Effects of the combination of bone morphogenetic protein-2 and nano-hydroxyapatite on the osseointegration of dental implants

Abstract

Objectives

This study aimed to investigate the in vitro osteoinductivity of the combination of bone morphogenetic protein-2 (BMP-2) and nano-hydroxyapatite (nHAp) and the in vivo effects of implants coated with nHAp/BMP-2.

Materials and Methods

To evaluate the in vitro efficacy of nHAp/BMP-2 on bone formation, bone marrow-derived mesenchymal stem cells (BM-MSCs) were seeded onto titanium disks coated with collagen (Col), Col/nHAp, or Col/nHAp/BMP-2. Protein levels were determined by a biochemical assay and reverse transcriptase-polymerase chain reaction. Stem cell differentiation was analyzed by flow cytometry. For in vivo studies with mice, Col, Col/nHAp, and Col/nHAp/BMP-2 were injected in subcutaneous pockets. Titanium implants or implants coated with Col/nHAp/BMP-2 were placed bilaterally on rabbit tibias and evaluated for 4 weeks.

Results

In the in vitro study, BM-MSCs on Col/nHAp/BMP-2 showed reduced levels of CD73, CD90, and CD105 and increased levels of glycosaminoglycan, osteopontin, and alkaline phosphatase activity. After 4 weeks, the Col/nHAp/BMP-2 implant showed greater bone formation than the control (P=0.07), while no differences were observed in bone implant contact and removal torque.

Conclusion

These results suggest that a combination of BMP-2 and an nHAp carrier would activate osseointegration on dental implant surfaces.

I. Introduction

Studies have been directed towards improving the osseointegration of dental implants by modifying the implant surface¹. Surface topography and chemical modification are two important elements that influence the bone/implant interface². Biochemical modification refers to the immobilization of bioactive peptides or growth factors such as bone morphogenetic protein (BMP)³.

BMP-2, a member of the transforming growth factor beta superfamily, binds to the receptors of mesenchymal stem cells, osteoblasts, and osteoclasts, and induce cell chemotaxis, proliferation, and differentiation. Dental implants placed in bone whose formation is induced by BMP-2 have been reported to exhibit successful osseointegration and respond well to functional loading, as do dental implants placed in native alveolar bone^4,5. High doses of BMP-2 are known to directly induce bone formation⁶. While BMP-2 has yielded promising results regarding osteogenesis, high dosage may produce detrimental side effects, including heterotopic bone formation, soft-tissue swelling, seroma formation, osteolysis, radiculopathy, and malignancy. Therefore, to achieve bone induction, a sustained-release carrier is needed for BMP-2 due to its short biological half-life and rapid diffusion when implanted in vivo^6-14.

Many materials have been tested as a delivery system for BMP, including synthesized polymers, collagen, tricalcium phosphate, polyethylene glycol hydrogels, and hydroxyapatite (HAp)^6,15. HAp has been applied to clinically approved bone substitutes due to its high osteoconductivity and maintenance of a constant shape. It also exhibits a high affinity for BMP-2, evenly distributes BMP-2 under pressure, and causes minimal foreign body reactions, and is therefore considered useful as a BMP carrier¹⁶. Lee et al.⁶ reported excellent results when BMP-2 was combined with HAp as bone-grafting material in a rabbit spinal fusion model. Furthermore, recent studies have produced improved results for implant surfaces coated with BMP-2. To our knowledge, no studies have been performed on the efficacy and effects of combining BMP-2 with nano-hydroxyapatite (nHAp) on implant surfaces. We hypothesized that a surface coating combining BMP-2 with nHAp would improve osseointegration; therefore, we have evaluated the osteoinductivity of BMP-2 combined with nHAp on dental implant surfaces in vitro and in vivo.

II. Materials and Methods

1. Preparation of titanium disks

Grade-4 titanium foils (5 cm×5 cm) were used. nHAp solution was purchased from Sigma-Aldrich Chemical (St. Louis, MO, USA). Human BMP-2 was donated by Daewoong Pharmaceutical (Seoul, Korea). The surface of each titanium disk was etched by sonification of the disks in Kroll’s reagent (4.0% HF, 7.2% HNO₃, and 88.8% water) for 10 minutes. The disks were then washed ultrasonically for 10 minutes each in acetone and triple-distilled water and placed in 40% HNO₃ for 40 minutes in order to passivate the surface.

