. 2020 Sep 15;10:15132. doi: 10.1038/s41598-020-72185-2

Impact of self-assembling peptides in remineralisation of artificial early enamel lesions adjacent to orthodontic brackets

Anahita Jablonski-Momeni 1,✉, R Nothelfer 1, M Morawietz 2, A Kiesow 2, H Korbmacher-Steiner 1
PMCID: PMC7493957  PMID: 32934335

Abstract

Enamel demineralisation can occur as a side effect during orthodontic treatment with fixed appliances. This study aimed to evaluate the efficacy of the self-assembling peptide P11-4 for remineralisation combined with fluorides, compared to application of fluoride varnish alone. De- and remineralisation was assessed by Quantitative light-induced fluorescence (QLF). Orthodontic brackets were bonded on 108 human enamel samples and white spot lesions were created. The samples were allocated randomly into three groups: Group I received no treatment, group II had a single application of fluoride varnish (22,600 ppm), and group III was treated with P11-4 following a single application of fluoride varnish. Quantitative light-induced fluorescence (QLF) measurements were performed at baseline, after demineralisation and after storage in remineralisation solution for 7 and 30 days. Non-parametric tests (Kruskal–Wallis test and Friedman test) were used for further analysis. After demineralisation, all samples showed a median ΔF -9.38% ± 2.79. After 30 days median ΔF values were as followed: group I = -9.04% ± 2.51, group II = -7.89 ± 2.07, group III = -6.08% ± 2.79). The median ΔF values differed significantly between all groups at all investigation times (p < 0.00001). Application of P11-4 with fluoride varnish was superior to the use of fluorides alone for remineralisation of enamel adjacent to brackets.

Subject terms: Diseases, Health care, Optics and photonics

Introduction

During fixed orthodontic treatment demineralisation may occur adjacent to brackets. Without special prevention concepts, early enamel changes may progress and white spot lesions occur. A meta-analysis showed that the incidence of new carious lesions formed during orthodontic treatment in patients was 45.8%1. According to some authors2 high treatment demand and occurrence of biofilm-related complications make orthodontic treatment a potential public health threat.

It is well accepted that caries progression is initiated by an imbalance of the remineralisation–demineralisation equilibrium favoring demineralisation3. Patients with fixed orthodontic treatment are usually subject to strict caries preventive care, including application of remineralisation agents containing fluoride4. Together with pit and fissure sealants5 and parent’s motivation6 the application of fluoride is the oldest aid for caries prevention7. It was reported in a recent meta-analysis8 that active patient reminders and flat surface sealants or fluoride varnish around orthodontic brackets might be associated with reduced white-spot-lesion burden, but the authors conclude that further research is needed. As another novel approach the use of bioactive glass (Biomin F paste) was shown to be an effective method for enamel remineralisation9.

Although the use of fluorides has been shown to prevent dental caries effectively10,11, limitations exist for the application of fluoride when the caries lesion has already progressed to the clinically visible white spot lesion and the best possible outcome would be an arrest of the lesion’s activity12. It was shown that a one-time application of fluoride varnish at the beginning of an orthodontic treatment did not provide any additional preventive benefit over sufficient dental hygiene with fluoride toothpaste regarding formation of white spot lesions and gingivitis in patients who were at low to moderate caries risk4. Nevertheless, the use of fluoride has a long history in dental practice and is accepted as a standard for caries prevention. Research is needed to evaluate new approaches which would support the effect of fluorides in preventing and arresting early caries lesions even more effectively.

Recently, biomimetic remineralisation strategies such as self-assembling peptides are considered to be a new perspective in caries prevention13–15. It is reported that the self-assembling peptide P11-4 forms a three dimensional matrix within the subsurface body of an initial enamel lesion and mimics enamel matrix proteins16,17. A high affinity of the P11-4 matrix for calcium ions is described, which acts as a nucleator for de novo hydroxyapatite formation16–18. Nowadays, the self-assembling peptide P11-4 is available in commercial products named Curolox Technology (credentis ag, Windisch, Switzerland). One available product is the CURODONT REPAIR which was developed for the in-depth biomimetic treatment of initial carious lesions.

Synthetic nanohydroxyapatite is also considered one of the most biocompatible and bioactive materials having similar morphology, structure, and crystallinity to the apatite crystal within enamel19. In vitro studies have shown that nanohydroxyapatite had the potential to remineralise initial enamel lesions with a comparable or even superior efficacy to that of fluoride20,21.

Non-operative, remineralising measures can only be used effectively if demineralisation is detected early. Beside visual, often subjective measures, the use of adjuvant procedures may provide additional benefit in objectifying and documentation of the demineralisation around orthodontic brackets and for digital demonstration. It is well known that demineralisation can be detected by light-induced fluorescence, since the fluorescence radiance at the site of a caries lesion is decreased22. It is possible to quantify the loss of fluorescence in a caries lesion in comparison with the fluorescence radiance level of sound enamel using systems like the Quantitative Light-induced Fluorescence (QLF). The method is suitable for detection and monitoring of mineral changes in incipient enamel lesions23–26.

The efficacy of P11-4 in remineralisation of early enamel lesions was shown using different detection methods such as laserfluorescence (DIAGNOdent)27,28 or impedance measurements29. But no published data are available using QLF as a reference standard. The aim of the present in-vitro study was to evaluate the effect of P11-4 in remineralisation of artificial lesions adjacent to orthodontic brackets with QLF.

Results

A number of 108 samples were included in the study. The analysis of the QLF values after de- and remineralisation showed no significant differences between different bracket materials (Kruskal–Wallis Test, p values: after demin = 0.23, after 7d remin = 0.67, after 30d remin = 0.46). Hence, the subsequent analyses were performed between the different treatment groups without further sub-analysis according to the various bracket types.

