. The contrasted behavior between low bias and high bias cannot be described by the usual photoconductive effects23 and evidences the rise of an additional recombination channel for photoexcited carriers. The photocurrent drop, by more than a factor two, suggests that this additional recombination channel is highly efficient with a characteristic time significantly shorter than the low-bias recombination time of ~30 ps. To get a more accurate determination of the voltage threshold for the ignition of this additional channel, we plot in Fig. 3c the difference ΔΙPC between the extrapolated linear regime (dashed red line in Fig. 3a) and the measured photocurrent. The obtained ΔΙPC() reveal a threshold at a voltage bias , signaling the switching of the additional recombination channel. The value of V0, observed in two distinct samples, points to an activation energy close to energy of the upper HPhP band (ℏΩII = 170–200 meV) with eV0 ~ (ℏΩII – ℏω) ≈ 54–84 meV. We therefore attribute the additional recombination channel to the emission of HPhPs in hBN layer41, consistent with previous works on similar hBN-encapsulated graphene where picosecond HPhP cooling times were reported14,42. In particular, a similar threshold was observed in noise thermometric experiments using samples of similar mobility19. Indeed, h-BN supports large number of propagating HPhP modes (electromagnetic modes originating in the coupling of photons to optical phonons) that can be very efficiently coupled to the carriers in graphene via near-field coupling (i.e. super-Planckian coupling)41. These previous works have also demonstrated that recombination of electron–hole pairs in graphene through the direct coupling with intrinsic optical phonon in graphene (of comparable energy ħΩOP = 170–200 meV) plays a minor role in hBN/graphene heterostructures. This is because non-polar optical phonons are coupled to electrons via the deformation potential, giving rise to a smaller relaxation rate.
Figure 3d shows the bias dependence of , a quantity which is directly proportional to the total recombination rate Γ(), itself the weighted sum of the Auger rate Γ1 and HPhP rate Γ2. Γ() increases strongly above the threshold V0 illustrating that Γ2 > Γ1. The gradual increase of Γ() for indicates that electric field enables an increasing number of carriers within the relaxed carrier distribution to gain energy for HPhP emission. In this picture, eV0 is the onset energy for HPhP emission. The photocurrent maximum in Fig. 3a at is larger than V0 as a result of the combined effects of Γ2 > Γ1 and the broadening of energy/momentum carrier distribution. The relevance of a bias voltage criterion in governing the local carrier energy, eV0 ~ ℏΩII − ℏω, can be questioned in a diffusive regime. It is, however, supported by previous experiments using noise thermometry19. Our understanding relies on the carrier–carrier scattering rate (τ < 50 fs), dominating over impurity scattering rate (τ < 0.3 ps deduced from the mobility). In graphene, carrier–carrier scattering is prominently collinear (due to momentum/energy conservation), meaning that it preserves momentum direction with respect to electric field orientation. Considering that Fermi velocity is energy independent in single layer graphene, the effect of electric field in carrier acceleration is independent of energy relaxation and therefore reminiscent of a ballistic case. In this picture, the electric field (bias) dependence maps the photocarrier energy distribution with respect to the HPhP energy. Figure 3c, d shows that it is broadened while keeping track of the optical pumping energy in the onset threshold eV0 = ℏΩ − ℏω < 0.1 eV. The bias dependence thus provides an energy spectroscopy of the local carrier energy distribution.
As discussed in Supplementary Note 5, we can extract the photoexcited carrier density Δnphoto coupled to the HPhP, which falls in the range of 109 cm−2 for Popt = 1 mW, and the corresponding power drained away by HPhP emission given by PHPhP = ΔnphotoℏωHPhP/τ, which scales with the µW level.
Keeping low-bias conditions, the photocurrent shows non-linear behavior as a function of the optical power, above 1 mW, as depicted in Fig. 3b for =20, 50, 90 mV. We have verified independently that the absorption is still constant and does not saturate over this optical power range. The photocurrent obeys a standard saturation law (plain lines in Fig. 3b), with a Psat ≈ 15 mW, independent of the graphene bias, corresponding to an absorbed optical power of 10 μW. To explain this non-linearity, let us consider that under large illumination, intraband carrier–carrier interactions (with ultrashort relaxation times of ∼20 fs) become more efficient, leading to a broadening of the hot carrier distribution within the electron and valence bands. Some fraction of hot carriers gain energy, potentially exceeding ℏΩII, enabling some photoexcited electron–hole pairs to efficiently recombine in the hyperbolic optical phonon modes of the hBN layer. Consequently, we attribute the photocurrent saturation observed at high incident optical power to the enhancement of photoexcited carrier rates that efficiently recombine into HPhPs. As shown in Supplementary Note 4, this saturation effect is more pronounced for light polarization perpendicular to the dc electric field (i.e. for lobes of photoexcited carriers along the DC electric field). This is a result of out-of-equilibrium Zener–Klein carriers that provide both an increased number of available intraband Coulomb scattering partners to the photoexcited carriers as well as Pauli blocking at low energy. Thus the photoexcited carriers are redistributed towards higher energy states and their coupling to HPhP are enhanced. As discussed in the non-linear regime driven by large bias, we can also extract the photoexcited carrier density Δnphoto coupled to the HPhP (see Supplementary Note 5) and we find Δnphoto in the same range 109 cm−2 with a similar threshold.
