Solvothermal synthesis of Fe3O4 nanospheres for high-performance electrochemical non-enzymatic glucose sensor

Jiasheng Xu 1,2, Yuting Sun 2, Jie Zhang 1,✉
PMCID: PMC7524729  PMID: 32994458

Abstract

Ferroferric oxide (Fe3O4) nanospheres have been synthesized via a facile solvothermal procedure to serve as an electrode material for high performance non-enzymatic glucose sensor. The as-synthesized Fe3O4 nanospheres with a uniform size from 16 to 18 nm, which can increase the reaction contact area and the active sites in the process of glucose detection. Benefiting from the particular nanoscale structure, the Fe3O4 nanospheres obviously enhanced the activity of electrocatalytic oxidation towards glucose. When the Fe3O4 nanospheres material was used for non-enzymatic glucose sensor, several electrochemical properties including the high sensitivity 6560 μA mM−1 cm−2 (0.1–1.1 mM), limit of detection 33 μM (S/N = 3) and good long-term stability were well demonstrated. Furthermore, Fe3O4 nanospheres electrode confirmed the excellent performance of selectivity in glucose detection with the interfering substances existed such as urea, citric acid, ascorbic acid, and NaCl. Due to the excellent electrocatalytic activity in alkaline solution, the Fe3O4 nanospheres material can be considered as a promising candidate in blood glucose monitoring.

Subject terms: Sensors and biosensors, Electrocatalysis

Introduction

Glucose is the predominant energy-producing substance for metabolism of human body and the levels of the blood glucose must be stable in a certain range to maintain the body activities1–4. However, high levels of the blood glucose that existed in human body may lead to diabetes and complications5. Diabetes, a serious metabolic disease, has become a global health problem as a growing threat to human body6–9. Hence, the use of appropriate treatment to monitor and detect glucose concentration in human blood has been particularly significant10–13. Several common techniques such as optical14, acoustic15,16, fluorescent17 and electrochemical method18 have been utilized for glucose monitoring and detection. Enzymatic glucose sensor and non-enzymatic glucose sensor are the earliest biosensor studied by researchers in the field of glucose analysis19. Enzymatic glucose sensor is usually based on the catalytic performance of glucose oxidase (GOx) to achieve the specific detection of glucose. Researchers have made a series of advances on enzymatic glucose sensor. Ramanavicius et al.20 evaluated the impedimetric glucose sensor based on the electrodes modified by both 1,10-Phenanthroline-5,6-dione and glucose oxidase. Valiuniene et al.21 investigated the glucose biosensor based on graphite electrode modified by Prussian blue, polypyrrole and glucose oxidase. Up to now, for some shortcomings including high-cost, low lifetime and poor stability, enzymatic electrochemical glucose sensor has been gradually replaced by non-enzymatic electrochemical glucose sensor22. Electrochemical non-enzymatic glucose sensor has played a key role in clinical diagnosis23.

In recent years, due to the high accuracy, sensitivity and efficiency, the electrochemical non-enzymatic glucose sensor has become a leading technology with boundless potential24–26. As the electrode material, noble metals are limited by the high cost. A series of transition metal oxides have become common materials for constructing electrochemical non-enzymatic glucose sensors27. Some transition metal oxides such as MnO2, CuO, Co3O4 and NiO were extensively studied because all of them could be utilized as alternatives to noble metals28. Nanomaterials have gradually become the most popular research direction due to their various excellent properties, which also leads to a new level of research in the field of sensing29. Due to low toxicity, biocompatibility, superparamagnetism and catalytic activity, Fe3O4 nanomaterials have received considerable interest30–32. Aside from the inherent properties, the structure and morphology of the Fe3O4 nanomaterials are also the key factors affecting the electrochemical sensing performance in glucose detecting33. It has been reported that the Fe3O4 nanoparticles in various shapes synthesized via different methods possess different properties34,35. With the kinetic capacity in glucose oxidation reaction and the large surface area, nano-spherical structures can offer more active sites and enhance the electrochemical performance36–38. Therefore, a facile process to synthesize Fe3O4 nanomaterials as the material of electrochemical non-enzymatic glucose sensor has become essential.

