. 2019 Nov 15;9(64):37484–37490. doi: 10.1039/c9ra07701d

Direct and sensitive detection of sulfide ions based on one-step synthesis of ionic liquid functionalized fluorescent carbon nanoribbons†

Tao Luo 1,‡, Xiaobo Wang 1,‡, Yuting Qian 2, Junjie Liu 1, Lequn Li 1, Jiyang Liu 2,✉, Jie Chen 1,✉
PMCID: PMC9075588  PMID: 35542298

Abstract

Despite widely reported fluorescence sensors for cations, direct detection of anions is nevertheless still rare. In this work, ionic liquid-functionalized fluorescent carbon nanoribbons (IL-CNRs) are one-step synthesized and serve as the fluorescent probes for direct and sensitive detection of sulfide ions (S2−). The IL-CNRs are synthesized based on electrochemical exfoliation of graphite rods in a water-IL biphasic system. The as-prepared IL-CNRs exhibit uniform structure, high crystallinity, strong blue fluorescence (absolute photoluminescence quantum yield of 11.4%), and unique selectivity towards S2−. Based on the fluorescence quenching of IL-CNRs by S2−, a fluorescence sensor is developed for direct, rapid and sensitive detection of S2− in the range of 100 nM to 1 μM and 1–300 μM with a low detection limit (LOD, 85 nM). Moreover, detection of S2− in a real sample (tap water) is also demonstrated.

Sensitive detection of sulfide ions is realized based on one-step synthesis of ionic liquid functionalized fluorescent carbon nanoribbons.graphic file with name c9ra07701d-ga.jpg

1. Introduction

Inorganic anions play a crucial role in industrial, biological and environmental fields.1 For instance, the sulfide (S2−) ion is highly toxic and harmful to human health and the ecological environment.2–4 Usually, the S2− ion is frequently distributed in natural water and wastewater samples because it is widely used in industrial processes (e.g. sulfur and sulfuric acid production, petroleum refineries, paper and pulp manufacturing, and sewage processing industries) and is also produced in biological systems (e.g. via reduction of sulfate ions by microbes or anaerobic processes of S-containing enzymes).4–6 As the S2− ion can stimulate the mucosa and has an extreme effect on the nervous system, exposure to S2− ions leads to unconsciousness and respiratory paralysis and is closely related to various diseases including Alzheimer's disease, Down's syndrome and cirrhosis of the liver.7–10 Therefore, simple, rapid and sensitive detection of S2− is of great importance.

In comparison with other technologies including gas chromatography, ion chromatography, titrimetry, colorimetry, and electrochemical method, fluorescent sensors are particularly attractive because of high sensitivity, simple operation and rapid detection.3,11–17 Recently, fluorescent sensors based on different fluorescent probes have been widely reported for detection of cations.18,19 However, only few researches focus on indirect detection of anions using fluorescent off–on strategy. For instance, Na et al. reported that Cu2+ ions caused aggregation of the GQDs and thereby quenched fluorescence.12 As the GQDs-Cu2+ aggregates can be dissociated by adding S2− ions and result in fluorescence turn-on, fluorescent detection of S2− ions could be realized. Based on the same off–on strategies, graphitic carbon nitride quantum dots-Hg2+,7 nitrogen and sulfur co-doped carbon dots (CDs)-Hg2+,6 CDs-gold nanoparticles,10 silver nanoparticles capped with CDs,9 CDs-MnO2 nanosheets,13 quinoline-Zn2+,2 calix[4]arene-Cu2+,11 and organic semiconductor polymer nanodots-Cu2+ systems8 were also applied for the detection of S2− ions. However, it still remains great challenge for improving the chemical selectivity of fluorescent probe to realize the direct detection of S2−.

Carbon-based fluorescent nanomaterials have attracted considerable interests as probes in fluorescent sensing due to good solubility, highly tunable photoluminescence properties and biocompatibility.20–24 Carbon nanoribbons (CNRs), which is thin elongated strips of sp2 bonded carbon atoms, have emerged as an exciting one-dimensional nanomaterial because of their large length-to-width ratio, abundant edge sides, high effective surface area, good flexibility, high conductivity, and tunable fluorescence.25–28 Due to the large interfacial area for π–π stacking in basal planes, CNRs exhibit potentials for the synthesis of advanced functional materials through simple modification or functionalization.

Ionic liquids (ILs) have been widely used in many fields because of a series of excellent physical and chemical properties.21,28,29 Particularly, ILs can easily combine with carbon nanomaterials due to π–π or cation–π interactions and the obtained composite materials exhibit unique characteristics.21,28–31 For instance, Wang et al. prepared highly charged CDs through one-pot pyrolysis with citric acid as carbon source and ionic liquid (1-aminopropyl-3-methylimidazolium bromide, [APMIm][Br]) as capping agent.32 Those IL-modified CDs exhibit capability of anion exchange and are able to act as fluorescent probe for direct detection of Fe(CN)63− anion. Our group also prepared IL-GQDs nanomaterial through post-modification of hydroxyl-functionalized GQDs (OH-GQDs) with 1-butyl-3-methyl imidazolium tetrafluoroborate (BMIMBF4) under ultrasonic treatment. The as-prepared IL-GQDs composite also displayed sensitive response towards Fe(CN)63−, owing to the anion exchange ability of IL.33 Inspired by these evidences, IL modified fluorescent nanocarbon materials possess great potentials for the direct detection of anions.

