Influence of Solvents' Polarity on the Physicochemical Properties and Photocatalytic Activity of Titania Synthesized Using Deinbollia pinnata Leaves

Yakubu Rufai 1,2, Sheela Chandren 1,3,*, Norazah Basar 1
PMCID: PMC7744779  PMID: 33344417

Abstract

Nanotechnology is one of the most interesting areas of research due to its flexibility to improve or form new products from nanoparticles (NPs), and as a fast, greener, more eco-friendly and sustainable solution to technological and environmental challenges. Among metal oxides of photocatalytic performance, the use of titania (TiO2) as photocatalyst is most popular due to its unique optical and electronic properties. Despite the wide utilization, the synthesis of TiO2 NPs bears many disadvantages: it utilizes various less environmental-friendly chemicals, high cost, requires high pressure and energy, and potentially hazardous physical and chemical methods. Hence, the development of green synthesis approach with eco-friendly natural products can be used to overcome these adverse effects. In this work, TiO2 NPs have been prepared by using Deinbollia pinnata leaves extracts, obtained by different solvents (n-hexane, ethyl acetate, and ethanol) with different polarities. The extracts acted as the reducing agent, while titanium isopropoxide as the precursor and water as the solvent. X-ray diffraction (XRD) pattern confirmed the synthesized TiO2 consist of anatase phase in high purity, with average crystallite size in the range of 19–21 nm. Characterization by using field emission scanning electron microscopy (FESEM) showed the TiO2 NPs possess a uniform semi-spherical shape in the size range of 33–48 nm. The energy dispersive X-ray (EDX) spectra of green TiO2 NPs showed two peaks for the main elements of Ti (61 Wt.%) and O (35 Wt.%). The band-gap energy of 3.2 eV was determined using UV-Vis spectroscopy. From the nitrogen sorption analysis, type V isotherm of the material was obtained, with BET surface area of 31.77 m2/g. The photocatalytic activity of synthesized TiO2 was evaluated for photodegradation of methyl orange (MO) under UV light irradiation. Based on the results, it is shown that TiO2 NPs synthesized with D. pinnata leaves extracted using ethyl acetate showed the most effective photodegradation performance, achieving 98.7% of MO conversion within 150 min. It can be concluded that the use of plant extracts in synthesis with TiO2 managed to produce highly crystalline anatase TiO2 with superior photocatalytic activity in the photodegradation of organic dye.

Keywords: TiO2, green synthesis, Deinbollia pinnata, solvents polarities, methyl orange, photodegradation

Introduction

The nature of nanostructured materials has prompted natural product researchers' attention to this field. The naturally occurring oxide of titanium (IV) oxide or titania (TiO2) possesses unique optical and electronic properties (Ahmad et al., 2019). The surface chemistry of nanostructures in terms of smaller size and uniqueness have already been utilized in medicine, nutrition, energy (Venugopal et al., 2017; Agarwal et al., 2018; Kim et al., 2018) and in the biosynthesis of TiO2 NPs with metabolites present in plants extract to reduce and stabilize bulk metal into elemental forms (Mohamad et al., 2014). Plants are a major segment of biodiversity affected by many living and non-living components with their medicinal values. This is due to the presence of certain chemicals/active ingredients used for the treatment of disorders, with low cost, eco-friendliness and easy availability in the forest (Patel, 2015). Stable biological NPs are achieved with appropriate choice of solvents polarity for plant extraction (reducing agents) and as toxic-free material (Raghad et al., 2016). Fungi, actinomycetes, bacteria, and plant extracts (Órdenes-Aenishanslins et al., 2014) have replaced chemical agents in the green synthesis materials. Furthermore, the usage of these materials can enhance the photocatalytic and pharmacological properties of the NPs produced. Bio-mediated TiO2 NPs have also been obtained from the extracts of Morinda citrifolia L. (Sundrarajan et al., 2017), Tamarindus indica (Hiremath et al., 2018); and Azadirachta indica (Thakur et al., 2019). The roots and leaves of D. pinnata are used in folkloric medicine as remedy for febrifuge, analgesic, bronchiasis intercostals, intestinal pains, jaundice, cough, asthma, and infections (Sotubo et al., 2016). Leaf extracts are used in fetus positioning during child birth (Kankara et al., 2015). The root act as an antibacterial agent (Sotubo et al., 2016).

Various synthesis methods of TiO2 NPs are available, such as solution combustion (Kitamura et al., 2007), sol-gel (Elbushra et al., 2018), hydrothermal (Bregadiolli et al., 2017), solvothermal (Dinh et al., 2012), microwave-assisted (May-Masnou et al., 2018), co-precipitation (Rab et al., 2018), and chemical vapor deposition (Lee et al., 2011). However, the sol-gel process clearly stood out due to the lower processing temperature (<100°C), which can produce highly crystalline particles with small sizes and high surface area. In addition, this method is also low in cost and can give fast composition homogeneity.

Dyes are major coloring agents used in industries for precious stones, paper, leather, plastic, textile, and food production. Hazardous waste water from dyeing process act as a major contaminant to the environment (Murugan and Parimelazhagan, 2014; Hejazi et al., 2020). The dye effluents are usually non-biodegradable, highly oxidizing, and stable to heat and light (Khataee and Mirzajani, 2010; Khataee et al., 2010) which attributed to their toxicity, undesirable aesthetic, and carcinogenicity (Khalik et al., 2017). This is due to their diversity and complex structure (Benkhaya et al., 2017), which need to be degraded. One example is methyl orange (MO), which is a commonly used dye.

