Highly efficient selective hydrogenation of levulinic acid to γ-valerolactone over Cu–Re/TiO2 bimetallic catalysts†

Yingxin Liu 1,2, Kai Liu 1, Meihua Zhang 1, Kaiyue Zhang 1, Jiao Ma 1, Shuwen Xiao 3,4, Zuojun Wei 3,4,✉, Shuguang Deng 2,✉
PMCID: PMC8978708  PMID: 35424528

Abstract

Highly active and thermally stable Cu–Re bimetallic catalysts supported on TiO2 with 2.0 wt% loading of Cu were prepared via an incipient wetness impregnation method and were applied for liquid phase selective hydrogenation of levulinic acid (LA) to γ-valerolactone (GVL) in H2. The effect of the molar ratios of Cu : Re on the physico-chemical properties and the catalytic performance of the Cu–Re/TiO2 catalysts was investigated. Moreover, the influence of various reaction parameters on the hydrogenation of LA to GVL was studied. The results showed that the Cu–Re/TiO2 catalyst with a 1 : 1 molar ratio of Cu to Re (Cu–Re(1 : 1)/TiO2) exhibited the highest performance for the reaction. Complete conversion of LA with a 100% yield of GVL was achieved in 1,4-dioxane solvent under the reaction conditions of 180 °C, 4.0 MPa H2 for 4 h, and the catalyst could be reused at least 6 times with only a slight loss of activity. Combined with the characterization results, the high performance of the catalyst was mainly attributed to the well-dispersed Cu–Re nanoparticles with a very fine average size (ca. 0.69 nm) and the co-presence of Cu–Re bimetal and ReOx on the catalyst surface.

Herein, we report a highly efficient and recyclable Cu–Re(1 : 1)/TiO2 bimetallic catalyst for liquid phase hydrogenation of levulinic acid to γ-valerolactone.graphic file with name d1ra05804e-ga.jpg

1. Introduction

Increasing global energy demands and diminishing fossil fuel stores have provided the scientific community with an unprecedented power in developing new economically viable routes to sustainable energy.1,2 Biomass, as a clean, renewable and new carbon source with the advantages of abundant reserves, low price and short generation period, is considered to be an indispensable energy source for human development in the future. Biomass can be converted into biofuels and high value-added chemicals through different technologies.2,3 γ-Valerolactone (GVL) is one of the most important sustainable biomass-derived chemicals, which can be used to participate in various reactions, as well as being applied as a food flavor, lubricant, plasticizer and reaction solvent, owing to its excellent physical and chemical properties.4–7

Typically, GVL can be obtained through hydrogenation and cyclization of biomass derivative levulinic acid (LA) over homogeneous or heterogeneous catalysts as shown in Scheme 1.8–10 In consideration of easy product separation and catalyst recycling, heterogeneous catalysts are preferred. Supported Ru, Rh, Pd, Pt, Au and Ir noble metal catalysts have been employed for the hydrogenation of LA into GVL.11–16 Among them, Ru-based catalysts have been proved to be one of the most active heterogeneous catalysts.17–21 Our previous work also showed that the Ru catalyst embedded in N-doped mesoporous carbon exhibited high performance for the hydrogenation of LA into GVL.22

Scheme 1. Reaction pathways for the hydrogenation of LA to GVL.

Scheme 1

Open in a new tab

At the same time, some researchers have focused on non-noble metal catalysts.23 The Cu-based non-noble metal catalysts, which are generally considered to be active for the selective hydrogenation of C Created by potrace 1.16, written by Peter Selinger 2001-2019 O bonds and relatively inactive for the hydrogenolysis of C–C bonds,24,25 have been reported to be effective for the hydrogenation of LA to GVL. For example, Hutchings et al.26 investigated the performance of Cu–ZrO2 catalyst for the hydrogenation of LA to GVL, and obtained over 90% of LA conversion after reaction 60 min at 200 °C and 35 bar H2. Xu et al.27 studied LA hydrogenation over Cu(30%)–WO3(10%)/ZrO2-CP-300 catalyst in ethanol and obtained the maximum GVL yield of 94% at 200 °C and 5 MPa H2 for 6 h. However, most of the copper monometallic catalysts exposed a lot of problems, such as a high copper loading and harsh reaction conditions.

Recently, bimetallic catalysts have caused widespread concern due to their unique catalytic performance. It is widely believed that the addition of another metal will enhance the catalytic activity and stability of the catalyst by changing the electronic and geometric properties of the first metal.28,29 Zhang et al.30 reported that using CuAg/Al2O3 as catalyst and THF as a solvent, LA conversion could reach 100%, and GVL selectivity was up to 99% at 180 °C and 1.4 MPa H2 for 4 h. Cai et al.31 developed 10Cu–5Ni/Al2O3 bimetallic catalyst for the transfer hydrogenation of ethyl levulinate to GVL with 2-butanol as the hydrogen donor, and obtained a 97% yield of GVL in 12 h at 150 °C. Yanase et al.32 tested bimetallic Cu–Co/Al2O3 catalyst for gas-phase hydrogenation of LA to GVL and obtained a GVL productivity of 5.46 kgGVL kgcatalyst−1 h−1 with a GVL selectivity higher than 99% at 250 °C for 24 h.