After demineralisation, all samples showed a distinct fluorescence loss with a median ΔF of − 9.38% (± 2.79) and a median ΔQ of − 1.13% × mm2 (± 4.96), respectively. The values for percentage of fluorescence loss (ΔF and ΔQ) after remineralisation are summarized for each group in Tables 1 and 2. In Fig. 1, representative images of each treatment group are presented. The samples were divided equally on the different groups randomly after demineralisation.

Table 1.

Results of the QLF measurements: ΔF (fluorescence loss [%]) in various groups (SD: standard deviation).

Time Group Minimum Maximum Mean Median SD
After demin I − 17.70 − 6.85 − 9.70 − 9.38 2.05
II − 18.60 − 6.90 − 10.12 − 9.43 3.13
III − 21.10 − 6.85 − 9.80 − 9.42 3.10
ΔF T7d I − 19.00 − 6.03 − 11.71 − 10.85 3.25
II − 16.40 − 6.37 − 10.19 − 9.73 3.24
III − 13.00 0.00 − 8.10 − 7.21 2.64
ΔF T30d I − 16.80 − 6.31 − 9.53 − 9.04 2.51
II − 14.40 − 6.24 − 8.29 − 7.89 2.07
III − 10.70 0.00 − 5.30 − 6.08 2.79
Open in a new tab

Group I = no treatment.

Group II = single application of fluoride varnish.

Group III = application of P11-4 + single application of fluoride varnish.

Table 2.

Results of the QLF measurements: ΔQ (fluorescence loss [%] x area [mm2]) in various groups (SD: standard deviation).

Time Group Minimum Maximum Mean Median SD
After demin I − 38.40 − 0.25 − 3.29 − 1.51 6.43
II − 24.10 − 0.10 − 2.91 − 0.98 5.26
III − 12.00 − 0.01 − 1.57 − 1.15 2.10
ΔF T7d I − 31.50 − 0.03 − 6.45 − 3.65 6.96
II − 23.90 − 0.07 − 4.61 − 1.93 5.85
III − 15.70 0.00 − 1.46 − 0.40 3.08
ΔF T30d I − 13.70 − 0.05 − 3.00 − 1.13 3.86
II − 18.00 − 0.02 − 2.16 − 0.62 3.84
III − 0.31 0.00 − 0.06 − 0.03 1.17
Open in a new tab

Group I = no treatment.

Group II = single application of fluoride varnish.

Group III = application of P11-4 + single application of fluoride varnish.

Figure 1.

Figure 1

Open in a new tab

Samples of each group with the corresponding fluorescence images at T30d. Values for ΔF and ΔQ are displayed above each QLF image. (a–c) Sample of group I (no treatment); (d–f) sample of group II (single application of fluoride varnish); (g–i) sample of group III (application of P11-4 + single application of fluoride varnish).

Comparison between the treatment groups (Kruskal–Wallis test and Dunn post-hoc tests) showed the following for the fluorescence values ΔF and ΔQ: After demineralisation all values were not significantly different from each other (p values 0.925 for ΔF and 0.143 for ΔQ, respectively. This indicated an equal allocation of the samples to each treatment group after demineralisation. At T7d ΔF values in group III were significantly lower that groups I and II (p = 0.00001). The same was confirmed for ΔQ values (p = 0.000006). At T30d ΔF and ΔQ in group III were still significantly lower than in groups I and II, indicating a higher remineralisation in the test group (ΔF: p = 0.00001, ΔQ: p < 0.000001).

Multiple comparisons between different time intervals in each individual treatment group (Friedman test) showed the following results: In group I fluorescence values decreased at T7d significantly (p < 0.00001) towards demineralisation but increased at T30d towards the baseline values (Table 1 and 2). In group II the fluorescence behavior remained unchanged after 7d but the values increased at T30d significantly (p = 0.0008) indicating mineral gain after 30 days. In group III the fluorescence values increased continuously at T7d and T30d (p < 0.00001) indicating a mineral gain at each study time.

The corresponding box-plots are presented in Fig. 2 and 3.

Figure 2.

Figure 2

Open in a new tab

Boxplots of the fluorescence measurements (fluorescence loss ΔF in %) in each group at the different investigation times. Group I = no treatment; Group II = single application of fluoride varnish; Group III = Application of P11-4 + single application of fluoride varnish.

Figure 3.

Figure 3

Open in a new tab

Boxplots of the fluorescence measurements (fluorescence loss times the area ΔQ in % × mm2) in each group at the different investigation times. Group I = no treatment; Group II = single application of fluoride varnish; Group III = Application of P11-4 + single application of fluoride varnish.

Discussion

Enamel demineralisation is known to be an undesired side effect of fixed orthodontic treatment. Initial lesions may progress towards cavities, and as a consequence orthodontic appliances may be removed prior to the proper end of the treatment2. Ever since, orthodontic treatment is stated to be at risk of becoming a public health threat2. So, it´s all the more important to modify the caries risk factors und emphasis on management strategies which focus on the remineralisation of the lesions. Such strategies are use of topical fluoride30–32, amorphous calcium phosphate33 or even a combination of both agents34. In addition, masking the lesions would improve the esthetic appearance of the teeth including bleaching, micro-abrasion or micro-invasive techniques such as resin infiltration35 with a camouflage effect. Moreover, microcrystalline hydroxyapatite (HAP) particles were suggested as suitable candidates for the prevention of demineralisation and the stimulation of remineralisation process on tooth tissue20,36. It was reported that after nanohydroxyapathite treatment the enamel was more mineralised37 and harder than demineralised enamel38.

