Polymerization shrinkage behaviour of resin composites functionalized with unsilanized bioactive glass fillers

Abstract

Previous work has shown that partial replacement of reinforcing fillers with unsilanized silica particles can diminish polymerization shrinkage stress of dental resin composites. The aim of the present study was to investigate whether such an effect can be attained by using unsilanized bioactive glass (BG). Incorporating BG fillers into resin composites is interesting due to their potential for exerting caries-preventive effects. Experimental light-curable composites with a total filler load of 77 wt% were prepared. Reinforcing fillers were partially replaced with 0–60 wt% of BG 45S5 and an experimental low-sodium fluoride-containing BG. The following properties were investigated: linear shrinkage, degree of conversion, shrinkage stress, maximum shrinkage stress rate, and time to achieve maximum shrinkage stress rate. The diminishing effect of BG 45S5 on shrinkage stress was mediated by a decrease in degree of conversion caused by this BG type. In contrast, as the degree of conversion remained unaffected by the experimental BG, the resulting shrinkage behaviour was governed by the effect of varying amounts of silanized and unsilanized fillers on material’s viscoelastic properties. The replacement of silanized reinforcing fillers with unsilanized BG did not reduce polymerization shrinkage stress unless the reduction was attained indirectly through a diminished degree of conversion.

Introduction

The persistent issue of secondary caries around composite restorations makes the research on bioactive resin composites with anti-caries activity a logical next step in the development of restorative composites¹. Bioactive composites functionalized with various types of reactive fillers have been extensively investigated due to their ion-releasing², antibacterial³, alkalizing⁴, and calcium phosphate-forming capabilities^5,6. An especially interesting type of reactive filler capable of exerting all of these beneficial effects pertains to the group of bioactive glasses (BGs). These reactive glasses with adjustable composition and properties have shown a promising potential to render resin composites more resistant to secondary caries^5,7–12. A particularly interesting modification of BGs involves fine-tuning of their sodium amount to attain a prolonged bioactive effect, and introducing fluorides as therapeutic ions capable of remineralizing dental hard tissues^5,7,12. The inevitable shortcoming of reactive BG fillers is their detrimental effect on the mechanical properties of the composite, especially when used in higher amounts^13,14. However, this negative effect can be mitigated by adjusting the ratio of BG and reinforcing fillers to the level which is sufficient to produce a desired bioactive effect, and yet does not significantly impair mechanical properties¹⁵.

Dental resin composites are composed of inorganic filler particles dispersed in a photo-curable resinous matrix. The filler particles are commonly coated with a functional silane, which enables their chemical bonding to the polymeric matrix¹⁶. The Si–O–Si bonds at the filler/matrix interface enhance the distribution of mechanical loads between the two phases with considerably different elastic moduli, thereby reinforcing the composite’s structure and improving its resistance to fracture¹⁷. Silane coating of filler particles has been used since the inception of resin composites, and its basic chemistry remained unchanged up to date. However, in bioactive composites, reactive fillers are preferably used without surface silanization^{2–5,7–12,18}. The hydrophobic silane coating on reactive fillers is undesired as their surfaces must remain accessible to water in order to be able to dissolve and exert bioactive effects¹⁹. Therefore, experimental bioactive composites commonly contain varying ratios of two filler types: (I) non-soluble silanized fillers, which reinforce the material structure; and (II) reactive unsilanized fillers, which are physically embedded in the composite but cannot establish chemical bonds with the polymeric matrix.

The inability of unsilanized fillers for bonding with the polymeric matrix affects the development of the composite’s viscoelastic properties during polymerization²⁰. The fact that the addition of unsilanized fillers can modify the mobility of the polymerizing resin inspired studies, which investigated this effect as a potential approach to reduce polymerization shrinkage stress^21,22. These studies showed that nano-sized unsilanized silica fillers can reduce polymerization shrinkage stress of resin composites, with the extent of reduction being dependent on composite viscosity and the presence of other silanized fillers. The mechanisms of shrinkage stress reduction by virtue of unsilanized fillers include an improved flow capability at the unbonded filler/matrix interface, and the development of gaps around unsilanized fillers that act as internal sites for stress relief²³. Because the detrimental effects of shrinkage stress (e.g. loss of marginal integrity, postoperative sensitivity, and secondary caries) are considered a major shortcoming of all resin composites²⁴, efforts to reduce shrinkage stress are relevant for future material improvements.