In this study, we report the Cu–Re/TiO2 bimetallic catalyst for the liquid phase hydrogenation of LA to GVL. The choice of metal Re as the second component is mainly based on the following considerations. Firstly, ReOx as well as TiO2 has many oxygen vacancies, which facilitates the adsorption of oxygen-containing functional groups, such as –OH and C Created by potrace 1.16, written by Peter Selinger 2001-2019 O,33,34 facilitating the catalytic conversion of LA. Secondly, Re oxophilic metal oxide can be partially reduced to a metallic state in a reducing atmosphere, and Re0 can serve as a second metal component to form a bimetal or alloy with another hydrogenation-active metal and provide a synergistic effect, which is beneficial to improve the hydrogenation catalytic performance and stability of the catalyst.35–37 Our previous work showed that the bimetallic catalyst Pt–Re exhibited high performance for hydrogenation of cinnamaldehyde to cinnamyl alcohol.38 And our recent study showed that bimetallic catalyst Fe–Re/TiO2 exhibited superior catalytic performance for LA hydrogenation to GVL compared to monometallic Fe and Re catalysts at similar metal content. Under optimized conditions, nearly full conversion of LA with a 95% yield of GVL could be achieved at 180 °C in water at a H2 pressure of 40 bar.39

Here, Cu–Re bimetallic catalysts supported on TiO2 with different Cu/Re molar ratios were prepared via an incipient wetness impregnation method. A structure–activity relationship was extensively discussed based on various characterization results and activity testing results. Moreover, the effect of reaction parameters on LA conversion was investigated.

2. Experimental

2.1. Materials

Levulinic acid (99.0%) was purchased from Shanghai Jingchun Reagent Co., Ltd. Cu(NO3)2·3H2O (99.99%) was purchased from Shanghai Aibi Chemical Reagent Co., Ltd, China. NH4ReO4 (99.99%) was purchased from Shanghai Macklin Biochemical Co., Ltd. 1,4-Dioxane (99.0%), methanol (99.9%) and TiO2 (99.0%) were purchased from Shanghai Aladdin Reagent Co., Ltd. All the chemicals used in this work were analytical reagents and were used without further purification.

2.2. Catalyst preparation

A series of Cu–Re/TiO2 bimetallic catalysts with different Cu : Re molar ratios were prepared by an incipient wetness impregnation method. In a typical procedure, an aqueous solution containing the required amount of Cu(NO3)2·3H2O and NH4ReO4 was added to the support TiO2 in a beaker. After impregnated for 24 h, the mixture was dried at 110 °C for 10 h and finally reduced at 500 °C in a tubular furnace under hydrogen flow for 3 h to obtain the target catalyst, which was denoted as Cu–Re(x : y)/TiO2, where x : y means the molar ratio of Cu to Re. The molar ratio of Cu to Re was varied from (3 : 1) to (1 : 1) by changing the Re content and using a fixed amount of Cu (2.0 wt%), in order to investigate the influence of Re content on the property of the Cu–Re/TiO2. Two monometallic catalysts 2.0 wt% Cu/TiO2 and 5.8 wt% Re/TiO2 were prepared by using the same method for comparison.

2.3. Catalyst characterization

The specific surface area was determined by N2 adsorption at −196 °C with the Brunauer–Emmett–Teller (BET) method using an ASAP 2010 instrument (Micromeritics Instrument Co.). The pore size distribution and pore volume were measured at −196 °C by using Barrett–Joyner–Halenda (BJH) analysis from the desorption branch of the N2 adsorption–desorption isotherms. Prior to N2 physisorption, the samples were degassed under vacuum at 250 °C for 10 h.

Transmission electron microscopy (TEM) images were obtained using a Tecnai G2 F30 S-Twin instrument (Philips-FEI Co., The Netherlands). Samples were prepared by dispersing the reduced catalyst powder in ethanol under ultrasound for 15–20 min and then dropping the suspension onto a copper grid coated with carbon film. The particle size distribution of the metal nanoparticles in each sample was determined from the corresponding TEM image by measuring the sizes of more than 100 particles.

H2 temperature-programmed reduction (H2-TPR) of the samples was performed on a Chemisorb FINESORB-3010 instrument. The dried catalyst samples were reduced at 10 °C min−1 under a gaseous mixture of 10 vol% hydrogen in nitrogen (gas flow rate: 60 mL min−1). Hydrogen consumption was monitored on a thermal conductivity detector (TCD).

X-ray photoelectron spectroscopy (XPS) spectra were obtained using an Escalab Mark II X-ray spectrometer (VG Co., United Kingdom) equipped with a magnesium anode (Mg Kα = 1253.6 eV). Energy corrections were performed using a 1s peak of the pollutant carbon at 284.6 eV. The sample was prepared by pressing the catalyst powder onto the surface with silver sol–gel.

2.4. Reaction procedure

The hydrogenation of LA to GVL was performed in a 25 mL stainless-steel autoclave equipped with magnetic stirring. In a typical reaction, 0.5 g of LA, 50 mg of catalyst and 10 mL of solvent 1,4-dioxane were introduced into the reactor. Then the reactor was sealed, purged with H2 five times, and pressurized with H2 to the required pressure. The autoclave was then heated to the required temperature and kept at this temperature for the required time under the continuous stirring speed of 1000 rpm to eliminate external diffusion. After the reaction, the autoclave was cooled to room temperature, the residual hydrogen gas was released and the reaction mixture was centrifuged. The solid catalyst was washed with 1,4-dioxane for the next cycle, and the separated liquid reaction solution was quantitatively analyzed with an Agilent 7890A gas chromatography equipped with an HP-5 capillary column (30.0 m × 0.32 mm × 0.25 μm) and a flame ionization detector (FID) using n-dodecane as an internal standard. The confirmation of the liquid products was performed on an Agilent 6890 GC system coupled to a mass spectrometer equipped with an Agilent 5973 quadrupole mass analyzer. The potential Cu and Re leach was detected by inductively coupled plasma-mass spectroscopy (ICP-MS, PerkinElmer Elan DRC-e).