In the present study the remineralisation effect of the self-assembling peptide P11-4 was assessed in combination with a fluoride varnish (test group), compared to the single application of the fluoride varnish and to samples which did not receive any additional treatment. In the test group significant fluorescence increase was observed after 7 and 30 days compared to the fluorescence behavior of the samples in group I and II, demonstrating a higher remineralisation in the test group (Tables 1 and 2). A study on bovine enamel samples showed that application of P11-4 alone did not lead to increased fluorescence using the QLF, indicating either lack of remineralisation or irregular crystals39. In another study on human enamel samples it could be shown that application of P11-4 on demineralised enamel and storage in a remineralising solution led to better surface quality than storage in distilled water27. The additional effect of P11-4 was shown in a randomized controlled trial, compared to the application of fluoride varnish alone in active occlusal initial caries lesions on erupting permanent molars40 where the test group showed significantly superior lesion regression. In another randomised controlled study it was shown that the size of early carious lesions on buccal surfaces was significantly reduced after application of self-assembling peptides compared to use of fluoride varnish alone41. The evaluation was performed visually and hence the interpretation of the size reduction was subjective. Results from a randomized in-situ study demonstrated the superior remineralising effect of the self-assembling peptide compared to fluoride use on demineralised bovine enamel28. The applied gel contained 1,000 ppm P11-4 and 900 ppm fluoride, recommended for homecare prevention. This gel should be applied twice a week after regular oral hygiene. In this context, however, the compliance of patients wearing fixed appliances with regard to their oral care routine at home should be considered and compliance-independent measures which can be applied in the dental office should be taken into account. Very recent studies could show that the application of P11-4 prior to bonding of orthodontic brackets doesn´t have an effect on the shear-bond strength of the brackets42. Hence, the additional treatment with P11-4 may decrease the risk of development of initial caries lesions during fixed orthodontic treatment.

Welk et al.29 could show the effect of P11-4 on orthodontic treatment induced carious lesions after the orthodontic multibracket treatment. The authors concluded that treatment of initial carious lesions with P11-4 led to better remineralisation of the subsurface lesions compared with the control teeth. Doberdoli et al.15 investigated the effectiveness of both monomeric self-assembling peptide P11-4 and the polymeric self-assembling peptide matrix in treatment of non-cavitated occlusal caries in children. The study showed that P11-4, applied either in combination with fluoride varnish or twice weekly as a gel was a superior treatment for early caries lesions, when compared to application of fluoride varnish alone.

In a meta-analysis it was indicated that a monthly use of fluoride varnish was the most effective protocol to enhance the remineralisation due to toothbrushing with a fluoride-containing dentifrice31. The fluorescence loss in the samples of our study indicated that the one-time application of fluoride varnish had no impact in the remineralisation process after 7 days but only after 30 days. Whereas in the test group (P11-4 + fluoride varnish) the fluorescence values decreased already after 7 days and a continuous significant mineral gain was still assessed at T30d. These results show clearly the additional remineralising effect of the self-assembling peptides on the short term.

As a consequence, in the clinical setting, recall intervals should be adjusted for assessing preventive interventions and the monitoring of initial lesions and reviews of behavioral and oral hygiene change plans43. Moreover, application of biomimetic agents can be taken into account depending on patient’s risk forward developing caries lesions. This would be a beneficial step to inhibit the progression of already established white-spot lesions adjacent to orthodontic brackets. This issue may be addressed when pH-cycling models are used to simulate oral pH fluctuation patterns and daily oral care. Moreover, the long-term effect of remineralisation agent can be better evaluated since results after pH-cycling may better be transferred to the clinical situation. This shows the limitation of the present study where a model of a certain clinical situation was considered. In our study we looked at remineralisation of already demineralised enamel and the set-up does not give any data on the inhibition of demineralisation which could be assessed using a pH-cycling model. Consequently the raised data is applicable for the remineralisation period in the mouth. Yet, as in any in vitro experiments, timelines cannot be translated to in vivo situations entirely.

The use of QLF is a common method to assess demineralisation adjacent to orthodontic brackets without sample destruction44–48. In QLF images the fluorescence correlates with mineral loss of a tooth surface49 and can be monitored over time. The ΔF corresponds to the percentage fluorescence loss with respect to the fluorescence of sound tooth tissue and is related to lesion depth, while ΔQ takes into account the area of the lesion and is related to the lesion volume50. The amount of fluorescence radiance loss is already validated with transversal and longitudinal microradiography and was reported to be closely correlated (r = 0.97) to the mineral loss in the lesion49,51,52. The method can be considered as suitable for monitoring of mineral changes in initial enamel lesions and for the evaluation of preventive measures53.

In the present study, different bracket materials had no significant effect on the measurements regarding de- and remineralisation. A possible deteriorating effect that fluoride containing agents can exert on orthodontic titanium wires was discussed. It was shown that the in vitro fluoride application caused an increase in friction resistance of Ni–Ti wires when compared to stainless steel wires. In vitro and in situ fluoride application caused deterioration in surface properties of Ni–Ti wires54. Some studies have investigated the differences between various types of brackets in terms of adhesion of cariogenic streptococci. In some studies no differences in the adherence to stainless steel, ceramic, or plastic brackets could be demonstrated55,56. In contrast, other studies revealed that ceramic or plastic brackets have a higher bacterial attachment rate than most of the metal brackets57–59. It must be considered that in the present study a demineralisation model was used which was without colonization of cariogenic microorganisms adjacent to the brackets. Therefore, this factor was not evaluated in our study. Nevertheless, outcomes of a systematic review concluded that there is currently no evidence for a possible influence of the design of the brackets (conventional or self ligating) over colony formation and adhesion of Streptococcus mutans and that other factors may have greater influence, such as the quality of the bracket type or the level of individual oral hygiene60.