In this work, in contrast to anion detection based on fluorescence off–on mode, a new type of ionic liquid-functionalized fluorescent carbon nanoribbons (IL-CNRs) were prepared using one-step electrochemical method, which is able to achieve direct and sensitive detection of sulfide ions. The IL-CNRs were in situ synthesized based on electrochemical exfoliation of graphite rods in water-IL (1-butyl-3-methylimidazolium hexafluorophosphate, [BMIM]PF6) biphasic system. The obtained IL-CNRs exhibit bright fluorescence, high crystallinity and uniform structure. Based on the selective fluorescent quenching by S2−, IL-CNRs can be served as fluorescent probes for direct and sensitive detection of S2−. In comparison with the previous cation-based fluorescent sensor, we for the first time demonstrate the application of IL-CNRs for direct and selective detection of S2−.

2. Experimental

2.1. Materials and reagents

High-purity graphite rods were purchased from China National Medicines Co. Ltd (China). 1-Butyl-3-methylimidazolium hexafluorophosphate ([BMIM]PF6) (>99%), ascorbic acid (AA), and 4-(2-hydroxyethyl)-1-piperazineethanesulfonic acid (HEPES), Na2S were purchased from Sigma Aldrich. Aqueous solutions of Na+, K+, Zn2+, Mg2+, Fe3+, Ca2+, Al3+, Ni2+, Cu2+, Cd2+ were prepared from their chloride salts. Solutions of Pb2+, Ag+ and Hg2+ were prepared from their nitrate salts. Aqueous solutions of CH3COO−, HCO3−, H2PO4−, HPO42−, NO2−, S2−, S2O32− were prepared from their sodium salts. SCN−, Cl−, NO3−, Br− were prepared from their potassium salts. All chemicals were of analytical grade and used without further treatment. Aqueous solutions were prepared with ultrapure water (18.2 MΩ cm, Milli-Q, Millipore).

2.2. Characterizations

Transmission electron microscopy (TEM) micrographs were obtained using a JEM-2100F transmission electron microscope (JEOL Ltd, Japan) at accelerating voltage of 200 kV. X-ray photoelectron spectroscopy (XPS) measurements were carried out on a PHI5300 at operating voltage of 14 kV (PE Ltd., USA). The Fourier transform infrared spectra (FTIR) were conducted with a Nicolet 5700 FTIR spectrometer (Thermo Electron Scientific Instruments Corp., USA). Fluorescence spectra were measured using FL 3C-11 spectrofluorometer (Horiba Scientific, USA).

2.3. One-step electrochemical synthesis of IL-CNRs

The IL-CNRs were one-step synthesized by electrochemical exfoliation of graphite rods. A two electrodes system was adopted with graphite rods (d = 3 mm) as both anode and cathode. The electrolyte was water-IL ([BMIm][PF6]) biphasic system (V/V, 4 : 6). Graphite rods were vertically inserted into electrolyte solution at a distance of 3 cm.21 A static voltage of 8 V was applied on graphite rod for 4 h with stirring the electrolyte. Afterwards, the resultant solution was centrifuged at 12 000 rpm for 10 min to remove large particles. To acquire IL-CNRs, the supernatant solution was then filtered using a 0.22 μm membrane and dialyzed in a dialysis bag (with cut-off molecular weight of 1000 Da), which is followed by freeze-drying.

2.4. Fluorescent detection of S2−

The selectivity of IL-CNRs towards different anions and cations were evaluated by measuring the fluorescent intensity of IL-CNRs solution in presence of different cations (Na+, K+, Zn2+, Mg2+, Fe3+, Ca2+, Al3+, Ni2+, Cu2+, Cd2+) or anions (CH3COO−, HCO3−, H2PO4−, SCN−, HPO42−, S2−, Cl−, NO3−, NO2−, Br−, S2O32−).

For S2− detection, standard stock solutions of S2− (0.1 M) were prepared and further diluted stepwise to obtain different concentrations. HEPES buffer (0.1 M, pH 7.0) containing AA (25 μM) was applied as the buffer solution. After reaction of IL-CNRs with different amount of S2− for 1 min at room temperature, the fluorescent intensity of the solution was recorded with the excitation wavelength fixed at 340 nm.

The relative fluorescence ratio (F/F0) or relative fluorescence quenching ratio (F0 − F/F0) were used to evaluate the quenching of IL-CNRs caused by ion, where F0 and F represent the fluorescent intensity of IL-CNRs solution in the absence and presence of ion, respectively.

