Bio-assisted synthesized Ag(0) nanoparticles stabilized on hybrid of sepiolite and chitin: efficient catalytic system for xanthene synthesis

Fatemeh Ghoreyshi Kahangi 1, Morteza Mehrdad 1, Majid M Heravi 2,✉, Samahe Sadjadi 3,✉
PMCID: PMC7499264  PMID: 32943666

Abstract

In this work, with the use of two natural compounds, chitin and sepiolite clay, a novel covalent hybrid is fabricated and applied as a support for the stabilization of silver nanoparticles with the aid of Kombucha extract as a natural reducing agent. The resultant catalytic system, Ag@Sep-N–CH, was characterized via XRD, TEM, FTIR, ICP, SEM, TGA, UV–Vis and BET. It was found that fine Ag(0) nanoparticles with mean diameter of 6.1 ± 1.8 nm were formed on the support and the specific surface area of the catalyst was 130 m2 g−1. The study of the catalytic performance of Ag@Sep-N–CH for catalyzing synthesis of xanthenes in aqueous media under mild reaction condition confirmed that Ag@Sep-N–CH exhibited high catalytic activity and could promote the reaction of various substrates to furnish the corresponding products in high yields. Moreover, the contribution of both chitin and sepiolite to the catalysis has been affirmed. It was found that hybridization of these two components led to synergistic effects and consequently improved the observed catalytic activity. Notably, the catalyst was recyclable up to several reaction runs.

Subject terms: Chemistry, Catalysis

Introduction

Use of metallic nanoparticles in catalysis is a hot topic in chemistry and in recent decades various nanocatalysts have been devised for vast chemical transformations. One of the most reported metallic nanoparticles is silver nanoparticle that has the capability of catalyzing numerous reactions. Moreover, this nanoparticle is a promising choice for other applications such as environmental remediation and sensing1–4. To form silver nanoparticles, silver salts are reduced via a reducing agent. Classically, chemical reducing reagents such as hydrazine hydrate are used for this purpose4,5. In a more eco-friendly approach, bio-based reducing agents such as plant extracts that are cost effective and non-hazardous reducing agents can replace the conventional chemical ones6.

Use of natural clays as low cost and available catalyst support is not a new topic and to date various clays have been reported for this purpose. The main advantages of clays are their high thermal and chemical stability and the presence of some functionalities that makes their tuning possible. Moreover, the chemical compositions and morphologies of clays can impart interesting features to them. Sepiolite (Sep) is a natural rod-like clay with compositional formula of Mg8Si12O30(OH)4(OH2)4·nH2O7. The structural unit in this hydrated Mg–Al silicate8 is composed of two tetrahedral silica sheets and a central octahedral sheet containing magnesium9. This feature along with the porosity of this clay gave rise to its extensive use for the catalytic applications10–12.

As xanthenes exhibit biological and pharmacological properties13–17, their synthesis has attained significant attention and numerous reports have been published on the synthesis of diverse derivatives of these heterocycles18,19. In fact, xanthenes not only found many applications in chemistry and pharmacology, they have been extensively utilized in other domains such as pH-sensitive fluorescent materials and dyes. As xanthene synthesis is a catalytic process, the key issue is evolving an effective catalyst that benefits from some features such as high activity, low-cost and reusability. Although various catalysts ranging from ionic liquids to nanoparticles have yet been developed, there are some unaddressed shortcomings and challenges20–24.

In the continuation of research on heterogeneous catalysts based on clays and clay-carbohydrate hybrids25–29, herein we wish to report a covalent hybrid of sepiolite clay and chitin (CH), Fig. 1, and its utility as a support for the stabilization of silver nanoparticles with assistance of Kombucha extract as a natural reducing agent. The catalytic activity of the resulting hybrid, Ag@Sep-N–CH, was appraised for one-pot synthesis of xanthenes in aqueous media and under mild reaction condition. Furthermore, the roles of sepiolite and chitin in catalysis were evaluated and the recyclability of the catalyst has been examined.

Figure 1.

Figure 1

Open in a new tab

The schematic procedure for the synthesis of Ag@Sep-N–CH.

Characterization

To assess the morphological change of sepiolite after incorporation of CH and Ag(0) nanoparticles, the TEM image of sepiolite (Fig. 2A) and Ag@Sep-N–CH (Fig. 2B,C) were recorded. As shown in Fig. 2A, the TEM analysis of sepiolite revealed that this clay showed rod like morphology. In Ag@Sep-N–CH TEM images (Fig. 2B,C), the sepiolite rods can be discerned, indicating that upon covalent grafting with CH and immobilization of silver nanoparticle, sepiolite morphology did not alter. On the other hand, in some parts of sepiolite rods, fine sheet can be observed that can be ascribed to CH. Furthermore, the spherical black spots on the sepiolite rods are ascribed to the silver nanoparticles. Measurement of silver nanoparticle sizes, Fig. 2D, showed that the mean diameter of these particles was 6.1 ± 1.8 nm.