In this paper, a high-performance electrochemical non-enzymatic glucose sensor has been presented. The Fe3O4 nanospheres have been synthesized in a facile solvothermal procedure, which are pasted on the Ni foam. Several electron microscopic analysis and diffraction techniques were used to characterize the properties of microstructure and morphology of Fe3O4 nanospheres. Satisfactorily, the Fe3O4 nanospheres displayed superior nanoscale size and electrocatalytic properties for detecting glucose (from 0.1 to 1.1 mM) and a limit of detection is 33 μM.

Results and discussion

The representative synthesis and electrochemical glucose detection process of the Fe3O4 nanospheres electrode is exhibited in Fig. 1. The synthesis of Fe3O4 nanospheres was carried out in a solvothermal procedure and the as-synthesized Fe3O4 nanospheres electrode was acted as a working electrode in three-electrode system for glucose detection. Firstly, FeCl3·6H2O, CTAB (hexadecyl trimethyl ammonium bromide), CH3COONa and EDA (ethylenediamine) were dissolved in EG (ethylene glycol) under magnetic stirring for 30 min at 50 °C. Then the mixed reagents were transferred to the autoclave to synthesize the target samples. The as-synthesized Fe3O4 nanospheres samples were pasted on Ni foam for electrochemical detecting. In the process of electrochemical sensing towards glucose, the glucose was oxidized into gluconolactone by the strongly oxidized Fe3+ which was formed rapidly in the NaOH electrolyte. At the same time, the electron transport reactions also occurred. Subsequently, the electrons were transferred to the Ni foam. The electrocatalytic oxidation towards glucose was finally realized under the interaction in the three-electrode system.

Figure 1.

Figure 1

Open in a new tab

The schematic illustrations of the synthesis and electrochemical glucose detection process of the Fe3O4 nanospheres electrode.

Crystallographic data and chemical composition of Fe3O4 nanospheres were identified by the powder X-ray diffraction analysis (XRD, in the 2θ range from 25° to 70°). All characteristic peaks are well consistent with the standard PDF card (JCPDS No. 03-0863) in Fig. 2, which indicate the products are pure Fe3O4. All characteristic peaks at 30.3°, 35.4°, 43.4°, 53.5°, 56.9° and 62.6° represent the (220), (311), (400), (422), (511) and (440) crystal faces of Fe3O4, respectively.

Figure 2.

Figure 2

Open in a new tab

XRD patterns of the Fe3O4 nanospheres synthesized by solvothermal reaction at 200 °C for 10 h. The vertical lines at bottom are the standard diffraction peaks of Fe3O4 from JCPDS card No. 03-0863.

In order to observe surface of the samples, the morphologies of Fe3O4 nanospheres has been presented by scanning electron microscope (SEM). The low magnification SEM microstructure images (in Fig. 3a,b) present an overall morphology of Fe3O4 nanospheres. The products with extremely small size exhibit a fine exterior surface and gathered together. Figure 3c,d show the high magnification SEM microstructure images of Fe3O4 nanospheres. It is observed that every Fe3O4 nanosphere is in general of sphere-like and possesses a uniform size of 16–18 nm.

Figure 3.

Figure 3

Open in a new tab

SEM images of Fe3O4 nanospheres sample. (a,b) Low magnification SEM images of Fe3O4 nanospheres. (c,d) High magnification SEM images of Fe3O4 nanospheres.

