. 2020 Jun 9;5(24):14417–14426. doi: 10.1021/acsomega.0c00966

Flexible Supercapacitors Prepared Using the Peanut-Shell-Based Carbon

Meng-Feng Wu 1, Chung-Hsuan Hsiao 1, Chi-Young Lee 1, Nyan-Hwa Tai 1,*
PMCID: PMC7315429  PMID: 32596579

Abstract

graphic file with name ao0c00966_0011.jpg

In this work, we report the fabrication and performance of supercapacitors made from carbonized peanut shells, which are renewable materials with a huge annual yield and are usually discarded directly by people. With proper treatment, peanut shells could be used for many applications. Herein, we demonstrate that the peanut shells treated with carbonization and activation processes not only possess an extremely high surface area but also provide a hierarchical structure for energy storage. The performance of the electrode can be further improved by nitrogen doping and adding graphene oxide to the electrode. The electrode shows a specific capacitance of 289.4 F/g, which can be maintained at an acceptable level even at a high scanning rate. In addition, a good capacitance retention of 92.8% after 5000 test cycles demonstrates that the electrode possesses an excellent electrochemical property.

1. Introduction

With the rapid development of technology, there is a demand for devices with high efficiency for energy storage. Supercapacitors, a promising candidate for high-performance energy storage devices, have drawn intensive attention because they possess many advantages, such as high power density (PD), long cycle life, short charging time, low maintenance cost, and wide thermal operating range. However, supercapacitors have their drawbacks: for example, a low energy density (ED) of about 3–30% for a battery.1−3 Because of their different energy storage mechanisms, supercapacitors can be divided into two types: electrical double-layer capacitors (EDLCs) and pseudocapacitors (PCs).4,5

According to the Helmholtz model, the Gouy–Chapman model, and the Stern model, an electric field is generated at the interface between the electrode and the electrolyte to store energy for the EDLCs. With more surface area of the electrode materials, the electrodes can attract more ions and thus possess higher capacitance.6,7 On the other hand, PCs utilize the reversible multielectron faradic redox reactions with charge transfer to store energy and generally exhibit a higher energy density and better capacitance than EDLCs. Nevertheless, the poor electrical conductivity of the electrode restricts the faradic redox reactions, thus lowering the power density and resulting in poor stability.8

In contrast, EDLCs have a better power density because of the good conductivity of the electrode materials. Some common materials for EDLCs include activated carbons (ACs), carbide-derived carbons (CDCs), graphene oxide (GO), and carbon nanotubes (CNTs). Among them, AC is the most widely adopted material owing to its high specific surface area, low cost, excellent chemical stability, and abundance in raw materials.9−11 However, ACs have a microporous structure with a narrow distribution in the range of 0.5–1.5 nm, which lacks larger pores and limits the electrolyte impregnation into the interior of the electrode materials. The hierarchical structure is a crucial factor for energy storage, especially at a high scan rate or current density. Improper pore size distribution and microstructure will lead to poor power density.12,13 To overcome this problem, it is imperative to design electrode materials with a proper microstructure for better properties. By introducing larger pores like mesopores or by improving the conductivity of the electrode materials, the routes for ion transport are increased and the electrical resistance of the electrode is reduced, thereby enhancing the power density. In this regard, the porosity of the structure must be preserved and a significant fraction of micropores need to be maintained to increase the high specific surface area for achieving high energy density.13,14

Besides pore structure design, nitrogen doping also enhances the electrochemical performance of the supercapacitors by way of introducing surface functional groups. The nitrogen atoms are mainly from four types of functional groups in the graphite lattice: pyrrolic-N (N5), pyridinic-N (N6), pyridinic-N+–O– (NX), and quaternary-N (NQ). These four functional groups can improve the conductivity of the electrode materials and also participate in the Faraday reaction, thereby contributing to the pseudocapacitance.13,15−18

Peanut is a nutritive food with plenty of sources throughout the world. Its annual global production exceeds 40 million metric tons. At the same time, millions of tons of peanut shells are discarded every year.19,20 If these peanut shells can be reused, it would not only be good for the environment but also be beneficial to develop new applications for modern devices, such as energy storage devices. Many biomasses were adopted as starting materials of carbon sources,21−29 such as kelp,24 tong cao pith, molasses,25 bamboo leaf,26−28 and bodhi leaf.29 Among them, kelp, tong cao pith, and molasses provided functional groups for increasing the capacitance, while bamboo leaf and bodhi leaf provided a hierarchical structure to the electrode.

Herein, peanut shells are selected as the primitive material for fabricating supercapacitor electrodes. Through the chemical activation process under optimal conditions, the specific surface area of the material is considerably increased and thus the enhancement of capacitance is achieved.30,31 Graphite papers are used as current collectors by utilizing their high conductivity, stability, and flexibility can be utilized to improve the applicability of the electrode. To further enhance the performance of the supercapacitor, the electrode materials were doped with nitrogen supplied from soy protein; as a result, both the pseudocapacitance and conductivity of the electrode were improved.32,33 In addition, graphene oxide (GO) was added to the materials; as expected, the specific surface area and the electrochemical performance of the electrode were improved further by an accompanying synergistic effect,34 and the reduction in capacitance at a high scan rate was alleviated.

2. Results and Discussion

2.1. Material Characterization and Electrochemical Evaluation of the AP Materials

Scanning electron microscopy (SEM) was performed to examine the morphology of the samples synthesized with different activation conditions. Figure 1a–e shows the SEM results of CP, AP-700-imp, AP-800-imp, AP-900-imp, and AP-800-phy samples, respectively. As show in Figure 1a, the surface of CP is smooth because it was simply subjected to carbonization without further treatment. The flat surface has a low specific surface area, which is detrimental to the energy storage of the capacitor. In Figure 1b–e, we can observe that the samples have porous surfaces because they were subjected to the carbonization and activation processes. A high roughness of the surface morphology increases the specific surface area of the material and thus contributes to the capacitance. Additionally, the morphologies of AP-700-imp, AP-800-imp, and AP-900-imp samples are totally different from each other, while AP-800-phy is somewhat similar to AP-800-imp. This shows that the different activation temperatures are the key factor causing the difference in surface morphology. During the KOH activation process, the following chemical reactions occurred35,36

2.1. 1
2.1. 2
2.1. 3
2.1. 4
2.1. 5

These chemical reaction equations describe how KOH reacts with carbon, which led to the porous structure and generated products such as potassium carbonate (K2CO3), potassium oxide (K2O), carbon dioxide (CO2), etc. Afterward, these three products kept reacting with carbon to generate more pores. The reaction described in eq 1 can spontaneously occur when the temperature is over 570 °C. However, the reaction described in eqs 2, 4, and 5 can only proceed when the temperature is over 700 °C.35,36 Because AP-700-imp samples did not go through the whole activation process, therefore, they kept a relatively smooth surface. Nevertheless, the morphology of the AP-900-imp sample cannot be explained simply based on the participating reactions. To find better explanations, we analyzed the Raman spectra and X-ray diffraction (XRD) patterns of the samples synthesized under different activation temperatures.