Figure 2.

Figure 2

Open in a new tab

(A) TEM image of sepiolite and (B, C) TEM images of Ag@Sep-N–CH. (D) Particle size distribution graph of Ag(0) nanoparticles.

In Fig. 3, the SEM images of sepiolite (Fig. 3A), Sep-N–CH (Fig. 3B) and Ag@Sep-N–CH (Fig. 3C) are illustrated. As shown, the SEM image of sepiolite is distinguished from Sep-N–CH. This observation indicated that introduction of CH induced morphological change to some extent. The morphology of Ag@Sep-N–CH is almost similar to that of Sep-N–CH, implying that immobilization of silver nanoparticles has slight effect on the morphology. This issue can be due to the low content of silver nanoparticles in the structure of the catalyst.

Figure 3.

Figure 3

Open in a new tab

SEM images of (A) sepiolite, (B) Sep-N–CH and (C) Ag@Sep-N–CH.

To confirm grafting of CH to sepiolite and formation of Ag@Sep-N–CH, TG curve of Ag@Sep-N–CH was compared with that of CH and sepiolite, Fig. 4. As illustrated, among three TG curves shown in Fig. 4, CH and sepiolite showed the lowest and the highest thermal stability respectively. This is a rational result as sepiolite is an inorganic clay with instinctive high thermal stability, while CH is a carbohydrate with low thermal resistance. The thermal stability of Ag@Sep-N–CH is between the two aforementioned samples, implying the conjugation of low thermally stable CH on sepiolite. In more detail, in the TG curve of Ag@Sep-N–CH, the first weight loss, discerned below 200 °C is due to the loss of structural water, while the second one at 380 °C is the sign of degradation of CH. According to TGA results, the content of CH was evaluated as 28 wt%.

Figure 4.

Figure 4

Open in a new tab

TG curves of CH, Sep and Ag@Sep-N–CH.

To verify the structure of the inorganic–organic hybrid of Ag@Sep-N–CH, FTIR spectrum of Ag@Sep-N–CH was achieved and compared with that of each components, Fig. 5. In the spectrum of sepiolite, the absorbance band at 1,014 cm−1 is observed due to the Si–O stretching. Additionally, the absorbance bands discerned at 3,560, 3,428, and 645 cm−1 are representative of stretching and bending vibrations of –OH functionality30. In the FTIR spectrum of CH, the absorbance bands of CH at 3,444 cm−1, 1662 cm−1 can be observed. In the case of the FTIR spectrum of Ag@Sep-N–CH, all the discussed absorbance bands can be detected. However, as the distinctive bands of CH overlapped with that of sepiolite, FTIR spectroscopy cannot provide enough proofs for confirming the formation of the hybrid. Notably, the shifts of the bands can be attributed to the interactions between functionalized CH and sepiolite.

Figure 5.

Figure 5

Open in a new tab

FTIR spectra of CH, Sep and Ag@Sep-N–CH.

As the specific surface area is one of the most important features of catalysts, this value was estimated for Ag@Sep-N–CH via BET method. Moreover, the specific surface area of the catalyst was compared with that of sepiolite. The results approved that upon grafting CH, the specific surface area of sepiolite reduced from 161 to 130 m2 g−1. Moreover, upon introduction of silver nanoparticles, the pore volume and pore diameter reduced to 30.0 cm3 g−1 and 2.2 nm respectively. Furthermore, the recorded nitrogen adsorption–desorption isotherm was of the type II with H3 hysteresis loops, Figure S131.

The XRD patterns of sepiolite and Ag@Sep-N–CH are illustrated in Figure S2. As shown the two XRD patterns are similar and displayed similar bands that can be assigned to sepiolite structure8. The reason for not observing the bands of silver nanoparticles can be accredited to low content of silver nanoparticles32.

To verify the potential of the extract for reducing Ag(I) to Ag(0), UV–Vis spectra of Kombucha extract and the mixture of Kombucha extract and AgNO3 were obtained, Fig. 6. It is well-established that Ag(0) nanoparticles displayed a specific band in the UV–Vis spectrum at λmax = 430 nm33,34 that can approve the reduction of Ag(I) to Ag(0). As shown, in Fig. 6, in the UV–Vis spectrum of the mixture of AgNO3 and Kombucha extract, the so-called characteristic band can be discerned, while this band is not appeared in the spectrum of Kombucha extract. This result indicated the successful reduction of silver salt via Kombucha extract.