2. Preparation of collagen/nHAp/BMP-2 composite solution and coating

The composite solution consisted of collagen (Col), nHAp, and BMP-2. A type I atelocollagen powder (Koken, Osaka, Japan) was dissolved at a concentration of 5 mg/mL, and chondroitin-6-sulfate, nHAp, and BMP-2 were dissolved at concentrations of 0.25 mg/mL, 0.03 mg/mL, and 100 μg/mL, respectively. The composite solution (500 μL) was coated onto the titanium foil (5 cm×5 cm), and the foil was dried for 24 hours at 4°C. For implants attached to the rabbit tibias, 20 μL of the composite solution was coated onto each implant, and the implant was dried for 24 hours at 4°C. The surfaces of the various titanium disks were characterized by static contact angle and atomic force microscopy (AFM).

3. AFM

To scan the surface, Nanomen II AFM (Veeco, Plainview, NY, USA) was used. Scans and readings were taken by tapping mode AFM at random sites (1 mm² each) for 3 disks using a 5-mm scan head. A cantilever with an attached tip was oscillated at its resonant frequency to scan across the sample surface. Typical amplitudes were 20-100 nm, which could vary when the tip scanned over bumps or depressions on a surface. The van der Waals forces were 200 pN or less. The surface roughness (root mean square [RMS]) was calculated using the Nanomen II software.

4. Contact angle

To measure the contact angle, a contact angle analyzer (DSA100; Krüss, Nürnberg, Germany) was used with 2 μm deionized water. The contact angle of the water droplet was measured after 10 seconds on both sides of the water droplet, and 5 samples per group were evaluated.

5. Release of BMP-2 from the disk

Release of BMP-2 from a bare titanium surface, Col, Col/BMP-2, or Col/nHAp/BMP-2 was determined by first incubating the disks with phosphate-buffered saline (PBS) at 37°C in sealed tubes blocked with bovine serum albumin and then recovering the released media at 1, 2, 3, 5, 7, and 9 days, followed by replacement with new PBS. BMP-2 was measured indirectly in the release media by using the human BMP-2 super X-ELISA kit obtained from Antigenix America (Huntington Station, NY, USA). Each group included 3 samples for loading and release.

6. Bone marrow-derived mesenchymal stem cell culture

Human bone marrow-derived mesenchymal stem cells (BM-MSCs) (passage 2) were purchased from Lonza (Portsmouth, NH, USA). The mononuclear cell fraction was isolated by Ficoll (0.77 g/mL) density gradient centrifugation. BM-MSCs (2×10⁵ cells) were seeded onto the 5 cm×5 cm titanium disks. The osteogenic medium consisted of DMEM containing 10% fetal bovine serum, 10 mM β-glycerophosphate, 50 μM Asc-2-P, and 10^–7 M dexamethasone (all from Sigma-Aldrich), and the medium was changed every 3 to 4 days.

7. Flow cytometry (FACS) after differentiation

Antibodies against human antigens CD90 and CD73 were purchased from BD Sciences (San Jose, CA, USA), and the antibody against CD105 was purchased from Ancell (Bayport, MN, USA). The fluorescence intensity of the cells was evaluated by a flow cytometer (FACScan; BD Sciences), and the data were analyzed using the CELLQUEST software (BD Sciences).

8. Biochemical assays for alkaline phosphatase (ALP), glycosaminoglycan (GAG), and osteopontin (OPN) production

ALP activity was measured from the cell supernatant by using SensoLyte pNPP Alkaline Phosphatase Assay Kit “Colorimetric” (AnaSpec, Fremont, CA, USA). The total intracellular sulfated GAG content was measured using a BlyscanSulfated Glycosaminoglycans Assay Kit (Bioassay, Hayward, CA, USA). The concentration of OPN protein in the culture medium was measured using a Quantikine Human Osteopontin Immunoassay kit (R&D Systems, Minneapolis, MN, USA). The samples were dissolved in dissociation reagent, and the absorbance was measured at 656 nm using a microplate reader (VERSAmax Tunable Microplate Reader; Molecular Devices, Sunnyvale, CA, USA).

