Magnesium-Based Metasurfaces for Dual-Function Switching between Dynamic Holography and Dynamic Color Display

Jianxiong Li †, Yiqin Chen ‡, Yueqiang Hu ‡,§, Huigao Duan ‡,§,*, Na Liu †,∥,⊥,*
PMCID: PMC7391991  PMID: 32267145

Abstract

graphic file with name nn0c01469_0005.jpg

Metasurface-based color display and holography have greatly advanced the state of the art display technologies. To further enrich the metasurface functionalities, recently a lot of research endeavors have been made to combine these two display functions within a single device. However, so far such metasurfaces have remained static and lack tunability once the devices are fabricated. In this work, we demonstrate a dynamic dual-function metasurface device at visible frequencies. It allows for switching between dynamic holography and dynamic color display, taking advantage of the reversible phase transition of magnesium through hydrogenation and dehydrogenation. Spatially arranged stepwise nanocavity pixels are employed to accurately control the amplitude and phase of light, enabling the generation of high-quality color prints and holograms. Our work represents a paradigm toward compact and multifunctional optical elements for future display technologies.

Keywords: metasurfaces, multifunction, holography, color display, magnesium

Metasurfaces, composed of spatially arranged metallic or dielectric antennas, enable a generation of optical elements with diverse capabilities.1−4 In particular, metasurfaces bring forward interesting design concepts to create light projection and display devices,5−10 which revolutionize the state of the art display technologies. Different from conventional color generation strategies using pigments and dyes, metasurfaces can yield vibrant and brilliant colors based on resonant excitations of optical antennas8,9,11,12 or nanocavities.13,14 The resulting color prints possess excellent stability, long durability, as well as high resolution and high data density, ideally suited for data storage and cryptography applications. Apart from color printing, high-quality holograms can also be produced based on metasurfaces.6,7,15−17 Such optical devices are ultrathin and ultracompact, constituting a milestone for modern display technologies.

Often, color printing and holography are separately implemented on metasurface devices. Very recently, research endeavors have been exerted to combine these two display functions within a single metasurface device.18−22 For example, monolithic stepwise nanocavity and holographic metasurface layers have been stacked together to achieve low-crosstalk color printing and full-color holography.19 In addition, single-layer dielectric metasurfaces have been employed to combine color printing and holography.18,20,22 However, these two strategies suffer from low efficiency and polarization sensitivity, respectively. More crucially, these metasurfaces are intrinsically static, as their optical functions are fixed once the devices are fabricated. This leaves out many opportunities that metasurfaces can offer.

In this work, we demonstrate a metasurface device, which allows for dual-function switching between dynamic holography and dynamic color display. The dynamic functionality is enabled by the phase-transition of magnesium (Mg), which can be transformed to magnesium hydride (MgH2) through hydrogen uptake.23−30 Importantly, MgH2 can be restored to Mg upon oxygen exposure. Such reversible metal to dielectric transitions are accompanied by dramatic optical response changes, which lay the foundation for building dynamic optical devices in the visible wavelength regime.

Results and Discussion

Figure 1a shows the schematic of the metasurface, which consists of spatially arranged stepwise pixels of subwavelength dimension. The metasurface can work as a holography device, creating high-quality holographic images. The metasurface can also work as a color display device, which produces microprints with vivid colors. These two display functions, dynamic holography and dynamic color display, can be readily switched through hydrogenation and dehydrogenation using hydrogen and oxygen, respectively. Figure 1b illustrates the fabrication process of the dual-function metasurface, which consists of stepwise pixels. Each pixel is a Fabry–Pérot (FP) nanocavity of subwavelength lateral dimension (500 nm). A silver (Ag, 100 nm) film and a silicon dioxide (SiO2, 190 nm) film are deposited on a silicon substrate, respectively. Here, the SiO2 layer is utilized to simplify the fabrication process, as it can contribute a common height for all the nanocavities. Stepwise pillars, made of hydrogen silsesquioxane (HSQ), are fabricated through multiple overlay procedures by electron beam lithography with the help of gold alignment markers. Subsequently, Mg (50 nm)/titanium (Ti, 2 nm)/palladium (Pd, 3 nm) films are successively deposited on the patterned sample.

Figure 1.

