. 2020 Feb 13;25(4):803. doi: 10.3390/molecules25040803

Carbon-Supported Raney Nickel Catalyst for Acetone Hydrogenation with High Selectivity

Shuliang Lu 1, Jiajia Wu 1, Hui Peng 1, Yong Chen 1,*
PMCID: PMC7070612  PMID: 32069793

Abstract

Catalysts with high selectivity play key roles in green chemistry. In this work, a granular Raney Ni catalyst using carbon as support (Raney Ni/C) was developed by mixing phenolic resin with Ni-Al alloy, conducting carbonization at high temperature, and leaching with alkaline liquor. The as-prepared Raney Ni/C catalyst is suitable for use in fix-bed reactors. Moreover, it shows high activity and selectivity for catalytic acetone hydrogenation. For instance, at the reaction temperature of 120 °C, the conversion of acetone can reach up to 99.9% and the main byproduct methyl isobutylcarbinol (MIBC) content can be diminished to 0.02 wt%. The Raney Ni/C may represent a new type of shaped Raney metal catalysts, which are important fix-bed catalysts in chemical industry.

Keywords: carbon-support, Raney nickel, acetone hydrogenation, acidity

1. Introduction

Catalysts play key roles in the chemical industry, and more than 90% of today’s chemical processes use catalysts [1,2]. Industrial catalysts have some well-defined features, e.g., activity, selectivity, stability, strength, recoverability, and poison resistance, related to the basic demands of productive process to achieve green, environmental, predictable, and economic operation [3]. Nowadays, it has been realized that the supports, used to disperse and anchor the catalytic active component, play a role in determining the catalytic properties as a result of their physical-chemical properties.

Isopropanol is a commonly used bulk chemical widely used in organic synthesis, industrial solvent, and fuel cells [4,5,6,7]. Catalytic acetone hydrogenation is a cheap, safe, and mature alternative method for isopropanol production due to its easy catalytic reduction of C=O into C-OH [8]. Currently, Raney nickel is adopted as a catalyst for the basic acetone hydrogenation process [5,8]. However, powdered Raney nickel cannot be applied in a fix-bed reactor, and is mainly employed in slurry phase reactors for batch productions. Besides Raney nickel, traditional metal/oxide catalysts are also used in acetone hydrogenation, including Ni/Al2O3 [9], Ni/CeO2 [10], Ni/SiO2 [11], and Pt/Fe3O4 [12]. Nevertheless, these tradition metal/oxide catalysts always exhibit acidity due to the intrinsic characteristics of supports. Consequently, acidity always leads to byproducts such as methyl isobutyl ketone (MIBK), methyl isobutylcarbinol (MIBC), isopropyl ether (IPE), and others [13,14,15,16,17,18,19], which require a further removal process. Additionally, the reclamation of traditional metal/oxide catalysts requires high-temperature calcination or strong acid/base dissolution, which can potentially cause environmental contamination.

Carbon materials have a variety of advantages (such as stable chemical-mechanical properties, ease with regards to reclamation [20,21,22,23,24]), and have wide applications in the metal catalysts as supports [25,26,27,28,29,30]. Moreover, the pore structures and surface properties of carbon materials can be adjusted by changing the carbon precursor, adjusting the carbonization temperature, and doping heteroatoms [31,32]. Therefore, a carbon material with weak acidity can be synthesized via the above-mentioned methods and used for supporting Raney nickel. In this case, challenges such as the difficulty of using Raney nickel powder in fixed-bed reactors, byproducts formation during the acetone hydrogenation catalyzed by acidity, and environmental contamination aroused from catalyst reclamation could be overcome. Here, a granular carbon-supported Raney nickel catalyst (Raney Ni/C) with weak acidity was prepared via mixing phenolic resin with Ni-Al alloy, conducting carbonization at high temperatures, and leaching with alkaline liquor. Then, the Raney Ni/C was characterized by Raman spectra, Scanning Electron Microscopy (SEM), Brunauer Emmett Teller (BET), and NH3 temperature-programmed desorption (NH3-TPD), respectively. Its catalytic properties in terms of acetone hydrogenation were studied at different reaction temperatures and compared with a traditional Ni/Al2O3 catalyst.