9. Reverse transcription-polymerase chain reaction (RT-PCR) for BM-MSCs

RT-PCR analysis was performed to compare the expression of bone-inducing markers such as type I collagen, type III collagen, osteonectin, OPN, BMP-2, osteoprotegerin, and GAPDH (internal control). Total cellular RNA was isolated by Trizol reagent (Invitrogen, Carlsbad, CA, USA). cDNA was synthesized by reverse transcription. The primers used for RT-PCR were purchased from Bioneer (Daejeon, Korea), and their sequences, reaction conditions, and product size (bp) are summarized in Table 1. The PCR products were then analyzed on 2% agarose gels and visualized by SYBR safe DNA gel staining (Invitrogen). The Image J software (National Institutes of Health, Bethesda, MD, USA) was used for quantitative analysis of RT-PCR amplicons on digitized gel images.

Table 1.

Primer sequences, reaction conditions, and product size for RT-PCR

Gene	Sequence	Product size (bp)	Annealing (℃)	Cycles
GAPDH	F: ACC ACA GTC CAT GCC ATC AC R: TTC ACC ACC CTG TTG CTG TA	450	55	25
Collagen1	F: GAA AAC ATC CCA GCC AAG AA R: CAG GTT GCC AGT CTC CTC AT	270	57	23
Collagen3	F: CAG GTG AAC GTG GAG CTG C R: TGC CAC ACG TGT TTC CGT GG	661 849	57	23
Osteonectin	F: CCA GAA CCA CCA CTG CAA AC R: GGC AGG AAG AGT CGA AGG TC	161	57	23
Osteopontin	F: TCG CAG ACC TGA CAT CCA GT R: TCG GAA TGC TCA TTG CTC TC	267	57	32
BMP-2	F: GTC CAG CTG TAA GAG ACA CC R: GTA CTA GCG ACA CCC ACA AC	316	54	31

(RT-PCR: reverse transcription-polymerase chain reaction, GAPDH: glyceraldehyde 3-phosphate dehydrogenase, BMP-2: bone morphogenetic protein-2)

10. Mouse subcutaneous injection

The experiments were approved by the Animal Care and Use Committee, Seoul National University (SNU-100122-8). For all experiments, the animals were housed and handled in strict accordance with the animal care guidelines of the Institute of Laboratory Animal Resources, Seoul National University. Col, Col/nHAp, or Col/nHAp/BMP-2 was added to 20 μL of mixing solution and injected into the subcutaneous pockets of nude mice.

11. Immunohistochemical staining

Mice were sacrificed and examined 4 weeks after injection of a composite solution. H&E stain, Masson’s trichrome (MT) stain, and immunochemistry were performed to assess bone formation and angiogenesis from the injected composite solution. Anti-osteonectin (1:500 dilution, AB 1858; Chemicon, Carlsbad, CA, USA) was used for osteonectin staining and anti-CD31 monoclonal antibody (Dako, Carpinteria, CA, USA) for CD31 staining, followed by standard immunohistochemical procedures. The images were examined under a light microscope (System Microscope CX 40-32PH; Olympus, Center Valley, PA, USA).

12. Implant installation on the rabbit tibia and removal torque measurement

Titanium implants treated with resorbable blasted media were used as the negative control while implants coated with Col/nHAp/BMP-2 were used as the experimental group. The mean weight of the rabbits was 3.3±0.25 kg at the time of the operation. The diameter and length of the implant were 3.3 mm and 7 mm, respectively. Two control implants were randomly placed in the right or left side tibia of each animal, and 2 experimental implants were placed in the contralateral side tibia. The animals were sacrificed after a follow-up period of 4 weeks. The implants on the proximal side were used for histomorphometric analysis, and those on the distal side were used for the removal torque test. Static torque was applied at a linearly increasing rate of 9.5 Ncm/second. The strength and rate of osseointegration of the bone implant were evaluated by the peak removal torque values (RTQ, Ncm).