Figure 1

Open in a new tab

(a) Schematic illustration of the dual-function switching between dynamic holography and dynamic color display by hydrogenation (H2) and dehydrogenation (O2). (b) Fabrication process of the dual-function metasurface device.

To elucidate the working principle of the dual-function dynamic metasurface, Figure 2a shows the schematic diagrams of light propagation in a nanocavity pixel at the Mg and MgH2 states, respectively. At the Mg state, the metallic (Mg/Ti/Pd) capping layers efficiently reflect the incident light in the visible wavelength range. The phase of the reflected light can be modulated by varying the HSQ height (tHSQ). Four different HSQ heights, tHSQ = 0, 80, 160, and 240 nm (see black stars in Figure 2b) are employed to define the discrete phase levels spanning in a 2π range at 633 nm, while maintaining high reflectance. The light wavefronts can thus be well controlled to generate phase-only holograms in the far field. Upon hydrogen exposure, Pd catalyzes the dissociation of hydrogen molecules into hydrogen atoms, which diffuse through Ti into Mg. Mg undergoes the metal to dielectric transition to form MgH2. The incident light can then transmit through the capping layers and experience multiple reflections inside the FP nanocavity,31 which is formed between the capping layers (TiH2/PdH) and the bottom Ag mirror (see Figure 2a). In this case, the cavity height is defined by the total thickness of MgH2 + HSQ + SiO2. As shown in the upper panel in Figure 2b, in contrast to the nearly unity reflectance for different pixels before hydrogenation (black curve), the reflectance intensity exhibits a clear dependence on the cavity height after hydrogenation (red curve). In addition, the associated phase differences become much smaller among different pixels (see red stars in Figure 2b) when compared to those before hydrogenation.

Figure 2.

Figure 2

Open in a new tab

Working principle and experimental results of dynamic holography. (a) Schematic diagrams of light propagation in the metasurface device before and after hydrogenation. (b) Simulated reflectance spectra and phase delay with incident light at the wavelength of 633 nm at the Mg (black) and MgH2 (red) states. (c) Phase distribution for the hologram of a musical note. (d) SEM images of the metasurface sample. (e) Experimentally recorded switchable hologram through hydrogenation (H2) and dehydrogenation (O2).

A holographic image of a musical note is designed based on the Gerchberg–Saxton algorithm, and its phase distribution is shown in Figure 2c. Figure 2d presents the scanning electron microscopy (SEM) image of the fabricated sample. A tilted view is shown as inset in Figure 2d. A high-quality hologram of a musical note with 58% efficiency is experimentally reconstructed at 633 nm (see Figure 2e), demonstrating the precise control of the stepwise pixel heights and thus the phase distribution. The incident laser light is linearly polarized along one lateral side of the stepwise pixels in the experiment. However, the reconstruction of the hologram is independent of the light polarization. It is noteworthy that the hologram is detected at an 11.5° off-axis angle along only one direction. Upon hydrogen exposure (5% in nitrogen), Mg is transformed to MgH2. The phase differences among different stepwise pixels significantly decrease, resulting in the disappearance of the hologram. When MgH2 is restored to Mg upon oxygen exposure (10% in nitrogen), the hologram comes into existence again. As a result, the phase transition between Mg and MgH2 enables dynamic holography that can be reversibly switched on/off by loading O2/H2.

Meanwhile, through hydrogenation and dehydrogenation, the stepwise pixels also experience abrupt changes in reflectance, rendering dynamic color generation possible. As revealed by the optical microscopy images in Figure 3a, before hydrogenation the pixels with different HSQ heights exhibit blank color when interacting with unpolarized white light, owing to their high reflectance in the visible wavelength range. This is also confirmed by the measured reflectance spectra of these pixels, which are characterized by the black curves in Figure 3b. After hydrogenation, the formation of the sharp FP resonances greatly modulates the reflectance spectra (red curves), resulting in vibrant color generations from the stepwise pixels (see Figure 3a). The FP resonance positions are largely dependent on the cavity height. The resonances shift to longer wavelengths when the cavity height increases. Figure 3c,d presents the simulated reflectance spectra and the electric field distributions, respectively, for a representative case of tHSQ = 240 nm. The two reflectance peaks at 755 and 510 nm correspond to the formation of the second- and third-order FP resonances, respectively (see the red curves). After dehydrogenation, the stepwise pixels return to the blank color state again. Therefore, the phase transition between Mg and MgH2 also enables dynamic color display that can be reversibly switched on/off by loading H2/O2.