Except the aforementioned studies on the incorporation of unsilanized non-soluble fillers as a means to reduce polymerization shrinkage stress in conventional composites^21,22, the corresponding effect has not been investigated for unsilanized reactive fillers in bioactive composites. The present study addressed this issue by investigating the polymerization shrinkage behaviour of experimental composites functionalized with conventional BG 45S5 and an experimental low-sodium fluoride-containing BG. The aim of the study was to investigate the effect of varying amounts (0–60 wt%) of two BG types on linear shrinkage, degree of conversion (DC), shrinkage stress, and shrinkage stress kinetics. The null hypotheses assumed that these properties would not be affected by (I) the amount of unsilanized BG fillers, and (II) the BG type.

Materials and methods

Experimental resin composites

Experimental resin composites were prepared according to a previous study¹². The resin matrix comprised bisphenol-A-glycidyldimethacrylate (Bis-GMA, Merck, Darmstadt, Germany) and triethylene glycol dimethacrylate (TEGDMA, Merck) in a weight ratio of 60:40. Camphorquinone (0.2 wt%; Merck) and ethyl-4-(dimethylamino) benzoate (0.8 wt%; Merck) were added to the blend of monomers. All components were mixed using a magnetic stirrer for 48 h.

BG 45S5 and inert barium glass were obtained as commercially available products from Schott (Mainz, Germany). The experimental low-sodium fluoride-containing BG was prepared on-request by Schott via the melt-quench route. In order to obtain similar particle sizes of BG 45S5 and the experimental BG, similar preparation and grinding procedures were used for both BG types. Inert barium glass fillers were silanized during the manufacturing process, whereas the BG fillers were unsilanized. The composition of BG and reinforcing (inert) fillers is shown in Table 1.

Table 1.

Compositional details of bioactive glass and reinforcing fillers used in experimental composites.

	Bioactive glass 45S5	Experimental fluoride-containing bioactive glass	Inert barium glass
Particle size (d50)	3 µm	3 µm	1 µm
Composition (wt%)	45.0% SiO2 24.5% CaO 24.5% Na2O 6.0% P2O5	33.5% SiO2 33.0% CaO 10.5% Na2O 11.0% P2O5 12.0% CaF2	55.0% SiO2 25.0% BaO 10.0% Al2O3 10.0% B2O3
Silanization (wt%)	None	None	3.2
Product name/LOT	G018-144/M111473	experimental batch	GM27884/Sil13696

Experimental composites with a total filler amount of 77 wt% were prepared by replacing a fraction of the reinforcing fillers (0–60 wt%) with either BG 45S5 or the experimental BG (Table 2). According to the type of BG, the experimental composite series were denoted as C-series (for conventional BG 45S5) and E-series (for the experimental BG). The control composite contained only reinforcing barium glass fillers.

Table 2.

Composition of experimental composites.

Material designation	Filler composition (wt%)			Total filler amount (wt%)
	Bioactive glass 45S5	Experimental fluoride-containing bioactive glass	Reinforcing fillers (inert barium glass: silica = 2:1 by wt%)
Control	0	0	77	77
C-series
C-10	10	0	67	77
C-20	20	0	57	77
C-40	40	0	37	77
C-60	60	0	17	77
E-series
E-10	0	10	67	77
E-20	0	20	57	77
E-40	0	40	37	77
E-60	0	60	17	77

The photoactivated resin system and the fillers were mixed using a dual asymmetric centrifugal mixing system (Speed Mixer TM DAC 150 FVZ, Hauschild & Co. KG, Hamm, Germany) at 2000 rpm. The mixing was performed in five 1-min intervals separated by 1-min breaks. After mixing, the prepared composites were deaerated in vacuum during 48 h.