2. Results and Discussion

The microstructure of Raney Ni/C was characterized by Raman spectrum. As shown in Figure 1, there are two bands at 1340 cm−1 (D band) and 1590 cm−1 (G band), which are not separated completely. The D band corresponds to the common feature of all disordered graphitic carbon, while the G band represents the graphitic carbon phase with an sp2 electronic configuration [33]. In addition, the relative intensity of both bands reflects the degree of graphitization [34]. Here, the ID/IG of Raney Ni/C is about 3.2, which indicates a low graphitization degree and demonstrates the dominant disordered structure of the carbon support of Raney Ni/C. In the N2-sorption measurements, the specific area and average pore width of Raney Ni/C are determined as 111 m2∙g−1 and 3.3 nm, respectively, by virtue of BET equation; the pore volume is calculated to be 0.092 cm3∙g−1 via Barrett-Joyner-Halenda (BJH) method; and the specific area, average pore width, and pore volume of Ni/Al2O3 are 105 m2∙g−1, 10.8 nm, and 0.29 cm3∙g−1, respectively. Hence, the Raney Ni/C is mesoporous and possesses a more small-aperture pore structure than Ni/Al2O3. SEM image shown in Figure 2 illustrates the porous structure of Raney Ni/C as expected. The acidities of both Raney Ni/C and Ni/Al2O3 were measured by NH3-TPD and are shown in Figure 3. Both Raney Ni/C and Ni/Al2O3 show two desorption peaks. Obviously, they have similar weak acidic site desorption peaks at 180 °C; meanwhile, the Raney Ni/C shows a smaller medium-strong acidic sites desorption peak than the Ni/Al2O3 at 350 °C [15]. As proven, the acidity of Raney Ni/C is weaker than Ni/Al2O3.

Figure 1.

Figure 1

Open in a new tab

Raman spectrum of Raney Ni/C catalyst.

Figure 2.

Figure 2

Open in a new tab

SEM image Raney Ni/C catalyst.

Figure 3.

Figure 3

Open in a new tab

NH3-TPD profiles of Raney Ni/C catalyst and Ni/Al2O3 catalyst.

The numerical results of acetone hydrogenation at 80–150 °C catalyzed by Raney Ni/C and Ni/Al2O3 are listed in Table 1. The conversion of acetone increases with increasing reaction temperature, and all reach above 99% at 120–150 °C, indicating the catalytic activity of Raney Ni/C is as high as that of commercialized Ni/Al2O3. Moreover, MIBC is the main byproduct of acetone hydrogenation. When the reaction temperature reached 150 °C, the concentration of MIBC catalyzed by Raney Ni/C was merely 500 ppm (0.05 wt%). As for Ni/Al2O3, the MIBC concentration was 56,000 ppm (5.6 wt%) at the same reaction conditions. Obviously, the Raney Ni/C catalyst can reduce the MIBC byproduct of acetone hydrogenation. This can be attributed to the different acidities of catalyst supports attached to carbon and Al2O3, respectively. Furthermore, in order to testify the effect of acidity on catalytic acetone hydrogenation, a strong acidic cation exchange resin was simply mixed with Raney Ni/C and used as an acetone hydrogenation catalyst. As shown in Table 1, the concentration of MIBC reached up to 150,000 ppm (15 wt%). The result confirms the MIBC byproduct is mainly caused by catalyst acidity and the yield of MIBC increases with the increasing catalyst acidity.

Table 1.

Numerical results of acetone hydrogenation catalyzed by Raney Ni/C, Ni/Al2O3, and mixed catalyst of Raney Ni/C and strong acidic cation exchange resin.

Catalyst Temperature (°C) Conversion of AC (%) MIBC (wt%)
Ni/Al2O3 a 80 94.3 0.3
100 99.9 1.9
120 99.9 2.6
150 99.9 5.6
Raney Ni/C b 80 76.3 0
100 93.4 0.006
120 99.9 0.02
150 99.9 0.05
Resin + Raney Ni/C c 100 99.9 15
Open in a new tab

Reaction conditions: a 20 g acetone, 1 g Ni/Al2O3, 3 Mpa H2 pressure, and magnetic stirring 10 h; b 20 g acetone, 1 g Raney Ni/C, 3 Mpa H2 pressure, and magnetic stirring 10 h; c 20 g acetone, 1 g strong acidic cation exchange resin, 1 g Raney Ni/C, 3 Mpa H2 pressure, and magnetic stirring 10 h.