Methyl orange dyes are stable under visible light, which can be easily degraded in the presence of catalyst (Chiu et al., 2019). It is known to cause irritation to reproductive, excretory, respiratory. and central nervous systems when in contact or consumed (Parida et al., 2013; Ljubas et al., 2015). Among all other methods to overcome its environmental hazard, photocatalysis has been proven effective for its degradation and removal of azo dyes in a less harmful (greener) method (Guettaï and Ait Amar, 2005). This present work focuses on the sol-gel green synthesis of TiO2 NPs using D. pinnata plant extracts obtained by different solvents with different polarities (n-hexane, ethyl acetate, and methanol). Their multi-functional group in the ethyl acetate crude extracts were characterized by Fourier transform infrared (FTIR) spectroscopy. The TiO2 NPs obtained were then characterized using X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), the energy dispersive X-ray (EDX), ultraviolet-visible light analysis (UV-Visible), nitrogen sorption analysis (N2 sorption), and photoluminescence analysis (PL). Following that, the photocatalytic activity of the synthesized TiO2 NPs was evaluated for the photocatalytic degradation of MO under UV light irradiation. This current work further shows the potential of utilizing plants extract in multi-fold directions, but such as in the case of biosynthesis.

Experimental

Materials

The materials used in this research were titanium isopropoxide (TTIP), C12H28O4Ti [Aldrich (97%)], methyl orange (MO) C14H14N3NaO3S [Aldrich (85%)], absolute ethanol (EtOH) C2H6O [MERK (100%)]. All materials were used as-received without further purification. Deionized water (MQ-H2O) was used throughout the experiments. Mettler H10, photoreactor chamber, membrane filter, syringe, centrifuge, UV lamp 1,200 W, glass beaker, cuvette, aluminum foil, and glass petri-dish were used as the apparatus in this work.

The D. pinnata (Poir.) Schumach. and Thonn leaves were collected from Okehi Local Government Area of Kogi State, Nigeria during dry season, early January, for 1 week (daytime temperature ranges from 28°C in January to 32°C). The plant was identified and confirmed at the Biological Department, Federal College of Education Okene Kogi State by Mrs. Aniama S.O.A., a botanist. The plant material was authenticated at Forestry Research Institute of Nigeria Ibadan through comparison with voucher specimen under accession number of FHI 3251. The leaves were collected, washed and air dried at room temperature for 1 month.

Extraction

Powdered plant material of D. pinnata (Poir.) Schumach. and Thonn was extracted using sonication method as shown in Figure 1. Briefly, the leaf samples were placed into several conical flasks (30 g each) and extracted with organic solvents (150 mL), which were n-hexane, ethyl acetate, and methanol, in a sonicator using ultrasonic-assisted extraction method for 10 min with agitation. This method utilizes the following software conditions of time, temperature, and solvent ratio. Upon completion, the samples were filtered into bottles and allowed to settle for 24 h. The combined filtrates were then concentrated in vacuo at 40°C using a rotary evaporator.

Figure 1.

Figure 1

Extraction steps of D. pinnata leaves.

Qualitative Phytochemical Screening of Extract

The D. pinnata ethyl acetate extract was subjected to chemical tests for the identification of their active constituents. The chemical tests were performed using the methods reported by Samkeliso et al. (2018).

Test for Phenols

Five percent ferric chloride was added to 2 mL of the leaf extract, which will show black coloration. This indicates the presence of phenols.

Test for Flavonoids

Ten milliliters of ethyl acetate was added to the leaf extract and the test tube containing this mixture was heated in the water bath. One milliliter of diluted ammonia was added to this mixture, which will give yellow color, showing the presence of flavonoids.

Test for Alkaloids (Mayer's Test)

Mayer's test reagent was added to 2 mL of the leaf extract, which will then give cream colored precipitation, indicating the presence of alkaloids.

Test for Steroids

Two milliliters of concentrated H2SO4 was added to 1 mL of the extract. Following that, 2 mL of acetic anhydride was added. The change in the color of extract from violet to blue or green will take place if steroids are present.

Test for Coumarins

Ten percent of the NaOH was added to the extract and chloroform was added. Formation of yellow color will show the presence of coumarin.

Synthesis of Green TiO2 NPs

The synthesis was carried out using the sol-gel method, where titanium (IV) isopropoxide (TTIP) was utilized as the precursor, D. pinnata extracts [1 g/5 mL] and deionized (DI) water as the medium. TiO2 NPS were prepared by dissolving 4 mL TTIP with 20 mL of DI water under constant stirring for 30 min at 30°C. This was followed by the gradual addition of 0.2 g/mL of DP extracts (either by n-hexane, ethyl acetate, or ethanol) with constant stirring at 50°C for 4 h before kept at room condition for 48 h of aging process. The resulting colloidal suspension was washed with ethanol and centrifuged three times at 10,000 rpm for 30 min. The samples were then dried at 95°C for 24 h in an oven, before being calcined at 500°C in a muffle furnace for 5 h. The calcined TiO2 NPs powder was further characterized spectroscopically.

Characterizations of Green TiO2 NPs

The crystallinity of the synthesized TiO2 NPs were performed by Rigaku Smart Lab, Germany with Cu Kα radiation (λ = 1.5418 Å) operated at 40 kV and 30 mA. The diffraction pattern was scanned in the 2θ range of 20–90°. The morphological features and surface characteristics of the photocatalyst were characterized using field emission scanning electron microscopy (FESEM) (JEOL JSM 6710F) equipped with EDX, at an accelerating voltage of 0.5–30 kV to determine the surface chemical element contents of the photocatalysts. The band gap energy of the TiO2 NPs were determined using UV-Vis near-IR (UV-Vis-NIR) spectrophometer (Shimadzu UV-3600 Plus UV-VIS-NIR). The spectra were recorded in the range of 300–500 nm at temperature rate/hold/time of 10:1,000:1.The specific surface area, micropore and pore size distribution of the TiO2 NPs were obtained using a multipoint Brunauer–Emmett–Teller (BET) analysis through the measurement of nitrogen adsorption–desorption isotherm as a function of relative pressure from a Quantachrome NOVA-4LX firmware with helium gas, and ambient temperature of 30.06°C. The thermal stability and heat flow were examined using thermogravimetric-differential scanning calorimetry analyzer (TGA-DSC, SHIMADZU DTG-60H). The scanning was performed within the furnace temperature range of 20–800°C with a heating rate and air flow rate of 10°C min−1 and 20 mL min−1, respectively. The electrons-holes recombination's of the photocatalysts through discrete electronic states were analyzed by Photoluminescence (Horiba-fluoroMax-4C spectrofluorometer) with emission of full spectrum range between 400 and 800 nm. The chemical functional groups were detected by Fourier transform infrared spectroscopy (1600 FT-IR). The spectra were recorded in the range of 400–4,000 cm−1 using PerkinElmer Spectrum One Spectrometer.