Figure 6.

Figure 6

Open in a new tab

UV–visible spectra of Kombucha extract and the mixture of AgNO3 and Kombucha extract.

The loading of silver nanoparticles on Sep-N–CH was measured by ICP analysis as 0.5 w/w%.

Catalytic activity

To appraise the catalytic performance of Ag@Sep-N–CH, synthesis of xanthene derivatives from reaction of aldehydes and dimedone was targeted. In the onset, by using reaction of benzaldehyde and dimedone as a model reaction, the reaction parameters such as solvent, catalyst loading and temperature have been optimized. In this regard, first, the model xanthene derivative was synthesized by using 0.02 g Ag@Sep-N–CH in water as solvent at room temperature. It was revealed that (Table S1) in this condition only moderate yield of the desired product has been achieved. To improve the yield of the product, the reaction was examined in different solvents. It was determined that the best result was obtained in H2O: EtOH (1:2). Next, to elucidate the influence of the reaction temperature on the yield of the product, the model reaction was repeated at 50 and 70 °C. As listed in Table S1, the optimum reaction temperature was found as 50 °C. Finally, the influence of the loading of Ag@Sep-N–CH was scrutinized by using 0.02–0.04 g catalyst. The results demonstrated that increase of the catalyst loading from 0.02 to 0.03 g gave rise to the increase of the reaction yield. However, increase of this value to 0.04 g had no effect on the yield of the product.

After finding the optimum reaction condition, more precise study on the role of the hybrid components has been carried out. First, the necessity of silver nanoparticles on the structure of the catalyst was appraised. In this context, a control catalyst, Sep-N–CH was prepared similar to the reported procedure and its activity for catalyzing the synthesis of the model xanthene was examined. The result, Table 1, affirmed that Sep-N–CH exhibited moderate catalytic activity and led to the formation of the desired product in 50% yield. This observation confirmed the necessity of incorporation of silver nanoparticles for achieving high catalytic activity. Next, to elucidate the efficiency of CH-NH2 and Sep-Cl as catalyst supports and investigate whether there is any synergism between functionalized chitin and sepiolite, two samples, Ag@Sep-Cl and Ag@CH-NH2, were fabricated through wet impregnation of silver nanoparticles on CH-NH2 and Sep-Cl as supports and then the activities of these samples for the model reaction were measured. As shown in Table 1, these two samples displayed moderate catalytic activities that were inferior compared to Ag@Sep-N–CH. This observation confirms that hybrid of CH-NH2 and Sep-Cl is a more effective support compared to sole CH-NH2 and Sep-Cl. This can be due to the synergism between the hybrid components.

Table 1.

Comparison of the catalytic activity of Ag@Sep-N–CH with some control catalysts.

Entry Catalyst Reaction time (h) Yield (%)a
1 Ag@Sep-N–CH 3 95
2 Sep-N–CH 5 50
1 Ag@Sep-Cl 4 65
3 Ag@CH-NH2 3.5 78
Open in a new tab

aReaction condition: 1 mmol of benzaldehyde and 2 mmol of dimedone and 0.03 g of catalyst at 50 °C in the mixture of H2O:EtOH (1:2).

In the next section, the scope of the present procedure is evaluated. In this regard, various aldehydes with electron-withdrawing and electron-donating groups were applied as starting materials for the synthesis of the corresponding xanthenes. Moreover, heterocyclic aldehyde, furfural has also been utilized as a substrate. The results, Table 2, established that all the used substrates could undergo the reaction using Ag@Sep-N–CH catalyst and led to the high yields of the corresponding xanthene derivatives. This result confirmed that this protocol can be generalized to diverse range of aldehydes.

Table 2.

Synthesis of various xanthenes under Ag@Sep-N–CH catalysis.graphic file with name 41598_2020_71866_Figa_HTML.jpg

Entry Substrate Yield (%)
1 Benzaldehyde 95
2 4-NO2-benzaldehyde 90
3 2-NO2-benzaldehyde 98
4 4-Me-benzaldehyde 93
5 4-MeO-benzaldehyde 90
6 2-MeO-benzaldehyde 90
7 4-Cl-benzaldehyde 95
8 Furfural 90
Open in a new tab

Comparison of the catalytic activity of Ag@Sep-N–CH with other catalysts

In the next part, Ag@Sep-N–CH performance for catalyzing the synthesis of the model xanthene was compared with some other catalysts, Table 3. Considering the fact that xanthenes are biologically-active compounds, various researchers focused on evolving efficient catalysts for their synthesis. Among the reported procedures in Table 3, some of them were not efficient and gave rise to low yields of the desired xanthene. Other tabulated catalysts showed competitive efficiency compared to Ag@Sep-N–CH. Although due to the different reaction condition, a precise comparison cannot be achieved, it can be inferred that Ag@Sep-N–CH can be recognized as an effective catalyst with comparable performance with reported catalysts. In detail, in the present protocol, high yield of the product can be achieved in aqueous media with use of relatively low catalyst loading at low temperature.