Figure 1.

Figure 1

Open in a new tab

SEM images of (a) CP, (b) AP-700-imp, (c) AP-800-imp, (d) AP-900-imp, and (e) AP-800-phy.

Figure 2a shows the Raman spectra of AP-700-imp, AP-800-imp, and AP-900-imp samples; all of them exhibit a D band (disorder band) at ∼1350 cm–1 and a G band (graphite band) at ∼1582 cm–1, which are the common features of graphite-based materials. The D band originates from the structural disorders, defects, or edges in graphite, while the G band is related to the in-phase vibrations of sp2 carbon atoms in the basal plane of graphite. The level of graphitization can be examined from the intensity ratio of the D to G band (ID/IG). A lower ID/IG value indicates a higher graphitization level, which indicates lesser disorders or defects in the samples.37−39 AP-900-imp with AP-700-imp, Figure 2a depicts the Raman spectrum of the AP-900-imp sample and shows the lowest ID/IG value, implying that the graphitization degree of the AP-900-imp sample is increased after being subjected to a relatively high temperature of 900 °C.

Figure 2.

Figure 2

Open in a new tab

(a) Raman spectra and (b) XRD patterns for the samples with different activation temperatures.

Figure 2b shows the XRD patterns of AP-700-imp, AP-800-imp, and AP-900-imp samples. AP-700-imp and AP-800-imp samples do not exhibit obvious peaks indicating amorphous structures, while the diffraction pattern of the AP-900-imp sample depicts the characteristic peaks of graphite at ∼26° (002) and ∼42° (100), demonstrating graphitization of the AP-900-imp sample owing to higher processing temperature. In short, both the Raman spectra and the XRD patterns show that AP-900-imp was graphitized at an activation temperature of 900 °C, which would restructure the porous surface and even cause the pore to collapse, thereby forming the morphology as shown in Figure 1d.

Figures 3 and S1 show the isotherm plots of the samples, demonstrating that all of the samples belong to Type I of the International Union of Pure and Applied Chemistry (IUPAC) with well-defined plateaus. Type I represents the samples possessing a micropore structure.40,41

Figure 3.

Figure 3

Open in a new tab

Isotherm plots of the samples.

Notably, the isotherm of AP-900-imp shows an evident hysteresis loop, indicating that AP-900-imp possesses a certain amount of mesopores as well.42,43 This result matches with the morphology shown in Figure 1d. Table 1 summarizes the pore volume and the Brunauer–Emmett–Teller (BET) specific surface area of all of the samples. SBET is 1276 m2/g for AP-900-imp, 1852 m2/g for AP-800-imp, 452 m2/g for AP-700-imp, and 911 m2/g for AP-800-phy. The optimal condition for the KOH activation process is found to be the impregnation method for obtaining a uniform mixture followed by the activation process at 800 °C.

Table 1. Surface Area and Pore Structure of AP-X-Ya.

  Vmicro (cm3/g) Vmeso (cm3/g) Vmeso/Vmicro SBET (m2/g)
AP-900-imp 0.582 0.134 0.230 1276
AP-800-imp 0.735 0.063 0.090 1852
AP-700-imp 0.132 0.037 0.028 452
AP-800-phy 0.387 0.067 0.170 911
Open in a new tab
a

Vmicro: micropore volume, Vmeso: mesopore volume, and SBET: specific surface area.

Figure 4a shows the comparison of cyclic voltammetry (CV) curves for the samples at a scan rate of 10 mV/s. The results indicate that the AP-800-imp sample has the highest Csp of 181.4 F/g. Figure S2 shows the CV curve of each sample at different scan rates that varied from 10 to 100 mV/s. All curves exhibit a nearly ideal rectangular shape, indicating excellent reversibility during the charge/discharge processes as for all of the samples. Figure 4b compares the galvanostatic charge/discharge (GCD) measurements of the samples at a current density of 0.4 A/g. Again, the AP-800-imp sample shows the longest discharge time with the highest Csp of 253.9 F/g. Figure S3 shows the results of GCD measurements for each sample at different scan rates that varied from 0.4 to 3.2 A/g. Both curves present symmetric isosceles triangles, which indicate excellent capacitive behavior.

Figure 4.

Figure 4

Open in a new tab

Comparison of (a) CV curves and (b) GCD curves. (c) Nyquist plot of AP-800-imp. (d) Comparison of Csp for the samples.

Figure 4c shows that the electrochemical impedance spectroscopy (EIS) plot of AP-800-imp depicts a vertical line in the low-frequency region, indicating an ideal capacitive behavior owing to rapid diffusion in the electrolyte and adsorption at the electrode/electrolyte interface. In the high-frequency region, a Z′ intercept, corresponding to the equivalent series resistance (ESR) and also known as the total Ohmic resistance or the internal resistance,44,45 of 1.27 Ω is obtained. ESR is defined as the sum of the contact resistance at the interface of the electrode/current collector, the bulk electrolyte resistance, and the electrode resistance.46

There is no apparent semicircle in the high-frequency region, implying that the charge-transfer resistance (Rct) is substantially low. Rct is defined as the sum of the electrolyte resistance in the porous structure of the electrode, the electrode resistance, and the contact resistance at the interface of the electrode/current collector.46 Apparently, AP-800-imp exhibits the lowest ESR and Rct, matching the results of CV and GCD measurements.