Figure 3.

Figure 3

Open in a new tab

Experimental results of dynamic color display. (a) Optical microscopy images and (b) experimental reflectance spectra of the stepwise pixels with different heights, tHSQ = 0, 80, 160, and 240 nm before and after hydrogenation. (c) Simulated reflectance spectra of the pixel (tHSQ = 240 nm) before and after hydrogenation. (d) Electric field distributions at the different FP resonances (see the black arrows in (c)) after hydrogenation. Third- and second-order FP resonances are excited at 510 and 755 nm, respectively.

The two different display functions, dynamic holography and dynamic color display, can be integrated within one metasurface device for dual-function switching. The SEM image of the dual-function metasurface is presented in Figure 4a. An enlarged view is shown as inset in the same figure. Stepwise pixels with four different HSQ heights are employed on the metasuface to create a color print ‘E = hν’ and a holographic image of the Max-Planck Society logo. Figure 4b shows the experimental results. Before hydrogenation, under illumination of white light the metasurface exhibits blank color, whereas at the incidence of laser light at 633 nm the metasurface generates a hologram of the Max-Planck Society logo. Upon hydrogen exposure, colors start to appear under white light illumination and a color print of ‘E = hν’ becomes vividly observable. The greenish background is due to the uniform superposition of the colors generated from the four sets of stepwise pixels that are used to construct the hologram. On the other side, after hydrogenation the hologram of the Max-Planck Society logo disappears. Subsequently, upon oxygen exposure, the color print vanishes and the hologram occurs again. Figure 4c shows the time evolutions of the gray level of the color print and the hologram intensity during hydrogenation and dehydrogenation, respectively. The evolution of the gray level, which indicates the pixel brightness changes, is obtained by tracking the averaged gray values of the area with ‘=’ pattern in Figure 4a. It decreases upon hydrogen exposure when the print transits from the blank state to the color state. It then increases upon oxygen exposure when returning from the color state to the blank state. Meanwhile, the light intensity of the hologram decreases and subsequently increases when the hologram is switched off/on through hydrogenation/dehydrogenation, respectively. All the experiments have been carried out at 80 °C to facilitate the switching upon H2 and O2 loading. The operations of the dynamic color display and dynamic holography are shown in Supporting Movies S1 and S2, respectively.

Figure 4.

Figure 4

Open in a new tab

Dynamic metasurface with dual-function. (a) SEM images of the dual-function metasurface. (b) Switching between dynamic color display and dynamic holography through hydrogenation and dehydrogenation. The Max Planck society logo is used with permission. (c) Time evolutions of the gray value of the color print and the hologram intensity during hydrogenation and dehydrogenation.

Conclusions

In conclusion, we have realized a dual-function metasurface for switching between dynamic holography and dynamic color display. The spatially arranged stepwise nanocavity pixels allow for accurate control over the amplitude and phase of light, enabling the facile design of metasurface color prints and holograms. In addition, the reversible phase-transition between Mg and MgH2 enables the dynamic functionality, leading to switchable holography and color display at visible frequencies. Our work represents a paradigm to realize multitasking optical elements, which broadens the realm of light projection devices and display technologies.

Experimental Methods

Sample Fabrications

The substrate was prepared by electron beam evaporation of Ag (120 nm) and SiO2 (190 nm) on a Si wafer. The multiple overlay patterning of the stepwise metasurface was performed using a Raith electron beam lithography system with an accelerating voltage of 30 kV and beam current of 890 pA. The spin-coated HSQ film was directly utilized without prebaking to avoid thermally induced cross-linking. Before carrying out the overlay fabrication, gold alignment markers were defined by a standard “sketch and peel” lithography process. To exactly define the heights of the stepwise pillars, the spinning speed and the concentration of the HSQ resist were finely tuned in each overlay. The details of the spin coating and exposures are shown in Table S1. The development time was 15 s to avoid the damage of the pillars fabricated in the previous overlays. Subsequently, Mg (50 nm)/Ti (2 nm)/Pd (3 nm) films were successively deposited on the patterned sample by electron beam evaporation.