The clearer structural properties of the as-synthesized Fe3O4 nanospheres were further presented by transmission electron microscope (TEM). Figure 4a,b display the typical TEM images of as-synthesized Fe3O4 nanospheres with a large quantity of well-dispersed nanospheres. Figure 4c,d display the high-resolution TEM (HRTEM) images with a clear lattice structure property. The spacing of lattice is calculated to be 0.286 nm, which is consistent with (220) interplanar spacing of the Fe3O4 nanospheres. Inset is the SAED pattern, the diameters of the two planes correspond to the (311) and (440) planes, which indicates that the Fe3O4 nanospheres have an excellent crystalline structure.

Figure 4.

Figure 4

Open in a new tab

TEM images of Fe3O4 nanospheres sample. (a,b) TEM images of Fe3O4 nanospheres. (c,d) HRTEM images of Fe3O4 nanospheres; inset is the SAED pattern of Fe3O4 nanospheres.

The CV curves of Fe3O4 nanospheres electrode under various glucose concentration (0–7 mM) in 0.5 M NaOH are displayed in Fig. 5a. It is obvious from these CV curves that the cathodic peak potential shows a slight positive shift when glucose concentration is increased gradually. The observation reveals that the Fe3O4 nanospheres electrode possesses a great advantage in electrocatalytic activity. In the glucose detecting process, some values such as applied working potential has played an important role. Figure 5b shows the current–time curves of Fe3O4 nanospheres electrode when adding glucose successively for every 100 s at various applied potential in 0.5 M NaOH. By comparison, Fe3O4 nanospheres electrode displays a weak sensitivity at the highest applied potential 0.60 V and the noise interference is large. Hence, the appropriate potential value option for Fe3O4 nanospheres electrode is 0.55 V. The ability of the Fe3O4 nanospheres electrode towards glucose electro-oxidation was further investigated at the selected potential of 0.55 V. As described in Fig. 5c, amperometric response increased significantly with the increase of glucose concentration in the NaOH. This result reveals an excellent electrocatalytic ability of Fe3O4 nanospheres electrode for detecting glucose. The calibration curve of the current density and glucose concentration are displayed in Fig. 5d, which determined the relevant measurement range of 0.1–1.1 mM (R2 = 0.9828). The sensitivity of Fe3O4 nanospheres electrode is 6560 μA mM−1 cm−2 by observing corresponding slope parameter and a corresponding detection limit is 33 μM (S/N = 3). We have compared sensitivity of Fe3O4 nanospheres electrode in electrochemical sensing towards glucose with the previously reported data on iron materials and other types of electrochemical sensors. Corresponding comparison of Fe3O4 nanospheres electrode with other electrode materials was summarized in Table 1. Sanaeifar et al. synthesized GOx/PVA-Fe3O4/Sn electrode and the sensitivity was 9.36 μA mM−1 cm−2; Vennila et al. prepared Ni-Co/Fe3O4/GCE which showed a sensitivity for 2171 μA mM−1 cm−2; Cao and his team synthesized Fe2O3 nanowire arrays which possessed a sensitivity for 726.9 μA mM−1 cm−2; Zhang et al. prepared 1 D Fe3O4 nanorod arrays and the sensitivity was 406.9 μA mM−1 cm−2. Obviously, compared with earlier reports, Fe3O4 nanospheres electrode has a higher sensitivity. It may benefit from the synergistic interactions between Fe3O4 nanospheres and Ni foam39. Electrochemical impedance spectroscopy (EIS) technique is also important to evaluate the electrochemical glucose sensor, which has been also carried out in other papers40. Figure 5e exhibits the Nyquist plot of Fe3O4 nanospheres electrode in the three-electrode system. Inset is a part of the Nyquist plot in the high frequency region which shows a semicircle shape with small diameter. It possesses a certain relationship with the controlled process of the charge transfer41. The diameter of the semicircle in Nyquist plot is equal to the charge transfer resistance (Rct) of the active surface area of the Fe3O4 nanospheres electrode, which was calculated to be 1.09 Ω. The low electrochemical impedance indicates a fast glucose oxidation kinetics in the process of glucose detection. The above series of results are sufficient to prove that the non-enzymatic glucose sensor based on the Fe3O4 nanospheres electrode possesses the excellent performance of providing the effective electron transport pathway for glucose detection. Some interfering substances, such as citric acid (CA), urea (UA) and Cl− from NaCl present in the human blood may have an effect on the Fe3O4 nanospheres electrode. Here, we study the anti-interference performance of the Fe3O4 nanospheres electrode through the current–time curve. Figure 5f shows the current–time curve of Fe3O4 nanospheres electrode in NaOH solution with the presence of 1 mM glucose, 0.1 mM CA, UA, ascorbic acid (AA) and NaCl. There was a significant current response when 1 mM of glucose was in NaOH solution. On the contrary, current response had little change with 0.1 mM other interfering substances in NaOH solution, revealing that Fe3O4 nanospheres electrode has great selectivity for glucose detection.