3. Materials and Methods

In this study, a typical Raney Ni/C was prepared as follows: 2.5 g Ni-Al alloy powder, 10 g powdery phenol formaldehyde resin, and 1.2 g hexamethylenetetramine were mixed by a high speed mixer (Zhongcheng pharmaceutical machinery, Changsha, Hunan, China). The mixture was filled into a 2 mm mold and compressed tightly at a pressure of 5 Mpa. Then, a 2 mm-thick plate was obtained. Next, the 2 mm-thick plate was dried at 150 °C for 30 min, and mechanically cut into particles with a particle size of approximately 2 mm. Finally, granular Raney Ni/C catalyst was obtained through carbonizing the 2 mm particles at the conditions of 800 °C and nitrogen atmosphere for 2 h, and aluminum of the carbonized particles was leached using alkaline liquid. The Ni-loading of granular Raney Ni/C is 20 wt%. The traditional Ni/Al2O3 catalyst was prepared according to the commercial impregnation method. To be specific, 10 g Ni(NO3)2∙6H2O was dissolved in 3 g deionized water, to which 10 g Al2O3 was added and impregnated for 1 h. The above mixture was dried at 120 °C for 12 h, followed with calcined at 360 °C for 4 h. Finally, Ni/Al2O3 was obtained after reduced by hydrogen at 400 °C for 8 h. The Ni-loading of Ni/Al2O3 was 20 wt%.

More detailed experimental information, including chemical materials, characterization methods, and hydrogenation experiment, is attached in the supplementary material.

4. Conclusions

Raney Ni is shaped as a granular catalyst by using carbon material as support. This Raney Ni/C can be used in fix-bed reactors, which overcomes the disadvantages of commonly used Raney nickel catalyst. Moreover, the Raney Ni/C can dramatically reduce the MIBC byproduct for catalytic acetone hydrogenation, as a result of the weak acidity of the carbon-support. The recycling of the Raney Ni/C would only need calcining in air to get rid of carbon-support, and the remaining metal alloys could be reused directly. We believe that the preparing method of the granular carbon-supported Raney nickel catalyst could be applied to a series of Raney metal catalysts, for instance, Raney cobalt and Raney copper, which are important fix-bed catalysts in chemical industry.

Supplementary Materials

Click here for additional data file. (227.2KB, pdf)

The following are available online, chemical materials, characterization methods, and hydrogenation experiment.

Author Contributions

Conceptualization, S.L.; methodology, S.L. and Y.C.; investigation, Y.C.; data curation, H.P.; writing—original draft preparation, Y.C.; writing—review and editing, S.L., J.W., H.P., and Y.C. All authors have read and agreed to the published version of the manuscript.

Funding

This research received no external funding.

Conflicts of Interest

The authors declare no conflict of interest.

Footnotes

Sample Availability: Samples of the compounds are not available from the authors.