13. Histological analysis

The fixated specimens were dehydrated in a graded ethanol series by using a dehydration system with agitation and a vacuum and embedded in light-curing methacrylate (Technovit 7200 VCL; Kulzer, Wehrheim, Germany). The implants were cut in a mid-axial coronal-apical plane using the sawing-and-grinding technique (EXAKT Apparatebau, Norderstedt, Germany). The bone implant contact (BIC) ratio and new bone formation area inside the thread area of the upper 3 threads were measured.

14. Statistical analysis

Statistical analysis was performed using the PASW Statistics software (ver. 18.0; IBM, Armonk, NY, USA). Numerical data are presented as mean values with the standard deviations. The Mann–Whitney test was carried out to analyze the differences in parameters of the rabbit implant installation model.

III. Results

1. Effect of nHAp and BMP-2 on titanium surface roughness and chemistry

Col/nHAp/BMP-2 increased the surface roughness more than Col, Col/BMP-2, and the bare titanium surface.(Fig. 1) The RMS values of the negative control, Col, Col/BMP-2, and Col/nHAp/BMP-2 were 357, 535, 539, and 872 nm, respectively.

Fig. 1.

Topographic and three-dimensional atomic force microscopic images of the coatings. Titanium: untreated titanium disk, Col: collagen-coated titanium surface, Col/BMP-2: collagen/bone morphogenetic protein-2 (BMP-2)-coated titanium surface, Col/nHAp/BMP-2: collagen/nano-hydroxyapatite/BMP-2-coated titanium surface. (RMS: root mean square)

The water contact angles on the bare titanium surface, Col, Col/BMP-2, and Col/nHAp/BMP-2 were 70.5°±8.2°, 42.2°±3.6°, 41.4°±2.6°, and 58.4°±3.0°, respectively.(Fig. 2) These results indicated that the collagen-coated titanium surface increased hydrophilicity, while the addition of nHAp slightly reduced the hydrophilicity of the collagen-coated titanium surface.

Fig. 2.

Static water contact angle on titanium surface. A. Negative control (resorbable blasted media surface titanium). B. Collagen-coated surface. C. Collagen/BMP-2-coated surface. D. Collagen/nHAp/BMP-2-coated surface. (BMP-2: bone morphogenetic protein-2, nHAp: nano-hydroxyapatite)

2. BMP-2 release

A solution containing 200 ng of BMP-2 was coated onto the titanium surfaces. Surfaces treated with Col/nHAp/BMP-2 exhibited a release of approximately 50% after 24 hours incubation and approximately 75% after 48 hours incubation, while Col/BMP-2 exhibited a 70% initial release within 24 hours, followed by an 88% release at 48 hours.(Fig. 3) Therefore, most of the coated BMP-2 was released within 5 days from Col/nHAp/BMP-2 and within 3 days from Col/BMP-2.

Fig. 3.

In vitro release curve of bone morphogenetic protein-2 (BMP-2) from various surface-treated titanium disks. The results are shown as mean±standard deviation values (n=3). An increase in BMP-2 release was observed within 24 hours. A sustained release in the Col/nHAp/BMP-2 group was observed between 1-5 days. (Col: collagen, nHAp: nano-hydroxyapatite)

3. FACS analysis after differentiation

BM-MSCs were tested for the presence of mesenchymal stem cell markers, including the antigens CD73, CD90, and CD105, with flow cytometry.(Fig. 4. A) BM-MSCs exhibited high expression of these markers prior to differentiation. Expression was down-regulated following culturing on the titanium surface coated with Col/nHAp/BMP-2 after 2 weeks.

Fig. 4.

Bone marrow-derived mesenchymal stem cell (BM-MSC) differentiation on differently treated titanium disks. A. Flow cytometry of typical CD markers present on BM-MSCs cultured on the Col-, Col/nHAp-, or Col/nHAp/BMP-2-coated titanium disks. CD73+, CD90+, and CD105+ cells were observed prior to differentiation. Reduction in mesenchymal CD73+, CD90+, and CD105+ cells was observed in the Col/nHAp/BMP-2 group. B. Biochemical assays for alkaline phosphatase (ALP) activity and intracellular glycosaminoglycan (GAG) and osteopontin expression in BM-MSCs. Cells on Col/nHAp/BMP-2 exhibited the highest expression. C. mRNA expression of different osteoblastic markers in BM-MSC. The highest expression was observed for type III collagen (Col III), osteocalcin, and osteoprotegerin in cells grown on Col/nHAp/BMP-2. The levels of type I collagen (Col I), osteopontin, osteonectin, and BMP-2 expression were higher in BM-MSCs on Col/nHAp and Col/nHAp/BMP-2 than in those with Col enrichment. (Col: collagen, nHAp: nano-hydroxyapatite, BMP-2: bone morphogenetic protein-2)