Photocatalytic Testing

The photocatalytic activity of the green TiO2 NPs was tested out in the degradation of methyl orange (MO, Aldrich 85%) using a 1,200 W lamp UV light source spaced at 3 cm horizontally. Prior to the test the stock solution of the water-based MO was prepared at 1,000 ppm in 100 mL and allowed to stand for 24 h. This was then followed by serial dilutions of 5, 10, 15, 20, 25, and 30 ppm. Five dilutions were used for the calibration curve, as shown in Figure 2, where R2 = 0.9999 was obtained from the straight line. For the reaction using the synthesized photocatalyst, the green TiO2 NPs synthesized was added to MO solution (50 mL) and sonicated. The solution was stirred using a magnetic stirrer in the dark condition for 1 h in order to reach the adsorption equilibrium. After reaching the adsorption equilibrium, the UV light was switched on 3 mL of the treated MO was collected after interval of 30, 60, 90, 120, and 150 min of reaction. The concentration of the MO from the withdrawn aliquot was analyzed using a UV-Vis spectrophotometer.

Figure 2.

Figure 2

Calibration curve spectra and line graph of M.O. Solution.

Results and Discussion

Possible Mechanism for the Formation of TiO2 NPs

Preliminary phytochemical screening was done using standard procedures to identify the constituents present in the extract, as described by Samkeliso et al. (2018). It involves observing plant samples for different classes of phytochemicals. This qualitative tests were used to provide an indication of the nature of phytochemicals present in D. pinnata (Poir.) Schumach. and Thonn's extract, as shown in Table 1.

Table 1.

Phytochemical constituents present in ethyl acetate leaf extracts of D. pinnata.

Constituents Results
Phenolics +++
Flavonoids +++
Alkaloids ++
Steroids ++
Coumarins ++

Table 1 shows that the plant of D. pinnata contains high amount of flavonoids and phenols that are important as surfactants and stabilizers. These constituents are able to prevent excessive agglomeration of the nanoparticulate material during the synthesis process. Other phyto-constituents present in the leaf extract were alkaloids, stereoids, and coumarins.

The mechanism for the formation of TiO2 is shown in Figure 3. TiO2 synthesis begins with complete hydrolysis of the precursor used [titanium isopropoxide, Ti(i-OPr)4] by direct interaction of the titanium source with water. Titanyl hydroxide was obtained according to the following reaction (Solano et al., 2019):

Figure 3.

Figure 3

Possible reaction mechanism for the formation of TiO2 NPs in presence of hydroxyl group (–OH) of leaf extract of D. pinnata.

Ti(i-OC3H7)4+3H2OTiO(OH)2+ 4C3H7OH

The FTIR data of D. pinnata ethyl acetate leaf extract displays the presence of a broad peak for OH functional group in the spectrum (Figure 13). It shows that the extract contains compounds having hydroxyl group as a functional group in the structure. Titanyl hydroxide can be dehydrated to give TiO2 nanoparticles by heating it with ethyl acetate leaf extracts of D. pinnata at about 50°C. In this process, D. pinnata extract serves as catalysts due to the present of compounds having hydroxyl group as a functional group in the structures (Selvaraj et al., 2012). Hence the reaction between D. pinnata extract and TiO(OH)2 might occur through the possible pathway which is described in Figure 3. Hence, water soluble compounds containing hydroxyl functional group are reported to be responsible for the stabilization of TiO2 nanoparticles.

Figure 13.

Figure 13

FTIR spectra of (A) D. pinnata crude extract and (B) synthesized TiO2 NPs.

Physicochemical Properties Green TiO2 NPs

In this research, green TiO2 NPs were successfully prepared by the sol-gel method using D. pinnata plant, extracted by different solvents with different polarities (n-hexane, ethyl acetate, and methanol). First, the preparation of green TiO2 NPs colloid was obtained by gradual addition of extracts into the continuously stirred titanium isopropoxide in distilled water. Subsequently, TiO2 NPs were washed with absolute ethanol several times and calcined at 500°C, before being characterized.

For the crystallinity studies done using XRD, as shown in Figure 4, the major peaks were at 2θ values of 25.18° (101), 37.73° (004), 47.94° (200), 53.76° (105), and 54.96° (211), which indicated the successful synthesis of anatase TiO2 NPS. The XRD pattern confirmed the synthesized TiO2 consist of anatase phase in high purity, with average crystallite size in the range of 19–21 nm. Scherer's equation (Lima et al., 2018), which relates the size of sub-micrometer crystallites in a solid to broadening of a sample peak in a diffraction pattern' illustrated as; D = Kλ/β cos θ where (D) is average crystal size for the main broadening anatase peak; K = Scherrer's coefficient constant (0.89) which depend on the crystallite shape, λ = X-ray wavelength; β = full width at half maximum intensity (FWHM) of diffraction peaks in radians and θ = Bragg's angle, has been used to correlate the sample analysis reference pattern. The average crystallite size of the synthesized TiO2 was 11 nm, which showed similarity with TiO2 NPs synthesis using the extracts of Syzygium cumini, as reported by Sethy et al. (2020). The order of their lattice parameters is as follows: the fraction from ethyl acetate (a = 3.79632, b = 9.52847) > n-hexane (a = 3.79223, b = 9.51600) > methanol (a = 3.79237, b = 9.51330), which indicates the qualitative merit for the fraction obtained by ethyl acetate [(0.149) > n-hexane fraction (0.136) >methanol extracts (0.121)]. This is indirectly proportional to their 2θ vales of (101), where ethyl acetate fractions with 25.2324 < n-hexane fractions at 25.2607 < methanol fractions at the value of 25.2608. Thus, XRD morphological studies showed significant crystallinity, crystal phase, and peak sharpness of green TiO2 obtained using ethyl acetate plant extracts compared to those of methanol and n-hexane fractions, by comparing their major peaks, lattice parameter, and qualitative merit. Since TiO2 synthesized with the extracts of D. pinnata plant using ethyl acetate as solvent showed better results, further characterizations were focused on the ethyl acetate green TiO2 NPS. The crystallographic database (DB card number 5000223) did match with the tetragonal anatase of high purity indexed at 97.55 (15%), as displayed in Figure 5. The 3D-tetragonal crystal structure showed a supportive lattice parameter at a = 3.7963Å and c = 9.52847Å with angle of 90°.The quantitative analysis showed a figure of merit at 0.149 with a space group at 141: 141/amd:1. Such crystallinity, crystal phase, and peak sharpness of green TiO2 NPS anatase were reported to influence their application as catalyst (Kim et al., 2018) or as support (Bagheri et al., 2014), acting as gas sensor (Zakrzewska and Radecka, 2017), degradation of pollutants (Phuinthiang and Kajitvichyanukul, 2019) and in solar cell (Kang et al., 2019).