Full photoconductive response including all regimes
Finally, we enlarge scope to the full photoconductive response including bi-non-linear effects. Figure 4a, b represent the carrier lifetimes as a function of (at Popt = 0.5 mW) and Popt (at = 0.1 V). They show that both and Popt act as distinct control knobs to switch on the pathway for hot carriers in graphene to recombine via HPhP emission in the hBN layer. Indeed, at low dc electric field and low optical power, the carrier lifetime is long, ~35 ps, and mainly governed by Auger recombination process, whereas we note that the ignition of the competing ultrafast HPhP recombination pathway is observed at large dc electric field and incident optical power. These results highlight the interplay between Auger recombination process and electron–hyperbolic phonon recombination channel. We deduce in Fig. 4a the characteristic time of the electron–hyperbolic phonon recombination process, corresponding to the carrier lifetime at very large bias, to picoseconds in full agreement with the picosecond hyperbolic cooling times measured in previous reports for hBN-encapsulated graphene14,41. This agreement confirms the validity of our method of carrier lifetime extraction. This two-recombination rate analysis is supported and quantified by theoretical fits of τ = Γ−1 in Fig. 4a, b (red lines) with Γ = Γ1 + Γ2 and Γ = Γ1 + Γ2(Pinc – P0), respectively. We deduce V0 = 0.07 V, P0 = 0.5 mW, 1/Γ1 ≈ 35 ps, and a unique −1/Γ2 ≈ 0.7 ps for both fits. Remarkably, the two different determinations of the threshold, from the onset in Fig. 3c on the one hand and by adjustment of large bias data in Fig. 4a on the other hand, give consistent values of the threshold voltage .
Figure 4c summarizes the interplay between optical and electrical pumping. It shows a color plot of the full scope of these two methods of pumping the hBN/graphene heterostructures. The ratio with is represented as a function of the electrical Joule power and the absorbed optical power Pabs. The linear regime appears as a red plateau; the non-linear regimes of Fig. 4a, b are represented by dashed lines. The symmetrical effects of electrical and optical powers are remarkably reflected in the color plot, including the first diagonal where both powers are comparably involved. This means that the photoresponse at charge neutrality merely measures the total number of excited carriers irrespective of their pumping pathway, presumably due to ultrafast intraband carrier–carrier scattering shuffling carrier energy. The non-linear regime at high Joule power and high absorbed optical power uniquely provides a true opto-electrical excitation of HPhPs. Combining mid-infrared illumination and large bias dc electric field in hBN/graphene heterostructure is very promising for developing source for HPhP optics. It promotes graphene/hBN heterostructures as a platform for studying the interplay between optical and electrical pumping of HPhP.
Discussion
In conclusion, using mid-infrared photoconductivity measurements we have investigated recombination processes of carriers photoexcited at low density and energy in graphene/hBN Zener–Klein transistors. We have shown remarkable long carrier lifetime, ~30 ps, in quasi-intrinsic graphene, ultimately limited by interband Auger processes. Long carrier lifetime in graphene/hBN heterostructures could have important implications for THz lasing and highly sensitive THz photodetection. We have also unveiled the possibility to switch on at finite dc bias or mid-infrared optical power the very efficient electron–hyperbolic phonon recombination channel. This allows the carrier lifetime control, which falls below a few picoseconds upon ignition of HPhP relaxation. Investigating recombination processes for non-equilibrium carriers at low density and energy in alternative materials such as bilayer graphene and topological insulators could provide unique basic physic knowledge. Furthermore, we have investigated the interplay between optical and electrical pumping and demonstrated the opto-electrical pumping of HPhPs in the hBN layer at high Joule power and high optical power. These works could promote graphene/hBN heterostructures as a platform for phonon polariton optics and nanoscale thermal management.