Figure 5.

Figure 5

Open in a new tab

(a) CV curves of Fe3O4 nanospheres electrode in 0.5 M NaOH containing various concentration of glucose (0–7 mM) at a scan rate of 20 mV s−1. (b) Effect of different potentials on amperometric response of Fe3O4 nanospheres electrode to the successive addition of 0.1 mM glucose. (c) Amperometric response of Fe3O4 nanospheres electrode upon the addition of various concentrations of glucose at 0.55 V. (d) Corresponding calibration curve of the response current density and glucose concentration. (e) Nyquist plot of the Fe3O4 nanospheres electrode. Inset is the equivalent circuit. (f) Amperometric response of the Fe3O4 nanospheres electrode towards the addition of 1 mM glucose and 0.1 mM different interfering substances.

Table 1.

Comparison of Fe3O4 nanospheres electrode with previously reported data in the literature.

No Electrode material Sensitivity (μA mM−1 cm−1) Linear range (mM) References
1. Gox/PVA-Fe3O4/Sn 9.36 0.005–30 42
2. Ni–Co/Fe3O4 2171 0.001–11 43
3. Fe2O3 nanowire array 726.9 0.015–8 44
4. 1 D Fe3O4 NRA 406.9 0.0005–3.67 45
5. Fe3O4 nanospheres 6560 0.1–1.1 This work
Open in a new tab

Figure 6 shows the CV curves of Fe3O4 nanospheres electrode after 1 day and 30 days in 0.5 M NaOH. As can be seen from the figure, there is no obvious change in the shape of CV curve after 30 days. Furthermore, the value of the current response after 30 days did not change much, which confirmed the satisfactory stability of the Fe3O4 nanospheres electrode.

Figure 6.

Figure 6

Open in a new tab

Comparing CV curves of Fe3O4 nanospheres electrode after 1 day and 30 days in 0.5 M NaOH.

Conclusions

In summary, Fe3O4 nanospheres with nanoscale size have been successfully synthesized in a facile solvothermal procedure. The electrochemical sensing performance of glucose in the three-electrode system has been investigated. The as-synthesized Fe3O4 nanospheres electrode demonstrated a high efficiency and excellent selectivity in electrochemical sensing of glucose. Inspiringly, in relevant measurement range (from 0.1 to 1.1 mM), Fe3O4 nanospheres electrode possesses a satisfactory sensitivity for 6560 μA mM−1 cm−2. The value of detection limit is 33 μM (S/N = 3). Thus, Fe3O4 nanospheres material has the potential to become a functional electrode material for detecting glucose in the research field of electrochemistry.