References

  • 1.Cui X., Li W., Ryabchuk P., Junge K., Beller M. Bridging homogeneous and heterogeneous catalysis by heterogeneous single-metal-site catalysts. Nat. Catal. 2018;1:385–397. doi: 10.1038/s41929-018-0090-9. [DOI] [Google Scholar]
  • 2.He L., Weniger F., Neumann H., Beller M. Synthesis, characterization, and application of metal nanoparticles supported on nitrogen-doped carbon: Catalysis beyond electrochemistry. Angew. Chem. Int. Ed. 2016;55:12582–12594. doi: 10.1002/anie.201603198. [DOI] [PubMed] [Google Scholar]
  • 3.Lloyd L. Handbook of Industrial Catalysts. Springer Science and Business Media LLC; New York, NY, USA: 2011. pp. 4–10. [Google Scholar]
  • 4.Yang Z., Chen W., Zheng J., Yang Z., Zhang N., Zhong C.-J., Chen B.H. Efficient low-temperature hydrogenation of acetone on bimetallic Pt-Ru/C catalyst. J. Catal. 2018;363:52–62. doi: 10.1016/j.jcat.2018.04.011. [DOI] [Google Scholar]
  • 5.Rahman A., S-Al-Deyab S. A review on reduction of acetone to isopropanol with Ni nano superactive, heterogeneous catalysts as an environmentally benevolent approach. Appl. Catal. A: Gen. 2014;469:517–523. doi: 10.1016/j.apcata.2013.10.015. [DOI] [Google Scholar]
  • 6.Ophardt H., Loos V., Hoogers G., Lang A. Direct isopropanol fuel cell. 10,230,120. U.S. Patent. 2019 Mar 12;
  • 7.Park H., Ou H.-H., Kang U., Choi J., Hoffmann M.R. Photocatalytic conversion of carbon dioxide to methane on TiO2/CdS in aqueous isopropanol solution. Catal. Today. 2016;266:153–159. doi: 10.1016/j.cattod.2015.09.017. [DOI] [Google Scholar]
  • 8.Balouch A., Umar A.A., Shah A.A., Salleh M.M., Oyama M. Efficient Heterogeneous Catalytic Hydrogenation of Acetone to Isopropanol on Semihollow and Porous Palladium Nanocatalyst. ACS Appl. Mater. Interfaces. 2013;5:9843–9849. doi: 10.1021/am403087m. [DOI] [PubMed] [Google Scholar]
  • 9.Jiang H., Lu S., Zhang X., Dai W., Qiao J. Polymer-Supported Raney Nickel Catalysts for Sustainable Reduction Reactions. Molecules. 2016;21:833. doi: 10.3390/molecules21070833. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 10.Rao P.V.R., Kumar V.P., Rao G.S., Chary K.V.R. Vapor phase selective hydrogenation of acetone to methyl isobutyl ketone (MIBK) over Ni/CeO2 catalysts. Catal. Sci. Technol. 2012;2:1665. doi: 10.1039/c2cy20021j. [DOI] [Google Scholar]
  • 11.Witsuthammakul A., Sooknoi T. Selective hydrodeoxygenation of bio-oil derived products: Ketones to olefins. Catal. Sci. Technol. 2015;5:3639–3648. doi: 10.1039/C5CY00367A. [DOI] [Google Scholar]
  • 12.Ji Y., Wu Y., Zhao G., Wang D., Liu L., He W., Li Y. Porous bimetallic Pt-Fe nanocatalysts for highly efficient hydrogenation of acetone. Nano Res. 2015;8:2706–2713. doi: 10.1007/s12274-015-0777-z. [DOI] [Google Scholar]
  • 13.Zhou Y., Duan H., Lin B., Han K., Wei J. Supported TiO2–Pd bifunctional catalysts for the one-pot synthesis of methyl isobutyl ketone from acetone: Modulation of the acid and base property of loaded TiO2 by support. React. Kinet. Mech. Catal. 2018;125:303–317. doi: 10.1007/s11144-018-1409-x. [DOI] [Google Scholar]
  • 14.Zhang S., Wu P., Yang L., Zhou Y., Zhong H. An efficient bifunctional catalyst of TiO2 coating and supported Pd on cordierite for one-pot synthesis of MIBK from acetone. Catal. Commun. 2015;71:61–64. doi: 10.1016/j.catcom.2015.08.007. [DOI] [Google Scholar]
  • 15.Ma R., Li Y., Wu G., He Y., Feng J., Zhao Y., Li D. Fabrication of Pd-based metal-acid-alkali multifunctional catalysts for one-pot synthesis of MIBK. Chin. J. Catal. 2018;39:1384–1394. doi: 10.1016/S1872-2067(18)63092-X. [DOI] [Google Scholar]
  • 16.Narayanan S., Unnikrishnan R. Selective hydrogenation of acetone to methyl isobutyl ketone (MIBK) over co-precipitated Ni/Al2O3 catalysts. Appl. Catal. A: Gen. 1996;145:231–236. doi: 10.1016/0926-860X(96)00165-2. [DOI] [Google Scholar]
  • 17.Yang S.-M., Wu Y.M. One step synthesis of methyl isobutyl ketone over palladium supported on AlPO4-11 and SAPO-11. Appl. Catal. A: Gen. 2000;192:211–220. doi: 10.1016/S0926-860X(99)00408-1. [DOI] [Google Scholar]
  • 18.Shen Y., Yi J., Yan Y., Liu D., Fan L., Li S. Hydrogenation and Condensation of Acetone over Ni/MgO–Al2O3 Prepared from Hydrotalcite Precursors. J. Chem. Eng. Jpn. 2016;49:656–662. doi: 10.1252/jcej.15we057. [DOI] [Google Scholar]