Despite the high Csp at a low scan rate, the AP-800-imp sample exhibits poor Csp at a high scan rate. From Figure 4d, one can clearly observe that the Csp of the AP-800-imp is worse than that of the AP-900-imp at 100 mV/s scan rate. It is probably due to the fact that the electron did not have enough time to transport from the deep interior of the sample to the collector to store energy at a high scan rate. In addition, based on the data shown in Table 1, it depicts that AP-800-imp lacks larger pores to enhance the transportation of the electrolyte into the sample. On the contrary, the AP-900-imp has enough mesopores to provide effective paths and it assists the transportation of the electrolyte into the sample. Therefore, the strategy to improve the capacitance under a high scan rate would be to tune the porous structure and improve the electrical conductivity.

2.2. Further Enhancing the Electrochemical Performance of Porous Bioactive Carbon Materials

To improve the low performance of the electrode at a high scan rate, soy protein was added to the peanut shells before the carbonization process, while the activation condition remained the same. Figures 5a and S4 show the results of the CV tests, and Figures 5b and S5 show the results of the GCD measurements. Both results show that AP-800-imp-5 exhibits the best capacitance of 207.9 F/g at a scan rate of 10 mV/s and 284.1 F/g at a current density of 0.4 A/g. Table S1 shows a comparison between the capacitance of the samples tested under different scan rates. From the data shown in Table S2 and Figure S6, it is found that the mesopore volume of the samples slightly increases with the amount of the introduced soy protein. Meanwhile, the micropore volume decreases, which causes a reduction of the BET specific surface area. In spite of the lower surface area, soy protein introduces nitrogen doping and, as a result, enhances the capacitance.

Figure 5.

Figure 5

Open in a new tab

Comparison of (a) CV curves and (b) GCD curves for the samples with different amounts of soy protein added.

To investigate the generated functional group via nitrogen doping, the X-ray photoelectron spectroscopy (XPS) test was performed on AP-800-imp-5-1.5 (Figure 6). It is observed that the surface is composed of carbon, nitrogen, and oxygen in the ratio of 84.9:13.5:1.6. The three peaks in the N 1s spectrum, as shown in Figure 6a, correspond to the three types of N-species in the graphite lattice, including pyrrolic-N (N5) at 400.0 eV, pyridinic-N (N6) at 398.2 eV, and quaternary-N (NQ) at 401.0 eV.47−49 The presence of these three groups improves electron transfer in the electrolyte to enhance pseudocapacitance and also enhances the electron mobility.50 The C 1s spectrum was deconvoluted into three peaks, including C–C at 284.5 eV, C–N at 285.2 eV, and C–O at 286.0 eV. The presence of C–N bonds indicates successful nitrogen doping of the graphite lattice.47−49

Figure 6.

Figure 6

Open in a new tab

(a) N 1s and (b) C 1s XPS spectra of AP-800-imp-5-1.5.

To further improve the performance of the electrode, GO was also added to the peanut shells before carbonization and subsequently treated by the same activation process as for the AP-800-imp-5 sample. Figure S7 shows the Raman spectrum, the XRD pattern, and atomic force microscopy (AFM) image of the sample containing GO. As can be seen, the Raman spectrum and the XRD pattern exhibit characteristic features of GO, and the AFM image illustrates the thickness of the single-layer GO flask to be 1.06 nm. Figures 7a and S8 show the results of CV tests for the samples having different amounts of GO, while Figures 7b and S9 depict the results of GCD measurements. Both results show that AP-800-imp-5-1.5 shows the best capacitance of 214.0 F/g at a scan rate of 10 mV/s and 289.4 F/g at a current density of 0.4 A/g. Based on the data shown in Table 2 and Figure S10, it is found that the mesopore volume dramatically increases with GO. Among the samples, AP-800-imp-5-1.5 has a certain amount of mesopores to assist transportation of the electrolyte into the electrode; meanwhile, the micropore volume has not been reduced significantly. As a result, the AP-800-imp-5-1.5 sample shows the best electrochemical performance.

Figure 7.

Figure 7

Open in a new tab

Comparison of (a) CV curves and (b) GCD curves for the samples with different amounts of GO added.

Table 2. Surface Area and Pore Structure of AP-800-imp-5-Ga.

  Vmicro (cm3/g) Vmeso (cm3/g) Vmeso/Vmicro SBET (m2/g)
AP-800-imp-5-0 0.518 0.096 0.190 1263
AP-800-imp-5-1.5 0.501 0.296 0.590 1691
AP-800-imp-5-3 0.407 0.396 0.970 1503
Open in a new tab
a

Vmicro: micropore volume, Vmeso: mesopore volume, and SBET: specific surface area.

Figure 8a and Table S3 compare the Csp of samples under different scan rates. They show excellent capacitance for AP-800-5-1.5, regardless of the scan rates. Figure 8b shows that, by adding the soy protein, the resistance of AP-800-imp-5 is significantly reduced from 1.27 to 0.49 Ω due to the presence of more free electrons. Furthermore, by adding a proper amount of GO, the resistance of AP-800-imp-5-1.5 is further slightly reduced from 0.49 to 0.43 Ω owing to better conductivity of the rGO, which was reduced from GO during the carbonization process under elevated temperature. Figure 8a,b proves that the problem of poor performance under a high scan rate was overcome with these strategies. In addition, we also tested the electroactive surface area (ESA), as shown in Figure S11.

Figure 8.

Figure 8

Open in a new tab

Comparison of (a) Csp, (b) Nyquist plot for the samples, and (c) the electrochemical mechanism.

The best sample, AP-800-imp-5-1.5, has a high ESA value, which is 3 times higher than that of CP, indicating that it possesses a hierarchical structure and utilizes the holes effectively. Figure 9a shows the AP-800-imp-5-1.5 electrode having a great cycling performance, which retains 92.8% of its initial capacitance after the test for 5000 cycles. Figure 9b shows the Ragone plot of the AP-800-imp-5-1.5 electrode and the comparison of our results with others fabricated using different biomasses and processes made.51−54 The result reveals that the energy density reaches as high as 25.72 Wh/kg with a power density of 160.0 W/kg at 0.4 A/g. In addition, another measurement shows that an energy density of 20.55 Wh/kg with a power density of 1280 W/kg can be attained when the test is performed under a current density of 3.2 A/g.

Figure 9.

Figure 9

Open in a new tab

(a) Cycling performance and (b) Ragone plot of AP-800-imp-5-1.5.