Table 3.

The comparison of the performance of Ag@Sep-N–CH with some other catalysts.

Entry Catalyst Solvent catalyst loading Temp. (°C) Yield (%) References
1 Ag@Sep-N–CH H2O:EtOH 0.03 g 50 95 This work
2 Nano-ZnO – 10 mol% 100 Trace 21
3 Fe2(SO4)3.7H2O – 10 mol% 120 86 35
4 Fe3O4@SiO2–SO3H – 0.05 g 110 97 22
5 Silica-bonded S-sulfonic acid (SBSSA) EtOH 0.03 g Reflux 98 23
6 Nano-NiO – 10 mol% 100 Trace 21
7 Barium Perchlorate EtOH 15 mol% Reflux 95 36
8 Nano titania-supported sulfonic acid (n-TSA) – 0.013 g 90 91 21
Open in a new tab

Reaction mechanism

According to the literature37, Ag@Sep-N–CH catalyzed synthesis of xanthene derivatives can be described as follow: Initially, Ag@Sep-N–CH activated the aldehyde. The activated aldehyde then reacted with the enol form of dimedone (Fig. 7) to generate an intermediate I. The latter underwent dehydration to form intermediate II. In the next step, intermediated II reacted with the second molecules of dimedone to furnish compound III. The latter then tolerated dehydration followed by cyclization to produce xanthene.

Figure 7.

Figure 7

Open in a new tab

Plausible reaction mechanism for the synthesis of xanthenes.

Catalyst reusability

To examine the reusability of Ag@Sep-N–CH, the synthesis of the model xanthene derivative was carried out by using the reused Ag@Sep-N–CH under the optimum condition. It was found out that by using the reused catalyst, the yield of the model reaction did not alter and remained as 95%. Encouraged by this result, the reused catalyst was recovered and applied for the third run of the same reaction. The result, Fig. 8A, demonstrated that upon third use, the reaction yield decreased from 95 to 80%. Reuse for the fourth time also confirmed further decrement of the yield of the model xanthene (75%). Finally, use of Ag@Sep-N–CH for the fifth run of the reaction resulted in significant drop of the efficiency of the catalyst to 50%.

Figure 8.

Figure 8

Open in a new tab

(A) Reuse of Ag@Sep-N–CH for the synthesis of the model xanthene derivative under optimum reaction condition. (B) TEM image of the reused Ag@Sep-N–CH after five runs of the model reaction under optimum reaction condition.

It was postulated that the reduction of the activity of Ag@Sep-N–CH can originate from leaching of silver nanoparticles that played the main role in the catalysis. To validate this assumption, Ag(0) loading of the recycled Ag@Sep-N–CH was measured via ICP method. It was determined that no leaching was occurred upon second run of the reaction. However, further reuse of Ag@Sep-N–CH triggered Ag(0) leaching and this value increased by increase of the number of cycles and reached to 10 wt.% of the initial loading of the fresh Ag@Sep-N–CH upon the fifth run.

The morphological change of Ag@Sep-N–CH after fifth run of the model reaction was also appraised. As shown in Fig. 8B, the TEM image of the reused Ag@Sep-N–CH affirmed that reuse of the catalyst caused agglomeration and increase of the average size of Ag(0) nanoparticles to some extent (the estimated mean particle size was 6.8 ± 1.5 nm). This issue can also contribute to the observed lower activity of the reused Ag@Sep-N–CH.

Experimental

Materials

Used chemicals for this research included, chitin (CH), Ag(NO3), (3‐amino propyl) triethoxysilane (APTES), (3-chloropropyl) trimethoxysilane (CPTES), dimedone, aldehydes, distilled water, toluene and ethanol. All chemicals were purchased from Sigma-Aldrich and used with no further purification. Sepiolite clay (Sep), PANGEL S9, was provided from TOLSA. The extract of that is a fermented mixture of yeast and bacteria was purchased from local store.