Linear shrinkage

Real-time linear shrinkage measurements were performed using a custom-made linometer, as described previously^25–28. Briefly, the setup consisted of a thin aluminium platelet (12 × 12 mm, thickness = 0.25 mm, m = 0.4 g) loosely placed on a solid metal frame. A perpendicular diaphragm fixed to the bottom side of the platelet extended into a recess of the infrared measuring sensor. A discoid composite specimen of standardized volume (V = 42 mm³, d = 6 mm) was placed on the upper side of the aluminium platelet and flattened using a glass plate to a thickness of 1.5 mm. The light guide tip of the curing unit (Bluephase PowerCure, Ivoclar Vivadent, Schaan, Liechtenstein; curing unit tip diameter: 9 mm, emission wavelength range: 390–500 nm, radiant exitance: 1340 mW/cm²) was positioned directly above the glass plate, and the composite specimen was light-cured through the glass plate for 20 s, resulting in a total radiant exposure of 26.8 J/cm². The curing unit performance was periodically verified using a calibrated and NIST-referenced UV–Vis spectrophotometer system (MARC; BlueLight Analytics, Halifax, Canada). Polymerization shrinkage caused the vertical displacement of the diaphragm which was detected by the infrared sensor at a data collection rate of 5 Hz and an accuracy of 0.1 µm. Linear shrinkage was measured in real-time for 15 min from the start of light-curing. The measurements were conducted inside a temperature-controlled chamber at 25 ± 1 °C, which simulated intraoral temperature after rubber-dam isolation²⁷. The data were logged by a personal computer, using an analog-to-digital converter and custom-made software. Ten experimental runs were performed for each group (n = 10).

Degree of conversion

The specimens used for linear shrinkage measurements were removed from the linometer immediately after completing the measurements, and mounted onto a diamond attenuated total reflectance (ATR) accessory of a Fourier transform infrared (FTIR) spectrometer (Cary 630 FTIR, Agilent Technologies, Santa Clara, CA, USA). The DC was evaluated on the bottom side of 1.5 mm thick discoid specimens, 15 min after the start of light-curing. This procedure of evaluating the DC at the endpoint of the observation period for linear shrinkage and shrinkage stress measurements was adopted from previous studies^{25–27,29,30}.

The FTIR spectra were collected with 100 scans, using a resolution of 4 cm⁻¹ in the wavelength range of 400–4000 cm⁻¹. Spectra from uncured composites were recorded under the same conditions. Ten experimental runs were performed for each group (n = 10). DC was calculated from the changes in the ratio of absorbance intensities (peak heights) of aliphatic C=C (1638 cm⁻¹) and aromatic C⋯C (1608 cm⁻¹) spectral bands using the following equation³¹:

$$\text{DC}(\%)=\left(1-\frac{(1638{\text{cm}}^{-1}/1608{\text{cm}}^{-1})\text{after curing}}{(1638{\text{cm}}^{-1}/1608{\text{cm}}^{-1})\text{before curing}}\right)\times 100$$