Figure 4.

Figure 4

XRD patterns of green TiO2 NPs synthesized from the extracts of D. pinnata plant using (A) methanol, (B) n-hexane, and (C) ethyl acetate as the extraction solvents.

Figure 5.

Figure 5

(A) The purity index and (B) 3D-tetragonal structure of anatase TiO2 obtained from the XRD results.

The FESEM images of green TiO2 NPS synthesized from the extracts of D. pinnata plant, obtained by ethyl acetate, with different magnifications, are shown in Figure 6. The size of the particles were in the range of 19–21 nm, and the particles were densely aggregated, with non-uniformed semi-spherical shapes. This also proved that TiO2 particles in nano-sized have been successfully obtained.

Figure 6.

Figure 6

FESEM images of synthesized green TiO2 NPs with magnifications of (A) 5,000 times and (B) 50,000 times.

The elemental analysis was performed via EDX. The EDX line scan spectrum of calcined TiO2 NPs in Figure 7 shows two peaks as the main chemical composition, which were Ti (61 wt.%) and O (35 wt.%). This is also consistent with the results obtained in the XRD analysis. The non-stoichiometric of TiO2 with the presence of oxygen can contribute to high performance in photocatalytic activity (Liu et al., 2012) with intense peak as bulk TiO2 and less intense peak as surface TiO2 (Ebrahimian et al., 2017). The EDX spectrum analysis showed that no other impurities were present in the synthesized green TiO2 NPs, which proved its high purity level.

Figure 7.

Figure 7

EDX spectrum of green TiO2 NPs synthesized from the extracts of D. pinnata plant using ethyl acetate as the extraction solvent.

The optical absorption properties of the green TiO2 NPs were studied by UV-Vis-NIR as the absorption potential is an important factor to reflect its photocatalysis. The wavelength dependent absorbance was within the range of 300–500 nm. The band gap energy (Eg) was calculated using this equation; Eg = 1239.8/λ in (Parida et al., 2013; Ljubas et al., 2015) where the absorption spectrum has a wavelength value of 378 nm, which indicated typical TiO2 anatase with high crystallinity as also reported by (Li et al., 2019), and band gap energy of 3.2 eV, as shown in Figure 8.

Figure 8.

Figure 8

UV-Vis of green TiO2 NPs.

The N2 isotherm and pore size distribution (inset) of the synthesized TiO2 NPs are shown in Figure 9. The isotherm is of type V isotherm, where a hysteresis loop can be seen. This indicates that the distribution of pores in an irregular flow rate (Tan et al., 2012). The BJH pore size distribution based on desorption branch showed major peaks starting from 2.02 to 6.00 nm with a broad peak at 3.98 nm, showing the mesoporosity. As for the specific surface area of synthesized TiO2 NPs, it was examined through BET multipoint graph, as shown in Figure 10. The BET surface area of the green TiO2 NPs was found to be 31.77 m2/g, which corresponds to correlation coefficient (r) of 0.99, as a liner graph (Ahmad et al., 2017).

Figure 9.

Figure 9

N2 isotherm and pore size distribution (inset) of the synthesized TiO2 NPs.

Figure 10.

Figure 10

BET plot of the synthesized green TiO2 NPs.

Thermogravimetric analysis is a method used to determine thermal stability and the fractions of volatile components by monitoring the weight changes at a constant heating rate (Pintana and Tippayawong, 2013). The differential scanning calorimetry deals with the heat flow-temperature and this analysis has been carried out in the temperature range of 20–800°C using the uncalcined sample, as shown in Figure 11. The first weight loss band can be seen at 102°C, which is attributed to the loss of adsorbed atmospheric water (Yang et al., 2017). The second noticeable peak at 278°C was assigned to lower molecular weight metabolites, such as long chain fatty acids, galloyl ester or long chain esters. The last weight loss at 503°C marked the decomposition of all organic compounds (Kim et al., 2018). The irregular band line shown in the spectrum may be attributed to the nature of the products formed. The higher percentage mass loss (70%) was found for lower molecular weight constituents. The temperature at 106 and 288°C are associated with the loss of ethanol-water mixtures residue and fatty acids/ester endothermically. The exothermic peaks at 98 and 180°C seen on the DSC curve may be attributed to early phase transformation (Marinescu and Sofronia, 2011). The third region at 500°C justified total phase transformation of residual organic constituents of high molecular weight strongly coordinated to TiO2 atoms such as triterpenoids.

Figure 11.

Figure 11

The TGA and DSC (inset) curves of the synthesized green TiO2 NPs.