Instrumentation and analysis

The applied instruments for the characterization of Ag@Sep-N–CH were follow: BRUKER, EQUINOX 55 apparatus for powder Fourier transform infrared (FT-IR) spectroscopy, METTLER TOLEDO instrument with heating rate of 10 °C min−1 for ), thermogravimetric analysis (TGA) under nitrogen atmosphere. Philips CM30300Kv instrument for transmission electron microscopy (TEM), BELSORP Mini II apparatus for Brunauer–Emmett–Teller (BET) analysis (degassing at 150 °C for 2 h). Siemens, D5000 apparatus using graphite monochromatic Cu-Kα for X-ray diffraction (XRD) analysis, UV–visible Spectrophotometer (PerkinElmer, Lambda 365) and Vista-pro for Inductively Coupled Plasma (ICP) analysis. Tescan instrument was used for recording SEM images.

Catalyst fabrication

Synthesis of the catalyst

Synthesis of Cl‐functionalized sepiolite (Sep‐Cl)

Sepiolite (2 g) was suspended in 80 mL toluene and mixed vigorously for 15 min. Subsequently, CPTES (2 mL) was added gradually and the mixture was sonicated for 30 min and then refluxed for 48 h at 110 °C under N2 atmosphere. At the end, the solid was filtered, washed several times with toluene and dried in a vacuum oven at 90 °C overnight.

Synthesis of amine‐functionalized chitin (CH-NH2)

A solution of APTES (2 mL) was added to a suspension of chitin (2 g) in dry toluene (40 mL). The mixture was then sonicated (power of 100 W) for 30 min and refluxed for 24 h at 110 °C. Afterwards, the resultant suspension was filtered and washed repeatedly with dry toluene and dried at 100 °C overnight.

Synthesis of sepiolite–chitin (Sep-N–CH)

Sepiolite-Cl (1.5 g) in dry toluene (30 mL) was suspended. Meanwhile, CH-NH2 (1.5 g) was crushed and well dispersed in toluene (30 mL) using ultrasonic irradiation of 100 W. Then, the two aforementioned suspension were mixed and refluxed for 24 h at 110 °C under N2 atmosphere. Upon completion of the reaction, the solid was filtered and placed in water. Then, the aqueous suspension was centrifuged. The obtained Sep-N–CH was gathered, washed with toluene repeatedly and dried in a vacuum oven at 100 °C.

Synthesis of Ag NPs and their embedding into Sep-N–CH: synthesis of Ag@Sep-N–CH

Sep-N–CH (1 g) was dispersed into a solution of AgNO3 (0.1 g) in deionized H2O (20 mL) under stirring condition at room temperature for 30 min. The silver ions were adsorbed onto the surfaces of Sep-N–CH via electrostatic attraction. Afterwards, the fresh extract of Kombucha (2 mL in 20 mL DW) as a reducing agent was added into the suspension. Upon addition of the Kombucha extract, the colour of the mixture darkened, which affirmed the reduction of silver ions to Ag(0). To stabilize Ag(0) NPs on Sep-N–CH, the mixture was stirred for 12 h. Finally, the product was separated and washed three times with EtOH/H2O and dried at 60 °C for 12 h, Fig. 1.

General procedure for xanthene synthesis

Aldehyde (1 mmol) and dimedone (2 mmol) were dissolved in 1:2 H2O: EtOH (3 mL). Then, Ag@Sep-N–CH (0.03 g) was introduced and the mixture was agitated at 50 °C for 3 h. At the end of the reaction, monitored by TLC, the reaction mixture was diluted with EtOH (15 mL) and Ag@Sep-N–CH was separated via simple filtration. Xanthene was then purified via recrystallization with EtOH. The yields of the reactions were measured by using GC.

Recycling of the catalyst

After the first run of the reaction, the catalyst was separated and washed with hot EtOH for three times. Subsequently, the recovered catalyst was dried in oven at 100 °C overnight and re-used for the next run of the reaction.

Conclusion

With the aim of using naturally occurring compounds for the catalytic purposes, chitin and sepiolite have been functionalized and covalently grafted. Subsequently, the resulting hybrid, Sep-N–CH, was used as a support for the stabilization of silver nanoparticles, reduced by the extract of Kombucha. Interestingly, the resultant catalyst, Ag@Sep-N–CH, exhibited high catalytic activity for promoting one-pot reaction of dimedone and aldehydes in aqueous media to furnish xanthene derivatives in high yields. The study of some control samples, including Ag@Sep-Cl and Ag@CH-NH2 affirmed superior activity of Ag@Sep-N–CH. This result established that hybridization of CH-NH2 and Sep-Cl can improve the activity of the final catalyst due to the synergistic effects. The present protocol for xanthene synthesis showed broad substrate scope and various aldehydes could tolerate this reaction to furnish the corresponding products in high yields. The study of the recyclability of the catalyst confirmed that although Ag@Sep-N–CH maintained its activity for the second run, upon further reuse its activity dropped and reached from 95 to 50% after fifth run.