2.3. Assembling and the Performance Tests of the Flexible Supercapacitor

Using the AP-800-imp-5-1.5 material as the electrode, PVA/H2SO4 as the electrolyte, and a nonwoven fabric as the separator, we assembled a flexible supercapacitor and tested its electrochemical performance, as shown in Figures S12 and 10. Since the gel electrolyte has a poor conductivity (usually less than 10 mS/cm) and low ion mobility as compared with the liquid electrolyte, making the charge and discharge processes slow, and increasing the ESR, it is unable to instantly perform a complete capacitive energy storage process.55−57 Therefore, the capacitance is only 10.75 F/g at a scan rate of 10 mV/s. Figure 10a shows the bending test of the flexible supercapacitor. It can be seen that when bent from 0 to 90°, the structure of the electrode is changed due to the applied bending stress over the material, resulting in a slight change in the cyclic voltammetry curve. When bent to 135 and 180°, reverse-bended to −90°, or re-bended back to 0′°, the areas of the CV curves are almost the same, which implies that the flexible supercapacitor can be retained and is stable at different bending angles. Figure 10b shows the retention tests and light-emitting diode (LED) illumination test (inset) powered by three flexible supercapacitors arranged in series. The result shows that after 2000 cycles, the flexible supercapacitor can retain about 82.9% of its initial capacitance. When the flexible supercapacitor is charged for 10 s, the red LED can be illuminated for up to 165 s, indicating that the capacitor has good energy storage performance.

Figure 10.

Figure 10

Open in a new tab

(a) Bending test, (b) cycling performance, and (inset) LED illumination test of the flexible supercapacitor.

3. Conclusions

In summary, we have synthesized the high-performance electrodes using the biomass converted from peanut shells as the primitive material. With the optimal activation process and the synergistic effect of soy protein and GO, AP-800-imp-5-1.5 exhibits a high Csp of 289.4 F/g at a current density of 0.4 A/g and 214.0 F/g at a scan rate of 10 mV/s. Even at a scan rate as high as 100 mV/s, a Csp of 131.1 F/g can be attained. It means that the problem of poor performance under a high scanning rate has been overcome. In addition, the flexible supercapacitor retains its performance even under bending, and a flexible supercapacitor set containing three supercapacitors arranged in series can illuminate the LED for up to 165 s after being charged for 10 s.

4. Experimental Section

4.1. Materials

The materials and chemicals used in this work are of experimental grade and were used as purchased. The peanuts were purchased from a local supermarket.

4.2. Sample Preparation

In this work, the peanut shells were used as the carbon source of the electrode material. They were washed several times with deionized (DI) water to remove unnecessary impurities and then placed in an oven at 90 °C for 24 h before the subsequent carbonization process.58 Afterward, they were ground to a fine powder in a pulverizer at 30 000 rpm.

4.2.1. Preparation of the Carbonized Peanut Shell Powder

A quartz boat filled with the peanut shell powder was placed in a tube furnace for carbonization. Argon gas with a flow rate of 500 sccm was channeled into the furnace and vacuumed below 10–2 mbar. The purging processes were repeated three times to eliminate the residual oxygen in the furnace as much as possible. The peanut shell powder was carbonized at 800 °C for 3 h under an argon atmosphere at a flow rate of 500 sccm. The product was further ground into a fine powder by a ball mill machine at 250 rpm and the product was designated as CP.

4.2.2. Preparation of the Activated Peanut Shell Powder

A mixture of CP and KOH with a CP/KOH weight ratio of 1:4 was prepared via the physical method and the impregnation method. For the physical method, the mixture was physically stirred for 30 min. As for the impregnation method, KOH was first dissolved in an alcohol solution, and then the CP powder was added to the solution. Subsequently, the mixture was heated at 65 °C for 24 h until the alcohol solution was completely evaporated. The magnetic stirring was applied throughout the process for uniform mixing of KOH and CP.

The dried mixture was placed in a ceramic boat and activated at three different temperatures of 700, 800, and 900 °C for 3 h under an argon flowing atmosphere at a flow rate of 1000 sccm. Subsequently, the final product was ball-milled into a uniform powder and washed with 10 wt % HCl. For ensuring safety, the product was washed with DI water several times until a pH value of 7.0 was reached and was named as activated powder (AP). The final samples were designated as AP-X-Y, according to the activation temperature and mixing method. X stands for the activation temperatures (700, 800, and 900 °C) and Y represents the mixing methods (phy: physical method, imp: impregnation method).

4.2.3. Preparation of Graphene Oxide

GO was prepared by the modified Hummers method, which can be found elsewhere.59 In short, 1 g of 325 mesh graphite flakes was slowly added to 100 mL of concentrated sulfuric acid (H2SO4). The solution was kept in an ice bath, stirred with a magnet for 1 h, and then 4 g of potassium permanganate (KMnO4) was gradually added followed by stirring at 40 °C for 6 h. The solution was diluted with 50 mL of DI water under stirring for 1 h. Subsequently, 100 mL of DI water and 40 mL of hydrogen peroxide (H2O2) were slowly added; the processes were performed under stirring. Once the color of the solution changed from dark purple to brilliant yellow-brown, the solution was placed at room temperature for 12 h for GO precipitation. Finally, the solution was centrifuged and diluted with DI water several times until it became neutral. The precipitated GO was dried in a vacuum pumping system at room temperature.

4.2.4. Addition of Soy Protein and Graphene Oxide

In this work, the soy protein and GO were used for further improving the electrochemical performance of the electrode that was prepared from APs. Before the carbonization process, the peanut shell powder was mixed with different amounts of soy protein (0, 5, and 10 wt %) and GO (0, 1.5, and 3 wt %) were mixed via stirring for 30 min. Then, the mixture was activated with the same conditions as for AP-800-imp. The samples were named as AP-800-imp-S-G, where S and G indicate the weight percentages of soy protein (0, 5, and 10 wt %) and GO (0, 1.5, and 3 wt %) in the mixture, respectively.