Optical Setups

The holograms were recorded by an optical setup shown in Figure S1. The light beam was generated from a laser diode source (633 nm). A linear polarizer (LP) was employed to obtain linearly polarized light. An optical lens and an aperture were utilized to reshape the light beam to a similar size as the sample area in order to avoid undesired reflected light. The light beam was incident on the metasurface sample placed in a homemade gas cell. The reflective hologram was projected onto the screen in the far field. All the experiments were carried out at 80 °C to facilitate the switching upon H2 or O2 loading. The hydrogenation and dehydrogenation experiments were carried out in a home-built stainless steel chamber. Ultrahigh-purity hydrogen, oxygen, and nitrogen were used with mass flow controllers to adjust the flow rates and gas concentrations in the chamber. The flow rates of the hydrogen and oxygen gases were both 1.0 L/min.

The color microprint was revealed using a NT&C bright-field reflection microscopy setup (using a Nikon ECLIPSE LV100ND microscope) illuminated by a white light source (Energetiq Laser-Driven Light Source, EQ-99). A digital CCD camera (Allied-Vision Prosilica GT2450C) was used to capture the color micrographs with a 10× (NA = 0.3) objective. The optical spectra were measured in a reflection mode using a microspectrometer (Princeton Instruments, Acton SP-2356 spectrograph with Pixis:256E silicon CCD camera) with the electric field of the unpolarized light in plane with the substrate surface. The reflectance spectra were measured from samples in a stainless-steel cell during hydrogenation and dehydrogenation. The measured reflectance spectra were normalized with respect to that of an Al mirror.

Acknowledgments

This project was supported by the European Research Council (ERC Dynamic Nano) grant as well as the National Natural Science Foundation of China (grant 51722503).The authors thank the support from the Max-Planck Institute for Solid State Research for the usage of clean room facilities.

Supporting Information Available

The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsnano.0c01469.

  • Movie S1: Recording of dynamic color display (MP4)

  • Movie S2: Recording of dynamic holography (MP4)

  • Numerical simulation parameters and holography designs (PDF)

Author Contributions

# These authors contributed equally to this work.

The authors declare no competing financial interest.

Supplementary Material

nn0c01469_si_001.mp4 (4.2MB, mp4)
nn0c01469_si_002.mp4 (1.3MB, mp4)
nn0c01469_si_003.pdf (626.6KB, pdf)