4. Biochemical assays for ALP, GAG, and OPN production

The BM-MSCs were cultured for 14 days, and assays for ALP, GAG, and OPN production were performed to evaluate bone induction.(Fig. 4. B) In the cells grown on the Col/nHAp/BMP-2 surface, ALP activity and GAG and OPN levels were significantly higher than those in the cells grown with Col enrichment. Cells on the Col/nHAp/BMP-2 surface also exhibited higher ALP activity and GAG and OPN levels than those on the Col/nHAp surface. These findings indicated that BMP-2 with nHAp maintains its biological activity and induces bone development in BM-MSCs.

5. RT-PCR

As seen in Fig. 4. C, type I and III collagen levels significantly increased in BM-MSCs grown on Col/nHAp and Col/nHAp/BMP-2, respectively. A similar expression pattern was observed for osteocalcin and osteoprotegerin in cells grown on Col/nHAp/BMP-2. Both the Col/nHAp and Col/nHAp/BMP-2 groups had higher levels of OPN, osteonectin, and BMP-2 expression than the Col group.

6. Mouse subcutaneous injections

At the 4th week, no obvious bone formations were observed for any of the injected materials, either macroscopically or microscopically (Fig. 5. A-I), although many cells had grown into both Col/nHAp and col/nHAp/BMP-2. Additionally, the injected materials were partially degraded. Application of von Kossa staining revealed the absence of mineralization in the Col group (Fig. 5. J), with higher intensity observed for Col/nHAp than for Col/nHAp/BMP-2.(Fig. 5. K, 5. L) Differentiation of osteoblasts was confirmed by staining for osteonectin. Staining for osteonectin was limited in the case of Col enrichment, whereas the strongest staining was observed in Col/nHAp/BMP-2.(Fig. 5. M-O) For evaluating angiogenesis, tissues surrounding the injected composite solution were stained for CD31. A higher degree of CD31 staining and angiogenesis was observed in Col/nHAp/BMP-2 than in Col/nHAp.(Fig. 5. P-R)

Fig. 5.

Histological images of the mouse subcutaneous pocket injection model. Col (A, D, G, J, M, P), Col/nHAp (B, E, H, K, N, Q), and Col/nHAp/BMP (C, F, I, L, O, R). Macroscopic images (A-C), H&E staining (D-F), Masson’s trichrome (MT) staining (G-I), von Kossa staining (J-L), osteonectin staining (M-O), and CD31 staining (P-R) (D-O: ×100, P-R: ×200, scale bars=200 µm). (Col: collagen, nHAp: nano-hydroxyapatite, BMP-2: bone morphogenetic protein-2)

7. Implant installation on the rabbit tibia

No differences in stability were observed between the 2 types of implants. Results of the histomorphometric analysis for the 4-week specimens are summarized in Fig. 6. Following 4 weeks of healing, the Col/nHAp/BMP-2 implant demonstrated slightly more new bone area than the negative control (P=0.07), whereas BIC and removal torque showed no significant differences, although the mean values were higher. The Col/nHAp/BMP-2 demonstrated a greater BIC (33.46%±6.91%) than the titanium implant (31.36%±3.22%), but the differences were not statistically significant. New bone area in the Col/nHAp/BMP-2 (73.69%±5.88%) was slightly higher than that of the titanium implant surface (62.24%±12.52%). Similarly, Col/nHAp/BMP-2 had a greater removal torque (26.63±4.41 Ncm) than the negative control (22.90±2.33 Ncm).

Fig. 6.