4.3. Characterizations

The morphologies, microstructures, and compositions were characterized by X-ray diffractometer (XRD, Shimadzu XRD 6000), field emission scanning electron microscopy (FESEM, Hitachi-SU8010), energy-dispersive spectroscopy (EDS, Hitachi-SU8010), and X-ray photoelectron spectroscopy (XPS, ULVAC-PHI PHI 5000 Versaprobe II). The microstructures of the samples were examined by a Raman spectroscope (Raman, Horiba Jobin Yvon HR 800 UV) equipped with a laser wavelength of 632.8 nm. The nitrogen adsorption/desorption isotherms were measured using a porosimetry analyzer (Micromeritics Tristar II 3020). The specific surface areas of the samples were determined by using the Brunauer–Emmett–Teller (BET) method at 77 K. The micropore and mesopore volumes were analyzed using the Barrett–Joyner–Helenda (BJH) method based on the nitrogen isotherm data.

4.4. Electrochemical Evaluation

The electrochemical properties of the electrodes were evaluated with a three-electrode system in a 1 M H2SO4 aqueous electrolyte at room temperature. Pt wire and Ag/AgCl were used as counter and reference electrodes, respectively. The working electrode was prepared using the synthesized active material, poly(vinylidene difluoride) (PVDF), and conductive carbon black in a mass ratio of 7:1:2 as the primary materials. Subsequently, an appropriate amount of N-methyl-2-pyrrolidone (NMP) was adopted as the binder to prepare a slurry, which was coated on a graphite paper by the dipping method for electrode preparation.

Cyclic voltammetry (CV), galvanostatic charge/discharge (GCD), and electrochemical impedance spectroscopy (EIS) were performed by the Potentiostat/Galvanostat Electrochemical Instrument (Autolab PGSTAT30 & FRA2). The specific capacitance (Csp, F/g) of the electrodes can be calculated from the CV curve by using eq 66(60,61)

4.4. 6

where Vc – Va represents the applied voltage range (V), m is the mass of the active material (g), ν is the scan rate (V/s), and I is the response current (A). Additionally, the Csp can also be calculated via the GCD measurement by using eq 7(62)

4.4. 7

where ΔV = Vc – Va corresponding to the applied voltage range (V), I′ is the constant discharge current (A), Δt is the discharging time (s), and m is the mass of the active material (g).

The energy density (ED, Wh/kg) and power density (PD, W/kg) can be calculated based on eqs 8 and 9, respectively

4.4. 8
4.4. 9

where V is the voltage change during the discharge process (V) and Δt is the discharge time (s).

The electroactive surface area (ESA) can be calculated from the CV test using the electrolyte containing 20 mM of K3Fe(CN)6 and 0.2 M of KCl at different scanning rates. According to the Randle–Sevcik equation, ESA can be calculated using eq 10(59,63)

4.4. 10

where IP represents the peak current (A), A is the ESA (cm2), D corresponds to the diffusion coefficient of [Fe(CN)6]3–/4– in the KCl solution (6.70 × 10–6 cm2/s), n is the number of electrons transferred in the redox event (usually 1), s is the scan rate (V/s), and C is the solvent concentration (mol/cm3).

Acknowledgments

The authors are thankful for the funding support from the Ministry of Science and Technology, Taiwan, under the contract MOST 107-2221-E-007-008-MY3.

Supporting Information Available

The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsomega.0c00966.

  • Isotherm plot curves of the AP powder (Figure S1); CV curves and GCD curves of AP-800-phy, AP-700-imp, AP-800-imp, and AP-900-imp (Figures S2 and S3); CV curves, GCD curves, and isotherm plot curves of AP-800-imp-0, AP-800-imp-5, and AP-800-imp-10 (Figures S4–S6); Raman spectra, XRD pattern, and AFM image of graphene oxide (Figure S7); CV curves, GCD curves, and isotherm plot curves of AP-800-imp-5-0, AP-800-imp-5-1.5, and AP-800-imp-5-3 (Figures S8–S10); ESA results of CP, AP-800-imp, and AP-800-imp-5-1.5 (Figure S11); CV curve, GCD curve, and EIS of the flexible supercapacitor (Figure S12); specific capacitances and surface area of the samples with different amounts of soy protein added (Tables S1 and S2); and specific capacitances of the samples with different amounts of GO added (Table S3) (PDF)

The authors declare no competing financial interest.

Supplementary Material

ao0c00966_si_001.pdf (956.1KB, pdf)