Photoluminescence (PL) is also an important technique to study the optical properties of the synthesized TiO2 NPs. Figure 12 shows the p spectrum of the synthesized green TiO2 NPs. These NPs show a strong luminescent emission peak at 520.3 nm with irregular broad peak surfaces, in the green region, and a weak emission peak at 468.6 nm at room temperature. These transitions could be attributed to the complete inter-band formation in dxy orbital with phytoconstituents, implying 3d2 4s2, and 3d0 in the Ti4+ ions (Yin et al., 2013). It was also observed that the second luminescence peak shifted toward the lower energy region. This may be attributed to the inter bonding of Ti-O from the carbonyl components in the plant signifying active anatase TiO2 of good light-response (Haghighatmamaghani et al., 2018). Furthermore, the shift toward the blue region may indicate a slight decrease in the particle sizes (Haque et al., 2017).

Figure 12.

Figure 12

PL spectrum of the synthesized green TiO2 NPs.

The FTIR spectrum of D. pinnata ethyl acetate extract and TiO2 NPs were indicated by Figures 13A,B, respectively. Absorption bands at 3,386, 2,927, 1,710, 1,612, 1,446, 1,043, and 756 cm−1 are due to O-H bond stretching, C-H bond stretching, C=O bond stretching of carbonyl groups, C=C bond stretching, C-O bond bending vibration on phenolic compound, C-O bond stretching of the hydroxyl group, and out-of-plane C-H bending for aromatic ring. These functional groups represent the phytochemicals present in the extract. In Figure 12B, the broad absorption band observed at 3,386 cm−1 represents O-H bond stretching due to adsorbed moisture at the surface of TiO2 NPs. The broad band at 537 cm−1 represents a characteristic peak of Ti-O-Ti bending mode of vibration which confirms the formation of metal oxygen bonding (Catauro et al., 2018). The TiO2 NPs calcined at 500°C showed no traces of organic components functional groups, which justified complete calcination.

Photocatalytic Activity

The photocatalytic activity of the green TiO2 NPs synthesized using the extracts of D. pinnata leaves with ethyl acetate as the solvent was tested out in the photodegradation of MO under UV light irradiation (1,200 W). The light source played a vital role in photocatalytic degradation as semiconductor compounds, such as TiO2, degrades volatile and organic pollutants under UV light irradiation (Cun et al., 2002; Laoufi and Bentahar, 2014; Luan et al., 2014). MO dye was chosen as the model organic pollutant and the photodegradation process was monitored by UV-visible spectrophotometer in the range of 800–200 nm. The degradation percentage was calculated using the following equation: D (%) = (Ci-Cf)/Ci × 100 where Ci is initial concentration, Cf is final concentration of MO at time (t) (Haque et al., 2017). Figure 14 shows the spectra of the reaction mixture withdrawn at intervals of 30, 60, 90, 120, and 150 min. After only 90 min, 51.72% of MO has been degraded. It was also observed that at 120 min, the photodegradation reached 81.36%, while at 150 min, 97.53% of MO photodegradation was obtained. It is evident that the rate of photodegradation of green TiO2 NPs photocatalyst on MO increased with longer irradiation time. This indicate faster interaction between the photons and green TiO2 NPs, which showed direct proportionality to the duration of irradiation. Therefore, MO (20 ppm) showed optimum irradiation duration of 150 min (97.53%). This can signify rapid formation of ∙OH radicals as active sites on the TiO2 NPs' surface for effective adsorption throughout the reaction (Youssef et al., 2016). Based on these results, it can be seen that an optimal performance of green TiO2 NPs can be achieved within a short time. This may indicate that extracts from plants as green substitute for the synthesis of NPs has the benefits of enhancing the charge carrier's separation (Solano et al., 2019), increasing specific surface area and overall photocatalytic performance. The physicochemical properties and photocatalytic activity have justified the efficient performance of green synthesized TiO2 NPs from D. pinnata plant for the photodegradation of MO.

Figure 14.

Figure 14

Absorbance spectra of photocatalytic degradation pattern of MO solution.

Conclusion

Based on the physicochemical characterization, TiO2 NPs have been successfully synthesized using the extracts of D. pinnata leaves. Different solvents used in the extraction also showed the contributions of solvents polarity in the extractions, where in this work, extracts using ethyl acetate showed superior characteristics. The synthesized green TiO2 NPs also showed good photocatalytic activity in the photodegradation of methyl orange dye under UV light irradiation. The work here showed that TiO2 NPs with good physicochemical properties and photocatalytic activity can be synthesized using extracts of plants, which can reduce or eliminate the use of harmful chemicals. Further work on the physicochemical properties and photocatalytic activity of TiO2 NPs obtained using extracts from n-hexane and methanol will be carried out.

Data Availability Statement

The original contributions presented in the study are included in the article/supplementary materials, further inquiries can be directed to the corresponding author/s.

Author Contributions

All authors listed have made a substantial, direct and intellectual contribution to the work, and approved it for publication.

Conflict of Interest

The authors declare that the research was conducted in the absence of any commercial or financial relationships that could be construed as a potential conflict of interest.

Footnotes

Funding. This research received funding from Ministry of Higher Education (MOHE) under the Fundamental Research Grant Scheme (R.J130000.7854.5F242) and Collaborative Research Grant (R.J130000.7354.4B502), Research Grant from Nippon Sheet Glass Foundation for Materials Science and Engineering (R.J130000.7354.4B515) and Universiti Teknologi Malaysia for Industry-International Incentive Grant (Q.J130000.3654.02M62). A great appreciation to Tertiary Education Trust Fund-Nigeria (TET Fund) for doctoral study support and Faculty of Science, Universiti Teknologi Malaysia for the research facilities.