Experimental details

Synthesis of the Fe3O4 nanospheres electrode

All chemicals were of analytical grade. In a conventional procedure, 1.0 g ferric chloride hexahydrate (FeCl3·6H2O), 1.0 g hexadecyl trimethyl ammonium bromide (CTAB) and 3.0 g sodium acetate trihydrate (CH3COONa) were first added into 20 mL ethylene glycol (EG) and magnetically stirred for 20 min at 50 °C to form a uniform yellow solution. Subsequently, adding 10 mL ethylenediamine (EDA) to above-mentioned yellow mixture with magnetically stirring for 10 min. Then, the as-synthesized sample was added to a Teflon-lined autoclave (50 mL) and kept it for 10 h at 200 °C. Fe3O4 nanospheres were collected by a magnet after cooling down the room temperature, using ethanol and deionized water to rinse them repeatedly. The synthesized Fe3O4 nanospheres were mixed with acetylene black, poly (vinylidene fluoride) (PVDF) and N-methyl-2-pyrrolidone (NMP) in a good percentage. Finally, pasting above mixture on Ni foam (length × width = 20 mm × 10 mm) as the working electrode.

Characterizations

The X-ray diffraction (XRD) was conducted on Rigaku RAD-3C diffractometer. Scanning electron microscope (SEM, JEOL S-4800), transmission electron microscope (TEM, JEOL JEM-2100F) were utilized to test the structure and morphologies of Fe3O4 nanospheres. Using an electrochemical workstation (CHI660D) for cyclic votammetry (CV) measurement and current–time analysis. Using platinum sheet for counter electrode, Hg/HgO electrode for reference electrode.

Acknowledgements

This work was supported by the National Key R&D Program of China (#2018YFF0215200) and the Talent Scientific Research Fund of LSHU (#2020XJJL-001).

Author contributions

J.X. conceived the idea and designed the experiments. Y.S. collected and analyzed the data and wrote the main manuscript. J.Z. contributed substantially to revisions and supervised paper. All authors reviewed the manuscript.

Competing interests

The authors declare no competing interests.