References

  1. Sulaiman N.; Hannan M. A.; Mohamed A.; Majlan E. H.; Wan Daud W. R. A review on energy management system for fuel cell hybrid electric vehicle: Issues and challenges. Renewable Sustainable Energy Rev. 2015, 52, 802–814. 10.1016/j.rser.2015.07.132. [DOI] [Google Scholar]
  2. Zhang L.; Hu X.; Wang Z.; Sun F.; Dorrell D. G. A review of supercapacitor modeling, estimation, and applications: A control/management perspective. Renewable Sustainable Energy Rev. 2018, 81, 1868–1878. 10.1016/j.rser.2017.05.283. [DOI] [Google Scholar]
  3. González A.; Goikolea E.; Barrena J. A.; Mysyk R. Review on supercapacitors: Technologies and materials. Renewable Sustainable Energy Rev. 2016, 58, 1189–1206. 10.1016/j.rser.2015.12.249. [DOI] [Google Scholar]
  4. Kim B. K.; Sy S.; Yu A.; Zhang J.. Electrochemical Supercapacitors for Energy Storage and Conversion. In Handbook of Clean Energy Systems; John Wiley & Sons Ltd., 2015; pp 1–25. [Google Scholar]
  5. Jost K.; Dion G.; Gogotsi Y. Textile energy storage in perspective. J. Mater. Chem. A 2014, 2, 10776–10787. 10.1039/c4ta00203b. [DOI] [Google Scholar]
  6. Kang J.; Wen J.; Jayaram S. H.; Yu A.; Wang X. Development of an equivalent circuit model for electrochemical double layer capacitors (EDLCs) with distinct electrolytes. Electrochim. Acta 2014, 115, 587–598. 10.1016/j.electacta.2013.11.002. [DOI] [Google Scholar]
  7. Chapman D. L. LI. A contribution to the theory of electrocapillarity. London, Edinburgh Dublin Philos. Mag. J. Sci. 1913, 25, 475–481. 10.1080/14786440408634187. [DOI] [Google Scholar]
  8. Ke Q.; Wang J. Graphene-based materials for supercapacitor electrodes – A review. J. Materiomics 2016, 2, 37–54. 10.1016/j.jmat.2016.01.001. [DOI] [Google Scholar]
  9. Chmiola J.; Largeot C.; Taberna P. L.; Simon P.; Gogotsi Y. Monolithic Carbide-Derived Carbon Films for Micro-Supercapacitors. Science 2010, 328, 480–483. 10.1126/science.1184126. [DOI] [PubMed] [Google Scholar]
  10. Wan K.; Liu S.; Zhang C.; Li L.; Zhao Z.; Liu T.; Xie Y. Supramolecular Assembly of 1D Pristine Carbon Nanotubes and 2D Graphene Oxides into Macroscopic All-Carbon Hybrid Sponges for High-Energy-Density Supercapacitors. ChemNanoMat 2017, 3, 447–453. 10.1002/cnma.201700037. [DOI] [Google Scholar]
  11. Kang D.; Liu Q.; Gu J.; Su Y.; Zhang W.; Zhang D. “Egg-Box”-Assisted Fabrication of Porous Carbon with Small Mesopores for High-Rate Electric Double Layer Capacitors. ACS Nano 2015, 9, 11225–11233. 10.1021/acsnano.5b04821. [DOI] [PubMed] [Google Scholar]
  12. Chang B.; Guo Y.; Li Y.; Yin H.; Zhang S.; Yang B.; Dong X. Graphitized hierarchical porous carbon nanospheres: simultaneous activation/graphitization and superior supercapacitance performance. J. Mater. Chem. A 2015, 3, 9565–9577. 10.1039/C5TA00867K. [DOI] [Google Scholar]
  13. Fuertes A. B.; Sevilla M. Hierarchical microporous/mesoporous carbon nanosheets for high-performance supercapacitors. ACS Appl. Mater. Interfaces 2015, 7, 4344–4353. 10.1021/am508794f. [DOI] [PubMed] [Google Scholar]
  14. Qiu Z.; Wang Y.; Bi X.; Zhou T.; Zhou J.; Zhao J.; Miao Z.; Yi W.; Fu P.; Zhuo S. Biochar-based carbons with hierarchical micro-meso-macro porosity for high rate and long cycle life supercapacitors. J. Power Sources 2018, 376, 82–90. 10.1016/j.jpowsour.2017.11.077. [DOI] [Google Scholar]
  15. Liu X.; Mi R.; Yuan L.; Yang F.; Fu Z.; Wang C.; Tang Y. Nitrogen-Doped Multi-Scale Porous Carbon for High Voltage Aqueous Supercapacitors. Front. Chem. 2018, 6, 475 10.3389/fchem.2018.00475. [DOI] [PMC free article] [PubMed] [Google Scholar]
  16. Chen J.; Xu J.; Zhou S.; Zhao N.; Wong C. Nitrogen-doped hierarchically porous carbon foam: a free-standing electrode and mechanical support for high-performance supercapacitors. Nano Energy 2016, 25, 193–202. 10.1016/j.nanoen.2016.04.037. [DOI] [Google Scholar]
  17. Guo D.; Shibuya R.; Akiba C.; Saji S.; Kondo T.; Nakamura J. Active sites of nitrogen-doped carbon materials for oxygen reduction reaction clarified using model catalysts. Science 2016, 351, 361–365. 10.1126/science.aad0832. [DOI] [PubMed] [Google Scholar]
  18. Jeong H. M.; Lee J. W.; Shin W. H.; Choi Y. J.; Shin H. J.; Kang J. K.; Choi J. W. Nitrogen-doped graphene for high-performance ultracapacitors and the importance of nitrogen-doped sites at basal planes. Nano Lett. 2011, 11, 2472–2477. 10.1021/nl2009058. [DOI] [PubMed] [Google Scholar]
  19. Ding J.; Wang H.; Li Z.; Cui K.; Karpuzov D.; Tan X.; Kohandehghan A.; Mitlin D. Peanut shell hybrid sodium ion capacitor with extreme energy–power rivals lithium ion capacitors. Energy Environ. Sci. 2015, 8, 941–955. 10.1039/C4EE02986K. [DOI] [Google Scholar]
  20. Lorenzo J. M.; Munekata P. E. S.; Sant’Ana A. S.; Carvalho R. B.; Barba F. J.; Toldrá F.; Mora L.; Trindade M. A. Main characteristics of peanut skin and its role for the preservation of meat products. Trends Food Sci. Technol. 2018, 77, 1–10. 10.1016/j.tifs.2018.04.007. [DOI] [Google Scholar]
  21. Cha J. S.; Park S. H.; Jung S. C.; Ryu C.; Jeon J. K.; Shin M. C.; Park Y. K. Production and utilization of biochar: A review. J. Ind. Eng. Chem. 2016, 40, 1–15. 10.1016/j.jiec.2016.06.002. [DOI] [Google Scholar]