3. Results and discussion

3.1. Catalytic performance of Cu–Re/TiO2 catalysts

To ascertain the effect of Re on the performance of Cu/TiO2 catalyst, a series of Cu–Re/TiO2 catalysts with different Cu : Re molar ratios were prepared and tested for hydrogenation of LA into GVL in a batch reactor in 1,4-dioxane solvent at 180 °C and 4.0 MPa H2 for 3 h, and the results are shown in Fig. 1. Monometallic 2 wt% Cu/TiO2 showed almost no activity for the reaction, over which the conversion of LA and the selectivity to GVL was only 0.7% and 2.4%, respectively. Although monometallic 5.8 wt% Re/TiO2 showed good selectivity toward GVL (98.7%), its activity was low, with a LA conversion of 68.4%. It can be seen that the addition of Re remarkably improved the catalytic performance of the Cu-based catalysts for LA hydrogenation, and the performance of the Cu–Re/TiO2 bimetallic catalysts increased with the increase in Re : Cu molar ratio. It was noteworthy that the Cu–Re(1 : 1)/TiO2 catalyst exhibited the highest activity and selectivity to GVL, giving a GVL yield as high as 97.5% at a LA conversion of 98.9%.

Fig. 1. Hydrogenation of LA to GVL over Cu–Re/TiO2 catalysts with different Cu : Re molar ratios. Reaction conditions: 0.5 g LA, 50 mg catalyst, 10 mL 1,4-dioxane, 4.0 MPa H2, 180 °C, 3 h, and 1000 rpm.

Fig. 1

Open in a new tab

3.2. Characterization of Cu–Re/TiO2 catalysts

N2 adsorption/desorption isotherms of support TiO2, monometallic Cu/TiO2 and Re/TiO2, and Cu–Re/TiO2 bimetallic catalysts are presented in Fig. 2, and the relative texture parameters (specific surface areas (SBET), pore volume and average pore diameter) of these samples are listed in Table 1. All the samples shown in Fig. 2 exhibited type IV isotherms, a typical characteristic for mesoporous materials.40 The SBET of TiO2 was kept no obvious change after supporting metal elements, while the pore volume and average pore diameter increased significantly, indicating a strong influence of the metal ions on TiO2 textural properties.41

Fig. 2. N2 adsorption–desorption isotherms of TiO2, Cu/TiO2, Re/TiO2 and Cu–Re/TiO2 catalysts.

Fig. 2

Open in a new tab

Structural properties of TiO2, Cu/TiO2, Re/TiO2 and Cu–Re/TiO2 catalysts.

Catalyst S BET a (m2 g−1) V p b (cm3 g−1) D p b (nm)
TiO2 53 0.15 11.3
Cu/TiO2 52 0.33 25.2
Cu–Re(3 : 1)/TiO2 60 0.39 26.0
Cu–Re(2 : 1)/TiO2 59 0.36 25.6
Cu–Re(1 : 1)/TiO2 60 0.32 25.6
Re/TiO2 61 0.33 26.4
Open in a new tab
a

The specific surface area was calculated by using the BET method.

b

The pore size and pore volumes were derived from the adsorption branches of isotherms by using the BJH model.

Fig. 3 shows the H2-TPR profiles of monometallic Cu/TiO2 and Re/TiO2, and bimetallic Cu–Re/TiO2 catalysts dried at 110 °C. In monometallic Cu/TiO2, two peaks occurred at 225 °C and 255 °C, which were likely attributed to the reduction of highly dispersed CuO species in intimate contact with TiO2 and the reduction of the oxide clusters with a structure similar to CuO, respectively.42 In the case of monometallic Re/TiO2, Re species reduced between 220 and 350 °C with a peak maximum at 288 °C, in agreement with the literature.43 On bimetallic Cu–Re(3 : 1)/TiO2 and Cu–Re(2 : 1)/TiO2 catalysts, two peaks were observed between 210 and 261 °C, and the peaks moved towards low temperature compared with the two monometallic catalysts Cu/TiO2 and Re/TiO2, which indicates that the addition of Re into Cu/TiO2 catalyst is of benefit to the reduction of metal oxide species. It is interesting to note that Cu–Re(1 : 1)/TiO2 bimetallic catalyst displayed a main broad peak at 289 °C and two additional ones with low intensity. The main peak shifted to higher temperature compared with monometallic catalyst Cu/TiO2, likely corresponding to monometallic Re-containing sample, indicating that there was a strong interaction between Cu and Re on this sample and that most of Re atoms were distributed in the periphery of unreduced Cu atoms throughout the catalyst.44 Furthermore, the reduction bands of Cu–Re(1 : 1)/TiO2 catalyst were changed to the symmetrical shape compared to those of other samples, which can be induced by a uniform reduction process caused by the homogeneity of metal particle size.44 Combined with the activity testing results of the catalysts as mentioned above, the improvement in the catalytic activity of the Cu–Re(1 : 1)/TiO2 catalyst was probably attributed to the strong interaction between Cu and Re.

Fig. 3. H2-TPR profiles of Cu/TiO2, Re/TiO2 and Cu–Re/TiO2 catalysts.