Footnotes

Publisher's note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

References

  • 1.Wang J. Electrochemical glucose biosensors. Chem. Rev. 2008;108:814–825. doi: 10.1021/cr068123a. [DOI] [PubMed] [Google Scholar]
  • 2.Zhang M, et al. Highly sensitive glucose sensors based on enzyme-modified whole-graphene solution-gated transistors. Sci. Rep. 2015;5:8311. doi: 10.1038/srep08311. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 3.Zhu Z, et al. A critical review of glucose biosensors based on carbon nanomaterials: carbon nanotubes and graphene. Sensors. 2012;12:5996–6022. doi: 10.3390/s120505996. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 4.Huang P, Shen M, Yu HH, Wei S, Luo SC. Surface engineering of phenylboronic acid-functionalized poly (3,4-ethylenedioxythiophene) for fast responsive and sensitive glucose monitoring. ACS Appl. Bio Mater. 2018;1:160–167. doi: 10.1021/acsabm.8b00060. [DOI] [Google Scholar]
  • 5.Wang Z, et al. Ternary NiCoP nanosheet array on a Ti mesh: a high-performance electrochemical sensor for glucose detection. Chem. Commun. 2016;52:14438–14441. doi: 10.1039/C6CC08078B. [DOI] [PubMed] [Google Scholar]
  • 6.Zaidi SA, Shin JH. Recent developments in nanostructure based electrochemical glucose sensors. Talanta. 2016;149:30–42. doi: 10.1016/j.talanta.2015.11.033. [DOI] [PubMed] [Google Scholar]
  • 7.Niu X, et al. Recent advances in non-enzymatic electrochemical glucose sensors based on non-precious transition metal materials: opportunities and challenges. RSC Adv. 2016;6:84893–84905. doi: 10.1039/C6RA12506A. [DOI] [Google Scholar]
  • 8.Newman JD, Turner AP. Home blood glucose biosensors: a commercial perspective. Biosens. Bioelectron. 2005;20:2435–2453. doi: 10.1016/j.bios.2004.11.012. [DOI] [PubMed] [Google Scholar]
  • 9.Huang BR, et al. Interfacial effect of oxygen-doped nanodiamond on CuO and micropyramidal silicon heterostructures for efficient nonenzymatic glucose sensor. ACS Appl. Bio Mater. 2018;1:1579–1586. doi: 10.1021/acsabm.8b00454. [DOI] [PubMed] [Google Scholar]
  • 10.Yoon H, Xuan X, Jeong S, Park JY. Wearable, robust, non-enzymatic continuous glucose monitoring system and its in vivo investigation. Biosens. Bioelectron. 2018;117:267–275. doi: 10.1016/j.bios.2018.06.008. [DOI] [PubMed] [Google Scholar]
  • 11.Gopalan AI, Muthuchamy N, Komathi S, Lee KP. A novel multicomponent redox polymer nanobead based high performance non-enzymatic glucose sensor. Biosens. Bioelectron. 2016;84:53–63. doi: 10.1016/j.bios.2015.10.079. [DOI] [PubMed] [Google Scholar]
  • 12.Bai Y, Sun Y, Sun C. Pt-Pb nanowire array electrode for enzyme-free glucose detection. Biosens. Bioelectron. 2008;24:579–585. doi: 10.1016/j.bios.2008.06.003. [DOI] [PubMed] [Google Scholar]
  • 13.Xu H, et al. Electrochemical non-enzymatic glucose sensor based on hierarchical 3D Co3O4/Ni heterostructure electrode for pushing sensitivity boundary to a new limit. Sens. Actuator B Chem. 2018;267:93–103. doi: 10.1016/j.snb.2018.04.023. [DOI] [Google Scholar]
  • 14.Rachim VP, Chung W-Y. Wearable-band type visible-near infrared optical biosensor for non-invasive blood glucose monitoring. Sens. Actuator B Chem. 2019;286:173–180. doi: 10.1016/j.snb.2019.01.121. [DOI] [Google Scholar]
  • 15.Luo J, et al. A new type of glucose biosensor based on surface acoustic wave resonator using Mn-doped ZnO multilayer structure. Biosens. Bioelectron. 2013;49:512–518. doi: 10.1016/j.bios.2013.05.021. [DOI] [PubMed] [Google Scholar]
  • 16.Hu R, Stevenson AC, Lowe CR. An acoustic glucose sensor. Biosens. Bioelectron. 2012;35:425–428. doi: 10.1016/j.bios.2012.02.026. [DOI] [PubMed] [Google Scholar]