  22. Gao Y. P.; Zhai Z. B.; Huang K. J.; Zhang Y. Y. Energy storage applications of biomass-derived carbon materials: batteries and supercapacitors. New J. Chem. 2017, 41, 11456–11470. 10.1039/C7NJ02580G. [DOI] [Google Scholar]
  23. Volk T.; Abrahamson L.; White E.; Neuhauser E.; Gray E.; Demeter C.; Lindsey C.; Jarnefeld J.; Aneshansley D.; Pellerin R. In Developing a Willow Biomass Crop Enterprise for Bioenergy and Bioproducts in the United States, Proceedings of Bioenergy, 2000.
  24. Zhang Y.; Jiang H.; Wang Q.; Zheng J.; Meng C. Kelp-derived three-dimensional hierarchical porous N, O-doped carbon for flexible solid-state symmetrical supercapacitors with excellent performance. Appl. Surf. Sci. 2018, 447, 876–885. 10.1016/j.apsusc.2018.04.061. [DOI] [Google Scholar]
  25. Hsiao C.; Lee C.; Tai N. Biomass-derived three-dimensional carbon framework for a flexible fibrous supercapacitor and its application as a wearable smart textile. RSC Adv. 2020, 10, 6960–6972. 10.1039/C9RA07441D. [DOI] [PMC free article] [PubMed] [Google Scholar]
  26. Zhang Y.; Wang C.; Jiang H.; Wang Q.; Zheng J.; Meng C. Cobalt-nickel silicate hydroxide on amorphous carbon derived from bamboo leaves for hybrid supercapacitors. Chem. Eng. J. 2019, 375, 121938 10.1016/j.cej.2019.121938. [DOI] [Google Scholar]
  27. Zhang Y.; Jiang H.; Wang Q.; Meng C. In-situ hydrothermal growth of Zn4Si2O7(OH)2·H2O anchored on 3D N, S-enriched carbon derived from plant biomass for flexible solid-state asymmetrical supercapacitors. Chem. Eng. J. 2018, 352, 519–529. 10.1016/j.cej.2018.07.055. [DOI] [Google Scholar]
  28. Wang Q.; Zhang Y.; Jiang H.; Meng C. In-situ grown manganese silicate from biomass-derived heteroatom-doped porous carbon for supercapacitors with high performance. J. Colloid Interface Sci. 2019, 534, 142–155. 10.1016/j.jcis.2018.09.026. [DOI] [PubMed] [Google Scholar]
  29. Nguyen D. D.; Hsiao C. H.; Su T. Y.; Hsieh P. Y.; Chen Y. L.; Chueh Y. L.; Lee C. Y.; Tai N. H. Bioinspired networks consisting of spongy carbon wrapped by graphene sheath for flexible transparent supercapacitors. Commun. Chem. 2019, 2, 137 10.1038/s42004-019-0238-9. [DOI] [Google Scholar]
  30. Abioye A. M.; Ani F. N. Recent development in the production of activated carbon electrodes from agricultural waste biomass for supercapacitors: a review. Renewable Sustainable Energy Rev. 2015, 52, 1282–1293. 10.1016/j.rser.2015.07.129. [DOI] [Google Scholar]
  31. Feng H.; Hu H.; Dong H.; Xiao Y.; Cai Y.; Lei B.; Liu Y.; Zheng M. Hierarchical structured carbon derived from bagasse wastes: a simple and efficient synthesis route and its improved electrochemical properties for high-performance supercapacitors. J. Power Sources 2016, 302, 164–173. 10.1016/j.jpowsour.2015.10.063. [DOI] [Google Scholar]
  32. Raymundo-Piñero E.; Cadek M.; Béguin F. Tuning Carbon Materials for Supercapacitors by Direct Pyrolysis of Seaweeds. Adv. Funct. Mater. 2009, 19, 1032–1039. 10.1002/adfm.200801057. [DOI] [Google Scholar]
  33. Li B.; Dai F.; Xiao Q.; Yang L.; Shen J.; Zhang C.; Cai M. Nitrogen-doped activated carbon for a high energy hybrid supercapacitor. Energy Environ. Sci. 2016, 9, 102–106. 10.1039/C5EE03149D. [DOI] [Google Scholar]
  34. Cheng Y.; Lu S.; Zhang H.; Varanasi C. V.; Liu J. Synergistic effects from graphene and carbon nanotubes enable flexible and robust electrodes for high-performance supercapacitors. Nano Lett. 2012, 12, 4206–4211. 10.1021/nl301804c. [DOI] [PubMed] [Google Scholar]
  35. Chen K.; Xue D. Multiple Functional Biomass-Derived Activated Carbon Materials for Aqueous Supercapacitors, Lithium-Ion Capacitors and Lithium-Sulfur Batteries. Chin. J. Chem. 2017, 35, 861–866. 10.1002/cjoc.201600785. [DOI] [Google Scholar]
  36. Wang J.; Kaskel S. KOH activation of carbon-based materials for energy storage. J. Mater. Chem. 2012, 22, 23710–23725. 10.1039/c2jm34066f. [DOI] [Google Scholar]
  37. Ribeiro-Soares J.; Oliveros M.; Garin C.; David M.; Martins L.; Almeida C.; Martins-Ferreira E.; Takai K.; Enoki T.; Magalhães-Paniago R.; et al. Structural analysis of polycrystalline graphene systems by Raman spectroscopy. Carbon 2015, 95, 646–652. 10.1016/j.carbon.2015.08.020. [DOI] [Google Scholar]
  38. Ferrari A. C. Raman spectroscopy of graphene and graphite: disorder, electron–phonon coupling, doping and nonadiabatic effects. Solid State Commun. 2007, 143, 47–57. 10.1016/j.ssc.2007.03.052. [DOI] [Google Scholar]
  39. Beams R.; Cançado L. G.; Novotny L. J. Raman characterization of defects and dopants in graphene. J. Phys.: Condens. Matter 2015, 27, 083002 10.1088/0953-8984/27/8/083002. [DOI] [PubMed] [Google Scholar]
  40. Grosman A.; Ortega C. Capillary condensation in porous materials. Hysteresis and interaction mechanism without pore blocking/percolation process. Langmuir 2008, 24, 3977–3986. 10.1021/la703978v. [DOI] [PubMed] [Google Scholar]
  41. Brunauer S.; Emmett P. H.; Teller E. Adsorption of gases in multimolecular layers. J. Am. Chem. Soc. 1938, 60, 309–319. 10.1021/ja01269a023. [DOI] [Google Scholar]
  42. Zhang Y.; Shao D.; Yan J.; Jia X.; Li Y.; Yu P.; Zhang T. The pore size distribution and its relationship with shale gas capacity in organic-rich mudstone of Wufeng-Longmaxi Formations, Sichuan Basin, China. J. Nat. Gas Geosci. 2016, 1, 213–220. 10.1016/j.jnggs.2016.08.002. [DOI] [Google Scholar]