Conclusions and clinical relevance

The present study is the first which demonstrated with the QLF the effectiveness of the P11-4 combined with fluoride varnish adjacent to orthodontic brackets on artificially demineralised human enamel. Although there are limitations of in-vitro studies it can be concluded that application of the highly concentrated self-assembling peptide P11-4 prior to topical fluoridation provides additional support for the regeneration of demineralised enamel in the short- term (up to 30 days). The effectiveness in mineral gain is superior to the one-time use of fluoride varnish. The benefit is to improve remineralisation of enamel especially in high caries risk patients like those with fixed orthodontic appliances, where fluoride alone might not be sufficient.

Material and methods

Study preparation and selection of the extracted teeth

The study protocol and the use of extracted human teeth were approved by the Ethics Committee of the Medical Faculty of the Philipps-University of Marburg, Germany (Ref. No.: 132/19). Prior to extraction each patient was informed and consent was obtained for the use of the teeth for study purposes. The research didn´t involve human participants.

A sample size calculation was performed with MedCalc (v19.2.1) based on preliminary (unpublished) data. A number of 13 samples was calculated for each treatment group (Power 0.90, α = 0.05), assuming a difference of mean of 4 and the standard deviation of 3 in each group.

The teeth were stored after extraction for 7–10 days in a 0.5% chloramine-T bacteriostatic solution (Merck, Darmstadt, Germany)42. The bulk of the adherent soft tissues was carefully removed and the teeth were cleaned with rotating brush and tooth cleansing paste with RDA value of 120 (Clinpro Prophy Paste, 3M ESPE, Seefeld, Germany). The buccal surface of the teeth were examined under a stereomicroscope (Leica MS 5, Leitz, Wetzlar, Germany) at 16 × magnification to control and exclude any surface defects. The teeth were stored in distilled water for further use27. The teeth were cut in a mesiodistal direction and each sample was fixed on a plexiglas slide (Dia-plus, Oststeinbek, Germany).

Preparation of the samples

On the buccal surface of each sample orthodontic brackets were bonded according to the manufacturer’s recommendation: Enamel surface was etched with 36% phosphoric acid gel for 30 s (Conditioner 36, Dentsply DeTrey, Konstanz, Germany), rinsed with water and dried using a three-in-one-syringe. Brackets were bonded in the center of each sample (Transbond XT primer and adhesive, 3M Unitek, Landsberg, Germany) and were light cured for 10 s according to manufacturer´s instruction (FlashMax P4 Ortho Pro, orthodontic light pen, CMS Dental, Copenhagen, Denmark; Peak Output Intensity: 6,000 mW/cm2). Different brackets were used to evaluate whether the material (stainless steel, titanium or ceramic) has an impact on the measurements. The orthodontic brackets were randomly bonded on the samples (n = 12 in each group) using the following types: equilibrium mini (material: stainless steel), equilibrium ti (material: titanium), and discovery pearl (material: ceramic composed of aluminum oxide crystals) (all brackets: DENTAURUM, Ispringen, Germany).

Demineralisation of the samples

A sample with different surface areas is presented in Fig. 4. On each sample, one side was covered by an acid resistance clear nail polish (Manhattan, Mainz, Germany) to protect this enamel part from demineralisation. To produce subsurface lesions, the samples were covered with a layer of a 8% methylcellulose (approximately 1.5 cm) on top of which was placed in excess 0.1 M lactate buffer, pH 4.6 61, at 37 ∘C (incubator type B, Heraeus GmbH, Hanau, Germany). After 14 days, the samples were taken out of the gel and were washed with a water jet from a three-in-one syringe to remove any gel remnants from the lesion surface. After that, the samples were rinsed with distilled water and were examined microscopically after air drying to control the surfaces for a dull, whitish surface resembling typical early enamel lesions.

Figure 4.

Figure 4

Open in a new tab

(a) Sample surface prior to demineralisation. (b) Scheme of the sample surface with different areas: Left side (red patterned area): demineralised surface. The surface was covered by nail varnish after demineralisation. Center of the surface: Orthodontic bracket. The area circular of the brackets (dark patterned area) was exposed to different remineralisation agents after demineralisation. Right side (green patterned area): sound enamel. The surface was covered by nail varnish prior to demineralisation.

The depth of the demineralised enamel surface was determined on representative histological samples after sectioning. For this procedure, the samples were cut with a diamond bladed saw (Presi Minitech 333, Presi GmbH, Hagen, Germany) and embedded in epoxy resin (SpexiFix20, Struers GmbH, Willich, Germany). The cross section surface was grinded to 4,000 grit by SiC abrasive paper (SiC Struers GmbH, Willich, Germany). The sections were evaluated under a microscope (BX51, Olympus GmbH, Hamburg, Germany) for determination of lesion depth. Lesion depth was determined by image analyzer software CellF* (BX51, Olympus GmbH, Hamburg, Germany). The mean depth of the demineralised area was 97.32 µm. A representative section with the demineralised area in the enamel surface is displayed in Fig. 5.

Figure 5.

Figure 5

Open in a new tab

Representative cross section with the demineralised area in the enamel surface.