  • 17.Yu S, Ding L, Lin H, Wu W, Huang J. A novel optical fiber glucose biosensor based on carbon quantum dots-glucose oxidase/cellulose acetate complex sensitive film. Biosens. Bioelectron. 2019;146:111760. doi: 10.1016/j.bios.2019.111760. [DOI] [PubMed] [Google Scholar]
  • 18.Hwang DW, Lee S, Seo M, Chung TD. Recent advances in electrochemical non-enzymatic glucose sensors - a review. Anal. Chim. Acta. 2018;1033:1–34. doi: 10.1016/j.aca.2018.05.051. [DOI] [PubMed] [Google Scholar]
  • 19.Zhu H, Li L, Zhou W, Shao Z, Chen X. Advances in non-enzymatic glucose sensors based on metal oxides. J. Mater. Chem. B. 2016;4:7333–7349. doi: 10.1039/C6TB02037B. [DOI] [PubMed] [Google Scholar]
  • 20.Ramanavicius A, Genys P, Oztekin Y, Ramanaviciene A. Evaluation of the redox mediating properties of 1,10-Phenanthroline-5,6-dione for glucose oxidase modified graphite electrodes. J. Electrochem. Soc. 2013;161:B31–B33. doi: 10.1149/2.021403jes. [DOI] [Google Scholar]
  • 21.Valiuniene A, Rekertaite AI, Ramanaviciene A, Mikoliunaite L, Ramanavicius A. Fast Fourier transformation electrochemical impedance spectroscopy for the investigation of inactivation of glucose biosensor based on graphite electrode modified by Prussian blue, polypyrrole and glucose oxidase. Colloid Surf. A. 2017;532:165–171. doi: 10.1016/j.colsurfa.2017.05.048. [DOI] [Google Scholar]
  • 22.Wu W, et al. Hybrid ZnO–graphene electrode with palladium nanoparticles on Ni foam and application to self-powered nonenzymatic glucose sensing. RSC Adv. 2019;9:12134–12145. doi: 10.1039/C8RA09599J. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 23.Xiao F, Li Y, Gao H, Ge S, Duan H. Growth of coral-like PtAu-MnO2 binary nanocomposites on free-standing graphene paper for flexible nonenzymatic glucose sensors. Biosens. Bioelectron. 2013;41:417–423. doi: 10.1016/j.bios.2012.08.062. [DOI] [PubMed] [Google Scholar]
  • 24.Weremfo A, Fong STC, Khan A, Hibbert DB, Zhao C. Electrochemically roughened nanoporous platinum electrodes for non-enzymatic glucose sensors. Electrochim. Acta. 2017;231:20–26. doi: 10.1016/j.electacta.2017.02.018. [DOI] [Google Scholar]
  • 25.Unnikrishnan B, Palanisamy S, Chen SM. A simple electrochemical approach to fabricate a glucose biosensor based on graphene-glucose oxidase biocomposite. Biosens. Bioelectron. 2013;39:70–75. doi: 10.1016/j.bios.2012.06.045. [DOI] [PubMed] [Google Scholar]
  • 26.Abdorahim M, et al. Nanomaterials-based electrochemical immunosensors for cardiac troponin recognition: an illustrated review. Trac-trend. Anal. Chem. 2016;82:337–347. doi: 10.1016/j.trac.2016.06.015. [DOI] [Google Scholar]
  • 27.Cella LN, Chen W, Myung NV, Mulchandani A. Single-walled carbon nanotube-based chemiresistive affinity biosensors for small molecules: ultrasensitive glucose detection. J. Am. Chem. Soc. 2010;132:5024–5026. doi: 10.1021/ja100503b. [DOI] [PMC free article] [PubMed] [Google Scholar]
  • 28.Yang YJ, Hu S. Electrodeposited MnO2/Au composite film with improved electrocatalytic activity for oxidation of glucose and hydrogen peroxide. Electrochim. Acta. 2010;55:3471–3476. doi: 10.1016/j.electacta.2010.01.095. [DOI] [Google Scholar]
  • 29.Lv J, et al. Facile synthesis of novel CuO/Cu2O nanosheets on copper foil for high sensitive nonenzymatic glucose biosensor. Sens. Actuator B Chem. 2017;248:630–638. doi: 10.1016/j.snb.2017.04.052. [DOI] [Google Scholar]
  • 30.Xing Y, et al. Controllable synthesis and characterization of Fe3O4/Au composite nanoparticles. J. Magn. Magn. Mater. 2015;380:150–156. doi: 10.1016/j.jmmm.2014.09.060. [DOI] [Google Scholar]