References

  1. Agarwal H., Nakara A., Shanmugam V. K. (2018). Anti-inflammatory mechanism of various metal and metal oxide nanoparticles synthesized using plant extracts: a review. Biomed. Pharmacother. 109, 2561–2572. 10.1016/j.biopha.2018.11.116 [DOI] [PubMed] [Google Scholar]
  2. Ahmad S., Munir S., Zeb N., Ullah A., Khan B., Ali J., et al. (2019). Green nanotechnology: a review on green synthesis of silver nanoparticles—an ecofriendly approach. Int. J. Nanomed. 14, 5087–5107. 10.2147/IJN.S200254 [DOI] [PMC free article] [PubMed] [Google Scholar]
  3. Ahmad T., Phul R., Alam P., Lone I. H., Shahazad M., Ahmed J., et al. (2017). Dielectric, optical and enhanced photocatalytic properties of CuCrO2 nanoparticles. RSC Adv. 7, 27549–27557. 10.1039/C6RA26888A [DOI] [Google Scholar]
  4. Bagheri S., Muhd Julkapli N., Bee Abd Hamid S. (2014). Titanium dioxide as a catalyst support in heterogeneous catalysis. Sci. World J. 2014, 1–21. 10.1155/2014/727496 [DOI] [PMC free article] [PubMed] [Google Scholar]
  5. Benkhaya S., El Harfi S., Elharfi A. (2017). Classifications, properties and applications of textile dyes : a review. Appl. J. Environ. Eng. Sci. 3, 311–320. 10.1016/j.heliyon.2020.e03271 [DOI] [Google Scholar]
  6. Bregadiolli B. A., Fernandes S. L., De Oliveira Graeff C. F. (2017). Easy and fast preparation of TiO2-based nanostructures using microwave assisted hydrothermal synthesis. Mater. Res. 20, 912–919. 10.1590/1980-5373-mr-2016-0684 [DOI] [Google Scholar]
  7. Catauro M., Tranquillo E., Dal Poggetto G., Pasquali M., Dell'Era A., Ciprioti S. V. (2018). Influence of the heat treatment on the particles size and on the crystalline phase of TiO2 synthesized by the sol-gel method. Materials 11, 2364–2375. 10.3390/ma11122364 [DOI] [PMC free article] [PubMed] [Google Scholar]
  8. Chiu Y. H., Chang T. F. M., Chen C. Y., Sone M., Hsu Y. J. (2019). Mechanistic insights into photodegradation of organic dyes using heterostructure photocatalysts. Catalysts 9:430 10.3390/catal9050430 [DOI] [Google Scholar]
  9. Cun W., Jincai Z., Xinming W., Bixian M., Guoying S., Ping'an P., et al. (2002). Preparation, characterization and photocatalytic activity of nano-sized ZnO/SnO2 coupled photocatalysts. Appl. Catal. B Environ. 39, 269–279. 10.1016/S0926-3373(02)00115-7 [DOI] [Google Scholar]
  10. Dinh C. T., Nguyen T. D., Kleitz F., Do T. O. (2012). A solvothermal single-step route towards shape-controlled titanium dioxide nanocrystals. Can. J. Chem. Eng. 90, 8–17. 10.1002/cjce.20574 [DOI] [Google Scholar]
  11. Ebrahimian A., Monazzam P., Fakhari B. (2017). Co/TiO2 nanoparticles : preparation, characterization and its application for photocatalytic degradation of methylene blue. Desalin. Publ. 63, 283–292. 10.5004/dwt.2017.20205 [DOI] [Google Scholar]
  12. Elbushra H., Ahmed M., Wardi H., Eassa N. (2018). Synthesis and characterization of TiO2 using sol-gel method at different annealing temperature. MRS Advances. 3, 2527–2535. 10.1557/adv.2018.23 [DOI] [Google Scholar]
  13. Guettaï N., Ait Amar H. (2005). Photocatalytic oxidation of methyl orange in presence of titanium dioxide in aqueous suspension. Part I: parametric study. Desalination 185, 427–437. 10.1016/j.desal.2005.04.048 [DOI] [Google Scholar]
  14. Haghighatmamaghani A., Haghighat F., Lee C. (2018). Performance of various commercial TiO2 in photocatalytic degradation of a mixture of indoor air pollutants: effect of photocatalyst and operating parameters. Sci. Technol. Built Environ. 4731, 1–41. 10.1080/23744731.2018.1556051 [DOI] [Google Scholar]
  15. Haque F. Z., Nandanwar R., Singh P. (2017). Evaluating photodegradation properties of anatase and rutile TiO2 nanoparticles for organic compounds. Optik 128, 191–200. 10.1016/j.ijleo.2016.10.025 [DOI] [Google Scholar]
  16. Hejazi S., Mohajernia S., Osuagwu B., Zoppellaro G., Andryskova P., Tomanec O., et al. (2020). On the controlled loading of single platinum atoms as a co-catalyst on TiO2 anatase for optimized photocatalytic H2 generation. Advan. Mater. 32:1908505. 10.1002/adma.201908505 [DOI] [PubMed] [Google Scholar]
  17. Hiremath S., Antony Raj M. A. L., Chandra Prabha M. N., Vidya C. (2018). Tamarindus indica mediated biosynthesis of nano TiO2 and its application in photocatalytic degradation of Titan yellow. J. Environ. Chem. Eng. 6, 7338–7346. 10.1016/j.jece.2018.08.052 [DOI] [Google Scholar]
  18. Kang X., Liu S., Dai Z., He Y., Song X., Tan Z. (2019). Titanium dioxide: from engineering to applications. Catalysts 9, 191–223. 10.3390/catal9020191 [DOI] [Google Scholar]
  19. Kankara S. S., Ibrahim M. H., Mustafa M., Go R. (2015). Ethnobotanical survey of medicinal plants used for traditional maternal healthcare in Katsina state, Nigeria. S. Afr. J. Bot. 97, 165–175. 10.1016/j.sajb.2015.01.007 [DOI] [Google Scholar]