Fig. 3

Open in a new tab

Fig. 4 displays the TEM images of the reduced Cu/TiO2 and Cu–Re/TiO2 catalysts. In the TEM image of monometallic Cu/TiO2 catalyst (Fig. 4(a)), only a few severely agglomerated Cu nanoparticles with a large average size (about 1.6 nm) were observed, which reduced the activity and selectivity of the catalyst significantly. For the three Cu–Re/TiO2 bimetallic catalysts (Fig. 4(b)–(d)), metal particles were smaller, with more narrow particle size distributions than Cu/TiO2, indicating that metal particles on Cu–Re bimetallic catalysts were uniformly distributed. In particular, Cu–Re(1 : 1)/TiO2 catalyst showed the largest metal dispersion and the smallest average metal particle size (0.69 nm). As shown in Fig. 4(d), the fringe spacing of Cu–Re(1 : 1) (0.207 nm) is between those of Cu(110) (0.200 nm) and Re(101) (0.211 nm),45,46 indicating that a Cu–Re alloy was formed in the reduced Cu–Re(1 : 1)/TiO2 catalyst and this was responsible for strong interaction between metallic Cu and Re species. The result is in good agreement with the TPR results.

Fig. 4. TEM images of (a) Cu/TiO2, (b) Cu–Re(3 : 1)/TiO2, (c) Cu–Re(2 : 1)/TiO2 and (d) Cu–Re(1 : 1)/TiO2 catalysts.

Fig. 4

Open in a new tab

Fig. 5 shows the XPS spectra for Cu 2p (Fig. 5(a)) and Re 4f (Fig. 5(b)) levels of the reduced Cu/TiO2, Re/TiO2 and Cu–Re(1 : 1)/TiO2 catalysts, and the corresponding binding energies are listed in Table 2. The XPS data for Cu 2p on both Cu/TiO2 and Cu–Re(1 : 1)/TiO2 catalysts reveal that the Cu species is essentially metallic Cu0.47 XPS analysis for Re 4f displays that Re is present in Re4+, Re6+ and Re7+ states in the case of monometallic Re/TiO2,48 and in Re0, Re4+ and Re7+ states in the case of bimetallic Cu–Re(1 : 1)/TiO2,44 indicating that the reduction of Re species is not complete, in agreement with the literature.43,44 Compared to the corresponding monometallic catalysts, the binding energy for the Cu 2p3/2 descends to higher values by ca. 0.3 eV, while the binding energy of ReO2 for Re 4f7/2 shifts to lower values by ca. 0.2 eV, indicating a strong interaction may exist between Cu and Re species,49 per the TPR and TEM results.

Fig. 5. XPS spectra of Cu/TiO2, Re/TiO2 and Cu–Re(1 : 1)/TiO2 catalysts.

Fig. 5

Open in a new tab

XPS results of Cu/TiO2, Re/TiO2 and Cu–Re(1 : 1)/TiO2 catalysts.

Catalyst Cu 2p3/2 (2p1/2) (BE/eV) Re 4f7/2 (4f5/2) (BE/eV)
Cu0 Re0 ReO2 ReO3 Re2O7
Cu/TiO2 931.7(951.6) — — — —
Cu–Re(1 : 1)/TiO2 932.0(951.9) 40.3(43.0) 42.0(44.2) — 45.8(48.2)
Re/TiO2 — — 42.2(44.6) 44.3(48.7) 46.2(48.4)
Open in a new tab

3.3. Effects of various reaction conditions on hydrogenation of LA

The effect of the reaction temperature in the range of 140–200 °C on the conversion of LA and the selectivity to GVL over Cu–Re(1 : 1)/TiO2 catalyst was investigated, and the results are shown in Fig. 6. It can be seen that the conversion of LA increased from 22.0% at 140 °C to 53.4% at 160 °C, and the GVL selectivity increased from 78.4% to 89.9%. With the increase in the temperature to 180 °C, GVL selectivity increased to 98.6% with a LA conversion of 98.9%. Further increasing reaction temperature to 200 °C, both LA conversion and GVL selectivity were up to 100%. Considering energy-saving and GVL yield, 180 °C was chosen as the reaction temperature in the following study.

Fig. 6. Effect of reaction temperature on hydrogenation of LA to GVL over Cu–Re(1 : 1)/TiO2 catalyst. Reaction conditions: 0.5 g LA, 50 mg catalyst, 10 mL 1,4-dioxane, 4.0 MPa H2, 3 h, and 1000 rpm.

Fig. 6

Open in a new tab

Fig. 7 compares LA hydrogenation results by reaction time over Cu/TiO2, Re/TiO2 and Cu–Re(1 : 1)/TiO2 catalysts. The bimetallic Cu–Re(1 : 1)/TiO2 catalyst exhibited the highest performance and produced a GVL yield of 97.5% after 3 h of reaction time. Extending the reaction time to 4 h, a GVL yield of 100% was achieved. In contrast, the monometallic Cu/TiO2 and Re/TiO2 catalysts showed a significantly lower activity, achieving a maximum GVL yield of 26.7% and 84.6%, respectively, after 4 h of reaction time. Combined with the characterization results of the catalysts, the excellent performance of Cu–Re(1 : 1)/TiO2 catalyst for LA hydrogenation to GVL was mainly attributed to the following three aspects. Firstly, Cu–Re miscible phase was formed in the Cu–Re(1 : 1)/TiO2 catalyst during the reduction process, facilitating the synergistic interaction between copper and rhenium. Secondly, Cu–Re nanoparticles were highly dispersed on the TiO2 support with uniform and small size (0.69 nm), which increased the active sites on the surface of the catalyst, thereby improving the catalytic activity. Thirdly, the addition of Re was beneficial to the reduction of CuO to Cu0, and inhibiting the oxidation of metal Cu0. And the presence of ReOx species in the catalyst facilitated the adsorption of LA and the transformation of a reaction intermediate 4-hydroxyvaleric acid to GVL.33

Fig. 7. Production of GVL as a function of reaction time during hydrogenation of LA over Cu/TiO2, Re/TiO2 and Cu–Re(1 : 1)/TiO2 catalysts. Reaction conditions: 0.5 g LA, 50 mg catalyst, 10 mL 1,4-dioxane, 4.0 MPa H2, and 1000 rpm.