3. Results and discussion

3.1. Preparation and structure characterizations of IL-CNRs

Electrochemical synthesis has particularly attracted attention owning to the inexpensive apparatus and easy operation under ambient conditions.34–36 As illustrated in Fig. 1, ionic liquid-functionalized fluorescent carbon nanoribbons (IL-CNRs) were easily synthesized through one-step electrochemical exfoliation of graphite rods in water-IL (1-butyl-3-methylimidazolium hexafluorophosphate, [BMIM]PF6) biphasic system. Owing to high ionic conductivity and wide electrochemical potential window, ILs shows potential as electrolyte in electrochemical synthesis.17,24 In the process of electrochemical exfoliation, the colour of electrolyte turned from colourless to pale yellow and afterward turned dark brown due to rapid flaking-off of abundant IL-CNRs. In comparison with the same procedure in pure water, this phenomenon cannot be observed, indicating the importance of ILs for improved conductivity and facilitated exfoliation. The formation of IL-CNRs can be observed by transmission electron microscopy (TEM) (Fig. 2). The length and width of IL-CNRs were about 40 nm and 5 nm (Fig. 2a–c), respectively. Clear lattice lines can be seen from the high-resolution TEM (HRTEM) image (Fig. 2d), indicating good crystallinity. The lattice spaces are 0.26 nm and 0.38 nm, that are consistent with the (100) and (002) lattice of graphite, respectively.21

Fig. 1. Schematic illustration for the preparation of IL-CNRs and detection of sulfide ions.

Fig. 1

Open in a new tab

Fig. 2. TEM (a–c) and HRTEM (d) images of IL-CNRs at different magnification. The indicated data are lattice parameters of IL-CNRs.

Fig. 2

Open in a new tab

The chemical composition of the as-prepared IL-CNRs were characterized by X-ray photoelectron spectroscopy (XPS). As shown in Fig. 3a, the XPS survey spectrum of IL-CNRs contains five distinct peaks of C 1s, N 1s, O 1s, P 2p, F 1s. The appearance of N, P, F reveals the formation of IL-CNRs nanocomposites. The C–C/C Created by potrace 1.16, written by Peter Selinger 2001-2019 C (sp2 C) peak is prominent in high resolution spectrum of C 1s, suggesting the graphitic structure in CNRs (Fig. 3b). This result is consistent with the good crystallinity demonstrated in HRTEM image (Fig. 2d). The appearance of C–N in high resolution spectrum of C 1s (Fig. 3b), N–C Created by potrace 1.16, written by Peter Selinger 2001-2019 C and quaternary N in high resolution spectrum of N 1s (Fig. 3c) confirm the existence of BMIM+ in IL-CNRs. The appearance of O 1s reveals the abundant oxygen-containing groups (Fig. 3d), suggesting good solubility of the as-prepared IL-CNRs. The F 1s peak (Fig. 3e) and P 2p peak (Fig. 3f) also prove the presence of PF6− anion in IL-CNRs, indicating the hybridization between CNRs and IL. These results evidence the successful formation of [BMIM]PF6 modified CNRs in the one-step electrochemical exfoliation of graphite. Consistently, Fourier transform infrared spectrum (FTIR) of IL-CNRs (Fig. S1 in ESI†) also shows characteristic vibrations of C–H (2962, 2922, and 2857 cm−1), C Created by potrace 1.16, written by Peter Selinger 2001-2019 C and C Created by potrace 1.16, written by Peter Selinger 2001-2019 N (1552 cm−1), –OH (3457 cm−1), C Created by potrace 1.16, written by Peter Selinger 2001-2019 O (1640 cm−1), and PF6− (1578 and 1027 cm−1), that agree well with [BMIM]PF6. In comparison with IL, UV-Vis spectrum of IL-CNRs exhibits the same large peak of π–π* transition (∼240 nm) and new peak at about 326 nm that corresponds to n–π* transition (Fig. S2 in ESI†). Taken together, [BMIM]PF6 are proven to be composited with CNRs.

Fig. 3. XPS survey spectrum (a) and high resolution C1s (b), N1s (c), O1s (d), P2p (e) and F1s (f) spectra of IL-CNRs.

Fig. 3

Open in a new tab

According to the above results, we propose that the mechanism for the preparation of IL-CNRs includes oxidative cleavage, ionic liquid intercalation and hybridization (Fig. 1).21,28–31 Firstly, the oxidation of water is expected to produce radicals (e.g. hydroxyl and oxygen radicals) when a high oxidation voltage is applied. Secondly, the oxidation of the edge planes opens up the edge sheets and leads to the expansion of the graphite anode, facilitating intercalation by PF6− between the graphene layers. Thirdly, the oxidative cleavage of the expanded graphene sheets generates CNRs. Finally, interaction between CNRs and BMIM+via π–π or cation–π interactions leads to stable IL-CNRs nanocomposites. In comparison with the preparation of CNRs using electron or ion beam etching, chemical ultrasound, lithographic patterning, oxidative cleavage, and chemical vapor deposition (CVD),37–40 this electrochemical method is simple, green and possesses potential for scalable production owing to inexpensive apparatus and easy operation.