  • 19.Bagabas A.A., Mokhtar M., Akhmedov V.M., Narasimharao K., Basahel S.N., Al-Rabiah A. Ru–C–ZnO Composite Catalysts for the Synthesis of Methyl Isobutyl Ketone via Single Step Gas Phase Acetone Self-Condensation. Catal. Lett. 2014;144:1278–1288. doi: 10.1007/s10562-014-1253-1. [DOI] [Google Scholar]
  • 20.Tasis D., Tagmatarchis N., Bianco A., Prato M. Chemistry of carbon nanotubes. Chem. Rev. 2006;106:1105–1136. doi: 10.1021/cr050569o. [DOI] [PubMed] [Google Scholar]
  • 21.Liang C., Li Z., Dai S. Mesoporous Carbon Materials: Synthesis and Modification. Angew. Chem. Int. Ed. 2008;47:3696–3717. doi: 10.1002/anie.200702046. [DOI] [PubMed] [Google Scholar]
  • 22.Georgakilas V., Perman J.A., Tuček J., Zbořil R. Broad Family of Carbon Nanoallotropes: Classification, Chemistry, and Applications of Fullerenes, Carbon Dots, Nanotubes, Graphene, Nanodiamonds, and Combined Superstructures. Chem. Rev. 2015;115:4744–4822. doi: 10.1021/cr500304f. [DOI] [PubMed] [Google Scholar]
  • 23.Shen K., Chen X., Chen J., Li Y. Development of MOF-Derived Carbon-Based Nanomaterials for Efficient Catalysis. ACS Catal. 2016;6:5887–5903. doi: 10.1021/acscatal.6b01222. [DOI] [Google Scholar]
  • 24.Bianco A., Chen Y., Chen Y., Ghoshal D., Hurt R.H., Kim Y.A., Koratkar N., Meunier V., Terrones M. A carbon science perspective in 2018: Current achievements and future challenges. Carbon. 2018;132:785–801. doi: 10.1016/j.carbon.2018.02.058. [DOI] [Google Scholar]
  • 25.Liu X., Conte M., Elias D., Lu L., Morgan D.J., Freakley S.J., Johnston P., Kiely C.J., Hutchings G.J. Investigation of the active species in the carbon-supported gold catalyst for acetylene hydrochlorination. Catal. Sci. Technol. 2016;6:5144–5153. doi: 10.1039/C6CY00090H. [DOI] [Google Scholar]
  • 26.Contreras-Mora J., Banerjee R., Bolton B.K., Valentin J., Monnier J.R., Williams C.T. Characterization and Evaluation of Carbon-Supported Noble Metals for the Hydrodeoxygenation of Acetic Acid. Org. Process. Res. Dev. 2018;22:1628–1635. doi: 10.1021/acs.oprd.8b00288. [DOI] [Google Scholar]
  • 27.Perez R.F., Soares O.S., De Farias A.M.D., Pereira M.F.R., Fraga M.A. Conversion of hemicellulose-derived pentoses over noble metal supported on 1D multiwalled carbon nanotubes. Appl. Catal. B: Environ. 2018;232:101–107. doi: 10.1016/j.apcatb.2018.03.042. [DOI] [Google Scholar]
  • 28.Qin Q., Heil T., Antonietti M., Oschatz M. Single-Site Gold Catalysts on Hierarchical N-Doped Porous Noble Carbon for Enhanced Electrochemical Reduction of Nitrogen. Small Methods. 2018;2:1800202. doi: 10.1002/smtd.201800202. [DOI] [Google Scholar]
  • 29.Du H., Zhao C.X., Lin J., Guo J., Wang B., Hu Z., Shao Q., Pan D., Wujcik E.K., Guo Z. Carbon Nanomaterials in Direct Liquid Fuel Cells. Chem. Rec. 2018;18:1365–1372. doi: 10.1002/tcr.201800008. [DOI] [PubMed] [Google Scholar]
  • 30.Singhania A., Bhaskarwar A.N. Performance of Activated-Carbon-Supported Ni, Co, and Ni-Co Catalysts for Hydrogen Iodide Decomposition in a Thermochemical Water-Splitting Sulfur-Iodine Cycle. Energy Technol. 2018;6:1104–1111. doi: 10.1002/ente.201700752. [DOI] [Google Scholar]
  • 31.Mironenko R.M., Belskaya O.B., Likholobov V.A. Approaches to the synthesis of Pd/C catalysts with controllable activity and selectivity in hydrogenation reactions. Catal. Today. 2019 doi: 10.1016/j.cattod.2019.03.023. [DOI] [Google Scholar]
  • 32.Wang X., Chen Z., Zhao X., Yao T., Chen W., You R., Zhao C., Wu G., Wang J., Huang W. Regulation of coordination number over single Co sites: Triggering the efficient electroreduction of CO2. Angew. Chem. Int. Ed. 2018;57:1944–1948. doi: 10.1002/anie.201712451. [DOI] [PubMed] [Google Scholar]
  • 33.Zhang J., Wang X., Qi G., Li B., Song Z., Jiang H., Zhang X., Qiao J. A novel N-doped porous carbon microsphere composed of hollow carbon nanospheres. Carbon. 2016;96:864–870. doi: 10.1016/j.carbon.2015.10.045. [DOI] [Google Scholar]
  • 34.Shi M.-M., Bao D., Li S.-J., Wulan B.-R., Yan J.-M., Jiang Q. Anchoring PdCu Amorphous Nanocluster on Graphene for Electrochemical Reduction of N2to NH3under Ambient Conditions in Aqueous Solution. Adv. Energy Mater. 2018;8:1800124. doi: 10.1002/aenm.201800124. [DOI] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Supplementary Materials

Click here for additional data file. (227.2KB, pdf)

Articles from Molecules are provided here courtesy of Multidisciplinary Digital Publishing Institute (MDPI)

RESOURCES