Assignment of the samples to the treatment groups

After demineralisation another side of the sample surface was covered by varnish in order to have a demineralised control in each sample (Fig. 4b). From each bracket group 12 samples were randomly allocated to three groups with different treatment strategies (n = 36 in each treatment group):

Group I, negative control, no treatment; group II, positive control: single application of fluoride varnish (Duraphat, containing 22,600 ppm fluoride; Colgate-Palmolive, New York, USA); group III, test group: onetime application of P11-4 (CURODONT REPAIR, Straumann AG, Basel, Switzerland) according to manufacturer’s instructions + single application of fluoride varnish.

The self-assembling peptide P11-4 was used as the clinically available CURODONT REPAIR with the chemical structure: Ace-Gln–Gln–Arg–Phe–Glu–Trp–Glu–Phe–Glu–Gln–Gln–NH2.

The material was applied to the tooth surfaces following the manufacturer´s protocol: The tooth surface was rinsed with sodium hypochlorite solution (2%, SPEIKO, Dr. Speier GmbH, Münster, Germany) to remove the pellicle. After air-drying, the surface was etched with 36% phosphoric acid gel for 20 s and was rinsed and dried thoroughly. Then the P11-4 was applied with its application tip. After five minutes, fluoride varnish was applied on the pre-treated surfaces. All samples were stored in a remineralisation solution, adjusted to a pH of 6.9. The solution was prepared by mixing 1.635 g KH2PO4 (2.403 mM), 1.700 g Na2HPO4 (2.395 mM), 6.335 g KCL (16.993 mM), 2.920 g NaCl (9.993 mM) and 0.830 g CaCl2 * 2 H2O (1.129 mM) in 5 L distilled water (all chemicals: Merck, Darmstadt, Germany). The pH was measured daily and the solution was replaced weekly. The samples were stored in the incubator at a constant temperature of 37 °C.

Quantitative light-induced fluorescence (QLF)

Noninvasive measurements were performed as the reference standard for the quantification of de- and remineralisation using the Quantitative light induced fluorescence method (QLF Inspektor Pro, Inspektor Research Systems, Amsterdam, Netherlands). The QLF analysis software Inspektor Pro 2.0.0.48 was used to quantify the fluorescence behavior of the enamel surfaces which is directly proportional to the mineral content62. The measurements were performed at baseline, after demineralisation and after 7 days (T7d) and 30 days (T30d) of treatment in the corresponding group. First, in the QLF baseline images (sound enamel) the region of interest adjacent to the orthodontic bracket was defined. This area was recalled on the following images after demineralisation and at T7d and T30d. Average percentage of fluorescence loss with respect to the fluorescence of sound tissue (ΔF, %) and fluorescence loss times the area (ΔQ, % × mm2) was calculated by the software.

All measurements were performed blinded to the group allocation. For this, the samples were removed from their container by an individual who was not involved in the study procedure. The same person replaced the samples after measurements for further storage.

All performed methods were carried out in accordance with the relevant guidelines and regulations.

Statistical evaluation

The data were analyzed using the statistical software MedCalc (v19.2.1). Data were tested for normal distribution using the Shapiro–Wilk’s test to check for normality (p < 0.05). Non-parametric tests (Kruskal–Wallis test and Friedman test) were used for further analysis. The significance level was set at α = 0.05.

Acknowledgements

The study was supported financially by the German Society of Dentistry and Oral Medicine (DGZMK). The Brackets were provided by DENTAURUM (Ispringen, Germany). The QLF was provided by Prof. Wiechmann (Bad Essen, Germany).

Author contributions

Conceived and designed the experiments: A.J.M., R.N., M.M., A.K., H.K.S. (all authors). Performed the study: A.J.M., R.N., M.M. Provided technical equipment and facilities to perform the measurements: A.J.M., M.M., A.K., H.K.S. Conducted the data acquisition: A.J.M., R.N., M.M., H.K.S. Analysed the data: A.J.M., M.M. Wrote and approved the paper: A.J.M., R.N., M.M., A.K., H.K.S. (all authors). Revised the manuscript: A.J.M., R.N., M.M., A.K., H.K.S. (all authors). Approved the revised manuscript prior to submission: A.J.M., R.N., M.M., A.K., H.K.S. (all authors).

Funding

Open Access funding provided by Projekt DEAL.

Data availability

The dataset generated and analysed during the current study was submitted with the manuscript as “Manuscript related file”. After publication the dataset are available from the corresponding author on reasonable request.

Competing interests

The authors declare no competing interests.