3.2. Fluorescence properties of IL-CNRs

The fluorescence properties of IL-CNRs were investigated and results were demonstrated in Fig. 4. The IL-CNRs show good solubility in water and appears light-yellow under daylight, while exhibit strong blue luminescence under UV light (365 nm) (inset in Fig. 4b). The maximum emission is located at 430 nm and the maximum excitation wavelength is 340 nm (Fig. 4a). Like most luminescent carbon nanomaterials, the IL-CNRs also exhibit excitation-dependent fluorescence behavior (Fig. 4b). IL-CNRs prepared under the same conditions independently exhibit the same maximus emission wavelength and a relative standard deviation (RSD) of 2.9% in fluorescence intensity (at 430 nm), indicating high stability and repeatability of the preparation. As the excitation wavelength increases, the fluorescence emission slightly red-shifts, which could be ascribed to size heterogeneity and distribution of different emissive sites on the carbon ribbons. Absolute photoluminescence quantum yield of IL-CNRs is measured to be 11.4%, which may be ascribed to the high crystallinity of IL-CNRs and the presence of BMIM+ on IL-CNRs surface which has electron-withdrawing nitrogen groups. The lifetime of B-GQDs is 5.9 ns (Fig. S3 in ESI†). The IL-CNRs also exhibits good photostability. As shown in Fig. S4 (ESI†), even after being illuminated for 4 h under UV light (365 nm), the fluorescent intensity remains 91%, indicating good anti-photobleaching property.

Fig. 4. (a) The FL excitation spectrum of IL-CNRs obtained at the emission wavelength of 430 nm and FL emission spectrum of IL-CNRs obtained with the excitation wavelength of 340 nm. (b) The FL emission spectra of IL-CNRs obtained with different excitation wavelengths. Insets are the IL-CNRs solutions under sunlight (left) and UV light (365 nm).

Fig. 4

Open in a new tab

3.3. Ion selectivity of IL-CNRs

Ionic liquids modified carbon materials have proven to exhibit anion exchange ability and have potential in direct detection of anion. Thus, the selectivity of the as-prepared IL-CNRs towards different anions were investigated. As revealed in Fig. 5a, the fluorescence of IL-CNRs is strongly quenched by S2−, but not the other physiologically or environmentally relevant anions (Fig. 5a). The lifetime of IL-CNRs in presence S2− is also revealed to be 5.9 ns (Fig. S5 in ESI†). The unchanged fluorescence lifetime of IL-CNRs in the presence of S2− indicates no charge transfer and exciton recombination process.18 The quenching might be ascribed to the ability of anion exchange originated from IL.32,33,41 As fluorescent carbon materials are usually easy to interact with metal cations and cause fluorescence quenching, the selectivity of IL-CNRs towards cations were also investigated. As demonstrated in Fig. 5b, Fe3+ cause fluorescent quenching, while other common cations did not significantly affect the fluorescence intensity of the IL-CNRs. The interactions between IL-CNRs and Fe3+ could be efficiently masked by ascorbic acid (AA). Thus, IL-CNRs have potential for direct and selective detection of S2− ions.

Fig. 5. The relative fluorescent ratio of IL-CNRs in presence of different anion (a) or cation (b). The concentration of ions was 0.3 mM.

Fig. 5

Open in a new tab

3.4. Detection of S2− ions using IL-CNRs as fluorescent probe

The detection of S2− ions using IL-CNRs as fluorescent probe was investigated. To obtain the highest sensitivity, the detection conditions including pH and incubation time were optimized. As illustrated in Fig. S6a (ESI†), S2− ions could quench the fluorescence of IL-CNRs very quickly. As the incubation time goes beyond 60 s, the fluorescence quenching reaches a plateau. Obviously, IL-CNRs possesses great potential for fast detection of S2− ions. Accordingly, the reaction time with IL-CNRs was set as 60 s in the following experiments. In order to avoid protonation of S2− ions, fluorescence quenching by S2− ions was investigated in near neutral solutions. The highest fluorescent quenching is observed at pH 7, which is chosen for further investigated (Fig. S6b in ESI†).

Owing to the fast and sensitive fluorescence quenching of IL-CNRs by S2− ions (insets in Fig. 6a), the fluorescent detection was performed under the optimum conditions. As demonstrated in Fig. 6a, S2− ions caused fluorescence quenching in dose dependent manner. Good linear correlation was found between (F0 − F)/F0 and the concentration of S2− ions from 100 nM to 1 μM and 1 to 300 μM (Fig. 6b). The limit of detection (LOD) for S2− ions is as low as 85 nM at a signal-to-noise ratio of 3. Thus, IL-CNRs based method is sensitive enough to detect the maximum allowable level of S2− ions in drinking water recommended by World Health Organization.42,43 As shown in Table S1 (ESI†), the detection limit obtained with the present method was lower than those obtained by carbon dots (CDs)-Ag+,44 covalent linking fluorescein isothiocyanate with branched-polyethylenimine (PEI-FITC),43 triarylimidazole chromophore (TPI-H)-Cu2+,45 Au nanoclusters,46 lysozyme-stabilized silver nanoclusters (Lys-Ag NCs),47 graphene quantum dot (GQDs)-Cu2+,48 but higher than that obtained using Cu nanoclusters,49,50 Au nanoclusters-Ce(iii),51 and silver nanoparticles capped with carbon dots (AgNPs-CDs).52