  43. Thommes M.; Kaneko K.; Neimark A. V.; Olivier J. P.; Rodriguez-Reinoso F.; Rouquerol J.; Sing K. Physisorption of gases, with special reference to the evaluation of surface area and pore size distribution (IUPAC Technical Report). Pure Appl. Chem. 2015, 87, 1051–1069. 10.1515/pac-2014-1117. [DOI] [Google Scholar]
  44. Taberna P. L.; Simon P.; Fauvarque J. F. Electrochemical characteristics and impedance spectroscopy studies of carbon-carbon supercapacitors. J. Electrochem. Soc. 2003, 150, A292–A300. 10.1149/1.1543948. [DOI] [Google Scholar]
  45. Xu P.; Gu T.; Cao Z.; Wei B.; Yu J.; Li F.; Byun J. H.; Lu W.; Li Q.; Chou T. Carbon Nanotube Fiber Based Stretchable Wire-Shaped Supercapacitors. Adv. Energy Mater. 2014, 4, 1300759 10.1002/aenm.201300759. [DOI] [Google Scholar]
  46. Mei B.-A.; Munteshari O.; Lau J.; Dunn B.; Pilon L. Physical interpretations of Nyquist plots for EDLC electrodes and devices. J. Phys. Chem. C 2018, 122, 194–206. 10.1021/acs.jpcc.7b10582. [DOI] [Google Scholar]
  47. Fan W.; Xia Y.-Y.; Tjiu W. W.; Pallathadka P. K.; He C.; Liu T. Nitrogen-doped graphene hollow nanospheres as novel electrode materials for supercapacitor applications. J. Power Sources 2013, 243, 973–981. 10.1016/j.jpowsour.2013.05.184. [DOI] [Google Scholar]
  48. Han J.; Xu G.; Ding B.; Pan J.; Dou H.; MacFarlane D. Porous nitrogen-doped hollow carbon spheres derived from polyaniline for high performance supercapacitors. J. Mater. Chem. A 2014, 2, 5352–5357. 10.1039/C3TA15271E. [DOI] [Google Scholar]
  49. Xie Q.; Bao R.; Zheng A.; Zhang Y.; Wu S.; Xie C.; Zhao P. Sustainable low-cost green electrodes with high volumetric capacitance for aqueous symmetric supercapacitors with high energy density. ACS Sustainable Chem. Eng. 2016, 4, 1422–1430. 10.1021/acssuschemeng.5b01417. [DOI] [Google Scholar]
  50. Hung C.-T.; Yu N.; Chen C.-T.; Wu P.-H.; Han X.; Kao Y.-S.; Liu T.-C.; Chu Y.; Deng F.; Zheng A.; Liu S.-B. Highly nitrogen-doped mesoscopic carbons as efficient metal-free electrocatalysts for oxygen reduction reactions. J. Mater. Chem. A 2014, 2, 20030–20037. 10.1039/C4TA04403G. [DOI] [Google Scholar]
  51. Teo E. Y. L.; Muniandy L.; Ng E.-P.; Adam F.; Mohamed A. R.; Jose R.; Chong K. High surface area activated carbon from rice husk as a high performance supercapacitor electrode. Electrochim. Acta 2016, 192, 110–119. 10.1016/j.electacta.2016.01.140. [DOI] [Google Scholar]
  52. Yang C. S.; Jang Y. S.; Jeong H. K. Bamboo-based activated carbon for supercapacitor applications. Curr. Appl. Phys. 2014, 14, 1616–1620. 10.1016/j.cap.2014.09.021. [DOI] [Google Scholar]
  53. Cheng B.-H.; Tian K.; Zeng R. J.; Jiang H. Preparation of high performance supercapacitor materials by fast pyrolysis of corn gluten meal waste. Sustainable Energy Fuels 2017, 1, 891–898. 10.1039/C7SE00029D. [DOI] [Google Scholar]
  54. Wang C. H.; Wen W. C.; Hsu H. C.; Yao B. Y. High-capacitance KOH-activated nitrogen-containing porous carbon material from waste coffee grounds in supercapacitor. Adv. Powder Technol. 2016, 27, 1387–1395. 10.1016/j.apt.2016.04.033. [DOI] [Google Scholar]
  55. Choudhury N. A.; Sampath S.; Shukla A. K. Hydrogel-polymer electrolytes for electrochemical capacitors: an overview. Energy Environ. Sci. 2009, 2, 55–67. 10.1039/B811217G. [DOI] [Google Scholar]
  56. Yu H.; Wu J.; Fan L.; Lin Y.; Xu K.; Tang Z.; Cheng C.; Tang S.; Lin J.; Huang M.; Lan Z. A novel redox-mediated gel polymer electrolyte for high-performance supercapacitor. J. Power Sources 2012, 198, 402–407. 10.1016/j.jpowsour.2011.09.110. [DOI] [Google Scholar]
  57. Senthilkumar S. T.; Selvan R. K.; Ponpandian N.; Melo J. S. Redox additive aqueous polymer gel electrolyte for an electric double layer capacitor. RSC Adv. 2012, 2, 8937–8940. 10.1039/c2ra21387g. [DOI] [Google Scholar]
  58. Han J.; Kim H. The reduction and control technology of tar during biomass gasification/pyrolysis: an overview. Renewable Sustainable Energy Rev. 2008, 12, 397–416. 10.1016/j.rser.2006.07.015. [DOI] [Google Scholar]
  59. Chu H. J.; Lee C. Y.; Tai N. H. Green preparation using black soybeans extract for graphene-based porous electrodes and their applications in supercapacitors. J. Power Sources 2016, 322, 31–39. 10.1016/j.jpowsour.2016.04.068. [DOI] [Google Scholar]
  60. Vijayakumar S.; Lee S. H.; Ryu K. S. Hierarchical CuCo2O4 nanobelts as a supercapacitor electrode with high areal and specific capacitance. Electrochim. Acta 2015, 182, 979–986. 10.1016/j.electacta.2015.10.021. [DOI] [Google Scholar]
  61. Yu D.; Qian Q.; Wei L.; Jiang W.; Goh K.; Wei J.; Zhang J.; Chen Y. Emergence of fiber supercapacitors. Chem. Soc. Rev. 2015, 44, 647–662. 10.1039/C4CS00286E. [DOI] [PubMed] [Google Scholar]
  62. Chen S.-M.; Ramachandran R.; Mani V.; Saraswathi R. Recent advancements in electrode materials for the high-performance electrochemical supercapacitors: a review. Int. J. Electrochem. Sci. 2014, 9, 4072–4085. [Google Scholar]
  63. Chu H. J.; Lee C. Y.; Tai N. H. Three-dimensional porous polyaniline/graphene-coated activated carbon fiber electrodes for supercapacitors. RSC Adv. 2016, 6, 111465–111471. 10.1039/C6RA20844D. [DOI] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Supplementary Materials

ao0c00966_si_001.pdf (956.1KB, pdf)

Articles from ACS Omega are provided here courtesy of American Chemical Society

RESOURCES