References

  1. Yu N.; Genevet P.; Kats M. A.; Aieta F.; Tetienne J. P.; Capasso F.; Gaburro Z. Light Propagation with Phase Discontinuities: Generalized Laws of Reflection and Refraction. Science 2011, 334, 333–337. 10.1126/science.1210713. [DOI] [PubMed] [Google Scholar]
  2. Yu N.; Capasso F. Flat Optics with Designer Metasurfaces. Nat. Mater. 2014, 13, 139–150. 10.1038/nmat3839. [DOI] [PubMed] [Google Scholar]
  3. Arbabi A.; Horie Y.; Bagheri M.; Faraon A. Dielectric Metasurfaces for Complete Control of Phase and Polarization with Subwavelength Spatial Resolution and High Transmission. Nat. Nanotechnol. 2015, 10, 937–943. 10.1038/nnano.2015.186. [DOI] [PubMed] [Google Scholar]
  4. Li J.; Chen S.; Yang H.; Li J.; Yu P.; Cheng H.; Gu C.; Chen H.-T.; Tian J. Simultaneous Control of Light Polarization and Phase Distributions Using Plasmonic Metasurfaces. Adv. Funct. Mater. 2015, 25, 704–710. 10.1002/adfm.201403669. [DOI] [Google Scholar]
  5. Li J.; Kamin S.; Zheng G.; Neubrech F.; Zhang S.; Liu N. Addressable Metasurfaces for Dynamic Holography and Optical Information Encryption. Sci. Adv. 2018, 4, eaar6768. 10.1126/sciadv.aar6768. [DOI] [PMC free article] [PubMed] [Google Scholar]
  6. Zheng G.; Mühlenbernd H.; Kenney M.; Li G.; Zentgraf T.; Zhang S. Metasurface Holograms Reaching 80% Efficiency. Nat. Nanotechnol. 2015, 10, 308–312. 10.1038/nnano.2015.2. [DOI] [PubMed] [Google Scholar]
  7. Wen D.; Yue F.; Li G.; Zheng G.; Chan K.; Chen S.; Chen M.; Li K. F.; Wong P. W.; Cheah K. W.; Pun E. Y.; Zhang S.; Chen X. Helicity Multiplexed Broadband Metasurface Holograms. Nat. Commun. 2015, 6, 8241. 10.1038/ncomms9241. [DOI] [PMC free article] [PubMed] [Google Scholar]
  8. Duan X.; Kamin S.; Liu N. Dynamic Plasmonic Colour Display. Nat. Commun. 2017, 8, 14606. 10.1038/ncomms14606. [DOI] [PMC free article] [PubMed] [Google Scholar]
  9. Kumar K.; Duan H.; Hegde R. S.; Koh S. C. W.; Wei J. N.; Yang J. K. W. Printing Colour at the Optical Diffraction Limit. Nat. Nanotechnol. 2012, 7, 557–561. 10.1038/nnano.2012.128. [DOI] [PubMed] [Google Scholar]
  10. Hu Y.; Li L.; Wang Y.; Meng M.; Jin L.; Luo X.; Chen Y.; Li X.; Xiao S.; Wang H.; Luo Y.; Qiu C.-W.; Duan H. Trichromatic and Tripolarization-Channel Holography with Noninterleaved Dielectric Metasurface. Nano Lett. 2020, 20, 994–1002. 10.1021/acs.nanolett.9b04107. [DOI] [PubMed] [Google Scholar]
  11. Ellenbogen T.; Seo K.; Crozier K. B. Chromatic Plasmonic Polarizers for Active Visible Color Filtering and Polarimetry. Nano Lett. 2012, 12, 1026–1031. 10.1021/nl204257g. [DOI] [PubMed] [Google Scholar]
  12. Goh X. M.; Zheng Y.; Tan S. J.; Zhang L.; Kumar K.; Qiu C.-W.; Yang J. K. W. Three-Dimensional Plasmonic Stereoscopic Prints in Full Colour. Nat. Commun. 2014, 5, 5361. 10.1038/ncomms6361. [DOI] [PubMed] [Google Scholar]
  13. Chen Y.; Duan X.; Matuschek M.; Zhou Y.; Neubrech F.; Duan H.; Liu N. Dynamic Color Displays Using Stepwise Cavity Resonators. Nano Lett. 2017, 17, 5555–5560. 10.1021/acs.nanolett.7b02336. [DOI] [PubMed] [Google Scholar]
  14. Wang Y.; Zheng M.; Ruan Q.; Zhou Y.; Chen Y.; Dai P.; Yang Z.; Lin Z.; Long Y.; Li Y.; Liu N.; Qiu C.-W.; Yang J. K. W.; Duan H. Stepwise-Nanocavity-Assisted Transmissive Color Filter Array Microprints. Research 2018, 2018, 8109054. 10.1155/2018/8109054. [DOI] [PMC free article] [PubMed] [Google Scholar]
  15. Ni X.; Kildishev A. V.; Shalaev V. M. Metasurface Holograms for Visible Light. Nat. Commun. 2013, 4, 2807. 10.1038/ncomms3807. [DOI] [Google Scholar]
  16. Huang L.; Chen X.; Mühlenbernd H.; Zhang H.; Chen S.; Bai B.; Tan Q.; Jin G.; Cheah K.-W.; Qiu C.-W.; Li J.; Zentgraf T.; Zhang S. Three-Dimensional Optical Holography Using a Plasmonic Metasurface. Nat. Commun. 2013, 4, 2808. 10.1038/ncomms3808. [DOI] [Google Scholar]