Fig. 6. (a) Fluorescence emission spectra of the IL-CNRs upon addition of various concentrations of S2− (from a to n: 0, 0.1, 0.2, 0.4, 0.6, 0.8, 1, 10, 50, 100, 150, 200, 250, 300 μM). Insets are the digital photos of IL-CNRs in the absence (left) and presence (right) of S2− (100 μM) under UV light (365 nm). (b) The linear dependence of the fluorescence quenching ratio (F0 − F)/F0 and the concentration of S2− ions. F0 and F were the fluorescence intensity of IL-CNRs in the absence and presence of S2− ions, respectively.

Fig. 6

Open in a new tab

3.5. Real sample analysis

In order to demonstrate the practical application of the developed fluorescent sensor in detection of S2− in real samples, tap water samples were analyzed by standard addition method. The recoveries ranges from 93.7–103.8% and the relative standard deviations (RSD) is less than 3.0% (Table S2†), indicating the potential for the detection of S2− in complicated real samples.

4. Conclusions

Ionic liquid-functionalized carbon nanoribbons (IL-CNRs) were readily synthesized using one-step electrochemical exfoliation of graphite rod in water-IL biphasic system. The hybridization of IL with CNRs not only results in bright fluorescence of CNRs but also endows IL-CNRs with specific interaction with S2− ions. Taking the advantages of bright photoluminescence and selectivity towards S2−, IL-CNRs are applied for fast, selective and sensitive detection of S2− ion. In contrast with fluorescent detection of S2− ion using turn-off–on mode, this IL-CNRs demonstrate its potential for practical use in direct detection of anions.

Conflicts of interest

There are no conflicts to declare.

Supplementary Material

RA-009-C9RA07701D-s001

Acknowledgments

The authors gratefully acknowledge the financial support from the National Natural Science Foundation of China (No. 81860512 and 81701721), Guangxi Universities' Young and Middle-aged Teachers Scientific Research Basic Ability Improvement Project (2019KY0139), and the Zhejiang Provincial Natural Science Foundation of China (LY19B050008 and LY20B050007).

†

Electronic supplementary information (ESI) available. See DOI: 10.1039/c9ra07701d