Supplementary information

Supplementary Information. (1.4MB, docx)

Acknowledgments

The authors appreciate the support of Iran Polymer and Petrochemical Institute and Universities of Alzahra and Guilan.

Author contributions

F.G.K.: experimental work, M.M.: financial support, M.M.H.: financial support, supervision, S.S.: financial support, supervision, writing the article, management.

Competing interests

The authors declare no competing interests.

Footnotes

Publisher's note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Contributor Information

Majid M. Heravi, Email: m.heravi@alzahra.ac.ir

Samahe Sadjadi, Email: s.sadjadi@ippi.ac.ir.

Supplementary information

is available for this paper at 10.1038/s41598-020-71866-2.

References

  • 1.Sharma VK, Yngard RA, Lin Y. Silver nanoparticles: green synthesis and their antimicrobial activities. Adv. Colloid Interface Sci. 2009;145:83–96. doi: 10.1016/j.cis.2008.09.002. [DOI] [PubMed] [Google Scholar]
  • 2.Prow TW, Grice JE, Lin LL, Faye R, Butler M, Becker W, Wurm EMT, Yoong C, Robertson TA, Soyer HP, Roberts MS. Nanoparticles and microparticles for skin drug delivery. Adv. Drug Deliv. Rev. 2011;63:470–491. doi: 10.1016/j.addr.2011.01.012. [DOI] [PubMed] [Google Scholar]
  • 3.Kelly FM, Johnston JH. Colored and functional silver nanoparticle—wool fiber composites. ACS Appl. Mater. Interfaces. 2011;3:1083–1092. doi: 10.1021/am101224v. [DOI] [PubMed] [Google Scholar]
  • 4.Cheng F, Betts JW, Kelly SM, Schaller J, Heinze T. Synthesis and antibacterial effects of aqueous colloidal solutions of silver nanoparticles using aminocellulose as a combined reducing and capping reagent. Green Chem. 2013;15:989–998. doi: 10.1039/C3GC36831A. [DOI] [Google Scholar]
  • 5.Shahriary M, Veisi H, Hekmati M, Hemmati S. In situ green synthesis of Ag nanoparticles on herbal tea extract (Stachys lavandulifolia)-modified magnetic iron oxide nanoparticles as antibacterial agent and their 4-nitrophenol catalytic reduction activity. Mater. Sci. Eng. C. 2018;90:57–66. doi: 10.1016/j.msec.2018.04.044. [DOI] [PubMed] [Google Scholar]
  • 6.Malmir M, Heravi MM, Sadjadi S, Hosseinnejad T. Ultrasonic and bio-assisted synthesis of Ag@HNTs-T as a novel heterogeneous catalyst for the green synthesis of propargylamines: a combination of experimental and computational study: synthesis of Propargylamines by Ag@HNTs-T with Computational Study. Appl. Organomet. Chem. 2018;32:e4291. doi: 10.1002/aoc.4291. [DOI] [Google Scholar]
  • 7.Lv Y, Hao F, Liu P, Xiong S, Luo H. Improved catalytic performance of acid-activated sepiolite supported nickel and potassium bimetallic catalysts for liquid phase hydrogenation of 1,6-hexanedinitrile. J. Mol. Catal. A Chem. 2017;426:15–23. doi: 10.1016/j.molcata.2016.10.029. [DOI] [Google Scholar]
  • 8.Degirmenbasi N, Boz N, Kalyon DM. Biofuel production via transesterification using sepiolite-supported alkaline catalysts. Appl. Catal. B. 2014;150:147–156. doi: 10.1016/j.apcatb.2013.12.013. [DOI] [Google Scholar]
  • 9.Guishui L, Lijun C, Bing Z, Yi L. Novel Bi2O3 loaded sepiolite photocatalyst : Preparationand characterization. Mater. Lett. 2016;168:143–145. doi: 10.1016/j.matlet.2016.01.051. [DOI] [Google Scholar]
  • 10.Liu S, Zhu D, Zhu J, Yang Q, Wu H. Preparation of Ag@AgCl-doped TiO2/sepiolite and its photocatalytic mechanism under visible light. J. Environ. Sci. 2017;60:43–52. doi: 10.1016/j.jes.2016.12.026. [DOI] [PubMed] [Google Scholar]
  • 11.Zhou F, Yan C, Wang H, Zhou S, Komarneni S. Sepiolite-TiO2 nanocomposites for photocatalysis : Synthesis by microwave hydrothermal treatment versus calcination. Appl. Clay Sci. 2017;146:246–253. doi: 10.1016/j.clay.2017.06.010. [DOI] [Google Scholar]