  • 31.Yang L, Ren X, Tang F, Zhang L. A practical glucose biosensor based on Fe3O4 nanoparticles and chitosan/nafion composite film. Biosens. Bioelectron. 2009;25:889–895. doi: 10.1016/j.bios.2009.09.002. [DOI] [PubMed] [Google Scholar]
  • 32.Ma N, et al. Novel electrochemical immunosensor for sensitive monitoring of cardiac troponin I using antigen-response cargo released from mesoporous Fe3O4. Biosens. Bioelectron. 2019;143:111608. doi: 10.1016/j.bios.2019.111608. [DOI] [PubMed] [Google Scholar]
  • 33.Huang W, et al. Fast synthesis of porous NiCo2O4 hollow nanospheres for a high-sensitivity non-enzymatic glucose sensor. Appl. Surf. Sci. 2017;396:804–811. doi: 10.1016/j.apsusc.2016.11.034. [DOI] [Google Scholar]
  • 34.Li Y, et al. Monodisperse Fe3O4 spheres: large-scale controlled synthesis in the absence of surfactants and chemical kinetic process. Sci. China Mater. 2019;62:1488–1495. doi: 10.1007/s40843-019-9466-x. [DOI] [Google Scholar]
  • 35.Chen Y, Hsu J, Chen Z, Lin Y, Hsu Y. Fabrication of Fe3O4 nanotube arrays for high-performance non-enzymatic detection of glucose. J. Electroanal. Chem. 2017;788:144–149. doi: 10.1016/j.jelechem.2017.02.007. [DOI] [Google Scholar]
  • 36.Li HB, Zhao P. Amorphous Ni–Co–Fe hydroxide nanospheres for the highly sensitive and selective non-enzymatic glucose sensor applications. J. Alloys Compd. 2019;800:261–271. doi: 10.1016/j.jallcom.2019.05.264. [DOI] [Google Scholar]
  • 37.Wang K, et al. Hierarchical Fe3O4@C nanospheres derived from Fe2O3/MIL-100(Fe) with superior high-rate lithium storage performance. J. Alloys Compd. 2018;755:154–162. doi: 10.1016/j.jallcom.2018.04.320. [DOI] [Google Scholar]
  • 38.He Z, et al. MOF-derived hierarchical MnO-doped Fe3O4@C composite nanospheres with enhanced lithium storage. ACS Appl. Mater. Interfaces. 2018;10:10974–10985. doi: 10.1021/acsami.8b01358. [DOI] [PubMed] [Google Scholar]
  • 39.Guo Q, Zeng W, Li Y. Highly sensitive non-enzymatic glucose sensor based on porous NiCo2O4 nanowires grown on nickel foam. Mater. Lett. 2019;256:126603. doi: 10.1016/j.matlet.2019.126603. [DOI] [Google Scholar]
  • 40.Ramanavicius A, Genys P, Ramanaviciene A. Electrochemical impedance spectroscopy based evaluation of 1,10-Phenanthroline-5,6-dione and glucose oxidase modified graphite electrode. Electrochim. Acta. 2014;146:659–665. doi: 10.1016/j.electacta.2014.08.130. [DOI] [Google Scholar]
  • 41.Tian K, Baskaran K, Tiwari A. Nonenzymatic glucose sensing using metal oxides–comparison of CuO, Co3O4, and NiO. Vacuum. 2018;155:696–701. doi: 10.1016/j.vacuum.2018.06.060. [DOI] [Google Scholar]
  • 42.Sanaeifar N, et al. A novel electrochemical biosensor based on Fe3O4 nanoparticles-polyvinyl alcohol composite for sensitive detection of glucose. Anal. Biochem. 2017;519:19–26. doi: 10.1016/j.ab.2016.12.006. [DOI] [PubMed] [Google Scholar]
  • 43.Vennila P, Yoo DJ, Kim AR, Kumar GG. Ni-Co/Fe3O4 flower-like nanocomposite for the highly sensitive and selective enzyme free glucose sensor applications. J. Alloys Compd. 2017;703:633–642. doi: 10.1016/j.jallcom.2017.01.044. [DOI] [Google Scholar]
  • 44.Cao X, Wang N. A novel non-enzymatic glucose sensor modified with Fe2O3 nanowire arrays. Analyst. 2011;136:4241–4246. doi: 10.1039/c1an15367f. [DOI] [PubMed] [Google Scholar]
  • 45.Chao Z, et al. Enzyme-free glucose sensing based on Fe3O4 nanorod arrays. Microchim. Acta. 2015;182:1811–1818. doi: 10.1007/s00604-014-1415-2. [DOI] [Google Scholar]

Articles from Scientific Reports are provided here courtesy of Nature Publishing Group