References

  1. Karuk Elmas S. N. Ozen F. Koran K. Gorgulu A. O. Sadi G. Yilmaz I. Erdemir S. Selective and sensitive fluorescent and colorimetric chemosensor for detection of CO32− anions in aqueous solution and living cells. Talanta. 2018;188:614–622. doi: 10.1016/j.talanta.2018.06.036. [DOI] [PubMed] [Google Scholar]
  2. Jung J. M. Kang J. H. Han J. Lee H. Lim M. H. Kim K. T. Kim C. A novel “off–on” type fluorescent chemosensor for detection of Zn2+ and its zinc complex for “on–off” fluorescent sensing of sulfide in aqueous solution, in vitro and in vivo. Sens. Actuators, B. 2018;267:58–69. doi: 10.1016/j.snb.2018.03.063. [DOI] [Google Scholar]
  3. Sammi H. Kukkar D. Singh J. Kukkar P. Kaur R. Kaur H. Rawat M. Singh G. Kim K.-H. Serendipity in solution–GQDs zeolitic imidazole frameworks nanocomposites for highly sensitive detection of sulfide ions. Sens. Actuators, B. 2018;255:3047–3056. doi: 10.1016/j.snb.2017.09.129. [DOI] [Google Scholar]
  4. Sun Q. Zhang W. Qian J. A ratiometric fluorescence probe for selective detection of sulfite and its application in realistic samples. Talanta. 2017;162:107–113. doi: 10.1016/j.talanta.2016.10.002. [DOI] [PubMed] [Google Scholar]
  5. Yao Y. Sun Q. Chen Z. Huang R. Zhang W. Qian J. A mitochondria-targeted near infrared ratiometric fluorescent probe for the detection of sulfite in aqueous and in living cells. Talanta. 2018;189:429–436. doi: 10.1016/j.talanta.2018.07.018. [DOI] [PubMed] [Google Scholar]
  6. Wu H. Tong C. Nitrogen- and Sulfur-codoped carbon dots for highly selective and sensitive fluorescent detection of Hg(2+) ions and sulfide in environmental water samples. J. Agric. Food Chem. 2019;67:2794–2800. doi: 10.1021/acs.jafc.8b07176. [DOI] [PubMed] [Google Scholar]
  7. Wang X. Yang X. Wang N. Lv J. Wang H. Choi M. Bian W. Graphitic carbon nitride quantum dots as an “off–on” fluorescent switch for determination of mercury(ii) and sulfide. Microchim. Acta. 2018;185:471. doi: 10.1007/s00604-018-2994-0. [DOI] [PubMed] [Google Scholar]
  8. Wang C. Sun J. Mei H. Gao F. Organic semiconductor polymer nanodots as a new kind of off–on fluorescent probe for sulfide. Microchim. Acta. 2016;184:445–451. doi: 10.1007/s00604-016-2027-9. [DOI] [Google Scholar]
  9. Sinduja B. John S. A. Silver nanoparticles capped with carbon dots as a fluorescent probe for the highly sensitive “off–on” sensing of sulfide ions in water. Anal. Bioanal. Chem. 2019;411:2597–2605. doi: 10.1007/s00216-019-01697-2. [DOI] [PubMed] [Google Scholar]
  10. Shahbazi N. Zare-Dorabei R. A novel “off–on” fluorescence nanosensor for sensitive determination of sulfide ions based on carbon quantum dots and gold nanoparticles: Central composite design optimization. Microchem. J. 2019;145:996–1002. doi: 10.1016/j.microc.2018.12.022. [DOI] [Google Scholar]
  11. Ramachandran M. Anandan S. Ashokkumar M. A luminescent on–off probe based calix[4]arene linked through triazole with ruthenium(ii) polypyridine complexes to sense copper(ii) and sulfide ions. New J. Chem. 2019;43:9832–9842. doi: 10.1039/C9NJ01632E. [DOI] [Google Scholar]
  12. Na W. Qu Z. Chen X. Su X. A turn-on fluorescent probe for sensitive detection of sulfide anions and ascorbic acid by using sulfanilic acid and glutathione functionalized graphene quantum dots. Sens. Actuators, B. 2018;256:48–54. doi: 10.1016/j.snb.2017.09.182. [DOI] [Google Scholar]
  13. Liu J. Liu C. Zhou Z. A turn-on fluorescent sulfide probe prepared from carbon dots and MnO2 nanosheets. Microchim. Acta. 2019;186:281. doi: 10.1007/s00604-019-3413-x. [DOI] [PubMed] [Google Scholar]
  14. Chen X. Yu S. Yang L. Wang J. Jiang C. Fluorescence and visual detection of fluoride ions using a photoluminescent graphene oxide paper sensor. Nanoscale. 2016;8:13669–13677. doi: 10.1039/C6NR02878K. [DOI] [PubMed] [Google Scholar]
  15. Wang Y. Zhang C. Chen X. Yang B. Yang L. Jiang C. Zhang Z. Ratiometric fluorescent paper sensor utilizing hybrid carbon dots-quantum dots for the visual determination of copper ions. Nanoscale. 2016;8:5977–5984. doi: 10.1039/C6NR00430J. [DOI] [PubMed] [Google Scholar]
  16. Wang H. Yang L. Chu S. Liu B. Zhang Q. Zou L. Yu S. Jiang C. Semiquantitative visual detection of lead ions with a smartphone via a colorimetric paper-based analytical device. Anal. Chem. 2019;91:9292–9299. doi: 10.1021/acs.analchem.9b02297. [DOI] [PubMed] [Google Scholar]
  17. Jiang C. Liu B. Han M. Zhang Z. Fluorescent nanomaterials for color-multiplexing test papers toward qualitative/quantitative assays. Small Methods. 2018;2:1700379. doi: 10.1002/smtd.201700379. [DOI] [Google Scholar]