Implant installation on rabbit tibia. A. Photograph of titanium implant (left) and Col/nHAp/BMP-2-coated implant (right). B-D. Bone implant contact, new bone area, and removal torque. At 4 weeks after implant installation on rabbit tibia, Col/nHAp/BMP-2 exhibited increased new bone area compared with the negative control (P=0.07), whereas bone implant contact and removal torque exhibited no significant difference, although the mean values were higher. (Col: collagen, nHAp: nano-hydroxyapatite, BMP-2: bone morphogenetic protein-2)

IV. Discussion

This study aimed to develop an implant surface that would allow the active growth factor BMP-2 to promote osseointegration. We thus investigated the biological response to BMP-2 combined with nHAp on titanium in vitro and in vivo. The results indicated that the coating potently increased osteoblastic differentiation of human BM-MSCs in vitro.

As a BMP-2 carrier, HAp also exhibited promising results. Recent studies with 5 different ceramic additives, that is, β-tricalcium phosphate and 4 types of HAp (e.g., nHAp, HAp), in the ectopic bone formation model of the rat thigh muscle have reported a higher bone density with 20 nm HAp than with the other additives¹⁷. Other studies found that BMP-7-transduced MSCs, seeded on nHAp composite, initially accelerated bone regeneration after implantation¹⁸. Using a rabbit model, Liu et al.¹⁹ demonstrated that an rhBMP-2-loaded gelatin/nHAp scaffold exhibited good osteogenic capability and could repair a segmental bone defect completely in 12 weeks. These findings were analogous to our results in vitro, which revealed osteoblastic differentiation of stem cells on titanium coated with nHAp and BMP-2. However, hydrophilicity was decreased when adding the nHAp on a collagen surface. Surface wettability was reported to be altered by biomaterial surface roughness, composition, and the presence of nanofeatures, and the effect of nHAp on surface wettability was controversial. These may be affected by the composition of the nHAp, such as the ratio of Ca/P, and further study would be necessary.

To study the influence of nHAp-BMP-2 on the differentiation of the BM-MSCs, we evaluated the expression of stem cell markers, as well as phenotypic markers of osteoblasts and osteogenic genes. FACS analysis demonstrated a loss of stemness with decreasing expression of CD73, CD90, and CD105. Biochemical assays revealed the highest levels of ALP, GAG, and OPN in Col/nHAp/BMP-2, followed by Col/nHAp. ALP activity is a phenotypic marker of osteoblasts and is characteristic of differentiation²⁰. GAG is the major organic extracellular matrix component, and changes in its composition are frequently seen in physiological and pathological remodeling processes such as bone formation or scarring²¹. The expression of OPN by osteoblasts early in bone development is consistent with the formation of the bone matrix²². Thus, higher ALP activity and greater expression of GAG and OPN in BM-MSCs on Col/nHAp/BMP-2 indicated that nHAp with BMP-2 can induce BM-MSCs to osteoblastic differentiation after culture for 14 days. These activities also increased on Col/nHAp, although to a lesser extent than for Col/nHAp/BMP-2. These results demonstrated the osteoinductive capacity of nHAp itself and the synergistic effect of coupling BMP-2 with nHAp.

The RT-PCR results revealed higher BMP-2 expression of cells on Col/nHAp and Col/nHAp/BMP-2 than on Col. For OPN and osteonectin levels, the early marker of bone development, similar patterns of expression were observed. These results also support the role of nHAp in osteoblast differentiation. A study by Prosecká et al.²³ reported a similar pattern in which a mixture of HAp and collagen could induce the osteogenic differentiation of MSCs. Expressions of osteocalcin and osteoprotegerin were highest in Col/nHAp/BMP-2. Osteocalcin is secreted solely by osteoblasts and is believed to play a role in bone mineralization and calcium ion homeostasis²⁴. Osteoprotegerin can reduce the production of osteoclasts by inhibiting the differentiation of osteoclast precursors into osteoclasts, and it also regulates the resorption of osteoclasts in vitro and in vivo²⁵. Considering these results and those from previous studies, it is possible that BMP-2 combined with nHAp stimulates the formation and mineralization of the bone due to their chemical or structural characteristics.