Footnotes

Publisher's note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

References

  • 1.Sundararaj D, Venkatachalapathy S, Tandon A, Pereira A. Critical evaluation of incidence and prevalence of white spot lesions during fixed orthodontic appliance treatment: A meta-analysis. J. Int. Soc. Prevent. Commun. Dent. 2015;5:433–439. doi: 10.4103/2231-0762.167719. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 2.Ren Y, Jongsma MA, Mei L, van der Mei HC, Busscher HJ. Orthodontic treatment with fixed appliances and biofilm formation–a potential public health threat? Clin. Oral Invest. 2014;18:1711–1718. doi: 10.1007/s00784-014-1240-3. [DOI] [PubMed] [Google Scholar]
  • 3.Featherstone, J.D. The continuum of dental caries—Evidence for a dynamic disease process. J. Dent. Res.83 (Spec No C), C39–C42 (2004). [DOI] [PubMed]
  • 4.Kirschneck C, Christl JJ, Reicheneder C, Proff P. Efficacy of fluoride varnish for preventing white spot lesions and gingivitis during orthodontic treatment with fixed appliances-a prospective randomized controlled trial. Clin. Oral Invest. 2016;20:2371–2378. doi: 10.1007/s00784-016-1730-6. [DOI] [PubMed] [Google Scholar]
  • 5.Muntean, A., Simu, M.R., Suhani, R., & Mesaros, A.S. Pit and fissure sealants penetration capacity and their correlation with fissure morphology. Med. Pharm. Rep.92 (Suppl No. 3), S50–S54. 10.15386/mpr-1517 (2019). [DOI] [PMC free article] [PubMed]
  • 6.Aljafari, A., ElKarmi, R., Kussad, J. & Hosey, M.T. General dental practitioners' approach to caries prevention in high-caries-risk children. Eur. Arch. Paediatr. Dent.22. 10.1007/s40368-020-00548-4 (online ahead of print) (2020). [DOI] [PubMed]
  • 7.Zampetti P, Scribante A. Historical and bibliometric notes on the use of fluoride in caries prevention. Eur. Arch. Paediatr. Dent. 2020;21:148–152. doi: 10.23804/ejpd.2020.21.02.10. [DOI] [PubMed] [Google Scholar]
  • 8.Tasios T, et al. Prevention of orthodontic enamel demineralization: A systematic review with meta-analyses. Orthod. Craniofac. Res. 2019;22:225–235. doi: 10.1111/ocr.12322. [DOI] [PubMed] [Google Scholar]
  • 9.Bakry A.S.et al. A novel fluoride containing bioactive glass paste is capable of re-mineralizing early caries lesions. Materials (Basel)11, 1636. 10.3390/ma11091636 (2018). [DOI] [PMC free article] [PubMed]
  • 10.Marinho, V.C., Higgins, J.P., Logan, S. & Sheiham, A. Topical fluoride (toothpastes, mouthrinses, gels or varnishes for preventing dental caries in children and adolescents. Cochrane Database Syst. Rev.4, CD002782 (2003). [DOI] [PMC free article] [PubMed]
  • 11.Marinho, V.C., Worthington, H.V., Walsh, T. & Clarkson, J.E. Fluoride varnishes for preventing dental caries in children and adolescents. Cochrane Database Syst. Rev.7, CD002279 (2013). [DOI] [PMC free article] [PubMed]
  • 12.Anderson M, et al. Effectiveness of early preventive intervention with semiannual fluoride varnish application in toddlers living in high-risk areas: A stratified cluster-randomized controlled trial. Caries Res. 2016;50:17–23. doi: 10.1159/000442675. [DOI] [PubMed] [Google Scholar]
  • 13.Alkilzy M, Santamaria RM, Schmoeckel J, Splieth CH. Treatment of carious lesions using self-assembling peptides. Adv. Dent. Res. 2018;29:42–47. doi: 10.1177/0022034517737025. [DOI] [PubMed] [Google Scholar]
  • 14.Philip N. State of the art enamel remineralization systems: The next frontier in caries management. Caries Res. 2019;53:284–295. doi: 10.1159/000493031. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 15.Doberdoli D, et al. Randomized clinical trial investigating self-assembling peptide P11-4 for treatment of early occlusal caries. Sci. Rep. 2020;10:4195. doi: 10.1038/s41598-020-60815-8. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 16.Kirkham J, et al. Self-assembling peptide scaffolds promote enamel remineralization. J. Dent. Res. 2007;86:426–430. doi: 10.1177/154405910708600507. [DOI] [PubMed] [Google Scholar]
  • 17.Kind L, et al. Biomimetic remineralization of carious lesions by Self-Assembling Peptide. J. Dent. Res. 2017;96:790–797. doi: 10.1177/0022034517698419. [DOI] [PubMed] [Google Scholar]
  • 18.Brunton PA, et al. Treatment of early caries lesions using biomimetic self-assembling peptides - A clinical safety trial. Br. Dent. J. 2013;215:E6. doi: 10.1038/sj.bdj.2013.741. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 19.Hannig M, Hannig C. Nanomaterials in preventive dentistry. Nat. Nanotechnol. 2010;5:565–569. doi: 10.1038/nnano.2010.83. [DOI] [PubMed] [Google Scholar]
  • 20.Huang SB, Gao SS, Cheng L, Yu HY. Remineralization potential of nano-hydroxyapatite on initial enamel lesions: An in vitro study. Caries Res. 2011;45:460–468. doi: 10.1159/000331207. [DOI] [PubMed] [Google Scholar]
  • 21.Najibfard K, Ramalingam K, Chedjieu I, Amaechi BT. Remineralization of early caries by a nano-hydroxyapatite dentifrice. J. Clin. Dent. 2011;22:139–143. [PubMed] [Google Scholar]
  • 22.Bjelkhagen H, Sundström F, Angmar-Månsson B, Ryden H. Early detection of enamel caries by the luminescence excited by visible laser light. Swed. Dent. J. 1982;6:1–7. [PubMed] [Google Scholar]