  18. Ge S. He J. Ma C. Liu J. Xi F. Dong X. One-step synthesis of boron-doped graphene quantum dots for fluorescent sensors and biosensor. Talanta. 2019;199:581–589. doi: 10.1016/j.talanta.2019.02.098. [DOI] [PubMed] [Google Scholar]
  19. Lu L. Zhou L. Chen J. Yan F. Liu J. Dong X. Xi F. Chen P. Nanochannel-confined graphene quantum dots for ultrasensitive electrochemical analysis of complex samples. ACS Nano. 2018;12:12673–12681. doi: 10.1021/acsnano.8b07564. [DOI] [PubMed] [Google Scholar]
  20. Xi F. Zhao J. Shen C. He J. Chen J. Yan Y. Li K. Liu J. Chen P. Amphiphilic graphene quantum dots as a new class of surfactants. Carbon. 2019;153:127–135. doi: 10.1016/j.carbon.2019.07.014. [DOI] [Google Scholar]
  21. Chen B. C. Lin H. P. Chao M. C. Mou C. Y. Tang C. Y. Mesoporous silica platelets with perpendicular nanochannels via a ternary surfactant system. Adv. Mater. 2004;16:1657–1661. doi: 10.1002/adma.200306327. [DOI] [Google Scholar]
  22. Arjmand M. Sadeghi S. Khajehpour M. Sundararaj U. Carbon nanotube/graphene nanoribbon/polyvinylidene fluoride hybrid nanocomposites: rheological and dielectric properties. J. Phys. Chem. C. 2016;121:169–181. doi: 10.1021/acs.jpcc.6b10741. [DOI] [Google Scholar]
  23. Yan Y. Gong J. Chen J. Zeng Z. Huang W. Pu K. Liu J. Chen P. Recent advances on graphene quantum dots: from chemistry and physics to applications. Adv. Mater. 2019;31:e1808283. doi: 10.1002/adma.201808283. [DOI] [PubMed] [Google Scholar]
  24. Wang L. Wang Y. Xu T. Liao H. Yao C. Liu Y. Li Z. Chen Z. Pan D. Sun L. Wu M. Gram-scale synthesis of single-crystalline graphene quantum dots with superior optical properties. Nat. Commun. 2014;5:5357. doi: 10.1038/ncomms6357. [DOI] [PubMed] [Google Scholar]
  25. Yang Y. Zhou J. Zhang H. Gai P. Zhang X. Chen J. Electrochemical evaluation of total antioxidant capacities in fruit juice based on the guanine/graphene nanoribbon/glassy carbon electrode. Talanta. 2013;106:206–211. doi: 10.1016/j.talanta.2012.12.030. [DOI] [PubMed] [Google Scholar]
  26. Fukumori M. Pandey R. R. Fujiwara T. TermehYousefi A. Negishi R. Kobayashi Y. Tanaka H. Ogawa T. Diameter dependence of longitudinal unzipping of single-walled carbon nanotube to obtain graphene nanoribbon. Jpn. J. Appl. Phys. 2017;56:06GG12. doi: 10.7567/JJAP.56.06GG12. [DOI] [Google Scholar]
  27. Sadeghi S. Arjmand M. Otero Navas I. Zehtab Yazdi A. Sundararaj U. Effect of nanofiller geometry on network formation in polymeric nanocomposites: comparison of rheological and electrical properties of multiwalled carbon nanotube and graphene nanoribbon. Macromolecules. 2017;50:3954–3967. doi: 10.1021/acs.macromol.7b00702. [DOI] [Google Scholar]
  28. Ananthanarayanan A. Wang X. Routh P. Sana B. Lim S. Kim D.-H. Lim K.-H. Li J. Chen P. Facile synthesis of graphene quantum dots from 3D graphene and their application for Fe3+ sensing. Adv. Funct. Mater. 2014;24:3021–3026. doi: 10.1002/adfm.201303441. [DOI] [Google Scholar]
  29. Xu Y. Liu J. Zhang J. Zong X. Jia X. Li D. Wang E. Chip-based generation of carbon nanodots via electrochemical oxidation of screen printed carbon electrodes and the applications for efficient cell imaging and electrochemiluminescence enhancement. Nanoscale. 2015;7:9421–9426. doi: 10.1039/C5NR01765C. [DOI] [PubMed] [Google Scholar]
  30. Li H. Chen L. Wu H. He H. Jin Y. Ionic liquid-functionalized fluorescent carbon nanodots and their applications in electrocatalysis, biosensing, and cell imaging. Langmuir. 2014;30:15016–15021. doi: 10.1021/la503729v. [DOI] [PubMed] [Google Scholar]
  31. Li X. Zhao Z. Facile ionic-liquid-assisted electrochemical synthesis of size-controlled carbon quantum dots by tuning applied voltages. RSC Adv. 2014;4:57615–57619. doi: 10.1039/C4RA09274K. [DOI] [Google Scholar]
  32. Wang B. Tang W. Lu H. Huang Z. Hydrothermal synthesis of ionic liquid-capped carbon quantum dots with high thermal stability and anion responsiveness. J. Mater. Sci. 2015;50:5411–5418. doi: 10.1007/s10853-015-9085-y. [DOI] [Google Scholar]
  33. Sun X. Qian Y. Jiao Y. Liu J. Xi F. Dong X. Ionic liquid-capped graphene quantum dots as label-free fluorescent probe for direct detection of ferricyanide. Talanta. 2017;165:429–435. doi: 10.1016/j.talanta.2016.12.085. [DOI] [PubMed] [Google Scholar]
  34. Ali M. E. A. Preparation of graphene nanosheets by electrochemical exfoliation of a graphite-nanoclay composite electrode: application for the adsorption of organic dyes. Colloids Surf., A. 2019;570:107–116. doi: 10.1016/j.colsurfa.2019.02.063. [DOI] [Google Scholar]