  20. Khalik W. F., Ong S. A., Ho L. N., Voon C. H., Wong Y. S., Yusoff N. A., et al. (2017). Comparison the performance of carbon plate and Pt-loaded carbon in photocatalytic fuel cell (PFC) process. AIP Conf. Proceed. 1828:020014 10.1063/1.4979385 [DOI] [Google Scholar]
  21. Khataee A. R., Mirzajani O. (2010). UV/peroxydisulfate oxidation of C. I. Basic Blue 3: modeling of key factors by artificial neural network. Desalination 251, 64–69. 10.1016/j.desal.2009.09.142 [DOI] [Google Scholar]
  22. Khataee A. R., Pons M. N., Zahraa O. (2010). Photocatalytic decolorisation and mineralisation of orange dyes on immobilised titanium dioxide nanoparticles. Water Sci. Technol. 62, 1112–1120. 10.2166/wst.2010.438 [DOI] [PubMed] [Google Scholar]
  23. Kim T. H., Go G. M., Cho H. B., Song Y., Lee C. G., Choa Y. H. (2018). A novel synthetic method for N doped TiO2 nanoparticles through plasma-assisted electrolysis and photocatalytic activity in the visible region. Front. Chem. 6, 1–10. 10.3389/fchem.2018.00458 [DOI] [PMC free article] [PubMed] [Google Scholar]
  24. Kitamura Y., Okinaka N., Shibayama T., Mahaney O. O. P., Kusano D., Ohtani B., et al. (2007). Combustion synthesis of TiO2 nanoparticles as photocatalyst. Powder Technol. 176, 93–98. 10.1016/j.powtec.2007.02.009 [DOI] [Google Scholar]
  25. Laoufi N. A., Bentahar F. (2014). Pesticide removal from water suspension by UV/TiO2 process : a parametric study. Desalin. Water Treat. 52, 1947–1955. 10.1080/19443994.2013.804453 [DOI] [Google Scholar]
  26. Lee H., Song M. Y., Jurng J., Park Y. K. (2011). The synthesis and coating process of TiO2 nanoparticles using CVD process. Powder Technol. 214, 64–68. 10.1016/j.powtec.2011.07.036 [DOI] [Google Scholar]
  27. Li Y., Fu Y., Zhu M. (2019). Green synthesis of 3D tripyramid TiO2 architectures with assistance of aloe extracts for highly efficient photocatalytic degradation of antibiotic ciprofloxacin. Appl.Catal. B Environ. 260, 1–9. 10.1016/j.apcatb.2019.118149 [DOI] [Google Scholar]
  28. Lima F. M., Martins F. M., Herbert P., Maia F., Fabíola A., Almeida L., et al. (2018). Nanostructured titanium dioxide average size from alternative analysis of Scherrer' s. Rev. Mat. 23, 1–10. 10.1590/s1517-707620170001.0301 [DOI] [Google Scholar]
  29. Liu F., Lu L., Xiao P., He H., Qiao L., Zhang Y. (2012). Effect of oxygen vacancies on photocatalytic efficiency of TiO2 nanotubes aggregation. Bull. Korean Chem. Soc. 33, 2255–2259. 10.5012/bkcs.2012.33.7.2255 [DOI] [Google Scholar]
  30. Ljubas D., Smoljanić G., Juretić H. (2015). Degradation of methyl orange and congo red dyes by using TiO2 nanoparticles activated by the solar and the solar-like radiation. J. Environ. Manage. 161, 83–91. 10.1016/j.jenvman.2015.06.042 [DOI] [PubMed] [Google Scholar]
  31. Luan J., Chen M., Hu W. (2014). Synthesis, characterization and photocatalytic activity of new photocatalyst ZnBiSbO4 under visible light irradiation. Int. J. Mol. Sci. 15, 9459–9480. 10.3390/ijms15069459 [DOI] [PMC free article] [PubMed] [Google Scholar]
  32. Marinescu C., Sofronia A. (2011). DSC investigation of nanocrystalline TiO2 powder. J. Therm. Anal. Calorim. 103, 49–57. 10.1007/s10973-010-1072-6 [DOI] [Google Scholar]
  33. May-Masnou A., Soler L., Torras M., Salles P., Llorca J., Roig A. (2018). Fast and simple microwave synthesis of TiO2/Au nanoparticles for gas-phase photocatalytic hydrogen generation. Front. Chem. 6, 1–13. 10.3389/fchem.2018.00110 [DOI] [PMC free article] [PubMed] [Google Scholar]
  34. Mohamad N. A. N., Arham N. A., Jai J., Hadi A. (2014). Plant extract as reducing agent in synthesis of metallic nanoparticles: a review. Advan. Mater. Res. 832, 350–355. 10.4028/www.scientific.net/AMR.832.350 [DOI] [Google Scholar]
  35. Murugan R., Parimelazhagan T. (2014). Comparative evaluation of different extraction methods for antioxidant and anti-inflammatory properties from Osbeckia parvifolia Arn.–an in vitro approach. J. King Saud Univ. 26, 267–275. 10.1016/j.jksus.2013.09.006 [DOI] [Google Scholar]
  36. Órdenes-Aenishanslins N. A., Saona L. A., Durán-Toro V. M., Monrás J. P., Bravo D. M., Pérez-Donoso J. M. (2014). Use of titanium dioxide nanoparticles biosynthesized by Bacillus mycoides in quantum dot sensitized solar cells. Microb. Cell Fac. 13:90. 10.1186/s12934-014-0090-7 [DOI] [PMC free article] [PubMed] [Google Scholar]
  37. Parida K. M., Pany S., Naik B. (2013). Green synthesis of fibrous hierarchical meso-macroporous N doped TiO2 nanophotocatalyst with enhanced photocatalytic H2 production. Int. J. Hydrog. Energy 38, 3545–3553. 10.1016/j.ijhydene.2012.12.118 [DOI] [Google Scholar]
  38. Patel D. K. (2015). Plants as a source of medicine. Med. Aromat. Plants S3:2167 10.4172/2167-0412.S3-e001 [DOI] [Google Scholar]
  39. Phuinthiang P., Kajitvichyanukul P. (2019). Degradation of paraquat from contaminated water using green TiO2 nanoparticles synthesized from Coffea arabica L. in photocatalytic process. Water Sci. Technol. 79, 905–910. 10.2166/wst.2018.493 [DOI] [PubMed] [Google Scholar]