  • 12.Ma Y, Wu X, Zhang G. Core-shell Ag@Pt nanoparticles supported on sepiolite nanofibers forthe catalytic reduction of nitrophenols in water: enhanced catalytic performance and DFT study. Appl. Catal. B. 2017;205:262–270. doi: 10.1016/j.apcatb.2016.12.025. [DOI] [Google Scholar]
  • 13.Zelefack F, Guilet D, Fabre N, Bayet C, Chevalley S, Ngouela S, Lenta BN, Valentin A, Tsamo E, Dijoux-Franca M-G. Cytotoxic and antiplasmodial xanthones from Pentadesma butyracea. J. Nat. Prod. 2009;72:954–957. doi: 10.1021/np8005953. [DOI] [PubMed] [Google Scholar]
  • 14.Nguyen HT, Lallemand MC, Boutefnouchet S, Michel S, Tillequin F. Antitumor psoropermum xanthones and sarcomelicope acridones: privileged structures implied in DNA alkylation. J. Nat. Prod. 2009;72:527–539. doi: 10.1021/np800644y. [DOI] [PubMed] [Google Scholar]
  • 15.Ion RM, Planner A, Wiktorowicz K, Frackowiak D. The incorporation of various porphyrins into blood cells measured via flow cytometry, absorption and emission spectroscopy. Acta. Biochim. 1998;45:833–845. doi: 10.18388/abp.1998_4279. [DOI] [PubMed] [Google Scholar]
  • 16.Saint-Ruf G, Hieu HT, Poupelin JP. The effect of dibenzoxanthenes on the paralyzing action of zoxazolamine. Naturwissenschaften. 1975;62:584. doi: 10.1007/BF01166986. [DOI] [PubMed] [Google Scholar]
  • 17.Li J, Lu L, Su W. A new strategy for the synthesis of benzoxanthenes catalyzed by proline triflate in water. Tetrahedron Lett. 2010;51:2434–2437. doi: 10.1016/j.tetlet.2010.02.149. [DOI] [Google Scholar]
  • 18.Yue X, Wu Z, Wang G, Liang Y, Sun Y, Song M, Zhan H, Bia S, Liu W. High acidity cellulose sulfuric acid from sulfur trioxide: a highly efficient catalyst for the one step synthesis of xanthene and dihydroquinazolinone derivatives. RSC Adv. 2019;9:28718–28723. doi: 10.1039/C9RA05748J. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 19.Bitaraf M, Amoozadeh A, Otokesh S. Nano-WO3-supported sulfonic acid: a versatile catalyst for the one-pot synthesis of 14-aryl-14h-dibenzo[a,j]xanthene derivatives under solvent-free conditions. Proc. Natl. Acad. Sci. 2019;89:437–443. doi: 10.1007/s40010-018-0498-2. [DOI] [Google Scholar]
  • 20.Salami M, Ezabadi A. A caffeine-based ionic liquid as a novel and eco-friendly catalyst for the synthesis of 1,8-dioxo-octahydroxanthenes under solvent-free conditions. Res. Chem. Intermed. 2019;45:3673–3686. doi: 10.1007/s11164-019-03814-3. [DOI] [Google Scholar]
  • 21.Amoozadeh A, Hosseininya SF, Rahmani S. Nano titania-supported sulfonic acid (n-TSA) as an efficient, inexpensive, and reusable catalyst for one-pot synthesis of 1, 8-dioxo-octahydroxanthene and tetrahydrobenzo[b]pyran derivatives. Res. Chem. Intermed. 2018;44:991–1011. doi: 10.1007/s11164-017-3148-4. [DOI] [Google Scholar]
  • 22.Naeimi H, Nazifi ZS. A highly efficient nano-Fe3O4encapsulated-silica particles bearing sulfonic acid groups as a solid acid catalyst for synthesis of 1,8-dioxo-octahydroxanthene derivatives. J. Nanopart. Res. 2013;15:2026–2037. doi: 10.1007/s11051-013-2026-2. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 23.Niknam N, Panahi F, Saberi D, Mohagheghnejad M. Silica-bonded S-sulfonic acid as recyclable catalyst for the synthesis of 1,8-dioxo-decahydroacridines and 1,8-dioxo-octahydroxanthenes. J. Heterocycl. Chem. 2010;47:292–300. doi: 10.1002/jhet.303. [DOI] [Google Scholar]
  • 24.Rashedian F, Saberi D, Niknam K. Silica-bonded N-propyl sulfamic acid: a recyclable catalyst for the synthesis of 1,8-dioxo-decahydroacridines, 1,8-dioxo-octahydroxanthenes and quinoxaline. J. Chin. Chem. Soc. 2010;57:998–1006. doi: 10.1002/jccs.201000139. [DOI] [Google Scholar]