Fig. 7

Open in a new tab

Table 3 shows the effect of solvent on the performance of Cu–Re(1 : 1)/TiO2 catalyst for hydrogenation of LA to GVL. When methanol was used as a solvent, GVL yield was only 88.1%, and the reaction intermediate 4-hydroxyvaleric acid was the only by-product (11.9%). In the solvent-free conditions, the conversion of LA and the selectivity to GVL reached 97.3% and 97.6%, respectively. A higher yield of GVL (97.5%) was achieved by using 1,4-dioxane as solvent. H2O as solvent gave the highest yield of GVL. However, the stability of Cu–Re(1 : 1)/TiO2 catalyst in H2O was poor, and the catalytic activity of the recovered catalyst dropped down substantially, giving a lower yield of GVL (less than 50%) than the first cycle (100%).

Hydrogenation of LA to GVL in various solvents over Cu–Re(1 : 1)/TiO2 catalysta.

Solvent Conversion (%) Selectivity (%)
GVL HVAb
1,4-Dioxane 98.9 98.6 1.1
H2O >99.9 >99.9 0
Methanol 100 88.1 11.9
No solvent 97.3 97.6 2.4
Open in a new tab
a

Reaction conditions: 0.5 g LA, 50 mg catalyst, 10 mL solvent, 4.0 MPa H2, 180 °C, 3 h, and 1000 rpm.

b

HVA: 4-hydroxyvaleric acid.

3.4. Recyclability of bimetallic Cu–Re(1 : 1)/TiO2 catalyst

The recyclability of the bimetallic Cu–Re(1 : 1)/TiO2 catalyst in the hydrogenation of LA into GVL was examined by performing six consecutive catalytic runs. At each cycle, after hydrogenation reaction in 1,4-dioxane solvent at 180 °C and 4.0 MPa H2 for 3 h, the catalyst was centrifuged, washed with 1,4-dioxane, and reused. As shown in Fig. 8, the Cu–Re(1 : 1)/TiO2 catalyst exhibited excellent stability. After being recycled six times, Cu–Re(1 : 1)/TiO2 still kept high activity and selectivity, achieving a GVL yield of 90.3%. Analysis of the reaction solution after the sixth run revealed no detectable leach of Cu and Re, which confirmed the high stability of the catalyst in 1,4-dioxane. The comparison with other Cu-containing catalysts (Table S1†) indicated that Cu–Re(1 : 1)/TiO2 developed in this work is a good catalyst for LA hydrogenation.

Fig. 8. Recyclability of Cu–Re(1 : 1)/TiO2 catalyst for hydrogenation of LA to GVL. Reaction conditions: 0.5 g LA, 50 mg catalyst, 10 mL 1,4-dioxane, 4.0 MPa H2, 180 °C, 3 h, and 1000 rpm.

Fig. 8

Open in a new tab

4. Conclusions

Hydrogenation of levulinic acid (LA) to γ-valerolactone (GVL) is one of the most promising reactions in the fields of biomass conversion into high value-added chemicals and biofuels. Cu-based catalysts are active non-noble catalysts for the hydrogenation of LA to GVL. However, hydrogenation of LA over monometallic Cu catalysts generally needs to be carried out at harsh reaction conditions due to the low activity of the catalysts. To obtain an efficient Cu-based catalyst, a series of Cu–Re/TiO2 bimetallic catalysts prepared by an incipient wetness impregnation method were tested for the liquid phase hydrogenation of LA. The introduction of a suitable amount of Re into Cu/TiO2 was demonstrated to remarkably improve the catalytic performance for the hydrogenation of LA to GVL. The Cu–Re/TiO2 catalyst with a 1 : 1 molar ratio of Cu to Re achieved as high as 100% yield of GVL at 180 °C and 4.0 MPa H2 for 4 h. The catalyst could be reused at least 6 times with slight activity loss. TEM results showed that the addition of Re decreased the average size of the metal nanoparticles, improved the dispersion of Cu, and formed Cu–Re alloy. H2-TPR results showed that the presence of Re promoted the reduction of Cu and there is a strong interaction between Cu and Re. XPS results evidenced the co-presence of the metallic Re and ReOx, and revealed that the addition of Re inhibited the oxidation of metallic Cu. The co-presence of Cu–Re bimetal and ReOx species in the samples, and the improved Cu reducibility and dispersion were predominantly responsible for the good catalytic performance of Cu–Re/TiO2 catalysts.

Conflicts of interest

There are no conflicts to declare.

Supplementary Material

RA-012-D1RA05804E-s001

Acknowledgments

This research was supported by the National Natural Science Foundation of China (21476211 and 21878269) and the Zhejiang Provincial Natural Science Foundation of China (LY18B060016).

†

Electronic supplementary information (ESI) available. See DOI: 10.1039/d1ra05804e