  • 23.Gomez J, Tellez M, Pretty IA, Ellwood RP, Ismail AI. Non-cavitated carious lesions detection methods: A systematic review. Commun. Dent. Oral Epidemiol. 2013;41:54–66. doi: 10.1111/cdoe.12021. [DOI] [PubMed] [Google Scholar]
  • 24.Tranaeus, S, Al-Khateeb, S., Björkman, S., Twetman, S. & Angmar-Månsson, B. Application of quantitative light-induced fluorescence to monitor incipient lesions in caries-active children: A comparative study of remineralisation by fluoride varnish and professional cleaning. Eur. J. Oral Sci.109, 71–75 (2001). [DOI] [PubMed]
  • 25.Pretty IA, Pender N, Edgar WM, Higham SM. The in vitro detection of early enamel de- and re-mineralization adjacent to bonded orthodontic cleats using quantitative light-induced fluorescence. Eur. J. Orthod. 2003;25:217–223. doi: 10.1093/ejo/25.3.217. [DOI] [PubMed] [Google Scholar]
  • 26.van der Veen MH, Mattousch T, Boersma JG. Longitudinal development of caries lesions after orthodontic treatment evaluated by quantitative light-induced fluorescence. Am. J. Orthod. Dentofac. Orthop. 2007;131:223–228. doi: 10.1016/j.ajodo.2005.07.017. [DOI] [PubMed] [Google Scholar]
  • 27.Jablonski-Momeni A, Heinzel-Gutenbrunner M. Efficacy of the self-assembling peptide P11-4 in constructing a remineralization scaffold on artificially-induced enamel lesions on smooth surfaces. J. Orofac. Orthop. 2014;75:175–190. doi: 10.1007/s00056-014-0211-2. [DOI] [PubMed] [Google Scholar]
  • 28.Jablonski-Momeni A, et al. Randomised in situ clinical trial investigating self-assembling peptide matrix P11-4 in the prevention of artificial caries lesions. Sci. Rep. 2019;9:269. doi: 10.1038/s41598-018-36536-4. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 29.Welk, A., Ratzmann, A., Reich, M., Krey, K.F. & Schwahn, C. Effect of self-assembling peptide P11-4 on orthodontic treatment-induced carious lesions. Sci. Rep.10, 6819. 10.1038/s41598-020-63633-0 (2020). [DOI] [PMC free article] [PubMed]
  • 30.Lenzi T.L., Montagner. A.F., Soares, F.Z. & de Oliveira Rocha, R. Are topical fluorides effective for treating incipient carious lesions?: A systematic review and meta-analysis. J. Am. Dent. Assoc.147, 84–91.e1. 10.1016/j.adaj.2015.06.018 (2016). [DOI] [PubMed]
  • 31.Höchli D, Hersberger-Zurfluh M, Papageorgiou SN, Eliades T. Interventions for orthodontically induced white spot lesions: A systematic review and meta-analysis. Eur. J. Orthod. 2017;39:122–133. doi: 10.1093/ejo/cjw065. [DOI] [PubMed] [Google Scholar]
  • 32.Cosma LL, Şuhani RD, Mesaroş A, Badea ME. Current treatment modalities of orthodontically induced white spot lesions and their outcome - A literature review. Med. Pharm. Rep. 2019;92:25–30. doi: 10.15386/cjmed-1090. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 33.Munjal, D., Garg, S., Dhindsa, A., Sidhu, G.K. & Sethi, H.S. Assessment of white spot lesions and in-vivo evaluation of the effect of CPP-ACP on white spot lesions in permanent molars of children. J Clin. Diagn. Res.10, ZC149–154. 10.7860/JCDR/2016/19458.7896 (2016). [DOI] [PMC free article] [PubMed]
  • 34.Tao S, et al. Efficacy of fluorides and CPP-ACP vs fluorides monotherapy on early caries lesions: A systematic review and meta-analysis. PLoS ONE. 2018;13:e0196660. doi: 10.1371/journal.pone.0196660. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 35.Sonesson M, Bergstrand F, Gizani S, Twetman S. Management of post-orthodontic white spot lesions: An updated systematic review. Eur. J. Orthod. 2017;39:116–121. doi: 10.1093/ejo/cjw023. [DOI] [PubMed] [Google Scholar]
  • 36.Hornby K, et al. Enamel benefits of a new hydroxyapatite containing fluoride toothpaste. Int. Dent. J. 2009;59:325–331. doi: 10.1002/idj.2009.59.6s1.325. [DOI] [Google Scholar]
  • 37.Muntean, A. et al. Toothpaste composition effect on enamel chromatic and morphological characteristics: In vitro analysis. Materials (Basel),12, 2610. 10.3390/ma12162610 (2019). [DOI] [PMC free article] [PubMed]
  • 38.Scribante, A, et al. Biomimetic effect of nano-hydroxyapatite in demineralized enamel before orthodontic bonding of brackets and attachments: Visual, adhesion strength, and hardness in in vitro tests. Biomed. Res. Int. 30, 6747498. 10.1155/2020/6747498 (2020) [DOI] [PMC free article] [PubMed]
  • 39.Golland L, Schmidlin PR, Schätzle M. The potential of self-assembling peptides for enhancement of in vitro remineralisation of white spot lesions as measured by quantitative laser fluorescence. Oral Health Prevent. Dent. 2017;15:147–152. doi: 10.3290/j.ohpd.a37931. [DOI] [PubMed] [Google Scholar]
  • 40.Alkilzy M, Tarabaih A, Santamaria RM, Splieth CH. Self-assembling peptide p11-4 and fluoride for regenerating enamel. J. Dent. Res. 2018;97:148–154. doi: 10.1177/0022034517730531. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 41.Bröseler F, et al. Randomised clinical trial investigating self-assembling peptide P11-4 in the treatment of early caries. Clin. Oral. Invest. 2020;24:123–132. doi: 10.1007/s00784-019-02901-4. [DOI] [PubMed] [Google Scholar]
  • 42.Knaup, T., Korbmacher-Steiner, H. & Jablonski-Momeni, A. Effect of the caries-protective self-assembling peptide P11-4 on shear bond strength of metal brackets. J. Orofac. Orthop. (2020, in press) [DOI] [PMC free article] [PubMed]