  35. Chen D. Wang F. Li Y. Wang W. W. Huang T. X. Li J. F. Novoselov K. S. Tian Z. Q. Zhan D. Programmed electrochemical exfoliation of graphite to high quality graphene. Chem. Commun. 2019;55:3379–3382. doi: 10.1039/C9CC00393B. [DOI] [PubMed] [Google Scholar]
  36. Fu Y. Gao G. Zhi J. Electrochemical synthesis of multicolor fluorescent N-doped graphene quantum dots as a ferric ion sensor and their application in bioimaging. J. Mater. Chem. B. 2019;7:1494–1502. doi: 10.1039/C8TB03103G. [DOI] [PubMed] [Google Scholar]
  37. Li X. Wang X. Zhang L. Lee S. Dai H. Chemically derived, ultrasmooth graphene nanoribbon semiconductors. Science. 2008;319:1229–1232. doi: 10.1126/science.1150878. [DOI] [PubMed] [Google Scholar]
  38. Jin C. Lan H. Peng L. Suenaga K. Iijima S. Deriving carbon atomic chains from graphene. Phys. Rev. Lett. 2009;102:205501. doi: 10.1103/PhysRevLett.102.205501. [DOI] [PubMed] [Google Scholar]
  39. Tapaszto L. Dobrik G. Lambin P. Biro L. P. Tailoring the atomic structure of graphene nanoribbons by scanning tunnelling microscope lithography. Nat. Nanotechnol. 2008;3:397–401. doi: 10.1038/nnano.2008.149. [DOI] [PubMed] [Google Scholar]
  40. Lemme M. C. Bell D. C. Williams J. R. Stern L. A. Baugher B. W. H. Jarillo-Herrero P. Marcus C. M. Etching of graphene devices with a helium ion beam. ACS Nano. 2009;3:2674–2676. doi: 10.1021/nn900744z. [DOI] [PubMed] [Google Scholar]
  41. Wang B. Song A. Feng L. Ruan H. Li H. Dong S. Hao J. Tunable amphiphilicity and multifunctional applications of ionic liquid-modified carbon quantum dots. ACS Appl. Mater. Interfaces. 2015;7:6919–6925. doi: 10.1021/acsami.5b00758. [DOI] [PubMed] [Google Scholar]
  42. Chen J. Li Y. Lv K. Zhong W. Wang H. Wu Z. Yi P. Jiang J. Cyclam-functionalized carbon dots sensor for sensitive and selective detection of copper(ii) ion and sulfide anion in aqueous media and its imaging in live cells. Sens. Actuators, B. 2016;224:298–306. doi: 10.1016/j.snb.2015.10.046. [DOI] [Google Scholar]
  43. Lv K. Chen J. Wang H. Zhang P. Yu M. Long Y. Yi P. One-pot fabrication of FRET-based fluorescent probe for detecting copper ion and sulfide anion in 100% aqueous media. Spectrochim. Acta, Part A. 2017;177:63–68. doi: 10.1016/j.saa.2017.01.031. [DOI] [PubMed] [Google Scholar]
  44. Barati A. Shamsipur M. Abdollahi H. Metal-ion-mediated fluorescent carbon dots for indirect detection of sulfide ions. Sens. Actuators, B. 2016;230:289–297. doi: 10.1016/j.snb.2016.02.075. [DOI] [Google Scholar]
  45. Wang Y. Qiu D. Li M. Liu Y. Chen H. Li H. A new “on–off–on” fluorescent probe containing triarylimidazole chromophore to sequentially detect copper and sulfide ions. Spectrochim. Acta, Part A. 2017;185:256–262. doi: 10.1016/j.saa.2017.05.061. [DOI] [PubMed] [Google Scholar]
  46. Wang L. Chen G. Zeng G. Liang J. Dong H. Yan M. Li Z. Guo Z. Tao W. Peng L. Fluorescent sensing of sulfide ions based on papain-directed gold nanoclusters. New J. Chem. 2015;39:9306–9312. doi: 10.1039/C5NJ01783A. [DOI] [Google Scholar]
  47. Sun H. Lu D. Xian M. Dong C. Shuang S. A lysozyme-stabilized silver nanocluster fluorescent probe for the detection of sulfide ions. Anal. Methods. 2016;8:4328–4333. doi: 10.1039/C6AY00300A. [DOI] [Google Scholar]
  48. Yu N. Peng H. Xiong H. Wu X. Wang X. Li Y. Chen L. Graphene quantum dots combined with copper(ii) ions as a fluorescent probe for turn-on detection of sulfide ions. Microchim. Acta. 2015;182:2139–2146. doi: 10.1007/s00604-015-1548-y. [DOI] [Google Scholar]
  49. Chen J. Li Y. Zhong W. Hou Q. Wang H. Sun X. Yi P. Jiang J. Novel fluorescent polymeric nanoparticles for highly selective recognition of copper ion and sulfide anion in water. Sens. Actuators, B. 2015;206:230–238. doi: 10.1016/j.snb.2014.09.034. [DOI] [Google Scholar]
  50. Li Z. Guo S. Lu C. A highly selective fluorescent probe for sulphide ions based on aggregation of Cu nanocluster induced emission enhancement. Analyst. 2015;140:2719–2725. doi: 10.1039/C5AN00017C. [DOI] [PubMed] [Google Scholar]
  51. Liu J. Bao H. Ma D. Leung C. Silver nanoclusters functionalized with Ce(iii) ions are a viable “turn-on–off” fluorescent probe for sulphide. Microchim. Acta. 2019;186:16. doi: 10.1007/s00604-018-3149-z. [DOI] [PubMed] [Google Scholar]
  52. Sinduja B. Abraham John S. Silver nanoparticles capped with carbon dots as a fluorescent probe for the highly sensitive “off–on” sensing of sulfide ions in water. Anal. Bioanal. Chem. 2019;411:2597–2605. doi: 10.1007/s00216-019-01697-2. [DOI] [PubMed] [Google Scholar]

Associated Data

This section collects any data citations, data availability statements, or supplementary materials included in this article.

Supplementary Materials

RA-009-C9RA07701D-s001
RA-009-C9RA07701D-s001.pdf (972.4KB, pdf)