References

  1. Gallezot P. Conversion of biomass to selected chemical products. Chem. Soc. Rev. 2012;41(4):1538–1558. doi: 10.1039/C1CS15147A. [DOI] [PubMed] [Google Scholar]
  2. Mika L. T. Cséfalvay E. Németh Á. Catalytic conversion of carbohydrates to initial platform chemicals: chemistry and sustainability. Chem. Rev. 2018;118(2):505–613. doi: 10.1021/acs.chemrev.7b00395. [DOI] [PubMed] [Google Scholar]
  3. Besson M. Gallezot P. Pinel C. Conversion of biomass into chemicals over metal catalysts. Chem. Rev. 2014;114(3):1827–1870. doi: 10.1021/cr4002269. [DOI] [PubMed] [Google Scholar]
  4. Alonso D. M. Wettstein S. G. Dumesic J. A. Gamma-valerolactone, a sustainable platform molecule derived from lignocellulosic biomass. Green Chem. 2013;15(3):584–595. doi: 10.1039/C3GC37065H. [DOI] [Google Scholar]
  5. Jain A. B. Vaidya P. D. Kinetics of hydrogenation of furfuryl alcohol and γ-valerolactone over Ru/C catalyst. Energy Fuels. 2020;34(8):9963–9970. doi: 10.1021/acs.energyfuels.0c01598. [DOI] [Google Scholar]
  6. Zhao Y. Fu Y. Guo Q. X. Production of aromatic hydrocarbons through catalytic pyrolysis of γ-valerolactone from biomass. Bioresour. Technol. 2012;114:740–744. doi: 10.1016/j.biortech.2012.03.057. [DOI] [PubMed] [Google Scholar]
  7. Wang G. H. Liu X. Q. Yang B. Si C. L. Parvez A. M. Jang J. Ni Y. H. Using green γ-valerolactone/water solvent to decrease lignin heterogeneity by gradient precipitation. ACS Sustainable Chem. Eng. 2019;7(11):10112–10120. doi: 10.1021/acssuschemeng.9b01641. [DOI] [Google Scholar]
  8. Omoruyi U. Page S. Hallett J. Miller P. W. Homogeneous catalyzed reactions of levulinic acid: To γ-valerolactone and beyond. ChemSusChem. 2016;9(16):2037–2047. doi: 10.1002/cssc.201600517. [DOI] [PubMed] [Google Scholar]
  9. Yu Z. H. Lu X. B. Liu C. Han Y. W. Ji N. Synthesis of γ-valerolactone from different biomass-derived feedstocks: Recent advances on reaction mechanisms and catalytic systems. Renewable Sustainable Energy Rev. 2019;112:140–157. doi: 10.1016/j.rser.2019.05.039. [DOI] [Google Scholar]
  10. Weng R. G. Yu Z. H. Xiong J. Lu X. B. Effects of water in the heterogeneous catalytic valorization of levulinic acid into γ-valerolactone and its derivatives. Green Chem. 2020;22(10):3013–3027. doi: 10.1039/D0GC01082K. [DOI] [Google Scholar]
  11. Wettstein S. G. Bond J. Q. Alonso D. M. Pham H. N. Datye A. K. Dumesic J. A. RuSn bimetallic catalysts for selective hydrogenation of levulinic acid to γ-valerolactone. Appl. Catal., B. 2012;117–118:321–329. doi: 10.1016/j.apcatb.2012.01.033. [DOI] [Google Scholar]
  12. Manzer L. E. Catalytic synthesis of α-methylene-γ-valerolactone: a biomass-derived acrylic monomer. Appl. Catal., A. 2004;272(1–2):249–256. doi: 10.1016/j.apcata.2004.05.048. [DOI] [Google Scholar]
  13. Feng J. Li M. Zhong Y. H. Xu Y. L. Meng X. J. Zhao Z. W. Feng C. G. Hydrogenation of levulinic acid to γ-valerolactone over Pd@UiO-66-NH2 with high metal dispersion and excellent reusability. Microporous Mesoporous Mater. 2020;294:109858. doi: 10.1016/j.micromeso.2019.109858. [DOI] [Google Scholar]
  14. Nemanashi M. Noh J. H. Meijboom R. Hydrogenation of biomass-derived levulinic acid to γ-valerolactone catalyzed by mesoporous supported dendrimer-derived Ru and Pt catalysts: An alternative method for the production of renewable biofuels. Appl. Catal., A. 2018;550:77–89. doi: 10.1016/j.apcata.2017.10.015. [DOI] [Google Scholar]
  15. Zhu S. H. Xue Y. F. Guo J. Cen Y. L. Wang J. G. Fan W. B. Integrated conversion of hemicellulose and furfural into γ-valerolactone over Au/ZrO2 catalyst combined with ZSM-5. ACS Catal. 2016;6(3):2035–2042. doi: 10.1021/acscatal.5b02882. [DOI] [Google Scholar]
  16. Wang J. R. Wang Y. Y. Tong X. L. Wang Y. W. Jin G. Q. Guo X. Y. Highly active Ir/SiC catalyst for aqueous hydrogenation of levulinic acid to γ-valerolactone. Catal. Commun. 2020;139:105971. doi: 10.1016/j.catcom.2020.105971. [DOI] [Google Scholar]
  17. Abdelrahman O. A. Heyden A. Bond J. Q. Analysis of kinetics and reaction pathways in the aqueous-phase hydrogenation of levulinic acid to form γ-valerolactone over Ru/C. ACS Catal. 2014;4(4):1171–1181. doi: 10.1021/cs401177p. [DOI] [Google Scholar]
  18. Tan J. J. Cui J. L. Ding G. Q. Deng T. S. Zhu Y. L. Li Y. W. Efficient aqueous hydrogenation of levulinic acid to γ-valerolactone over a highly active and stable ruthenium catalyst. Catal. Sci. Technol. 2016;6(5):1469–1475. doi: 10.1039/C5CY01374G. [DOI] [Google Scholar]