  • 25.Sadjadi S. Halloysite-based hybrids/composites in catalysis. Appl. Clay Sci. 2020;189:105537. doi: 10.1016/j.clay.2020.105537. [DOI] [Google Scholar]
  • 26.Sadjadi S, Heravi MM, Malmir M. Pd@HNTs-CDNS-g-C3N4: a novel heterogeneous catalyst for promoting ligand and copper-free Sonogashira and Heck coupling reactions, benefits from halloysite and cyclodextrin chemistry and g-C3N4 contribution to suppress Pd leaching. Carbohydr. Polym. 2018;186:25–34. doi: 10.1016/j.carbpol.2018.01.023. [DOI] [PubMed] [Google Scholar]
  • 27.Sadjadi S, Malmir M, Heravi MM, Kahangi FG. Biocompatible starch-halloysite hybrid: An efficient support for immobilizing Pd species and developing a heterogeneous catalyst for ligand and copper free coupling reactions. Int. J. Biol. Macromol. 2018;118:1903–1911. doi: 10.1016/j.ijbiomac.2018.07.053. [DOI] [PubMed] [Google Scholar]
  • 28.Sadjadi S, Heravi MM, Kazemi SS. Ionic liquid decorated chitosan hybridized with clay: a novel support for immobilizing Pd nanoparticles. Carbohydr. Polym. 2018;200:183–190. doi: 10.1016/j.carbpol.2018.07.093. [DOI] [PubMed] [Google Scholar]
  • 29.Sadjadi S, Heravi MM, Raja M, Kahangi FG. Palladium nanoparticles immobilized on sepiolite–cyclodextrin nanosponge hybrid: efficient heterogeneous catalyst for ligand- and copper-free C–C coupling reactions. Appl. Organomet. Chem. 2018;32:e4508. doi: 10.1002/aoc.4508. [DOI] [Google Scholar]
  • 30.Liu R, Wang J, Zhang J, Xie S, Wang X, Ji Z. Honeycomb-like micro-mesoporous structure TiO2/sepiolite composite for combined chemisorption and photocatalytic elimination of formaldehyde. Microporous Mesoporous Mater. 2017;248:234–245. doi: 10.1016/j.micromeso.2017.04.029. [DOI] [Google Scholar]
  • 31.Yuan P, Southon PD, Liu Z, Green MER, Hook JM, Antill SJ, Kepert CJ. Functionalization of halloysite clay nanotubes by grafting with γ-aminopropyltriethoxysilane. J. Phys. Chem. C. 2008;112:15742–15751. doi: 10.1021/jp805657t. [DOI] [Google Scholar]
  • 32.Mallik S, Dash SS, Parida KM, Mohapatra BK. Synthesis, characterization, and catalytic activity of phosphomolybdic acid supported on hydrous zirconia. J. Colloid Interface Sci. 2006;300:237–243. doi: 10.1016/j.jcis.2006.03.047. [DOI] [PubMed] [Google Scholar]
  • 33.Aravinthan A, et al. Sunroot mediated synthesis and characterization of silver nanoparticles and evaluation of its antibacterial and rat splenocyte cytotoxic effects. Int. J. Nanomed. 2015;10:1977. doi: 10.2147/IJN.S79106. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 34.Krishnaraj C, Jagan EG, Rajasekar S, Selvakumar P, Kalaichelvan P, T. & Mohan N. Synthesis of silver nanoparticles using Acalypha indica leaf extracts and its antibacterial activity against water borne pathogens. Colloids Surf. B. 2010;76:50–56. doi: 10.1016/j.colsurfb.2009.10.008. [DOI] [PubMed] [Google Scholar]
  • 35.Khoeiniha R, Ezabadi A, Olyaei A. An efficient solvent-free synthesis of 1,8-dioxooctahydroxanthenes using Fe2(SO4)3·7H2O as catalyst. Iran. Chem. Commun. 2016;4:273–282. [Google Scholar]
  • 36.Sadat SN, HatamJafari F. One-pot synthesis of 1,8-dioxo-octahydroxanthene derivatives. Orient. J. Chem. 2015;31:191–1193. doi: 10.13005/ojc/310275. [DOI] [Google Scholar]
  • 37.Arzehgar Z, Aydi A, Mirzaei Heydari M. Silver functionalized on hydroxyapatite-core-shell magnetic γ-Fe2O3: an enviromentaly and readily recyclable nanatalyst for the one-pot synthesis of 14H-dibenzo[a, j]xanthenes derivatives. Asian J. Green Chem. 2018;2:281–298. doi: 10.22034/ajgc.2018.61867. [DOI] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Supplementary Materials

Supplementary Information. (1.4MB, docx)