  40. Pintana P., Tippayawong N. (2013). Nonisothermal thermogravimetric analysis of Thai Lignite with high CaO content. Sci. World J. 2013, 1–7. 10.1155/2013/216975 [DOI] [PMC free article] [PubMed] [Google Scholar]
  41. Rab N., Chong F. K., Mohamed H. I., Lim W. H. (2018). Preparation of TiO2 nanoparticles by hydrolysis of TiCl 4 using water and glycerol solvent system. J. Phys. Conf. Ser. 1123, 1–8. 10.1088/1742-6596/1123/1/012065 [DOI] [Google Scholar]
  42. Raghad D. H., Abdul J., Nuaman R. S., Abd A. N. (2016). Biological synthesis of titanium dioxide nanoparticles by Curcuma longa plant extract and study its biological properties. World Sci. News 49, 204–222. Available online at: www.worldscientificnews.com [Google Scholar]
  43. Samkeliso T., Fanyana M., Michael P. (2018). Analysis of the phytochemical contents and antioxidant activities of crude extracts from Tulbaghia species. J. Tradit. Chin. Med. 38, 272–729. 10.1016/j.jtcm.2018.04.005 [DOI] [PubMed] [Google Scholar]
  44. Selvaraj M. R., Bharathia A., Prabhakarn A., Abdul Rahuman A., Velayutham K., Rajakumar G., et al. (2012). Efficient phytosynthesis and structural characterization of rutile TiO2 nanoparticles using Annona squamosa peel extract. Spectrochim. Acta A Mol. Biomol. Spectrosc. 98, 86–90. 10.1016/j.saa.2012.08.055 [DOI] [PubMed] [Google Scholar]
  45. Sethy N. K., Arif Z., Mishra P. K., Kumar P. (2020). Green synthesis of TiO2 nanoparticles from Syzygium cumini extract for photo-catalytic removal of lead (Pb) in explosive industrial wastewater. De Gruyter 9, 171–181. 10.1515/gps-2020-0018 [DOI] [Google Scholar]
  46. Solano R. A., Herrera A. P., Maestre D., Cremades A. (2019). Fe-TiO2 nanoparticles synthesized by green chemistry for potential application in waste water photocatalytic treatment. J. Nanotechnol. 2019, 1–11. 10.1155/2019/4571848 [DOI] [Google Scholar]
  47. Sotubo S. E., Lawal O. A., Osunsami A. A., Ogunwande I. A. (2016). Constituents and insecticidal activity of Deinbollia pinnata essential oil. Nat. Prod. Commun. 11:1889. 10.1177/1934578x1601101228 [DOI] [PubMed] [Google Scholar]
  48. Sundrarajan M., Bama K., Bhavani M., Jegatheeswaran S., Ambika S., Sangili A., et al. (2017). Obtaining titanium dioxide nanoparticles with spherical shape and antimicrobial properties using M. citrifolia leaves extract by hydrothermal method. J. Photochem Photobiol. B Biol. 171, 117–124. 10.1016/j.jphotobiol.2017.05.003 [DOI] [PubMed] [Google Scholar]
  49. Tan Y. H., Davisa J. A., Fujikawaa K., Ganesh N. V., Demchenko A. V., Stine K. J. (2012). Surface area and pore size characteristics of nanoporous gold subjected to thermal, mechanical, or surface modification studied using gas adsorption isotherms, cyclic voltammetry, thermogravimetric analysis, and scanning electron microscopy. J. Mater.Chem. 22, 6733–6745. 10.1039/c2jm16633j [DOI] [PMC free article] [PubMed] [Google Scholar]
  50. Thakur B. K., Kumar A., Kumar D. (2019). Green synthesis of titanium dioxide nanoparticles using Azadirachta indica leaf extract and evaluation of their antibacterial activity. S. Afr. J. Bot. 124, 223–227. 10.1016/j.sajb.2019.05.024 [DOI] [Google Scholar]
  51. Venugopal K., Ahmad H., Manikandan E., Thanigai Arul K., Kavitha K., Moodley M. K., et al. (2017). The impact of anticancer activity upon beta vulgaris extract mediated biosynthesized silver nanoparticles (Ag-NPs) against human breast (MCF-7), lung (A549) and pharynx (Hep-2) cancer cell lines. J. Photochem. Photobiol. B Biol. 173, 99–107. 10.1016/j.jphotobiol.2017.05.031 [DOI] [PubMed] [Google Scholar]
  52. Yang C., Dong W., Cui G., Zhao Y., Shi X., Xia X. (2017). Highly-efficient photocatalytic degradation of methylene blue by PoPD-modified TiO2 nanocomposites due to effect of TiO2 with PoPD. Sci. Rep. 7, 1–12. 10.1038/s41598-017-04398-x [DOI] [PMC free article] [PubMed] [Google Scholar]
  53. Yin W., Zhang L., Wang Z., Wang T., Zhou C., Selloni A., et al. (2013). Electronic structure and photoabsorption of Ti3+ ions in reduced anatase and rutile TiO2. Physical Chem. Chem. Phys. 1, 1–9. 10.1039/c8cp02648c [DOI] [PubMed] [Google Scholar]
  54. Youssef N. A., Shaban S. A., Ibrahim F. A., Mahmoud A. S. (2016). Degradation of methyl orange using Fenton catalytic reaction. Egypt. J. Pet. 25, 317–321. 10.1016/j.ejpe.2015.07.017 [DOI] [Google Scholar]
  55. Zakrzewska K., Radecka M. (2017). TiO2-based nanomaterials for gas sensing- influence of anatase and rutile contributions. Nanoscale Res. Lett. 12, 1–8. 10.1186/s11671-017-1875-5 [DOI] [PMC free article] [PubMed] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Data Availability Statement

The original contributions presented in the study are included in the article/supplementary materials, further inquiries can be directed to the corresponding author/s.


Articles from Frontiers in Chemistry are provided here courtesy of Frontiers Media SA