Shrinkage stress

Real-time measurements of shrinkage stress were performed using a custom-made stress analyser, as described previously^{25–27,29,30}. The semi-rigid setup with compliance of 0.4 μm/N was used to simulate the partial relief of shrinkage stress through the displacement of dental hard tissues²⁷. A standardized amount of the composite material (V = 42 mm³, d = 6 mm) was applied onto a metal cylinder connected to a load cell (PM 11-K; Mettler, Greifensee, Switzerland). The composite was flattened by a glass plate to a thickness of 1.5 mm in order to produce the discoid composite specimen with the base surface area of 28 mm². Bonding the bases of the discoid specimens to the metal cylinder and the glass plate resulted in the ratio of bonded to unbonded surface area (C-factor) of 2.0. To ensure bonding of the composite to the glass plate and metal cylinder, their surfaces were sandblasted using aluminium oxide (50 μm; Renfert, Hilzingen, Germany), rinsed with a stream of demineralized water for 30 s, dried using pressurized air stream, and treated with a silane-containing primer Monobond Plus (Ivoclar Vivadent). To confirm that the sandblasted surfaces were clean from aluminium oxide particles, visual inspection was performed using a stereomicroscope at 40× magnification (M3Z; Leica/Wild, Heerbrugg, Switzerland). The composite specimen was light-cured through the glass plate in the same manner as described for the linear shrinkage measurements. Forces resulting from polymerization shrinkage were detected by the load cell at a data collection rate of 5 Hz and accuracy of 0.001 N. Real-time shrinkage stress data were collected for 15 min from the start of light-curing, inside a temperature-controlled chamber at 25 ± 1 °C. The data were logged by a personal computer, using an analog-to-digital converter and custom-made software. Ten experimental runs were performed for each group (n = 10). Shrinkage stress was calculated by dividing force values by the surface area of the composite specimen base (28 mm²). The obtained data were used to plot the curves of polymerization shrinkage stress versus time. First derivatives of these curves were calculated as a measure of the shrinkage stress rate. The plots of first derivatives versus time were used to estimate kinetic parameters: maximum shrinkage stress rate and time to achieve maximum shrinkage stress rate.

Statistical analysis

Normality of distribution and homogeneity of variances were checked using Levene’s and Shapiro–Wilk’s tests, respectively. The effects of the BG type and BG amount were investigated by two-way ANOVA. After obtaining highly significant results (p < 0.001) for both factors and their interactions, mean values of linear shrinkage, DC, shrinkage stress, maximum shrinkage stress rate, and time to achieve maximum shrinkage stress rate were compared among the composites using one-way ANOVA and Tukey’s adjustment for multiple comparisons. The statistical analysis was performed using SPSS (version 20, IBM, Armonk, NY, USA) at an overall level of significance of α = 0.05.

Results

The real-time linear shrinkage and shrinkage stress data are illustrated in Figs. 1 and 2, respectively. Plots in Fig. 1 were used to determine linear shrinkage values at the end of the 15-min observation period, whereas the plots in Fig. 2 were used to determine the shrinkage stress at the end of the 15-min observation period, and the kinetic parameters: maximum shrinkage stress rate and time to achieve maximum shrinkage stress rate.

Figure 1.

Averaged curves (n = 10) of linear shrinkage for the composites functionalized with bioactive glass 45S5 (continuous lines) and the experimental bioactive glass (dashed lines).

Figure 2.

Averaged curves (n = 10) of shrinkage stress for the composites functionalized with bioactive glass 45S5 (continuous lines) and the experimental bioactive glass (dashed lines).

Linear shrinkage values measured 15 min after the start of light-curing are shown in Fig. 3. The addition of 10–20 wt% of BG 45S5 significantly increased linear shrinkage compared to the control composite. Within the C-series, a significant decrease in linear shrinkage was identified with increasing amounts of BG 45S5. The addition of 10 wt% of the experimental BG produced linear shrinkage similar to that of the control composite, whereas 20–60 wt% of the experimental BG significantly increased linear shrinkage.

Figure 3.

Linear shrinkage (mean values ± standard deviation) measured after 15 min. Same letters denote statistically homogeneous groups.

The DC after 15 min of the start of light-curing is shown in Fig. 4. The composite with 10 wt% of BG 45S5 had similar DC as the control composite, whereas higher amounts of BG 45S5 led to significantly lower DC values. Within the C-series, an overall trend of DC decline with increasing amounts of BG 45S5 was observed. In contrast, the DC values of all composites in the E-series were statistically similar to that of the control composite.

Figure 4.

Degree of conversion (mean values ± standard deviation) measured after 15 min. Same letters denote statistically homogeneous groups.

Shrinkage stress values measured 15 min after the start of light-curing are shown in Fig. 5. The addition of BG 45S5 resulted in a significant decline in shrinkage stress. In contrast, the addition of the experimental BG led to shrinkage stress values similar to that of the control composite, except for 40 wt% of the experimental BG, which produced a significantly higher shrinkage stress.

Figure 5.

Shrinkage stress (mean values ± standard deviation) measured after 15 min. Same letters denote statistically homogeneous groups.