Methods
Sample fabrication
The monolayer graphene and hexagonal BN flakes were produced by micro-mechanical exfoliation of bulk crystals on SiO2/Si substrates. We identified monolayer graphene sample by optical contrast and Raman spectroscopy, and clean hBN flakes were chosen after bright- and dark-field optical microscopy. Afterwards, we composed the hBN/graphene/hBN van der Waals heterostructures using a hot pick-up technique and we transferred the sandwich on the top of a 12-nm-thick Ni electrode. We localized the encapsulated graphene using Raman spectroscopy and we measured the hBN thickness and roughness using atomic force microscopy. After the sample characterization, we performed e-beam lithography on the heterostructure in order to define the design of the device (W × L = 10.4 µm × 20 µm) on the cleanest region of the sandwich and to obtain an HSQ resist mask. This mask was used to etch (Reactive Ion Etching) the top hBN layer in order to connect the graphene with one-dimensional edge contacts43. The last step of the device fabrication was the e-beam lithography to design the source, drain, and gate electrodes and metal evaporation (Cr-Au).
Experiment
The experiment is based on a CO2 laser delivering 10.6 µm wavelength light modulated at 5 kHz. The laser light is focused on the sample using an aspheric Ge lens. The sample is placed within a liquid He cryostat with ZnSe optical window. The photocurrent signal is measured with a lock-in amplifier. A photovoltaic multiple junction detector is used to measure the mid-infrared light transmitted through the hBN/graphene heterostructure-based device.
Supplementary information
Acknowledgements
We thank Marco Polini, Andrea Tomadin, and Dmitry Svintsov for valuable discussions. This project has received funding from the European Research Council (ERC) under the European Union’s Horizon 2020 research and innovation program (grant agreement No. 820133) and partial funding from the European Union Horizon 2020 research and innovation program under grant agreement No. 785219. Graphene Core 2. P.H. was supported by the China Scholarship Council and Program of Sino-French Education for Research.
Author contributions
P.H., J.M., J.T., and S.D. conceived the optical experiment, H.G. and B.P conceived the electrical experiment. P.H. conducted the photoconductivity measurements and H.G. conducted the electrical characterization. F.V. designed the sample electrical connection. S.M. conducted electric field calculation. E.R., H.G., T.T., and K.W. participated in sample fabrication. J.M., R.F., and B.P. participated in data analysis. J.M., S.D., R.F., and B.P. wrote the manuscript with contributions from the co-authors.
Data availability
Statements of data availability and any associated references are available in Supplementary Information.
Competing interests
The authors declare no competing interests.
Footnotes
Peer review information Nature Communications thanks Yaguo Wang and the other anonymous reviewer(s) for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Supplementary information is available for this paper at 10.1038/s41467-020-14714-1.
References
- 1.Banszerus L, et al. Ultrahigh-mobility graphene devices from chemical vapor deposition on reusable copper. Sci. Adv. 2015;1:e1500222. doi: 10.1126/sciadv.1500222. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 2.Gierz I, et al. Snapshots of non-equilibrium Dirac carrier distributions in graphene. Nat. Mater. 2013;12:1119–1124. doi: 10.1038/nmat3757. [DOI] [PubMed] [Google Scholar]
- 3.Winzer T, Malić E, Knorr A. Microscopic mechanism for transient population inversion and optical gain in graphene. Phys. Rev. B. 2013;87:165413. doi: 10.1103/PhysRevB.87.165413. [DOI] [Google Scholar]
- 4.Castilla S, et al. Fast and sensitive terahertz detection using an antenna-integrated graphene pn junction. Nano Lett. 2019;19:2765–2773. doi: 10.1021/acs.nanolett.8b04171. [DOI] [PubMed] [Google Scholar]