  19. Mamun O. Saleheen M. Bond J. Q. Heyden A. Investigation of solvent effects in the hydrodeoxygenation of levulinic acid to c-valerolactone over Ru catalysts. J. Catal. 2019;379(C):164–179. doi: 10.1016/j.jcat.2019.09.026. [DOI] [Google Scholar]
  20. Gao X. Q. Zhu S. H. Dong M. Wang J. G. Fan W. B. Ru nanoparticles deposited on ultrathin TiO2 nanosheets as highly active catalyst for levulinic acid hydrogenation to γ-valerolactone. Appl. Catal., B. 2019;259:118076. doi: 10.1016/j.apcatb.2019.118076. [DOI] [Google Scholar]
  21. Hommes A. ter Horst A. J. Koeslag M. Heeres H. J. Yue J. Experimental and modeling studies on the Ru/C catalyzed levulinic acid hydrogenation to γ-valerolactone in packed bed microreactors. Chem. Eng. J. 2020;399:125750. doi: 10.1016/j.cej.2020.125750. [DOI] [Google Scholar]
  22. Wei Z. J. Lou J. T. Su C. M. Guo D. C. Liu Y. X. Deng S. G. An efficient and reusable embedded Ru catalyst for the hydrogenolysis of levulinic acid to γ-valerolactone. ChemSusChem. 2017;10(8):1720–1732. doi: 10.1002/cssc.201601769. [DOI] [PubMed] [Google Scholar]
  23. Dutta S. Yu I. K. M. Tsang D. C. W. Ng Y. H. Ok Y. S. Sherwood J. Clark J. H. Green synthesis of gamma-valerolactone (GVL) through hydrogenation of biomass-derived levulinic acid using non-noble metal catalysts: A critical review. Chem. Eng. J. 2019;372:992–1006. doi: 10.1016/j.cej.2019.04.199. [DOI] [Google Scholar]
  24. He Z. Lin H. Q. He P. Yuan Y. Z. Effect of boric oxide doping on the stability and activity of a Cu-SiO2 catalyst for vapor-phase hydrogenation of dimethyl oxalate to ethylene glycol. J. Catal. 2011;277(1):54–63. doi: 10.1016/j.jcat.2010.10.010. [DOI] [Google Scholar]
  25. Gong J. L. Yue H. R. Zhao Y. J. Zhao S. Zhao L. Lv J. Wang S. P. Ma X. B. Synthesis of ethanol via syngas on Cu/SiO2 Catalysts with Balanced Cu0-Cu+ Sites. J. Am. Chem. Soc. 2012;134(34):13922–13925. doi: 10.1021/ja3034153. [DOI] [PubMed] [Google Scholar]
  26. Orlowski I. Douthwaite M. Iqbal S. Hayward J. S. Davies T. E. Bartley J. K. Miedziak P. J. Hirayama J. Morgan D. J. Willock D. J. Hutchings G. J. The hydrogenation of levulinic acid to γ-valerolactone over Cu-ZrO2 catalysts prepared by a pH-gradient methodology. J. Energy Chem. 2019;36:15–24. doi: 10.1016/j.jechem.2019.01.015. [DOI] [Google Scholar]
  27. Xu Q. Li X. L. Pan T. Yu C. G. Deng J. Guo Q. X. Fu Y. Supported copper catalysts for highly efficient hydrogenation of biomass-derived levulinic acid and γ-valerolactone. Green Chem. 2016;18(5):1287–1294. doi: 10.1039/C5GC01454A. [DOI] [Google Scholar]
  28. Kelly T. G. Chen J. G. Metal overlayer on metal carbide substrate: unique bimetallic properties for catalysis and electrocatalysis. Chem. Soc. Rev. 2012;41(24):8021–8034. doi: 10.1039/C2CS35165J. [DOI] [PubMed] [Google Scholar]
  29. Yu W. T. Porosoff M. D. Chen J. G. G. Review of Pt-based bimetallic catalysis: from model surfaces to supported catalysts. Chem. Rev. 2012;112(11):5780–5817. doi: 10.1021/cr300096b. [DOI] [PubMed] [Google Scholar]
  30. Zhang L. Mao J. B. Li S. M. Yin J. M. Sun X. D. Guo X. W. Song C. S. Zhou J. X. Hydrogenation of levulinic acid into gamma-valerolactone over in situ reduced CuAg bimetallic catalyst: Strategy and mechanism of preventing Cu leaching. Appl. Catal., B. 2018;232:1–10. doi: 10.1016/j.apcatb.2018.03.033. [DOI] [Google Scholar]
  31. Cai B. Zhou X. C. Miao Y. C. Luo J. Y. Pan H. Huang Y. B. Enhanced catalytic transfer hydrogenation of ethyl levulinate to γ-valerolactone over a robust Cu-Ni bimetallic catalyst. ACS Sustainable Chem. Eng. 2017;5(2):1322–1331. doi: 10.1021/acssuschemeng.6b01677. [DOI] [Google Scholar]
  32. Yanase D. Yoshida R. Kanazawa S. Yamada Y. Sato S. Efficient formation of γ-valerolactone in the vapor-phase hydrogenation of levulinic acid over Cu-Co/alumina catalyst. Catal. Commun. 2020;139:105967. doi: 10.1016/j.catcom.2020.105967. [DOI] [Google Scholar]
  33. Takeda Y. Nakagawa Y. Tomishige K. Selective hydrogenation of higher saturated carboxylic acids to alcohols using a ReOx-Pd/SiO2 catalyst. Catal. Sci. Technol. 2012;2(11):2221–2223. doi: 10.1039/C2CY20302B. [DOI] [Google Scholar]
