Abstract
Introduction
The Bis-GMA, which is known to possess toxic properties to the human body, is part of the chemical structure of several direct dental restorative materials [1]. However, currently, there are composite resins on the market that are free of this monomer [2]. From the dental resin are released many other compounds [3]. The aim of this study was to analyse the composition of restorative materials from three different brands, and to verify whether or not Bis-GMA monomers are present in their composition.
Materials and methods
Samples of the Enamel plus HRi® Universal Dentine (Micerium), Enamel plus HRi® Bio Function (Micerium), Filtek® One Bulk Fill Restorative (3 M ESPE) and Admira® Fusion (VOCO) resins were prepared using three different methods: light-curing resin specimens placed for 18 min in an ethanol/water solution; light-curing resin specimens placed for 180 min in an ethanol/water solution; resin samples eluted in an acetonitrile solution without being photopolymerized. These samples were analysed using the HPLC (High Performance Liquid Chromatography) technique.
Results
HEMA, Bis-GMA and UDMA monomers were found in the composite resin Enamel plus HRi® Universal Dentine (Micerium); UDMA monomers were detected in Enamel plus HRi® Bio Function (Micerium); UDMA and TEGDMA monomers were revealed in Filtek® One Bulk Fill Restorative (3 M ESPE), and HEMA and UDMA peaks were obtained in Admira® Fusion (VOCO).
Discussion and conclusions
The release of most of the residual monomers occurs in the first minutes after polymerisation. As shown in the results, the difference of the concentrations of monomers, detected by the HPLC method, between the resins eluted during 18 min and 180 min, was not significant. It was concluded that in samples of non-polymerized resins, it is possible to detect a larger number of residual monomers, and that Bis-GMA is only present in Enamel plus HRi® Universal Dentine (Micerium) resin.
Acknowledgements
The authors would like to acknowledge to VOCO GmbH, Micerium and 3M for providing the dental resins and to the Biomaterials Laboratory of Egas Moniz.
References
- 1.Fleisch AF, Sheffield PE, Chinn C, et al. Bisphenol A and related compounds in dental materials. Pediatrics. 2010;126(4):760–768. [DOI] [PMC free article] [PubMed] [Google Scholar]
- 2.Klauer E, Belli R, Petschelt A, et al. Mechanical and hydrolytic degradation of an Ormocer®-based Bis-GMA-free resin composite. Clin Oral Invest. 2019;23(5):2113–2121. [DOI] [PubMed] [Google Scholar]
- 3.Gul P, Miloglu FD, Akgul N.. HPLC analysis of eluted monomers from dental composite using different immersion media. J Liq Chromatogr Related Technol. 2014;37(2):155–170. [Google Scholar]