- 5.Koppens F, et al. Photodetectors based on graphene, other two-dimensional materials and hybrid systems. Nat. Nanotechnol. 2014;9:780–793. doi: 10.1038/nnano.2014.215. [DOI] [PubMed] [Google Scholar]
- 6.Jago R, Winzer T, Knorr A, Malic E. Graphene as gain medium for broadband lasers. Phys. Rev. B. 2015;92:085407. doi: 10.1103/PhysRevB.92.085407. [DOI] [Google Scholar]
- 7.Satou A, Ryzhii V, Kurita Y, Otsuji T. Threshold of terahertz population inversion and negative dynamic conductivity in graphene under pulse photoexcitation. J. Appl. Phys. 2013;113:143108. doi: 10.1063/1.4801916. [DOI] [Google Scholar]
- 8.Ryzhii V, Dubinov AA, Otsuji T, Mitin V, Shur MS. Terahertz lasers based on optically pumped multiple graphene structures with slot-line and dielectric waveguides. J. Appl. Phys. 2010;107:054505. doi: 10.1063/1.3327212. [DOI] [Google Scholar]
- 9.Tielrooij K, et al. Photoexcitation cascade and multiple hot-carrier generation in graphene. Nat. Phys. 2013;9:248–252. doi: 10.1038/nphys2564. [DOI] [Google Scholar]
- 10.Mihnev M, et al. Microscopic origins of the terahertz carrier relaxation and cooling dynamics in graphene. Nat. Commun. 2016;7:11617. doi: 10.1038/ncomms11617. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 11.Winnerl S, et al. Time-resolved spectroscopy on epitaxial graphene in the infrared spectral range: relaxation dynamics and saturation behavior. J. Phys. Condens. Matter. 2013;25:054202. doi: 10.1088/0953-8984/25/5/054202. [DOI] [PubMed] [Google Scholar]
- 12.Strait J, et al. Very slow cooling dynamics of photoexcited carriers in graphene observed by optical-pump terahertz-probe spectroscopy. Nano Lett. 2011;11:4902–4906. doi: 10.1021/nl202800h. [DOI] [PubMed] [Google Scholar]
- 13.Winzer T, Malic E. The impact of pump fluence on carrier relaxation dynamics in optically excited graphene. J. Phys. Condens. Matter. 2013;25:054201. doi: 10.1088/0953-8984/25/5/054201. [DOI] [PubMed] [Google Scholar]
- 14.Tielrooij K, et al. Out-of-plane heat transfer in van der Waals stacks through electron–hyperbolic phonon coupling. Nat. Nanotechnol. 2018;13:41–46. doi: 10.1038/s41565-017-0008-8. [DOI] [PubMed] [Google Scholar]
- 15.Dai S, et al. Graphene on hexagonal boron nitride as a tunable hyperbolic metamaterial. Nat. Nanotechnol. 2015;10:682–686. doi: 10.1038/nnano.2015.131. [DOI] [PubMed] [Google Scholar]
- 16.Winnerl S, et al. Carrier, relaxation in epitaxial graphene photoexcited near the Dirac point. Phys. Rev. Lett. 2011;107:237401. doi: 10.1103/PhysRevLett.107.237401. [DOI] [PubMed] [Google Scholar]
- 17.Winnerl S, Jago R, Malic E. Experimentally accessible signatures of Auger scattering in graphene. Phys. Rev. B. 2016;94:235430. doi: 10.1103/PhysRevB.94.235430. [DOI] [Google Scholar]
- 18.Vandecasteele N, et al. Current-voltage characteristics of graphene devices: Interplay between Zener-Klein tunneling and defects. Phys. Rev. B. 2010;82:045416. doi: 10.1103/PhysRevB.82.045416. [DOI] [Google Scholar]
- 19.Yang W, et al. A graphene Zener–Klein transistor cooled by a hyperbolic substrate. Nat. Nanotechnol. 2018;13:47–52. doi: 10.1038/s41565-017-0007-9. [DOI] [PubMed] [Google Scholar]
- 20.Zhong H, Zhang Z, Xu H, Qiu C, Peng L-M. Comparison of mobility extraction methods based on field-effect measurements for graphene. AIP Adv. 2015;5:057136. doi: 10.1063/1.4921400. [DOI] [Google Scholar]
- 21.Kane G, Lazzeri M, Mauri F. High-field transport in graphene: the impact of Zener tunneling. J. Phys. Condens. Matter. 2015;27:164205. doi: 10.1088/0953-8984/27/16/164205. [DOI] [PubMed] [Google Scholar]
- 22.Xia F, et al. Ultrafast graphene photodetector. Nat. Nanotechnol. 2009;4:839–843. doi: 10.1038/nnano.2009.292. [DOI] [PubMed] [Google Scholar]
- 23.Freitag M, et al. Photoconductivity of biased graphene. Nat. Photon. 2013;7:53–59. doi: 10.1038/nphoton.2012.314. [DOI] [Google Scholar]
- 24.Schuler S, et al. Controlled generation of a p–n junction in a waveguide integrated graphene photodetector. Nano Lett. 2016;16:7107–7112. doi: 10.1021/acs.nanolett.6b03374. [DOI] [PubMed] [Google Scholar]