Maximum shrinkage stress rates are shown in Fig. 6. The addition of BG 45S5 resulted in a significant decrease in maximum shrinkage stress rate. Compared to the control composite, the shrinkage stress rates for the composites functionalized with the experimental BG were unchanged (for 10 wt%), increased (for 20 and 40 wt%), or reduced (for 60 wt%).

Figure 6.

Maximum shrinkage stress rate (mean values ± standard deviation). Same letters denote statistically homogeneous groups.

The time to achieve maximum shrinkage stress rate is shown in Fig. 7. The addition of BG 45S5 resulted in a significant increase in the time to achieve maximum shrinkage stress rate. The addition of 10–40 wt% of the experimental BG had no effect on time to achieve maximum shrinkage stress rate, whereas a significantly longer time to achieve maximum shrinkage stress rate was observed for 60 wt% of the experimental BG.

Figure 7.

Time to achieve maximum shrinkage stress rate (mean values ± standard deviation). Same letters denote statistically homogeneous groups.

Discussion

This study investigated the effect of replacing silanized reinforcing fillers with 0–60 wt% of different unsilanized BG fillers on shrinkage properties of experimental composites. Although the composites with high amounts of unsilanized BG fillers would not be beneficial clinically due to their poor mechanical properties¹³, the wide range of BG amounts was chosen in order to explore shrinkage behaviour as a function of the wt% of unsilanized BG fillers²². The first null hypothesis was accepted only for the DC of the composites functionalized with the experimental BG, which was not affected by the BG amount. As the BG amount and type significantly influenced linear shrinkage, shrinkage stress, maximum shrinkage rate, and time to achieve maximum shrinkage rate, both null hypotheses were rejected for these properties.

The decrease of DC with increasing BG amounts observed in the composites functionalized with BG 45S5 is consistent with previous studies of experimental composites featuring similar compositions^32,33. On the other hand, no negative effect on DC was identified in composites functionalized with the experimental low-sodium fluoride-containing BG in a previous study¹² nor in the present study. The potential of BG 45S5 for inhibiting methacrylate polymerization and limiting the final DC has been tackled in previous studies^12,32–35, and the polymerization inhibition was explained by the inactivation of free radicals mediated by oxides on the surface of unsilanized BG particles³⁶. A detailed analysis of the mechanisms responsible for different effects of BG 45S5 and the experimental BG on polymerization reaction and final DC values is out of the scope of this study. Nevertheless, the significantly different influence of the two types of BG fillers on the DC of experimental composites enabled insight into shrinkage behaviour that was either governed by the changing DC (C-series) or that was DC-independent (E-series). As DC has been shown to be diminished at the boundary layer of resin that is immediately adjacent to filler particles, incorporating larger particles reduces total filler surface area and thus can be expected to improve DC³⁷. This improvement in DC was not identified in our study when smaller reinforcing filler particles (d50 = 1 µm) were replaced by larger BG fillers (d50 = 3 µm). Considering that BG fillers had a wide particle size distribution, it is likely that the nominal difference in d50 was too small to exert a measurable effect on DC. Even though the DC in the E-series was not affected by the presence of BG fillers, the BG amounts of 20 wt% and higher led to a significant increase in linear shrinkage. Unlike volumetric shrinkage, which is expected to increase proportionally to DC²⁰, linear shrinkage can deviate from being directly dependent on DC due to the tendency of linometers to measure only the portion of shrinkage that takes place after gelation³⁸. Before the onset of gelation, the reduction in the volume of the discoid specimen can be partly compensated by the shrinkage in the radial direction³⁹. At the gel point, the polymerizing composite reaches the elastic modulus that is sufficient for overcoming the gravitational force of the aluminium platelet (0.004 N) and producing a measurable displacement⁴⁰. Therefore, the development of the composite’s viscoelastic properties during polymerization determines the fraction of volumetric shrinkage that is captured by linear measurements. As the viscoelastic properties of the experimental composites in this study were affected by variations in relative amounts of silanized and unsilanized fillers²¹, different fractions of total volumetric shrinkage were captured by linear measurements. Because the development of shrinkage stress is primarily governed by post-gel shrinkage, the obtained linear shrinkage values are meaningful regardless of not being directly correlated to the overall volumetric shrinkage.