The mRNA expression levels of type I collagen were highest in BM-MSCs cultured on Col/nHAp, followed by Col/nHAp/BMP-2, while the expression level of type III collagen was highest on Col/nHAp/BMP-2. Type I collagen is the main component of the organic part of bone, whereas type III collagen, a major component of the extracellular matrix, is commonly found alongside type I collagen and is produced before the tougher type I collagen is synthesized^26,27. Some studies have reported that BMP-2 inhibits collagen synthesis. Song et al.²⁸ reported that the expression of mRNA for collagen types II and V was significantly down-regulated following treatment with rhBMP-2, while the effect of rhBMP-2 on the expression of mRNA for type I collagen was minimal, and the expression of mRNA for type III collagen was enhanced in a dose-dependent manner by treatment with BMP-2. No mechanism has yet been proposed to explain the effects of BMP-2 on collagen synthesis, although data from this study suggest a diverse role for BMP-2 on collagen formation.

The mouse subcutaneous injection model did not show any obvious bone formation in any of the groups at 4 weeks. Other studies using BMP-2 in ectopic bone formation models have reported high bone density on histological assessment, with dense bone, lacunae, ossification centers, osteoblasts, and osteocytes¹⁷. Although no obvious bone formations were observed either macroscopically or microscopically, the Col/nHAp/BMP-2 group strongly expressed osteonectin, an early marker of osteoblast differentiation, indicating a potential for bone formation after long periods²⁹.

Treating the implant surface with bioactive materials such as HAp and BMP-2 has been studied recently to promote osseointegration. Shi et al.³⁰ developed a sustained BMP-2 release system based on rhBMP-2 encapsulated poly-D,L-lactide-co-glycolide microspheres-loaded chitosan/collagen scaffolds and demonstrated improved osseointegration ability. Chatzinikolaidou et al.³¹ demonstrated the feasibility of enhancing peri-implant osseointegration and gap bridging by using immobilized BMP-2 on implant surfaces. Implants soaked in 2 mL of sterile water containing 1.0 mg BMP-2 with polylactic acid as the carrier exhibited both qualitative and quantitative improvements in osseointegration at the implant-bone interface³².

However, the results of our rabbit tibia implant model suggested that implants coated with BMP-2 and nHAp failed to produce any significant statistical differences, although the mean values for BIC, new bone area, and removal torque were higher. This could be due either to the BMP-2 release from the nHAp/BMP-2 coated implant or the role of BMP in bone formation.

In the release kinetics of BMP-2, most of the coated BMP-2 was released within 5 days for the Col/nHAp/BMP-2 group. Although BMP-2 incorporated with nHAp exhibited a slower release pattern than BMP-2 alone, recent studies have reported more sustained release patterns³³. Hence, the similar results observed between the collagen implant and BMP-2 combined with nHAp-coated implants would be explained by our relatively rapid release of BMP-2 compared to that seen in other studies. Therefore, a study with a 2-week observation period after placement of the BMP-2 implant would be necessary.

There remains some controversy regarding the efficacy of BMP in bone formation, as several factors are known to affect the osteoinductive ability of BMP-2. Recently, it has been reported that BMP-2 promotes the adipogenic differentiation of periodontal ligament stem cells both in vitro and in vivo, in association with a reduced amount of cementum and periodontal ligament formation²⁸. Other studies have also reported that BMP-2 significantly enhances the adipogenic as well as osteogenic potential of alveolar bone-derived stromal cells in a dose- and time-dependent manner⁵. The inhibitory effect of rhBMP-2 on collagen synthesis is related to the down-regulation of the minor, rather than the major, components of collagen²⁸. In addition, BMP-2 stimulates both the formation and resorption of bone at high doses³⁴. Although the presently used loading dose of BMP-2 is very low according to current clinical standards, it still might be excessive in this bony environment. Or on the contrary, our results could be due to too low a concentration of BMP-2. During the placement process of the implant, BMP-2 may be reduced greatly, and further study to rigidly fix the BMP-2 on the implant would be necessary.

V. Conclusion

BMP-2 combined with nHAp induced mesenchymal stem cell differentiation and osteoblastic differentiation in vitro and in vivo with the mouse pocket injection model, although no significant differences were observed in the rabbit tibia implant model. Therefore, our study suggests that BMP-2 combined with a nHAp carrier has the potential to function as an osseointegration activator on the surfaces of dental implants.