  • 43.Pitts, N.B. et al. ICCMS™ guide for practitioners and educators. Full guide. https://www.iccms-web.com (2014). Accessed 18 June 2020.
  • 44.Aljehani A, Tranaeus S, Forsberg CM, Angmar-Månsson B, Shi XQ. In vitro quantification of white spot enamel lesions adjacent to fixed orthodontic appliances using quantitative light-induced fluorescence and DIAGNOdent. Acta Odontol. Scand. 2004;62:313–318. doi: 10.1080/00016350410001793. [DOI] [PubMed] [Google Scholar]
  • 45.de Josselin de Jong, E. et al. A new method for in vivo quantification of changes in initial enamel caries with laser fluorescence. Caries Res.29, 2–7 (1995). [DOI] [PubMed]
  • 46.Gokce G, Savas S, Kucukyilmaz E, Veli I. Effects of toothpastes on white spot lesions around orthodontic brackets using quantitative light-induced fluorescence (QLF): An in vitro study. J. Orofac. Orthop. 2017;78:480–486. doi: 10.1007/s00056-017-0106-0. [DOI] [PubMed] [Google Scholar]
  • 47.van der Veen MH, Attin R, Schwestka-Polly R, Wiechmann D. Caries outcomes after orthodontic treatment with fixed appliances: Do lingual brackets make a difference? Eur. J. Oral Sci. 2010;118:298–303. doi: 10.1111/j.1600-0722.2010.00733.x. [DOI] [PubMed] [Google Scholar]
  • 48.Visel D, Jäcker T, Jost-Brinkmann PG, Präger TM. Demineralization adjacent to orthodontic brackets after application of conventional and self-etching primer systems. J. Orofac. Orthop. 2014;75:358–373. doi: 10.1007/s00056-014-0233-9. [DOI] [PubMed] [Google Scholar]
  • 49.Hafström-Björkman, U., Sundström, F., de Josselin de Jong, E., Oliveby, A. & Angmar-Månsson, B. Comparison of laser fluorescence and longitudinal microradiography for quantitative assessment of in vitro enamel caries. Caries Res.26, 241–247 (1992). [DOI] [PubMed]
  • 50.Waller, E., van Daelen, C.J. & van der Veen, M.H. Application of QLF™ for Diagnosis and quality assessment in clinical practice. Version: 11, https://www.inspektor.nl/download/WhitepaperQLF-11.pdf (2012). Accessed 18 June 2020.
  • 51.Emami Z, et al. Mineral loss in incipient caries lesions quantified with laser fluorescence and longitudinal microradiography. A methodologic study. Acta Odontol. Scand. 1996;54:8–13. doi: 10.3109/00016359609003502. [DOI] [PubMed] [Google Scholar]
  • 52.Ando M, et al. Relative ability of laser fluorescence techniques to quantitate early mineral loss in vitro. Caries Res. 1997;31:125–131. doi: 10.1159/000262387. [DOI] [PubMed] [Google Scholar]
  • 53.Al-Khateeb, S., Forsberg, C.M., de Josselin de Jong, E. & Angmar-Månsson, B. A longitudinal laser fluorescence study of white spot lesions in orthodontic patients. Am. J. Orthod. Dentofacial Orthop.113, 595–602 (1998). [DOI] [PubMed]
  • 54.Abbassy MA. Fluoride influences nickel-titanium orthodontic wires' surface texture and friction resistance. J. Orthod. Sci. 2016;5:121–126. doi: 10.4103/2278-0203.192114. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 55.Anhoury P, et al. Microbial profile on metallic and ceramic bracket materials. Angle Orthod. 2002;72:338–343. doi: 10.1043/0003-3219(2002)072<0338:MPOMAC>2.0.CO;2. [DOI] [PubMed] [Google Scholar]
  • 56.Papaioannou W, Gizani S, Nassika M, Kontou E, Nakou M. Adhesion of Streptococcus mutans to different types of brackets. Angle Orthod. 2007;77:1090–1095. doi: 10.2319/091706-375.1. [DOI] [PubMed] [Google Scholar]
  • 57.Ahn SJ, Lim BS, Lee YK, Nahm DS. Quantitative determination of adhesion patterns of cariogenic streptococci to various orthodontic adhesives. Angle Orthod. 2006;76:869–875. doi: 10.1043/0003-3219(2006)076[0869:QDOAPO]2.0.CO;2. [DOI] [PubMed] [Google Scholar]
  • 58.Van Gastel J, et al. Microbial adhesion on different bracket types in vitro. Angle Orthod. 2009;79:915–921. doi: 10.2319/092908-507.1. [DOI] [PubMed] [Google Scholar]
  • 59.Pramod S, Kailasam V, Padmanabhan S, Chitharanjan AB. Presence of cariogenic streptococci on various bracket materials detected by polymerase chain reaction. Aust. Orthod. J. 2011;27:46–51. [PubMed] [Google Scholar]
  • 60.do Nascimento, L.E., de Souza, M.M., Azevedo, A.R. & Maia, L.C. Are self-ligating brackets related to less formation of Streptococcus mutans colonies? A systematic review. Dental Press J. Orthod.19, 60–68 (2014). [DOI] [PMC free article] [PubMed]
  • 61.ten Cate JM, et al. Preparation and measurement of artificial enamel lesions, a four-laboratory ring test. Caries Res. 1996;30:400–407. doi: 10.1159/000262351. [DOI] [PubMed] [Google Scholar]
  • 62.van der Veen, M.H. & de Josselin de Jong, E. Application of quantitative light-induced fluorescence for assessing early caries lesions. in Faller, R.V. (ed.) Assessment of Oral Health: Diagnostic Techniques and Validation Criteria, Monograph Oral Science Vol. 17, pp 144–162 (Karger, Basel, 2000). [DOI] [PubMed]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Data Availability Statement

The dataset generated and analysed during the current study was submitted with the manuscript as “Manuscript related file”. After publication the dataset are available from the corresponding author on reasonable request.