- 25.Ma Q, et al. Giant intrinsic photoresponse in pristine graphene. Nat. Nanotechnol. 2019;14:145–150. doi: 10.1038/s41565-018-0323-8. [DOI] [PubMed] [Google Scholar]
- 26.Malic E, Winzer T, Wendler F, Knorr A. Review on carrier multiplication in graphene. Phys. Status Solidi B. 2016;253:2303–2310. doi: 10.1002/pssb.201600416. [DOI] [Google Scholar]
- 27.Jago R, Wendler F, Malic E. Microscopic understanding of the photoconduction effect in graphene. Phys. Rev. B. 2017;96:085431. doi: 10.1103/PhysRevB.96.085431. [DOI] [Google Scholar]
- 28.Tomadin A, et al. The ultrafast dynamics and conductivity of photoexcited graphene at different Fermi energies. Sci. Adv. 2018;4:2375–2548. doi: 10.1126/sciadv.aar5313. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 29.Jared H, et al. Very slow cooling dynamics of photoexcited carriers in graphene observed by optical-pump terahertz-probe spectroscopy. Nano Lett. 2011;11:4902–4906. doi: 10.1021/nl202800h. [DOI] [PubMed] [Google Scholar]
- 30.Nagashio K, Nishimura T, Toriumi A. Estimation of residual carrier density near the Dirac point in graphene through quantum capacitance measurement. Appl. Phys. Lett. 2013;102:173507. doi: 10.1063/1.4804430. [DOI] [Google Scholar]
- 31.Baudin, E., Voisin, C. & Plaçais, B. Hyperbolic phonon polariton electroluminescence as an electronic cooling pathway. Adv. Funct. Mater. 10.1002/adfm.201904783 (2019).
- 32.Rana F, et al. Carrier recombination and generation rates for intravalley and intervalley phonon scattering in graphene. Phys. Rev. B. 2009;79:115447. doi: 10.1103/PhysRevB.79.115447. [DOI] [Google Scholar]
- 33.Tse W-K, Sarma SD. Energy relaxation of hot Dirac fermions in graphene. Phys. Rev. B. 2009;79:235406. doi: 10.1103/PhysRevB.79.235406. [DOI] [Google Scholar]
- 34.Graham M, et al. Photocurrent measurements of supercollision cooling in graphene. Nat. Phys. 2013;9:103–108. doi: 10.1038/nphys2493. [DOI] [Google Scholar]
- 35.Betz A, et al. Supercollision cooling in undoped graphene. Nat. Phys. 2013;9:109–112. doi: 10.1038/nphys2494. [DOI] [Google Scholar]
- 36.Alymov G, Vyurkov V, Ryzhii V, Satou A, Svintsov D. Auger recombination in Dirac materials: a tangle of many-body effects. Phys. Rev. B. 2018;97:205411. doi: 10.1103/PhysRevB.97.205411. [DOI] [Google Scholar]
- 37.Rana F. Electron-hole generation and recombination rates for Coulomb scattering in graphene. Phys. Rev. B. 2007;76:155431. doi: 10.1103/PhysRevB.76.155431. [DOI] [Google Scholar]
- 38.Guo Q, et al. Efficient electrical detection of mid-infrared graphene plasmons at room temperature. Nat. Mater. 2018;17:986–992. doi: 10.1038/s41563-018-0157-7. [DOI] [PubMed] [Google Scholar]
- 39.Yao Y, et al. High-responsivity mid-infrared graphene detectors with antenna-enhanced photocarrier generation and collection. Nano Lett. 2014;14:3749–3754. doi: 10.1021/nl500602n. [DOI] [PubMed] [Google Scholar]
- 40.König-Otto JC, et al. Slow noncollinear Coulomb scattering in the vicinity of the Dirac point in graphene. Phys. Rev. Lett. 2016;117:087401. doi: 10.1103/PhysRevLett.117.087401. [DOI] [PubMed] [Google Scholar]
- 41.Principi A, et al. Super-Planckian electron cooling in a van der Waals stack. Phys. Rev. Lett. 2017;118:126804. doi: 10.1103/PhysRevLett.118.126804. [DOI] [PubMed] [Google Scholar]
- 42.Woessner A, et al. Electrical detection of hyperbolic phonon-polaritons in heterostructures of graphene and boron nitride. npj 2D Mater. Appl. 2017;1:25. doi: 10.1038/s41699-017-0031-5. [DOI] [Google Scholar]
- 43.Wang L, et al. One-dimensional electrical contact to a two-dimensional material. Science. 2013;342:614–617. doi: 10.1126/science.1244358. [DOI] [PubMed] [Google Scholar]
Associated Data
This section collects any data citations, data availability statements, or supplementary materials included in this article.
Supplementary Materials
Data Availability Statement
Statements of data availability and any associated references are available in Supplementary Information.