  17. Wan W.; Gao J.; Yang X. Full-Color Plasmonic Metasurface Holograms. ACS Nano 2016, 10, 10671–10680. 10.1021/acsnano.6b05453. [DOI] [PubMed] [Google Scholar]
  18. Wei Q.; Sain B.; Wang Y.; Reineke B.; Li X.; Huang L.; Zentgraf T. Simultaneous Spectral and Spatial Modulation for Color Printing and Holography Using All-Dielectric Metasurfaces. Nano Lett. 2019, 19, 8964–8971. 10.1021/acs.nanolett.9b03957. [DOI] [PMC free article] [PubMed] [Google Scholar]
  19. Hu Y.; Luo X.; Chen Y.; Liu Q.; Li X.; Wang Y.; Liu N.; Duan H. 3D-Integrated Metasurfaces for Full-Colour Holography. Light: Sci. Appl. 2019, 8, 86. 10.1038/s41377-019-0198-y. [DOI] [PMC free article] [PubMed] [Google Scholar]
  20. Bao Y.; Yu Y.; Xu H.; Guo C.; Li J.; Sun S.; Zhou Z. K.; Qiu C. W.; Wang X. H. Full-Colour Nanoprint-Hologram Synchronous Metasurface with Arbitrary Hue-Saturation-Brightness Control. Light: Sci. Appl. 2019, 8, 95. 10.1038/s41377-019-0206-2. [DOI] [PMC free article] [PubMed] [Google Scholar]
  21. Wen D.; Cadusch J. J.; Meng J.; Crozier K. B. Multifunctional Dielectric Metasurfaces Consisting of Color Holograms Encoded into Color Printed Images. Adv. Funct. Mater. 2020, 30, 1906415. 10.1002/adfm.201906415. [DOI] [Google Scholar]
  22. Yoon G.; Lee D.; Nam K. T.; Rho J. ″Crypto-Display″ in Dual-Mode Metasurfaces by Simultaneous Control of Phase and Spectral Responses. ACS Nano 2018, 12, 6421–6428. 10.1021/acsnano.8b01344. [DOI] [PubMed] [Google Scholar]
  23. Sterl F.; Strohfeldt N.; Walter R.; Griessen R.; Tittl A.; Giessen H. Magnesium as Novel Material for Active Plasmonics in the Visible Wavelength Range. Nano Lett. 2015, 15, 7949–7955. 10.1021/acs.nanolett.5b03029. [DOI] [PubMed] [Google Scholar]
  24. Duan X.; Kamin S.; Sterl F.; Giessen H.; Liu N. Hydrogen-Regulated Chiral Nanoplasmonics. Nano Lett. 2016, 16, 1462–7466. 10.1021/acs.nanolett.5b05105. [DOI] [PubMed] [Google Scholar]
  25. Yu P.; Li J.; Li X.; Schütz G.; Hirscher M.; Zhang S.; Liu N. Generation of Switchable Singular Beams with Dynamic Metasurfaces. ACS Nano 2019, 13, 7100–7106. 10.1021/acsnano.9b02425. [DOI] [PMC free article] [PubMed] [Google Scholar]
  26. Yu P.; Li J.; Zhang S.; Jin Z.; Schütz G.; Qiu C.-W.; Hirscher M.; Liu N. Dynamic Janus Metasurfaces in the Visible Spectral Region. Nano Lett. 2018, 18, 4584–4589. 10.1021/acs.nanolett.8b01848. [DOI] [PubMed] [Google Scholar]
  27. Duan X.; Liu N. Magnesium for Dynamic Nanoplasmonics. Acc. Chem. Res. 2019, 52, 1979–1989. 10.1021/acs.accounts.9b00157. [DOI] [PMC free article] [PubMed] [Google Scholar]
  28. Duan X.; Liu N. Scanning Plasmonic Color Display. ACS Nano 2018, 12, 8817–8823. 10.1021/acsnano.8b05467. [DOI] [PubMed] [Google Scholar]
  29. Sterl F.; Linnenbank H.; Steinle T.; Mörz F.; Strohfeldt N.; Giessen H. Nanoscale Hydrogenography on Single Magnesium Nanoparticles. Nano Lett. 2018, 18, 4293–4302. 10.1021/acs.nanolett.8b01277. [DOI] [PubMed] [Google Scholar]
  30. Duan X.; Griessen R.; Wijngaarden R. J.; Kamin S.; Liu N. Self-Recording and Manipulation of Fast Long-Range Hydrogen Diffusion in Quasifree Magnesium. Phys. Rev. Mater. 2018, 2, 085802. 10.1103/PhysRevMaterials.2.085802. [DOI] [Google Scholar]
  31. Yue Z.; Xue G.; Liu J.; Wang Y.; Gu M. Nanometric Holograms Based on a Topological Insulator Material. Nat. Commun. 2017, 8, 15354. 10.1038/ncomms15354. [DOI] [PMC free article] [PubMed] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Supplementary Materials

nn0c01469_si_001.mp4 (4.2MB, mp4)
nn0c01469_si_002.mp4 (1.3MB, mp4)
nn0c01469_si_003.pdf (626.6KB, pdf)

Articles from ACS Nano are provided here courtesy of American Chemical Society

RESOURCES