In analogy to the E-series, an increase in linear shrinkage caused by the addition of BG fillers was also identified in the C-series for BG amounts of 10–20 wt% (compared to the control composite). For higher BG amounts (40–60 wt%), that effect was surpassed by a significant decrease in DC, leading to the overall lower linear shrinkage. Considering the results from the C-series and E-series together, it appears that the addition of unsilanized BG fillers increased linear shrinkage unless the DC was diminished due to high BG amounts. In the latter case, the effect of diminished DC prevailed, leading to an overall decrease in linear shrinkage.

The trend of DC being decreased by increasing BG amounts appears to be the major determinant of shrinkage stress behaviour in the C-series. As DC was gradually reduced throughout the C-series, the shrinkage stress parameters were affected accordingly: shrinkage stress after 15 min and maximum shrinkage stress rate were decreased, whereas the time to achieve maximum shrinkage rate was prolonged. An exception to this pattern was identified for high amounts of BG 45S5 (40–60 wt%) for which the DC values reached a plateau, whereas the trend of decreasing shrinkage stress and maximum stress rate continued. Variations in the BG amount thus produced a comparatively more pronounced influence on shrinkage stress parameters than on DC. Nevertheless, even small, non-significant DC differences can lead to significant differences in elastic moduli⁴¹, which in turn reflect on shrinkage stress. This might explain why statistically significant differences in the shrinkage stress properties were observed throughout the whole C-series despite the corresponding DC values plateauing for BG amounts of 40–60 wt%.

The fact that the DC in the E-series remained unchanged by varying BG amounts helped to isolate the direct effect of unsilanized BG fillers on shrinkage stress development without the influence of DC as a confounding factor. Contrary to the expectations derived from previous studies that increasing amounts of unsilanized BG fillers would diminish shrinkage stress^21,22, such an effect was not observed. Moreover, a small but statistically significant increase in shrinkage stress and maximum stress rate was identified for the composites with intermediate BG amounts (E-40 for shrinkage stress; E-20 and E-40 for maximum stress rate). Although being surprising, the results of shrinkage stress peaking for a certain BG amount and decreasing for lower or higher BG amounts are in line with a report which showed that the addition of unsilanized fillers does not necessarily affect shrinkage stress in a mathematically monotonic manner²². The shrinkage stress development is determined by a complex interaction of the composite’s viscoelastic properties and polymerization kinetics. Both of these factors are independently affected by varying proportions of silanized and unsilanized fillers^21,42. Additionally, the interactions of unsilanized fillers with monomers can affect molecular mobility at the filler/resin interface, thereby counteracting the expected reduction in shrinkage stress²¹. These interactions produced a non-monotonic dependence of shrinkage stress properties on the amount of BG fillers, whereby shrinkage stress and maximum stress rate reached peak values for certain BG amounts (40 and 20 wt%, respectively), and declined afterward. On the other hand, the time to achieve maximum shrinkage rate was constant for BG amounts of up to 40 wt% and then increased for 60 wt% of BG.

The aforementioned small, but statistically significant, increase in polymerization shrinkage stress and stress rate identified in the E-series was speculated to originate from the effect of unsilanized BG particles on the development of viscoelastic properties during polymerization. A detailed rheokinetic analysis was not performed in the present study because such measurements are inherently challenging^43,44, and the hypothesized effect of unsilanized particles on stress reduction was not expected to be mediated by changes in rheological behaviour. Instead, the stress reduction was expected to occur due to the formation of gaps at the filler/resin interface²³, and consequently lower interfacial stress concentration²². As the stress reduction was not identified in the E-series, and the addition of unsilanized fillers has been previously reported to increase the viscosity of experimental composites²¹, the effect of unsilanized fillers on rheological properties was speculated to have caused the small increase in polymerization shrinkage stress and stress rate in the E-series. Another factor that might have affected the rheological properties of the experimental composites is the difference in particle size between the reinforcing and BG fillers. However, considering that the grinding processing of glass fillers produced wide particle size distributions, the nominal differences in particle size likely had a negligible impact on the obtained results.