  34. Detwiler M. D. Majumdar P. Gu X. K. Delgass W. N. Ribeiro F. H. Greeley J. Zemlyano D. Y. Characterization and theory of Re films on Pt(111) grown by UHV-CVD. Surf. Sci. 2015;640:2–9. doi: 10.1016/j.susc.2015.05.015. [DOI] [Google Scholar]
  35. Tamura M. Tokonami K. Nakagawa Y. Tomishige K. Selective hydrogenation of crotonaldehyde to crotyl alcohol over metal oxide modified Ir catalysts and mechanistic insight. ACS Catal. 2016;6(6):3600–3609. doi: 10.1021/acscatal.6b00400. [DOI] [Google Scholar]
  36. Keels J. M. Chen X. Karakalos S. Liang C. H. Monnier J. R. Regalbuto J. R. Aqueous-phase hydrogenation of succinic acid using bimetallic Ir-Re/C catalysts prepared by strong electrostatic adsorption. ACS Catal. 2018;8(7):6486–6494. doi: 10.1021/acscatal.8b01006. [DOI] [Google Scholar]
  37. Yang F. F. Liu D. Wang H. Liu X. Han J. Y. Ge Q. F. Zhu X. L. Geometric and electronic effects of bimetallic Ni-Re catalysts for selective deoxygenation of m-cresol to toluene. J. Catal. 2017;349:84–97. doi: 10.1016/j.jcat.2017.01.001. [DOI] [Google Scholar]
  38. Wei Z. J. Zhu X. M. Liu X. S. Xu H. Q. Li X. H. Hou Y. X. Liu Y. X. Pt-Re/rGO bimetallic catalyst for highly selective hydrogenation of cinnamaldehyde to cinnamylalcohol. Chin. J. Chem. Eng. 2019;27(2):369–378. doi: 10.1016/j.cjche.2018.04.022. [DOI] [Google Scholar]
  39. Huang X. M. Liu K. T. Vrijburg W. L. Ouyang X. H. Dugulan A. I. Liu Y. X. Verhoeven M. W. G. M. T. Kosinov N. A. Pidko E. A. Hensen E. J. M. Hydrogenation of levulinic acid to γ-valerolactone over Fe-Re/TiO2 catalysts. Appl. Catal., B. 2020;278:119314. doi: 10.1016/j.apcatb.2020.119314. [DOI] [Google Scholar]
  40. Sing K. Everett D. Haul R. Moscou L. Pierotti R. Rouquerol J. Siemieniewsks T. Reporting physisorption data for gas/solid systems with special reference to the determination of surface area and porosity. Pure Appl. Chem. 1985;57(4):603–619. [Google Scholar]
  41. Deshmane V. G. Owen S. L. Abrokwah R. Y. Kuila D. Mesoporous nanocrystalline TiO2 supported metal (Cu, Co, Ni, Pd, Zn, and Sn) catalysts: Effect of metal-support interactions on steam reforming of methanol. J. Mol. Catal. A: Chem. 2015;408:202–213. doi: 10.1016/j.molcata.2015.07.023. [DOI] [Google Scholar]
  42. Jiang X. Y. Ding G. H. Lou L. P. Chen Y. X. Zheng X. M. Catalytic activities of CuO/TiO2 and CuO-ZrO2/TiO2 in NO + CO reaction. J. Mol. Catal. A: Chem. 2004;218(2):187–195. doi: 10.1016/j.molcata.2004.02.020. [DOI] [Google Scholar]
  43. Tapin B. Epron F. Especel C. Ly B. K. Pinel C. Besson M. Influence of the Re introduction method onto Pd/TiO2 catalysts for the selective hydrogenation of succinic acid in aqueous-phase. Catal. Today. 2014;235:127–133. doi: 10.1016/j.cattod.2014.02.018. [DOI] [Google Scholar]
  44. Kang K. H. Hong U. G. Bang Y. Choi J. H. Kim J. K. Lee J. K. Han S. J. Song I. K. Hydrogenation of succinic acid to 1,4-butanediol over Re-Ru bimetallic catalysts supported on mesoporous carbon. Appl. Catal., A. 2015;490:153–162. doi: 10.1016/j.apcata.2014.11.029. [DOI] [Google Scholar]
  45. Rather R. A. Singh S. Pal B. A Cu+1/Cu0-TiO2 mesoporous nanocomposite exhibits improved H2 production from H2O under direct solar irradiation. J. Catal. 2017;346:1–9. doi: 10.1016/j.jcat.2016.11.021. [DOI] [Google Scholar]
  46. Shao Z. F. Li C. Di X. Xiao Z. H. Liang C. H. Aqueous-phase hydrogenation of succinic acid to γ-butyrolactone and tetrahydrofuran over Pd/C, Re/C and Pd-Re/C catalysts. Ind. Eng. Chem. Res. 2014;53(23):9638–9645. doi: 10.1021/ie5006405. [DOI] [Google Scholar]
  47. Shi R. J. Wang F. Tana Li Y. Huang X. M. Shen W. J. A highly efficient Cu/La2O3 catalyst for transfer dehydrogenation of primary aliphatic alcohols. Green Chem. 2010;12(1):108–113. doi: 10.1039/B919807P. [DOI] [Google Scholar]
  48. Suknev A. Zaikovskii V. Kaichev V. Paukshtis E. Sadovskaya E. Bal'zhinimaev B. The nature of active sites in Pt-ReOX/TiO2 catalysts for selective hydrogenation of carboxylic acids to alcohols. J. Energy Chem. 2015;24(5):646–654. doi: 10.1016/j.jechem.2015.09.003. [DOI] [Google Scholar]
  49. Hong E. Bang S. Cho J. H. Jung K. D. Shin C. H. Reductive amination of isopropanol to monoisopropylamine over Ni-Fe/γAl2O3 catalysts: Synergetic effect of Ni-Fe alloy formation. Appl. Catal., A. 2017;542:146–153. doi: 10.1016/j.apcata.2017.05.003. [DOI] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Supplementary Materials

RA-012-D1RA05804E-s001
RA-012-D1RA05804E-s001.pdf (117.2KB, pdf)