The effect of the unsilanized BG fillers on the reduction of shrinkage stress was identified only as a consequence of the reduction in DC (C-series) but not when DC was maintained (E-series). Except the significantly slower development of shrinkage stress in the composite with the highest BG amount (E-60), no direct DC-independent reduction of shrinkage stress was produced by the unsilanized BG fillers. The discrepancy between these results and the results of the previous studies that identified a stress-reducing potential of unsilanized fillers^21,22 can be attributed to two major differences in experimental conditions. First, the mentioned studies used nano-sized silica particles (average size of 40 nm), whereas the BG particles used in the present study were two orders of magnitude larger. A considerable difference in the interfacial surface area between the resin and unsilanized filler particles could have affected their potential to relieve shrinkage stress. Second, shrinkage stress in the mentioned studies was measured using a rigid device with a feedback loop that compensated for load cell compliance. The stress values obtained by this type of devices are more sensitive to the composite’s elastic modulus compared to the stress values obtained by a more compliant device used in the present study⁴⁵. It is therefore plausible that the results of the mentioned studies^21,22 were governed by the effect of unsilanized fillers on the development of composite’s elastic modulus during polymerization, whereas our results were more dependent on the effect of the unsilanized BG fillers on the resin mobility. Considering the major role of device compliance in the measurements of shrinkage stress, the results obtained using compliance similar to that of dental hard tissues in this study can be regarded as more clinically meaningful than those obtained in highly rigid setups⁴⁶.

Considering the negative effects of unsilanized BG fillers on the mechanical properties of resin composites^13,14, it should be noted that the clinical advantage of the shrinkage stress relief identified in the C-series may be limited. Although considerable stress reductions were observed in the C-series by using BG amounts of 40–60 wt%, such high fractions of unsilanized versus reinforcing fillers would considerably diminish mechanical properties, especially since higher BG amounts also led to reduced DC⁴⁷. The mechanical properties could be expected to further decrease over time due to high water sorption caused by soluble BG fillers⁴⁸.

The curing conditions used in this study were determined in a preliminary study, which showed that curing with 1340 mW/cm² for 20 s produced homogeneous curing throughout the 1.5 mm thick specimens. Although the specimens were thoroughly cured, the development of polymerization shrinkage stress might have been influenced by the effect of unsilanized BG fillers on polymerization kinetics³³. This aspect will be addressed in forthcoming studies that will investigate the dynamic changes of DC and light transmittance during polymerization using real-time FTIR and UV–vis spectrometry, respectively.

Conclusions

The effect of unsilanized bioactive glass fillers on polymerization shrinkage properties differed between two types of bioactive glass. The diminishing effect of bioactive glass 45S5 on shrinkage stress was mediated by a decrease in degree of conversion caused by this bioactive glass type. In contrast, no reduction of shrinkage stress was observed for the experimental low-sodium fluoride-containing bioactive glass. Therefore, the hypothesized benefits of unsilanized bioactive glass fillers on the reduction of polymerization shrinkage stress were not identified under the conditions of this study, unless this reduction was attained indirectly through a diminished degree of conversion.

Author contributions

M.P. research idea, study conception, experimental design, performed experiments, data acquisition and interpretation, statistical analysis, wrote manuscript. D.M. study conception, data interpretation, revised and approved final manuscript. T.A. study conception, experimental design, supervision, data interpretation, revised and approved final manuscript. Z.T. study conception, experimental design, supervision, data interpretation, revised and approved final manuscript. T.T.T. research idea, study conception, experimental design, supervision, data interpretation, revised and approved final manuscript.

Funding

The research was funded by a grant of the Swiss Federal Department of Economic Affairs, Education and Research (2019.0221).

Data availability

The datasets generated during and/or analysed during the current study are available from the corresponding author on reasonable request.